研究了热处理工艺(退火温度、保温时间、冷却方式)对含Mn的Fe-6.5wt%Si高硅钢热轧带的显微组织及硬度的影响。结果表明,退火温度对Fe-6.5wt%Si合金的组织和显微硬度均有较大影响,随退火温度升高,平均晶粒尺寸和显微硬度均明显增大。小于1 h退火时,晶粒长大缓慢,而长时间(>1 h)退火时,一些次表层晶粒将发生异常长大。水冷组织比空冷组织略细小,但水冷显著降低了显微硬度。Mn含量提高能抑制850℃退火时晶粒的长大,并且促进退火后高硅钢的软化。 The influences of heat treatment process(annealing temperature,heating time,cooling methods) on the microstructure and microhardness of Fe-6.5wt%Si high silicon steel containing manganese for hot rolled strip were studied.The results show that the annealing temperature has a great effect on the microstructure and microhardness of Fe-6.5wt%Si alloy,and as the annealing temperature increases,the average grain sizes and microhardness will significantly increase.When annealing time for less than 1 h... 

根据本发明的一个实施例的取向电工钢板的制造方法，其包含：对板坯进行热轧，以制造热轧钢板的步骤；对热轧钢板进行热轧板退火的步骤；对热轧板退火后的热轧钢板进行一次冷轧的步骤；对一次冷轧后的钢板进行一次脱碳退火的步骤；对完成脱碳退火的钢板进行二次冷轧的步骤；对完成二次冷轧的钢板进行二次脱碳退火的步骤；以及对二次脱碳退火后的钢板进行连续退火的步骤。

通过测试取向硅钢不同工艺条件下的碳含量,探讨了CGO取向硅钢碳含量控制的最优处理条件,研究了脱碳温度和脱碳时间对相同初始碳含量取向硅钢的脱碳效果的影响。结果表明,在气氛为(15%~20%)H2+(75%~80%)N2,炉压差为10~20 Pa的条件下,CGO取向硅钢合适的脱碳温度为1 073 K~1 123 K,脱碳时间为10~20 min。在该处理条件下,能取得较好的脱碳效果。 By means of testing carbon content of oriented silicon steel below the distinct technical conditions,inquires the excellent handle terms of carbon content controlling for CGO oriented silicon steel,studies effects of decarburization annealing temperature and decarburization annealing time to the oriented silicon steel decarburization efficiency in same initial carbon content.The results show that,under the condition of atmosphere(15% ~ 20%) H2+(75% ~ 80%)N2 and furnace pressure difference 10 ~ 2... 

研究了无取向硅钢钙处理前后夹杂物的行为,重点考察了钙处理前后夹杂物的成分、类型、形貌和尺寸研究的变化情况,为实际生产中无取向硅钢的钙处理提供理论指导。试验发现:钙处理前夹杂物主要以Al2O3、Al2O3-MgO为主,且在夹杂物表面有AlN析出,钙处理后夹杂物以Al2O3-MgO-CaS-CaO系复合夹杂物为主,还含有少量的SiO2或AlN;钙处理前后,夹杂物形貌由多边形或不规则形逐渐向球形或近似球形转变,并且夹杂物尺寸不断增大;钙处理前后,含钙夹杂物的比例发生突变,由10%增大到74.5%,且随着钙处理时间的延长,含钙夹杂物比例下降,表明钙处理使夹杂物变性后易聚集长大并上浮去除。 Behavior of inclusions before and after calcium treatment in non-oriented silicon steel was researched by investigating changes of compositions,types,shapes and sizes of inclusions before and after calcium treatment,for the purpose of providing theoretical guidance for calcium treatment of non-oriented silicon steel in actual situation. Results indicated that Al2O3 and Al2O3-MgO were main types of inclusions before calcium treatment,sometimes AlN maybe precipitate in the outer of inclusions. Al2... 

本发明属于涂料技术领域，具体公开了一种用于取向硅钢的无铬无机绝缘涂料，包括以下重量份配比的原料：小颗粒硅溶胶10‑50份、大颗粒硅溶胶10‑50份、磷酸二氢铝溶液5‑50份、助剂0.1‑10份及水10‑100份。本发明还提供了一种用于取向硅钢的无铬无机绝缘涂料的制备方法，通过将小颗粒硅溶胶和大颗粒硅溶胶混合均匀成硅溶胶混合液后加水得到混合硅溶胶水溶液；再依次向其中加入磷酸二氢铝和助剂并持续拌至均匀，得到用于取向硅钢的无铬无机绝缘涂料。本发明提供的无铬无机绝缘涂料适用于取向硅钢，使取向硅钢环保无害的同时具有与含铬取向硅钢相当的耐腐蚀时效，从而实现取向硅钢产业绿色化并大大改善取向硅钢的综合性能。

