通过热力学计算与模拟试验研究了含钒钛取向硅钢中氮化物析出相的析出规律与析出行为,并探讨了含钒钛元素的氮化物析出相作为薄板坯连铸连轧流程制备取向硅钢中辅助抑制剂的可行性.研究表明,在所冶炼的含钒钛取向硅钢的成分范围内,Ti N在钢液凝固末期便具备析出的热力学条件,而Al N与VN只可能在凝固后的α+γ或α+Fe3C两相区内析出.含钒钛取向硅钢中氮化物析出相以成分复杂的复合析出相为主,且随着钒钛加入量的增加,钢中抑制剂析出相总的分布密度由于含钒钛元素的氮化物析出相的增加而明显提高,使抑制剂抑制初次再结晶晶粒正常长大的能力得以加强,最终成品的磁感应强度值B8由1.857 T提升至1.898 T.同时,加入不高于0.007%的Ti与不高于0.005%的V不会影响中间脱碳退火工序的脱碳效果以及高温退火净化阶段硫、氮的脱除效果,其形成的含钒钛元素的纳米级氮化物析出相适合作为薄板坯连铸连轧流程制备取向硅钢的辅助抑制剂. The precipitation behavior of nitride precipitates in grain-oriented silicon steel containing vanadium and titanium elements produced by thin slab casting and rolling process was studied by thermodynamic calculation and simulation experiment. The feasibility of nitride precipitates containing V and Ti elements as auxiliary inhibitors was also investigated. It is found that Ti N is likely to precipitate at the final stage of solidification in the grain-oriented silicon steel,but VN and Al N can p... 

在实验室试制了TSCR流程的低碳低硅无取向硅钢,研究了在850～1050℃不同温度常化对冷轧量0.5mm厚钢板再经950℃×7min退火后的组织、织构和磁性能的影响。结果表明:随常化温度的升高,使热轧板晶粒尺寸增大,晶界更清晰,组织均匀性更好;由于第二相AlN和MnS析出物尺寸比较大,使冷轧退火后钢板晶粒也随常化温度升高呈单调增大趋势;γ有利织构和{111}、{112}不利织构与常化温度升高同时增强,但前者增强更多;冷轧板退火后铁损随常化温度升高呈单调下降,磁感呈单调上升趋势。 The low-carbon and low-silicon non-oriented silicon steel was prepared by thin slab casting and rolling(TSCR) in lab.The effect of normalizing at different temperatures in 850-1 050℃on microstructure, texture and magnetic properties of 0.5 mm cold-rolled sheets after annealing at 950℃for 7 min was researched. The results show that with increasing the normalizing temperature,the grain size of hot-rolled sheets increased,the grain boundaries were more clear and the rnicrostructure uniformity was b... 

通过对激光粒度分析仪测量硅钢级氧化镁(MgO)的分析条件进行优化,如分散介质、分散方式、样品预处理、仪器暗淡度等,探讨了硅钢级MgO粒度范围测量重现性较好的试验方法,满足硅钢生产过程控制对MgO粒度的要求。 The analysis condition of the laser particle size analyzer on grain oriented silicon-steel grade magnesium oxide is optimized,including the dispersion medium,dispersion methods,sample preparation,and instrument obscuration,etc.Therefore,particle size measurement with good reproducibility for silicon-steel magnesium oxide is discussed,which may meet the requirement of MgO particle size for silicon-steel process control. 

研究表明,硅钢中的夹杂物对成品带钢的磁性能有显著影响。为研究冶炼过程硅钢中的夹杂物遗传变化,进而提出更有效的控制措施加以去除,本文结合典型的无取向硅钢生产炉次,采用非水溶液电解提取+扫描电镜观察方法分析冶炼过程中上述炉次典型试样的夹杂物。结果表明:转炉冶炼结束、RH精炼开始时,钢的氧化物夹杂总量最大,约为0.23%;RH精炼过程中,氧化物夹杂总量不断降低,并在脱碳结束时达到最低,约为0.02%;连铸过程中,氧化物夹杂总量仍有不断降低趋势,但夹杂物的平均尺寸变化不大。本试验条件下,中间包试样的夹杂物数量约为1.59×104个/mm3。 As we all know, the non-metallic inclusion effects magnetic properties of silicon steel sheets obviously. The article aims to study the heredity of non-metallic inclusion in non-oriented silicon steels during the steel making process, and then provides a more effective controlling measure to remove the inclusions. Based on the typical non-oriented silicon steel charges, the non-aqueous solution extraction and SEM observation were adopted to analyze the non-metallic inclusions. Results show that,... 

