【作者】 康凌晨； 王丽娜； ...

采用RH精炼添加钙合金方式对硅钢进行钙处理。结果表明,钙合金添加量为0.67、1.00、1.67kg/t钢时,钢中钙含量分别为0、2×10-6、4×10-6;随着钙合金添加量增大,钢中夹杂物粒度逐渐由0～2μm向2～4、4～6μm偏移;不同钙处理条件下,钢中均存在粒径小于1μm和粒径为1～5μm的MnS、CuxS夹杂物,后者或单独存在,或同AlN、CaS夹杂复合;粒径为5～10μm区间,钢中的夹杂物基本以钙的氧、硫化物为主。与钙处理前相比,钙合金添加量为0.67、1.00、1.67kg/t钢时,粒径小于1.0μm的微细夹杂物减少幅度分别为68.06%、87.50%、94.94%。钙合金添加量为1.67kg/t钢时,可以去除钢中绝大部分的微细夹杂物。 Ca alloy was added into the liquid steel during RH refining,and the results show that Ca concentration in final Si steel sheets is insignificant,about 0,2×10-6 and 4×10-6 when the added amount of Ca is 0.67,1.00 and 1.67 kg/t steel,respectively.With the increase in the added Ca alloy amount,the inclusions in the steel gradually change from those of 0～2 μm to those of 2～4 and 4～6 μm.Under different Ca treatments,there exist MnS and CuxS inclusions whose size is below 1 μm as well as MnS and CuxS ... 

利用OM、TEM与EDS技术,对Fe-3.2%Si低温取向硅钢热轧板进行不同常化冷却工艺处理后的显微组织、析出相及最终产品的磁性能进行分析,并与热轧板的组织和析出相进行对比。结果表明,常化板较热轧板的表层组织均匀,基体中再结晶比例增加,带状组织变窄;常化板中析出物的数量明显比热轧板的多,析出物主要有AlN、MnS及复合析出的(Cu,Mn)S等。在常化温度1120℃、保温3 min的条件下,采用二段式冷却较空冷、淬沸水、淬常温水的冷却工艺,常化板表层显微组织更均匀,沿板厚方向的显微组织的不均匀性显著,取向硅钢的磁性能最高;常化后采用二段式冷却工艺析出的细小析出物数量最多,且弥散分布在基体中,抑制剂的抑制效果最好,对成品获得高磁性最有利。 Microstructure, precipitate and magnetic characteristic of final products with different normalizing cooling processes for Fe-3.2%Si low-temperature hot-rolled grain-oriented silicon steel were analyzed and compared with the hot-rolled plate by optical microscopy(OM), transmission electron microscopy(TEM), and energy dispersive spectrometry(EDS). The results show that, the surface microstructure is uniform, the proportion of recrystallization in matrix increases, and the banding textures are nar... 

【作者】 卢鹏； ...

【摘要】 <正>日前,宝钢自主研发的新型高磁感取向...

【作者】 王桦； 舒子龙； ...

硅钢工业退火炉温度控制具有强耦合、纯滞后、多扰动等特点,它的控制方法代表着一类非线性系统控制的解决方法。以硅钢工业退火炉温度为控制对象,在双交叉限幅控制的基础上引入了智能学习系统,形成了基于智能学习系统的双交叉限幅控制方法来解决此类非线性系统的控制问题,并通过模块化的编程来实现其功能。结果表明:与传统的PID控制相比,该控制方法的控制精度、抗扰性等控制指标有明显提高,是解决此类非线性控制的一种有效方法。 The temperature control of silicon steel industrial annealing furnace has the features of strong coupling,pure lag,multidisturbance. The control method represents the solution of a class of nonlinear control systems. The control object is the temperature control of silicon steel industrial an-nealing furnace, the intelligent learning system based on Double Across Limit Control is introducedand used to solve control problem of this kind of nonlinear system, and the module programming isused to re... 

针对硅钢连续退火机组的主要能源介质消耗现状,对现有生产工艺和设备研究采取机组循环用水、增加清洗段漂洗级数等措施可节约大概27 m3/h的过滤水量,并可减少78%的弱碱处理量;将炉子烟气换热系统增加一级余热回收,每年回收的余热相当于583 t标煤消耗,可节约蒸汽5 368 t。 The present situation of energy consumption for silicon steel annealing line is analyzed in this paper.In existing process and equipment conditions,increasing the number of cleaning series will lead to a saving of about 27 m3/h of filter water and reduce 78 % of weak base processing volume.For the flue gas heat-exchange system,adding a waste heat recovery device will recover waste heat equivalent to 583 tons of standard coal per year,corresponding to a saving of steam 5 368 t per year. 

