硅钢资料

以能量平衡和辐射换热理论为基础,通过合理假定,建立了硅钢无氧化加热炉数学模型。采用数值计算的方法,通过自编程序,完成对带钢加热过程温度场的仿真。结果显示:数学模型能够反映带钢在无氧化炉内的加热过程,其升温曲线能够与工艺曲线相吻合;现行炉温分布并非最优,数学模型能够为炉温分布的优化、炉段的设计提供理论依据。 Mathematical model of NOF Section of Continuous Annealing Furnace is established based on energy balance and radiation heat exchange. The temperature field of steel is simulated by mathematical computation. The simulating results show that the mathematical model can reflect the heating process of silicon steel in NOF section, and the heat-up curve is coincide with the processing curve. From the results,it is known that the current furnace temperature gradient is not the best, and the mathematica... 

以马鞍山钢铁集团公司电工钢板形优化控制研究项目为背景,系统地研究了热轧、冷连轧和单机架轧机在电工钢生产过程中的边缘降控制问题。通过现场数据采集、工况数值模拟计算和工业化大生产试验,设计出适用、合理的电工钢板形控制的辊型优化曲线,满足了不同工序、不同机型的板形控制策略要求,解决了电工钢板形质量问题,取得了显著的经济效益。 Based on the project of electric steel strip shape optimization control,problem of edge drop control was systematically studied in production of electric steel of hot-rolling mill,cold-rolling mill and single stand mill.Roll optimization contour was designed out in point and reasonable by collection of work condition data,numerical simulation and test of industrial production.The shape control system can meet with the different working steps and difference mills,and quality problem of electric s... 

本发明属于硅钢制造技术领域，具体涉及一种改善硅钢热轧板边部质量的加工方法，包括：连铸、铸坯预变形处理、铸坯加热处理和热轧处理；其中，所述铸坯预变形处理包括：在所述铸坯的温度为500～900℃下，对所述铸坯的沿长度方向的两侧壁通过立辊施加压力，直至形变量h为10～50mm；所述铸坯加热处理的加热温度为1100～1200℃，保温时间为4～6h。本发明提供的改善硅钢热轧板边部质量的加工方法，采用铸坯两侧壁的侧压工艺，有效解决了热轧板边部裂纹的缺陷，提高了边部塑性，提高了成材率并降低了生产成本。

本实用新型涉及一种硅钢切边重卷机组，包括依次衔接布置的开卷机、入口穿带装置、入口转向夹送辊、入口剪、切边单元、出口转向夹送辊和卷取单元，所述切边单元包括沿带钢运行方向依次衔接布置的切边夹送辊、入口稳定辊、切边剪和出口稳定辊，所述切边剪的废料出口侧衔接布置有碎边剪，所述碎边剪的废料出口侧配置有切边废料输出装置。本实用新型提供的硅钢切边重卷机组，采用切边剪+碎边剪的组合对带钢进行切边操作，避免了传统的废边卷取方式，能较好地适用于硅钢切边操作。采用切边夹送辊与入口稳定辊和出口稳定辊配合，能显著地提高切边操作时带钢运行稳定性以及保证带钢切边质量，可相应地提高生产效率。

根据本发明的一个实施例的取向电工钢板的制造方法，其包含：对板坯进行热轧，以制造热轧钢板的步骤；对热轧钢板进行热轧板退火的步骤；对热轧板退火后的热轧钢板进行一次冷轧的步骤；对一次冷轧后的钢板进行一次脱碳退火的步骤；对完成脱碳退火的钢板进行二次冷轧的步骤；对完成二次冷轧的钢板进行二次脱碳退火的步骤；以及对二次脱碳退火后的钢板进行连续退火的步骤。

本发明涉及码垛装置技术领域，且公开了一种电机硅钢片加工用码垛装置，包括底板，所述底板的顶面活动连接有夹板，所述底板的顶面固定安装有固定板，所述固定板的中部活动连接有螺纹杆，所述螺纹杆的表面固定安装有齿轮一，所述底板的顶面固定安装有固定轴，所述固定轴的顶端活动连接有齿圈。该电机硅钢片加工用码垛装置，齿圈在旋转时带动啮合齿旋转，通过啮合齿与齿轮一的啮合带动齿轮一转动，齿轮一在转动时通过与夹板底端的啮合，可以带动三个夹板同时移动，从而可以改变三个夹板之间的面积值，从而实现装置可以对不同规格的硅钢片进行码垛，操作简单，降低了操作人员的劳动强度。

