通过微观组织表征、高温拉伸和断口形貌分析,研究了钇(Y)元素对6.5%Si无取向硅钢组织、高温拉伸及断裂机制的影响。研究结果表明,添加Y元素可以在钢液中形成YS和YP的复合析出。YS和YP可以充当异质形核基底,提高形核率,细化凝固组织。热轧组织不均匀,由表层至芯部分别形成等轴晶、等轴晶/拉长晶和拉长晶的混合组织。退火后,热轧变形组织转变为等轴晶,含Y实验钢的退火组织得到明显细化。500℃时效处理后,含Y实验钢具备较低的有序度,300℃的拉伸断口呈现韧性断裂特征,断后伸长率达到20.2%。相反,无Y实验钢发生脆性断裂,断后伸长率仅为2.1%。研究结果证实,Y元素可以通过组织细化和降低有序度提高6.5%Si无取向硅钢的中温塑性。 The effects of yttrium(Y)on microstructure,elevated-temperature tensile properties and fracture mechanism of 6.5% Si non-oriented electrical steel were investigated by means of microstructure characterization,high-temperature tensile test and fracture analysis.The results showed that the doping of Y introduced composite Y-rich precipitates(YS/YP)in the melt.YS and YP precipitates were qualified for heterogeneous nucleation agents,which thus raised the nucleation rate and refined the solidificati... 

本实用新型公开了一种生产硅钢片的轧制装置，包括工作台，所述工作台的正面开设有收集腔，收集腔的内底壁滑动连接有收纳盒，工作台的上表面分别固定连接有两个支撑板和倒L型滑动台，两个支撑板的相对面分别转动连接有上压辊和下压辊，上压辊的外表面套设有两个调节环，两个调节环的相对面均固定连接有切刀，工作台的上表面开设有与收集腔相连通的下料孔，下料孔的内侧壁开设有滑动槽。该生产硅钢片的轧制装置，通过设置上压辊、下压辊与驱动电机，便于对硅钢片进行传动，通过设置调节环、切刀与固定螺栓，便于根据生产需求调节硅钢片切边的距离，从而使整个装置具有方便对轧制后硅钢片进行切边处理的效果，方便后续轧制工作的进行。

本发明公开了一种硅钢冷连轧轧制过程温度获取方法、装置及电子设备，通过获取硅钢冷连轧生产过程的工业参数数据以及各机架间硅钢的实际温度测试数据，然后基于工业参数数据以及预设初始模型，确定硅钢冷连轧生产过程的温度预测模型，接着基于硅钢轧制前的预热温度以及温度预测模型，得到硅钢冷连轧轧制过程各机架变形区出口与下一机架变形区入口之间的预测温度数据，再将预测温度数据与实际温度测试数据进行对比，并根据对比结果中的温度差异值对相应机架间的乳化液参数进行修正，直至温度差异值小于预设阈值，得到修正后的温度预测模型，能够用于实现硅钢冷连轧轧制过程中，任意采样点硅钢温度的获取。

一种薄规格中高牌号无取向硅钢酸轧生产工艺，属于无取向硅钢冷轧成型技术领域，该生产工艺在焊接前对焊缝预加热和焊接后对焊缝两次后加热，采用五机架六辊冷连轧机组轧制，其压下率分别为35％‑45％、35％‑45％，30％‑36％，25％‑30％，1％‑10％，第一二冷轧机间、第二三冷轧机间、第三四冷轧机间、第四五冷轧机间的单位张力分别为120‑130KN/mm2、130‑140KN/mm2、150‑160KN/mm2和160‑180KN/mm2，本发明的有益效果是，本发明通过对冷连轧的工艺进行改进优化，提高了薄规格中高牌号无取向硅钢带的轧制效率，提高了同板差的合格率，降低了轧制的断带率和轧烂率。

本发明提出一种预判取向硅钢冷轧脆断发生的方法，将酸洗带头20‑30cm进行剪切取样，在取到的样板上面注明工作侧和传动侧；将取好的样板送至焊缝检测冲压机处，通过冲压机对样板进行冲压，根据不同钢带厚度，设定不同冲孔机压力，对样板进行冲压后，通过观察裂纹形貌，预判常化卷在冷轧轧制过程中是否会发生脆断，本发明使带钢在冷轧前能够制定相应的对策措施，从而降低冷轧断带所产生的损失。

本发明涉及硅钢收卷技术领域，具体公开了硅钢冷涂后锥度张力收卷工艺，将张力卷筒装配到卷取机上，张力卷筒包括转轴和若干支撑板，若干支撑板形成圆筒结构，若干支撑板上连接块底部的斜面形成锥形结构；还包括位于转轴两端的驱动杆，驱动杆转动连接有锥形杆，锥形杆与锥形结构为锥度配合，锥形杆的长度为L；将硅钢头部搭接在张力卷筒外部，当硅钢在张力卷筒外部卷绕4～7圈后，驱动杆移动的速度为V；当锥形杆进入的距离为1/3L时，将速度降低至2/3V；当锥形杆进入的距离为2/3L时，将速度降低至1/3V；当锥形杆全部进入时，驱动杆停止移动，硅钢继续卷绕。本专利公开的收卷工艺利用了锥度张力原理，得到的硅钢卷不会坍塌。

为了消除硅钢在连续退火机组产生的浪形缺陷,对浪形缺陷产生的主要原因进行了分析。制定了相应控制措施,对炉内带钢张力、冷却段输出、碳套辊与带钢的同步性、无氧化炉燃烧状态等参数进行了调整;在生产组织上安排高低牌号宽窄规格穿插生产、定期更换碳套辊等,实施后效果明显。 The main cause leading to waviness defects of silicon steel is analyzed in order to eliminate the waviness defects of silicon steel in continuous annealing line.And thus corresponding measures for controlling these defects are made by means of adjusting these parameters such as the tension of silicon steel coils in continuous annealing furnace,the output in cooling section and the combusting condition of the non-oxidation furnace as well as keeping the synchronization between carbon sleeved roll... 

采用中、厚板坯生产技术对取向硅钢进行了研制和开发,对热轧及后工序样品进行了金相组织观察和EBSD分析,探讨了两种组织及织构的差异性,研究结果表明:除高温退火样品外,中板坯生产的取向硅钢各工序样品平均晶粒尺寸大;厚板坯生产的取向硅钢热轧和常化样品亚表层Goss织构强;中板坯和厚板坯的脱碳退火板织构没有明显区别。中板坯生产的取向硅钢成本低,产品磁性能和质量与厚板坯相当。 Grain oriented silicon steel was researched and developed by medium thickness slab and thick slab.Microstructures observation and EBSD analysis to the samples of hot rolling and following processes were carried out,respectively.The differences between the two kinds of microstructures and textures were discussed.The results show that the average grain sizes of every process samples are larger except that of high temperature annealing samples of grain oriented silicon steel produced by medium thic... 

本发明提供一种电磁屏蔽用1050铝/50W800无取向电工钢钢板生产方法，包括S1)、将轧制好的铝卷和钢卷分别放置在两个开卷机上开卷；S2)、开卷后分别采用HCl、NaOH溶液清洗；S3)、用旋转钢丝刷法对铝板、钢板待结合面进行机械处理10‑15s；S4)、将铝板、钢板置于丙酮溶液中超声波清洗2‑3min；S5)、将表面处理后的铝板、钢板进行预拉伸或者预压缩，S6)、将预应力处理的铝板、钢板边部进行焊接；S7)、将焊接好的钢铝板进行轧前的预热处理；S8)、然后进行连续退火炉中进行退火处理，本发明将金属铝板、钢板通过热轧轧制复合化结合在一起，界面剪切强度≥100MPa，反复弯曲次数≥10次。

【作者】 陶永根； ...

本实用新型涉及一种便捷型铁芯硅钢片组装系统。该便捷型铁芯硅钢片组装系统包括硅钢片叠放装置，硅钢片叠放装置包括固定座，固定座上通过轴承转动装配有齿圈，固定座上固定连接有与齿圈同轴的固定盘，固定盘的中心设有中心孔，固定盘上设有六个沿固定盘径向延伸的滑槽，六个滑槽沿固定盘周向均匀分布，每个滑槽内分别滑动装配有滑块，齿圈的上侧面设有上螺纹，滑槽的下侧面设有与上螺纹相匹配的下螺纹，滑块的内端设有定位板，定位板的外侧面上设有用于与硅钢片中心孔孔壁上的割槽相匹配的定位条。相比于现有技术，本实用新型能够对硅钢片进行定位，从而确保各片硅钢片的中心孔以及割槽相对应，提高了硅钢片叠放效率，从而提高了生产效率。

本实用新型涉及电机技术领域，具体涉及一种具有低应力结构的硅钢片、转子和电机。包括硅钢片、开设在硅钢片上的磁钢槽和嵌设在所述磁钢槽内的磁钢组件，所述磁钢组件包括多个磁钢组，所述磁钢组包括靠近转子边缘的一对小永磁体和靠近转子内侧的一对大永磁体，所述硅钢片在转子轭部沿周向分布有径向开槽，且所述径向开槽从硅钢片的中心向边缘延伸。其通过在转子轭部沿周向分设置从硅钢片的中心向边缘延伸的径向开槽，能降低大永磁体左右两侧铁芯刚度差距，从而有效降低隔磁桥处的应力，防止磁钢和铁芯产生形变而断裂。其无需改变电机转子外圆结构，在保证转矩输出的前提下，防止高速旋转时带来空气啸叫声。