{100}织构因具有两个易磁化方向能够明显的提高磁性能,因此如何在表面获得具有{100}织构一直是无取向电工钢研究焦点。本文主要介绍了获得{100}织构的主要工艺方法及其基本原理,并结合实际生产过程对各工艺方法的优缺点进行了分析;一方面,优化无取向电工钢的成分,降低碳、锰元素含量以避免脱碳退火和真空退火,简化生产工艺;另一方面,调节升温速度、降温速度和退火气氛,使{100}晶面的表面能或弹性应变能最低,制备具有{100}织构柱状晶组织的无取向电工钢是今后的发展方向。 Because { 100} texture has two easy magnetization directions,which can significantly improve magnetization properfies,how to develop { 100} texture is a focus for researchers and manufactures. In the paper,main manufacturing processes and basic principle are introdued,and their advantages and disadvantages in practical production are analyzed. On the one hand,the production process can be simplified by optimizing chemical compositions,such as reducing the content of C and Mn,which can avoid deca... 

【摘要】 <正>编号:2012016获奖等级:特等完成单位:...

【机构】 武汉钢铁学院轧钢七二级电工钢结业小组； ...

研究了取向硅钢制备过程中常见的两种冷轧工艺,主要研究了一阶段冷轧与两阶段冷轧+中间退火工艺对初次再结晶组织及织构的影响.结果表明:采用两阶段冷轧+中间退火工艺制备以Cu2S为主抑制剂的取向硅钢,其初次再结晶平均晶粒尺寸为18.1μm,高斯晶粒的体积分数为0.6%,迁移性强的重位点阵晶界(Σ5+Σ9)和高能晶界(20°~45°取向偏差角)所占比例分别为1.8%和50.4%.与一阶段冷轧工艺相比,其初次再结晶晶粒较细,且高斯晶核与特征晶界所占的比例较高,有利于高斯晶粒发生二次再结晶. Two common cold-rolling processes of grain oriented silicon steel and the effects of the single stage cold rolling and tw o-stage cold rolling w ith intermediate annealing processes on the primary recrystallization microstructure and texture w ere investigated. The results revealed that for the grain oriented silicon steel prepared under the tw o-stage cold rolling process w ith intermediate annealing w ith Cu 2 S as the main inhibitor,the average grain size of the primary recrystallization micr... 

对3层高硅电工钢复合板铸坯进行热轧及温轧变形加工后，采用正火、退火两种热处理方式处理，并观察轧制过程中产生的裂纹，研究不同状态下复合板的磁性能。对不同状态下的试样进行扩散退火处理，研究复合板中裂纹变化及其对磁性能的影响。结果表明：不同热处理工艺下合金内部的裂纹尺寸差异明显，裂纹尺寸对复合板的磁性能影响显著，相对于深裂纹，其他因素的影响较小；温轧变形加工后，复合板内层出现有序组织，但该有序组织在合金存在深裂纹的前提下并不能从本质上提高合金的磁性能；扩散退火工艺可以消除复合板内部的浅裂纹及微裂纹，但不能消除尺寸较大的裂纹，故而不能显著提高存在深裂纹的复合板的磁性能。 After hot rolling and warm rolling deformation processing of casting billet for three-layer high silicon electrical steel composite plate, it was normalized and annealed for heat treatment. Then, the cracks produced during the rolling process were observed, and the magnetic properties of composite plate in different states were also investigated. Furthermore, the samples in different states were subjected to diffusion annealing treatment, and the changes of crack in composite plate and their eff... 

取向硅钢利用析出物作为抑制剂,抑制初次再结晶晶粒的长大,抑制剂是取向硅钢发生二次再结晶的基本条件之一。文中通过低温板坯加热技术制备取向硅钢,采用透射电镜(TEM)观察并研究了高温退火阶段抑制剂的演化过程。结果表明,渗氮后形成的非晶态Si3N4析出物不稳定,在700～750℃退火升温阶段转化为(Al,Si)N;(Al,Si)N颗粒在800℃发生团聚,随后长大并粗化;(Al,Si)N是低温取向硅钢主要抑制剂,随退火温度的升高,(Al,Si)N抑制力大幅下降。 Precipitates as inhibitor are used to inhibit the grain growth of primary recrystallization in grain-oriented silicon steel,and inhibitor is one of the basic conditions for occurring of secondary recrystallization.The grain-oriented silicon steel was produced by low temperature slab heating and nitriding technique.The evolution of inhibitor was observed by transmission electron microscopy.The results show that Si3N4 particles are precipitated after nitriding,and Si3N4 particles are amorphous and... 

