硅钢资料

通过热力学计算与模拟试验研究了含钒钛取向硅钢中氮化物析出相的析出规律与析出行为,并探讨了含钒钛元素的氮化物析出相作为薄板坯连铸连轧流程制备取向硅钢中辅助抑制剂的可行性.研究表明,在所冶炼的含钒钛取向硅钢的成分范围内,Ti N在钢液凝固末期便具备析出的热力学条件,而Al N与VN只可能在凝固后的α+γ或α+Fe3C两相区内析出.含钒钛取向硅钢中氮化物析出相以成分复杂的复合析出相为主,且随着钒钛加入量的增加,钢中抑制剂析出相总的分布密度由于含钒钛元素的氮化物析出相的增加而明显提高,使抑制剂抑制初次再结晶晶粒正常长大的能力得以加强,最终成品的磁感应强度值B8由1.857 T提升至1.898 T.同时,加入不高于0.007%的Ti与不高于0.005%的V不会影响中间脱碳退火工序的脱碳效果以及高温退火净化阶段硫、氮的脱除效果,其形成的含钒钛元素的纳米级氮化物析出相适合作为薄板坯连铸连轧流程制备取向硅钢的辅助抑制剂. The precipitation behavior of nitride precipitates in grain-oriented silicon steel containing vanadium and titanium elements produced by thin slab casting and rolling process was studied by thermodynamic calculation and simulation experiment. The feasibility of nitride precipitates containing V and Ti elements as auxiliary inhibitors was also investigated. It is found that Ti N is likely to precipitate at the final stage of solidification in the grain-oriented silicon steel,but VN and Al N can p... 

本发明涉及一种农用电机用无取向硅钢的生产方法，包括钢水化学成分设计、热轧工艺和冷轧工艺等步骤；钢水化学成分包括：C≤0.04％、Si0.35‑0.55％、Mn0.10‑0.30％、Als0.02‑0.06％、P≤0.030％、S≤0.0040％、O≤0.003％、N≤0.003％，余量为Fe及不可避免的夹杂物。本发明方法生产出的硅钢与家用电机目前使用的普通无取向电工钢50BW1300相比，磁感提高0.02T以上，而且采用普通C含量≤0.040％设计，不需要深脱碳，大幅降低炼钢工序成本，采用无Al无P，低Mn含量，降低合金成本，与普通50BW1300无取向电工钢产品相比，生产成本大幅降低。

本实用新型涉及一种硅钢片叠压精准定位设备，包括压台、压板和仿形燕尾键，所述压台上开有与仿形燕尾键下端相对的限位槽，所述压板设置与压台上方，所述压板上开有与仿形燕尾键上端相对的限位孔。本技术方案当硅钢片叠放压合之后，仿形燕尾键可以去除，并能够在硅钢片组成的铁芯上形成燕尾槽，用于后期燕尾键的组装，且能够保证燕尾槽内的结构规则，便于后期燕尾键组装。

本发明公开了一种改善高牌号无取向硅钢表面色差缺陷的方法，属于冷轧卷板表面质量改进技术领域。所述方法为：将连铸坯依次进行热轧、常化、酸洗、单机架轧制和连续退火工序，其中按重量百分数计，所述的连铸坯含有如下成分：C＜0.003%、Si1.6~2.0%、Mn0.35~0.65%、Al0.35~0.65%、P＜0.02%、S＜0.0025%、余量为Fe和其他不可避免的杂质元素，所有成分合计100%；其中热轧工序的卷取温度为620~640℃。本发明所述方法能够降低带钢表面氧化铁厚度并改变带钢表面氧化铁结构，改善高牌号无取向硅钢表面色差缺陷。

利用加热炉模拟、动态再结晶以及热模拟等试验方法以及扫描电镜、金相显微镜等分析观察手段对无取向硅钢边裂的成因进行了探讨。结果表明,长时间加热使得板坯边部晶粒异常长大,晶界氧化并脱碳,轧制过程中边部温度过低,动态再结晶过程变弱,使得板坯边部延伸性能变差,是导致硅钢边裂的主要原因。建议通过适当降低铸坯加热温度、缩短保温时间、提高终轧温度来改善硅钢边裂缺陷。 The behaviors of high temperature oxidation,dynamic recrystallization,and hot ductility,microstructure evolution were investigated on the non-oriented electrical steel sheets to discuss the formation of edge crack.The key causes of cracking was found to be the coarse as-cast microstructure,grain boundary oxidation and decarburization in reheating furnace,as well as reduced temperature at strip edge region during hot rolling process resulting in reduced hot ductility and lack of enough dynamic re... 

以市场上购买的取向硅钢成品板为原料，经不同压下率冷轧至0.23～0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量，利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征，分析了硅钢超薄带的塑性变形行为。结果发现，在平面压缩应力下，{112}<111>滑移系的取向因子较大。随冷轧压下率的增加，Goss织构的含量逐渐减少，{212}<141>织构组分的含量先增加后减少，{111}<112>织构组分的含量逐渐增加，织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶，其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。 The commercial finished oriented silicon steel plate as the raw material were rolled to 0.23-0.08 mm. With the X-ray diffractometer(XRD), the texture components and their volume fractions in the cold-rolled samples were detected. And the orientation factor distribution of the cross-section of the samples was measured by the electron backscattering technique(EBSD). The morphology and crystallographic characteristics of twins were observed, and the plastic deformation behaviors of the ultra-thin o... 

