硅钢资料

本发明属于金属材料加工技术领域，具体涉及取向硅钢罩式炉高温退火低保温阶段二段式退火工艺，包括：将涂镁取向硅钢卷装入密闭的罩式炉中，并向罩式炉内通入氮气将炉内氧气充分排出；通电升温并将氮气转换为10m3/h氨分解气，接着点燃放散阀，将温度升至500‑600℃，恒温13h；500‑600℃低保温结束后检测内部气体露点是否小于0℃；本发明提供的取向硅钢罩式炉高温退火低保温阶段二段式退火工艺能够解决普通冷轧取向硅钢罩式炉高温退火热处理低保温阶段，钢卷在高温下不被水蒸汽氧化，消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷，降低钢带铁损、提高磁感、降低生产成本。

电工钢试样加工产生的剪切应力会恶化钢板的磁性,对不同牌号硅钢片的横向、纵向试样退火前后磁性能的变化进行研究,结果表明:无取向硅钢片在剪切过程中横向、纵向的磁性受到剪切应力影响是不一样的。 The electrical steel sample processing magnetic of electrical steel will worsen due to the shear stress of sample. In this paper,the magnetic change of transverse,longitudinal specimens of different type of silicon steel sheet before and after annealing are studied. The results show that the magnetic of non- oriented silicon steel sheet affected in the process of shear is not the same in horizontal and vertical direction. 

采用\"热轧复合+冷轧减薄+退火\"方法成功制备了0.20mm厚的硅浓度梯度高硅钢薄带,并采用SEM和X射线衍射技术对制备过程中组织和织构演变进行了研究。热轧复合板微观组织呈明显层状分布,复合界面为紧密冶金结合且经过83%的大冷轧变形未开裂。热轧和冷轧复合板带中均形成强α和γ织构,再结晶退火后形成强γ织构。冷轧和退火织构沿板厚呈显著的梯度分布特征,其主要来自于复合界面两侧硅浓度和初始热轧织构的差异性以及冷变形的不均匀性。 Gradient high silicon steel thin sheets with thickness of 0.20 mm were successfully produced by the rolling and annealing method,including hot rolling bonding,cold rolling,and annealing.Microstructure and texture evolution was investigated by means of SEM and X-ray diffraction.Microstructure of hot-rolling-bonding shows obviously layered distribution,the composite interface was closely metallurgical bonding and no cracking appears even after 83%cold rolling.Strongαandγfibers develop in the hot a... 

本实用新型提供了一种去角硅钢片铁芯加工用的吊装装置，包括安装板，所述安装板下设有防护筒，所述防护筒包括左半筒和右半筒，所述安装板上设有移动组件，所述移动组件包括气缸，所述气缸连接有伸缩杆，所述伸缩杆另一端连接有安放框架；所述左半筒和右半筒底壁皆设为开口状且侧壁上设有连通槽，所述左半筒和右半筒上分别设有防护组件，所述防护组件包括异型板和连接盒，所述异型板底部连接有固定板，所述固定板和连接盒之间连接有挤压弹簧，所述挤压弹簧内部设有传动杆，所述左半筒和右半筒内部两侧分别设有防护板。本实用新型可以有效挂住硅钢片，不会挤压坏封胶，且具有防护措施。

【机构】 商务部进出口公平贸易局； ...

本发明涉及卷取领域，具体涉及硅钢卷取机卷筒结构，包括机架、收卷辊和按压捆绑机构，按压捆绑机构位于收卷辊一侧，按压捆绑机构包括按压单元和捆绑单元，捆绑单元包括捆绑辊、转动辊、成卷的胶带和两个滑块，两个滑块均滑动设置于机架上，滑块的下端固定有能与机架相抵的下卡块，捆绑辊固定设置于两个滑块之间，捆绑辊上设有凹槽；按压单元包括两个按压部，每个按压部包括按压管和弹簧，按压管通过弹簧与凹槽的侧壁连接，转动辊设置于按压管内，成卷的胶带套设于转动辊上，凹槽的侧壁设有供胶带通过的通槽。采用本技术方案时，有利于避免成卷的硅钢卷松动且能对硅钢卷进行捆绑。

