硅钢资料

本实用新型公开了一种硅钢片焊接模具，包括底座，底座上均匀排布有多条滑槽，每条滑槽内连接有一根垂直设置的定位杆，定位杆底部穿过底座连接一气缸，气缸连接在底座底部。本实用新型结构设计合理巧妙，移动不同位置的定位杆，将定位杆与硅钢片贴合，不同滑槽内的定位杆之间相互错位，并利用气缸将硅钢片定位，这种结构不可以适用于各种形状的硅钢片，使用方便快捷。

采用光学显微镜和X射线衍射仪研究了常化退火处理对无取向硅钢热轧板和成品退火板显微组织和织构的影响。结果表明:常化退火处理消除了热轧板中的变形组织,促使变形晶粒完成再结晶;常化退火处理使高斯织构和立方织构易通过再结晶在变形带内形核和长大,可显著降低成品退火板的{111}和{112}不利织构组分的占有率,提高{100}和{110}有利织构组分的占有率,从而有利于提高无取向硅钢成品板的磁性能。 The effect of normalizing annealing treatment on microstructure and texture of non-oriented silicon steel hot rolled plates and final products were investigated by means of optical microscope and X-ray diffractometer analysis.The results show that the deformed microstructure of the hot rolled plates transformed into recrystallized grain after normalizing annealing treatment.The grains of Goss texture and cubic texture crystallographic orientation were formed and grown by recrystallization in the... 

一种高硅钢的电渣重熔生产方法，电渣重熔过程渣系组成为，按重量计，CaF255%～59%、Al2O326%～30%、CaO7%～10%、SiO21%～9%，所述高Si钢，按重量计，钢中含有Si0.5%～2.0%，Al0.01％～0.05％。采用本专利设计的渣系成分配比，保护气氛电渣的情况下，可有效控制Si含量0.5‑2.0%的高Si钢电渣过程不增铝。

本发明涉及一种用于伴随用于生产非晶粒取向的电工钢带的热处理来加工含硅冷轧钢板的方法，其中，钢板2所含硅的重量比例在1.5％和6％之间，并且其中，钢板以带形状态提供并且在热处理期间在连续的过程中运动通过具有加热区域、保持区域和冷却区域的退火设备，其中，钢板在退火设备3沿垂直的主运送方向运动。

取向硅钢因其高磁导率、低矫顽力和大电阻系数等特性，被广泛应用于大中型变压器和大型电动机铁芯的制造。因取向硅钢性能和成分控制严格，生产工艺复杂，故其产品代表了钢铁企业特殊钢生产的最高水平。本文介绍了新钢公司卷板厂1580热连轧线生产取向硅钢过程中出现的窄尺问题，研究了取向硅钢产品的特点，分析了热轧过程中的组织转变，并结合生产实际提出了改进措施。通过对加热炉钢坯加热模式、粗轧轧制策略、精轧轧制工艺、二级模型等方面的优化和改进，取向硅钢窄尺情况明显好转，提高了产品的成材率和市场口碑。 The oriented silicon steel is widely used in the iron core manufacture of large and mediumsized transformers and large motors because of its high permeability, low coercivity and large resistance coefficient. Due to the performance and composition control of oriented silicon steel is strict, the production process is complex,therefore, its products represent the highest level of special steel production in iron and steel enterprises. This paper introduces the problem of narrow gauge in the produ... 

结合工业化生产过程中出现的同卷带钢头、尾磁性能差异现象,对50SW1300牌号无取向硅钢同卷带钢头、尾试样的夹杂物、晶体织构和显微组织进行了分析研究。结果表明,夹杂物、晶体织构是影响成品钢卷磁性能的重要因素。夹杂物是造成同卷带钢头、尾铁损差异的主要原因。夹杂物数量越多,尤其是小尺寸的夹杂物数量越多,对成品带钢的磁性能影响越大,对于本试验而言,AlN和MnS是影响成品带钢磁性能的主要夹杂物。晶体织构是造成同卷带钢头、尾磁感应强度差异的主要原因。有益的{100}和Goss织构含量越大,有害的{111}<110>和{111}<112>织构含量越小,即有益织构与有害织构含量比越大,成品带钢的磁感应强度越大。 Based on the industrial manufacture of non-oriented silicon steel sheets 50SW1300, the magnetic property variation of head and tail of the same finished steel sheets was discussed by analyzing non-metallic inclusion, crystal texture, and microstructure. Results show that, both of the non-metallic inclusion and the crystal texture will affect the magnetic properties significantly. The non-metallic inclusion is the key factor of the core loss variation of head and tail of the same finished steel s... 

