近年来，在节能减排背景之下，国内外众多研究者对无取向电工钢磁性能的提升做了大量研究。为了探索无取向电工钢磁性能提升的方法，对锡或锑对无取向电工钢磁性能的作用机制(晶粒尺寸和晶体织构的控制)进行分析。基于该作用机制，介绍锡或锑的添加对无取向电工钢磁性能的影响。经研究发现，适量的锡或锑在晶界偏聚，不会阻碍晶界的移动并且致使晶粒尺寸降低；与此同时，锡或锑在晶界偏聚不仅抑制{111}织构在原始晶界处形核及生长，还降低(100)晶粒表面能，促进(100)晶粒生长。因此，适量添加锡或锑，可使无取向电工钢铁损下降、磁感提升。最后结合生产工艺，建议无取向电工钢的研究方向应为稀土含量对高牌号无取向硅钢夹杂物尺寸和数量分布的影响，锡或锑的添加量和常化工艺参数(常化时间、常化温度)对常化晶粒尺寸的影响。 In recent years, due to the background of energy saving and emission reduction, numerous researchers all around the world have done a lot of investigations on the improvement of magnetic properties for non-oriented electrical steel. In order to explore the method of improving the magnetic properties of non-oriented electrical steel, the mechanism of tin or antimony on the magnetic properties(the control of grain size and crystallographic texture) of non-oriented electrical steel is illuminated. ... 

本文研究了丙烯酸树脂含量对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响.用盐雾实验、动电位极化及交流阻抗等试验手段研究了不同树脂含量对硅钢绝缘涂层的耐盐雾性能和电化学行为的影响,同时采用SEM对涂层的表面形貌和附着性进行研究.结果表明,树脂含量为19.9~29.4%时,涂层的耐蚀性和附着性最好;树脂含量过多时,涂层的耐蚀性和附着性均较差. This paper studies the influence of acrylic resin on the performance of insulating coating of aluminum dihydrogen phosphate on chromium-free non-oriented silicon steel.Salt spray experiment,potentiodynamic polarization and electrochemical impedance spectroscopy were used to study the influence of acrylic resin content on the salt spray resistance and electrochemical behavior of the insulation coating of nonoriented silicon steel.The surface morphologys and adhesion of coating were tested by SEM.... 

介绍了攀钢冶炼电工钢过程硫含量变化以及过程回硫、增硫情况,采取针对性措施,如:提高铁水装入量、转炉采用石英砂代替复合造渣剂造渣、RH脱硫等,降低钢中硫含量。结果表明:采取相应措施后,电工钢炼成率大幅提高,成品w[S]≤0.008%的比例由改进前的62%提高到92.4%,取得了明显的冶金效果。 The resulfurization and the change of sulphur content in production of electrical steel is analyzed.The targeted measures have been taken,such as increase the loaded quantity of liquid iron,quartz sand replaces the composite slagging agent in the converter and RH desulfurization to decrease the sulphur content of the steel.The result shows,after the measures have been taken,the finished product ratio of electrical steel increase a lot.The ratio of sulfur content of finished product no more than ... 

研究稀土Ce的添加对含Sn高磁感无取向电工钢磁性能及夹杂物的影响。对比分析了两种成分钢的磁性能以及各过程工艺条件下夹杂物种类和分布情况。结果表明,在含Sn高磁感无取向电工钢中加入稀土元素Ce可以粗化夹杂物,提高成品晶粒的均匀性,有效降低铁损;同时Ce的添加不影响Sn元素提高磁感的效果,磁感保持不变。 Effect of Ce on magnetic properties and inclusion of Sn-bearing high permeability non-oriented electrical steel was investigated. A comparative analysis of the magnetic properties and the types and distributions of inclusion in the two sheets with different composition shows that the addition of Ce to the Sn-bearing high permeability non-oriented electrical steel can coarse the inclusion,improve the homogeneity of the finished grain and effectively decrease the core loss. Also,the addition of Ce... 

【作者】 陶永根； ...

介绍了烟气余热利用系统的工艺流程及控制思想,结合该系统在钢厂硅钢连续退火机组中的应用实践,估算出烟气余热利用系统每年可节约蒸汽5 040 t,经济效益良好,同时分析了该系统存在的问题及对策。 Introduced a method about the process and control of the application of waste heat system, which had been used into a silicon steel continuous annealing line and profiting a good economic benefit by saving a large number of steam every year, which has been estimated about 5 040 tons, and analyzed the problems and solutions existed in this system. 

