硅钢资料

Fe-6.5%Si高硅钢是一种具有高磁导率、低矫顽力和低铁损等优异软磁性能的合金,但是其室温脆性和低的热加工性能严重影响了其在工业领域的应用。综述了Fe-6.5%Si高硅钢的性能,评述了合金的改性法、特殊轧制法、快速凝固法、沉积扩散法、粉末冶金法等制备工艺。 It is well known that 6.5%Si high silicon steel is one kind of soft magnetic materials with higher re-lative permeability,lower coercive force and iron loss than those of conventional industrial silicon steel.However,their room-temperature embrittleness and poor workability limit their practical applications in the industry.The pre-paration technique such as modification treatment on alloy,special rolling,rapid solidification,CVD and powder me-tallurgy is reviewed. 

本实用新型涉及取向硅钢高温连续退火炉领域，尤其涉及一种取向硅钢高温连续退火炉隔离装置，包括安装在炉壳上的隔离炉门及设置在隔离炉门四周的密封井；隔离炉门顶部两侧安装有水冷却装置；水冷却装置上部设有隔离炉门动力牵引装置；密封井包括固定密封井和伸缩密封井，伸缩密封井位于固定密封井内部并与固定密封井滑动连接，伸缩密封井与固定密封井端部连接处设有密封装置。本实用新型可以确保隔离炉门升降过程中实现无缝全密封状态，提高密封效果，且采用伸缩密封井实际降低了密封井的高度，间接降低了水冷却装置连接管道上升至最高点的净空标高，与传统固定式密封井高度相比可以降低高度50％～80％，从而降低厂房净空标高，节省厂房基建投资。

本实用新型公开了一种取向硅钢绝缘涂液用废液回收利用装置，涉及取向硅钢绝缘涂液技术领域，为解决现有取向硅钢绝缘涂液的废液在回收时没有进行多层热分解，导致回收利用率低的问题。所述下料筒的下端设置有调节筒，所述调节筒的下端设置有分流筒，所述分流筒的下端设置有出料筒，所述调节筒的内部设置有下料板，所述下料板的一端设置有转轴，所述转轴的一端设置有交流电机，所述下料板的侧表面设置有外接孔，所述下料筒的筒壁内设置有加热板，所述下料筒的内部设置有一级过滤网，所述分流筒的内部设置有隔挡板，所述隔挡板的一侧设置有二级过滤网。

研究了常化温度、常化时间及常化后冷却速度对Si的质量分数为1.6%的无取向电工钢成品磁性能的影响。结果表明:在850~1 050℃范围内,随着常化温度的升高,成品铁损先减小后增大,成品磁感应强度先增大后减小;当常化温度为1 000℃时,成品平均铁损最低,平均磁感应强度最高;常化时间从3min延长到7min时,成品铁损先减小后增大,成品磁感应强度则呈单调下降趋势;随着常化冷却速度的降低,成品铁损先减小后增大,成品磁感应强度则呈单调增大趋势;对于Si的质量分数为1.6%的无取向电工钢,最佳的常化制度为:在1 000℃进行常化,时间5min,常化后空冷。对热轧板进行常化后,热轧板发生了不同程度的再结晶和晶粒长大。提高常化温度、延长常化时间、降低冷却速度,都能使常化板晶粒粗化,进而粗化成品板晶粒,改善磁性能。通过扫描电镜观察发现,成品板中析出物主要为AlN和MnS的复合析出物,以及少量的单独析出的AlN和MnS,而常化工艺主要是通过粗化析出相,减少细小析出相数量,从而减少对晶界钉扎作用来改善成品磁性能。 The effects of normalizing temperature,normalizing time and cooling rate after normalizing on magnetic properties of non-oriented electrical steel with mass fraction of Si of 1.6% were investigated.The results show that core loss of product decreases first and then increases,while magnetic induction increases first and then decreases with the increase of normalizing temperature from 850 to 1 050℃.Average core loss of product is the lowest and average magnetic induction is the highest when normal... 

