本实用新型公开了一种变压器用硅钢板滑石丸粘接加工设备，用于对变压器用硅钢片进行贴片，其结构包括：机械臂、抓取头、分道排序机构，所述抓取头位于机械臂的末端，用于抓取滑石丸，在抓取头上能够同时抓取多个滑石丸，配合机械视觉系统，就能够更精确的确定贴片位置，并完成贴片，提高了生产效率；所述分道排序机构包括：振动盘、排料板，振动盘中储存有一定的滑石丸，振动盘顶部的出料口与排料板连接，工作时振动盘中的滑石丸依次从出料口进入排料板中，在排料板上的物料通道中运动，物料通道的末端是多条分支，且末端向外敞开，抓取头能够在物料通道末端同时抓取多个滑石丸。

研究了冷轧大压下量,950℃退火时间对一种新型含铜无取向电工钢晶粒度和织构的影响。结果表明,大压下量冷轧,随压下量的增加,退火晶粒向γ线聚集,形成强{111}<112>织构。提高冷轧压下率,退火织构{111}<100>,{110}<001>强度减弱,增加退火时间,退火织构{111}<110>,{100}<001>,{110}<001>强度变弱。采用87.5%冷轧压下率和950℃退火60 s,有利织构{100},{110}占有率最大。 The effect of annealing(950 ℃) time with high cold rolling reduction on grain size and texture of a new non-oriented electrical steel containing copper was investigated.The results show that for high cold rolling reduction,most annealed grains are oriented along γ-fibre with increasing cold rolling reduction ratio and strong texture {111}<112> is formed.With increasing the cold rolling reduction ratio,the intensity of annealed texture {111}<110>,{011}<100> decreases.With increa... 

本发明涉及电气行业机电设备用软磁材料技术领域，具体公开了一种高硅含量硅钢极薄带的制造方法。所述的高硅含量硅钢极薄带的制造方法，其包含如下步骤：(1)将高硅硅钢母材进行纵剪分条，然后制成卷料；(2)将卷料升温至140～160℃，压制成厚度为0.05～0.1mm的带料；(3)将带料进行脱脂处理；再经干燥后得脱脂后的带料；(4)将脱脂后的带料在保护气氮气中，在780℃～940℃温度下退火处理5～10min，即得所述的高硅含量硅钢极薄带。由该方法制备得到的高硅含量硅钢极薄带具较好的抗拉强度以及较高的磁感应强度；且该方法制备步骤简单，有利于降低高硅含量硅钢极薄带的生产成本。

本实用新型公开了一种硅钢片组扣件自动压平装置，包括：定位单元，定位单元包括转盘、校位板和第一驱动组件，第一驱动组件连接并驱动校位板沿竖直方向运动，校位板滑动连接有第一校位柱，第一校位柱相对转盘偏心布置；第一推送单元，位于转盘的一侧，第一推送单元包括第一推送气缸和第一推块，第一推送气缸连接并驱动第一推块沿水平方向运动；冲压单元，位于转盘背离第一推送气缸的一侧，冲压单元包括第二驱动组件和冲压柱，第二驱动组件连接并驱动冲压柱沿竖直方向运动。转盘、校位柱和第一驱动组件配合，周向定位硅钢片组，再通过冲压柱将凸出于硅钢片组的扣件压平，完成硅钢片组的整形，整体更为美观，方便后续的装配使用。

本发明公开了一种变压器硅钢片回收检测装置，包括检测传送带、防层叠机构、CCD摄像头、分料传送带、合格料箱和不合格料箱，所述防层叠机构和图像提取机构沿检测传送带传送方向依次布置，所述防层叠机构包括剥离辊，所述剥离辊及CCD摄像头均位于检测传送带上方，剥离辊与检测传送带向靠近的一面移动方向相反，分料传送带位于检测传送带后方，合格料箱与不合格料箱位于分料传送带后方，本发明能够将回收的硅钢片进行一一的快速检测，并对检测结果进行分类，检测效率高。

一种高硅钢材料的制备方法，步骤包括靶材、金属基材表面清理；排除密闭容器内空气、通保护气；双辉光等离子预轰击靶材和基材，净化表面；等离子溅射、加热、保温；缓慢冷却取出。预轰击靶材、基材，去除表面吸附层、活化基材，交替升高基材电压、靶材电压，使靶材中的合金元素被离子轰击而溅射出来、扩散进入基材内部形成表面高硅钢层。“双辉光等离子表面冶金技术”制备高硅钢的工艺简单易行、可控性高、成本低、无污染且基体和表面的结合力高，适合大规模产业化生产；更重要的是该方法采用交替离子轰击、扩渗速度快，结合强度高，得到硅含量均匀分布或呈梯度分布的高硅钢材料，为制备更高品质的无噪音、低铁损的高硅钢产业化奠定基础。

从取向硅钢生产路线的选择、工艺技术的改进和生产设备的改造三方面进行了生产取向硅钢的节能降耗技术改造.通过完善多元抑制剂配方生产低温取向硅钢,通过加抛丸的酸洗、带面超声波清洗、改进连续退火炉以及余热循环利用等技术改造,使2012年取向硅钢的产量与未进行技术改造前的2009年相比提高了2.5倍,产品磁性上升了一个半牌号,能耗下降了8.9%,成材率提高了6.4%,生产成本下降了22%,综合效益显著. Energy saving technological transformation was carried out in the production of grain oriented silicon steel from three aspects of the oriented silicon steel production process route selection,technology improvement and equipment renovation.Through the improvement of multiple inhibitor formulations for producing low-temperature grain-oriented silicon steel,and by adding the blasting pickling,the belt surface ultrasonic cleaning,improvement of continuous annealing furnace,waste heat recycling tec... 

采用\"热轧复合+冷轧减薄+退火\"方法成功制备了0.20mm厚的硅浓度梯度高硅钢薄带,并采用SEM和X射线衍射技术对制备过程中组织和织构演变进行了研究。热轧复合板微观组织呈明显层状分布,复合界面为紧密冶金结合且经过83%的大冷轧变形未开裂。热轧和冷轧复合板带中均形成强α和γ织构,再结晶退火后形成强γ织构。冷轧和退火织构沿板厚呈显著的梯度分布特征,其主要来自于复合界面两侧硅浓度和初始热轧织构的差异性以及冷变形的不均匀性。 Gradient high silicon steel thin sheets with thickness of 0.20 mm were successfully produced by the rolling and annealing method,including hot rolling bonding,cold rolling,and annealing.Microstructure and texture evolution was investigated by means of SEM and X-ray diffraction.Microstructure of hot-rolling-bonding shows obviously layered distribution,the composite interface was closely metallurgical bonding and no cracking appears even after 83%cold rolling.Strongαandγfibers develop in the hot a... 

本发明涉及电工钢的生产方法，更具体地说，涉及一种预应力生产中低牌号无取向电工钢的方法，包括铁水预处理；预处理后的铁水进行转炉冶炼并吹氩脱氧；吹氩后的钢水送入精炼炉中进行冶炼并加入低碳合金进行合金化；合金化处理的钢水通过薄板坯连铸机铸成板坯并采用薄板胚连铸连轧生产工艺进行轧制获得热轧板；所述热轧板经过酸洗冷轧，随后进行预应力拉伸并退火，采用涂层进行涂镀、烧结后卷取。本发明采用预应力拉伸，改善无取向电工钢退火前钢板内部应力的分布，制备的冷轧无取向电工钢产品的电磁性能P15/50≤5.4W/kg，磁感应强度≥1.72T，板形同板差≤8um。

针对硅钢连续生产线设备存在的故障、隐患以及精度等影响产品质量的问题进行分析及改造,实现保证生产线设备稳定运行、提高设备精度及硅钢产品质量的目的。 This paper analyzes and transforms the electrical equipment failures, risks existed in slicon continuous production line, and the effect of accuracy to product quality, in order to ensure stable operation of equipment in production line and improve the accuracy of device, quality of silicon. 

根据本发明的一个实施例的粘接涂料组合物，其包含聚乙烯丙烯酸酯，所述聚乙烯丙烯酸酯包含由以下化学式1表示的重复单元和由以下化学式2表示的重复单元，所述聚乙烯丙烯酸酯包含65至90重量％的由以下化学式1表示的重复单元、10至35重量％的由以下化学式2表示的重复单元。

本发明公开了一种宽频率低铁损无取向电工钢及其制备方法，属于无取向电工钢生产制造技术领域。它从电工钢表面向内依次包括0.005mm～0.1mm的渗透层和钢材内芯；所述渗透层是由硅原子向电工钢内渗透形成，渗透层中的硅元素含量为3wt％～8wt％；所述钢材内芯包括2.0wt％～5.5wt％的硅元素和不少于93.2wt％的铁元素。本发明能保证无取向电工钢具有低频低铁损性能同时有效降低高频条件下的铁损，具体铁损性能为：铁损P1.5/50≤2.35W/kg，铁损P1.0/400≤13.8W/kg。