硅钢资料

研究的两种取向硅钢（%:No1-0.042C、3.16Si、0.009Al、0.07Mn、0.50Cu、0.015S、0.0084N和No2-0.040C、3.20Si、0.014Al、0.22Mn、0.49Cu、0.016S、0.008 2N）由50 kg真空感应炉冶炼,锻成（mm）350×120×35板坯,经1 250℃30 min加热,开轧温度1 100℃,5道次热轧成2.3 mm板,终轧温度950～1 000℃。实验结果表明,两热轧板沿板厚方向存在组织和织构的不均匀性,热轧板次表层为再结晶组织,有较强的Goss织构组分;中心层为形变组织,具有典型的形变织构。含0.22%Mn的No2钢次表层{110}〈001〉织构组分比含0.07%Mn的No1钢弱,中心层{001}〈110〉织构组分大大强于0.07%Mn No1钢,导致两者磁性能差异,0.22%Mn No2钢磁感应强度(B₈₀₀)和铁损(P_1.7/50)分别为1.87 T和1.24 W/kg,0.07%Mn No1钢分别为1.88 T和1.18 W/kg。 Studied both grain-oriented silicon steels（%:No1- 0.042C,3.16Si,0.009Al,0.07Mn,0.50Cu, 0.015S,0.0084N and No2-0.040C,3.20Si,0.014Al,0.22Mn,0.49Cu,0.016S,0.0082N） are melted by a 50 kg vacuum induction furnace,forged to（mm） 350×120×35 slab,heated at 1 250℃for 30 min,with beginning rolling temperature 1 100℃hot-rolled to 2.3 mm plate by 5 passes,finishing-rolled at 950～1000℃.Test results show that the structure and texture along thickness of both hot-rolled plates are inhomogeneous:the subsurface ... 

本申请提供了一种取向硅钢铸坯的制备方法及铸坯系统，该制备方法用于对精炼后的钢水进行连铸处理，所述连铸处理包括以下步骤：进行凝固处理，以使所述精炼后的部分钢水凝固形成坯壳；凝固处理时，进行电磁搅拌，以使所述精炼后的剩余钢水最终形成铸坯，其中，所述电磁搅拌的位置和结晶器出口的间距为0.3～1.5m，所述电磁搅拌的电流范围为0A～900A。上述制备方法通过调节电磁搅拌的位置和电流大小来调节电磁搅拌的强度，进而通过电磁搅拌的强度来调节等轴晶的生成量，扩大等轴晶率的范围。

该电磁钢板用涂布组合物含有环氧树脂、酚类固化剂(A)、以及从芳香族胺和双氰胺中选择的一种以上的胺类固化剂(B)，所述酚类固化剂(A)的含量相对于所述环氧树脂100质量份为1～40质量份，所述胺类固化剂(B)的含量相对于所述环氧树脂100质量份为0.5～5质量份。

本发明公开了一种变压器硅钢片回收检测装置，包括检测传送带、防层叠机构、CCD摄像头、分料传送带、合格料箱和不合格料箱，所述防层叠机构和图像提取机构沿检测传送带传送方向依次布置，所述防层叠机构包括剥离辊，所述剥离辊及CCD摄像头均位于检测传送带上方，剥离辊与检测传送带向靠近的一面移动方向相反，分料传送带位于检测传送带后方，合格料箱与不合格料箱位于分料传送带后方，本发明能够将回收的硅钢片进行一一的快速检测，并对检测结果进行分类，检测效率高。

本发明公开了一种硅钢氧化镁废水资源化处理方法及处理系统，硅钢氧化镁废水进入过滤浓缩干化一体化装置经预过滤、过滤、干燥、排泥后得到清液和泥饼；泥饼经烘干后得到烘干泥饼；烘干泥饼溶解于硫酸溶液中，反应后的混合液固液分离得到上层清液和沉淀物，上层清液经中和、蒸发结晶后得到结晶物，沉淀物进行清洗、烘干处理。本发明还设计了实现上述处理方法的处理系统，该系统包括过滤浓缩干化一体化装置、烘干装置、溶解装置以及产水箱；本发明的硅钢氧化镁废水经处理后的清液满足回用要求，可返回机组循环利用，实现废水回用，泥饼经烘干、溶解后可分别作为钛白粉生产原料和土壤改良剂，具有经济环保双重效果，以及良好的社会效益和环境效益。

本发明属于退火工艺技术领域，公开了一种高牌号无取向硅钢剪切方法，包括：待剪切带钢由夹送辊输送到达剪切位后，夹送辊释放对所述待剪切带钢的夹持；位于所述待剪切带钢下方的下剪刃上移，推顶所述待剪切带钢在低张力状态下持续向上运动；在所述待剪切带钢与上剪刃接触后，将所述待剪切带钢剪断。本发明提供的高牌号无取向硅钢剪切方法能够极大的减少高牌号无取向硅钢的剪切缺陷，降低废品量，提升剪切效率。

