硅钢资料

利用OM、SEM、TEM等实验方法研究了卷取工艺对一种新型含铜无取向电工钢晶粒度和析出相的影响。结果表明,该电工钢热轧带卷取后的晶粒尺寸为18～24μm,在卷取过程中,热轧带中有一定数量的第二相析出,经EDS能谱及选区电子衍射分析,这些析出相主要为AlN。随着卷取工艺的变化,该电工钢的晶粒度大小变化不明显,析出相的类型、尺寸大小不发生改变,体积分数发生一定的改变。 The effects of coiling process on grain size and precipitates of a new copper-bearing non-oriented electrical steel were investigated by OM,TEM and other experimental method.The results show that the grain size of hot-rolled bands after coiling is 18～24 μm.The second phases precipitate during coiling process.They are mainly AlN by EDS spectra and selected area electron diffraction.With the change of coiling process,the grain size of the electrical steel does not change significantly;the type and... 

本文研究了丙烯酸树脂含量对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响.用盐雾实验、动电位极化及交流阻抗等试验手段研究了不同树脂含量对硅钢绝缘涂层的耐盐雾性能和电化学行为的影响,同时采用SEM对涂层的表面形貌和附着性进行研究.结果表明,树脂含量为19.9~29.4%时,涂层的耐蚀性和附着性最好;树脂含量过多时,涂层的耐蚀性和附着性均较差. This paper studies the influence of acrylic resin on the performance of insulating coating of aluminum dihydrogen phosphate on chromium-free non-oriented silicon steel.Salt spray experiment,potentiodynamic polarization and electrochemical impedance spectroscopy were used to study the influence of acrylic resin content on the salt spray resistance and electrochemical behavior of the insulation coating of nonoriented silicon steel.The surface morphologys and adhesion of coating were tested by SEM.... 

简述了无取向硅钢环保涂层发展背景,分析了硅钢环保涂层的特点及国内、外研究进展,提出了硅钢保涂层下一步的发展方向。 The back ground of environmental protection coating of non-oriented silicon steel was described in this paper.The characteristics and study progress in domestic and foreign of environmental protection coating of non-oriented silicon steel were analysised.The next development direction of environmental protection coating of non-oriented silicon steel was put forward. 

针对宝钢硅钢常化退火过程中产生的退火炉辊印缺陷问题,通过实际生产的大数据与产品质量问题相结合,将数据挖掘、数据分析方法应用到实际,一定程度上解决了现场实际生产中的痛点,为现场生产提供决策支撑,避免了以前通过人工识别判定存在疏漏和无法定量判断的问题,形成了一套具有鲁棒性和可操作性的钢铁生产过程数据分析方法。通过智慧决策系统平台获取实际生产和表检仪数据,基于Pearson相关系数算法进行变量挑选和特征工程,并应用随机森林算法对数据建立分类预测模型,实现了质量问题的溯源和监控,通过数据量化预测了炉辊印缺陷是否可通过轧制消除的质量问题,识别准确率达到96.43%。 In views of the normalizing annealing furnace roll marks problem occurred in the process of normalizing annealing of silicon steel in Baosteel,by combining big data from actual production with product quality problems,data mining and data analysis methods were applied to actual production to solve the pain points and provide decision support,a robust and practical data analysis method for the steel production process has been developed,which avoided the previous problems of omission and non-quan... 

以青海盐湖氯化镁为初级原料,采用喷雾热解法制备原料氧化镁。原料氧化镁通过水化制备氢氧化镁。将氢氧化镁过滤、洗涤、烘干、粉碎、煅烧,制备硅钢级氧化镁。本文重点考察煅烧温度、煅烧时间、料层厚度等因素对氧化镁水化率的影响,采用均匀实验设计和DPS数据处理,确定最优煅烧实验条件为:煅烧温度1250℃,煅烧保温时间4小时,料层厚度0.5cm。在此条件下得到的硅钢级氧化镁完全满足硅钢及氧化镁的行业标准。 The magnesium oxide is prepared by Spray pyrolysis process,which magnesium chloride from Qinghai Salt Lake is used as primary raw material,and hydrated to magnesium hydroxide,then obtained silicon steel magnesia through filtering,washing,drying,crushing and calcinations.In this paper,influences of some factors on magnesia hydration rate are studied,such as calcination temperature,calcination time and material thickness.After average experimental design and DPS data processing,optimal calcination... 

