借助OM、激光共聚焦显微镜、质谱仪和电解萃取等设备和方法，研究了添加微量稀土La（质量分数0.001 1%）的取向硅钢在轧制前采用不同加热保温时间对抑制剂固溶行为的影响。结果表明：当稀土取向硅钢在1 250℃分别保温10、20、30 min后，试验钢晶粒尺寸随保温时间延长有先快后慢的长大趋势；三种抑制剂元素Mn、Cu和Al均发生固溶，保温时间对Mn和Cu两种元素的固溶影响明显，固溶量分别由69.8%和43.7%增加至84.2%和85.2%；随着保温时间的延长，稀土取向硅钢中抑制剂的小尺寸未溶物逐渐减少直至消失，较大尺寸未溶物（300～600 nm）逐渐转变为小尺寸未溶物逐步溶入基体中，数量减少且未溶物的类型由复杂逐渐转变为单一。 In this paper the solid solution behavior of the inhibitor under various holding time in 0.001 1 %La oriented silicon steel during reheating had been investigated by using OM, LM, methods of electrolytic extraction and mass spectrometer. The results showed that grain size of the test steel increased significantly with the holding time prolonging when the rare earth oriented silicon steel was heated to1 250 ℃ and held for 10, 20 min and 30 min respectively, and the growth trend slowed down after ... 

针对硅钢连续生产线设备存在的故障、隐患以及精度等影响产品质量的问题进行分析及改造,实现保证生产线设备稳定运行、提高设备精度及硅钢产品质量的目的。 This paper analyzes and transforms the electrical equipment failures, risks existed in slicon continuous production line, and the effect of accuracy to product quality, in order to ensure stable operation of equipment in production line and improve the accuracy of device, quality of silicon. 

本发明提供虽然为薄壁但磁特性优异的方向性电磁钢板的制造方法。本发明的一个方案提供一种方向性电磁钢板的制造方法，其包括热轧工序、任选的热轧板退火工序、酸洗工序、冷轧工序、一次再结晶退火工序、成品退火工序和平坦化退火工序，在酸洗工序中，使用包含0.0001g/L～5.00g/L的Cu的酸洗溶液，冷轧钢板的板厚为0.15mm～0.23mm，一次再结晶退火工序的升温工序中的30℃～400℃的温度区域的平均升温速度超过50℃/秒且为1000℃/秒以下。

本实用新型公开了一种铁芯硅钢片卷材的自动放卷上料装置，包括放卷机、导向平台和防折组件，所述导向平台间距设置在放卷机的下方，所述导向平台与放卷机之间构成供料带缓冲的缓冲空间，所述料带在缓冲空间内呈U型状走向，所述导向平台的上方间距设置有防折组件，所述防折组件与导向平台之间构成供所述料带通过的导向通道，所述防折组件设置在料带的内弯侧。通过防折组件对料带的内弯侧进行支撑，能够有效的防止料带被过度弯折，能够对料带进行缓冲和缓冲保护，保证料带放卷上料的稳定性。

本发明公开了一种适应高频率工况下低铁损无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯—热轧—正火—酸洗—冷轧—连续退火—涂绝缘涂层并固化；所述冷轧步骤中，采用六辊单机架往复式轧机经5道次一次冷轧至目标厚度，冷轧过程中前三道次采用变速异步轧制方法，使钢板表层在剪应力作用下位错密度增加，这样在退火后表层晶粒尺寸细化而心部晶粒粗大，通过本发明的方法可生产得到心部为粗大等轴晶粒，表层为纳米级细等轴晶粒的电工钢产品，该产品的铁损P1.5/50≤2.35W/kg，P1.0/400≤14.0W/kg。

在实验室模拟CSP流程制备了不同含量稀土铈(质量分数0~0.018%)的1.2%Si无取向电工钢,并对其进行1 000℃×5min的再结晶退火处理,研究了铈质量分数对无取向电工钢夹杂物、显微组织、再结晶织构和磁性能的影响。结果表明:随着铈质量分数的增加,微细夹杂物数量、再结晶晶粒尺寸、{100}和{110}织构组分、磁感应强度先增后减,{111}织构组分、铁损先减后增;铈的质量分数为0.005 1%时,钢中的夹杂物数量最少,再结晶晶粒尺寸最大,有利织构最多,磁性能最优,铁损P15/50为3.253W·kg-1,磁感应强度B50为1.751T。 Non-oriented electrical steels containing different contents rare earth Ce element(0-0.018wt%) were prepared in the laboratory by simulated CSP(compact strip production)process,and then recrystallization annealing at 1 000 ℃ for 5 min were performed,the effects of Ce content on inclusion,microstructure, recrystallization texture and magnetic properties of non-oriented electrical steels were studied.The results show that with the increase of Ce content,the amounts of fine inclusion,the size of re... 

