针对某厂DMS森吉米尔轧机生产无取向硅钢表面麻面缺陷的问题,根据生产实际,对其形成原因从乳化液及工作辊两方面因素进行了分析。结果表明:乳化液对麻面缺陷的产生有一定影响,但不是主要因素,主要原因是由于二十辊森吉米尔轧机工作辊辊径较小,轧制相同长度带钢轧辊运转周期较大,容易产生疲劳失效而导致。为此,提出通过调整冷轧工序成品轧制道次的压下率以减小轧制力,从而减小工作辊的磨损疲劳;通过对轧制乳化液浓度、温度的合理控制,以改善润滑效果、提高轧制速度,而进一步缓解轧辊疲劳的改进措施,使该钢厂无取向硅钢麻面缺陷发生率由原来的18%降至0.8%,带钢表面质量明显改善。 For the problem of surface pockmarks of non-oriented silicon steel strip produced by a DMS Sendzimir mill, based on the production practice, the formation causes were analyzed from two aspects of emulsion and working roll. The results show that the emulsion has a certain effect on the formation of surface pockmarks defects, but it is not the main factor. The main reason is that the working roll diameter of the 20-high Sendzimir mill is small, and the running period of the roll rolling the same l... 
2022-01-28 108 5.8

介绍了CSP工艺生产无取向电工钢各工序的设备特点、采用的工艺控制手段和电工钢产品质量情况,结合生产实践证明了马钢CSP工艺开发的无取向电工钢产品丰富了薄板坯连铸连轧的品种结构,发挥了薄板坯连铸连轧生产无取向电工钢性能均一、稳定的特点。 The equipment characteristic,the process control method and the quality of non-orientated silicon steel by CSP process were introduced.Combined with the production situation,it is proved that production of non-orientated silicon steel developed on Masteel CSP line would enrich product structure of thin slab continuous casting and rolling,and it exerts stable performance of non-orientated silicon steel. 
2013-06-28 108 5.8

采用光学显微镜、X射线衍射仪等分析了宁波钢铁有限公司生产的取向硅钢不同工序下的组织及织构演变规律。结果表明:铸坯经过热轧后,沿着厚度方向组织不均匀;一次冷轧并经脱碳退火后,组织由条状纤维状变成等轴状的初次再结晶晶粒,初次再结晶平均晶粒尺寸为18.17μm,织构主要以α织构和γ织构为主;在二次冷轧后,晶粒再次被压缩,转变为纤维状,织构主要为γ织构;经过高温退火后,发生二次再结晶,晶粒异常长大,晶粒尺寸达到厘米级,织构成分为单一且锋锐的Goss织构。 The microstructure and texture evolution of oriented silicon steel produced by Ningbo Iron and Steel Co.,Ltd.were analyzed by optical microscope and X-ray diffraction.The results showed that the microstructure of the slab was inhomogenous along the thickness direction after hot rolling.After first cold rolling and decarburizing annealing,the microstructure changed from strip fibrous to equiaxed primary recrystallized grains,and the average grain size of the primary recrystallization microstructu... 
2022-01-28 108 5.8

本实用新型公开了一种取向电工钢的多项性能检测装置,涉及取向电工钢技术领域,为解决检测装置在对取向电工钢涂层性能检测时较为繁杂,增加了检测难度,检测的误差增加,且检测装置的性能检测较为单一,检测效果不佳的问题。所述底座的上方设置有安装架和吊梁架,所述安装架上设置有输料辊,输料辊设置有两个,两个所述输料辊之间设置有输送带,所述吊梁架的下方设置有弹性胶带,所述弹性胶带上方的两侧均设置有第三电动伸缩杆,且第三电动伸缩杆的两端分别与吊梁架和弹性胶带通过螺钉连接,所述弹性胶带的一侧设置有检测架,所述检测架上设置有激光灯、第一滤光片、接收器、第二滤光片和聚光片,所述激光灯和第一滤光片设置在弹性胶带的上方。
2021-11-24 108 6.8

研究了电工钢SXRC的显微结构和疲劳性能,并与DP钢进行了比较。结果表明,退火温度低温化能够有效的抑制电工钢的再结晶。该钢在固溶铌的作用下,能够在保证电机磁性的同时具有一定的强度。与DP钢相比,SXRC钢的抗疲劳性能更好。 The microstructures and fatigue properties of the electrical steel SXRC we re investigated, and the properties were also compared with the steel DP. The results show that the recrystallization of the electrical steel can be suppressed at lower annealing temperature. The steel presents favorable motor magnetic and also a compatible strength with the help of solid-solution Nb. Compared with the steel DP, the fatigue resistance of the steel SXRC is preferable. 
2014-09-28 108 5.8

6.5%(质量分数)Si高硅钢具有优异的软磁性能和广阔的应用前景,然而其室温脆性和低的热加工性极大地制约了它的发展。近年来,人们对高硅钢制备技术的研究已经取得了很大的进展,如何通过织构的优化提高高硅钢的磁性能越来越受到人们的关注,归纳和总结了不同工艺制备的高硅钢中的织构演变规律和特点,以及对应的典型磁性能。 6.5wt% Si high silicon steel has excellent soft magnetic properties and wide application prospect.However,the brittleness of room-temperature and poor workability of cold rolling limit its deve-lopment.Recently,the researches of the preparations of high silicon steel have been already made great breakthroughs,and then,more and more attentions are focused on how to optimizing the texture of high silicon steel so as to obtain the best magnetic properties.The evolution of textures of 6.5% Si high s... 
2014-11-28 108 5.8

