本发明公开了一种控制无取向硅钢厚度稳定性的轧制工艺，涉及硅钢厚度控制方法领域。本发明通过降低硅钢精轧入口温度，并调节粗轧区域、精轧区域和卷取区域的生产参数，保证后续卷取工序的轧制稳定性及卷形质量，严格控制无取向硅钢的厚度稳定性。本发明提供的轧制工艺使硅钢的厚度命中率得到了明显提升，提升了后续冷轧工艺的轧制速度，轧制力波动减小，提高了产品质量。

以构建高磁感、低铁损、免轧制高硅电工钢铁芯为出发点,提出采用单辊甩带制备非晶铁硅合金薄带、微氧化法在铁硅合金粉末表面包覆高电阻率铁硅氧化物薄膜制备核壳异质结构高硅电工钢纳米粉末、放电等离子烧结快速成形制备颗粒间绝缘的高硅电工钢铁芯。研究了不同氧化包覆时间对SPS烧结试样密度、物相组成、微观结构和静磁性能的影响。研究表明,在氧化包覆5h烧结温度800℃工艺条件下,制备的6.5%Si高硅电工钢铁芯的静磁性能最佳,饱和磁化强度为128.84A.m2/kg、矫顽力为2.25kA/m、剩磁为3.47A.m2/kg。其饱和磁化强度与粉末压延法制备的高硅钢相当,但矫顽力降低了1/3。 The paper takes preparation 6.5%Si steel with high induction,low core loss and removing rolling as the starting point,amorphous Fe-Si ribbons was synthesized by melt spinning method,6.5%Si steel nanopowders with high resietivity core shell structure was prepared by the slight oxidation process and 6.5% Si steel iron core with evaluating internal was sintered by spark plasma sintering process(SPS).The essay focuses studies the effects of different oxidation cladding time on sample density,phase c... 

介绍了双蓄热燃烧技术的特点和高温硅钢加热炉的特点,探讨了双蓄热燃烧技术在高温硅钢加热炉中使用的技术难点,分析了双蓄热燃烧技术在高温硅钢加热炉上使用的可能性。 Introduced characteristics of double regenerative combustion technology and high temperature silicon steel reheating furnace,discussed technical difficulties for using double regenerative combustion technology,analyzed the possibility of double regenerative combustion technology applied to high temperature silicon steel reheating furnace. 

本发明提供一种无取向硅钢用涂层溶液及其制备方法和应用，以所述无取向硅钢用涂层溶液的总质量为基础计，所述无取向硅钢用涂层溶液包括如下质量百分含量的原料组分：磷酸盐溶液55％～60％；树脂溶液20％～25％；二乙二醇丁醚2％～4％；改性剂3％～5％；余量为水。由本发明所述无取向硅钢用涂层溶液形成的绝缘涂层厚度均匀，表面光滑，具有优良的绝缘性、耐腐蚀性、附着性，而且硅钢片的冲片性能好、叠片系数高。

本发明涉及一种在连续的退火和覆层线(1)中对非晶粒取向的电工钢带(2)进行再结晶退火的方法，其中电工钢带(2)在感应炉(5)中以至少80K/s的加热速率加热到至少680℃的温度，并且然后在可能的第二连续炉(8)中以最大20K/s的加热速率加热到至少820℃的温度，其中在感应炉(5)上游将电工钢带(2)首先经由第一连续炉(3)以至多60K/s的加热速率加热到至少300℃的温度。

无取向硅钢的磁性能主要取决于铁素体的晶粒尺寸、晶体织构和钢中的夹杂物。通过合适的化学成分设计以及采用适宜的夹杂物控制技术,可以获得最佳的夹杂物控制效果,使其纯净度大幅度提高或者无害,最终获得磁性能优良的高级别无取向硅钢。同时,为满足节能、环保、高效需求,无取向硅钢正朝着节能降耗、环境友好以及多功能、高效率、易加工等方向发展。 The magnetic properties of non-oriented silicon steel mainly depend on the grain size of ferrite,the crystallographic texture,and the inclusions in the steel.The optimum inclusion control effects can be obtained through a suitable chemical composition design and an appropriate inclusion control technique,and then the liquid steel will get be clean or the inclusion will get be harmless,finally the excellent magnetic property of the non-oriented silicon steel can be obtained.Meanwhile,in order to ... 