本实用新型公开了一种硅钢片焊接模具，包括底座，底座上均匀排布有多条滑槽，每条滑槽内连接有一根垂直设置的定位杆，定位杆底部穿过底座连接一气缸，气缸连接在底座底部。本实用新型结构设计合理巧妙，移动不同位置的定位杆，将定位杆与硅钢片贴合，不同滑槽内的定位杆之间相互错位，并利用气缸将硅钢片定位，这种结构不可以适用于各种形状的硅钢片，使用方便快捷。

应用CAFE法对6.5%Si高硅钢铸锭凝固组织进行了模拟研究,确定出了适合高硅钢组织模拟的模型。进一步用该模型研究了过热度及冷却条件对凝固组织的影响,结果表明,随着过热度的降低,凝固组织中柱状晶比例和晶粒平均面积均减小。水冷条件下,高硅钢铸锭凝固组织几乎全是柱状晶,而且晶粒粗大。空冷条件下,等轴晶区扩大,但柱状晶仍占主要部分。缓冷条件下,等轴晶区占主要部分,晶粒平均面积和空冷条件下相当。 The solidification structure of 6. 5% Si steel ingot was simulated based on CAFE method and the model suitable for simulating the structure of high silicon steel wad ascertained. The influence of superheat and cooling condition on the solidification structure were studied. It was shown that with the superheat decreasing,the proportion of columnar crystals decrease,and the average grain size become smaller. Under water cooling condition,the solidification structure of casting was composed of almo... 

本申请涉及硅钢制造技术领域，尤其涉及一种去除耐热刻痕取向硅钢中熔覆物的化学试剂及其方法。所述化学试剂的组分以质量分数计包括：强酸溶液：8％～20％；酸性氧化剂：5％～15％或助剂：5％～20％；其余为溶剂；其中，所述强酸溶液包括硫酸、盐酸和硝酸中任意一种。本申请实施例提供的该方法，通过10％～20％强酸溶液，可快速有效地去除取向硅钢刻痕处的熔融物，而酸性氧化剂：5％～15％，或助剂：5％～20％结合合适浓度的强酸溶液，可以将取向硅钢的基体破坏降到最小，两种综合作用，得到表面平整的耐热刻痕取向硅钢。

主要对硅钢退火炉耐材施工进行阐述,对一期工程与二期工程施工经验进行总结,包括设计、施工、耐材生产、人员素质等方面,指出了工程项目所所存在的不足,为同类型炉窑的施工提供借鉴。 This paper describes the construction of silicon steel annealing furnace refractories;and it was summarized the construction experience of phase-Ⅰ and phase-Ⅱ projects,including design,construction,refractory production,the quality of personnel etc,and pointed out the shortcomings of the project,which provided a reference for the construction of the same type of furnaces. 

本文介绍了无取向硅钢C6涂液的性能,研究了配水量、固化程度和涂层厚度等因素对无取向硅钢C6涂层性能的影响。结果表明,随着配水量的增加,完全固化所需的时间增加,涂液固体含量降低,涂层厚度减小;随着固化程度的提高,涂层硬度先增大然后趋于恒定,而柔韧性逐渐变差,在过固化后急剧恶化;涂层厚度对涂层的表面外观、附着性和绝缘层间电阻均有显著影响。 Based on the introduction about the performance of C6 varnish for non-oriented silicon steel sheets,effects of water amount,curing degree and coating thickness are discussed. Results show that with the increase of water amount,the time required to cure completely extends,and both the solid content of C6 varnish and the coating thickness decrease. As the curing degree increases,the hardness of the coating increases first and then tends to be constant,however the flexibility degenerates,especially... 

本发明涉及一种提高取向硅钢冷轧加工性的生产方法，工艺流程为：冶炼、连铸、热轧、常化、酸洗、冷轧、脱碳渗氮、涂MgO、高温退火、涂绝缘层及热拉伸平整；粗轧中坯厚度35‑45mm，两段常化后进行带钢横向分段式冷却水分布。本发明通过对热轧中坯厚度、终轧温度及卷取温度，常化冷却水量及控制方式的调控，使轧前表层晶粒尺寸降低5‑10μm、珠光体体积分数降低6％，轧材冷轧加工性明显改善、成材率可提高8％以上。通过后续冷轧、脱碳退火和高温退火等工序处理，可保证完善的二次再结晶组织及良好磁性能。