对低温法生产的以AlN为主抑制剂的Hi-B取向硅钢高温退火过程进行了中断实验,借助EBSD及TEM技术对高温退火连续升温过程中织构与析出物的演变进行了研究。实验结果表明,800℃时ODF图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;950~1 000℃时高斯晶粒异常长大,偏离角3~6°;高温退火过程析出物主要有球形、规则立方形及不规则多面体形3种形貌,由于渗N的影响,Zener因子先增大再减小,并且析出物在高斯晶界前沿优先粗化。 The annealing process at high temperature of Hi-B silicon steel using low slab reheat temperature and with AlN as the inhibitor has been studied by interrupting test,and the evolution of texture and precipitates during continuous heating-up in the annealing process at high temperature was analyzed by EBSD and TEM. The results showed that Goss texture appears in ODF at 800 ℃,but the intensity of Goss texture was very weak and the deviation angle was more than10°. Goss grains grow abnormally durin... 

本实用新型公开了硅钢片生产用上料装置，属于硅钢片生产领域，包括本体，所述本体包括侧板和U型板，所述侧板固定连接在U型板的一侧，所述本体的顶部横向设置有平移机构，所述平移机构上安装有气缸，所述气缸的底部安装有吸盘，所述U型板内腔的底部竖向固定连接有弹簧，所述弹簧远离U型板的一端水平固定连接有升降板，所述平移机构包括电机、螺纹杆、限位板和移动块，所述电机安装在侧板的顶部，所述电机的输出轴与螺纹杆的一端固定连接，通过设置弹簧，在第一个物料从上料装置移出后弹簧的弹力推动剩余物料，使得剩余物料进行上升，避免吸盘触碰不到物料的问题，简化吸盘移动轨迹，加快上料速度。

冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content 、high added value product. Its process is complex, its production cycle is of length, and its process control is difficult, which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, which directly determines iron loss of the silicon steel and electromagnetic property,as well as other many index. 

本实用新型公开了一种硅钢片立式送料装置，包括装置主体，装置主体上方安装有固定板架和活动板架，固定板架和活动板架上方均安装有料架，固定板架通过螺栓固定在装置主体的上方，活动板架滑动安装在装置主体的上方；装置主体内部位于固定板架和活动板架的下方安装有推料板，本实用新型适用于硅钢片生产，该装置通过将其中一个料架安装安装在活动板架的上方，而装置主体的两侧上方开设有滑槽，滑槽沿装置主体的长度方向开设，活动板架采用倒“U”型结构，活动板架的两个竖直端滑动卡合在滑槽内，这样的结构设置使得活动板架能够在水平方向移动调整位置，从而使两个料架的间距可调，使该装置能够适用于不同大小型号的物料使用。

本发明公开了一种低损耗宽料取向硅钢的生产方法。本发明所述生产方法是通过在罩式炉的内罩中增加带有通气孔的聚气罩及与聚气罩配合的炉底板，配合工艺优化，控制原料化学成分，使气体和钢卷之间的浓度更均匀，反应更充分，气流流动方向更易控制，所制备的取向硅钢性能稳定，磁性能优良，且铁损达到1.12W/KG以下的比例提高至98.77％，平均铁损达到1.06W/KG以内，使取向硅钢卷的铁损大幅度降低，电磁性能更好。

本实用新型涉及风电磁钢盒技术领域，且公开了一种风电磁钢盒高精度加工模具，包括上模和下模，上模位于下模的上方，下模的前侧通过多个螺栓螺纹连接有安装板，安装板的前侧固定设有两个对称设置的固定板，两个固定板之间固定设有固定杆，固定杆的杆壁两端均通过第一转动轴承转动连接有套筒，套筒的两侧均开设有环形槽，两个环形槽的槽壁内部均设有限位机构，两个固定板相靠近一侧均开设有四个呈四角对称设置的插孔，套筒的两端均通过套环固定设有环形板，环形板的两侧均开设有滑槽，两个滑槽之间设有推动机构。本实用新型能够消除风电磁钢盒加工过程中人工将板件送至模具之间所带来的的危险。

薄带连铸流程下取向硅钢粗大λ晶粒(〈100〉//ND,normal direction)的“遗传”会导致磁性能恶化.为解决这一问题，针对取向硅钢的热轧孪生行为开展研究，结果表明：凝固组织粗大的取向硅钢在650℃热轧时可产生大量{112}〈111〉形变孪晶，这与具有高层错能的硅钢在较高温度下难以孪生变形的传统认知不同.热轧过程中复杂的应力状态降低了变形孪晶的取向依赖性，由于具有更高的储存能，孪晶界/孪晶界及孪晶界/晶界交叉点成为再结晶形核的优先位置，大大提高了常化过程中的再结晶率，受沿孪晶界应变分布及孪晶间距离的限制，沿孪晶界形核的再结晶晶粒通常呈“饼状”,最终形成以细小且取向漫散的再结晶晶粒为主的常化组织，消除了初始凝固组织中有害的粗大λ晶粒. In strip casting grain-oriented silicon steels, the inheritance of coarse λ grains(〈100〉//ND, normal direction) can deteriorate their magnetic properties. To solve the problem, twinning behaviors in strip casting grain-oriented silicon steels during hot rolling were investigated in this work. It is found that after rolling at 650 ℃, a number of {112}〈111〉deformation twins are formed in the coarse solidification microstructure of the steels, in contrast to the well-accepted view that it is diffic... 