本实用新型涉及物料混合技术领域，尤其为一种用于硅钢绝缘涂料温控反应釜，包括反应釜，所述反应釜右侧上方固定连接有输料管，所述输料管右端面固定连接有电机外壳，所述输料管右侧上方内部固定连接有入料管，所述电机外壳内部右侧固定连接有第二电机，所述第二电机左侧顶端转动连接有输料轴，所述反应釜上端面固定连接有第一电机；本实用新型中,通过设置的输料轴，能将物料慢慢输送至反应釜内，防止一次性将物料倒入反应釜中发生强烈反应，并且将小块物料放置进入料管时，可以在入料管内进行堆积，而第二电机旋转带动输料轴运动时，可以将入料管底部的物料卷进输料轴的空隙中，移动至顶端，物料会自动落下，非常方便。

对无取向电工钢中的夹杂进行了系统的分析。利用小样电解,采取不同电解液,不同的分离方法对无取向电工钢中稳定和不稳定夹杂物进行了提取、分离和收集。利用扫描电镜(SEM)、X-射线衍射、ICP等对电解分离收集的夹杂物进行了定性和定量分析。 The inclusion analysis of the non-oriented electrical steel has been investigated.By using small sample electrolytic analysis,with different electrolytes and different separation ways,the stable inclusions and unstable inclusions was drew,separated,and collected.With utilizing the methods of SEM,X-ray and ICP,the qualitative and quantitative analysis of inclusions in the non-oriented electrical steel was obtained. 

基于简化的取向硅钢片模型,系统地对不同的交流激励下的硅钢叠片内铁损、交链磁通和空气中指定位置的法向漏磁的分布进行了\"单片级\"的测量,并建立了相应的硅钢叠片级问题的三维有限元分析模型,进行了大规模的数值计算分析。模型实验和数值分析的结果表明垂直进入硅钢片的漏磁通和损耗呈现浅透入的特点,在硅钢片内引起的涡流损耗在总铁损中占据了\"举足轻重\"的份额。用电磁场有限元分析软件MagNet瞬态场时步法计算结果与测量结果相吻合,说明本文方法研究复杂的硅钢叠片问题的有效性。 The measurement and 3D finite element analysis of the iron loss,interlinkage flux inside the laminated silicon steel sheets and the magnetic flux densities at the specified positions are carried out based on a verifying silicon steel sheet model.The modeling results show that the leakage flux vertically through the silicon steel sheets has the peculiarity of shin effect,and the eddy current loss caused by the AC leakage flux is a significant component of the total iron loss.The calculated result... 

本发明涉及一种高压电机用无取向硅钢50SBW600的制备方法，包括，S1，将装有精炼钢水的钢包运至回转台，回转台转到浇铸位置后，将钢水注入中间包；S2，中间包通过水口将所述钢水分配至若干个结晶器中，所述结晶器中设置有浸入式水口，S3,钢水在结晶器内生成晶核，结晶器将带有晶核的钢水下放至通道；S4，通道上设有第二电磁搅拌器，第二电磁搅拌器对通道内钢水进行电磁搅拌,所述钢水在通道中逐步转换为钢坯；S5,拉矫辊将的所述钢坯拉出通道并对钢坯进行形态矫正；S6,切断装置所述钢坯进行切割。本发明通过在无取向硅钢50SBW600制备过程中设置双电磁搅拌装置，充分保证连铸过程中钢坯中的等轴晶数量，保障了产品表面缺陷质量。

本实用新型公开了一种硅钢片组扣件自动压平装置，包括：定位单元，定位单元包括转盘、校位板和第一驱动组件，第一驱动组件连接并驱动校位板沿竖直方向运动，校位板滑动连接有第一校位柱，第一校位柱相对转盘偏心布置；第一推送单元，位于转盘的一侧，第一推送单元包括第一推送气缸和第一推块，第一推送气缸连接并驱动第一推块沿水平方向运动；冲压单元，位于转盘背离第一推送气缸的一侧，冲压单元包括第二驱动组件和冲压柱，第二驱动组件连接并驱动冲压柱沿竖直方向运动。转盘、校位柱和第一驱动组件配合，周向定位硅钢片组，再通过冲压柱将凸出于硅钢片组的扣件压平，完成硅钢片组的整形，整体更为美观，方便后续的装配使用。

本实用新型涉及一种硅钢片纵剪边料收卷装置，包括：用于将收卷装置固定于地面的机架底座，机架底座一端设置固定支架，固定支架上安装电动定尺收料盘；在机架底座上设置电动可移动支架，电动可移动支架在机架底座的长方向上相对固定支架移动，电动可移动支架上安装电动可调收料盘；电动可移动支架、电动定尺收料盘、电动可调收料盘与PLC控制系统连接，PLC控制系统用于控制电动可移动支架的移动距离、以及控制电动定尺收料盘和电动可调收料盘的收料速度。将本实用新型的硅钢片纵剪边料收卷装置安装在硅钢片滚剪线切刀后面的输送平台的下部，卧式布局，不占用外部空间，和滚剪线无缝集成在一起，自动完成硅钢片纵剪边料的收卷工作。