本实用新型公开了一种电工钢自粘涂层液生产用搅拌釜，包括釜体，釜体的内部通过两个第一隔板分隔成第一安装腔、第二安装腔和搅拌腔，釜体的内部设有传动组件，传动组件包括伺服电机、主动轴和两个从动轴，伺服电机固定安装在釜体顶端的中部，伺服电机的输出轴与主动轴的顶端固定连接，本实用新型的有益效果是：通过设有八个与十二个搅拌叶片相交错的挡板，避免搅拌轴在搅拌过程中产生离心力造成漩涡，使自粘内外侧的涂层液得到充分搅拌，通过设有循环泵机、第二隔板和流通槽使搅拌釜内的自粘涂层液处于流通的状态，使底部不易被搅拌的涂层液能够得到充分搅拌，在提高搅拌釜的灵活性的同时，保留其原有的稳定性。

在Gleeble-3500热/力模拟试验机上对HW600钢进行高温压缩试验,研究在不同试验条件下的变形抗力。试验结果表明:变形温度对变形抗力的影响最为显著,在相同的变形速率下,随着变形温度的升高,变形抗力降低;在同一变形温度下,变形速率增大,变形抗力增加;在同一变形温度、变形速率下,随着变形程度的增加,变形抗力急剧增大,真应变达到0.1后,变形抗力增加趋势变缓。 The high-temperature compression test is done for HW600 steel with Gleeble-3500 thermal simulation testing machine to research its resistance to deformation under different test conditions.It is showed from result that deformation temperature has greatest effect on the resistance,and along with the temperature getting higher the resistance lowered under same deformation rate;the resistance increases along with deformation rate getting greater under same temperature;and under same deformation tem... 

本发明涉及一种硅钢片叠装用上料系统，包括放置板，设置于硅钢片横剪线的出料端处，用于接收硅钢片并堆放；供料板，设置于硅钢片叠装线的上料端处，用于接取放置板并对进行初定位；输送单元，设置于硅钢片横剪线的出料口处，用于放置板并实现放置板的输送；转运单元，设置于输送单元的出料口处，用于接取放置板并将放置板输送给供料板；上料单元，设置于硅钢片叠装线的上料端处，用于接取供料板并为硅钢片叠装线进行供料。本发明的优点在于：通过放置板、供料板、输送单元、转运单元、上料单元之间的相互配合，从而将硅钢片横剪线裁切好的硅钢片送至硅钢片叠装线处进行叠装，整个过程无需再由人工搬运，大大降低了人工劳动。

采用取向分布函数和取向线分析方法对低温板坯加热取向硅钢从热轧到初次再结晶工艺阶段的织构进行了研究。研究表明:一次冷轧后各层的织构组分与热轧板各层面的织构组分存在着继承关系,次表层存在很强的{001}<110>织构,中心层的织构和热轧板的中心层相似,存在强的{001}<110>和{112}<110>织构;中间退火后发生再结晶,各织构组分的强度有所减弱,Goss织构组分再次出现;二次冷轧后沿厚度方向上的织构不均匀性不明显,{111}<112>织构强度最高,几乎是其他织构组分的1倍,{001}<110>织构大幅降低;初次再结晶后织构沿厚度方向没有明显的不均匀性,{111}<110>为最强的织构组分,并且具有一定强度的Goss位向。 The texture from the first cold rolling to the primary recrystallization of low temperature slab reheating grain-oriented electrical steel were researched by orientation distribution function and orientation distribution intensity technique.The results show that after the first stage of cold rolling,there is a strong {001}<110> texture in the subsurface and the texture in center layer is very similar to the center layer of hot band which has strong {001}<110> and {112}<110> tex... 

本实用新型公开了一种高磁感低铁损取向硅钢切割用废屑清理装置，包括激光切割台，所述激光切割台上端滑动连接有一个滑动导轨，所述滑动导轨上滑动连接有一个切割主机，所述激光切割台上端均匀固定连接有一组锯齿板，相邻两个所述锯齿板之间均固定连接有一个导流板，所述导流板两端高度低于中间位置高度，所述激光切割台上端且与导流板两侧相对应位置均开设有一个收集槽，所述收集槽内均卡接有一个收集框，所述收集槽底部侧壁固定连接有循环水管，本实用新型的有益效果是：通过循环水泵使水在循环水管和排水管之间循环流动，从而可以使切割废屑顺着水流进入收集框内进行收集，避免切割废屑粘附在锯齿板之间难以清理的情况。

【摘要】 <正>国家硅钢技术研究中心自2008年落户武...