结合工业化生产的50A1300牌号无取向硅钢,分析了化学成分、RH精炼脱氧方式、板坯装炉温度以及热轧平整工艺等对磁性能的影响,探讨成品钢磁性能的改善。结果表明,采取改善后,50A1300牌号无取向硅钢的磁性能得到明显改善。2012年,该钢种平均铁损、磁感应强度分别达到5.26 W/kg、1.762 T,能够较好地满足用户市场需求及同行对标需要。 Based on the industrial manufacture of 50A1300 grade non-oriented silicon steel sheets,effects of chemical composition,deoxidization method in RH vacuum refining,charging temperature of steel slabs,hot rolling and flattening progress on magnetic properties are analyzed.The optimization methods of magnetic properties of steels are discussed. Results show that the magnetic properties are obviously improved by the adopted measures above. In 2012,the average core loss and the magnetic induction of 5... 

本发明提供一种无取向电工钢的制造方法，包括连铸和RH精炼工序，连铸坯化学元素质量含量为C≤0.0050%、Si：0.50~2.20%、Mn：0.20~1.20%、P：0.020~0.040%、S≤0.0020%、Als≤0.0050%、Ti≤0.0005%、N≤0.0025%，余量为Fe及不可避免的杂质；且0.4≤Mn/Si≤0.6；RH精炼工序，脱碳结束后向钢中同时加入铝粒、微碳硅铁复合脱氧，使用铝粒脱除氧量与使用微碳硅铁脱除氧量之比为1/15~1/5，钢中主要生成低熔点MnO‑SiO2‑Al2O3夹杂，能被快速去除，钢水洁净度高。本发明电工钢与现有的电工钢相比，在相同磁感应强度下铁损更低。

【机构】 商务部进出口公平贸易局； ...

本发明涉及电工钢的生产方法，更具体地说，涉及一种预应力生产中低牌号无取向电工钢的方法，包括铁水预处理；预处理后的铁水进行转炉冶炼并吹氩脱氧；吹氩后的钢水送入精炼炉中进行冶炼并加入低碳合金进行合金化；合金化处理的钢水通过薄板坯连铸机铸成板坯并采用薄板胚连铸连轧生产工艺进行轧制获得热轧板；所述热轧板经过酸洗冷轧，随后进行预应力拉伸并退火，采用涂层进行涂镀、烧结后卷取。本发明采用预应力拉伸，改善无取向电工钢退火前钢板内部应力的分布，制备的冷轧无取向电工钢产品的电磁性能P15/50≤5.4W/kg，磁感应强度≥1.72T，板形同板差≤8um。

本发明公开了一种适应高频率工况下低铁损无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯—热轧—正火—酸洗—冷轧—连续退火—涂绝缘涂层并固化；所述冷轧步骤中，采用六辊单机架往复式轧机经5道次一次冷轧至目标厚度，冷轧过程中前三道次采用变速异步轧制方法，使钢板表层在剪应力作用下位错密度增加，这样在退火后表层晶粒尺寸细化而心部晶粒粗大，通过本发明的方法可生产得到心部为粗大等轴晶粒，表层为纳米级细等轴晶粒的电工钢产品，该产品的铁损P1.5/50≤2.35W/kg，P1.0/400≤14.0W/kg。

研究了常化温度、常化时间及常化后冷却速度对Si的质量分数为1.6%的无取向电工钢成品磁性能的影响。结果表明:在850~1 050℃范围内,随着常化温度的升高,成品铁损先减小后增大,成品磁感应强度先增大后减小;当常化温度为1 000℃时,成品平均铁损最低,平均磁感应强度最高;常化时间从3min延长到7min时,成品铁损先减小后增大,成品磁感应强度则呈单调下降趋势;随着常化冷却速度的降低,成品铁损先减小后增大,成品磁感应强度则呈单调增大趋势;对于Si的质量分数为1.6%的无取向电工钢,最佳的常化制度为:在1 000℃进行常化,时间5min,常化后空冷。对热轧板进行常化后,热轧板发生了不同程度的再结晶和晶粒长大。提高常化温度、延长常化时间、降低冷却速度,都能使常化板晶粒粗化,进而粗化成品板晶粒,改善磁性能。通过扫描电镜观察发现,成品板中析出物主要为AlN和MnS的复合析出物,以及少量的单独析出的AlN和MnS,而常化工艺主要是通过粗化析出相,减少细小析出相数量,从而减少对晶界钉扎作用来改善成品磁性能。 The effects of normalizing temperature,normalizing time and cooling rate after normalizing on magnetic properties of non-oriented electrical steel with mass fraction of Si of 1.6% were investigated.The results show that core loss of product decreases first and then increases,while magnetic induction increases first and then decreases with the increase of normalizing temperature from 850 to 1 050℃.Average core loss of product is the lowest and average magnetic induction is the highest when normal...