研究了退火温度对3.1%Si无取向硅钢组织和磁性能的影响规律。结果表明:退火温度从940℃提高至1 000℃,平均晶粒尺寸由98μm增加到145μm,铁损P_1.5/50从2.576 W/kg降低至2.408W/kg。随着退火温度的升高,γ不利织构组分强度逐渐降低,{111}〈112〉织构组分强度降低约16%,磁感B₅₀逐渐升高,磁性能水平提高。 The effects of annealing temperature on microstructure and texture and magnetic properties of 3.1%Si non-oriented silicon steel were investigated in this paper.The results showed that,when the annealing temperature increased from 940℃ to 1 000℃,the average grain size of metallographic structure increased from 98μm to 145μm,the iron loss value P_1.5/50 decreased from2.576 W/kg to 2.408 W/kg.And as the annealing temperature increased,the strength of the unfavorable texture componentγgrad... 

本发明公开了一种无取向电工钢清洗工艺，包括以下步骤：1)在脱脂剂箱体中添加脱脂剂溶剂，通过喷射泵将脱脂剂分别从上下两路管道喷出，经过流量控制电磁阀进入喷射梁，通过喷嘴喷洒在带钢表面；2)带钢轧制后温度为100～150℃，速度为600～1000m/min，带钢表面高温确保脱脂剂与带钢表面残留油脂反应充分，且在高速下喷射的脱脂剂与带钢相向而行，使带钢表面反应后残留硅泥、铁粉被迅速带走；3)喷射后的脱脂剂流入收集槽中，通过泵重新打入脱脂剂箱体中，实现脱脂剂的循环利用。其利用轧制时产生的高温及高速对带钢表面残留乳化液斑迹、铁粉、硅泥进行清洗，清洗彻底高效。

采用取向分布函数分析了无取向电工钢不同再结晶退火温度下的织构变化及织构对磁感应强度和铁损的影响,并计算了无取向电工钢的磁晶各向异性能。结果表明,随着实验钢的再结晶退火温度升高,Goss织构和立方织构组分显著增强,而{111}面织构强度却减弱。较高的退火温度有利于减小织构因子,提高磁感应强度。磁晶各向异性能计算结果显示,随着再结晶退火温度升高,无取向电工钢板的磁晶各向异性能降低。 The recrystallization texture and the relationship of texture to magnetic induction intensity and core loss of a non-oriented electrical steel were investigated by orientation distribution function analysis. The magnetic anisotropy energy of the steel was calculated also. The results show that,the intensity of Goss texture and cubic texture increases,but the intensity of { 111} texture decreases with increasing recrystallization annealing temperatures of the steel. The higher annealing temperatu... 

本发明涉及取向硅钢技术领域，且公开了包括以下步骤：步骤一：冶炼，冶炼经转炉和RH精炼后得到钢水，在进行冶炼的过程中通入空气并设置总进气量100‑300Nl/min，且通入的空气中氧含量为20‑21％之间。该磁性优良的高磁感取向硅钢的气氛控制工艺，通过在不同的流程中，加入一定配比的氧气和氮气的含量，有效的提升每个阶段的气氛控制精度，从而得到最终的高磁感取向硅钢达到优良，避免了因气压、流量等因素影响最终高磁感取向硅钢磁力效果，炉渣中FeO含量减少，提高钢回收率和炉衬寿命，进而也起到降低生产成本的效果，且进行精确的气氛控制，使得在进行高磁感取向硅钢的冶炼中，使得冶炼的效果更好，使得冶炼出来的高磁感取向硅钢的磁性更加的优良。

本实用新型公开了E字型硅钢片的级进模冲压装置，属于冲压模具设备领域，所述下模具包括与冲孔凸模、冲方孔凸模、切断凸模分别对应且相适配的冲孔凹模、冲方孔凹模、切断凹模，所述上模具上设有对条料板进行输送的导料板，所述冲孔凸模、冲孔凹模均设有两对并且并排设置，且每对冲孔凸模、冲孔凹模均设有两个，每个所述冲孔凸模、冲方孔凸模、切断凸模的顶端均用微米级间隙固定安装于上模具上，所述冲孔凹模、冲方孔凹模、切断凹模的底端均用微米级间隙固定安装在下模具上。本实用新型中各个凸、凹模分别采用硬质合金拼块、镶块式的结构并用微米级间隙固定安装在上、下模具上，这样不仅可节省材料的费用，同时还便于人们后期对模具的维修和使用。

试验了通过NaCl-KCl-NaF-SiO₂熔盐在电流密度50 mA/cm²、电沉积脉冲电流正反向比9:1和750⁸50℃60min电沉积下阴极（/mm）20×20×0.5的1.6Si无取向冷轧硅钢片断面层硅的分布,并通过计算得出Si的扩散系数。结果表明,电沉积温度由750℃提高至850℃时,试样中Si含量增加,扩散的深度由18μm提高到40μm;电沉积温度与Si在钢中的扩散系数近似符合Arrhenius指数关系。 The distribution of silicon at cross section of cathode（/mm） 20 × 20 × 0.5 sheet of 1.6Si non-oriented cold rolled silicon steel after electro-deposit treatment by NaCl-KCl-NaF-SiO₂ molten salt with current intensity 50 mA/cm²,electro-deposit pulse current positive-negative ratio 9:1 at 750 850 ℃ for 60 min has been tested and the diffusion coefficient of Si is obtained by calculation.Results show that with increasing electro-deposit temperature from 750 ℃ to 85... 

