本发明公开了一种提高薄板坯连铸生产高铝无取向硅钢可浇性的方法，在保证生产顺行、质量稳定的基础上，能使高铝无取向硅钢连浇炉数由10炉提高至16炉，在提高小时产量、降低生产成本方面效果显著。

研究了应用电感耦合等离子体质谱法(ICP-MS)测定硅钢中痕量铜和镍的分析方法。采用硝酸分解样品,通过内标校正和基体匹配消除了基体干扰的影响,同时根据测量时存在的质谱干扰情况,选择同位素65Cu和60Ni作为测定元素和通过调节仪器参数使双电荷离子的产率最低,以减少带来的干扰。该方法用于硅钢中痕量铜和镍的测定,所得的结果与ICP-AES法测定结果完全吻合,各元素测定结果的RSD值小于5%,加标回收率为97.3%～100.3%。 A method for the determination trace copper and nickel in silicon steel by inductively coupled plasma mass spectrometry(ICP-MS) was studied.The samples were dissolved in HNO3.The effect of matrix interference was eliminated by internal standard correction and matrix matching.Meanwhile,according to the mass spectral interferences in determination,the isotopes including 65Cu and 60Ni were used as measuring elements.The yield of double-charge ions were minimized by adjusting instrumental parameters... 

本发明公开了一种高牌号硅钢的穿带激光焊接方法，包括：将焊缝中硅含量降低到Si焊＜1.9%。采用激光+填丝焊接，填丝ER50‑6碳钢焊丝；根据焊缝截面积和激光焊接速度；激光填丝焊接时，激光线能量应足够大，达到填丝在熔池中充分混合，均匀分布，不至于填丝的成分浮在熔池的上半部分。采用此方法使焊缝组织从粗大铁素体变成细小、致密的无碳贝氏体，晶内沉淀相和晶间脆性相相对大幅减少，提高了焊缝韧性和成形性能，保证了高硅硅钢带的穿带焊接和连续生产。

一种低温高磁感取向硅钢的热轧方法：经转炉冶炼并浇注成坯；对铸坯加热后进行粗轧：首先确定粗轧减宽量；根据所确定的粗轧减宽量进行粗轧；进行精轧；常规进行下工序。本发明采用低温板坯加热技术，降低了板坯烧损和修炉负担，且边裂发生率比现有技术的不低于18%的基础上能降低5%以上，由此节约资源及降低能耗。

【作者】 王爱华； ...

电工钢反复弯曲次数是电工钢性能检验的重要指标之一,直接影响到用户在使用电工钢过程的机加工性能。主要分析了试样宽度、试样张力、晶粒取向、反复弯曲设备等因素对电工钢反复弯曲试验的影响,并对各个因素的影响程度进行量化以及原因探讨,从而归纳形成各影响因素的基本规律,以便为电工钢实际生产、用户使用提供科学指导。结果表明:试样宽度增加,反复弯曲次数也会不断增加,晶粒位向对取向电工钢的反复弯曲次数影响较大,当支座顶部到拨杆底部的距离减小或拉紧力增加时,反复弯曲次数会不断减小,但当拉紧力达到60N以上时,对反复弯曲次数影响不大,试样经退火后,反复弯曲次数略有上升。 The reverse bend number is an important performance of electrical steels′capabilities,affecting the machining performance directly when the customers used.It investigated some factors,such as sample′s width,sample′s tension load,grain orientation and equipment,how to effect the reverse bend test for electrical steel,measured the influence degree,and discussed the reason,in order to form basic rules which could be guided the manufacturing and using for electrical steel.Results showed that the rev... 

