试验研究了退火温度(850~950℃)和时间(5~18 min)对2.3 mm热轧硅钢板(/%:0.036C,3.15Si,0.21Mn,0.005P,0.007S,0.032A1)6道次轧制的0.35 mm冷轧板组织和织构的影响。结果表明,退火温度越高,晶粒平均尺寸越大,900℃5 min退火时平均晶粒尺寸41.39μm,试样织构主要集中在γ取向线上的{111}<112>织构组分和{111}<110>织构组分;900℃18 min退火时平均晶粒尺寸为48.08μm,试样的{111}面织构和{112}面织构密度都明显减弱,{001}面织构增强,磁性能较优。 The effect of annealing temperature(850 ~950 ℃) and holding time(5 ~ 18 min) on structure and texture of 0.35 mm sheet by 6 passes cold-rolling from 2.3 mm hot-rolled plate of silicon steel(/%:0.036 C,3.15 Si,0.21 Mn,0.005 P,0.007 S,0.032A1) has been tested and studied.Results show that the higher the annealing temperature the coarser the average grain size;As annealing at 900 ℃ for 5 min the average grain size of steel sheet is 41.39 μm,and the texture in sample is mainly concentrated in y orie... 

本实用新型公开了一种取向硅钢二轧料氧化镁冷涂装置，包括主体，所述主体的中部安装有架体，且架体的右侧安装有冷涂机构，所述冷涂机构的右端一侧安装有液压气缸，且液压气缸的内壁连接有连接杆，所述架体的前后两端安装有调节架机构，所述调节架机构的表面安装有防护块，且防护块的内壁安装有橡皮套。该取向硅钢二轧料氧化镁冷涂装置设置有冷涂机构，且箱体通过安装有单独喷管和连接喷头，便于使用者两者兼合使用，可使用单独喷管也可连接喷头，使用者可根据自己使用的需求，对单独喷管和连接喷头进行针对性使用，单独喷管通过安装扣将连接喷头进行拼接使用，箱体通过旋转轴与支撑架的旋转，便于将箱体进行角度旋转。

【作者】 卢鹏； ...

根据本发明的一个实施例的双取向电工钢板，以重量％计，所述钢板包含Si：2.0至4.0％、Al：0.01至0.04％、S：0.0004至0.02％、Mn：0.05至0.3％、N：0.01％以下且0％除外、C：0.005％以下且0％除外、P：0.005至0.15％、Ti：0.001至0.005％、Ca：0.0001至0.005％和Mg：0.0001至0.005％，余量包含Fe和其他不可避免的杂质，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的面积分数为60至99％，具有从{100}＆lt;025＆gt;起15°以内的取向的晶粒的面积分数为1至30％。

一种硅钢生产线退火炉前的换热装置，包含有抽风机（1）、立柱（2）、热交换器（3）、软管（4）和热风机（5）；其特征在于：所述的热交换器（3）由若干组U形不锈钢管连接而成，一端固定在轴套（8）上，另一端通过链条（10）连接在立柱（2）顶端的链条盘（9）上，当链条盘（9）转动时，链条（10）拉动热交换器（3）绕着横轴（7）抬起或放下。本实用新型通过抽风机（1）将清洁空气抽到热交换器（3）内进行加热，然后再通过软管（4）将热空气输送到热风机（5）内来加热硅钢板（14），有效的利用了热能，避免了凝露导致的板面发蓝现象。

本发明属于金属材料加工技术领域，具体涉及取向硅钢罩式炉高温退火低保温阶段节能工艺，包括：1)将涂镁取向硅钢卷装入密闭的罩式炉中，并向罩式炉内通入氮气将炉内氧气充分排出，使炉内氧含量浓度≤300PPm；2)通电升温并将氮气转换为10m3/h氮气与氨分解气的混合气体，升温2h将温度升温至500‑600℃后，恒温13h；3)将温度氮气与氨分解气的混合气体转换为12m3/h氨分解气，并升温2h将温度升至650℃恒温15h，使内部气体露点小于‑10℃；本发明提供退火工艺，钢卷在高温下不被水蒸汽氧化，消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷，降低钢带铁损、提高磁感、降低生产成本。此外，本发明进一步减少退火过程中氨分解气的用量，具有极高的工业应用价值。

阐述了国内外高磁感取向硅钢的生产研究水平与发展趋势,包括通过提高高斯晶粒取向度、细化磁畴、涂覆张力涂层、减薄钢片厚度进一步降低铁损以及低温加热技术和短流程技术新工艺。分析高磁感取向硅钢在我国大型电力变压器上的应用情况,结果表明,发展更薄规格高磁感、低铁损、低磁致伸缩取向硅钢可为大型变压器的安全性、节能性及环保性提供有效保障。 The research progress and development trend of high magnetic induction grain-oriented silicon steel at home and abroad are summarized,including the technology of improving the Goss alignment,refining domain wall,adding stress coating,decreasing thickness of sheet,and the new technique of reducing heating temperature of casting slab and shortening operational.Moreover,the application of high magnetic induction grain-oriented silicon in power transformer is presented.Developing grain-oriented sili... 

