本发明是高磁感取向硅钢的脱碳退火工艺，首先对硅钢卷进行放卷、活套、清洗；再对硅钢进行脱碳、渗氮处理，氨气流量6‑20m3/h、加湿槽温度30‑70℃，脱碳温度780‑880℃、机组速度45‑75m/min、气氛中氢气比例20‑60％、氮气比例40％‑80％，然后冷却到常温；对硅钢进行活套；再对硅钢进行涂覆氧化镁，涂覆量4‑10g/㎡；最后对硅钢进行干燥和收卷成硅钢卷；通过本发明对高磁感取向硅钢的脱碳退火工艺流程进行了优化设计，调整了脱碳退火工艺中氨气流量、气氛、加湿槽水温等参数，优化了高磁感取向硅钢中碳元素、氮元素和氧元素的含量，最终使高磁感取向硅钢实现稳定的性能，磁感达1.92T。

利用EBSD技术研究了电工钢中长轴平行于轧向的柱状晶样品在热轧和退火过程中组织和取向的演变规律,并与长轴平行于板法向的样品的已有研究结果进行对比。结果表明,无论柱状晶按何种方向排列,只要表面存在剪切力,热轧后都可形成剪切织构,同时中心形成轧制织构,主要包括旋转立方织构和{112}<1-10>。柱状晶造成的影响主要体现在板中心层,长轴平行于轧向排列的样品热轧时形成的粗大旋转立方晶粒要到脱碳退火后才能完全消除,但破坏了正常的不同取向晶粒间的取向差分布及尺寸均匀性,导致二次再结晶不完全及磁性能降低。 The evolution of microstructure and grain orientation in an electrical steel containing columnar grains with its long axis being parallel to the rolling direction of sheet was studied during hot rolling and annealing by EBSD technique.The results are compared with those of samples containing columnar grains being parallel to normal direction of sheet reported in the reference [3].It was shown that,whether the long axis of columnar grains was arranged in RD or ND,shear textures can be formed in t... 

本发明公开一种高牌号无取向硅钢的轧制方法，用于控制森基米尔二十辊轧机对原料带钢进行轧制，所述方法包括：根据所述原料带钢的规格参数，确定所述森基米尔二十辊轧机的第一中间辊的辊型及第二中间辊的辊型；根据所述原料带钢的合金含量及所述规格参数，确定所述第一中间辊的有效平面量；根据所述规格参数，确定所述森基米尔二十辊轧机的径向调整机构的凸度值；根据所述合金含量，设定所述森基米尔二十辊轧机进行轧制时的负荷分配和张力；按照所设定的负荷分配和张力分配对所述原料带钢进行轧制，且在轧制过程中以预设乳化液流量进行喷淋，以制得成品。本发明可减少高牌号无取向硅钢在轧制过程中发生脆性断裂，提高轧制的稳定性及生产效率。

本发明公开了一种减少低温高磁感取向硅钢点状露金缺陷的方法。本发明通过控制低温高磁感取向硅钢的脱碳和渗氮工艺，特别是通过控制脱碳露点、渗氮露点、脱碳氧化度、脱碳时间来调节钢板经脱碳渗氮后表面形成的内氧化层中FeO/SiO2的比例，结合氧化镁退火隔离剂的含水率控制，获得了一种可避免点状露金缺陷的低温高磁感取向硅钢生产方法。

针对某厂DMS森吉米尔轧机生产无取向硅钢表面麻面缺陷的问题，根据生产实际，对其形成原因从乳化液及工作辊两方面因素进行了分析。结果表明：乳化液对麻面缺陷的产生有一定影响，但不是主要因素，主要原因是由于二十辊森吉米尔轧机工作辊辊径较小，轧制相同长度带钢轧辊运转周期较大，容易产生疲劳失效而导致。为此，提出通过调整冷轧工序成品轧制道次的压下率以减小轧制力，从而减小工作辊的磨损疲劳；通过对轧制乳化液浓度、温度的合理控制，以改善润滑效果、提高轧制速度，而进一步缓解轧辊疲劳的改进措施，使该钢厂无取向硅钢麻面缺陷发生率由原来的18%降至0.8%,带钢表面质量明显改善。 For the problem of surface pockmarks of non-oriented silicon steel strip produced by a DMS Sendzimir mill, based on the production practice, the formation causes were analyzed from two aspects of emulsion and working roll. The results show that the emulsion has a certain effect on the formation of surface pockmarks defects, but it is not the main factor. The main reason is that the working roll diameter of the 20-high Sendzimir mill is small, and the running period of the roll rolling the same l... 