对1990~2010年在我国申请的冷轧无取向硅钢涂层的专利数量、专利技术领域分布进行了统计,对典型涂层专利技术进行了分析,探讨了无取向硅钢涂层的发展趋势。统计分析结果表明,目前无取向硅钢涂层典型的专利技术主要有自粘结涂层、无铬含稀土元素涂层、含钼酸盐环保涂层及采用有机-无机纳米杂化材料为主成膜物形成的涂层等。无取向硅钢涂层发展的趋势主要是无铬环保的半无机、半有机型涂层。 The patent quantity of cold-rolled non-oriented silicon steel coating and distribution of technology fields applied in China in 1990-2010 were summarized.The analysis results indicate that typical patent technologies include self-adhesion coating,chromium-free and with rare earth element coating,environment-friendly and with molybdate coating,coatings with organic-inorganic hybrid materials as main forming agent and so on.The main development trends of coatings on silicon steel are among semi-in... 

研究了卷取工艺对一种新型含铜无取向电工钢晶粒尺寸、织构演变、铁损和磁感应强度的影响。结果表明,试样织构组分主要为{111}、{112}、{100}和高斯织构,在550℃卷取、保温2～3h,{100}织构有增强趋势,磁感应强度较高,铁损较低。 The effects of coiling process on grain size,texture,core loss and magnetic induction of a new cold rolled non-oriented electrical steel with copper were investigated.The results show that there are mainly {111},{112},{100} and {110}<001> texture.Coiling at 550℃and keeping for 2～3 hours,the {100} texture is enhanced,magnetic induction is higher and core loss is lower. 

采用光学显微镜、X射线衍射仪等分析了宁波钢铁有限公司生产的取向硅钢不同工序下的组织及织构演变规律。结果表明:铸坯经过热轧后,沿着厚度方向组织不均匀;一次冷轧并经脱碳退火后,组织由条状纤维状变成等轴状的初次再结晶晶粒,初次再结晶平均晶粒尺寸为18.17μm,织构主要以α织构和γ织构为主;在二次冷轧后,晶粒再次被压缩,转变为纤维状,织构主要为γ织构;经过高温退火后,发生二次再结晶,晶粒异常长大,晶粒尺寸达到厘米级,织构成分为单一且锋锐的Goss织构。 The microstructure and texture evolution of oriented silicon steel produced by Ningbo Iron and Steel Co.,Ltd.were analyzed by optical microscope and X-ray diffraction.The results showed that the microstructure of the slab was inhomogenous along the thickness direction after hot rolling.After first cold rolling and decarburizing annealing,the microstructure changed from strip fibrous to equiaxed primary recrystallized grains,and the average grain size of the primary recrystallization microstructu... 

本发明公开了一种基于机器视觉的高牌号冷轧硅钢孔洞检测系统。该系统包括：线扫光源、线阵相机、速度检测模块和工控机；线扫光源安装在钢板生产线中钢板的下方，且线扫光源的光线能够对准钢板和线阵相机；线阵相机安装在钢板的上方，且与工控机连接，用于连续扫描钢板以获取连续的钢板图像；速度检测模块与线阵相机连接，用于检测钢板的移动速度，线阵相机能够根据钢板的移动速度调整行频；工控机用于根据钢板图像检测钢板是否存在孔洞。本发明的基于机器视觉的高牌号冷轧硅钢孔洞检测系统通过利用线阵相机和工控机能够实现冷轧钢板的孔洞的自动检测，检测效率高，识别精度高，能够降低漏检率和误检率，操作方便，安全可靠。

本发明是改善硅钢边缘裂边的工艺，包括：S1：对普通取向硅钢卷进行放卷、活套、清洗、加热、冷却；S2：对硅钢进行收卷，收卷张力系数为3‑9kg/mm2；S3：对硅钢卷用收紧带收紧打包，打包带张力为3‑8kg；S4：罩式炉进行炉底板检测，炉底板不平度＜2mm；S5：将收紧打包后的硅钢卷送入罩式炉内进行高温退火处理；本发明的优点：通过调整取向硅钢材料生产过程中对CA线收卷张力的控制、CA收紧带的使用与控制、罩式炉炉底板的平整度，实现1200mm以上宽度材料平均不良切边宽度≤45mm，边部裂边尺寸减少40％。有效提高了加工材料成材率，提高了纵剪材料使用率，降低了吨钢成本，减少了纵剪生产停顿，提高了效率。