针对目前大部分无取向电工钢处理液为含铬处理液、且需在较高温度下固化的情况,在分析成膜物质性质的基础上,试验研究了一种可低温快速固化的电工钢环保绝缘处理液,研究了其涂装工艺,并测定了涂层的附着性、绝缘性、耐热性、耐蚀性等性能。试验结果表明:该处理液可在150~250℃下快速烘干固化,涂层表面光滑且致密均匀,性能优良,可满足中小电机的使用要求。 At present,most of the insulating fluid for non-oriented electrical steel contains chromium,and should be cured at high temperature.On the basis of analyzing the characteristics of the film-forming substance,a kind of eco-friendly insulating fluid with lower curing temperature for non-oriented electrical steel sheet was developed in the experiments.Then its coating process was studied,and the adhesiveness,insulativity,heat resistance,corrosion resistance and other properties of the coating was m... 

对两种硅钢水溶性极厚绝缘涂层进行了不同温度的热老化实验。通过TG-DTA,GDS,FT-IR,SEM和光泽度仪等测试方法对老化的涂层进行分析表征,提出了评估硅钢水溶性极厚绝缘涂层热老化性能的合理温度区间,探讨了涂层热老化行为,并分析了两种涂层热老化性能的差异。结果表明,涂层附着性随着老化时间的延长逐渐下降。FT-IR表征结果显示,热老化过程中,涂料交联形成的化学键未发生断裂,交联剂氨基树脂的三嗪环被破坏是聚合物三维网络结构坍塌的主要原因。 Thermal aging expriments at different temperature were carried out on two types of water-soluble and extra-thick insulation coatings for non-oriented silicon steel,and a series of test methods such as glossmeters,TG-DTA,FT-IR,GDS,SEM were applied in analysis.For evaluating the thermal aging effect of this kind of insulation coating,the proper temperature range was proposed.The difference of aging performance between two coatings was been investigated and the related behaviors were been discussed... 

本发明提供了一种无取向硅钢RH顶枪喷粉脱硫工艺，RH脱碳结束测温定氧，立即加入铝粒脱氧合金化、之后立即依次连续加入合金进行成分调整，合金加完后立即开始顶枪喷粉；加入铝粒的量＝铝粒理论加入量+0.2‑0.4kg/t钢；喷粉时，控制喷粉速度与钢液循环流量相匹配；本发明从真空条件下脱硫热力学和动力学角度出发对具有顶枪喷粉功能的RH脱硫工艺进行改进，提高脱硫率。

本实用新型涉及一种硅钢片叠装上料用转运装置，包括一输送单元，输送单元包括输送支架、输送辊，在各个输送支架均配备有一用于接收裁切好的硅钢片并堆放形成硅钢片料堆的放置板；一供料单元，包括供料板、供料支架、供料辊、支撑组件；一转运单元，包括转运支架、转运底座、转运辊、推料板、推动机构、电磁铁、转运齿条、转运齿轮、转运导轨、转运导座、导向轮、行走滚轮。本实用新型的优点在于：通过输送单元、供料单元及转运单元之间的相互配合，从而能够将满料的放置板自动输送并呈日字形自动排布好，无需再由人工搬运放置，大大减少了人工劳动，降低了人工劳动强度。

介绍了重庆钢铁股份有限公司炼钢厂生产低碳低硅钢的脱氧工艺,对连铸过程中水口结瘤的原因进行分析,并提出了优化措施。生产实践表明:钢水中的活性氧质量分数控制在10×10-6～30×10-6时,单中包浇铸炉数由6～7炉提高到11～12炉,同时能保证连铸顺行和减少铸坯气孔。 The deoxidation process of low-carbon and low-silicon steel in steel plant of Chongqing Steel was introduced.The nuzzle clogging was analyzed and some measures were put forward.Production experiments showed that when the active oxygen was controlled between 10×10-6～30×10-6,the amount of furnaces would rise from 6～7 to 11～12,which will make the casting process work well and reduce casting holes. 

本实用新型公开了一种变压器铁芯硅钢片的收片装置，包括固定平台、硅钢片出料机构、压片机构、支撑平台和升降调节机构，所述固定平台设置在硅钢片出料机构的出料端下方，所述压片机构对应于硅钢片出料机构的出料口设置在硅钢片出料机构的上方，从所述硅钢片出料机构传送出的硅钢片通过压片机构压覆在固定平台上；所述固定平台上设置有升降调节机构，所述升降调节机构的升降端设置有支撑平台，所述支撑平台相对于固定平台在竖向方向上位移调节设置，能够对硅钢片叠放平面进行高度调节，保证出料高度的一致性，使得出料规整性较好。