本发明涉及一种硅钢片视觉识别与无损检测方法，测量硅钢片的厚度并且计算已经叠积完成的硅钢片的总高度，记录最后叠积的一片硅钢片的形状和两定位孔坐标，计算和输出当前硅钢片的形状、两定位孔坐标的位置偏差值和两定位孔坐标的定位孔间距，记录硅钢片两端的接缝宽度和坐标并且输出搭接形状，判断定位孔间距、两定位孔位置、接缝宽度是否符合标准，以及两片硅钢片是否已经搭接上，通过打齐硅钢片使之符合要求、或者停机人工调整。本发明还涉及一种硅钢片视觉识别与无损检测装置。本发明利用激光测距仪、相机实现了无损检测，实现了每片硅钢片高度值、定位孔、接缝宽度的即时自动测量，通过PLC控制系统将控制信息传输至机械臂进行放置精度微调。

研究了组织和析出物对高效电机用无取向硅钢退火板磁性能的影响。结果表明:随着退火温度升高,退火板平均晶粒尺寸增加,P15/50明显降低,B50略有升高。退火温度在1 000℃时,退火板的综合性能较好。析出物主要是AlN、(MnS+AlN)和(MnS+Al2O3)复合析出物,尺寸较粗大,主要集中在1.0～2.5μm,还发现少量百纳米以下的细小AlN和TiN。实验室模拟TSCR流程试制的高效电机用无取向硅钢,铁损平均值小于4.00 W/kg,磁感应强度大于1.75 T,适合作中小型高效电机铁芯材料。 Effects of microstructure and precipitation on magnetic property of non-oriented silicon steel sheets after annealing for high-efficiency motor are studied in the paper by experiments.The annealed sheet exhibits a larger average grain size,obviously decreasing iron loss and slightly raising magnetic induction with increasing temperature.The annealed sheet has better comprehensive properties at a annealing temperature of 1 000 ℃.The main precipitates are compounds of AlN、(MnS+AlN)and(MnS+Al2O3) w... 

本发明揭示了一种高牌号无取向硅钢及其生产方法，生产方法包括冶炼、连铸、热轧、酸洗、切边、常化、冷轧，冶炼最终所得钢水化学成分以质量百分比计为：C≤0.005％、Si≥2.8％、Als0.5～1.2％、Mn0.25～0.8％、P≤0.02％、S≤0.0040％、N≤0.0020％、Nb≤0.0020％、V≤0.0020％、Ti≤0.0020％，其余为Fe以及不可避免的杂质；切边工序对热轧卷板的两侧进行切边，单侧的剪切宽度为10～20mm；常化在罩式退火炉中进行，均热温度为T＝{(990～1010)‑100×[30×(Si)+20×(Al)]}℃，(Si)为Si的质量百分比，(Al)为Al的质量百分比，均热时间为6h，之后冷却；钢卷在罩式退火炉中冷却至预设温度T0时取出送至冷轧线冷轧，T0为120～180℃，第一道次轧制时的轧制力恒定且轧制力为11000～12000kN。本发明可避免高牌号无取向硅钢在冷轧过程中由于脆性高而导致的频繁断带。

本实用新型涉及变压器铁芯生产技术领域，尤其涉及一种硅钢片卷自动上料装置。包括所述底座上方设置有支撑座，所述支撑座上方转轴连接有翻转座，所述翻转座前后两侧设置有支撑柱，所述托架底部前后两侧设置有支撑套，所述支撑套对应滑动连接在支撑柱上，所述支撑套左侧上方设置有凸台，所述凸台右侧在支撑套上方设置有卡槽，所述卡槽右侧开口，所述硅钢带卷设置在卡槽内部，将钢卷平躺放置在托架的卡槽内部，通过翻转液压缸可将托架和钢卷进行树立，钢卷一侧靠在托架上，钢卷树立过程比较平稳，通过三组液压缸可实现钢卷自动上料的过程，在钢卷树立过程中，可通过绳索将钢卷固定在托架上。

本发明公开了一种生产高表面质量镀铝硅钢带的方法，属于连续热浸镀铝硅技术领域。本发明的生产高表面质量镀铝硅钢带的方法，包括酸洗、冷轧、清洗、连续退火、热浸镀铝硅和冷却处理，所述冷却包括预冷段和强冷段，其中预冷段是通过预冷风机将带钢温度冷却至620～630℃，强冷段包括三段强冷，三段强冷采用水雾冷却，且控制强冷段冷却速率≥30℃/s。本发明通过控制钢带表面粗糙度、清洗质量、退火炉气氛、气刀参数以及镀层结晶控制器参数，可以有效控制铝硅产品表面结晶尺寸、减少漏镀等典型缺陷，生产出高表面镀铝硅钢带。

本发明提供了一种高硅钢及其制备方法，所述高硅钢由如下质量分数的化学成分组成：Si：5.0‑7.0％，Ni：0.001‑0.05％，Ce：0.0001‑0.0002％，其余为Fe和不可避免的杂质。本发明提供的高硅钢的延伸率为15‑22％，抗拉强度为739‑824MPa，磁感应强度B8为1.26‑1.29T，铁损P2/10k＝68‑80W/kg，矫顽力为10.6‑13.4/m，最大磁导率为19000‑25000，具有良好的磁性能和延伸性能，易加工且可大规模生产应用。

电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

硅钢高温退火环形炉炉壳制作与安装精度要求较高,施工时通过对壳体原材料矫正、炉壳板拼焊、下料切割、型钢骨架组装及焊接、骨架及炉壳板矫正、骨架与炉壳板组装及焊接、炉壳矫正、零配件装置、定位钻孔、报验检查、出厂、内侧板安装、外侧板安装、顶板安装等环节的工艺技术控制,能保质高效地完成硅钢高温退火环形炉炉壳制作与安装,为以后同类工程的施工提供可借鉴经验。 The required precision of manufacture and installation technique of the silicon steel high temperature annealing annular-furnace shell is high.During construction , manufacture and installation of the silicon steel high temperature annealing annular-furnace shell could be finished high efficiently through correcting the raw materials of shell , furnace shell plate welding , material cutting , steel frame assembly and welding , skeleton and shell plate correction , skeleton and furnace shell asse... 

本实用新型提供一种对硅钢片横剪线片料进行穿针叠柱与输送的装置，包括输送装置、穿针定位装置、纵向移动平台和转运装置，所述的输送装置设在纵向移动平台上方，所述的穿针定位装置位于输送装置底部，穿针定位装置固定在纵向移动平台上，所述的转运装置布置在输送装置的输出侧；所述的转运装置通过对接机构与输送装置对接。本实用新型能够完成硅钢片的穿针叠柱，并将此硅钢片柱整体输送到指定工位。本实用新型采用输送装置和穿针定位装置的上下分层布置结构，首先完成了硅钢片的穿针定位，然后完成硅钢片柱的整体输送，整个工艺方法中不使用吊运设备，提高了生产效率。

本发明属于取向硅钢制备技术领域，具体涉及一种软磁材料取向硅钢退火工艺。所述退火工艺主要包括：涂覆隔离剂、按照一定速率升温后进行保温，以5‑10℃/min的速率进行降温；在降温过程中施加恒定磁场，之后继续降温即可实现。该退火工艺能够有效降低铁损失，提高磁感强度。同时具有较好的耐腐蚀性能和机械性能。

【机构】 中国金属学会电工钢分会； ...

研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient...