本发明公开了一种改善取向硅钢边部变形的热处理辅助方法，在高温退火工序前，在钢卷的下端预设位置处放置阻热环并固定；在高温退火完成后，拆除固定件并移除所述阻热环。本发明通过施加阻热环，降低了取向硅钢卷在高温退火过程中的升温速率，降低了钢卷在升温及冷却过程中的胀缩量，有效改善了边部变形情况。同时，本发明由于采用一体式隔热材料，其装配及移除难度大幅度降低，有利于推广应用。

通过实验室25 kg真空感应炉冶炼和锻轧研究了0.26%～0.95%Al含量对0.5 mm 2.2%Si无取向硅钢冷轧板组织、织构和磁性能的影响。试验结果表明,0.26%～0.81%Al含量时,随钢中Al含量的增加,成品退火钢板的晶粒尺寸增加同时铁损减少;当Al含量大于0.81%时,随Al含量增加,钢板的晶粒尺寸减小,同时铁损增加。Al含量对硅钢板磁感的影响没有明显的规律。2.2%Si无取向硅钢的合适Al含量为0.48%～0.81%。 The effect of 0.26%～0.95%Al content on structure,texture and magnetic performance of 0.5 mm cold rolled sheet of 2.2%Si non-oriented silicon steel has been studied by a 25 kg vacuum induction furnace smelting,and forging -rolling in laboratory.Results show that as 0.26%～0.81%Al,with increasing Al content in steel the grain size of annealed finished sheet increases while iron loss of sheet decreases,and as Al content in steel is more than 0.81%,the grain size of sheet decreases while iron loss in... 

该电磁钢板用涂布组合物是含有环氧树脂、高温固化型交联剂以及无机微粒的电磁钢板用涂布组合物，相对于所述环氧树脂的100质量份，所述高温固化型交联剂为5～30质量份，所述无机微粒是从金属氢氧化物、在25℃下与水反应而成为金属氢氧化物的金属氧化物、以及具有羟基的硅酸盐矿物中选择的一种以上，所述无机微粒的体积平均粒径为0.05～2.0μm，所述环氧树脂的含量相对于所述电磁钢板用涂布组合物的总质量为45质量％以上，所述无机微粒的含量相对于所述环氧树脂100质量份为1～100质量份。

对碳-锰-硅钢进行不同配分温度的Q&P(Quenching and Partitioning)处理,测试了热处理后不同钢的力学性能和残余奥氏体含量,并用扫描电子显微镜和透射电镜观察其显微组织,分析了配分温度对显微组织和力学性能的影响。结果表明:试验钢显微组织基本由低碳板条状马氏体、块状铁素体和条状残余奥氏体组成;随配分温度的升高,试验钢的抗拉强度呈下降趋势,伸长率与奥氏体含量的变化趋势相同,但变化规律不确定;提高锰含量能稳定残余奥氏体,从而提高试验钢的伸长率,并使伸长率对配分温度不敏感。 The C-Mn-Si steel was quenched and partitioned at different partitioning temperatures,the mechanical properties and residual austenite contents were investigated,the microstructure was observed by SEM and TEM,and the effect of partitioning temperature on microstructure and mechanical properties was analyzed.The results show that the microstructure of the tested steel consisted of lath martensite with low carbon,nubby ferrite and banded residual austenite.The tensile strength of the tested steel ... 

本实用新型公开了一种实验室模拟硅钢带连续常化退火炉，属于热处理技术领域。该退火炉包括：炉膛，沿退火炉本体的长度方向贯通，所述炉膛的两端的开口处设有炉门，炉门上设有透气孔，炉膛内自左向右依次分为多个加热区；滑轨，沿炉膛的长度方向设于所述炉膛的底部；移动机构，设在滑轨上且能沿滑轨移动；牵引绳，由耐高温材料制成，其一端与移动机构连接，另一端延伸至退火炉本体的外部；牵引绳收放机构，设于退火炉本体的外部，并与牵引绳的外端连接，用于收放牵引绳。本实用新型的退火炉采用三段加热区域，独立控温，能够模拟硅钢带预热、加热、均热、冷却等连续常化工艺，实验条件更接近工业生产。

借助电子背散射衍射(EBSD)及ZEISS-200MAT金相显微镜对某钢厂普通取向硅钢(CGO)进行研究,研究结果表明:热轧板组织、织构沿板厚方向存在明显的不均匀性,在热轧板表层及次表层发生再结晶,同时存在强度较高的Goss织构,中心层存在较强的{001}<110>变形织构。冷轧组织均呈纤维状条带组织,一次冷轧后,热轧板中的Goss织构消失,织构主要为α、γ织构,经中间脱碳退火后,α、γ织构强度减弱,并出现一定强度的Goss织构和利于Goss织构发展的{554}<225>、{332}<113>等织构,经二次冷轧后,二次冷轧织构类型与一次冷轧织构一致,但织构强度不同。 The grain-oriented silicon steel produced by a steel factory was investigated by EBSD and ZEISS-200 MAT metallographic microscope.The results show that the textures and microstructures along thickness of hot rolled slab are inhomogeneous.The surface layer and the layer near that are recrystallized structure which has a high Goss texture,but there is deformation texture{001}<110>in the central layer.The structure after cold rolling is a structure like fiber strip.After the first cold rollin... 

