本发明提供了一种超低铁损无取向硅钢薄带，以质量百分比计，其成分包括C≤0.005％，Si：3.5～4.0％，Mn：0.1～0.3％，Als≤0.005％，P≤0.05％，S≤0.005％，Cu≤0.08％，N≤0.003％，Sn：0.04～0.08％，其余为Fe及不可避免杂质，所述硅钢薄带中Mn与S的含量比Mn/S≥50，所述硅钢薄带厚度为0.3‑0.4mm。本发明还提供了一种超低铁损无取向硅钢薄带的制备方法。本发明提供的一种超低铁损无取向硅钢薄带，具有高磁感、低铁损等优良性能，且其制备工艺流程短、容易实现、生产效率高、生产成本低、节能降耗明显。

结合工业化生产过程中出现的同卷带钢头、尾磁性能差异现象,对50SW1300牌号无取向硅钢同卷带钢头、尾试样的夹杂物、晶体织构和显微组织进行了分析研究。结果表明,夹杂物、晶体织构是影响成品钢卷磁性能的重要因素。夹杂物是造成同卷带钢头、尾铁损差异的主要原因。夹杂物数量越多,尤其是小尺寸的夹杂物数量越多,对成品带钢的磁性能影响越大,对于本试验而言,AlN和MnS是影响成品带钢磁性能的主要夹杂物。晶体织构是造成同卷带钢头、尾磁感应强度差异的主要原因。有益的{100}和Goss织构含量越大,有害的{111}<110>和{111}<112>织构含量越小,即有益织构与有害织构含量比越大,成品带钢的磁感应强度越大。 Based on the industrial manufacture of non-oriented silicon steel sheets 50SW1300, the magnetic property variation of head and tail of the same finished steel sheets was discussed by analyzing non-metallic inclusion, crystal texture, and microstructure. Results show that, both of the non-metallic inclusion and the crystal texture will affect the magnetic properties significantly. The non-metallic inclusion is the key factor of the core loss variation of head and tail of the same finished steel s... 

通过微观组织表征、高温拉伸和断口形貌分析,研究了钇(Y)元素对6.5%Si无取向硅钢组织、高温拉伸及断裂机制的影响。研究结果表明,添加Y元素可以在钢液中形成YS和YP的复合析出。YS和YP可以充当异质形核基底,提高形核率,细化凝固组织。热轧组织不均匀,由表层至芯部分别形成等轴晶、等轴晶/拉长晶和拉长晶的混合组织。退火后,热轧变形组织转变为等轴晶,含Y实验钢的退火组织得到明显细化。500℃时效处理后,含Y实验钢具备较低的有序度,300℃的拉伸断口呈现韧性断裂特征,断后伸长率达到20.2%。相反,无Y实验钢发生脆性断裂,断后伸长率仅为2.1%。研究结果证实,Y元素可以通过组织细化和降低有序度提高6.5%Si无取向硅钢的中温塑性。 The effects of yttrium(Y)on microstructure,elevated-temperature tensile properties and fracture mechanism of 6.5% Si non-oriented electrical steel were investigated by means of microstructure characterization,high-temperature tensile test and fracture analysis.The results showed that the doping of Y introduced composite Y-rich precipitates(YS/YP)in the melt.YS and YP precipitates were qualified for heterogeneous nucleation agents,which thus raised the nucleation rate and refined the solidificati... 

本发明提供一种在同一卷材内得到稳定的磁特性的方向性电磁钢板的制造方法。上述方向性电磁钢板的制造方法，包括如下步骤：将具有规定的成分组成的钢坯热轧而制成热轧板，将上述热轧板退火而制成热轧板退火板，对上述热轧板退火板实施1次或隔着中间退火的2次以上的冷轧而制成最终板厚的冷轧板，对上述冷轧板实施一次再结晶退火和二次再结晶退火；上述冷轧包括至少1次的压下率为80％以上且轧制速度为设定值R0(mpm)期间的钢板温度T0(℃)与轧制速度为0.5×R0(mpm)以下期间的钢板温度T1(℃)满足式(1)的冷轧。

本实用新型公开了一种硅钢片焊接模具，包括底座，底座上均匀排布有多条滑槽，每条滑槽内连接有一根垂直设置的定位杆，定位杆底部穿过底座连接一气缸，气缸连接在底座底部。本实用新型结构设计合理巧妙，移动不同位置的定位杆，将定位杆与硅钢片贴合，不同滑槽内的定位杆之间相互错位，并利用气缸将硅钢片定位，这种结构不可以适用于各种形状的硅钢片，使用方便快捷。

本发明提供能够制造实现高磁通密度且磁特性优异的方向性电磁钢板的新颖并且得以改良的方向性电磁钢板的制造方法。本发明的一方案提供一种方向性电磁钢板的制造方法，其特征在于，其包含热轧工序、冷轧工序、一次再结晶退火工序、最终退火工序及平坦化退火工序，并进行喷丸处理和/或矫平加工处理及与溶液相接触的处理，上述溶液含有规定量的Cu等，pH为‑1.5以上且低于7，液温为15℃以上且100℃以下，钢板在上述溶液中浸渍的时间为5秒以上且200秒以下。

