常化快冷是生产高牌号无取向硅钢和高磁感取向硅钢不可缺少的一个工艺环节,气-雾冷却则是实现常化快冷的关键方式之一。介绍了国内自主设计建设的常化酸洗机组气雾冷却系统的技术特性,并对其特点进行了系统分析,最后给出该系统在设计、运行参数的选择上若干注意事项,对气-雾冷却系统设计和使用具有一定的指导作用。 The normalizing rapid cooling is a indispensable process to high grade non-oriented silicon steel and high magnetic induction oriented silicon steel’ s production. The fog cooling is a key ways of coming true the normalizing rapid cooling. This paper introduces the technical features of the fog cooling system in normalizing pickling line which is the domestic independent design and construction. Meanwhile,the fog cooling system’s characteristic is analyzed systematacially. In the end,this paper ... 

为了解决目前冷轧产线硅钢现有切边技术存在的微裂纹、应力、毛刺和边浪等问题,采用光纤激光器进行了高速切割实验,对激光功率、切割速度、激光模式等影响因素进行了分析,同时对高速切割时的切割前沿形状进行了研究。结果表明,切割最高速度随着功率的增加而增加;随着离焦量的增加,切割质量下降,挂渣增多,切缝宽度增加,切割深度变浅;基模激光器能量密度更高,所以薄板切割时的切割速度高于多模激光器;切割前沿随着切割速度的增加会变得平缓,速度足够大时,切割前沿甚至接近与切割方向平行,此时切缝下部存在挂渣现象。 In order to solve the problems such as micro crack,stress,burr,edge waves and so on,existing in cold rolling production line of silicon steel side cutting,experimentsof high speed laser cutting using fiber laser were carried out.Laser power,cutting speed,laser mode and other factors were analyzed,at the same time,cutting front geometries were studied.The results show that the maximum speed increases with power.And the increases of defocus result in poor quality,wider kerf and shallowerkerf.Energ... 

6.5%(质量分数)Si高硅钢具有优异的软磁性能和广阔的应用前景,然而其室温脆性和低的热加工性极大地制约了它的发展。近年来,人们对高硅钢制备技术的研究已经取得了很大的进展,如何通过织构的优化提高高硅钢的磁性能越来越受到人们的关注,归纳和总结了不同工艺制备的高硅钢中的织构演变规律和特点,以及对应的典型磁性能。 6.5wt% Si high silicon steel has excellent soft magnetic properties and wide application prospect.However,the brittleness of room-temperature and poor workability of cold rolling limit its deve-lopment.Recently,the researches of the preparations of high silicon steel have been already made great breakthroughs,and then,more and more attentions are focused on how to optimizing the texture of high silicon steel so as to obtain the best magnetic properties.The evolution of textures of 6.5% Si high s... 

综述了国内外大钢铁企业与研究机构采用获得抑制剂法生产低温高磁感取向硅钢的开发及应用情况,分析了以该法生产高磁感取向硅钢过程中抑制剂的控制技术,包括固有抑制剂组成方案、气态渗氮方式与工艺及高温退火工艺的制定.研究表明,固有抑制剂组成方案的设计思路大体一致,化合物抑制剂以AlN为主、硫化物为辅,同时添加少量Sn,Sb等单元素抑制剂,但组成元素含量存在一定差别;在脱碳退火后用NH3进行非平衡渗氮处理已成为气态渗氮的主要方式,但最佳方式仍未明确,具体选择需依据实际生产条件,相应脱碳及渗氮工艺的控制条件差别较大;高温退火工艺中升温制度差别不大,升温阶段退火气氛中N2含量的选择存在差别.此外,分析了抑制剂控制技术目前存在的关键问题,并指出了进一步的研究方向. The current application and exploitation on production of low-temperature high magnetic induction grain-oriented silicon steel with acquired inhibitor method at both iron and steel enterprises and research institutions in the world are reviewed. The control techniques of inhibitors, which include the composition design for inherent inhibitors, nitriding method and process, and secondary recrystallization annealing, are thoroughly analyzed and proposed. It is indicated that the design ideas for i... 