借助OM、激光共聚焦显微镜、质谱仪和电解萃取等设备和方法，研究了添加微量稀土La（质量分数0.001 1%）的取向硅钢在轧制前采用不同加热保温时间对抑制剂固溶行为的影响。结果表明：当稀土取向硅钢在1 250℃分别保温10、20、30 min后，试验钢晶粒尺寸随保温时间延长有先快后慢的长大趋势；三种抑制剂元素Mn、Cu和Al均发生固溶，保温时间对Mn和Cu两种元素的固溶影响明显，固溶量分别由69.8%和43.7%增加至84.2%和85.2%；随着保温时间的延长，稀土取向硅钢中抑制剂的小尺寸未溶物逐渐减少直至消失，较大尺寸未溶物（300～600 nm）逐渐转变为小尺寸未溶物逐步溶入基体中，数量减少且未溶物的类型由复杂逐渐转变为单一。 In this paper the solid solution behavior of the inhibitor under various holding time in 0.001 1 %La oriented silicon steel during reheating had been investigated by using OM, LM, methods of electrolytic extraction and mass spectrometer. The results showed that grain size of the test steel increased significantly with the holding time prolonging when the rare earth oriented silicon steel was heated to1 250 ℃ and held for 10, 20 min and 30 min respectively, and the growth trend slowed down after ... 

本发明公开了一种硅钢冷连轧轧制过程温度获取方法、装置及电子设备，通过获取硅钢冷连轧生产过程的工业参数数据以及各机架间硅钢的实际温度测试数据，然后基于工业参数数据以及预设初始模型，确定硅钢冷连轧生产过程的温度预测模型，接着基于硅钢轧制前的预热温度以及温度预测模型，得到硅钢冷连轧轧制过程各机架变形区出口与下一机架变形区入口之间的预测温度数据，再将预测温度数据与实际温度测试数据进行对比，并根据对比结果中的温度差异值对相应机架间的乳化液参数进行修正，直至温度差异值小于预设阈值，得到修正后的温度预测模型，能够用于实现硅钢冷连轧轧制过程中，任意采样点硅钢温度的获取。

本发明公开了一种带有紧固硅钢带的非晶合金铁心制造方法，包括以下步骤：步骤(1)：切割非晶带材片和紧固硅钢带；步骤(2)：对所述非晶带材片和紧固硅钢带进行套装与成型，每组非晶带材片两端搭接，紧固硅钢带设置于非晶带材片之间，得到成型铁心；步骤(3)：对所述成型铁心进行磁场热处理；步骤(4)：对所述成型铁心进行表面涂封。通过本发明提供的方法生产非晶合金铁心，操作方便、提升非晶合金铁心的结构稳定性，并且进一步降低铁心因磁致伸缩产生的噪声。

1.本外观设计产品的名称：硅钢片横剪线。;2.本外观设计产品的用途：对硅钢片料带的冲切、裁断。;3.本外观设计产品的设计要点：在于形状与图案的结合。;4.最能表明设计要点的图片或照片：立体图。;

分析了影响脱碳效果和结晶行为的各种要素及其相互制约关系,提出了Hi-B连续退火工艺曲线,总结得出快速加热及合理稳态气氛是实现工艺制度的关键。结合实际工程,介绍了在连续退火炉设计中快速加热和气氛设计的考虑方法,并指出随着Hi-B产品的发展,如何改进这些方法将是连退工程研发的方向之一。 The factors which affect decarbonization and crystallization and the mutual restriction between them were analyzed.A complete continuous annealing process for Hi-B was put forward.As a result,the rapid heating and the proper steady atmosphere were two important factors.According to an actual project,the consider methods for designing rapid heating and proper steady atmosphere were introduced,and it is pointed that with the development of Hi-B technique,how to improve these techniques would be on... 

通过制备磷酸二氢铝硅钢涂层,研究了氧化锌对无铬涂层耐盐雾性能、电化学性能和附着性的影响。结果表明,硅钢表面涂层含有4.0%的氧化锌时,涂层具有最高的耐腐蚀性能和电化学性能,而且其致密表面最为平整,没有裂纹出现。 The effects of ZnO on the salt spray resistance property, electrochemical performance and adhesiveness of silicon steel insulating coating were studied. The results show that the best corrosion resistance and electrochemical properties can be obtained when the coating contains 4.0% oxide zinc, and the dense surface is smooth without cracks.