本实用新型公开了一种硅钢板带加工用表面成型设备，包括底座，所述底座的上端固定连接有底部支撑架，所述底部支撑架的上端固定连接有机体，所述机体的上端固定连接有密封盖。本实用新型在打磨过程中，水泵可以将过滤箱内的冷却液通过进液机构上的进液管泵入到进液机构内，再经过进液孔进入到第二转轴内，再进入到打磨辊筒内，最后经过喷头喷到钢带表面，对钢带表面进行冷却，且可以将打磨下来的粉末带走，防止粉末飘散；冷却在喷出后，经过集液斗的收集，进入到过滤箱内，在过滤箱内设置过滤网可以对冷却液进行过滤，从而可以对冷却液进行重复使用。

本实用新型涉及一种具有在线测量功能的电工钢片横剪线，包括床身，床身上沿其长度方向安装有导轨，电工钢片在外部驱动辊带动下以导轨为导向移动；位于导轨一端端头外部的床身上安装有测量辊组件，位于导轨另一端处的床身上安装有影像测量组件；测量辊组件、导轨和影像测量组件的中心位于同一直线上，影像测量组件横跨设置于导轨上方；位于测量辊组件和影像测量组件之间的床身上依次安装有冲孔组件、V冲组件和斜剪组件；本实用新型通过测量辊组件对电工钢片行进长度进行检测，通过影像测量组件对电工钢片成型尺寸进行检测，从而便利于及时调整横剪线整体的运行状态，有效助力于保证合格率，并降低了人工负担。

本发明涉及变压器的技术领域，特别是涉及一种应用电工钢的变压器，其通过设置扇叶与冷凝盘管，通过冷却液与风冷共同对电工钢铁芯进行降温，避免电工钢铁芯工作过热导致电工钢铁芯损坏，提高使用稳定性；包括变压器箱体、两组固定支撑腿、电工钢铁芯、固定卡块、风机支架、风机、扇叶转轴、扇叶、冷却箱体、循环泵、冷却管、冷凝盘管、冷风机支架和冷风机，所述变压器箱体内部设置有空腔，所述变压器箱体右端连通设置有散热口，两组所述固定支撑腿对称固定安装在变压器箱体内部，所述固定支撑腿内端设置有紧固卡槽，所述电工钢铁芯左右两端对称固定安装有两组固定卡块，所述固定卡块固定卡装在固定支撑腿紧固卡槽中。

本发明揭示了一种无取向硅钢及其生产方法。所述生产方法包括：按照Si0.8～1.1％、Mn0.2～0.4％、不添加Sn和Sb进行炼钢，并制坯；将铸坯加热到1060～1120℃并保温150min以上，而后轧成厚度40～45mm的中间坯，再经精轧、卷取得到厚度为3.00±0.25mm的热轧卷板，精轧开轧温度≤872℃+1000*(11*[Si]‑14*[Mn]+21*[Al])；精轧终轧温度≤820℃，卷取温度≤560℃；常化、酸连轧，得到厚度为0.500±0.005mm的冷硬卷，常化温度850～900℃；成品退火温度820～880℃，退火后经冷却、涂层和精整，得到无取向硅钢。

本实用新型公开一种硅钢片卷料悬吊上料装置，包括装配架，装配架之间装配有若干个左右间隔设置的硅钢片卷料限位装置，所述硅钢片卷料限位装置用于装载硅钢片卷料、装配架包括前后对称设置的架板，所述架板上具有矩形凸出端、前、后部位之间所述矩形凸出端之间装配有若干个左右间隔设置的长螺杆、长螺杆贯穿所述硅钢片卷料限位装置，所述长螺杆的端部螺纹连接有螺母、架板的底部固定连接有两个左右间隔设置的轮架杆，所述轮架杆的左右两端均转动连接有滚轮、轮架杆之间固定连接有C形架杆，所述C形架杆上固定连接有悬吊环体，实现将大量生产加工使用的硅钢片卷料进行上料。采用上述方式不仅实现将大量生产加工需要的硅钢片卷料进行输送。