传统轧制法制备6.5wt.%高硅钢过程中温轧工艺具有显著不同于3 wt.%Si的电工钢的特点及组织织构特征,是开发新型基于织构优化的高硅钢的关键环节。采用EBSD技术对通过热轧、温轧、冷轧及退火工艺制备0.3mm厚的6.5wt.%Si电工钢板的组织和织构进行分析,重点研究温轧过程中的中间退火和大、小压下率组合以控制织构。结果表明,在热轧退火板是部分再结晶组织的情况下,一次性温轧或先小形变量、中间退火后再大形变量的工艺可得到更多的Goss晶粒;经过最终退火后Goss取向会发生偏转,形成部分黄铜取向,而{111}〈112〉取向的晶粒内形核生成近Goss取向的再结晶晶粒;大压下量轧制是最终组织中{111}取向晶粒较多的主要原因。 Warm rolling,a key process of developing new type high-Si electrical steel based on texture optimization,has significant different characteristics from 3wt% Si steel in conventional preparing process. 0. 3mm thickness 6. 5wt. % Si steel,obtained by a series of processes including hot and warm rolling,intermediate annealing and then cold rolling,was analyzed from microstructure and texture by EBSD,which are utilized mainly for investigating the intermediate annealing process and the combination o... 

研究了铝和铬元素在无取向电工钢晶粒长大过程中对织构及晶界变化的影响规律。试验结果表明:电工钢在晶粒长大过程中的主要织构组分均为{111}<112>。在晶粒生长期间,不加铝的1号试样中,{111}<112>、{111}<110>织构组分强化,而{100}<001>织构组分弱化;与1号试样相比,在加入0.2%的铝(质量分数,下同)的2号试样中,{111}<112>、{111}<110>织构组分强化(增加)的速率下降,{100}<001>织构组分变化不明显,甚至稍有增加。在含铝的试样中再加入0.3 5%的铬之后(3号试样),{111}<112>{、111}<110>和{100}<001>织构组分的变化规律与1号试样相似,但当电工钢中加入0.72%的铬之后(4号试样),上述3种织构组分的变化规律与2号试样相似。对于在晶粒生长期间持续变化的3种织构组分而言,1号试样的{1 1 1}<112>和{111}<110>织构组分的高(低)取向差角度晶界频率下降(... The effect rule of Aluminm and Chromium on texture and grain boundary transformation in the nonoriented electrical steel during grain growth was investigated.The experimental result shows that the main texture component is {111}<112> in the electrical steel.The {111}<112> and {111}<110> components in specimen 1 without Alumium were strengthened during grain growth whereas {100}<001> component was weakened.But the growth rate of {111}<112> and {111}<110> compon... 

对高磁感取向硅钢冷轧板分别进行800、950、1050和1120℃不脱碳的预退火处理,在800℃预退火,成品的磁性能较好。织构分析的结果表明,随着预退火温度升高,初次再结晶后有利织构组分{111}<112>与不利织构组分(118)[110]的比值f(111)/f(118)逐渐降低,初次再结晶织构的变化是成品磁性的影响因素之一。 Preliminary annealing process at different temperatures for cold-rolled strips of a high permeability grain-oriented silicon steel was investigated to study the effect of the annealing temperature on microstructure and magnetic performance of the steel.Results show that the magnetic performances of the products annealed at 800 ℃ are best.Analysis of primary recrystallization texture indicates that with rising temperature,f(111)/f(118) which is the ratio of the favorable component {111}<112>... 

