【机构】 宝山钢铁股份有限公司规划与科技部； ...

本实用新型公开了硅钢片生产用上料装置，属于硅钢片生产领域，包括本体，所述本体包括侧板和U型板，所述侧板固定连接在U型板的一侧，所述本体的顶部横向设置有平移机构，所述平移机构上安装有气缸，所述气缸的底部安装有吸盘，所述U型板内腔的底部竖向固定连接有弹簧，所述弹簧远离U型板的一端水平固定连接有升降板，所述平移机构包括电机、螺纹杆、限位板和移动块，所述电机安装在侧板的顶部，所述电机的输出轴与螺纹杆的一端固定连接，通过设置弹簧，在第一个物料从上料装置移出后弹簧的弹力推动剩余物料，使得剩余物料进行上升，避免吸盘触碰不到物料的问题，简化吸盘移动轨迹，加快上料速度。

介绍了CSP工艺生产无取向电工钢各工序的设备特点、采用的工艺控制手段和电工钢产品质量情况,结合生产实践证明了马钢CSP工艺开发的无取向电工钢产品丰富了薄板坯连铸连轧的品种结构,发挥了薄板坯连铸连轧生产无取向电工钢性能均一、稳定的特点。 The equipment characteristic,the process control method and the quality of non-orientated silicon steel by CSP process were introduced.Combined with the production situation,it is proved that production of non-orientated silicon steel developed on Masteel CSP line would enrich product structure of thin slab continuous casting and rolling,and it exerts stable performance of non-orientated silicon steel. 

本发明涉及一种冷轧硅钢厚度缺陷识别方法、装置及系统，本发明的方法包括如下步骤：采集带钢设定厚度及其实际测量厚度并保存；将带钢实际测量厚度与带钢设定厚度相减得到实时厚度差；根据实时厚度差计算厚度缺陷评分；根据评分结果，确定带钢在厚度这一指标的缺陷等级。本发明评估过程考虑了厚度波动情况，并进行量化，能成功识别冷轧硅钢的厚度缺陷，设别准确性较高，提高了冷轧硅钢生产水平，为冷轧硅钢质量控制提供依据。

本发明属于取向硅钢制备技术领域，具体涉及一种软磁材料取向硅钢退火工艺。所述退火工艺主要包括：涂覆隔离剂、按照一定速率升温后进行保温，以5‑10℃/min的速率进行降温；在降温过程中施加恒定磁场，之后继续降温即可实现。该退火工艺能够有效降低铁损失，提高磁感强度。同时具有较好的耐腐蚀性能和机械性能。

本实用新型公开了一种硅钢片焊接模具，包括底座，底座上均匀排布有多条滑槽，每条滑槽内连接有一根垂直设置的定位杆，定位杆底部穿过底座连接一气缸，气缸连接在底座底部。本实用新型结构设计合理巧妙，移动不同位置的定位杆，将定位杆与硅钢片贴合，不同滑槽内的定位杆之间相互错位，并利用气缸将硅钢片定位，这种结构不可以适用于各种形状的硅钢片，使用方便快捷。

试验2.3Si无取向硅钢(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al)冷轧板由常化和未常化的2.5 mm热轧板冷轧至0.6 mm(压下率76%),经750~950℃2.5 min中间退火后再冷轧至0.5 mm(压下率16.7%),成品板经890℃+960℃2.5 min退火。研究了中间退火温度对该钢晶粒尺寸、织构和磁性能的影响。结果表明,随中间退火温度的升高,二次冷轧前晶粒和成品晶粒增大,成品中不利织构组分{111}和{112}减弱,磁性能得到改善。热轧板经过常化时的磁性能明显好于未经常化时的磁性能,但中间退火温度较高时常化对磁性能的有利作用减弱。 The test cold sheet of 2.3Si non-oriented silicon steel(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al) is first cold-rolled from normalized and un-normalizing 2.5 mm hot-rolled plate to 0.6 mm sheet(reduction 76%),then intermediate annealed at 750~950℃ for 2.5 min and double cold-rolled to 0.5 mm sheet(reduction16.7%),the finished sheet annealed at 890℃+960℃ for 2.5 min.Effect of the intermediate annealing temperature on grain size,texture and magnetic performance of the steel has been studied.... 

