硅钢资料

以市场上购买的取向硅钢成品板为原料，经不同压下率冷轧至0.23～0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量，利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征，分析了硅钢超薄带的塑性变形行为。结果发现，在平面压缩应力下，{112}<111>滑移系的取向因子较大。随冷轧压下率的增加，Goss织构的含量逐渐减少，{212}<141>织构组分的含量先增加后减少，{111}<112>织构组分的含量逐渐增加，织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶，其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。 The commercial finished oriented silicon steel plate as the raw material were rolled to 0.23-0.08 mm. With the X-ray diffractometer(XRD), the texture components and their volume fractions in the cold-rolled samples were detected. And the orientation factor distribution of the cross-section of the samples was measured by the electron backscattering technique(EBSD). The morphology and crystallographic characteristics of twins were observed, and the plastic deformation behaviors of the ultra-thin o... 

通过微观组织表征、高温拉伸和断口形貌分析,研究了钇(Y)元素对6.5%Si无取向硅钢组织、高温拉伸及断裂机制的影响。研究结果表明,添加Y元素可以在钢液中形成YS和YP的复合析出。YS和YP可以充当异质形核基底,提高形核率,细化凝固组织。热轧组织不均匀,由表层至芯部分别形成等轴晶、等轴晶/拉长晶和拉长晶的混合组织。退火后,热轧变形组织转变为等轴晶,含Y实验钢的退火组织得到明显细化。500℃时效处理后,含Y实验钢具备较低的有序度,300℃的拉伸断口呈现韧性断裂特征,断后伸长率达到20.2%。相反,无Y实验钢发生脆性断裂,断后伸长率仅为2.1%。研究结果证实,Y元素可以通过组织细化和降低有序度提高6.5%Si无取向硅钢的中温塑性。 The effects of yttrium(Y)on microstructure,elevated-temperature tensile properties and fracture mechanism of 6.5% Si non-oriented electrical steel were investigated by means of microstructure characterization,high-temperature tensile test and fracture analysis.The results showed that the doping of Y introduced composite Y-rich precipitates(YS/YP)in the melt.YS and YP precipitates were qualified for heterogeneous nucleation agents,which thus raised the nucleation rate and refined the solidificati... 

本发明公开了一种基于硅钢服役特性的立体卷铁心单框损耗测量方法及系统，根据硅钢片在立体卷铁心中的服役特性，获得测量铁心单框所需的非正弦励磁电压波形，通过所述立体卷铁心的心柱绕组电压和单框绕组电压之间的关系，确定所述被测立体卷铁心单框所需的电压有效值，再通过计算机、数据采集卡D/A转换器、功率放大器、隔离变压器和示波器，直接在所述立体卷铁心单框上加载励磁电压，利用功率表测量立体卷铁心单框损耗。本发明利用硅钢的服役特性，获得测量立体卷铁心单框所需的非正弦励磁电压波形和电压有效值，再将励磁电压直接加载到被测立体卷铁心单框，测量立体卷单框铁心损耗。

本发明提供一种含铜一般取向硅钢及其制备方法，制备方法包括：对钢板进行脱碳退火，得到脱碳钢，其中，将所述脱碳钢的氧含量控制在如下公式计算的范围内：ψO＝(0.0504×ωSi×H2±0.00005)×106，其中，ψO为脱碳钢的氧含量，单位为ppm；ωSi为钢板中Si的重量百分含量；H为钢板的厚度，单位为mm；将所述脱碳钢进行冷轧、涂布氧化镁涂层、卷曲和成卷退火，得到退火钢卷；对所述退火钢卷进行开卷，再涂敷张应力涂层和拉伸平整退火，制得含铜一般取向硅钢。本发明根据钢板中Si的实际含量及钢板厚度，调整脱碳钢的氧含量，以获得表面质量良好、磁性水平稳定的含铜一般取向硅钢产品。

阐述了国内外高磁感取向硅钢的生产研究水平与发展趋势,包括通过提高高斯晶粒取向度、细化磁畴、涂覆张力涂层、减薄钢片厚度进一步降低铁损以及低温加热技术和短流程技术新工艺。分析高磁感取向硅钢在我国大型电力变压器上的应用情况,结果表明,发展更薄规格高磁感、低铁损、低磁致伸缩取向硅钢可为大型变压器的安全性、节能性及环保性提供有效保障。 The research progress and development trend of high magnetic induction grain-oriented silicon steel at home and abroad are summarized,including the technology of improving the Goss alignment,refining domain wall,adding stress coating,decreasing thickness of sheet,and the new technique of reducing heating temperature of casting slab and shortening operational.Moreover,the application of high magnetic induction grain-oriented silicon in power transformer is presented.Developing grain-oriented sili... 

