本发明适用于电机硅钢片卷绕成型，用于各种条形冲带的电机定子铁芯卷绕机构，它包括PLC控制系统、人机操作面板、精密双轨道移动架、锁紧机构、同步电机、条形硅钢片导向槽、左右立板、一对可调整平导轮、一对齿轮、传动主轴、气（液）可调节机构、上锥形压辊、下锥形压辊、凸轮盘、驱动定位销、从动轴、左右移动护板、调整锁紧螺母、硅钢片收紧定型器、收集旋转盘、成型螺栓、特制吊装螺栓、旋转电机及机架等。采用本机构，可将各种规格条形冲带辊压成螺旋状，经收紧定型器处理后，定型的叠片不会出现褶皱,可满足不同电机定子铁芯的要求，加工质量较佳。

在现普通冷轧无取向硅钢的基础上,降低Si含量,复合添加少量辅助元素,组合热轧板处理和成品退火加热技术,研制出了免常化处理的高磁感、低铁损并具有良好耐酸腐蚀性能的新系列无取向电工钢。 Based on existing common cold rolled non-oriented silicon steel,a new series of non-orientedelectrical steel with high induction,low core loss and excellent anti-corrosion property has been developed by reducing Si element,adding complexly a small amount of supplementary elements,and employing combined treatment of hot rolled sheet and finished product annealed heated technology. 

采用CVD法制备6.5%Si高硅钢,介绍了具体的制备工艺过程,研究了温度对渗硅速率和试样质量减轻的影响,同时分析了扩散时间对高硅钢中硅分布的影响。结果表明:在CVD反应过程中,反应温度高于1050℃将大大提高渗硅速率,但当温度大于1200℃后,渗硅速率趋于稳定;渗硅后,试样会减轻、减薄,随着温度升高,试样质量减轻的速率逐渐增大,在1200℃左右趋于稳定;扩散时间越长,硅分布越均匀,结合制备效率进行考虑,满足Δw表-中/b≤5的时间为适宜的扩散时间。 6.5%Si high silicon steel was manufactured by using CVD method and the process was introduced,the influence of temperature on the siliconizing rate and quality reducing rate,diffusion time on silicon distribution were investigated.Results as follows: the siliconizing rate will increase quickly when the temperature is higher than 1050 ℃,but the siliconizing rate will become steadily as the temperature up to 1200 ℃;The quality reducing rate will increase with the elevating of temperature and the r... 

本实用新型公开了一种硅钢炉底辊套管生产用专用夹具，包括工作台，所述工作台的顶端表面设置有旋转云台，所述旋转云台的顶端表面设置有固定柱，所述固定柱通过转轴安装有固定杆，且转轴的端部通过联轴器安装有第一电机，所述固定杆的端部通过转轴转动连接有安装杆，所述转轴的端部通过联轴器安装有第二电机。本实用新型中，通过旋转云台、固定柱、第一电机、固定杆、第二电机、安装杆、第三电机、连接杆和机械爪的相互配合使用下，实现了对炉底辊套管的全自动夹取，有效的降低现场工作人员的劳动负荷，避免操作人员通过夹具在夹取可能出现的意外事件，极大的提高了夹取效率。

本实用新型公开了一种硅钢卷放卷辅助装置，包括支撑板、摆臂、气缸和连动杆，所述摆臂一端通过第一转轴枢接在支撑板上，所述连动杆的一端通过第二转轴枢接在摆臂的中部，另一端通过转轴与气缸的输出端连接，所述气缸的缸筒固定在支撑板上，所述摆臂远离支撑板的一端设置有承载座，所述承载座上开设有弧形槽口，所述槽口处设置有滚动组件；所述滚动组件包括设置在承载座上的第一支撑架和可转动设置在第一支撑架上的滚柱。其可有效防止硅钢卷从辊筒上掉落，保证了生产的安全性。

