研究二次冷轧压下率对于硅的质量分数为3.0%的无取向硅钢组织结构和磁性能的影响。结果表明:当第二次冷轧压下率从0变化至16.7%时,铁损逐渐增加,磁感逐渐降低。当第二次冷轧压下率大于16.7%时,随压下率的增加,铁损逐渐减小,磁感逐渐增加。当第二次冷轧压下率大于38%时,二次冷轧法所能获得的磁性能明显优于一次冷轧法。 Effect of double cold reduction on magnetic,microstructure and texture of 3.0% Si non-oriented silicon steel sheets was investigated.The results show that the iron loss increases and magnetic induction reduces as the percentage redcution in secondary cold rolling changes from 0 to 16.7%.The core loss can be reduced remarkably,and magnetic induction can get a little benefit if the percentage redcution in double cold reduction is higher 16.7%.In case of higher than 38% of the percentage redcution ... 

本发明公开了一种基于机器视觉的高牌号冷轧硅钢孔洞检测系统。该系统包括：线扫光源、线阵相机、速度检测模块和工控机；线扫光源安装在钢板生产线中钢板的下方，且线扫光源的光线能够对准钢板和线阵相机；线阵相机安装在钢板的上方，且与工控机连接，用于连续扫描钢板以获取连续的钢板图像；速度检测模块与线阵相机连接，用于检测钢板的移动速度，线阵相机能够根据钢板的移动速度调整行频；工控机用于根据钢板图像检测钢板是否存在孔洞。本发明的基于机器视觉的高牌号冷轧硅钢孔洞检测系统通过利用线阵相机和工控机能够实现冷轧钢板的孔洞的自动检测，检测效率高，识别精度高，能够降低漏检率和误检率，操作方便，安全可靠。

本实用新型提出一种EI型硅钢片，所述EI型硅钢片呈长方形，其包括两个E形片和两个I形片，所述两个E形片开口相对且对称设置，所述两个I形片分别连接于两个E形片相接形成的两个空挡内，所述长方形的长度A为120mm，宽度B为88mm；其中，E形片的高度C为60mm，中间舌部宽度D为29.5mm，舌部高度E为44mm，其上两侧边柱宽度F为13.25mm；I形片宽度G为16mm，长度H为88mm。本实用新型采用两个E形片和两个I形片对称设置，在冲压时充分利用材料，不会造成多余废料，且其与现有EI90型硅钢片相比，其面积为EI90型硅钢片面积的97.78％，即硅钢材料重量也为EI90的97.78％，减少了硅钢用量。

一种无取向硅钢用轧制工作辊，属于轧机工作辊技术领域，该轧制工作辊，包括锥形曲面段和平直段，锥形曲面段包括弧形段Ⅰ和弧形段Ⅱ，弧形段Ⅰ的弧面内凹，弧形段Ⅱ的弧面外凸，弧形段Ⅱ和平直段与带钢接触，弧形段Ⅰ的一端水平向外延伸，弧形段Ⅰ的另一端与弧形段Ⅱ的一端相切，弧形段Ⅱ的另一端与平直段相切，本实用新型的有益效果是，该工作辊整体结构简单，轧制效率高，降低了辊耗，消除了工作辊边部的急剧弹性压扁、弹性变形，降低了轧制断带的风险，可有效控制钢带边部的边降和形状。

一种基于大数据分析技术的电工钢用户选材询单推荐方法，于终端计算机内、以可与终端计算机各数据库进行信息交互的形式、设置一计算模块；经此计算模块完成依次的基于各数据库的有效信息的采集、用户询单选材推荐方案模型的设置、基于有效信息及推荐方案模型完成推荐牌号的生成，根据设定的评估模型对生成的推荐牌号及信息评估运算的运行，据此建立对用户的选材询单推荐。本发明的一种基于大数据分析技术的电工钢用户选材询单推荐方法，基于L4计算机系统开发出的计算模块及相应的可与计算模块进行信息交互的用户界面完成，形成可根据不同用户需求对应的不同评价体系，完成与不同用户需求适配的方案推荐。