介绍了普通取向硅钢(CGO)和高磁感取向硅钢(Hi-B)铸坯高温加热两次冷轧、一次冷轧和铸坯低温加热两次冷轧、一次冷轧法4种成熟生产工艺的主要技术参数,取向硅钢理论研究(Goss晶核和抑制剂)和生产技术现状。取向钢的发展趋势为:提高(110)[001]晶粒取向度,降低取向硅钢铁损,发展铸坯低温加热(≤1 300℃)和薄板坯连铸连轧流程生产取向硅钢工艺。 Main technology parameters of four developed process:cast bloom higher temperature heating-double cold rolling or single cold rolling,lower temperature heating-double cold rolling or single rolling process for production of common grain oriented silicon steel(CGO) and high magnetic induction grain oriented silicon steel(Hi-B),theory research on grain oriented steel(Goss nucleus and inhibitor) and present situation of process are summarized in this paper.The development trend of grain oriented si... 

本文介绍了无取向硅钢C6涂液的性能,研究了配水量、固化程度和涂层厚度等因素对无取向硅钢C6涂层性能的影响。结果表明,随着配水量的增加,完全固化所需的时间增加,涂液固体含量降低,涂层厚度减小;随着固化程度的提高,涂层硬度先增大然后趋于恒定,而柔韧性逐渐变差,在过固化后急剧恶化;涂层厚度对涂层的表面外观、附着性和绝缘层间电阻均有显著影响。 Based on the introduction about the performance of C6 varnish for non-oriented silicon steel sheets,effects of water amount,curing degree and coating thickness are discussed. Results show that with the increase of water amount,the time required to cure completely extends,and both the solid content of C6 varnish and the coating thickness decrease. As the curing degree increases,the hardness of the coating increases first and then tends to be constant,however the flexibility degenerates,especially... 

本实用新型公开了一种电工钢表面清洗装置，包括机架、第一传送链和叶片，所述机架的上端固定有顶板，且顶板的内部连接有加料杆，并且加料杆的上端内部设置有固定帽，所述顶板的侧面固定有第一电动机，且第一电动机的一端连接有丝杆，所述丝杆的外侧设置有电动推杆，所述第二转动轴的侧面连接有第二传送链，所述顶板的下端连接有连接架，且连接架的内部设置有第三电动机，所述连接架的底部设置有第二清洁杆，所述机架的内部开设有固定孔。该电工钢表面清洗装置，往加料杆的内部加入清洁液，清洁液会被加料干底部的海绵吸收，当料与加料杆的底部摩擦时，清洁液就会附着在料的表面，从而实现定量的往装置的内部加入清洁液。

对熔融态钢液进行处理,研究了电脉冲对于取向硅钢凝固组织的影响作用,利用正交试验法研究了脉冲电容、频率、处理时间和电压等脉冲参数的作用效果。结果表明:电脉冲对钢锭晶粒组织具有明显的细化作用,凝固组织的等轴晶比例大幅上升,影响等轴晶比例的最显著性因素为脉冲频率,最优正交试验参数为电容1 200μF,脉冲频率1 Hz,处理时间5 s,脉冲电压800 V。随着输入能量的增大等轴晶率先增大后减小,脉冲输入能量为某值时,等轴晶率最大,利用经典形核理论和热力学对这一现象进行了解释。 The influence of electric pulse on the solidification structure of oriented silicon steel was investigated by applying electric pulse in molten steel.The affection due to different electric pulse parameters such as electric capacity,frequency,applied time and voltage was studied by orthogonal design test.The result showed that solidification structure of oriented silicon steel could be improved by the electric pulse,and the equiaxed crystal ratio increased obviously.The most influential paramete... 

本发明公开了一种普通级稀土取向硅钢制备方法，通过添加稀土元素，利用第二相作用，对铸坯组织、热轧组织、初次再结晶晶粒和二次再结晶晶粒的影响，改善成品磁性能，即降低铁损，提高磁感。