硅钢资料

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

利用OM、TEM与EDS技术,对Fe-3.2%Si低温取向硅钢热轧板进行不同常化冷却工艺处理后的显微组织、析出相及最终产品的磁性能进行分析,并与热轧板的组织和析出相进行对比。结果表明,常化板较热轧板的表层组织均匀,基体中再结晶比例增加,带状组织变窄;常化板中析出物的数量明显比热轧板的多,析出物主要有AlN、MnS及复合析出的(Cu,Mn)S等。在常化温度1120℃、保温3 min的条件下,采用二段式冷却较空冷、淬沸水、淬常温水的冷却工艺,常化板表层显微组织更均匀,沿板厚方向的显微组织的不均匀性显著,取向硅钢的磁性能最高;常化后采用二段式冷却工艺析出的细小析出物数量最多,且弥散分布在基体中,抑制剂的抑制效果最好,对成品获得高磁性最有利。 Microstructure, precipitate and magnetic characteristic of final products with different normalizing cooling processes for Fe-3.2%Si low-temperature hot-rolled grain-oriented silicon steel were analyzed and compared with the hot-rolled plate by optical microscopy(OM), transmission electron microscopy(TEM), and energy dispersive spectrometry(EDS). The results show that, the surface microstructure is uniform, the proportion of recrystallization in matrix increases, and the banding textures are nar... 

本发明涉及取向硅钢制造技术领域，公开了一种快速判断取向硅钢初次再结晶晶粒直径的方法，包括如下步骤：选取取向硅钢热轧来料，进行生产，对产出的钢板在同部位各取若干个拉伸试样，加工拉伸和分析，取得屈服强度，在拉伸试样部位两侧连续制取金相试样，计算对应拉伸试样的平均晶粒直径D，将性能数据和平均晶粒直径进行统计分析，建立屈服强度与晶粒直径的对应关系，实际生产时，在产出的钢板上取判断试样，取得判断试样的屈服强度，进而取得判断试样的晶粒直径。本发明快速判断取向硅钢初次再结晶晶粒直径的方法，通过机械性能检验，来间接指示初次晶粒的大小，检测速度快，评价更准确。

本发明涉及收卷装置技术领域，且公开了一种用于硅钢片横剪线的卷料自动上料装置，包括底座，所述底座顶端固定连接有底托，所述底托的顶端活动连接有外筒，所述外筒的中间通过轴承活动连接有阻力轴，所述阻力轴的正面固定连接有内筒，所述内筒外侧与外筒内侧的中间活动连接有连轴，所述连轴的中间固定连接有送料电机，所述送料电机的一侧固定连接有卷轴卡辊。本发明将原本固定式卡辊及送料电机，设置为可绕外筒内壁进行移动的活动式卡辊，在进行上料时通过外筒将卷轴卡辊旋动至底端进行直接上料，无需停机替换，提高了卷料替换的连续性，同时避免了使用吊车进行吊装过程中吊装不稳定造成的上料精度不高和卷轴掉落损坏等问题。

本实用新型公开了一种硅钢片表面涂漆装置，包括平台，所述平台的上表面固定安装有固定框，固定框的内顶壁开设有矩形槽，矩形槽的两侧内壁转动连接有丝杠，且固定框的侧面设置有用于驱动丝杠转动的驱动电机，丝杠的表面螺纹连接有移动块，移动块的下表面固定安装有连接杆。该硅钢片表面涂漆装置，在对硅钢片进行喷涂时，能够将硅钢片挂在挂钩上，并启动驱动电机带动丝杠转动，从而使硅钢片移动至雾化喷头的位置后，在喷涂泵和旋转电机的作用下对其进行旋转喷涂，从而有效的提高了喷涂的均匀度，同时喷涂完成后，驱动电机反转，并启动暖风机，在硅钢片向外移动的过程中通过蛇形管道对其进行热风干处理，简单便捷，有效的提高了工作效率。

对无取向电工钢中的夹杂进行了系统的分析。利用小样电解,采取不同电解液,不同的分离方法对无取向电工钢中稳定和不稳定夹杂物进行了提取、分离和收集。利用扫描电镜(SEM)、X-射线衍射、ICP等对电解分离收集的夹杂物进行了定性和定量分析。 The inclusion analysis of the non-oriented electrical steel has been investigated.By using small sample electrolytic analysis,with different electrolytes and different separation ways,the stable inclusions and unstable inclusions was drew,separated,and collected.With utilizing the methods of SEM,X-ray and ICP,the qualitative and quantitative analysis of inclusions in the non-oriented electrical steel was obtained. 

简要介绍了宝钢无取向电工钢的发展历程、产品大纲、电磁性能控制情况,以及高附加值新产品的开发、应用情况。概述了近年来宝钢无取向电工钢生产技术进步,主要包括夹杂物控制技术、连轧机高牌号硅钢制造技术、同板差控制技术、环保涂层开发技术等。 This paper briefly summarizes the development history, product catalogue, and magnetic properties of non-oriented electrical steel sheets at Baosteel, as well as the development and application of high-value-added steel grades. Recent advances in manufacturing electrical steel sheets are also introduced, including technologies for controlling inclusion, producing high-grade steel strips by a tandem rolling mill, and controlling the transverse thickness difference of steel sheets, as well as the ... 

对高牌号无取向电工钢国内生产情况、工艺技术、产品性能及应用领域等进行了阐述,并探讨了高牌号无取向电工钢产品的发展趋势。 This paper introduces basic facts on the production status,process technology and products’ properties and their applications of non-oriented electrical steel with high grade at home,and then discusses the development trend on technology for producing the non-oriented electrical steel with high grade. 

本发明涉及一种电机定子硅钢片激光焊接装置，其包括底座；工作台，其安装于所述底座；下压旋转组件，其包括：焊接支座，其安装于所述底座上；用于压紧定子硅钢片的下压组件，所述下压组件位于所述工作台的上方，且可沿垂直于所述工作台的板面的方向移动；用于驱动所述定子硅钢片旋转的旋转组件，其安装于所述下压组件靠近所述工作台的一端，所述旋转组件可绕所述下压组件的轴线旋转；以及激光焊接头组件，其固定于所述底座。通过在焊接工作台上设置下压旋转组件，下压组件可以驱动下压使定子硅钢片压紧，旋转组件可以驱动定子硅钢片旋转，进行下一道焊缝焊接，直到该定子硅钢片所有焊缝焊接完成，使用方便，省时省力。

结合工业化生产的50A1300牌号无取向硅钢,分析了化学成分、RH精炼脱氧方式、板坯装炉温度以及热轧平整工艺等对磁性能的影响,探讨成品钢磁性能的改善。结果表明,采取改善后,50A1300牌号无取向硅钢的磁性能得到明显改善。2012年,该钢种平均铁损、磁感应强度分别达到5.26 W/kg、1.762 T,能够较好地满足用户市场需求及同行对标需要。 Based on the industrial manufacture of 50A1300 grade non-oriented silicon steel sheets,effects of chemical composition,deoxidization method in RH vacuum refining,charging temperature of steel slabs,hot rolling and flattening progress on magnetic properties are analyzed.The optimization methods of magnetic properties of steels are discussed. Results show that the magnetic properties are obviously improved by the adopted measures above. In 2012,the average core loss and the magnetic induction of 5... 

本发明公开一种硅钢级氧化镁制备方法、硅钢级氧化镁保护膜，涉及氧化镁制备技术领域。将得到的粗氧化镁产品进行净化处理；将净化处理后的粗氧化镁产品与金属镁碳还原剂，在真空状态下，利用真空碳热还原技术进行金属镁的置换，制得金属镁；金属镁碳还原剂与粗氧化镁产品的质量比为（1~1.5）：1；制得的金属镁在纯氧下制得氧化镁；将制得氧化镁根据实际需求获得不同粒径硅钢级氧化镁颗粒。本发明产品各项指标优于企业标准的硅钢级氧化镁。而且不会受原料中含有的钙等杂质的影响，产品纯度很容易达标，同时，还存在能耗较低、生产成本低等优点，解决了业在降低能耗方面的突破可应用于工业化生产。

就冷轧硅钢废水处理生产中面临的主要问题进行分析,从技术角度及运行管理角度提出工艺优化升级改进措施及应对策略;同时从后续深度处理,逐步实现零排放目标的角度进行探讨,为冷轧硅钢废水减量化、出路乃至废水零排放提供一些思路。 The main problems in the wastewater treatment process of cold-rolled silicon steel lines are analyzed and process upgrading measures and optimization strategy are put forward from both technical and management views.At the same time,downstream deep treatment to gradually achieve the target of zero discharge is discussed,to provide some ideas for reduction or even zero discharge of wastewater from cold-rolled silicon steel lines.