本发明涉及硅钢板技术领域，尤其涉及一种硅钢板毛刺修整机，包括工作台，所述工作台顶端面的一侧通过升降座安装有打磨机构，工作台顶端的另一侧设置有连接柱，连接柱上部的一侧水平安装固定有横梁，横梁底端面的中部竖直安装有液压杆，液压杆的底端安装有打磨机构，且上、下两个打磨机构交错分布，本发明中通过上、下两个打磨机构的主打磨带对硅钢板的顶端面和底端面进行打磨，副打磨带对硅钢板的侧端面进行打磨，从而能够对硅钢板的水平端面以及侧端面同时进行打磨去毛刺，提高了硅钢板整体毛刺修整的效率。

本实用新型涉及切割设备技术领域，尤其涉及一种电工钢切片用切割刀架。其包括机架、升降架、第一输送辊、第二输送辊、升降块和切割装置；升降架和升降块均设置有两个；两个升降架均设置在机架上；两个升降块分别滑动设置在两个升降架上；第一输送辊的两端分别转动设置在两个升降块上；升降架上设置有用于驱动升降块移动的升降机构；第二输送辊转动设置在机架上，且第二输送辊位于第一输送辊的下方；机架上设置有用于驱动第二输送辊转动的驱动电机；第二输送辊上设置有用于驱动第一输送辊转动的传动机构；切割装置滑动设置在机架上；机架上设置有用于驱动切割装置移动的驱动机构。本实用新型能够方便对电工钢进行切割，且能够自动放卷。

{100}织构因具有两个易磁化方向能够明显的提高磁性能,因此如何在表面获得具有{100}织构一直是无取向电工钢研究焦点。本文主要介绍了获得{100}织构的主要工艺方法及其基本原理,并结合实际生产过程对各工艺方法的优缺点进行了分析;一方面,优化无取向电工钢的成分,降低碳、锰元素含量以避免脱碳退火和真空退火,简化生产工艺;另一方面,调节升温速度、降温速度和退火气氛,使{100}晶面的表面能或弹性应变能最低,制备具有{100}织构柱状晶组织的无取向电工钢是今后的发展方向。 Because { 100} texture has two easy magnetization directions,which can significantly improve magnetization properfies,how to develop { 100} texture is a focus for researchers and manufactures. In the paper,main manufacturing processes and basic principle are introdued,and their advantages and disadvantages in practical production are analyzed. On the one hand,the production process can be simplified by optimizing chemical compositions,such as reducing the content of C and Mn,which can avoid deca... 

针对某厂DMS森吉米尔轧机生产无取向硅钢表面麻面缺陷的问题，根据生产实际，对其形成原因从乳化液及工作辊两方面因素进行了分析。结果表明：乳化液对麻面缺陷的产生有一定影响，但不是主要因素，主要原因是由于二十辊森吉米尔轧机工作辊辊径较小，轧制相同长度带钢轧辊运转周期较大，容易产生疲劳失效而导致。为此，提出通过调整冷轧工序成品轧制道次的压下率以减小轧制力，从而减小工作辊的磨损疲劳；通过对轧制乳化液浓度、温度的合理控制，以改善润滑效果、提高轧制速度，而进一步缓解轧辊疲劳的改进措施，使该钢厂无取向硅钢麻面缺陷发生率由原来的18%降至0.8%,带钢表面质量明显改善。 For the problem of surface pockmarks of non-oriented silicon steel strip produced by a DMS Sendzimir mill, based on the production practice, the formation causes were analyzed from two aspects of emulsion and working roll. The results show that the emulsion has a certain effect on the formation of surface pockmarks defects, but it is not the main factor. The main reason is that the working roll diameter of the 20-high Sendzimir mill is small, and the running period of the roll rolling the same l... 

