硅钢资料

采用电解法和扫描电镜研究了300 t转炉-RH精炼钙处理对无取向硅钢板（%:≤0.005C、1.2～2.2Si、0.2～0.6Mn、≤0.20P、≤0.005S、0.2～0.6Al、0～0.01Ca）中夹杂物的影响。结果表明,钢中Al含量为0.25%和0.35%时,钢中溶解氧均小于1×10^-4%,钙处理后都会产生CaS夹杂物,尤其是含0.35%Al的钢水;钙处理可以有效减少钢中的夹杂物数量,尤其是0.5μm以下的微细夹杂物数量;钙处理后夹杂物的种类以AlN、CaS为主,同时还含有少量的氧化物夹杂物以及AlN-CaS复合夹杂物,尺寸主要为1.5～5.0μm。 The effect of 300 t converter-RH refining calcium treatment on inclusions in non-oriented silicon steel sheet （%:≤0.005C,1.2～2.2Si,0.2～0.6Mn,≤0.20P,≤0.005S,0.2～0.6A1,0～0.01Ca） has been studied by electrolysis and scanning electron microscope.Results show that with 0.25%and 0.35%Al content in steel,all the dissolved oxygen in liquid is less than 1×10^-4%,and the CaS inclusions are produced after calcium treatment,especial for the liquid containing 0.35%Al;the amount of inclusions in ste... 

利用EBSD技术研究了电工钢中长轴平行于轧向的柱状晶样品在热轧和退火过程中组织和取向的演变规律,并与长轴平行于板法向的样品的已有研究结果进行对比。结果表明,无论柱状晶按何种方向排列,只要表面存在剪切力,热轧后都可形成剪切织构,同时中心形成轧制织构,主要包括旋转立方织构和{112}<1-10>。柱状晶造成的影响主要体现在板中心层,长轴平行于轧向排列的样品热轧时形成的粗大旋转立方晶粒要到脱碳退火后才能完全消除,但破坏了正常的不同取向晶粒间的取向差分布及尺寸均匀性,导致二次再结晶不完全及磁性能降低。 The evolution of microstructure and grain orientation in an electrical steel containing columnar grains with its long axis being parallel to the rolling direction of sheet was studied during hot rolling and annealing by EBSD technique.The results are compared with those of samples containing columnar grains being parallel to normal direction of sheet reported in the reference [3].It was shown that,whether the long axis of columnar grains was arranged in RD or ND,shear textures can be formed in t... 

研究了传统工艺流程生产的2%Si无取向电工钢在不同退火温度下的磁性能。研究结果表明,随着退火温度的升高,显微组织均匀性提高且晶粒尺寸增大;有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;成品的铁损P1.5/50先下降后略有上升,磁感B50上升平缓;在890℃×2 min的退火工艺条件下,成品电工钢的磁性能最佳,对应的铁损P1.5/50小于3.2 W/kg,磁感B50高于1.74 T。 In this paper,the effect of annealing temperature on magnetic properties of non-oriented electrical steel with 2% silicon was studied.Results show that the uniformity of microstructure and the average grain size increase with the rise of annealing temperature.The texture components of annealing can be improved by enhancing {100} <0vw>,α,η fiber textures and weakening {111} <112> fiber texture.The tendency of core loss P1.5/50 shows that it decreases first and then increases,while the... 

研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient... 

介绍了国内、外电工钢极薄带的生产现状及市场应用的情况,以及典型生产企业的生产规模、产品性能和应用领域,指出扩大高牌号无取向电工钢生产、提高产品质量是目前电工钢发展的迫切要求。 The production situation and market application of ultra thin electrical steel strip at home and abroad were described.The production capability,product property and application area of typical corporation were introduced.The results indicate that the urgency needed of electrical steel development is expanding high-grade non-oriented electrical steel production and improving products quality at present. 

研究稀土Ce的添加对含Sn高磁感无取向电工钢磁性能及夹杂物的影响。对比分析了两种成分钢的磁性能以及各过程工艺条件下夹杂物种类和分布情况。结果表明,在含Sn高磁感无取向电工钢中加入稀土元素Ce可以粗化夹杂物,提高成品晶粒的均匀性,有效降低铁损;同时Ce的添加不影响Sn元素提高磁感的效果,磁感保持不变。 Effect of Ce on magnetic properties and inclusion of Sn-bearing high permeability non-oriented electrical steel was investigated. A comparative analysis of the magnetic properties and the types and distributions of inclusion in the two sheets with different composition shows that the addition of Ce to the Sn-bearing high permeability non-oriented electrical steel can coarse the inclusion,improve the homogeneity of the finished grain and effectively decrease the core loss. Also,the addition of Ce... 

