基于BOF→RH→CSP生产工艺,研究了RH精炼过程钢中夹杂物类型演变及MgO·Al2O3夹杂物形成规律,同时对MgO·Al2O3夹杂物的形成条件进行了热力学计算,借助CFD数值模拟软件研究了RH精炼过程卷渣行为。研究发现,RH精炼过程20和30 min时,w([MgO])/w([Al2O3])为0.005~0.020,未发现MgO·Al2O3夹杂物;RH出站后夹杂物w([MgO])/w([Al2O3])为0.3~0.5,且RH精炼结束后MgO·Al2O3夹杂物占夹杂物总量的58.4%;另外,RH精炼过程钢液表面速度CFD模拟结果为0.57 m/s,大于临界卷渣速度0.45 m/s,且顶渣成分与夹杂物成分相近,存在卷渣现象。热力学计算表明,钢液与炉渣平衡时钢中w([Al])为0.31%~0.37%,w([Mg])为0.00024%~0.00028%,在MgO·Al2O3生成区域之内。减少RH处理过程卷渣,浇铸过程下渣及控制顶渣和包衬相中MgO质量分数可抑制MgO·Al2O3夹杂物形成。 Based on the practical production of non-oriented silicon steel, the evolution of inclusion type and the formation of MgO·Al2O3inclusion were analyzed in the process of BOF→RH→CSP. The thermodynamic conditions for forming MgO·Al2O3inclusion were discussed and the behavior of slag entrapment of molten steel was also simulated by CFD software during RH refining. The results showed that the value of w([MgO])/w([Al2O3]) was in the range of 0.005-0.020 and no MgO · Al2O3 inclusion was observed at 20 ... 

本实用新型涉及一种便捷型铁芯硅钢片组装系统。该便捷型铁芯硅钢片组装系统包括硅钢片叠放装置，硅钢片叠放装置包括固定座，固定座上通过轴承转动装配有齿圈，固定座上固定连接有与齿圈同轴的固定盘，固定盘的中心设有中心孔，固定盘上设有六个沿固定盘径向延伸的滑槽，六个滑槽沿固定盘周向均匀分布，每个滑槽内分别滑动装配有滑块，齿圈的上侧面设有上螺纹，滑槽的下侧面设有与上螺纹相匹配的下螺纹，滑块的内端设有定位板，定位板的外侧面上设有用于与硅钢片中心孔孔壁上的割槽相匹配的定位条。相比于现有技术，本实用新型能够对硅钢片进行定位，从而确保各片硅钢片的中心孔以及割槽相对应，提高了硅钢片叠放效率，从而提高了生产效率。

本发明提供了基于硅钢片性能的分类方法、系统、计算机和存储介质，通过抽样选取待分析硅钢片，获取待分析硅钢片的基准B‑H曲线和基准B‑P曲线，以及通过预设检测方法测得待分析硅钢片的样本B‑H曲线和样本B‑P曲线后，根据预设磁通密度监测范围分别选取基准B‑H曲线、基准B‑P曲线、样本B‑H曲线和样本B‑P曲线对应的B‑H基准样本点、B‑P基准样本点、B‑H待分析样本点和B‑P待分析样本点，并基于依此分别得到B‑H样本点距离与B‑P样本点距离分析待分析硅钢片的性能，以及根据分析结果对待分析硅钢片进行分类的方法，基于性能曲线的数据分析对硅钢片性能进行合理的评估分类，不仅实现了对硅钢片质量的有效监控，而且为其使用策略的制定提供可靠依据，保证产品质量的同时，为产品用料选择提供便利。

对熔融态钢液进行处理,研究了电脉冲对于取向硅钢凝固组织的影响作用,利用正交试验法研究了脉冲电容、频率、处理时间和电压等脉冲参数的作用效果。结果表明:电脉冲对钢锭晶粒组织具有明显的细化作用,凝固组织的等轴晶比例大幅上升,影响等轴晶比例的最显著性因素为脉冲频率,最优正交试验参数为电容1 200μF,脉冲频率1 Hz,处理时间5 s,脉冲电压800 V。随着输入能量的增大等轴晶率先增大后减小,脉冲输入能量为某值时,等轴晶率最大,利用经典形核理论和热力学对这一现象进行了解释。 The influence of electric pulse on the solidification structure of oriented silicon steel was investigated by applying electric pulse in molten steel.The affection due to different electric pulse parameters such as electric capacity,frequency,applied time and voltage was studied by orthogonal design test.The result showed that solidification structure of oriented silicon steel could be improved by the electric pulse,and the equiaxed crystal ratio increased obviously.The most influential paramete... 

本发明提供一种线状槽的形成图案，其兼得低装配系数化的效果和高磁通密度。在钢板的表面具有多个在横切该钢板的轧制方向的方向延伸的线状槽的方向性电磁钢板中，在上述线状槽相互间的上述钢板的表面形成从该表面凹陷的凹型缺陷，将上述钢板的上述凹型缺陷的体积分率相对于不存在该凹型缺陷的状态的钢板设为0.0025vol％～0.01vol％，以每1m2钢板为30个～200个的频率形成切断上述线状槽的上述延伸的中断部。

【作者】 朱传芳； 潘恒韬； ...

结合工业化生产的无取向硅钢,探讨了氧硫交互作用对钢中夹杂物生成的影响。借助非水溶液电解+扫描电镜法,研究了不同O、S含量下钢中夹杂物的变化规律。结果表明,本实验条件下,提高O含量、降低S含量,会劣化热轧组织再结晶效果。在劣化效果上,O的作用大于S;低Si、无Al硅钢中,应尽可能降低O含量、适当提高S含量,以粗化钢中微细夹杂物,减少尺寸小于1.0μm的夹杂物的数量;O、S含量与钢中夹杂物数量不具有关联性。生产过程中,不仅要严格控制O、S含量,还要严格控制生产工艺,以免生成较多的有害夹杂物。 Based on the industrial production of non-oriented silicon steel,the effects of interaction between oxygen and sulfur on the formation of inclusions were discussed.The change of non-metallic inclusions in steel sheets was investigated by means of electrolysis with non-aqueous solution under different oxygen and sulfur content.Results show that the recrystallization microstructure of hot rolled sheets will be deteriorated with the increase of oxygen content and the decrease of sulfur content.The ... 

本实用新型公开了一种硅钢板带生产加工用除油烘干装置，包括壳体，所述壳体的外表面上对称设置有电机，所述电机的输出端固定连接有输送带，所述壳体的顶部设置有机体，所述机体的内部设置有除油机构，所述除油机构的一侧设置油烘干机构，所述壳体的底部设置油收集箱，所述收集箱的内部设置有收集槽。本实用新型，利用除油机构可对成硅钢板带生产后进行一定的除油处理，除油的效果更好更彻底，同时相比以往的方式提高了一定的工作效率，具有一定的实用性，利用烘干机构可进行除油后的成硅钢板带进行烘干处理，防止水渍残留在表面上，影响一定的美观效果，具有一定的实用性。

介绍了国内无底层取向电工钢生产技术水平、产量和用途，简述了无底层取向电工钢作为取向电工钢超/极薄带母料及应用于制作大型发电机组铁心、风电等电机铁心和变压器铁心等的情况。 The production technology level,output and application of domestic glassless grainoriented electrical steel were introduced,and the application of glassless grain-oriented electrical steel as parent material of ultra-thin strip of grain-oriented electrical steel and in making large-scale electric generator cores,wind power motor cores and transformer cores were briefly described. 

热轧轧制工艺对产品性能和轧制稳定性影响很大,对中低牌号无取向电工钢,当在两相区轧制时,热轧塑性明显降低,板形变坏,易出现边裂等情况。以50W1000为例,通过对其变形抗力进行研究,得出把两相区控制在F4与F5之间为最佳轧制工艺的结论。在此基础上制定了一套较为合理的热轧工艺制度。采用新的轧制工艺后,50W1000热轧精轧的稳定性明显改善,热轧产品合格率由开发初期的40%左右提高到95%以上。 The hot rolling process has great influence on product′s performance and rolling stability.For the low medium grade non-oriented electrical steel,when non-oriented electrical steel is rolled in tow phase region,the hot rolling plasticity reduces obviously,the shape of strip goes bad and easily to crack at the edge.The deformation resistance of 50W1000 steel was investigated.The results show that the optimal rolling process is to control the two phase region between F4 and F5.Based on the results... 

本实用新型公开了一种连续热浸镀铝锌硅钢板,包括硅钢裸板，所述硅钢裸板的左侧边固定连接有第一铝锌输送条，所述硅钢裸板的右侧边固定连接有第二铝锌输送条。本实用新型，通过给待镀铝锌层的硅钢裸板左右侧边设置铝锌输送条，避免了镀层完成后需要对未镀膜的部位进程切除，降低了生产繁杂度，节约了生产成本，避免了材料的浪费，通过给铝锌输送条的前后侧面设置直齿面，提高连续热浸镀膜过程中的输送精度，从而提高了镀膜的均匀性，通过给铝锌输送条设置导向槽，提高硅钢板输送过程中的运动稳定性，通过优化硅钢钣的自身结构，提高了热浸镀铝锌层的效率，并节约了生产成本。

热卷箱位于热连轧带钢生产线粗轧与精轧机之间,是热连轧生产中比较理想的中间保温设备。由于取向硅钢变形温度区间较窄,在生产中易出现边裂现象,同时中间坯的边部温度难于得到保证,因此一般不采用热卷箱设备生产,限制了传统热连轧生产线产品开发的品种。通过合理优化热卷箱控制工艺参数,解决了某厂传统热连轧生产线用热卷箱生产取向硅钢的边部质量问题,成功地生产出取向硅钢带。 The hot coil-box is an ideal heat retaining apparatus for hot rolling,lined between roughing mill and finishing mill. But oriented silicon steel has a narrow deformation temperature range,so that the edge crack easily occurs and it is difficult to insure the temperature of the intermediate blank. Therefore,the hot coil-box is rarely used in producing oriented silicon steel,which restricts the product development of the traditional hot rolling line. The article reasonable optimized process parame...