本发明公开了一种硅钢环形炉内罩的内圆直径自动检测装置及方法，该内圆直径自动检测装置包括设置在检测点地面上的水平工作台，设置在所述水平工作台上的水平调节机构，设置在所述水平工作台上的扫描机构，以及与所述扫描机构通信互联的检测处理机构。该内圆直径自动检测装置是非接触式设备，不受内罩温度的限制，使用方便灵活，设备可靠性好，安全性高，对环境无污染，不仅能够有效节约校圆机的使用频次，而且大大增强了炉子的安全可靠性。

在实验室模拟CSP流程制备了不同含量稀土铈(质量分数0~0.018%)的1.2%Si无取向电工钢,并对其进行1 000℃×5min的再结晶退火处理,研究了铈质量分数对无取向电工钢夹杂物、显微组织、再结晶织构和磁性能的影响。结果表明:随着铈质量分数的增加,微细夹杂物数量、再结晶晶粒尺寸、{100}和{110}织构组分、磁感应强度先增后减,{111}织构组分、铁损先减后增;铈的质量分数为0.005 1%时,钢中的夹杂物数量最少,再结晶晶粒尺寸最大,有利织构最多,磁性能最优,铁损P15/50为3.253W·kg-1,磁感应强度B50为1.751T。 Non-oriented electrical steels containing different contents rare earth Ce element(0-0.018wt%) were prepared in the laboratory by simulated CSP(compact strip production)process,and then recrystallization annealing at 1 000 ℃ for 5 min were performed,the effects of Ce content on inclusion,microstructure, recrystallization texture and magnetic properties of non-oriented electrical steels were studied.The results show that with the increase of Ce content,the amounts of fine inclusion,the size of re... 

【摘要】 <正>编号:2012016获奖等级:特等完成单位:...

以市场上购买的取向硅钢成品板为原料，经不同压下率冷轧至0.23～0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量，利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征，分析了硅钢超薄带的塑性变形行为。结果发现，在平面压缩应力下，{112}<111>滑移系的取向因子较大。随冷轧压下率的增加，Goss织构的含量逐渐减少，{212}<141>织构组分的含量先增加后减少，{111}<112>织构组分的含量逐渐增加，织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶，其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。 The commercial finished oriented silicon steel plate as the raw material were rolled to 0.23-0.08 mm. With the X-ray diffractometer(XRD), the texture components and their volume fractions in the cold-rolled samples were detected. And the orientation factor distribution of the cross-section of the samples was measured by the electron backscattering technique(EBSD). The morphology and crystallographic characteristics of twins were observed, and the plastic deformation behaviors of the ultra-thin o... 

本实用新型公开了一种硅钢片冲压模具，包括上模和下模，上模和下模之间通过导向杆连接，下模上设有出料槽，出料槽的底部设有一磨盘，磨盘通过齿轮连接电机。本实用新型结构设计合理巧妙，当硅钢片冲压下落时，磨盘通过电机带动转动，对硅钢片的周围进行打磨，使硅钢片边缘平整，叠铆时上下不易错位。

本实用新型提出了一种非取向极薄硅钢带刮油装置，包括机壳、固定架、第一安装板及第二安装板；机壳内侧设有固定架，固定架上端设有第一承托板，第一承托板上方设有第一安装板，第一安装板上至少设有一个上刮油刀片，第一安装板与第一弹簧下端连接，第一弹簧上端与机壳顶端相连接，固定架下端与第二弹簧上端连接，第二弹簧下端连接第二安装板，第二安装板上至少设有一个下刮油刀片，机壳底部设有第二承托板，第二承托板与下刮油刀片对应设置；上刮油刀片和下刮油刀片一端设有固定安装孔，另一端均设有斜面。本实用新型的刮油刀片通过弹簧自适应抵接于厚度不同的硅钢带表面，清洁效果好，设计结构简单，维护方便，可循环利用，降低了生产成本。

研究了退火温度和退火时间对电沉积硅钢试样中的断面层组织、硅在试样中的分布情况、织构分布和磁性能的影响。结果表明:退火温度为1000℃、退火时间为210 min时得到的试样晶粒分布均匀、硅在试样中分布均匀、硅平均浓度为6.3715%(接近6.5%)。试样的织构分析及磁性能检测的结果表明,在较高温度下延长退火时间可增加{100}和{110}面织构,降低铁损,所得试样的磁性能较为良好。 The effect of annealing temperature and time on the microstructure, distribution of silicon,texture and magnetism of the high silicon steel prepared by electrodeposition was investigated. The results showed that after annealing at 1000℃ for 210 min, the mean grain size of steel was about 190 μm with a uniform grain size distribution, and the silicon is also uniformly distributed on the entire cross section with an average Si concentration 6.3715%(close to 6.5%); With the increasing annealing tim... 