本发明涉及一种硅钢热处理方法，尤其涉及一种取向硅钢极薄带绝缘层涂覆方法，包括以下步骤：(1)接入普碳钢引带的准备工作；(2)各炉段张力的设定工作；(3)炉内气氛及温度的调节工作；(4)绝缘层厚度及厚度的检测工作；(5)极薄带涂层涂覆及烘干工作；(6)极薄带表面绝缘涂层及磁性能检测工作。本发明采用与极薄带厚度相当的普碳钢作为引带，通过引带测试产线张力和绝缘层涂覆的厚度，一方面可通过普碳钢薄带的运行加速炉内温度和气氛的稳定性，节约炉内稳定时间；另一方面可通过成本较低的普碳钢检测炉内张力和温度的设定，及绝缘涂层的涂覆效果，避免开始采用硅钢带出现断带，及涂覆不合格后造成产品报废带来的成本升高。

利用EBSD技术研究了电工钢中长轴平行于轧向的柱状晶样品在热轧和退火过程中组织和取向的演变规律,并与长轴平行于板法向的样品的已有研究结果进行对比。结果表明,无论柱状晶按何种方向排列,只要表面存在剪切力,热轧后都可形成剪切织构,同时中心形成轧制织构,主要包括旋转立方织构和{112}<1-10>。柱状晶造成的影响主要体现在板中心层,长轴平行于轧向排列的样品热轧时形成的粗大旋转立方晶粒要到脱碳退火后才能完全消除,但破坏了正常的不同取向晶粒间的取向差分布及尺寸均匀性,导致二次再结晶不完全及磁性能降低。 The evolution of microstructure and grain orientation in an electrical steel containing columnar grains with its long axis being parallel to the rolling direction of sheet was studied during hot rolling and annealing by EBSD technique.The results are compared with those of samples containing columnar grains being parallel to normal direction of sheet reported in the reference [3].It was shown that,whether the long axis of columnar grains was arranged in RD or ND,shear textures can be formed in t... 

采用取向分布函数分析了无取向电工钢不同再结晶退火温度下的织构变化及织构对磁感应强度和铁损的影响,并计算了无取向电工钢的磁晶各向异性能。结果表明,随着实验钢的再结晶退火温度升高,Goss织构和立方织构组分显著增强,而{111}面织构强度却减弱。较高的退火温度有利于减小织构因子,提高磁感应强度。磁晶各向异性能计算结果显示,随着再结晶退火温度升高,无取向电工钢板的磁晶各向异性能降低。 The recrystallization texture and the relationship of texture to magnetic induction intensity and core loss of a non-oriented electrical steel were investigated by orientation distribution function analysis. The magnetic anisotropy energy of the steel was calculated also. The results show that,the intensity of Goss texture and cubic texture increases,but the intensity of { 111} texture decreases with increasing recrystallization annealing temperatures of the steel. The higher annealing temperatu... 

采用低温板坯加热制备取向硅钢,通过透射电镜(TEM)观察并研究热轧板中的析出物,用ODF织构法研究热轧板距表面1/8、1/4和1/2处的织构分布。结果表明,热轧板中的析出物主要是密排六方AlN,AlN形貌呈规则长方形,AlN颗粒大小不等,分布密度低;热轧板中的织构沿板厚方向,由亚表层的{110}<001>织构向1/2中心层的α线织构变化,其中{110}<001>织构在热轧板距表面1/4层处最强。 The low temperature grain-oriented silicon steels were produced by acquired inhibitor method.The precipitates in hot rolling strip were observed and studied by transmission electron microscope,and the texture distribution in 1/8,1/4 and 1/2 layers of hot rolling strip were analyzed by ODF method.The results showed that the square shaped h-AlN is the main precipitates in hot rolling strip.The precipitates are varying in size and distribution.The texture of hot rolling strip in thick direction are... 

本实用新型公开了一种电工钢表面清洗装置，包括机架、第一传送链和叶片，所述机架的上端固定有顶板，且顶板的内部连接有加料杆，并且加料杆的上端内部设置有固定帽，所述顶板的侧面固定有第一电动机，且第一电动机的一端连接有丝杆，所述丝杆的外侧设置有电动推杆，所述第二转动轴的侧面连接有第二传送链，所述顶板的下端连接有连接架，且连接架的内部设置有第三电动机，所述连接架的底部设置有第二清洁杆，所述机架的内部开设有固定孔。该电工钢表面清洗装置，往加料杆的内部加入清洁液，清洁液会被加料干底部的海绵吸收，当料与加料杆的底部摩擦时，清洁液就会附着在料的表面，从而实现定量的往装置的内部加入清洁液。

借助OM、激光共聚焦显微镜、质谱仪和电解萃取等设备和方法，研究了添加微量稀土La（质量分数0.001 1%）的取向硅钢在轧制前采用不同加热保温时间对抑制剂固溶行为的影响。结果表明：当稀土取向硅钢在1 250℃分别保温10、20、30 min后，试验钢晶粒尺寸随保温时间延长有先快后慢的长大趋势；三种抑制剂元素Mn、Cu和Al均发生固溶，保温时间对Mn和Cu两种元素的固溶影响明显，固溶量分别由69.8%和43.7%增加至84.2%和85.2%；随着保温时间的延长，稀土取向硅钢中抑制剂的小尺寸未溶物逐渐减少直至消失，较大尺寸未溶物（300～600 nm）逐渐转变为小尺寸未溶物逐步溶入基体中，数量减少且未溶物的类型由复杂逐渐转变为单一。 In this paper the solid solution behavior of the inhibitor under various holding time in 0.001 1 %La oriented silicon steel during reheating had been investigated by using OM, LM, methods of electrolytic extraction and mass spectrometer. The results showed that grain size of the test steel increased significantly with the holding time prolonging when the rare earth oriented silicon steel was heated to1 250 ℃ and held for 10, 20 min and 30 min respectively, and the growth trend slowed down after ...