试验2.3Si无取向硅钢(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al)冷轧板由常化和未常化的2.5 mm热轧板冷轧至0.6 mm(压下率76%),经750~950℃2.5 min中间退火后再冷轧至0.5 mm(压下率16.7%),成品板经890℃+960℃2.5 min退火。研究了中间退火温度对该钢晶粒尺寸、织构和磁性能的影响。结果表明,随中间退火温度的升高,二次冷轧前晶粒和成品晶粒增大,成品中不利织构组分{111}和{112}减弱,磁性能得到改善。热轧板经过常化时的磁性能明显好于未经常化时的磁性能,但中间退火温度较高时常化对磁性能的有利作用减弱。 The test cold sheet of 2.3Si non-oriented silicon steel(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al) is first cold-rolled from normalized and un-normalizing 2.5 mm hot-rolled plate to 0.6 mm sheet(reduction 76%),then intermediate annealed at 750~950℃ for 2.5 min and double cold-rolled to 0.5 mm sheet(reduction16.7%),the finished sheet annealed at 890℃+960℃ for 2.5 min.Effect of the intermediate annealing temperature on grain size,texture and magnetic performance of the steel has been studied.... 

本发明提供一种绝缘被膜的密合性和被膜张力优异的带绝缘被膜的方向性电磁钢板。是在方向性电磁钢板的表面具有以镁橄榄石为主体的基底被膜且在上述基底被膜的表面形成以硅磷酸盐玻璃为主成分的绝缘被膜而成的带绝缘被膜的方向性电磁钢板，通过使上述基底被膜和绝缘被膜中的Sr、Ca、Ba为特定的浓度梯度，从而使上述绝缘被膜的密合性和被膜张力提高。

本实用新型提供了一种便于清洗的冷轧硅钢生产用轧机，两个所述支架安装在底座上，所述支架上设有安装盖，支架之间设有上支撑辊，上支撑辊下设有上工作辊，上工作辊安装在支架之间，上工作辊下设有下工作辊，这种便于清洗的冷轧硅钢生产用轧机，在使用的时候，可以对于冷轧硅钢进行生产处理，生产之后可以进行清洗设备，安装的上工作辊与下工作辊可以对于硅钢进行冷轧处理，在工作时，两侧安装的承重块可以对于机械进行一个固定，起到稳固作用，两侧安装的转动辊可以放置硅钢，安装的清洗头可以对于机械进行清洗，吹风器可以对于机械进行干燥处理，防止机械生锈，底座上安装的沥水板可以隔断灰尘和铁屑，防止堵塞。

本实用新型涉及一种改进的点火器线圈硅钢片结构，包括E型件和I型件，所述E型件和I型件组合成日字形，它们可相互转动；所述E型件包括竖边和设置在竖边三个横边，三个横边分别为上横边，中横边和下横边，它们分别与竖边垂直连接；其中所述竖边的转角位置圆角处理，竖边外侧为弧形边；所述上横边的端面设置插缝；所述中横边的端头设置凹部；所述下横边的端头设置凸部；所述I型件上端两侧对称设置凹台；所述凹台具有弧形凹边；所述I型件通过凹台设置在插缝可以旋转。本实用新型设计新颖，改进巧妙，由于E型件具有弧形边可以有利于拾取，方便工作操作，E型件和I型件采用插合的方式，整体结构稳定，便于安装，增加了组合体的稳定性。

本申请提供了一种高强度变压器取向硅钢片，属于变压器硅钢片领域，该一种高强度变压器取向硅钢片，包括第一硅钢片本体和固定机构，所述第一硅钢片本体表面开设有两个第一通孔、两个第一通槽和一个第二通槽，所述第一通槽间隔设置在两个所述第一通孔之间，所述第一硅钢片本体表面设有滑条，所述第二硅钢片本体插接在所述通槽内，所述第一螺纹杆插接在所述第二通孔内，所述第二螺纹杆插接在所述第一通孔内，所述螺帽螺纹连接在所述第一螺纹杆和所述第二螺纹杆两端，该一种高强度变压器取向硅钢片能够将垂直和横向均产生拉力来固定硅钢片减轻了振动，噪音小且利用凹槽和滑条进行堆叠能够精确的将硅钢片表面的通孔对齐。

本发明属于双取向硅钢技术领域，公开了一种双取向硅钢薄带及其制备方法，包括：选取具有Si、Al、Mn、C和Fe，且具有一定取向的硅钢薄带；将其进行冷轧；将冷轧板在N2、H2保护气氛中进行退火处理。本发明通过合理的轧制和退火工艺搭配，使具有Goss取向的硅钢薄带转变为具有旋转立方取向的硅钢薄带，将单取向硅钢转变为双取向硅钢。本发明具有工艺简单和便于利用钢铁企业现有设备的特点，所制备的双取向硅钢薄带具有双向铁损低和磁感高的性能。本发明制备的双取向硅钢薄带在与轧向成45°的两个方向上具有优异的双向磁性能，解决了现有双取向硅钢薄带的制备工艺复杂、设备要求高、不利于工业生产的问题。