本发明涉及电机技术领域，具体涉及一种具有低应力隔磁桥的硅钢片和电机转子。包括硅钢片、开设在硅钢片上的若干个磁钢槽组和永磁体，若干个磁钢槽组沿所述硅钢片周向分布，每个磁钢槽组均至少包括一对沿径向对称分布的磁钢槽，永磁体嵌设于磁钢槽内，磁钢槽朝向硅钢片内侧的一端设有空腔，一对磁钢槽的空腔之间通过隔磁桥隔离，隔磁桥的空腔上壁面与空腔侧壁面之间通过第一椭圆弧过渡连接，隔磁桥的空腔下壁面与空腔侧壁面之间通过第二椭圆弧过渡连接。有效降低该处隔磁桥在拐角处所受应力，进而提高该隔磁桥的强度，避免磁钢和铁芯产生形变而断裂。

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and... 

运用电子背散射衍射(EBSD)技术,研究了50W600无取向硅钢在热轧→冷轧→退火工序间织构的演变。结果表明:由于热轧板沿板厚方向的应力场和温度场存在差异,导致热轧板不同层织构类型和强度存在差异;热轧板表层主要存在铜型、黄铜和高斯织构,1/4层织构主要为α纤维织构和较弱的高斯织构,中心层织构较单一,主要为α纤维织构;和热轧板相比,冷轧板各层织构差异较小,为典型的轧制织构(α纤维织构和γ纤维织构);退火板各层都表现为γ纤维织构增强、α纤维织构减弱,旋转立方织构基本消失。 The texture evolution of 50W600non-oriented silicon steel in hot rolling,cold rolling and annealing process was investigated by electron back-scatter diffraction(EBSD)technology.Results show that the hot rolled plate texture types and intensities along thickness direction were different because of the different stress fields and temperature fields.The major texture types in the surface of hot rolled plate were copper,brass and Gauss texture.The texture was composed ofαfibre texture and weaker Ga... 

根据本发明的一个实施例的无取向电工钢板，以重量％计，所述钢板包含Si：1.5％以下、C：0.01％以下且0％除外、Mn：0.03至3％、P：0.01至0.2％、S：0.001至0.02％、Al：0.01％以下且0％除外、N：0.005％以下且0％除外、和Cu：0.02至0.3％，Ca和Mg各自单独或以合计含量包含0.0001至0.005重量％，Sb和Sn各自单独或以合计含量包含0.001至0.2重量％，余量包含Fe和不可避免的杂质。

采用双辊薄带连铸工艺试制了2.6 mm厚5.28%Si-1.11%Al高硅钢薄带,对比了1050℃×5 min正火及不正火铸带280℃冷轧至0.5 mm后,再经900～1100℃退火的磁性能。结果表明,高硅钢铸带显微组织为等轴晶组织,正火后铸带边部晶粒长大,中心层晶粒变化较小。成品中析出物主要为较粗大的AlN和AlN+MnS复合析出物,尺寸为0.5～2.5μm。与不正火试样相比,正火试样成品铁损大幅降低,磁感小幅下降;随退火温度的升高,两种工艺下铁损和磁感都是先降低后升高,在1050℃出现最低值。 2.6 mm thickness 5.28% Si-1.11% Al non-oriented high silicon steel was produced by twin roll thin strip casting.Magnetic property of the strip un-normalized and normalized at 1050 ℃×5 min was contrasted after cold rolled to 0.5 mm at 280 ℃ and 900-1100 ℃ final annealing.The results show that microstructure of the strip is equiaxed crystal.The surface grain is coarsened and the center layer grain has little change of the normalized strip.The main precipitates are AlN and MnS+AlN with 0.5-2.5 μm s... 

针对川威950的工艺现状,结合无取向低硅钢SGG生产的工艺特点,主要从控制其钢坯加热和轧制以及终轧温度和卷曲温度几方面入手,进行无取向低硅钢生产的工艺控制研究。同时根据近6000吨的生产实践表明,该工艺措施能很好的满足该钢种的需要。 950 process Chuanwei status quo,with non-oriented silicon steel production process features low,mainly from the control of billet heating and rolling and finish rolling temperature and coiling temperature of several aspects,for non-oriented silicon steel production process of low control at the same time According to nearly 6,000 tons of production practice shows that the process measures could well meet the needs of the steel. 