硅钢资料

本发明涉及金属冶炼工艺，尤其是一种降低无取向硅钢W800冶炼成本的方法，开吹阶段，着火后，加入头批渣料，石灰加入量占石灰总加入量的70%，石灰石加入量占石灰石总加入总量的100%，轻烧白云石加入量占轻烧白云石总加入总量的100%，待化渣后，枪位降低；化渣后将剩余30%石灰加入，加入剩余石灰过程中利用矿石调整温度；吹炼后期，并逐步压枪，终点拉碳枪位至1.4m，并使枪位在此高度不少于30s；到达冶炼终点。本工艺通过降低转炉渣量、提碳降氧和提高终点温度来减少铁水锰氧化量和促进氧化锰还原量，进而降低RH金属锰加入量，降低生产成本。

根据相关的取向电工钢典型专利技术,概述了日本高磁感低铁损取向电工钢低温板坯加热、抑制剂合理调节、关键成分Mn、C、Sn和Sb调节与利用、新型退火剂和绝缘溶液的制备及细化磁畴等生产工艺最新动态和进展情况,并提出了国内企业申请取向电工钢专利时应当借鉴之处。 According to related typical patent technology for grain-oriented electrical steel sheets,the recent trends and progress situation for production process of grain-oriented electrical steel sheets with high magnetic flux density and low core loss in Japan are summarized including low temperature slab heating,suitably regulating inhibitors,adjusting and utilizing key element Mn,C,Sn and Sb,manufacturing for new annealing agent and insulating solutions,and fining magnetic domain,and some suggestion... 

针对节能电机对无取向电工钢在磁性能方面的特殊要求,采用普通W600牌号的热轧板为原料,通过大量的现场工艺试验,研究总结出了\"超低张力\"的运行工艺、\"先快后慢\"的加热工艺、\"先湿后干\"的退火脱碳工艺、\"先缓后急\"的冷却工艺,生产出P1.5/50≤4.0 W/kg、B50≥1.70 T的冷轧电工钢产品,满足了节能电机的要求。 Based on the special requirements of no-oriented electrical steel for saving energy motor in magnetic aspects,using common W600 brand of hot rolled plate as raw material,through a large number of real tests,an ultra-low tension process,heating process which was quick at first and then slow,annealing decarburization process which was dry after the first wet,and a cooling technology of \"slow after the first urgent\" were concluded.Electrical steel product with P1.5/50≤4.0W/kg,B50≥1.70T was produced... 

本实用新型公开了一种硅钢片落料收集箱，涉及到硅钢片加工领域，包括支撑架，所述支撑架的顶端通过回转轴承活动连接有收集箱，所述支撑架的一端固定连接有落料筒，所述收集箱的顶端固定连接有进料口，所述收集箱的下端一侧固定连接有出料口。本实用新型通过在支撑架上设置有可活动的落料筒，落料筒能够根据不同型号的硅钢片将出料口转动至不同的收集箱处，使得本装置能够将不同型号的硅钢片进行分类收集，提高了本装置的工作效率，并通过限位组件能够将落料筒限位，防止落料筒随意转动，保证了本装置收集的稳定性，同时在落料筒的内部设置有缓冲块，缓冲块在阻尼板和缓冲弹簧的作用下起到了阻尼缓冲的作用，避免硅钢片在落料的过程中受损。

【摘要】 <正>编号:2012016获奖等级:特等完成单位:...

结合工业化生产的高效硅钢,进行了RH精炼稀土处理试验研究。针对不同的稀土处理条件,观察了夹杂物的形貌和尺寸分布,探讨了稀土处理后钢中的夹杂物形成、变化规律。结果表明:试验条件下,最佳的稀土合金添加数量为0.6～0.9 kg/t。经过合适的稀土处理后,可以有效抑制尺寸相对较小的、不规则的AlN、MnS复合夹杂生成,促进钢中微细夹杂物的聚合、上浮,钢质纯净度得到明显提高。此时,钢中全氧含量最低,脱硫效果最佳,钢中的夹杂物主要是尺寸相对较大的、近似球形或者椭球形的稀土类夹杂。 Based on the industrial production of non-oriented silicon steel,the experiment on RE treatment during the RH refining process was studied.The morphology and the size distribution were observed for the steel specimens treated with different RE treatment conditions.Further more,the formation and change of inclusions of final steel sheets after RE treatment were discussed.The results show that the suitable RE added amount was 0.6～0.9 kg/t.After the suitable RE treatment,the formation of AlN and Mn... 