以CaO-CaF2复合渣系为脱硫剂,在RH精炼过程采用真空投入法进行高牌号无取向电工钢深脱硫工业试验,采用KTH模型计算分析了RH炉渣成分对硫容量CS的影响。研究结果表明,炉渣成分控制在w((CaO))/w((SiO2))为5~7,w((CaO))/w((Al2O3))为1.5~1.8,w((Al2O3))为25%~30%,w((FeO+MnO))<5%,脱硫剂加入量为6~8kg/t时,钢中硫质量分数从平均0.003 1%降低到0.001 8%,最高脱硫率达到47.1%,平均脱硫率为41.7%。 The industrial trials on deep desulphurization of high grade non-oriented electrical steel were finished through using CaO-CaF2complex based fluxes in RH process.Using the KTH model,the effect of refining slag composition on the sulfide capacities was analyzed.The results show that the chemical composition of refining slag(mass fraction,%)is w((CaO/SiO2))between 5to 7,w((CaO))/w((Al2O3))beween 1.5to 1.8,w((Al2O3)) between 25%to 30%,w((FeO+MnO))less than 5%,and the desulphurizer addition level of... 

通过测试取向硅钢不同工艺条件下的碳含量,探讨了CGO取向硅钢碳含量控制的最优处理条件,研究了脱碳温度和脱碳时间对相同初始碳含量取向硅钢的脱碳效果的影响。结果表明,在气氛为(15%~20%)H2+(75%~80%)N2,炉压差为10~20 Pa的条件下,CGO取向硅钢合适的脱碳温度为1 073 K~1 123 K,脱碳时间为10~20 min。在该处理条件下,能取得较好的脱碳效果。 By means of testing carbon content of oriented silicon steel below the distinct technical conditions,inquires the excellent handle terms of carbon content controlling for CGO oriented silicon steel,studies effects of decarburization annealing temperature and decarburization annealing time to the oriented silicon steel decarburization efficiency in same initial carbon content.The results show that,under the condition of atmosphere(15% ~ 20%) H2+(75% ~ 80%)N2 and furnace pressure difference 10 ~ 2... 

研究了冷轧95%变形量无取向硅钢不同退火温度(710～1 050℃)下再结晶织构特征.再结晶刚完成时(710℃退火),呈现强γ({111<112>～<134>)与弱{114}<481>织构特征;随退火温度升高至900℃,γ明显减弱,{114}<481>组分持续增强,形成典型的{h,1,1}<1/h,1,2>织构;进一步升温至1 050℃,再结晶织构不再发生明显变化.基于EBSD分析,{114}<481>组分的持续强化可归因于其明显的尺寸优势以及较高频率的高能晶界(取向差角为20°～45°). A non-oriented silicon steel was heavily rolled to 95% reduction and subsequently annealed at 710~1 050 ℃ to investigate recrystallization texture evolution.When annealed at 710 ℃ with complete recrystallization,the texture is characterized by a strong partial γ fiber spreading from {111}<112> to {111}<134> and a weak {114}<481> component.As annealing at 900 ℃,γ fiber is decreased significantly while {114}<481> is increased consistently,producing a typical {h,1,1}<1/h,... 

为满足用户对无取向电工钢中硫含量的要求,采用CaO-CaF2复合渣系为脱硫剂,利用RH投入法对无取向电工钢进行深脱硫试验。试验结果表明,RH精炼渣成分控制在w CaO43%~51%、w Al2O325%~31%、w MgO4%~6%、w SiO29%~12%、w(FeO+MnO)3%~6%,在脱硫剂加入量为6~8 kg/t时,钢中平均硫含量从32×10-6降低到18×10-6,RH平均脱硫率为43.3%,最高达47.1%。利用KTH模型计算精炼终渣平均硫容量为0.003 1,RH精炼结束时渣-钢间实际平均硫分配比从14增加到52。 In order to satisfy the requirements of consumers on sulfur content in non-oriented electrical steel,taking( CaO-CaF 2) based flux as desulfurizer,industrial experiments on deep desulphurization of non-oriented electrical steel were carried out during RH process. The results show that as the compositions of refining slag are appropriately controlled with w CaO of 43% ~ 51%,w Al2O3 of 25% ~ 31%,w MgO of 4% ~ 6%,w SiO2 of 9% ~ 12%,and w( FeO + MnO) of 3% ~ 6%,and the desulfurizer added are at 6 ~ ... 

在实验室模拟CSP流程制备了不同含量稀土铈(质量分数0~0.018%)的1.2%Si无取向电工钢,并对其进行1 000℃×5min的再结晶退火处理,研究了铈质量分数对无取向电工钢夹杂物、显微组织、再结晶织构和磁性能的影响。结果表明:随着铈质量分数的增加,微细夹杂物数量、再结晶晶粒尺寸、{100}和{110}织构组分、磁感应强度先增后减,{111}织构组分、铁损先减后增;铈的质量分数为0.005 1%时,钢中的夹杂物数量最少,再结晶晶粒尺寸最大,有利织构最多,磁性能最优,铁损P15/50为3.253W·kg-1,磁感应强度B50为1.751T。 Non-oriented electrical steels containing different contents rare earth Ce element(0-0.018wt%) were prepared in the laboratory by simulated CSP(compact strip production)process,and then recrystallization annealing at 1 000 ℃ for 5 min were performed,the effects of Ce content on inclusion,microstructure, recrystallization texture and magnetic properties of non-oriented electrical steels were studied.The results show that with the increase of Ce content,the amounts of fine inclusion,the size of re... 