根据本发明的一个实施例的双取向电工钢板，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的分数为50至75％，并且具有从{100}＆lt;380＆gt;起15°以内的取向的晶粒的分数为50至75％。

采用磁控溅射方法,分别在纯Fe以及低硅钢基片上沉积富Si膜,并对其进行真空扩散热处理.通过能谱分析及X射线衍射研究了Si在纯Fe与低硅钢基体中的扩散特征,运用DICTRA软件建立了扩散模型.研究发现Si在纯Fe基体中扩散时发生γ-Fe(Si)→α-Fe(Si)相转变,扩散速率受控于相界面的迁移.当沿截面Si含量梯度不足以驱动相界面正向迁移时,延长扩散时间会发生相界面回迁现象,最终趋于单一相内均匀化扩散过程.Si在低硅钢基体中的扩散符合Fick扩散第二定律. Si-rich films were deposited on pure iron and low-Si steel substrates by direct current magnetron sputtering,and then were subjected to vacuum annealing.The distribution characteristics of Si across Fe and low-Si steel substrates were studied by energy spectrum analysis(EDS) and X-ray diffraction(XRD).DICTRA software was used to simulate the diffusion models.It is found that the diffusion behavior of Si in the Fe substrate is from γ-Fe(Si) phase to α-Fe(Si) phase and the rate of diffusion is con... 

硅钢连续退火线是无取向硅钢生产的成品线。由于受机组布置的影响,带钢经转向辊进出口活套后,当套量达到60%后就出现偏离生产线的情况,从而影响最终产品的质量及成材率,甚至损坏设备。针对某冷轧厂硅钢连续退火机组出口活套入口处带钢跑偏开展纠偏研究,利用Matlab对该纠偏系统进行动态仿真研究,分析系统的稳定性。 Silicon steel continuous annealing line is non oriented silicon steel production of finished product line.Due to the influence of unit layout,strip by roll Import & Export loop,when the set volume reached 60% after the emergence of deviation from the production line,thus affecting the quality of the final product and the rate of finished products,and even damage the equipment.For the export of continuous annealing line in cold rolling silicon steel strip deviation rectification loop at the e... 

根据新日铁、JFE及浦项等国外钢铁公司2008年以来在日本专利局、欧洲专利局(EP)及世界知识产权组织(WIPO)申请公开的有关生产Hi-B取向电工钢典型专利技术,概述了近年来国外大型钢铁企业采用低温板坯加热(坯加热温度<1 280℃)技术生产Hi-B取向电工钢主要技术重点,即将调节关键化学成分Al、N、Sn及Sb等与工艺改进相结合。最后介绍了国外大型钢铁企业采用低温板坯加热技术生产Hi-B取向电工钢实例。 The latest developments on technology for manufacturing Hi-B grain oriented electrical steel sheets developed by Nippon Steel Corp.,JFE Steel and POSCO were described according to the patents published by World Intellectual Property Organization,Japan Patent Office and European Patent Office over the recent years.The low temperature slab heating process(particularly slab-heating temperature<1 280 ℃) together with suitably adjusting key chemical elements such as Al,N,Sn and Sb elements was the... 

对w(Si)=3%无取向硅钢进行表面机械研磨处理(SMAT)和异步轧制(CSR),获得表面纳米结构,再进行550～650℃、4 h固体粉末渗硅处理,用透射电镜(TEM)、扫描电镜(SEM)和X射线衍射仪(XRD)研究表层组织演变。结果表明:经过SMAT后,w(Si)=3%无取向硅钢表面形成了等轴状、取向呈随机分布的、晶粒尺寸为10 nm的纳米晶组织;异步轧制后,表面纳米晶组织保持不变;550～650℃、4 h渗硅处理后,SMAT+CSR样品表面形成化合物层,其厚度随着温度的升高由17μm增加到52μm;化合物层由Fe3Si和FeSi相组成. Nanostructured surface layer was fabricated on a 3%(mass fraction) non-grain oriented silicon steel by means of surface mechanical attrition treatment(SMAT) and cross-shear rolling(CSR),and then a solid powder siliconizing treatment was carried out for the SMAT+CSR sample at 550~650 ℃ for 4 h.The microstructural evolution was examined by using transmission electron microscopy(TEM),scanning electron microscopy(SEM) and X-ray diffraction(XRD).Experimental results show that: equiaxed nanocrystallin...