通过测试取向硅钢不同工艺条件下的碳含量,探讨了CGO取向硅钢碳含量控制的最优处理条件,研究了脱碳温度和脱碳时间对相同初始碳含量取向硅钢的脱碳效果的影响。结果表明,在气氛为(15%~20%)H2+(75%~80%)N2,炉压差为10~20 Pa的条件下,CGO取向硅钢合适的脱碳温度为1 073 K~1 123 K,脱碳时间为10~20 min。在该处理条件下,能取得较好的脱碳效果。 By means of testing carbon content of oriented silicon steel below the distinct technical conditions,inquires the excellent handle terms of carbon content controlling for CGO oriented silicon steel,studies effects of decarburization annealing temperature and decarburization annealing time to the oriented silicon steel decarburization efficiency in same initial carbon content.The results show that,under the condition of atmosphere(15% ~ 20%) H2+(75% ~ 80%)N2 and furnace pressure difference 10 ~ 2... 

研究了CSP流程试制50W270高牌号无取向硅钢热轧→常化→冷轧→退火过程中织构的演变.利用电子背散射衍射技术对全流程织构进行测量和分析.发现热轧板织构在厚度方向上存在较大差异,表层主要为铜型、黄铜和高斯织构,1/4层存在微弱的高斯织构和旋转立方织构,中心层以γ纤维织构和旋转立方织构为主,还含有较弱的α纤维织构.与热轧板相比,常化板表层和1/4层织构变化不大,中心层旋转立方织构和α纤维织构增强.冷轧板各层均具有α纤维织构和γ纤维织构.与冷轧板相比,成品板各层中α纤维织构基本消失,还出现了立方织构和高斯织构. This article focuses on texture evolution in 50W270 high-brand non-oriented silicon steel produced by CSP in hot rolling,normalizing,cold rolling,and annealing processes.The texture in the whole process was measured and analyzed by electron back-scatter diffraction.It is found that the texture along the thickness direction in hot-rolled strips changes obviously;there are mainly copper,brass,and Goss textures in the surface layer;the 1/4 layer has weak Goss texture and rotating cube texture;γ-fib... 

【作者】 王磊； ...

本发明公开了一种提高薄板坯连铸生产高铝无取向硅钢可浇性的方法，在保证生产顺行、质量稳定的基础上，能使高铝无取向硅钢连浇炉数由10炉提高至16炉，在提高小时产量、降低生产成本方面效果显著。

本发明提供了一种轴向开关磁阻电机转子硅钢块的成型方法，包括(a)提供一硅钢片盘，其中所述硅钢片盘具有内端部和外端部，及贯穿所述内端部和所述外端部的多个固定孔，相邻的两个所述固定孔之间形成硅钢块；(b)提供多个齿棒，逐一将多个所述齿棒依次插入于所述固定孔；(c)提供一固型组件，将所述固型组件固定于所述内端部和所述外端部上；(d)沿着所述硅钢块和所述固定孔之间界定的切割位置进行切割，以获得组装转子的多个硅钢块。所述硅钢片盘通过所述固定孔分隔成多个形状一致的所述硅钢块，多个所述硅钢块通过切割分离，并可对应组装成一转子，成型方便快捷，还保障产品形状的一致性，实现工业化批量生产。

本发明公开了一种低损耗宽料取向硅钢的生产方法。本发明所述生产方法是通过在罩式炉的内罩中增加带有通气孔的聚气罩及与聚气罩配合的炉底板，配合工艺优化，控制原料化学成分，使气体和钢卷之间的浓度更均匀，反应更充分，气流流动方向更易控制，所制备的取向硅钢性能稳定，磁性能优良，且铁损达到1.12W/KG以下的比例提高至98.77％，平均铁损达到1.06W/KG以内，使取向硅钢卷的铁损大幅度降低，电磁性能更好。