针对宝钢集团、日本新日铁住金和JFE公司公开的相关专利等资料,总结了国内外高强度无取向电工钢的研究进展,分析了不同电工钢的化学成分、生产工艺及产品性能,指出固溶强化、细晶强化、析出强化、位错强化都有可能被用来提高无取向电工钢的强度,并阐述了四种强化方式的优缺点;指出在高强度无取向电工钢的研发过程中,需根据其具体用途确定目标性能,再采用合适的强化手段,最终实现力学性能、磁性能和生产性能之间的平衡。 The research progress of high strength non-oriented electrical steels at home and abroad is summarized according to related patents brought into the public by Baosteel,Nippon Steel & Sumitomo Metal corporation and JFE corporation.The characteristics of chemical composition,production technology and properties of products in the patents are analyzed.Each of solution strengthening method,fine-grain strengthening method, precipitation strengthening method or dislocations strengthening method ma... 

研究了退火温度对3.1%Si无取向硅钢组织和磁性能的影响规律。结果表明:退火温度从940℃提高至1 000℃,平均晶粒尺寸由98μm增加到145μm,铁损P_1.5/50从2.576 W/kg降低至2.408W/kg。随着退火温度的升高,γ不利织构组分强度逐渐降低,{111}〈112〉织构组分强度降低约16%,磁感B₅₀逐渐升高,磁性能水平提高。 The effects of annealing temperature on microstructure and texture and magnetic properties of 3.1%Si non-oriented silicon steel were investigated in this paper.The results showed that,when the annealing temperature increased from 940℃ to 1 000℃,the average grain size of metallographic structure increased from 98μm to 145μm,the iron loss value P_1.5/50 decreased from2.576 W/kg to 2.408 W/kg.And as the annealing temperature increased,the strength of the unfavorable texture componentγgrad... 

本实用新型公开了一种取向电工钢的多项性能检测装置，涉及取向电工钢技术领域，为解决检测装置在对取向电工钢涂层性能检测时较为繁杂，增加了检测难度，检测的误差增加，且检测装置的性能检测较为单一，检测效果不佳的问题。所述底座的上方设置有安装架和吊梁架，所述安装架上设置有输料辊，输料辊设置有两个，两个所述输料辊之间设置有输送带，所述吊梁架的下方设置有弹性胶带，所述弹性胶带上方的两侧均设置有第三电动伸缩杆，且第三电动伸缩杆的两端分别与吊梁架和弹性胶带通过螺钉连接，所述弹性胶带的一侧设置有检测架，所述检测架上设置有激光灯、第一滤光片、接收器、第二滤光片和聚光片，所述激光灯和第一滤光片设置在弹性胶带的上方。

根据本发明的一个实施例的双取向电工钢板，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的分数为50至75％，并且具有从{100}＆lt;380＆gt;起15°以内的取向的晶粒的分数为50至75％。

本实用新型公开了一种变压器铁芯硅钢片纵剪滚切装置，包括纵剪机本体、弹性压覆机构和涂油机构，所述纵剪机本体的进料端设置有弹性压覆机构，料带通过弹性压覆机构压覆在纵剪机本体的支撑平台上，所述支撑平台上凹设有安装凹槽，所述安装凹槽内设置有涂油机构，所述涂油机构朝向于料带的底面涂油，通过涂油机构对板材的切割面进行涂油，能够对料带起到润滑和冷却的作用，提升料带切割质量。

通过制备磷酸二氢铝硅钢涂层,研究了氧化锌对无铬涂层耐盐雾性能、电化学性能和附着性的影响。结果表明,硅钢表面涂层含有4.0%的氧化锌时,涂层具有最高的耐腐蚀性能和电化学性能,而且其致密表面最为平整,没有裂纹出现。 The effects of ZnO on the salt spray resistance property, electrochemical performance and adhesiveness of silicon steel insulating coating were studied. The results show that the best corrosion resistance and electrochemical properties can be obtained when the coating contains 4.0% oxide zinc, and the dense surface is smooth without cracks. 

本发明涉及一种硅钢热处理方法，尤其涉及一种取向硅钢极薄带绝缘层涂覆方法，包括以下步骤：(1)接入普碳钢引带的准备工作；(2)各炉段张力的设定工作；(3)炉内气氛及温度的调节工作；(4)绝缘层厚度及厚度的检测工作；(5)极薄带涂层涂覆及烘干工作；(6)极薄带表面绝缘涂层及磁性能检测工作。本发明采用与极薄带厚度相当的普碳钢作为引带，通过引带测试产线张力和绝缘层涂覆的厚度，一方面可通过普碳钢薄带的运行加速炉内温度和气氛的稳定性，节约炉内稳定时间；另一方面可通过成本较低的普碳钢检测炉内张力和温度的设定，及绝缘涂层的涂覆效果，避免开始采用硅钢带出现断带，及涂覆不合格后造成产品报废带来的成本升高。