分析了影响脱碳效果和结晶行为的各种要素及其相互制约关系,提出了Hi-B连续退火工艺曲线,总结得出快速加热及合理稳态气氛是实现工艺制度的关键。结合实际工程,介绍了在连续退火炉设计中快速加热和气氛设计的考虑方法,并指出随着Hi-B产品的发展,如何改进这些方法将是连退工程研发的方向之一。 The factors which affect decarbonization and crystallization and the mutual restriction between them were analyzed.A complete continuous annealing process for Hi-B was put forward.As a result,the rapid heating and the proper steady atmosphere were two important factors.According to an actual project,the consider methods for designing rapid heating and proper steady atmosphere were introduced,and it is pointed that with the development of Hi-B technique,how to improve these techniques would be on... 
2011-02-28 108 5.8

本发明公开了一种变压器用硅钢片冲切设备,包括输送机、双向冲压机构、缓冲抬升机构和磁吸式清洁器四部分,输送机的末端安装有支撑架,双向冲压机构安装于支撑架上且由驱动机构、导向板、冲压头、连接器和冲切刀片组成,驱动机构的底部垂直安装于导向板的中部,导向板的两端与支撑架相连接,冲压头分设有两组且对称滑动设置于导向板上,驱动机构的两端与两组冲压头相连接,连接器安装于冲压头的末端,两组连接器的下端与冲切刀片的上沿转动连接。本发明所设计的冲切设备采用全自动运作的方式,并且配合有缓冲式的冲压机构,可以减小冲切过程中的形变率,整个机体的运作通过PLC控制器进行控制运作,提高装置的智能化程度。
2021-11-29 108 6.8

研究了冷轧大压下量,950℃退火时间对一种新型含铜无取向电工钢晶粒度和织构的影响。结果表明,大压下量冷轧,随压下量的增加,退火晶粒向γ线聚集,形成强{111}<112>织构。提高冷轧压下率,退火织构{111}<100>,{110}<001>强度减弱,增加退火时间,退火织构{111}<110>,{100}<001>,{110}<001>强度变弱。采用87.5%冷轧压下率和950℃退火60 s,有利织构{100},{110}占有率最大。 The effect of annealing(950 ℃) time with high cold rolling reduction on grain size and texture of a new non-oriented electrical steel containing copper was investigated.The results show that for high cold rolling reduction,most annealed grains are oriented along γ-fibre with increasing cold rolling reduction ratio and strong texture {111}<112> is formed.With increasing the cold rolling reduction ratio,the intensity of annealed texture {111}<110>,{011}<100> decreases.With increa... 
2011-01-28 108 5.8

本实用新型公开了E字型硅钢片的级进模冲压装置,属于冲压模具设备领域,所述下模具包括与冲孔凸模、冲方孔凸模、切断凸模分别对应且相适配的冲孔凹模、冲方孔凹模、切断凹模,所述上模具上设有对条料板进行输送的导料板,所述冲孔凸模、冲孔凹模均设有两对并且并排设置,且每对冲孔凸模、冲孔凹模均设有两个,每个所述冲孔凸模、冲方孔凸模、切断凸模的顶端均用微米级间隙固定安装于上模具上,所述冲孔凹模、冲方孔凹模、切断凹模的底端均用微米级间隙固定安装在下模具上。本实用新型中各个凸、凹模分别采用硬质合金拼块、镶块式的结构并用微米级间隙固定安装在上、下模具上,这样不仅可节省材料的费用,同时还便于人们后期对模具的维修和使用。
2021-03-10 108 6.8

本发明公开了一种改善高牌号无取向硅钢表面色差缺陷的方法,属于冷轧卷板表面质量改进技术领域。所述方法为:将连铸坯依次进行热轧、常化、酸洗、单机架轧制和连续退火工序,其中按重量百分数计,所述的连铸坯含有如下成分:C<0.003%、Si1.6~2.0%、Mn0.35~0.65%、Al0.35~0.65%、P<0.02%、S<0.0025%、余量为Fe和其他不可避免的杂质元素,所有成分合计100%;其中热轧工序的卷取温度为620~640℃。本发明所述方法能够降低带钢表面氧化铁厚度并改变带钢表面氧化铁结构,改善高牌号无取向硅钢表面色差缺陷。
2021-03-25 107 6.8

本发明公开了一种冷轧取向硅钢EBSD用样品电解抛光制样方法,包括:S1.机械抛光,切取10mm*10mm规格试样用超声仪清洗,在不同粒度的砂纸上预磨后在金相试样抛光机上抛光至镜面;S2.电解抛光,利用struerslectropol‑5型电解抛光机对机械抛光好的试样进行电解抛光;S3.EBSD检测。本发明主要解决现有设备技术条件下如何得到高质量的EBSD检测技术样品的问题,适用于大批量冷轧取向硅钢的EBSD样品制备,发明本方法后实验过程简单快捷,节约了实验时间和成本。
2021-10-20 107 6.8