本发明提供了一种强磁性取向高硅钢极薄带及其制备方法，属于电工钢制造领域，所述强磁性取向高硅钢极薄带包括以下质量百分比的元素：C：0.0045％～0.0060％、Si：4.5％～5.0％、Mn：0.23％～0.32％、S：0.02％～0.03％、Bi：0.03％～0.08％、Als：0.027％～0.035％、Cu：0.02％～0.03％，N：0.008％～0.010％，P＜0.005％，其余为铁，其中所述Cu、S、N元素在熔炼时以含硫氮和铜的多核配位化合物的方式加入所述高硅钢；本发明通过对取向高硅钢的原料组分进行设计，采用含硫氮和铜的多核配位化合物和Bi元素作为合金抑制剂，所制得的强磁性取向高硅钢极薄带晶粒细小，组织均匀，具有高磁感应强度，低铁损的优良磁性能。

针对攀钢高硫铁水冶炼现状,结合不同生产工艺路线,论述了攀钢近年来为实现低硫电工钢的生产,在铁水预处理、转炉冶炼、钢水精炼过程中硫控制技术的开发与应用,形成了低硫洁净钢生产工艺技术,实现了低硫电工钢的生产。低硫电工钢RH脱硫率可达到20%左右,成品[S]控制在0.006%左右。 According to the smelting situations of hot metal with high sulphur content at Panzhihua Steel,combined with different produce processes,technologies for controlling the sulfur content during hot metal pretreatment,converter smelting,and second refining are developed. Technologies in low-sulfur clean steelmaking are formed. Low-sulfur electric steel are produced. As for the desulfurization rate of lowsulfur electric steel can reach about 20%,and the content of [S] in products is controlled to ab... 

利用EBSD技术研究了电工钢中长轴平行于轧向的柱状晶样品在热轧和退火过程中组织和取向的演变规律,并与长轴平行于板法向的样品的已有研究结果进行对比。结果表明,无论柱状晶按何种方向排列,只要表面存在剪切力,热轧后都可形成剪切织构,同时中心形成轧制织构,主要包括旋转立方织构和{112}<1-10>。柱状晶造成的影响主要体现在板中心层,长轴平行于轧向排列的样品热轧时形成的粗大旋转立方晶粒要到脱碳退火后才能完全消除,但破坏了正常的不同取向晶粒间的取向差分布及尺寸均匀性,导致二次再结晶不完全及磁性能降低。 The evolution of microstructure and grain orientation in an electrical steel containing columnar grains with its long axis being parallel to the rolling direction of sheet was studied during hot rolling and annealing by EBSD technique.The results are compared with those of samples containing columnar grains being parallel to normal direction of sheet reported in the reference [3].It was shown that,whether the long axis of columnar grains was arranged in RD or ND,shear textures can be formed in t... 

在50Kg氧化镁坩埚真空感应炉上进行高硅电工钢的脱氧试验。结果表明,通过控制原料的成分、高真空下的碳氧反应和炉衬分解向钢液中的供氧,可使钢液的总氧含量≤15×10-6;在维持高温高真空条件下,当钢液中的反应达到一定程度后,延长精炼时间并不能降低钢液的总氧含量;完成精炼后加入硅钙合金沉淀脱氧可进一步降低钢液的总含氧量,但脱氧效果有限。 The test of high-silicon electric steel deoxidation has been carried out in 50Kg vacuum induction furnace with magnesium oxide crucible.Results show that the total oxygen could be ≤15×10-6in molten steel by controlling material components,carbon-oxygen reaction in high vacuum and oxygen contamination from crucible materials on molten steel;And when the reaction was carried through to a certain extent,total oxygen in molten steel could not be reduced by the extension of refining period in high va... 

采用XRD、SEM和激光粒度仪等手段,观察并研究了不同特性氧化镁在硅钢表面形成硅酸镁底层形貌特点,并结合热力学和差热-失重分析了MgO-SiO2的反应机理。研究结果表明:粒度小,活性值高的特种氧化镁在高温退火过程中与基体表面氧化物生成的硅酸镁底层,界面中硅酸镁底层嵌入基体较多,表面致密,颗粒细小,有利于形成附着性能优良的硅酸镁底层。 Surface microstructure of Mg2SiO4 coatings formed on the surface of oriented silicon steel coated with different kinds of MgO was investigated by XRD and SEM.The reaction mechanism between MgO and SiO2 was analyzed by TG-DSC and thermodynamic calculation.Results revealed that when the MgO with finer microstructure size and higher activity is employed,a dense Mg2SiO4 layer with finer microstructure and good binding to the steel substrate can be obtained.The results are very helpful for the prepar... 

【作者】 严伟明； ...