本发明公开了一种精确控制高磁感取向硅钢板坯Als含量的方法，转炉出钢20～40秒时，定量加入金属铝，加入量按0.15～0.35kg/吨钢；转炉出钢及合金加入后，底吹搅拌均匀3～5min后，加入一定量金属铝后再底吹搅拌均匀3～5min后将钢水吊运至RH开始精炼处理，铝加入量按[WAls目标+(0.009～0.0120％)]范围控制；钢水在RH精炼过程经过2～3次酸溶铝的成分微调后结束精炼，精炼结束Als按[WAls目标+(0.0030～0.0045％)]目标范围控制；RH精炼结束样酸溶铝检测结果出来后，在连铸开浇前，在钢包内补加铝线使钢液中Als在[WAls目标+Δ浇注Als损]目标范围内；连铸进行氩气环流保护浇注，其中氩气环流流量控制在6～12m3/h；浇注成合格板坯后按正常工艺进行热轧及后工序生产。

通过观察冲剪边缘组织,测量冲剪边缘的显微硬度、残余应力的分布情况和磁性能的变化研究了冲剪加工对无取向硅钢50WW800边缘组织和磁性能的影响。对冲剪后硅钢片进行750℃退火,分析退火对组织和磁性能的影响。结果表明,硅钢片剪切边缘会存在0.4 mm的形变硬化层,边缘应力大,铁损增加。退火后变形减小,形变硬化层变小,残余应力大幅度减少,铁损减少。 The influence of punching process on cutting edge microstructure and magnetic properties of non-oriented silicon steel 50WW800was studied by observing microstructure and measuring microhardness near cutting edge.The residual stress distribution in the silicon steel tooth and magnetic properties were measured.Effect of annealing at 750 ℃ on microstructure and magnetic properties of the silicon steel was analyzed.The results show that a cut-edge hardening layer up to 0.4 mm is observed,residual st... 

在50Kg氧化镁坩埚真空感应炉上进行高硅电工钢的脱氧试验。结果表明,通过控制原料的成分、高真空下的碳氧反应和炉衬分解向钢液中的供氧,可使钢液的总氧含量≤15×10-6;在维持高温高真空条件下,当钢液中的反应达到一定程度后,延长精炼时间并不能降低钢液的总氧含量;完成精炼后加入硅钙合金沉淀脱氧可进一步降低钢液的总含氧量,但脱氧效果有限。 The test of high-silicon electric steel deoxidation has been carried out in 50Kg vacuum induction furnace with magnesium oxide crucible.Results show that the total oxygen could be ≤15×10-6in molten steel by controlling material components,carbon-oxygen reaction in high vacuum and oxygen contamination from crucible materials on molten steel;And when the reaction was carried through to a certain extent,total oxygen in molten steel could not be reduced by the extension of refining period in high va... 

一种提高有效氮和底层质量的高磁感取向硅钢制造方法：冶炼后连铸成坯；对铸坯加热；热轧、常化及酸洗后时效冷轧；在湿式气氛下脱碳退火；在湿式混合气氛下均热；在湿式混合气氛下渗氮退火；进行后工序。本发明与现有技术相比，通过合理控制渗氮过程，提高渗氮后钢板基体内氮含量与总氮量之间的比例达到80%以上，使无点状露晶产生，最终获得产品的底层质量优异。

【作者】 康凌晨； 王丽娜； ...

本文中简要介绍了武汉钢铁有限公司采用薄板坯连铸连轧CSP(compact strip production, CSP)工艺生产中低牌号无取向硅钢的实践情况.CSP工艺生产的硅钢具有成品磁性均匀、板形好的优势，但是在利用该技术生产中低牌号无取向硅钢时，常存在成品板表面瓦楞状缺陷严重、连铸生产效率低等问题.通过优化炼钢成分、热轧等相关工艺，可消除热轧板厚度方向中心的粗大形变组织，从源头上避免了粗大{100}<011>纤维组织的出现，消除了瓦楞状缺陷；通过提升冶炼效率和控制钢中夹杂物总量，可优化隧道炉的加热温度与在炉时间，大幅度提升了连铸生产效率，实现了中低牌号无取向硅钢的批量稳定制造，使CSP产线成为中低牌号无取向硅钢热轧板原料的主要供给生产线.如何进一步提升钢水纯洁度、提高连铸生产效率、降低生产成本，以及挖掘该产线生产薄带钢的技术优点，是未来工作的重点. This paper briefly introduces the practice of producing medium and low grade non oriented silicon steel(NGO) with CSP(compact strip production, CSP)technology in Wuhan Iron and Steel Co., Ltd.. This technology has the inherent advantages of uniform magnetic properties and good shape for silicon steel finished strip. However, in the actual production process, there are serious corrugated defects on the surface of silicon steel finished strip, and production efficiency of continuous casting is low...