为进行磷酸盐系无铬无取向硅钢涂层烧结固化工艺研究,首先对磷酸盐系无铬无取向硅钢涂层进行热重-差示扫描量热(TG-DSC)分析;然后在不同烧结固化温度条件下,测定涂层板温随时间变化曲线;最终获得涂层烧结固化温度与时间(T-t)工艺曲线。通过中性盐雾试验、动电位极化、交流阻抗、涂层附着力以及扫描电子显微镜(SEM)和能谱(EDS)分析验证。结果表明,根据涂层烧结固化温度与时间(T-t)工艺曲线制备的涂层结构致密、性能优异,证明该工艺曲线具有合理性与正确性。 In order to study the curing process of chromium-free non-oriented silicon steel coatings,phosphatic chromium-free non-oriented silicon steel insulating coating was prepared and TG-DSC analysis of the coating was conducted,then the change of the actual temperature of the coated non-oriented silicon steel sheet with time at different curing temperatures was studied. Based on the experiments,the processing curves of curing temperature vs. curing time( T-t) for the chromium-free non-oriented silico... 

对冷轧无取向硅钢在冶炼过程中各个工序的顶渣进行了检测,分析了顶渣变化原因,并得出结论:硅钢生产宜采用复吹转炉,以降低吹炼终点渣中TFe含量,进而减轻对精炼的压力;使用低S、低Al2O3含量中间包覆盖剂;RH脱氧及合金化顺序采用先加硅铁后加铝;首罐宜经LF提温并降低渣中TFe。 The top-surface slag used for the various production processes in smelting coldrolled non-oriented electrical steel is tested and based on tested results the cause of the top surface slag change is analyzed.So it is concluded that the combined blown converter is more suitable to be used for smelting electrical steel in order to reduce the content of TFe in slag at blow end point and then much better results can be achieved during the period of refining.Secondly the tundish flux contenting low co... 

利用OM、EBSD等手段研究了热轧板两段式正火时在700℃保温不同时间(0、10、30、60 min)对含Sb冷轧无取向电工钢磁性能的影响。结果表明,700℃保温10 min处理的样品铁损最小,磁感最高。对成品板的组织分析结果表明,试样的晶粒尺寸随700℃保温时间的延长先增大后减小,保温10 min时晶粒尺寸达到最大;分析成品试样织构发现,有利织构组分随700℃保温时间的延长先增加后减少,保温10 min时有利织构组分所占百分比最高。因此,含Sb冷轧无取向电工钢两段式正火时在700℃保温10 min时磁性能最好。 Effect of two-stage normalization on magnetic property of non-oriented electrical steel containing antimony was investigated by using optical microscope(OM) and electron back-scattered diffraction technology(EBSD).The experimental results show that the iron loss and magnetic permeability of the specimen insulated at 700 ℃ for 10 min are lowest and highest respectively.The grain size of the finish specimens increases first and then decreases with the increase of holding time.Similarly,the advanta... 

Fe-6.5%Si高硅钢是一种具有高磁导率、低矫顽力和低铁损等优异软磁性能的合金,但是其室温脆性和低的热加工性能严重影响了其在工业领域的应用。综述了Fe-6.5%Si高硅钢的性能,评述了合金的改性法、特殊轧制法、快速凝固法、沉积扩散法、粉末冶金法等制备工艺。 It is well known that 6.5%Si high silicon steel is one kind of soft magnetic materials with higher re-lative permeability,lower coercive force and iron loss than those of conventional industrial silicon steel.However,their room-temperature embrittleness and poor workability limit their practical applications in the industry.The pre-paration technique such as modification treatment on alloy,special rolling,rapid solidification,CVD and powder me-tallurgy is reviewed. 

基于TEAM(Testing Electromagnetic Analysis Methods)Problem 21基准模型和不同类型的磁化曲线Bm-Hm及Bm-Hb数据,分别在50 Hz至200 Hz的频率范围内计算了基准模型的硅钢叠片内的损耗及磁通,并考虑集肤效应和材料的电-磁各向异性的影响。数值计算结果与实验测量结果具有很好的一致性。提出的有限元建模方法和基于模拟结果的分析、结论有助于提高大型电力变压器的电磁设计的有效性。 Based on TEAM(Testing Electromagnetic Analysis Methods) Problem 21 standard model and the different B-H(such as Bm-Hm and Bm-Hb) curves,the iron loss and magnetic flux inside the grain-oriented(GO) silicon steel lamination are modeled under different frequency(from 50 Hz to 200 Hz) in this paper,And the influences of skin effect and electric-magnetic anisotropy on the numerical simulation results have been examined.The calculated and measured results with respect to the model are in good agreeme... 

【作者】 康凌晨； 王丽娜； ...

