硅钢资料

以市场上购买的取向硅钢成品板为原料，经不同压下率冷轧至0.23～0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量，利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征，分析了硅钢超薄带的塑性变形行为。结果发现，在平面压缩应力下，{112}<111>滑移系的取向因子较大。随冷轧压下率的增加，Goss织构的含量逐渐减少，{212}<141>织构组分的含量先增加后减少，{111}<112>织构组分的含量逐渐增加，织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶，其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。 The commercial finished oriented silicon steel plate as the raw material were rolled to 0.23-0.08 mm. With the X-ray diffractometer(XRD), the texture components and their volume fractions in the cold-rolled samples were detected. And the orientation factor distribution of the cross-section of the samples was measured by the electron backscattering technique(EBSD). The morphology and crystallographic characteristics of twins were observed, and the plastic deformation behaviors of the ultra-thin o... 

针对攀钢高硫铁水冶炼现状,结合不同生产工艺路线,论述了攀钢近年来为实现低硫电工钢的生产,在铁水预处理、转炉冶炼、钢水精炼过程中硫控制技术的开发与应用,形成了低硫洁净钢生产工艺技术,实现了低硫电工钢的生产。低硫电工钢RH脱硫率可达到20%左右,成品[S]控制在0.006%左右。 According to the smelting situations of hot metal with high sulphur content at Panzhihua Steel,combined with different produce processes,technologies for controlling the sulfur content during hot metal pretreatment,converter smelting,and second refining are developed. Technologies in low-sulfur clean steelmaking are formed. Low-sulfur electric steel are produced. As for the desulfurization rate of lowsulfur electric steel can reach about 20%,and the content of [S] in products is controlled to ab... 

含铜抑制剂作为取向硅钢的主抑制剂或辅助抑制剂不仅可以抑制初次晶粒的长大,促进二次再结晶,还可以降低铸坯的加热温度。取向硅钢中主要抑制剂为10～50 nm Cu₂S,在钢的铸坯、热轧、冷轧、脱碳等工艺过程均可析出;（Cu,Mn）_1.8S、Cu_1.8S、ε-Cu等主要作为辅助抑制剂,尺寸一般为30～50 nm（或大于50 nm）,主要在热轧阶段析出。总结了国内外有关取向硅钢中含铜抑制剂析出行为的研究进展,当前主要研究不同生产流程和工序中含铜抑制剂的析出行为和作用机理。 As main inhibitor or auxiliary inhibitor for grain-oriented silicon steel,the particles of inhibitor bearing copper not only inhibit the primary crystal growing and promote the secondary recrystallization,but also decrease the heat temperature of casting slab.The main inhibitor for grain-oriented silicon steel is 10～50 nm Cu₂S,which precipitate in process and procedure including steel casting slab,hot rolling,cold rolling and decarburizing process,while the 30～50 nm or more than 50 nm... 

【作者】 姚昌国； ...

以青海盐湖水氯镁石为初级原料,采用喷雾热解法制备原料氧化镁,原料氧化镁通过水化制备硅钢级氧化镁前驱体氢氧化镁。原料氧化镁水化实验中对水化剂、水化温度、水化时间、液固比、搅拌速度及陈化时间对水化率、过滤速度和纯度的影响进行系统研究。采用均匀实验设计和DPS数据处理,(依次)通过建模分析、二次多项式模型回归建立数学模型,再通过各因素方差分析和总方差分析,确定了理论最优实验条件,再用理论最优条件作重复实验进行验证,最终确定了原料氧化镁的最佳水化条件。在水化温度60℃,水化时间105 min,液固比4,陈化时间4 h,水化剂1含量4.0%,水化剂2含量3.15%,洗水量4倍,搅拌速度120 r/min时,原料氧化镁的水化率达99.50%以上,得到的硅钢级氧化镁前驱体氢氧化镁纯度高、过滤性能良好。 By spray pyrolysis method,bischofite in Qinghai salt Lake,as primary raw material,was used to prepare precursor raw material MgO for silicon-steel MgO.The precursor raw material MgO was used for preparing Mg(OH)2 which was the precursor of silicon-steel MgO,by hydration method.In the hydration experiment of precursor raw material MgO,some experiment parameters were investigated systematically.such as the hydrated agent,the temperature and time of hydration,liquid/solid ratio that affected the hy... 