研究了组织和析出物对高效电机用无取向硅钢退火板磁性能的影响。结果表明:随着退火温度升高,退火板平均晶粒尺寸增加,P15/50明显降低,B50略有升高。退火温度在1 000℃时,退火板的综合性能较好。析出物主要是AlN、(MnS+AlN)和(MnS+Al2O3)复合析出物,尺寸较粗大,主要集中在1.0～2.5μm,还发现少量百纳米以下的细小AlN和TiN。实验室模拟TSCR流程试制的高效电机用无取向硅钢,铁损平均值小于4.00 W/kg,磁感应强度大于1.75 T,适合作中小型高效电机铁芯材料。 Effects of microstructure and precipitation on magnetic property of non-oriented silicon steel sheets after annealing for high-efficiency motor are studied in the paper by experiments.The annealed sheet exhibits a larger average grain size,obviously decreasing iron loss and slightly raising magnetic induction with increasing temperature.The annealed sheet has better comprehensive properties at a annealing temperature of 1 000 ℃.The main precipitates are compounds of AlN、(MnS+AlN)and(MnS+Al2O3) w... 

研究了常化温度、常化时间及常化后冷却速度对Si的质量分数为1.6%的无取向电工钢成品磁性能的影响。结果表明:在850~1 050℃范围内,随着常化温度的升高,成品铁损先减小后增大,成品磁感应强度先增大后减小;当常化温度为1 000℃时,成品平均铁损最低,平均磁感应强度最高;常化时间从3min延长到7min时,成品铁损先减小后增大,成品磁感应强度则呈单调下降趋势;随着常化冷却速度的降低,成品铁损先减小后增大,成品磁感应强度则呈单调增大趋势;对于Si的质量分数为1.6%的无取向电工钢,最佳的常化制度为:在1 000℃进行常化,时间5min,常化后空冷。对热轧板进行常化后,热轧板发生了不同程度的再结晶和晶粒长大。提高常化温度、延长常化时间、降低冷却速度,都能使常化板晶粒粗化,进而粗化成品板晶粒,改善磁性能。通过扫描电镜观察发现,成品板中析出物主要为AlN和MnS的复合析出物,以及少量的单独析出的AlN和MnS,而常化工艺主要是通过粗化析出相,减少细小析出相数量,从而减少对晶界钉扎作用来改善成品磁性能。 The effects of normalizing temperature,normalizing time and cooling rate after normalizing on magnetic properties of non-oriented electrical steel with mass fraction of Si of 1.6% were investigated.The results show that core loss of product decreases first and then increases,while magnetic induction increases first and then decreases with the increase of normalizing temperature from 850 to 1 050℃.Average core loss of product is the lowest and average magnetic induction is the highest when normal... 

【摘要】 <正>日前,宝钢自主研发的新型高磁感取向...

【作者】 朱传芳； 潘恒韬； ...

概述了高磁感取向硅钢生产工艺的研究现状及发展趋势。介绍了国内外薄板坯连铸连轧流程生产高磁感取向硅钢的研究现状。从流程工序特点、热履历、组织与抑制剂控制方面进行对比,分析了薄板坯连铸连轧流程相对传统板坯流程生产高磁感取向硅钢的技术优势,在此基础上提出了利用该流程生产高磁感取向硅钢需要解决的主要技术难点。 The current status and development trend of production process for high magnetic induction grain-oriented silicon steel are summarized.The research status of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process at home and abroad is introduced.The potential technical advantages of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process are obtained by analyzing in terms of process characteristics,t... 

综述了退火温度、时间对无取向电工钢磁性的影响。退火温度主要影响无取向电工钢不同织构的占有率,退火时间主要影响晶粒尺寸的大小,晶粒尺寸的变化对织构的形成也有一定的影响。磁感最高点出现在纤维组织完全消失,(111)面织构组分较弱的组织状态。铁损的降低主要依赖于磁滞损耗的降低,织构的影响不大。 The effects of annealing temperature and time on the non-oriented electrical steel magnetic properties were reviewed.Annealing temperature and time mainly affects the different textures share and the grain sizes of non-oriented electrical steel respectively.Changes of the grain sizes also have a certain effect on textures formation.The highest point of the magnetic induction value in the fibrous tissue completely disappears and{111} plane texture has a lower state of the component content.Iron l...