针对攀枝花钢钒有限公司难以稳定生产w(S)≤0.006%高级别电工钢的问题,通过开发RH脱硫剂、钢包渣改性及工艺参数控制,形成了RH脱硫系统工艺技术。经工业试验表明,采用该工艺技术后,钢水脱硫率最高达到42%,成品w(S)控制在0.005%以下,全氧、氮含量也得到了较好的控制,且脱硫剂没有引起钢水增碳,满足高级别电工钢的生产要求。 In light of the difficulty of production of high level electrical steel w(S)≤0.006 % steadily in Panzhihua steel & vanadium Co.,Ltd.the process technology of RH desulfurization system has been formed by developing the RH desulfurizer,modifying the ladle slag and controlling the process parameters.Industrial experiments show that the desulfurization rate of hot metal rises to 42 % and the w(S) of the finished products is controlled in below 0.005 % and total oxygen and nitrogen contents are a... 

本文对某厂硅钢DR510温度、成分及过程控制水平和成品的组织、力学性能进行了研究,并在此基础上提出了工艺优化方案,有一定的借鉴和推广价值。 In this paper,the critical process and the products quality,including temperature,composition and process controlling level,the organization and mechanical properties of the finished product,were studied.On the basis of that the optimized technical plan provided,and this control technology is worth using and spreading. 

结合扫描电镜和大样电解研究了CSP流程W800牌号无取向电工钢表面线状缺陷中夹杂物成分及来源，采用SPSS软件回归分析了生产过程各因素对表面线状缺陷的影响。研究表明：稳态浇铸过程铸坯中大型夹杂物含量为5.39 mg/10 kg。引起无取向电工钢表面线状缺陷的大型夹杂物主要为脱氧产物、镁铝尖晶石和钢包顶渣，主要类型为Al₂O₃、MgO-Al₂O₃、CaO-Al₂O₃-MgO和CaO-Al₂O₃-SiO₂。非稳态浇铸过程钢水洁净度明显降低，热轧板表面线状缺陷比例上升。影响表面线状缺陷的主要因素为RH出站时顶渣的w（CaO）/w（Al₂O₃）、RH脱氧结束氧位及中间包最低吨位。 Combining scanning electron microscopy and large sample electrolysis, the composition and source of inclusions in the surface linear defects of W800 grade non-oriented electrical steel in the CSP process were studied. SPSS software was used to regress and analyze the main factors which affected the surface linear defects in the steelmaking process. Research shows that the content of large inclusions in the steady state casting process is 5.39 mg/10 kg. The large inclusions which cause linear def... 

借助电子背散射衍射(EBSD)及ZEISS-200MAT金相显微镜对某钢厂普通取向硅钢(CGO)进行研究,研究结果表明:热轧板组织、织构沿板厚方向存在明显的不均匀性,在热轧板表层及次表层发生再结晶,同时存在强度较高的Goss织构,中心层存在较强的{001}<110>变形织构。冷轧组织均呈纤维状条带组织,一次冷轧后,热轧板中的Goss织构消失,织构主要为α、γ织构,经中间脱碳退火后,α、γ织构强度减弱,并出现一定强度的Goss织构和利于Goss织构发展的{554}<225>、{332}<113>等织构,经二次冷轧后,二次冷轧织构类型与一次冷轧织构一致,但织构强度不同。 The grain-oriented silicon steel produced by a steel factory was investigated by EBSD and ZEISS-200 MAT metallographic microscope.The results show that the textures and microstructures along thickness of hot rolled slab are inhomogeneous.The surface layer and the layer near that are recrystallized structure which has a high Goss texture,but there is deformation texture{001}<110>in the central layer.The structure after cold rolling is a structure like fiber strip.After the first cold rollin... 

对取向硅钢在不同气氛下的高温退火工艺进行实验室模拟，利用X射线衍射仪（XRD）分析了硅钢退火至900℃和1170℃时的样品表面氧化层和底层的物相组成，采用场发射扫描电镜（SEM）观察了样品表面氧化层和底层在截面方向上的微观形貌特征，并计算了高温退火一次升温阶段氧化反应的吉布斯自由能以及900℃时退火气氛的氧分压。结果表明：当退火气氛的露点温度保持一定时，较高的氢气含量有利于生成完整连续的底层；当退火气氛的水氢分压比保持一定时，在露点温度与氢气含量两者较低的条件下，底层附着性不佳易脱落，较高条件下，底层中夹杂着较多的铁单质；当氧化层中无FeO时，底层完整连续但易脱落，当FeO层较薄时，底层下方存在部分未反应的SiO₂,当FeO层较厚时，底层不完整连续且有分层。 The high temperature annealing process of grain-oriented silicon steel in different atmospheres was simulated in the laboratory. X-ray diffractometer（XRD） was used to analyze the phase compositions of the surface oxide layer and forsterite film of the silicon steel annealed to 900 ℃ and 1170 ℃. Field-emission scanning electron microscopy（SEM） was used to observe the micro morphology characteristics of the surface oxide layer and forsterite film of the samples in the cross section direction. The ... 

【作者】 韩超； 代智肄； ...

采用\"热轧复合+冷轧减薄+退火\"方法成功制备了0.20mm厚的硅浓度梯度高硅钢薄带,并采用SEM和X射线衍射技术对制备过程中组织和织构演变进行了研究。热轧复合板微观组织呈明显层状分布,复合界面为紧密冶金结合且经过83%的大冷轧变形未开裂。热轧和冷轧复合板带中均形成强α和γ织构,再结晶退火后形成强γ织构。冷轧和退火织构沿板厚呈显著的梯度分布特征,其主要来自于复合界面两侧硅浓度和初始热轧织构的差异性以及冷变形的不均匀性。 Gradient high silicon steel thin sheets with thickness of 0.20 mm were successfully produced by the rolling and annealing method,including hot rolling bonding,cold rolling,and annealing.Microstructure and texture evolution was investigated by means of SEM and X-ray diffraction.Microstructure of hot-rolling-bonding shows obviously layered distribution,the composite interface was closely metallurgical bonding and no cracking appears even after 83%cold rolling.Strongαandγfibers develop in the hot a... 

观察了取向硅钢极薄带经冷轧至不同厚度,并经过不同工艺热处理后的显微组织及亚结构。结果表明:冷轧压下量越大,显微组织中位错密度越高,冷变形组织越多,等轴晶粒越少;增加冷轧压下量可以使试样的再结晶温度降低,当钢带厚度为0.08 mm时,在650℃退火时就能发生明显的再结晶。 Microstructure and substructure of the grain oriented ultra-thin silicon steel sheets is analyzed,which are rolled down to different thickness and treated with different heat treatment process.The result shows that there are higher dislocation density,more cold deformation structure and less equiaxed crystal grain in microstructure of the steel sheets with more cold rolled reduction.Increase of cold rolled reduction will decrease recrystallization temperature,and when thickness of the steel shee... 

为满足用户对无取向电工钢中硫含量的要求,采用CaO-CaF2复合渣系为脱硫剂,利用RH投入法对无取向电工钢进行深脱硫试验。试验结果表明,RH精炼渣成分控制在w CaO43%~51%、w Al2O325%~31%、w MgO4%~6%、w SiO29%~12%、w(FeO+MnO)3%~6%,在脱硫剂加入量为6~8 kg/t时,钢中平均硫含量从32×10-6降低到18×10-6,RH平均脱硫率为43.3%,最高达47.1%。利用KTH模型计算精炼终渣平均硫容量为0.003 1,RH精炼结束时渣-钢间实际平均硫分配比从14增加到52。 In order to satisfy the requirements of consumers on sulfur content in non-oriented electrical steel,taking( CaO-CaF 2) based flux as desulfurizer,industrial experiments on deep desulphurization of non-oriented electrical steel were carried out during RH process. The results show that as the compositions of refining slag are appropriately controlled with w CaO of 43% ~ 51%,w Al2O3 of 25% ~ 31%,w MgO of 4% ~ 6%,w SiO2 of 9% ~ 12%,and w( FeO + MnO) of 3% ~ 6%,and the desulfurizer added are at 6 ~ ... 

晶界和{100}柱状晶在硅钢生产过程中对织构的遗传和演变有关键作用,因此本文利用晶体塑性有限元方法进行立方和旋转立方取向双晶在晶界不同位向时晶体取向演变的全场模拟。模拟显示,三种晶界位向下,晶界都具有诱发晶内产生S形状形变不均匀和缓解局部形变不均匀区取向转动的特点,立方和旋转立方取向双晶在带有剪切作用的轧制条件下都显示明显的取向稳定性。GB⊥RD(表示晶界垂直于轧向)晶界位向时,旋转立方取向晶粒优先在晶界中心位置发生取向转动,而立方取向则优先在远离晶界的端部发生取向转动。GB⊥TD(表示晶界垂直于横向)的晶界位向下,其晶界阻碍作用最小,双晶内产生的取向漫散度大,织构强度较低;除绕TD转动外,也具有复杂的绕RD、ND的取向转动。GB⊥ND(表示晶界垂直于法向)的晶界位向下,取向转动与GB⊥RD时相近,但有少量取向绕ND转动。 Grain boundaries and initial{100}columnar grains play a key role in the inheritance and evolution of texture in the production of electrical steels.In this paper,the crystal plasticity finite element method was used to simulate the grain orientation evolution of cube and rotated-cube oriented bicrystals when grain boundary was set to different orientations.It was shown that the grain boundary in three grain boundary orientations demonstrated the characteristics of inducing Sshape deformation inh... 

【作者】 胡志强； 张文康； ...

提出以“云边一体化架构”构建硅钢智慧决策系统，来解决原硅钢制造L1～L5系统架构模式下的数字信息孤岛、业务功能割裂等问题。在此基础上，开发了云边协同的自学习型控制模型及业务决策模型，构建起硅钢“智慧大脑”，形成了以研发、制造、服务等核心业务数字化融合的智能化决策支持新模式，探索出一条钢铁制造业数字化、智能化转型之路。 SIDS(Silicon-steel Intelligent Decision-making System)based on \"cloud-edge integration architecture\" was proposed to solve the problems of data silos and business function fragmentation in the original L1～L5 system architecture.On this basis,the self-learning control model and decision-making model of cloud-edge collaboration were developed,the \"smart brain\" of silicon steel department was constructed,and a new intelligent decision-making support model of digital integration of core businesses s...