对RH法(真空循环脱气法)生产的冷轧硅钢的脱硫原理及影响因素进行了分析研究。研究表明:降低顶渣中FeO、MnO的含量,提高钢液温度,增加脱硫剂的加入量并延长其循环时间有利于提高脱硫效率。 The principles of desulfurization and its influence factors of cold rolling silicon steel during RH process have been studied in this paper.The result indicated that reducing contents of FeO and MnO,rising temperature of the liquid steel,increasing quantity of desulfurizer,lengthening cycle time of desulfurzer are benefit for desulfurization. 

一种无取向电磁钢板用热轧钢板，其以质量％计，含有C：0.0010～0.0050％、Si：1.90％～3.50％、Al：0.10％～3.00％、Mn：0.05～2.00％、P：0.100％以下、S：0.005％以下、N：0.0040％以下、B：0.0060％以下、Sn：0～0.50％、Sb：0～0.50％、Cu：0～0.50％、REM：0～0.0400％、Ca：0～0.0400％及Mg：0～0.0400％，剩余部分为Fe及杂质；该无取向电磁钢板用热轧钢板的特征在于，在无取向电磁钢板用热轧钢板的板宽方向端部中，板厚中心部(t/2位置)的加工组织的硬度HD为Hv220以下。

本发明提供一种绝缘被膜的密合性和被膜张力优异的带绝缘被膜的方向性电磁钢板。是在方向性电磁钢板的表面具有以镁橄榄石为主体的基底被膜且在上述基底被膜的表面形成以硅磷酸盐玻璃为主成分的绝缘被膜而成的带绝缘被膜的方向性电磁钢板，通过使上述基底被膜和绝缘被膜中的Sr、Ca、Ba为特定的浓度梯度，从而使上述绝缘被膜的密合性和被膜张力提高。

本实用新型涉及硅钢生产设备技术领域，具体公开了一种硅钢清洗用多段式清洗辊结构，包括中间辊和可拆卸连接在中间辊两端的支撑辊，所述中间辊和支撑辊的外径相等，中间辊与支撑辊的外壁上均固定有刷毛，所述支撑辊远离中间辊的端部为封闭设置，且同轴固定有转轴。采用本专利中的清洗辊结构，只用更换中间辊即可，无需对整个清洗辊进行更换，节省了设备成本投入；另外将支撑辊远离中间辊的端部为封闭设置，则是为了防止在工作时，液体渗入，避免对清洗辊的内部结构产生腐蚀等问题。

本发明揭示了一种无取向硅钢及其生产方法。所述生产方法包括：按照Si0.8～1.1％、Mn0.2～0.4％、不添加Sn和Sb进行炼钢，并制坯；将铸坯加热到1060～1120℃并保温150min以上，而后轧成厚度40～45mm的中间坯，再经精轧、卷取得到厚度为3.00±0.25mm的热轧卷板，精轧开轧温度≤872℃+1000*(11*[Si]‑14*[Mn]+21*[Al])；精轧终轧温度≤820℃，卷取温度≤560℃；常化、酸连轧，得到厚度为0.500±0.005mm的冷硬卷，常化温度850～900℃；成品退火温度820～880℃，退火后经冷却、涂层和精整，得到无取向硅钢。

本实用新型涉及变压器铁芯装配技术领域，具体公开了一种硅钢片铁芯的装配工装，包括底座、对称设于底座上的两个承压条以及快速装夹机构；所述快速装夹机构包括设于两个承压条一侧的安装框架、安装于安装框架两侧的侧挡板、紧固组件以及将安装框架和承压条之间定位的卡接组件；所述卡接组件包括安装于安装框架一侧的定位块、以及开设于承压条一侧的定位槽，所述定位块的内部开设有安装槽，本实用新型通过快速装夹机构能够实现安装框架的快速定位，从而便于安装框架的安装，有效的提高了安装框架的拆装效率，有助于硅钢片铁芯的快速装配，可提高硅钢片铁芯的装配效率，增加硅钢片铁芯的生产效益。