【机构】 武钢研究院； ...

【作者】 刘彤； ...

研究了硅钢铸坯再加热过程中夹杂物的析出行为。采用非水溶液电解提取+扫描电镜观察方法,观察了试样的显微组织,统计了夹杂物的尺寸、种类、数量、分布。结果表明,均热温度为1 523 K时,水淬试样的夹杂物尺寸绝大部分小于0.5μm,0.5～5.0μm的夹杂物数量很少,没有发现5.0μm以上的夹杂物。此外,均热时间为10、30、60、90、120、240 min时,对应试样中0.05～0.2μm的夹杂物数量分别为4.04×104、4.73×104、3.70×104、3.33×104、3.10×104、1.56×104个/mm3。绝大部分夹杂物以MnS、AlN、CuxS类为主,并以三类夹杂物中的两类复合或三类复合居多。三类复合夹杂物总量占每组试样夹杂物总量的90%或以上。随均热时间延长,典型的夹杂物组成会发生如下变化:MnS+AlN+CuxS MnS+AlN AlN。与此同时,MnS、AlN、CuxS三者复合比例从45.2%(均热10 min)降为9.7%(均热240 min)。 The methods of electrolysis extraction from nonaqueous solution and scanning electron microscope were adopted to study the precipitation behavior of non-metallic inclusions in Si steel slabs during reheating processes.The morphologies,chemical compositions,quantity and size distribution of non-metallic inclusions in these steel samples were analyzed.Results show that,when the soaking temperature is 1 523 K,almost all of the non-metallic inclusions are smaller than 0.5 μm,few are in the range of ... 

针对新日铁公开的相关专利,总结日本高强度无取向电工钢的研究进展,分析了各专利化学成分、生产工艺及产品性能的特点,指出固溶强化、细晶强化、析出强化、位错强化都有可能被用来提高无取向电工钢的强度。在高强度无取向电工钢的研发过程中,需要根据其具体用途确定目标性能,再采用合适的强化手段,从而实现力学性能、磁性能和生产性能之间的平衡。 Authors summarize the research progress of high strength non-oriented electrical steel in Japan by learning related patents brought into the public by Nippon Steel. Authors also analyze the characteristics of the chemical composition, production technology and properties of products in the patents and point out that any ones of solution strengthening method, fine-grain strengthening method, precipitation strengthening method or dislocations strengthening method may be used to improve the strengt... 

采用中、厚板坯生产技术对取向硅钢进行了研制和开发,对热轧及后工序样品进行了金相组织观察和EBSD分析,探讨了两种组织及织构的差异性,研究结果表明:除高温退火样品外,中板坯生产的取向硅钢各工序样品平均晶粒尺寸大;厚板坯生产的取向硅钢热轧和常化样品亚表层Goss织构强;中板坯和厚板坯的脱碳退火板织构没有明显区别。中板坯生产的取向硅钢成本低,产品磁性能和质量与厚板坯相当。 Grain oriented silicon steel was researched and developed by medium thickness slab and thick slab.Microstructures observation and EBSD analysis to the samples of hot rolling and following processes were carried out,respectively.The differences between the two kinds of microstructures and textures were discussed.The results show that the average grain sizes of every process samples are larger except that of high temperature annealing samples of grain oriented silicon steel produced by medium thic... 

【作者】 张正贵； 李战库； ...

就冷轧硅钢废水处理生产中面临的主要问题进行分析,从技术角度及运行管理角度提出工艺优化升级改进措施及应对策略;同时从后续深度处理,逐步实现零排放目标的角度进行探讨,为冷轧硅钢废水减量化、出路乃至废水零排放提供一些思路。 The main problems in the wastewater treatment process of cold-rolled silicon steel lines are analyzed and process upgrading measures and optimization strategy are put forward from both technical and management views.At the same time,downstream deep treatment to gradually achieve the target of zero discharge is discussed,to provide some ideas for reduction or even zero discharge of wastewater from cold-rolled silicon steel lines.