通过热力学计算与模拟试验研究了含钒钛取向硅钢中氮化物析出相的析出规律与析出行为,并探讨了含钒钛元素的氮化物析出相作为薄板坯连铸连轧流程制备取向硅钢中辅助抑制剂的可行性.研究表明,在所冶炼的含钒钛取向硅钢的成分范围内,Ti N在钢液凝固末期便具备析出的热力学条件,而Al N与VN只可能在凝固后的α+γ或α+Fe3C两相区内析出.含钒钛取向硅钢中氮化物析出相以成分复杂的复合析出相为主,且随着钒钛加入量的增加,钢中抑制剂析出相总的分布密度由于含钒钛元素的氮化物析出相的增加而明显提高,使抑制剂抑制初次再结晶晶粒正常长大的能力得以加强,最终成品的磁感应强度值B8由1.857 T提升至1.898 T.同时,加入不高于0.007%的Ti与不高于0.005%的V不会影响中间脱碳退火工序的脱碳效果以及高温退火净化阶段硫、氮的脱除效果,其形成的含钒钛元素的纳米级氮化物析出相适合作为薄板坯连铸连轧流程制备取向硅钢的辅助抑制剂. The precipitation behavior of nitride precipitates in grain-oriented silicon steel containing vanadium and titanium elements produced by thin slab casting and rolling process was studied by thermodynamic calculation and simulation experiment. The feasibility of nitride precipitates containing V and Ti elements as auxiliary inhibitors was also investigated. It is found that Ti N is likely to precipitate at the final stage of solidification in the grain-oriented silicon steel,but VN and Al N can p... 

本发明公开了一种超高效变频空调压缩机用无取向硅钢薄带及其制造方法，属于无取向硅钢技术领域。本发明包括以下重量百分比的组分：C≤0.003％，Si：2.0％～2.5％，Mn：0.15％～0.5％，Als：0.3％～0.7％，Sn：0.05％～0.11％，S≤0.003％，P≤0.03％，B：0.002％～0.004％，Ca：0.003％～0.005％，N≤0.003％，Ti≤0.003％，其余为Fe及不可避免的杂质，且Mn/S比控制在20～60范围内，B/N比控制在0.7～1.5，Ca/S的比例≥1。为解决现有技术中存在的问题，本发明通过添加合金元素以及偏析元素，配合连铸、热轧、常化和连续退火等热处理工艺，以及优良的冷轧板形控制技术，实现0.30～0.35mm厚度薄规格的高效无取向硅钢产品，具备优异的磁性能和高屈强比的力学性能，满足高效变频空调压缩机电机磁性能和关节式定子高速冲裁对力学性能和板形的高标准要求。

本发明涉及一种农用电机用无取向硅钢的生产方法，包括钢水化学成分设计、热轧工艺和冷轧工艺等步骤；钢水化学成分包括：C≤0.04％、Si0.35‑0.55％、Mn0.10‑0.30％、Als0.02‑0.06％、P≤0.030％、S≤0.0040％、O≤0.003％、N≤0.003％，余量为Fe及不可避免的夹杂物。本发明方法生产出的硅钢与家用电机目前使用的普通无取向电工钢50BW1300相比，磁感提高0.02T以上，而且采用普通C含量≤0.040％设计，不需要深脱碳，大幅降低炼钢工序成本，采用无Al无P，低Mn含量，降低合金成本，与普通50BW1300无取向电工钢产品相比，生产成本大幅降低。

本实用新型涉及一种硅钢片叠压精准定位设备，包括压台、压板和仿形燕尾键，所述压台上开有与仿形燕尾键下端相对的限位槽，所述压板设置与压台上方，所述压板上开有与仿形燕尾键上端相对的限位孔。本技术方案当硅钢片叠放压合之后，仿形燕尾键可以去除，并能够在硅钢片组成的铁芯上形成燕尾槽，用于后期燕尾键的组装，且能够保证燕尾槽内的结构规则，便于后期燕尾键组装。

利用加热炉模拟、动态再结晶以及热模拟等试验方法以及扫描电镜、金相显微镜等分析观察手段对无取向硅钢边裂的成因进行了探讨。结果表明,长时间加热使得板坯边部晶粒异常长大,晶界氧化并脱碳,轧制过程中边部温度过低,动态再结晶过程变弱,使得板坯边部延伸性能变差,是导致硅钢边裂的主要原因。建议通过适当降低铸坯加热温度、缩短保温时间、提高终轧温度来改善硅钢边裂缺陷。 The behaviors of high temperature oxidation,dynamic recrystallization,and hot ductility,microstructure evolution were investigated on the non-oriented electrical steel sheets to discuss the formation of edge crack.The key causes of cracking was found to be the coarse as-cast microstructure,grain boundary oxidation and decarburization in reheating furnace,as well as reduced temperature at strip edge region during hot rolling process resulting in reduced hot ductility and lack of enough dynamic re... 

本实用新型公开了一种硅钢片焊接模具，包括底座，底座上均匀排布有多条滑槽，每条滑槽内连接有一根垂直设置的定位杆，定位杆底部穿过底座连接一气缸，气缸连接在底座底部。本实用新型结构设计合理巧妙，移动不同位置的定位杆，将定位杆与硅钢片贴合，不同滑槽内的定位杆之间相互错位，并利用气缸将硅钢片定位，这种结构不可以适用于各种形状的硅钢片，使用方便快捷。

公开了一种取向硅钢酸洗圆盘剪的剪切方法，方法中，取向硅钢的钢带经酸洗槽酸洗、漂洗、烘干之后，清除表面的氧化铁皮后进入圆盘剪，根据所述钢带的宽度调整圆盘剪的机架之间的距离，根据钢带厚度h调节圆盘剪的上刀片和下刀片间隙△，以及上刀片和下刀片的边缘重叠量C，使得间隙△为h/0.9，重叠量C为1.05‑0.2*h，钢带通过上刀片和下刀片时，上刀片和下刀片施加剪切力于钢带上构成切断面，切断面占带钢厚度的1/5～1/3，随着咬合深度的增加，切断面的变形量也随之增加，直到切断面从钢带断裂形成撕断面。