通过微观组织表征、高温拉伸和断口形貌分析,研究了钇(Y)元素对6.5%Si无取向硅钢组织、高温拉伸及断裂机制的影响。研究结果表明,添加Y元素可以在钢液中形成YS和YP的复合析出。YS和YP可以充当异质形核基底,提高形核率,细化凝固组织。热轧组织不均匀,由表层至芯部分别形成等轴晶、等轴晶/拉长晶和拉长晶的混合组织。退火后,热轧变形组织转变为等轴晶,含Y实验钢的退火组织得到明显细化。500℃时效处理后,含Y实验钢具备较低的有序度,300℃的拉伸断口呈现韧性断裂特征,断后伸长率达到20.2%。相反,无Y实验钢发生脆性断裂,断后伸长率仅为2.1%。研究结果证实,Y元素可以通过组织细化和降低有序度提高6.5%Si无取向硅钢的中温塑性。 The effects of yttrium(Y)on microstructure,elevated-temperature tensile properties and fracture mechanism of 6.5% Si non-oriented electrical steel were investigated by means of microstructure characterization,high-temperature tensile test and fracture analysis.The results showed that the doping of Y introduced composite Y-rich precipitates(YS/YP)in the melt.YS and YP precipitates were qualified for heterogeneous nucleation agents,which thus raised the nucleation rate and refined the solidificati... 

公开了一种取向硅钢酸洗圆盘剪的剪切方法，方法中，取向硅钢的钢带经酸洗槽酸洗、漂洗、烘干之后，清除表面的氧化铁皮后进入圆盘剪，根据所述钢带的宽度调整圆盘剪的机架之间的距离，根据钢带厚度h调节圆盘剪的上刀片和下刀片间隙△，以及上刀片和下刀片的边缘重叠量C，使得间隙△为h/0.9，重叠量C为1.05‑0.2*h，钢带通过上刀片和下刀片时，上刀片和下刀片施加剪切力于钢带上构成切断面，切断面占带钢厚度的1/5～1/3，随着咬合深度的增加，切断面的变形量也随之增加，直到切断面从钢带断裂形成撕断面。

本发明公开了一种无取向电工钢清洗工艺，包括以下步骤：1)在脱脂剂箱体中添加脱脂剂溶剂，通过喷射泵将脱脂剂分别从上下两路管道喷出，经过流量控制电磁阀进入喷射梁，通过喷嘴喷洒在带钢表面；2)带钢轧制后温度为100～150℃，速度为600～1000m/min，带钢表面高温确保脱脂剂与带钢表面残留油脂反应充分，且在高速下喷射的脱脂剂与带钢相向而行，使带钢表面反应后残留硅泥、铁粉被迅速带走；3)喷射后的脱脂剂流入收集槽中，通过泵重新打入脱脂剂箱体中，实现脱脂剂的循环利用。其利用轧制时产生的高温及高速对带钢表面残留乳化液斑迹、铁粉、硅泥进行清洗，清洗彻底高效。

通过制备磷酸二氢铝硅钢涂层,研究了氧化锌对无铬涂层耐盐雾性能、电化学性能和附着性的影响。结果表明,硅钢表面涂层含有4.0%的氧化锌时,涂层具有最高的耐腐蚀性能和电化学性能,而且其致密表面最为平整,没有裂纹出现。 The effects of ZnO on the salt spray resistance property, electrochemical performance and adhesiveness of silicon steel insulating coating were studied. The results show that the best corrosion resistance and electrochemical properties can be obtained when the coating contains 4.0% oxide zinc, and the dense surface is smooth without cracks. 

试验了通过NaCl-KCl-NaF-SiO₂熔盐在电流密度50 mA/cm²、电沉积脉冲电流正反向比9:1和750⁸50℃60min电沉积下阴极（/mm）20×20×0.5的1.6Si无取向冷轧硅钢片断面层硅的分布,并通过计算得出Si的扩散系数。结果表明,电沉积温度由750℃提高至850℃时,试样中Si含量增加,扩散的深度由18μm提高到40μm;电沉积温度与Si在钢中的扩散系数近似符合Arrhenius指数关系。 The distribution of silicon at cross section of cathode（/mm） 20 × 20 × 0.5 sheet of 1.6Si non-oriented cold rolled silicon steel after electro-deposit treatment by NaCl-KCl-NaF-SiO₂ molten salt with current intensity 50 mA/cm²,electro-deposit pulse current positive-negative ratio 9:1 at 750 850 ℃ for 60 min has been tested and the diffusion coefficient of Si is obtained by calculation.Results show that with increasing electro-deposit temperature from 750 ℃ to 85... 

从取向硅钢生产路线的选择、工艺技术的改进和生产设备的改造三方面进行了生产取向硅钢的节能降耗技术改造.通过完善多元抑制剂配方生产低温取向硅钢,通过加抛丸的酸洗、带面超声波清洗、改进连续退火炉以及余热循环利用等技术改造,使2012年取向硅钢的产量与未进行技术改造前的2009年相比提高了2.5倍,产品磁性上升了一个半牌号,能耗下降了8.9%,成材率提高了6.4%,生产成本下降了22%,综合效益显著. Energy saving technological transformation was carried out in the production of grain oriented silicon steel from three aspects of the oriented silicon steel production process route selection,technology improvement and equipment renovation.Through the improvement of multiple inhibitor formulations for producing low-temperature grain-oriented silicon steel,and by adding the blasting pickling,the belt surface ultrasonic cleaning,improvement of continuous annealing furnace,waste heat recycling tec...