通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 

本发明是关于一种薄规格无取向硅钢35BW440，该无取向硅钢35BW440包括以下质量百分比的元素：C：≤0.003％，Si：0.8％‑2.0％，Mn：0.4％‑1.2％，P：≤0.015％，S：≤0.003％，Als：0.25％‑0.6％，N：≤0.003％，Sb：0.04％‑0.1％，O：≤0.0025％，其余为Fe及不可避免的杂质。在没有电磁搅拌设备增加无取向硅钢磁感应强度的前提下，通过加入Sb元素，增加对电磁性能有利的{110}和{100}织构组分，提高电磁性能，采用二次冷轧及中间连续退火的工艺，提高无取向硅钢的表面质量。

本实用新型提供了一种新型的去角硅钢片，包括硅钢片本体，所述硅钢片本体包括叠放区和防护区，所述硅钢片本体设有防护结构，所述防护结构包括叠放区上设有的多个均匀分布的降噪凹槽，所述防护区上下两端分别设有多个防护条，且两两防护条之间设为连接槽，每个所述防护条皆包括与硅钢片本体连接的防护层和减震层，所述防护区底部两侧分别设有减震柱，所述防护区中间设有贯穿孔，所述贯穿孔内设有绝缘螺栓。本实用新型能降低噪音和减少震动影响，从而避免使得变压器寿命及功能性降低。

本发明公开了一种低铁损高磁导率无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯，板坯经加热炉加热，再经热轧得到热轧板，然后经空冷和水冷后在500～650℃进行卷取；热轧板经常化处理、盐酸酸洗；酸洗后在可逆轧机上进行冷轧；最后经成品退火，退火温度为840～900℃，加热时间为240～500s；然后以不超过3℃/s的冷却速度冷却至500℃以下；涂覆绝缘涂层、固化，后经二次退火，即可得到低铁损高磁导率无取向电工钢，其磁性能满足P1.5/50≤3.50W/kg，μ1.5≥3800Gs/Oe，B5000≥1.76T的要求。

本实用新型公开了一种硅钢片激光曲线开料机，本实用新型涉及电力设备技术领域，目前现有的硅钢立体三角形卷铁芯的机械式斜度开料机在开料过程中精度差、效率低，且在硅钢片送料的过程中，长时间后硅钢片容易发生松散情况，同时只能对单一厚度的硅钢片进行输送工作，包括放料组件和开料组件以及收料组件，所述放料组件用于对硅钢片的放料工作，所述开料组件用于对硅钢片的开料工作，所述收料组件用于对硅钢片的收料工作。该硅钢片激光曲线开料机，通过利用高速激光曲线开料，效率高精度好，且硅钢片在输送的过程中，能够自动调整导向辊的位置，进而能够对硅钢片起到很好的导向作用，使其表面时刻为张紧状态，进而保证硅钢片的开料效果。

本发明公开了一种改善取向硅钢边部变形的热处理辅助方法，在高温退火工序前，在钢卷的下端预设位置处放置阻热环并固定；在高温退火完成后，拆除固定件并移除所述阻热环。本发明通过施加阻热环，降低了取向硅钢卷在高温退火过程中的升温速率，降低了钢卷在升温及冷却过程中的胀缩量，有效改善了边部变形情况。同时，本发明由于采用一体式隔热材料，其装配及移除难度大幅度降低，有利于推广应用。

本发明提供了基于硅钢片性能的分类方法、系统、计算机和存储介质，通过抽样选取待分析硅钢片，获取待分析硅钢片的基准B‑H曲线和基准B‑P曲线，以及通过预设检测方法测得待分析硅钢片的样本B‑H曲线和样本B‑P曲线后，根据预设磁通密度监测范围分别选取基准B‑H曲线、基准B‑P曲线、样本B‑H曲线和样本B‑P曲线对应的B‑H基准样本点、B‑P基准样本点、B‑H待分析样本点和B‑P待分析样本点，并基于依此分别得到B‑H样本点距离与B‑P样本点距离分析待分析硅钢片的性能，以及根据分析结果对待分析硅钢片进行分类的方法，基于性能曲线的数据分析对硅钢片性能进行合理的评估分类，不仅实现了对硅钢片质量的有效监控，而且为其使用策略的制定提供可靠依据，保证产品质量的同时，为产品用料选择提供便利。

本实用新型涉及一种取向硅钢氧化镁线涂层装置，尤其涉及一种取向硅钢氧化镁涂层线用冷涂辊，具有涂层辊本体及包覆在涂层辊本体外层的橡胶涂层；涂层辊本体内部为空腔结构，空腔结构内通有循环冷冻液。本实用新型涂层辊内部设计成空腔结构，并通过循环冷冻液对涂层辊进行冷却降温，既可以达到通过涂层辊对氧化镁进行降温的目的，从而满足工艺要求，防止质量缺陷的产生，还可延缓涂层辊因反复摩擦生热造成橡胶层老化，从而延缓涂层辊使用寿命。

利用电子探针面分析、状态分析及电子背散射衍射相分析技术研究硅钢高温氧化铁皮的显微结构。电子探针面分析可以直观的看出元素的分布状态,初步判断氧化铁皮的结构,而状态分析可以准确表征常规氧化铁皮中铁元素的状态,对于合金元素富集区域则通过电子背散射衍射相分析技术来标定。结果表明,高温氧化铁皮的结构主要有4层,即最外层为厚度约为10μm的Fe2O3相,次外层为Fe3O4相,中间层为FeO相上分布有颗粒状的Fe3O4相,最内层为FeO相和Si元素富集的Fe2SiO4相。其中Fe2SiO4层的分布特征与加热温度密切相关:1 100℃时,Fe2SiO4相呈颗粒状,弥散分布在FeO层;1 200℃时,Fe2SiO4相呈液态,侵入基体和疏松的FeO层,且沿着FeO晶界呈网状分布。 The microstructure of high temperature oxide scale on silicon steel was characterized by electron probe microanalyzer(EPMA)mapping analysis,state analysis and electron backscatter diffraction(EBSD)phase analysis.The element distribution and the initial structure of the oxide scale could be detected by EPMA mapping analysis apparently.And the state of iron in the conventional oxide scales could be determined by state analysis.Meanwhile,the alloy-rich region could be identified by EBSD phase analy... 

采用取向分布函数和取向线分析方法对低温板坯加热取向硅钢从热轧到初次再结晶工艺阶段的织构进行了研究。研究表明:一次冷轧后各层的织构组分与热轧板各层面的织构组分存在着继承关系,次表层存在很强的{001}<110>织构,中心层的织构和热轧板的中心层相似,存在强的{001}<110>和{112}<110>织构;中间退火后发生再结晶,各织构组分的强度有所减弱,Goss织构组分再次出现;二次冷轧后沿厚度方向上的织构不均匀性不明显,{111}<112>织构强度最高,几乎是其他织构组分的1倍,{001}<110>织构大幅降低;初次再结晶后织构沿厚度方向没有明显的不均匀性,{111}<110>为最强的织构组分,并且具有一定强度的Goss位向。 The texture from the first cold rolling to the primary recrystallization of low temperature slab reheating grain-oriented electrical steel were researched by orientation distribution function and orientation distribution intensity technique.The results show that after the first stage of cold rolling,there is a strong {001}<110> texture in the subsurface and the texture in center layer is very similar to the center layer of hot band which has strong {001}<110> and {112}<110> tex... 

本实用新型涉及一种硅钢片胶带缠绕机，包括底座、动力单元、夹紧装置和胶带缠绕装置。其中，夹紧装置设于底座上，被配置为适于夹紧硅钢片组。进一步，夹紧装置上设置有周向滑槽，周向滑槽沿硅钢片组的外周设置，胶带缠绕装置与动力单元连接，并可滑动地连接于周向滑槽内。动力单元工作能够带动胶带缠绕装置沿周向滑槽移动，以将胶带缠绕于硅钢片组的外周，完成硅钢片组的定型封装。胶带缠绕过程中，无需人工操作，实现了硅钢片组的自动封装，代替了传统的人工封装，大大降低了操作人员的工作强度，提高了硅钢片的封装效率。

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang...