本发明属于硅钢制造技术领域，具体涉及一种改善硅钢热轧板边部质量的加工方法，包括：连铸、铸坯预变形处理、铸坯加热处理和热轧处理；其中，所述铸坯预变形处理包括：在所述铸坯的温度为500～900℃下，对所述铸坯的沿长度方向的两侧壁通过立辊施加压力，直至形变量h为10～50mm；所述铸坯加热处理的加热温度为1100～1200℃，保温时间为4～6h。本发明提供的改善硅钢热轧板边部质量的加工方法，采用铸坯两侧壁的侧压工艺，有效解决了热轧板边部裂纹的缺陷，提高了边部塑性，提高了成材率并降低了生产成本。

利用加热炉模拟、动态再结晶以及热模拟等试验方法以及扫描电镜、金相显微镜等分析观察手段对无取向硅钢边裂的成因进行了探讨。结果表明,长时间加热使得板坯边部晶粒异常长大,晶界氧化并脱碳,轧制过程中边部温度过低,动态再结晶过程变弱,使得板坯边部延伸性能变差,是导致硅钢边裂的主要原因。建议通过适当降低铸坯加热温度、缩短保温时间、提高终轧温度来改善硅钢边裂缺陷。 The behaviors of high temperature oxidation,dynamic recrystallization,and hot ductility,microstructure evolution were investigated on the non-oriented electrical steel sheets to discuss the formation of edge crack.The key causes of cracking was found to be the coarse as-cast microstructure,grain boundary oxidation and decarburization in reheating furnace,as well as reduced temperature at strip edge region during hot rolling process resulting in reduced hot ductility and lack of enough dynamic re... 

一种基于临界变形制备高强度无取向电工钢的方法，按以下步骤进行：(1)按电工钢成分真空精炼钢水，连铸制成连铸坯；(2)在900～1100℃热处理30～120min，然后热轧制成热轧板；(3)冷轧冷轧板；冷轧板厚度为目标厚度+(0.01～0.1)mm；(4)在400～700℃进行一次退火处理，在850～1200℃进行二次退火处理；(5)酸洗去除氧化层，然后进行温轧或二次冷轧进行临界变形。本发明的方法利用位错强化机制采用临界变形提高无取向电工钢的强度的原理，利用一次退火二次退火进行一次调控织构并临界变形对织构二次调控的方法增加对磁性能有利的再结晶织构来优化磁性能，该生产方式工艺简单，成本较低，生产效率高，适用于大批量生产。

本发明公开了一种适应高频率工况下低铁损无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯—热轧—正火—酸洗—冷轧—连续退火—涂绝缘涂层并固化；所述冷轧步骤中，采用六辊单机架往复式轧机经5道次一次冷轧至目标厚度，冷轧过程中前三道次采用变速异步轧制方法，使钢板表层在剪应力作用下位错密度增加，这样在退火后表层晶粒尺寸细化而心部晶粒粗大，通过本发明的方法可生产得到心部为粗大等轴晶粒，表层为纳米级细等轴晶粒的电工钢产品，该产品的铁损P1.5/50≤2.35W/kg，P1.0/400≤14.0W/kg。

本发明涉及一种硅钢热处理方法，尤其涉及一种取向硅钢极薄带绝缘层涂覆方法，包括以下步骤：(1)接入普碳钢引带的准备工作；(2)各炉段张力的设定工作；(3)炉内气氛及温度的调节工作；(4)绝缘层厚度及厚度的检测工作；(5)极薄带涂层涂覆及烘干工作；(6)极薄带表面绝缘涂层及磁性能检测工作。本发明采用与极薄带厚度相当的普碳钢作为引带，通过引带测试产线张力和绝缘层涂覆的厚度，一方面可通过普碳钢薄带的运行加速炉内温度和气氛的稳定性，节约炉内稳定时间；另一方面可通过成本较低的普碳钢检测炉内张力和温度的设定，及绝缘涂层的涂覆效果，避免开始采用硅钢带出现断带，及涂覆不合格后造成产品报废带来的成本升高。

研究了冷轧95%变形量无取向硅钢不同退火温度(710～1 050℃)下再结晶织构特征.再结晶刚完成时(710℃退火),呈现强γ({111<112>～<134>)与弱{114}<481>织构特征;随退火温度升高至900℃,γ明显减弱,{114}<481>组分持续增强,形成典型的{h,1,1}<1/h,1,2>织构;进一步升温至1 050℃,再结晶织构不再发生明显变化.基于EBSD分析,{114}<481>组分的持续强化可归因于其明显的尺寸优势以及较高频率的高能晶界(取向差角为20°～45°). A non-oriented silicon steel was heavily rolled to 95% reduction and subsequently annealed at 710~1 050 ℃ to investigate recrystallization texture evolution.When annealed at 710 ℃ with complete recrystallization,the texture is characterized by a strong partial γ fiber spreading from {111}<112> to {111}<134> and a weak {114}<481> component.As annealing at 900 ℃,γ fiber is decreased significantly while {114}<481> is increased consistently,producing a typical {h,1,1}<1/h,... 