分析了太原钢铁(集团)有限公司第二炼钢厂80 t RH生产冷轧硅钢脱碳、脱硫原理及影响因素,认为通过合理控制RH到站钢水碳和氧含量、加大插入管内径、采用快速抽真空度等可提高脱碳效果。降低顶渣中FeO和MnO含量,保证脱硫剂加入后的循环时间可以提高RH脱硫率。 The present article analyzes the principle of decarburization and desulfurization in refining the cold rolled silicon steel in the 80 t RH in No.2 Steelmaking Plant of Taiyuan Iron & Steel(Group) Corp.,and its influencing factors.It’s determined that the decarburization effect can be achieved by properly controlling the cabon and oxygen contents in the hot metal coming into the RH station,enlarging the inner diameter of snorkel and adopting the fast evacuation method.In the meanwhile the des... 

针对薄板坯连铸连轧流程结合\"获得抑制剂法\"所制备的低温高磁感取向硅钢,通过热力学计算研究了AlN与MnS在连铸与均热过程中的析出规律与行为。计算结果表明,连铸过程中AlN在凝固后的高温α相中便可能析出,而MnS仅可能在凝固后的α+γ两相区内析出。钢中AlN与MnS在均热过程中均处于部分固溶与部分析出的状态。后续高温渗氮处理后初次晶粒的异常长大并不明显,表明渗氮处理前钢中固有抑制剂的数量相对充足。 The precipitation behavior of MnS and AlN in low-temperature high magnetic induction grain-oriented silicon steel produced by thin slab casting and rolling process with\"acquired inhibitor method\"during continuous casting and soaking was studied by thermodynamic calculation.The calculated results show that AlN is likely to precipitate in ferrite after solidification.However,MnS can precipitate only in the two phase region of ferrite and austenite.Meanwhile,MnS and AlN in the steel can not be comp... 

研究表明,硅钢中的夹杂物对成品带钢的磁性能有显著影响。为研究冶炼过程硅钢中的夹杂物遗传变化,进而提出更有效的控制措施加以去除,本文结合典型的无取向硅钢生产炉次,采用非水溶液电解提取+扫描电镜观察方法分析冶炼过程中上述炉次典型试样的夹杂物。结果表明:转炉冶炼结束、RH精炼开始时,钢的氧化物夹杂总量最大,约为0.23%;RH精炼过程中,氧化物夹杂总量不断降低,并在脱碳结束时达到最低,约为0.02%;连铸过程中,氧化物夹杂总量仍有不断降低趋势,但夹杂物的平均尺寸变化不大。本试验条件下,中间包试样的夹杂物数量约为1.59×104个/mm3。 As we all know, the non-metallic inclusion effects magnetic properties of silicon steel sheets obviously. The article aims to study the heredity of non-metallic inclusion in non-oriented silicon steels during the steel making process, and then provides a more effective controlling measure to remove the inclusions. Based on the typical non-oriented silicon steel charges, the non-aqueous solution extraction and SEM observation were adopted to analyze the non-metallic inclusions. Results show that,... 

采用双辊薄带连铸技术试制了3.98%Si-0.71%Al无取向硅钢铸带,研究了二次冷轧法对硅钢组织和磁性能的影响。结果表明:硅钢铸带显微组织为等轴晶组织,铸带再结晶较完全,常化对铸带显微组织影响较小。二次冷轧工艺和一次冷轧工艺下,最终退火后成品显微组织为等轴晶组织,二次冷轧法最终退火后的晶粒尺寸小于一次冷轧法。二次冷轧法能够提高成品磁性能. Effect of double cold rolling on magnetic properties and microstructure of 3.98%Si-0.71%Al non-oriented silicon Steel Sheets cast by twin-roll thin strip casting process were investigated.The results show that the structure of the thin strip is equiaxed crystal,the recrystallization is complete and normalizing has lesser effect on microstructure.Using both cold rolled and double cold rolled process,the microstructure is equiaxed grain after final annealing.The average grain size of annealed shee... 

【作者】 张正贵； 李战库； ...

【作者】 陶永根； ...

采用扫描电镜、原子力显微镜研究了铬酸镁半无机绝缘涂层的微观结构。结果表明,涂层厚度为数微米,涂层中的有机树脂乳液颗粒均匀分布在无机涂层的表面,从而保证了涂层具有良好的冲片性能。采用极化曲线研究了涂层的耐蚀性能,发现铬酸镁与铬酸锌绝缘涂层的耐蚀性能相当。 In this paper,the microstructure and anti-corrosion property of magnesium chromate coating on non-oriented silicon steel were studied.The microstructure was observed by SEM and AFM.The anti-corrosion properties were evaluated by polarization curves.The results show that the thickness of coating is several microns and the polymer particles were scattered on the surface of inorganic coating,which is the guarantee for lamination property.The corrosion resistance of the magnesium chromate film was e...