运用EBSD和光学显微镜,研究了0.25%~0.45%Cu对无取向电工钢热轧板显微组织,成品板显微组织、织构和磁性能的影响。实验结果表明:卷取过程中Cu元素在热轧板表层的偏聚作用显著阻碍了热轧板表层再结晶晶粒长大,导致热轧板表层晶粒尺寸随着Cu含量增加而逐渐较小,但热轧板中间晶粒尺寸变化不大。同时发现Cu元素能够明显改善织构类型,使有利织构组分增加,不利织构组分减少,同时减弱织构强度。从实验结果可知0.35%Cu能够显著改善电工钢的磁性能,铁损P15/50最低达到4.1 W/kg,磁感B50最高值达到1.8 T。 Effects of high content Cu on microstructure of hot rolled plates and microstructure,texture and magnetic properties of annealed finish product plates of non-oriented electrical steel were examined by means of EBSD technique and optical microscope. The results show that surface segregation of Cu significantly hindered recrystallized grain growth of surface layer in hot rolled plate during the coiling,as a result,the surface grain sizes of the hot-rohed plates decrease with the increase of Cu con... 

分析总结退火工艺各参数对冷轧无取向硅钢磁性能的影响,结合设计和生产实践经验介绍退火工艺中各参数的实际生产取值,并针对现生产工艺过程中出现的典型问题提出解决办法。 It is analyzed and summarized the great influences on magnetism of cold rolled non-oriented silicon steel affected by various annealing process data in this article.The relevant settled ways is raised.According to the actual value presetting ways for various annealing process data based on design and production,as well as typical problems occurred during production. 

目前随着电工钢用户冲压设备的升级,冲压速度逐步提高,对电工钢产品的硬度和强度指标提出了更高的要求。与普通硬度级别的无取向硅钢相比,高硬度50BW600的Hv硬度提高15~20,达到125以上,同时对电磁性能指标也有较高要求。本钢通过化学成份和热轧及冷轧连退生产工艺的设计,经过小批量生产试验,满足用户要求。通过对工艺的严格控制,在大批量生产过程中,保证了产品的力学性能和电磁性的检验合格率。 Currently with upgrading of stamping equipment of silicon steel user, gradually increasing of stamping speed, propose higher demand for hardness and strength of silicon steel. Compared with conventional 50BW600, high hardness 50BW600 have higher hardness, reach greater than 125Hv. Through design of chemical composition with hot mill and annealing, production test of small quantities, stamping performance meet user request. 

本发明公开了一种硅钢片压装工装，其涉及电机生产技术领域。其技术方案要点包括下压板，所述下压板上设置有限位结构，所述限位结构用于在硅钢片压装过程中对硅钢片进行限位；所述限位结构包括能够转动调节的限位挡块，所述限位挡块包括多个分别用于对不同尺寸规格的硅钢片进行限位的限位面，且该多个所述限位面与限位挡块的转动轴线之间的最小距离均不相同。本发明能够适用于多种规格的硅钢片，而且操作方便，稳定性好。

本实用新型公开了一种能限位的硅钢片，包括主体，主体的上表面设置有限位柱，限位柱的轴心处开设有散热孔，主体的上表面开设有限位槽，主体的外壁设置有凹槽，主体的下表面设置有限位凸起，主体的下表面开设有限位孔；该一种能限位的硅钢片通过在主体的外壁设置凹槽可以方便拿取，在其上下表面分别设置限位柱与限位孔，可以使主体间的位置相对固定不会轻易挪动。

一种硅钢生产线上的牵引装置，包含有底座（1）、支架（2）、平移机构（3）、上压板（4）、下托板（5）、气缸（6）、转向辊（7）和对中摄像头（8）；所述的平移机构（3）包含有长条齿轮（14）、齿轮（15）、电机（16）和滚轮轴承（17）；其特征在于：所述的齿轮（15）固定在电机（16）的输出轴上，并且与长条齿轮（14）啮合；使得平移机构（3）可以由电机（16）驱动在导轨（10）上左右滑动。本实用新型通过气缸（6）驱动上压板（4）和下托板（5）夹紧钢带（9），由平移机构（3）带动钢带（9）进行左右平移，避免了原先夹送辊刮伤钢带（9）表面涂层，减少了带头的浪费。