以取向电工钢成分为基础,制备了含C或Mn和S的4种实验钢。观察了接近平衡析出状态实验钢经60%冷轧后在600～1000℃范围再结晶退火过程中微观组织演变,统计分析了再结晶体积分数随退火时间的变化规律,进而计算了各实验钢静态再结晶的激活能。观察了高含C实验钢退火初期再结晶晶粒优先出现的部位。结果表明900～1000℃范围内各实验钢铁素体的化学成分相似,因而其再结晶激活能基本一致。在600～800℃范围内铁素体内会有阻碍再结晶进程的三次渗碳体析出,从而使再结晶激活能明显提高。高C含量实验钢中还会有从奥氏体转变而来的粗大珠光体或渗碳体,轧制过程中其附近形成的变形区会促进600～800℃加热时该区域附近率先发生再结晶形核、降低再结晶激活能。固溶的Mn、S元素可微弱提高再结晶激活能,但高Mn、S含量会改变粗渗碳体从奥氏体析出时的形态。 Four experimental steels based on grain oriented electrical steel containing C,or Mn and S were prepared.Microstructure evolution of the steels close to a state of equilibrium precipitation were observed during annealing processes at 600-1000 ℃after 60% cold rolling,the changes of recrystallization volume fraction were analyzed statistically as the annealing was prolonged,and the activation energy for static recrystallization of the steels were calculated.The locations,where the recrystallizatio... 

在实验室模拟CSP工艺条件下制备了取向硅钢,研究了二次冷轧中间退火工艺对组织和织构的影响。结果表明,中间退火温度对取向硅钢脱碳,高温退火组织及织构均产生明显影响。经940℃中间退火后,取向硅钢脱碳再结晶晶粒较850℃中间退火的多,且再经高温退火处理后,晶粒粗化,最大晶粒尺寸达4.8 mm;高斯织构组分密度达27.00,较850℃中间退火试样高。 Grain-oriented silicon steel was prepared by simulated CSP technology in laboratory. Effects of secondary cold-rolled intermediate annealing on microstructure and texture were studied. The results show that intermediate annealing has obvious effects on the microstructure and texture of the steels after decarburization annealing and high temperature annealing. After intermediate annealing at 940 ℃,recrystallized grain of decarburization annealed steel is more than that of intermediate annealed at... 

【作者】 吴玉美； 陆晔； ...

采用低温板坯加热制备取向硅钢,通过透射电镜(TEM)观察并研究热轧板中的析出物,用ODF织构法研究热轧板距表面1/8、1/4和1/2处的织构分布。结果表明,热轧板中的析出物主要是密排六方AlN,AlN形貌呈规则长方形,AlN颗粒大小不等,分布密度低;热轧板中的织构沿板厚方向,由亚表层的{110}<001>织构向1/2中心层的α线织构变化,其中{110}<001>织构在热轧板距表面1/4层处最强。 The low temperature grain-oriented silicon steels were produced by acquired inhibitor method.The precipitates in hot rolling strip were observed and studied by transmission electron microscope,and the texture distribution in 1/8,1/4 and 1/2 layers of hot rolling strip were analyzed by ODF method.The results showed that the square shaped h-AlN is the main precipitates in hot rolling strip.The precipitates are varying in size and distribution.The texture of hot rolling strip in thick direction are... 

基于简化的取向硅钢片模型,系统地对不同的交流激励下的硅钢叠片内铁损、交链磁通和空气中指定位置的法向漏磁的分布进行了\"单片级\"的测量,并建立了相应的硅钢叠片级问题的三维有限元分析模型,进行了大规模的数值计算分析。模型实验和数值分析的结果表明垂直进入硅钢片的漏磁通和损耗呈现浅透入的特点,在硅钢片内引起的涡流损耗在总铁损中占据了\"举足轻重\"的份额。用电磁场有限元分析软件MagNet瞬态场时步法计算结果与测量结果相吻合,说明本文方法研究复杂的硅钢叠片问题的有效性。 The measurement and 3D finite element analysis of the iron loss,interlinkage flux inside the laminated silicon steel sheets and the magnetic flux densities at the specified positions are carried out based on a verifying silicon steel sheet model.The modeling results show that the leakage flux vertically through the silicon steel sheets has the peculiarity of shin effect,and the eddy current loss caused by the AC leakage flux is a significant component of the total iron loss.The calculated result... 

晶界和{100}柱状晶在硅钢生产过程中对织构的遗传和演变有关键作用,因此本文利用晶体塑性有限元方法进行立方和旋转立方取向双晶在晶界不同位向时晶体取向演变的全场模拟。模拟显示,三种晶界位向下,晶界都具有诱发晶内产生S形状形变不均匀和缓解局部形变不均匀区取向转动的特点,立方和旋转立方取向双晶在带有剪切作用的轧制条件下都显示明显的取向稳定性。GB⊥RD(表示晶界垂直于轧向)晶界位向时,旋转立方取向晶粒优先在晶界中心位置发生取向转动,而立方取向则优先在远离晶界的端部发生取向转动。GB⊥TD(表示晶界垂直于横向)的晶界位向下,其晶界阻碍作用最小,双晶内产生的取向漫散度大,织构强度较低;除绕TD转动外,也具有复杂的绕RD、ND的取向转动。GB⊥ND(表示晶界垂直于法向)的晶界位向下,取向转动与GB⊥RD时相近,但有少量取向绕ND转动。 Grain boundaries and initial{100}columnar grains play a key role in the inheritance and evolution of texture in the production of electrical steels.In this paper,the crystal plasticity finite element method was used to simulate the grain orientation evolution of cube and rotated-cube oriented bicrystals when grain boundary was set to different orientations.It was shown that the grain boundary in three grain boundary orientations demonstrated the characteristics of inducing Sshape deformation inh...