硅钢资料

【摘要】 <正>3月底,宝钢\"低温高磁感取向硅钢制造...

基于BOF→RH→CSP生产工艺,研究了RH精炼过程钢中夹杂物类型演变及MgO·Al2O3夹杂物形成规律,同时对MgO·Al2O3夹杂物的形成条件进行了热力学计算,借助CFD数值模拟软件研究了RH精炼过程卷渣行为。研究发现,RH精炼过程20和30 min时,w([MgO])/w([Al2O3])为0.005~0.020,未发现MgO·Al2O3夹杂物;RH出站后夹杂物w([MgO])/w([Al2O3])为0.3~0.5,且RH精炼结束后MgO·Al2O3夹杂物占夹杂物总量的58.4%;另外,RH精炼过程钢液表面速度CFD模拟结果为0.57 m/s,大于临界卷渣速度0.45 m/s,且顶渣成分与夹杂物成分相近,存在卷渣现象。热力学计算表明,钢液与炉渣平衡时钢中w([Al])为0.31%~0.37%,w([Mg])为0.00024%~0.00028%,在MgO·Al2O3生成区域之内。减少RH处理过程卷渣,浇铸过程下渣及控制顶渣和包衬相中MgO质量分数可抑制MgO·Al2O3夹杂物形成。 Based on the practical production of non-oriented silicon steel, the evolution of inclusion type and the formation of MgO·Al2O3inclusion were analyzed in the process of BOF→RH→CSP. The thermodynamic conditions for forming MgO·Al2O3inclusion were discussed and the behavior of slag entrapment of molten steel was also simulated by CFD software during RH refining. The results showed that the value of w([MgO])/w([Al2O3]) was in the range of 0.005-0.020 and no MgO · Al2O3 inclusion was observed at 20 ... 

以市场上购买的取向硅钢成品板为原料，经不同压下率冷轧至0.23～0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量，利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征，分析了硅钢超薄带的塑性变形行为。结果发现，在平面压缩应力下，{112}<111>滑移系的取向因子较大。随冷轧压下率的增加，Goss织构的含量逐渐减少，{212}<141>织构组分的含量先增加后减少，{111}<112>织构组分的含量逐渐增加，织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶，其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。 The commercial finished oriented silicon steel plate as the raw material were rolled to 0.23-0.08 mm. With the X-ray diffractometer(XRD), the texture components and their volume fractions in the cold-rolled samples were detected. And the orientation factor distribution of the cross-section of the samples was measured by the electron backscattering technique(EBSD). The morphology and crystallographic characteristics of twins were observed, and the plastic deformation behaviors of the ultra-thin o... 

本实用新型公开了一种生产硅钢片的轧制装置，包括工作台，所述工作台的正面开设有收集腔，收集腔的内底壁滑动连接有收纳盒，工作台的上表面分别固定连接有两个支撑板和倒L型滑动台，两个支撑板的相对面分别转动连接有上压辊和下压辊，上压辊的外表面套设有两个调节环，两个调节环的相对面均固定连接有切刀，工作台的上表面开设有与收集腔相连通的下料孔，下料孔的内侧壁开设有滑动槽。该生产硅钢片的轧制装置，通过设置上压辊、下压辊与驱动电机，便于对硅钢片进行传动，通过设置调节环、切刀与固定螺栓，便于根据生产需求调节硅钢片切边的距离，从而使整个装置具有方便对轧制后硅钢片进行切边处理的效果，方便后续轧制工作的进行。

以能量平衡和辐射换热理论为基础,通过合理假定,建立了硅钢无氧化加热炉数学模型。采用数值计算的方法,通过自编程序,完成对带钢加热过程温度场的仿真。结果显示:数学模型能够反映带钢在无氧化炉内的加热过程,其升温曲线能够与工艺曲线相吻合;现行炉温分布并非最优,数学模型能够为炉温分布的优化、炉段的设计提供理论依据。 Mathematical model of NOF Section of Continuous Annealing Furnace is established based on energy balance and radiation heat exchange. The temperature field of steel is simulated by mathematical computation. The simulating results show that the mathematical model can reflect the heating process of silicon steel in NOF section, and the heat-up curve is coincide with the processing curve. From the results,it is known that the current furnace temperature gradient is not the best, and the mathematica... 

本发明公开了一种超薄取向硅钢用的半有机绝缘涂料。该半有机绝缘涂料，按质量百分比计，包括以下组分：10～25％磷酸盐，1～10％含有环氧基的硅烷耦合剂，0.2～2.0％有机硅烷，1～10％铬酐，1.5～6％二氧化硅粒子，0.3～5％碱，余量为水；其中二氧化硅粒子的粒径为100～300nm。该半有机绝缘涂料应用于超薄取向硅钢表面时，既提高了涂层与基体的附着性，又保证了涂层的绝缘性和耐热性，涂层附着性为A级，叠片系数大于0.96，可耐900℃高温，并且涂层较薄(小于1μm)时，钢板的绝缘电阻大于30Ω·cm2/片，绝缘性能优异，可满足超薄取向硅钢的应用需求。

介绍了国内无底层取向电工钢生产技术水平、产量和用途，简述了无底层取向电工钢作为取向电工钢超/极薄带母料及应用于制作大型发电机组铁心、风电等电机铁心和变压器铁心等的情况。 The production technology level,output and application of domestic glassless grainoriented electrical steel were introduced,and the application of glassless grain-oriented electrical steel as parent material of ultra-thin strip of grain-oriented electrical steel and in making large-scale electric generator cores,wind power motor cores and transformer cores were briefly described. 