采用固溶强化、细晶强化和位错强化方法,模拟TSCR流程试开发高强度无取向电工钢,试开发钢的主要合金成分为3%Si、0.83%Al和2.99%Mn。分析热轧、常化、退火后的钢板组织,并针对不同的成品板组织,详尽地分析了相应的力学性能和磁性能。试验电工钢平均晶粒直径为12.37μm时,R p0.2为530 MPa,R m为618 MPa;当退火制度为700℃×4 min,成品组织完全为未再结晶的回复组织时,R p0.2为853.5 MPa,R m为895.5 MPa。该成分的电工钢P15/50或P10/400最小时,对应的平均晶粒直径都大于59.67μm;P10/800或P10/1000最小时,对应的平均晶粒直径都处于12.37~59.67μm尺寸区间。 TSCR was simulated to develop high-strength non-oriented electrical steel with 3% of Si,0.83% of Al and 2.99% of Mn by solution strengthening,grain refinement strengthening and dislocation strengthening.The microstructures of hot rolled plates,normalized plates and annealed plates were analyzed.Furthermore,the mechanical properties and magnetic properties of products with different microstructures were detailedly studied.As the average grain diameter of the steel was 12.37 μm,the yield strength ... 

本发明提供一种无取向硅钢用涂层溶液及其制备方法和应用，以所述无取向硅钢用涂层溶液的总质量为基础计，所述无取向硅钢用涂层溶液包括如下质量百分含量的原料组分：磷酸盐溶液55％～60％；树脂溶液20％～25％；二乙二醇丁醚2％～4％；改性剂3％～5％；余量为水。由本发明所述无取向硅钢用涂层溶液形成的绝缘涂层厚度均匀，表面光滑，具有优良的绝缘性、耐腐蚀性、附着性，而且硅钢片的冲片性能好、叠片系数高。

本实用新型涉及变压器材料检测技术领域，具体为一种硅钢片检测装置，包括材料检测装置主体，材料检测装置主体包括相互连接的铁损测试仪主机及磁导计，磁导计的顶端设置有清洁机构，清洁机构包括固定盒、拉块及刷块，固定盒固接于磁导计上，拉块插设于固定盒中、能够在固定盒中上下移动，固定盒的内部底面上及拉块的底端上分别安装有刷块，铁损测试仪主机上还设有束线机构。本实用新型使得用户可在检测硅钢片前，对硅钢片两面沾染的灰尘污渍进行擦拭，避免灰尘污渍影响对硅钢片的测定结果，可方便地对刷块进行清洁更换，使得用户可方便地对电源线和导线进行收纳。

本实用新型涉及一种硅钢卷用放料架，属于硅钢卷放料技术领域。包括底板、升降台、支撑座、旋转座、固定轴、内限位块、轴套和外挡块，所述底板上设有升降台，升降台上设有支撑座，支撑座上设有旋转座，旋转座上对称设有两组固定轴，所述固定轴内侧固定有内限位块，其外侧设有可拆卸的外挡块，所述轴套安装在内限位块和外挡块之间的固定轴上且可相对固定轴转动；本实用新型采用升降台，方便人工将笨重的硅钢卷轻松的装入固定轴上，通过可拆卸的外挡块固定，安装快捷，节省人力，安全可靠。

本发明公布了以铜析出粒子为抑制剂的一类取向电工钢及其生产方法，所述取向电工钢化学成分的质量百分比为：C：0.001％～0.07％；Si：2.5％～3.5％；Si+Mn+Al：≤3.5％；Cu：1.0％～2.0％；S：≤0.003％；N：≤0.0045％；其余为Fe和不可避免杂质元素。该取向电工钢的生产工艺步骤可以包括：连铸坯板坯加热、热轧、常化、冷轧、脱碳处理、时效处理、二次再结晶退火处理等。本方法免除了高温热轧加热和二次再结晶后高温长时间加热以净化钢板基体的退火环节，进而可实现连续式二次再结晶退火，大幅度降低了生产能耗，并显著提高生产效率。