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 

研究的两种取向硅钢（%:No1-0.042C、3.16Si、0.009Al、0.07Mn、0.50Cu、0.015S、0.0084N和No2-0.040C、3.20Si、0.014Al、0.22Mn、0.49Cu、0.016S、0.008 2N）由50 kg真空感应炉冶炼,锻成（mm）350×120×35板坯,经1 250℃30 min加热,开轧温度1 100℃,5道次热轧成2.3 mm板,终轧温度950～1 000℃。实验结果表明,两热轧板沿板厚方向存在组织和织构的不均匀性,热轧板次表层为再结晶组织,有较强的Goss织构组分;中心层为形变组织,具有典型的形变织构。含0.22%Mn的No2钢次表层{110}〈001〉织构组分比含0.07%Mn的No1钢弱,中心层{001}〈110〉织构组分大大强于0.07%Mn No1钢,导致两者磁性能差异,0.22%Mn No2钢磁感应强度(B₈₀₀)和铁损(P_1.7/50)分别为1.87 T和1.24 W/kg,0.07%Mn No1钢分别为1.88 T和1.18 W/kg。 Studied both grain-oriented silicon steels（%:No1- 0.042C,3.16Si,0.009Al,0.07Mn,0.50Cu, 0.015S,0.0084N and No2-0.040C,3.20Si,0.014Al,0.22Mn,0.49Cu,0.016S,0.0082N） are melted by a 50 kg vacuum induction furnace,forged to（mm） 350×120×35 slab,heated at 1 250℃for 30 min,with beginning rolling temperature 1 100℃hot-rolled to 2.3 mm plate by 5 passes,finishing-rolled at 950～1000℃.Test results show that the structure and texture along thickness of both hot-rolled plates are inhomogeneous:the subsurface ... 

采用取向分布函数和取向线分析方法对低温板坯加热取向硅钢从热轧到初次再结晶工艺阶段的织构进行了研究。研究表明:一次冷轧后各层的织构组分与热轧板各层面的织构组分存在着继承关系,次表层存在很强的{001}<110>织构,中心层的织构和热轧板的中心层相似,存在强的{001}<110>和{112}<110>织构;中间退火后发生再结晶,各织构组分的强度有所减弱,Goss织构组分再次出现;二次冷轧后沿厚度方向上的织构不均匀性不明显,{111}<112>织构强度最高,几乎是其他织构组分的1倍,{001}<110>织构大幅降低;初次再结晶后织构沿厚度方向没有明显的不均匀性,{111}<110>为最强的织构组分,并且具有一定强度的Goss位向。 The texture from the first cold rolling to the primary recrystallization of low temperature slab reheating grain-oriented electrical steel were researched by orientation distribution function and orientation distribution intensity technique.The results show that after the first stage of cold rolling,there is a strong {001}<110> texture in the subsurface and the texture in center layer is very similar to the center layer of hot band which has strong {001}<110> and {112}<110> tex... 

为满足用户对无取向电工钢中硫含量的要求,采用CaO-CaF2复合渣系为脱硫剂,利用RH投入法对无取向电工钢进行深脱硫试验。试验结果表明,RH精炼渣成分控制在w CaO43%~51%、w Al2O325%~31%、w MgO4%~6%、w SiO29%~12%、w(FeO+MnO)3%~6%,在脱硫剂加入量为6~8 kg/t时,钢中平均硫含量从32×10-6降低到18×10-6,RH平均脱硫率为43.3%,最高达47.1%。利用KTH模型计算精炼终渣平均硫容量为0.003 1,RH精炼结束时渣-钢间实际平均硫分配比从14增加到52。 In order to satisfy the requirements of consumers on sulfur content in non-oriented electrical steel,taking( CaO-CaF 2) based flux as desulfurizer,industrial experiments on deep desulphurization of non-oriented electrical steel were carried out during RH process. The results show that as the compositions of refining slag are appropriately controlled with w CaO of 43% ~ 51%,w Al2O3 of 25% ~ 31%,w MgO of 4% ~ 6%,w SiO2 of 9% ~ 12%,and w( FeO + MnO) of 3% ~ 6%,and the desulfurizer added are at 6 ~ ...