【摘要】 针对采用含钒铁水生产无取向电工钢存在的铁水脱硫率低、转炉冶炼过程回硫量大、成品硫含量偏高的问题,通过对含钒钛铁水脱硫,减少转炉冶炼过程回硫以及RH脱硫技术等方面的研究,大幅度降低了电工钢成品硫含量。生产表明钢中w(S)=0.001 9%～0.006 9%,平均为0.004 2%;w(S)≤0.008%的比例达到了100%,且w(S)≤0.005%的比例也达到了91.43%。
【Abstract】 In cognizance of the problems of low desulphurization rate for hot metal,large sulfur-recovery in converter as well as high sulfur content in products in producing non-orientation electrical steel with vanadium-content hot metal countermeasures have been carried out.Sulfur content in non-orientation electrical steel is decreased obviously by way of study on technologies of desulphurization for hot metal with vanadium & titanium,sulfur-recovery control in converter and desulphurization in RH …
【关键词】 无取向电工钢；
铁水脱硫；
转炉回硫；
RH脱硫；
【Key words】 non-orientation electrical steel；
desulphurization of hot metal；
sulfur pick up in hot metal in converter；
desulphurization in RH refining；
铁水脱硫；
转炉回硫；
RH脱硫；
【Key words】 non-orientation electrical steel；
desulphurization of hot metal；
sulfur pick up in hot metal in converter；
desulphurization in RH refining；