结合扫描电镜和大样电解研究了CSP流程W800牌号无取向电工钢表面线状缺陷中夹杂物成分及来源，采用SPSS软件回归分析了生产过程各因素对表面线状缺陷的影响。研究表明：稳态浇铸过程铸坯中大型夹杂物含量为5.39 mg/10 kg。引起无取向电工钢表面线状缺陷的大型夹杂物主要为脱氧产物、镁铝尖晶石和钢包顶渣，主要类型为Al₂O₃、MgO-Al₂O₃、CaO-Al₂O₃-MgO和CaO-Al₂O₃-SiO₂。非稳态浇铸过程钢水洁净度明显降低，热轧板表面线状缺陷比例上升。影响表面线状缺陷的主要因素为RH出站时顶渣的w（CaO）/w（Al₂O₃）、RH脱氧结束氧位及中间包最低吨位。 Combining scanning electron microscopy and large sample electrolysis, the composition and source of inclusions in the surface linear defects of W800 grade non-oriented electrical steel in the CSP process were studied. SPSS software was used to regress and analyze the main factors which affected the surface linear defects in the steelmaking process. Research shows that the content of large inclusions in the steady state casting process is 5.39 mg/10 kg. The large inclusions which cause linear def... 

对高牌号无取向电工钢35W300的成品进行了第二次退火,对第二次退火后的成品性能、纵横向磁性能差异和组织变化进行了分析。结果表明,随着第二次退火温度的升高,晶粒长大,磁性能优化。铁损平均值下降0.087 5W/kg,磁感平均值升高0.008T。第二次退火温度为820℃的产品的磁性能能够满足用户使用要求。 The product of high grade non-oriented electrical steel 35W300 was annealed at the second time.Microstructure,the difference of magnetic properties in the vertical and horizontal and were studied.The results show that the grain grew up and magnetic properties optimized with the increase of annealing temperature for the second time.Iron loss average declines in 0.0875 W/kg,magnetic induction average increases 0.008 T.The magnetic properties can meet the requirements of users at the second anneali... 

本发明提供了基于硅钢片性能的分类方法、系统、计算机和存储介质，通过抽样选取待分析硅钢片，获取待分析硅钢片的基准B‑H曲线和基准B‑P曲线，以及通过预设检测方法测得待分析硅钢片的样本B‑H曲线和样本B‑P曲线后，根据预设磁通密度监测范围分别选取基准B‑H曲线、基准B‑P曲线、样本B‑H曲线和样本B‑P曲线对应的B‑H基准样本点、B‑P基准样本点、B‑H待分析样本点和B‑P待分析样本点，并基于依此分别得到B‑H样本点距离与B‑P样本点距离分析待分析硅钢片的性能，以及根据分析结果对待分析硅钢片进行分类的方法，基于性能曲线的数据分析对硅钢片性能进行合理的评估分类，不仅实现了对硅钢片质量的有效监控，而且为其使用策略的制定提供可靠依据，保证产品质量的同时，为产品用料选择提供便利。

分析了影响脱碳效果和结晶行为的各种要素及其相互制约关系,提出了Hi-B连续退火工艺曲线,总结得出快速加热及合理稳态气氛是实现工艺制度的关键。结合实际工程,介绍了在连续退火炉设计中快速加热和气氛设计的考虑方法,并指出随着Hi-B产品的发展,如何改进这些方法将是连退工程研发的方向之一。 The factors which affect decarbonization and crystallization and the mutual restriction between them were analyzed.A complete continuous annealing process for Hi-B was put forward.As a result,the rapid heating and the proper steady atmosphere were two important factors.According to an actual project,the consider methods for designing rapid heating and proper steady atmosphere were introduced,and it is pointed that with the development of Hi-B technique,how to improve these techniques would be on... 

本实用新型公开了一种无取向硅钢绝缘涂层粘结性检测装置，涉及涂层粘结性检测技术领域，为解决现有的无取向硅钢绝缘涂层，在对绝缘涂层粘结性检测过程中，其检测结构单一，容易导致检测不准的问题。所述基座的上方设置有存料罐，所述存料罐的内壁设置有防腐涂层，所述存料罐的底部设置有声波感应器，所述声波感应器的一侧设置有液位感应器，所述液位感应器的一侧设置有自控温度调整器，所述存料罐的上方设置有控制盘，所述控制盘的表面设置有PLC操控器，所述控制盘的上方设置有电机，所述电机的一侧设置有带轮结构，所述带轮结构的一侧设置有伸缩气缸，所述伸缩气缸的一侧设置有联动结构，所述伸缩气缸的一端设置有收缩棒。