本发明提供一种超低铝无取向硅钢夹杂物控制方法。该钢种化学成分质量百分比为C≤0.005％，Si：0.25％‑1.50％，Mn：0.15％‑0.55％，P：0.02％‑0.06％，S≤0.005％，Als≤0.005％，余量为Fe及不可避免的杂质。工艺流程为：KR→BOF→RH→连铸。转炉出钢严格控制下渣量，出钢结束加石灰、渣面脱氧剂调渣；RH脱碳结束后，先加低碳低硫硅铁、金属铝或铝钙铁合金复合脱氧，最后加入金属锰、磷铁进行合金化，然后净循环6‑10min，破空出钢运至连铸浇注。得到钢水中主要为SiO2‑Al2O3系夹杂，避免了生成低熔点SiO2‑MnO系夹杂，轧制延展变长，影响晶粒长大；同时也避免了生成高SiO2组分类酸性夹杂，导致耐材的侵蚀。可显著改善钢中非金属夹杂物类型，提高无取向硅钢的性能，并提高了钢水浇注性能。

对低温法生产的以AlN为主抑制剂的Hi-B取向硅钢高温退火过程进行了中断实验,借助EBSD及TEM技术对高温退火连续升温过程中织构与析出物的演变进行了研究。实验结果表明,800℃时ODF图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;950~1 000℃时高斯晶粒异常长大,偏离角3~6°;高温退火过程析出物主要有球形、规则立方形及不规则多面体形3种形貌,由于渗N的影响,Zener因子先增大再减小,并且析出物在高斯晶界前沿优先粗化。 The annealing process at high temperature of Hi-B silicon steel using low slab reheat temperature and with AlN as the inhibitor has been studied by interrupting test,and the evolution of texture and precipitates during continuous heating-up in the annealing process at high temperature was analyzed by EBSD and TEM. The results showed that Goss texture appears in ODF at 800 ℃,but the intensity of Goss texture was very weak and the deviation angle was more than10°. Goss grains grow abnormally durin... 

本实用新型公开了一种铁芯硅钢片移动夹具，包括底板，所述底板上表面固定连接有固定板，所述底板的后表面固定连接有支撑腿，右侧所述支撑腿的前表面固定连接有转轴，所述转轴的外表面转动连接有转动板，所述底板的上表面且位于固定板的右侧固定连接有支杆，所述底板的上表面且位于支杆的右侧固定连接有第一电机。本实用新型，通过设计转动板、第一绳索与第二伸缩杆，实现在转移硅钢片时，将其竖直排列，增加其抗弯能力，通过设计第一伸缩杆与限位块，实现其在移动的过程中避免相互摩擦，达到保护硅钢片的目的，通过设计滑动板、第二伸缩杆、支撑板，实现在上下转运的过程中，仅有上侧进行接触，且呈三角形更加稳定。

采用电解法和扫描电镜研究了300 t转炉-RH精炼钙处理对无取向硅钢板（%:≤0.005C、1.2～2.2Si、0.2～0.6Mn、≤0.20P、≤0.005S、0.2～0.6Al、0～0.01Ca）中夹杂物的影响。结果表明,钢中Al含量为0.25%和0.35%时,钢中溶解氧均小于1×10^-4%,钙处理后都会产生CaS夹杂物,尤其是含0.35%Al的钢水;钙处理可以有效减少钢中的夹杂物数量,尤其是0.5μm以下的微细夹杂物数量;钙处理后夹杂物的种类以AlN、CaS为主,同时还含有少量的氧化物夹杂物以及AlN-CaS复合夹杂物,尺寸主要为1.5～5.0μm。 The effect of 300 t converter-RH refining calcium treatment on inclusions in non-oriented silicon steel sheet （%:≤0.005C,1.2～2.2Si,0.2～0.6Mn,≤0.20P,≤0.005S,0.2～0.6A1,0～0.01Ca） has been studied by electrolysis and scanning electron microscope.Results show that with 0.25%and 0.35%Al content in steel,all the dissolved oxygen in liquid is less than 1×10^-4%,and the CaS inclusions are produced after calcium treatment,especial for the liquid containing 0.35%Al;the amount of inclusions in ste...