介绍了硅钢氧化镁制备方法及高质量硅钢氧化镁制备技术的研究进展,并对利用我国丰富的卤水资源制备硅钢氧化镁进行了展望。 The preparation methods of silicon steel magnesium oxide and research progress of high quality silicon steel magnesium oxide preparation technology were introduced.The use of abundant brine resources in the preparation of silicon steel magnesium oxide was prospected. 

采用XRD、SEM和激光粒度仪等手段,观察并研究了不同特性氧化镁在硅钢表面形成硅酸镁底层形貌特点,并结合热力学和差热-失重分析了MgO-SiO2的反应机理。研究结果表明:粒度小,活性值高的特种氧化镁在高温退火过程中与基体表面氧化物生成的硅酸镁底层,界面中硅酸镁底层嵌入基体较多,表面致密,颗粒细小,有利于形成附着性能优良的硅酸镁底层。 Surface microstructure of Mg2SiO4 coatings formed on the surface of oriented silicon steel coated with different kinds of MgO was investigated by XRD and SEM.The reaction mechanism between MgO and SiO2 was analyzed by TG-DSC and thermodynamic calculation.Results revealed that when the MgO with finer microstructure size and higher activity is employed,a dense Mg2SiO4 layer with finer microstructure and good binding to the steel substrate can be obtained.The results are very helpful for the prepar... 

研究了冷轧大压下量,950℃退火时间对一种新型含铜无取向电工钢晶粒度和织构的影响。结果表明,大压下量冷轧,随压下量的增加,退火晶粒向γ线聚集,形成强{111}<112>织构。提高冷轧压下率,退火织构{111}<100>,{110}<001>强度减弱,增加退火时间,退火织构{111}<110>,{100}<001>,{110}<001>强度变弱。采用87.5%冷轧压下率和950℃退火60 s,有利织构{100},{110}占有率最大。 The effect of annealing(950 ℃) time with high cold rolling reduction on grain size and texture of a new non-oriented electrical steel containing copper was investigated.The results show that for high cold rolling reduction,most annealed grains are oriented along γ-fibre with increasing cold rolling reduction ratio and strong texture {111}<112> is formed.With increasing the cold rolling reduction ratio,the intensity of annealed texture {111}<110>,{011}<100> decreases.With increa... 

无取向硅钢的磁性能主要取决于铁素体的晶粒尺寸、晶体织构和钢中的夹杂物。通过合适的化学成分设计以及采用适宜的夹杂物控制技术,可以获得最佳的夹杂物控制效果,使其纯净度大幅度提高或者无害,最终获得磁性能优良的高级别无取向硅钢。同时,为满足节能、环保、高效需求,无取向硅钢正朝着节能降耗、环境友好以及多功能、高效率、易加工等方向发展。 The magnetic properties of non-oriented silicon steel mainly depend on the grain size of ferrite,the crystallographic texture,and the inclusions in the steel.The optimum inclusion control effects can be obtained through a suitable chemical composition design and an appropriate inclusion control technique,and then the liquid steel will get be clean or the inclusion will get be harmless,finally the excellent magnetic property of the non-oriented silicon steel can be obtained.Meanwhile,in order to ... 

通过固溶度积公式计算及热模拟实验,对不同热装和加热温度条件下的无取向硅钢铸坯中析出相进行了研究.在低于950℃热装时,铸坯中AlN的析出量和尺寸不再变化,但MnS和AlN-MnS的数量及平均尺寸随着热装温度降低而进一步增加,并在温度低于600℃时达到最大值后保持不变.与1200℃相比,1100℃加热的铸坯中AlN、MnS的总固溶量相对更少.相比850℃热装,600℃热装再加热到1100℃的铸坯中AlN和MnS的总固溶量更少,且AlN和MnS尺寸更大.合适的热装温度和加热温度分别为600℃和1100℃. Based on solubility product calculation and thermal simulation experiments,precipitated phases in continuous casting slabs of non-oriented silicon steel were systematically studied at different hot charging and heating temperatures.When the hot charging temperature is below 950 ℃,the content and size of AlN remain unchanged,but the quantity and size of MnS and AlN-MnS increase when the hot charging temperature decreases,reach maximum and remain unchanged when the hot charging temperature is belo... 

分析总结退火工艺各参数对冷轧无取向硅钢磁性能的影响,结合设计和生产实践经验介绍退火工艺中各参数的实际生产取值,并针对现生产工艺过程中出现的典型问题提出解决办法。 It is analyzed and summarized the great influences on magnetism of cold rolled non-oriented silicon steel affected by various annealing process data in this article.The relevant settled ways is raised.According to the actual value presetting ways for various annealing process data based on design and production,as well as typical problems occurred during production.