本发明涉及取向硅钢技术领域，且公开了包括以下步骤：步骤一：冶炼，冶炼经转炉和RH精炼后得到钢水，在进行冶炼的过程中通入空气并设置总进气量100‑300Nl/min，且通入的空气中氧含量为20‑21％之间。该磁性优良的高磁感取向硅钢的气氛控制工艺，通过在不同的流程中，加入一定配比的氧气和氮气的含量，有效的提升每个阶段的气氛控制精度，从而得到最终的高磁感取向硅钢达到优良，避免了因气压、流量等因素影响最终高磁感取向硅钢磁力效果，炉渣中FeO含量减少，提高钢回收率和炉衬寿命，进而也起到降低生产成本的效果，且进行精确的气氛控制，使得在进行高磁感取向硅钢的冶炼中，使得冶炼的效果更好，使得冶炼出来的高磁感取向硅钢的磁性更加的优良。

试验了通过NaCl-KCl-NaF-SiO₂熔盐在电流密度50 mA/cm²、电沉积脉冲电流正反向比9:1和750⁸50℃60min电沉积下阴极（/mm）20×20×0.5的1.6Si无取向冷轧硅钢片断面层硅的分布,并通过计算得出Si的扩散系数。结果表明,电沉积温度由750℃提高至850℃时,试样中Si含量增加,扩散的深度由18μm提高到40μm;电沉积温度与Si在钢中的扩散系数近似符合Arrhenius指数关系。 The distribution of silicon at cross section of cathode（/mm） 20 × 20 × 0.5 sheet of 1.6Si non-oriented cold rolled silicon steel after electro-deposit treatment by NaCl-KCl-NaF-SiO₂ molten salt with current intensity 50 mA/cm²,electro-deposit pulse current positive-negative ratio 9:1 at 750 850 ℃ for 60 min has been tested and the diffusion coefficient of Si is obtained by calculation.Results show that with increasing electro-deposit temperature from 750 ℃ to 85... 

从取向硅钢生产路线的选择、工艺技术的改进和生产设备的改造三方面进行了生产取向硅钢的节能降耗技术改造.通过完善多元抑制剂配方生产低温取向硅钢,通过加抛丸的酸洗、带面超声波清洗、改进连续退火炉以及余热循环利用等技术改造,使2012年取向硅钢的产量与未进行技术改造前的2009年相比提高了2.5倍,产品磁性上升了一个半牌号,能耗下降了8.9%,成材率提高了6.4%,生产成本下降了22%,综合效益显著. Energy saving technological transformation was carried out in the production of grain oriented silicon steel from three aspects of the oriented silicon steel production process route selection,technology improvement and equipment renovation.Through the improvement of multiple inhibitor formulations for producing low-temperature grain-oriented silicon steel,and by adding the blasting pickling,the belt surface ultrasonic cleaning,improvement of continuous annealing furnace,waste heat recycling tec... 

利用EBSD技术研究了电工钢中长轴平行于轧向的柱状晶样品在热轧和退火过程中组织和取向的演变规律,并与长轴平行于板法向的样品的已有研究结果进行对比。结果表明,无论柱状晶按何种方向排列,只要表面存在剪切力,热轧后都可形成剪切织构,同时中心形成轧制织构,主要包括旋转立方织构和{112}<1-10>。柱状晶造成的影响主要体现在板中心层,长轴平行于轧向排列的样品热轧时形成的粗大旋转立方晶粒要到脱碳退火后才能完全消除,但破坏了正常的不同取向晶粒间的取向差分布及尺寸均匀性,导致二次再结晶不完全及磁性能降低。 The evolution of microstructure and grain orientation in an electrical steel containing columnar grains with its long axis being parallel to the rolling direction of sheet was studied during hot rolling and annealing by EBSD technique.The results are compared with those of samples containing columnar grains being parallel to normal direction of sheet reported in the reference [3].It was shown that,whether the long axis of columnar grains was arranged in RD or ND,shear textures can be formed in t... 

本发明公开了一种超高效变频空调压缩机用无取向硅钢薄带及其制造方法，属于无取向硅钢技术领域。本发明包括以下重量百分比的组分：C≤0.003％，Si：2.0％～2.5％，Mn：0.15％～0.5％，Als：0.3％～0.7％，Sn：0.05％～0.11％，S≤0.003％，P≤0.03％，B：0.002％～0.004％，Ca：0.003％～0.005％，N≤0.003％，Ti≤0.003％，其余为Fe及不可避免的杂质，且Mn/S比控制在20～60范围内，B/N比控制在0.7～1.5，Ca/S的比例≥1。为解决现有技术中存在的问题，本发明通过添加合金元素以及偏析元素，配合连铸、热轧、常化和连续退火等热处理工艺，以及优良的冷轧板形控制技术，实现0.30～0.35mm厚度薄规格的高效无取向硅钢产品，具备优异的磁性能和高屈强比的力学性能，满足高效变频空调压缩机电机磁性能和关节式定子高速冲裁对力学性能和板形的高标准要求。

取向硅钢因其高磁导率、低矫顽力和大电阻系数等特性，被广泛应用于大中型变压器和大型电动机铁芯的制造。因取向硅钢性能和成分控制严格，生产工艺复杂，故其产品代表了钢铁企业特殊钢生产的最高水平。本文介绍了新钢公司卷板厂1580热连轧线生产取向硅钢过程中出现的窄尺问题，研究了取向硅钢产品的特点，分析了热轧过程中的组织转变，并结合生产实际提出了改进措施。通过对加热炉钢坯加热模式、粗轧轧制策略、精轧轧制工艺、二级模型等方面的优化和改进，取向硅钢窄尺情况明显好转，提高了产品的成材率和市场口碑。 The oriented silicon steel is widely used in the iron core manufacture of large and mediumsized transformers and large motors because of its high permeability, low coercivity and large resistance coefficient. Due to the performance and composition control of oriented silicon steel is strict, the production process is complex,therefore, its products represent the highest level of special steel production in iron and steel enterprises. This paper introduces the problem of narrow gauge in the produ...