针对宝钢集团、日本新日铁住金和JFE公司公开的相关专利等资料,总结了国内外高强度无取向电工钢的研究进展,分析了不同电工钢的化学成分、生产工艺及产品性能,指出固溶强化、细晶强化、析出强化、位错强化都有可能被用来提高无取向电工钢的强度,并阐述了四种强化方式的优缺点;指出在高强度无取向电工钢的研发过程中,需根据其具体用途确定目标性能,再采用合适的强化手段,最终实现力学性能、磁性能和生产性能之间的平衡。 The research progress of high strength non-oriented electrical steels at home and abroad is summarized according to related patents brought into the public by Baosteel,Nippon Steel & Sumitomo Metal corporation and JFE corporation.The characteristics of chemical composition,production technology and properties of products in the patents are analyzed.Each of solution strengthening method,fine-grain strengthening method, precipitation strengthening method or dislocations strengthening method ma... 

为开发高效电机用冷轧无取向电工钢,借助实验室薄板坯连铸连轧模拟设备及扫描电镜、透射电镜等检验手段研究了成分、组织、织构和析出物等对无取向电工钢磁性能的影响规律;结果表明:常化处理使组织均匀化并增加有利于磁性提高的织构组分;采用CSP流程开发的高效电机用无取向电工钢铁损平均值3.4 0 W/kg,磁感≥1.68 T。 In order to develop electrical steel for high efficiency motor,effect of components,microstructure,texture and precipitation on magnetic property of electrical steel are analyzed.From the result,normalizing treatment makes microstructure uniform and increases component of favorable texture.Iron loss of electrical steel developed by CSP line is 3.40W/kg and magnetic induction is more than 1.68T. 

根据本发明的一个实施例的双取向电工钢板，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的分数为50至75％，并且具有从{100}＆lt;380＆gt;起15°以内的取向的晶粒的分数为50至75％。

本申请实施例公开了一种硅钢片卷绕机调节装置，包括底部支撑座，所述底部支撑座一侧的内部活动套接有伸缩调节板，所述伸缩调节板的上部固定连接有上部定位套，所述上部定位套内部的上端活动套接有第一定位板，所述上部定位套的内部安装有第一螺纹定位杆。该硅钢片卷绕机调节装置，通过带动硅钢片夹持在上下两个夹持板之间，即可带动夹持板之间的挤压力，带动硅钢片两侧位置进行限定，避免硅钢片收卷时出现振动和偏移的问题，同时装置夹持板的内部活动套接有滚轮，即可在硅钢片移动过程中，可带动滚轮旋转，即可带动硅钢片与滚轮之间的摩擦阻力降低，至此可带动硅钢片移动时的灵活性，避免硅钢片移动时出现卡死的问题。

采用铸坯低倍组织检验和化学分析的方法,研究板坯连铸机二冷区电磁搅拌器电流和频率参数对无取向电工钢XG800WR板坯中心偏析和等轴晶率的影响,结果表明:铸坯等轴晶率随着搅拌器电流强度和电流频率的增大而增加。采用二冷区电磁搅拌可减小中心易偏析元素S的偏析,试验得出:减小铸坯S偏析效果最好的电磁搅拌参数为电流380～400A,频率6Hz。 The effect of electromagnetic stirring current and frequency parameter at secondary cooling area on the central segregation and equiaxed crystal ratio of XG800WR non - oriented electrical steels slab was investigated through the methods of chemical and macrostructure analysis.The results shows that the rate of equiaxed crystal zone is going up with increasing of current intensity and current frequency.Electromagnetic stirring in the secondary cooling area can be easily reduced segregation caused... 

本实用新型涉及一种取向硅钢氧化镁线涂层装置，尤其涉及一种取向硅钢氧化镁涂层线用冷涂辊，具有涂层辊本体及包覆在涂层辊本体外层的橡胶涂层；涂层辊本体内部为空腔结构，空腔结构内通有循环冷冻液。本实用新型涂层辊内部设计成空腔结构，并通过循环冷冻液对涂层辊进行冷却降温，既可以达到通过涂层辊对氧化镁进行降温的目的，从而满足工艺要求，防止质量缺陷的产生，还可延缓涂层辊因反复摩擦生热造成橡胶层老化，从而延缓涂层辊使用寿命。