采用取向分布函数分析了无取向电工钢不同再结晶退火温度下的织构变化及织构对磁感应强度和铁损的影响,并计算了无取向电工钢的磁晶各向异性能。结果表明,随着实验钢的再结晶退火温度升高,Goss织构和立方织构组分显著增强,而{111}面织构强度却减弱。较高的退火温度有利于减小织构因子,提高磁感应强度。磁晶各向异性能计算结果显示,随着再结晶退火温度升高,无取向电工钢板的磁晶各向异性能降低。 The recrystallization texture and the relationship of texture to magnetic induction intensity and core loss of a non-oriented electrical steel were investigated by orientation distribution function analysis. The magnetic anisotropy energy of the steel was calculated also. The results show that,the intensity of Goss texture and cubic texture increases,but the intensity of { 111} texture decreases with increasing recrystallization annealing temperatures of the steel. The higher annealing temperatu... 

研究了CSP工艺生产≤0.005%C-1.1%Si的2.2mm无取向电工钢热轧板在800～1000℃常化对0.5mm冷轧板840℃退火后组织和磁性能的影响。结果表明,热轧板常化温度升高,冷轧板退火后的再结晶晶粒增大,铁损降低,磁感增加;热轧板常化温度超过900℃,因第二相固溶而后弥散析出,退火后冷轧晶粒细化,铁损增加,因此该无取向电工钢热轧板最佳常化温度为900℃。 The effect of normalizing at 800-1000℃ of CSP produced plate(≤0.005%C-1.1%Si) on the microstructure and magnetic properties of downstream cold-rolled non-oriented electrical steel annealed at 840℃ was studied.Results show that with increasing normalizing temperature of hot-rolled material the recrystallized grain size of annealed sheet increases,iron loss reduced and magnetic induction increases.As normalizing temperature excesses 900℃,grain is refined and iron loss increases after annealing due... 

采用铸坯低倍组织检验和化学分析的方法,研究板坯连铸机二冷区电磁搅拌器电流和频率参数对无取向电工钢XG800WR板坯中心偏析和等轴晶率的影响,结果表明:铸坯等轴晶率随着搅拌器电流强度和电流频率的增大而增加。采用二冷区电磁搅拌可减小中心易偏析元素S的偏析,试验得出:减小铸坯S偏析效果最好的电磁搅拌参数为电流380～400A,频率6Hz。 The effect of electromagnetic stirring current and frequency parameter at secondary cooling area on the central segregation and equiaxed crystal ratio of XG800WR non - oriented electrical steels slab was investigated through the methods of chemical and macrostructure analysis.The results shows that the rate of equiaxed crystal zone is going up with increasing of current intensity and current frequency.Electromagnetic stirring in the secondary cooling area can be easily reduced segregation caused... 

针对某厂DMS森吉米尔轧机生产无取向硅钢表面麻面缺陷的问题，根据生产实际，对其形成原因从乳化液及工作辊两方面因素进行了分析。结果表明：乳化液对麻面缺陷的产生有一定影响，但不是主要因素，主要原因是由于二十辊森吉米尔轧机工作辊辊径较小，轧制相同长度带钢轧辊运转周期较大，容易产生疲劳失效而导致。为此，提出通过调整冷轧工序成品轧制道次的压下率以减小轧制力，从而减小工作辊的磨损疲劳；通过对轧制乳化液浓度、温度的合理控制，以改善润滑效果、提高轧制速度，而进一步缓解轧辊疲劳的改进措施，使该钢厂无取向硅钢麻面缺陷发生率由原来的18%降至0.8%,带钢表面质量明显改善。 For the problem of surface pockmarks of non-oriented silicon steel strip produced by a DMS Sendzimir mill, based on the production practice, the formation causes were analyzed from two aspects of emulsion and working roll. The results show that the emulsion has a certain effect on the formation of surface pockmarks defects, but it is not the main factor. The main reason is that the working roll diameter of the 20-high Sendzimir mill is small, and the running period of the roll rolling the same l... 

根据新日铁、JFE及浦项等国外钢铁公司2008年以来在日本专利局、欧洲专利局(EP)及世界知识产权组织(WIPO)申请公开的有关生产Hi-B取向电工钢典型专利技术,概述了近年来国外大型钢铁企业采用低温板坯加热(坯加热温度<1 280℃)技术生产Hi-B取向电工钢主要技术重点,即将调节关键化学成分Al、N、Sn及Sb等与工艺改进相结合。最后介绍了国外大型钢铁企业采用低温板坯加热技术生产Hi-B取向电工钢实例。 The latest developments on technology for manufacturing Hi-B grain oriented electrical steel sheets developed by Nippon Steel Corp.,JFE Steel and POSCO were described according to the patents published by World Intellectual Property Organization,Japan Patent Office and European Patent Office over the recent years.The low temperature slab heating process(particularly slab-heating temperature<1 280 ℃) together with suitably adjusting key chemical elements such as Al,N,Sn and Sb elements was the... 