利用DSC、XRD,结合热焓分析对硅钢级氧化镁和二氧化硅的固相反应行为进行了研究。比较了不同二氧化硅原料及混合方法对硅钢级氧化镁反应性的影响,找到了一种更为有效的硅钢级氧化镁反应性的评估方法,克服了传统柠檬酸活性法在比较不同厂家生产的氧化镁的反应性上的局限性。进一步研究了Na₂B₄O₇添加剂、TiO₂添加剂对氧化镁和二氧化硅反应行为的影响,结果表明,Na₂B₄O₇添加剂含量的增加对反应有利,而TiO₂添加剂对反应有阻碍作用。 The solid-state reaction behavior between silicon-steel grade MgO and SiO₂ was investigated by DSC and XRD combined with enthalpimetric analysis.The influence of different kinds of SiO₂ and different preparation methods were studied and a specifical measurement that is more reliable was proposed to evaluate reactivity of silicon steel grade MgO.It overcomes the limitation of the traditional citric acid activity（CAA） method,which can not be used to evaluate the reactivity of... 

【机构】 武汉钢铁学院轧钢七二级电工钢结业小组； ...

【作者】 李波； 杨晓江； ...

针对新能源汽车的发展，制备了含Ni固溶强化、含Cu析出强化以及含Ni+Cu复合强化3%Si无取向硅钢，研究了强化方式对无取向硅钢组织、织构和性能的影响。结果表明：固溶强化型无取向硅钢热轧板中形成了粗大{221}<221>晶粒，冷轧过程中剪切变形明显并在退火后形成良好再结晶织构。析出强化型无取向硅钢热轧板中心层形成γ取向粗大晶粒，在后续的加工中γ织构逐渐增强并最终得到相对细小的再结晶晶粒。复合强化型无取向硅钢热轧板中保留了强λ取向带状组织，退火后形成了有益的Goss织构和λ织构。固溶强化型与复合强化型无取向硅钢磁感应强度B₅₀分别达到1.742、1.688 T,高于析出强化型无取向硅钢的1.645 T。同时，复合强化型无取向硅钢高频铁损最低，其P_1.0/400和P_{1.0/1 000}分别低至20.97、82.69 W/kg,这与其较小的晶粒尺寸和织构改善有关。强度计算结果表明：Ni元素固溶强化对强度的提高有限，屈服强度为468 MPa,纳米Cu析出可显著提高屈服强度（强度增量约200 MPa）,且主要来自于模量强... For the development of new energy vehicles, 3%Si non-oriented silicon steel were processed by solid solution strengthening with Ni, precipitation strengthening with Cu, and composite strengthening with Ni and Cu. The effects of different strengthening methods on the microstructure, texture and properties of high-strength non oriented silicon steel were studied.The results show that coarse {221}<221> grains are formed in the hot rolled sheet of solution strengthened non-oriented silicon ste... 

取向硅钢常化工序主要采用现场实测带钢温度的方式测定冷却速率，并通过稳定冷却水温、调整冷却水量及喷梁运行数量等方式保证合理的冷却速率，给常化工艺设计和生产带来诸多不便。通过对常化工艺水冷过程带钢的传热分析求解，在建立带钢水冷温度模型的基础上，研究了不同冷却工艺参数对带钢温度及冷却速率的影响规律以及冷却工艺的交互作用结果。结果表明：模型计算结果能够较好地反映取向硅钢在常化水冷过程中的温度及冷却速率的变化，其计算误差为0.80%～4.11%;在特定取向硅钢厚度规格和常化工艺下，随着常化冷却水量及有效冷却长度的增加，带钢水冷温度及冷却速率与呈非线性变化；常化水冷工艺主要通过调控带钢与冷却水之间热交换量和交换时间实现对带钢温度的控制，实际生产中需综合考虑机组速度、冷却水量及有效冷却长度之间的交互作用，选定喷梁投入数量和冷却水量以获得稳定的冷却速率。 The cooling rate of normalization process mainly determined by measuring the grain oriented silicon steel strip temperature on site, and ensures the cooling rate by stabilizing the cooling water temperature, adjusting the cooling water volume and the operation quantity of spray beam, which brings inconvenience to the normalization process design and production. Based on the heat transfer of strip in the water cooling section of normalization process, the water cooling temperature model for the n...