本实用新型公开了一种风电机组取向电工钢用罩式炉的砂封振动装置，包括：基座，设置有行走机构，行走机构带动基座沿环形砂封槽槽壁行走；振动齿座，与基座连接，定位座和基座之间夹设有弹性缓振件；振动件，与定位座固定连接；振动齿，与振动齿座固定连接，设置于基座的行走轨迹内侧。该风电机组取向电工钢用罩式炉的砂封振动装置利用砂封槽的槽壁作为行走机构的轨道，振动齿不仅可以平整砂封槽中的密封砂，振动状态下还能使密封砂填充得更趋密实，避免局部密封不良的问题，优化密封效果。

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

本发明涉及一种消除硅钢边部翘皮的方法及硅钢，包括预处理板坯；加热预处理后的板坯，并控制所述板坯在加热炉的预热段时间不低于40分钟；粗轧板坯，并调整所述板坯侧压的减宽量为成品硅钢宽度的0.8％～1.2％；以及控制侧压立辊的凸缘与所述板坯的边部之间保留间隙。本发明所述的消除硅钢边部翘皮的方法及硅钢，能够显著消除硅钢的边部翘皮，以及在不能完全消除边部翘皮缺陷的情况下，约束翘皮位置发生在距离边部＜8mm区域，工艺调整简单易操作，不需要调整现有设备和系统架构，显著提升硅钢表面质量。

本实用新型公开了硅钢专用消泡剂生产温度控制装置，包括底板及设置在底板上端的温控桶，所述温控桶的内部设置有温控腔，所述温控桶的上下两端分别安装有进料口及出料口，所述温控桶的内部设置有便于温度控制的温度控制机构，所述底板上设置有用于搅拌的搅拌机构；所述温度控制机构包括安装在温控桶上的进气管及出气管，所述进气管及出气管与温控腔的内部相通设置。本实用新型的硅钢专用消泡剂生产温度控制装置，整个温控处理操作简单、实施便捷，便于对消泡剂进行温度控制，且冷却介质或者加热介质可以直接对消泡剂进行加热或是降温，降低了输送过程中的能量消耗，提高了消泡剂温度控制的效率。

本发明公开一种冷轧硅钢的横向同板差控制方法，具体如下：S1、确定冷轧钢板横向同板差的影响因子，包括：热轧钢卷的热卷凸度、工作辊辊型插入量、中间辊窜动值及冷轧钢卷的总切边量；S2、以影响因子为变量构建冷轧钢板横向同板差的计算模型；S3、将热轧钢卷的热卷凸度及冷轧钢板的目标横向同板差输入计算模型，确定最小冷轧钢卷总切边量下的工作辊辊型插入量及中间辊窜动值。明确客户所需的横向同板差，通过改变工作辊辊型插入量X2及工作辊窜动值X3，以此得到冷轧成品钢卷的总切边量最小值，在满足客户对横向同板差的使用要求前提下，降低生产成本，提高产品竞争力。

目前随着电工钢用户冲压设备的升级,冲压速度逐步提高,对电工钢产品的硬度和强度指标提出了更高的要求。与普通硬度级别的无取向硅钢相比,高硬度50BW600的Hv硬度提高15~20,达到125以上,同时对电磁性能指标也有较高要求。本钢通过化学成份和热轧及冷轧连退生产工艺的设计,经过小批量生产试验,满足用户要求。通过对工艺的严格控制,在大批量生产过程中,保证了产品的力学性能和电磁性的检验合格率。 Currently with upgrading of stamping equipment of silicon steel user, gradually increasing of stamping speed, propose higher demand for hardness and strength of silicon steel. Compared with conventional 50BW600, high hardness 50BW600 have higher hardness, reach greater than 125Hv. Through design of chemical composition with hot mill and annealing, production test of small quantities, stamping performance meet user request. 

采用硅钢自动测量装置及X射线衍射仪检测出样品在实验前后的磁性能参数和织构强度.结果表明:较低的电压、9 Hz、较长的处理时间以及退火温度为650℃有利于增高铁损降低比例;较低的电压、较高的频率以及退火温度为650℃有利于增加磁感应强度增高比例.最佳的提高磁性能的实验参数是:频率为9 Hz,电压为500 V,处理时间为6 min,退火温度为650℃.通过织构分析可以验证:取向硅钢磁感应强度的变化取决于{110}<001>晶粒取向度值,而{110}<001>取向度值可看成是一个反映总体平均偏离角大小情况的综合值. An automatic measurement system for silicon steel and an X-ray diffraction meter were used for measuring the magnetic property parameters and texture of ex-processed samples and processed samples.It is shown that under the condition of a lower voltage,9Hz,a longer processed time and an annealing temperature of 650℃,the decrease rate of iron loss can be increased;a lower voltage,a higher frequency and an annealing temperature of 650℃ are in favor of improving the increase rate of magnetic inducti... 

分析了高转矩和高转速条件下高效驱动马达铁芯材料对无取向硅钢磁性能要求,讨论了无取向硅钢的高磁通密度和低铁损对电机转矩和效率的影响,介绍了国内外高磁感无取向硅钢发展情况。在生产工艺上,提高钢质纯净度,弱化夹杂物和第二相粒子对畴壁移动和再结晶晶粒长大的钉扎作用,添加微量晶界和带钢表面的偏析元素促使有利织构发展等技术可提高无取向硅钢的磁通密度。 The requirements of high efficient drive motor core materials under the conditions of high torque and high speed were analyzed.The effects of high magnetic flux density of non-oriented silicon steel on the torque and efficiency of the motor were discussed.The development of non-oriented silicon steel with high magnetic was introduced.The magnetic flux density of non-oriented silicon steel sheet can be obviously improved by some production technologies,such as purification steel,weakening the pin... 

本发明公开了一种弧形硅钢片、弧形硅钢片治具及弧形硅钢片制造方法；弧形硅钢片治具包括压制底板和侧挤压板，压制底板和侧挤压板之间具有挤压间隙，挤压间隙的两侧分别设置有位于压制底板内侧的外挤压面和位于压制底板外侧的内挤压面，外挤压面和内挤压面的对应位置上开设有若干齿槽加工台阶，压制底板的下方开设有若干与挤压间隙连通的焊接孔，压制底板和侧挤压板的侧面对应位置设置有贯穿压制底板和侧挤压板的冲压模孔；通过弧形硅钢片制造方法，采用弧形硅钢片治具制成弧形硅钢片。本发明采用弧形硅钢片治具及弧形硅钢片制造方法实现动子中弧形硅钢片的压制成型，通过弧形硅钢片实现直线电机的圆周运动或圆弧运动。

轧制力是影响冷轧带钢厚度精度的关键因素。为实现高精度的冷轧带钢厚度控制,通过优化变形抗力模型参数和摩擦系数模型参数提高冷轧轧制力模型计算精度,并使用指数平滑法的自学习算法保证轧制力精度的稳定性。在首钢股份公司迁安钢铁公司20辊森基米尔轧机生产线进行S12硅钢钢种轧制力优化试验,将优化的模型参数应用于L2并投入现场生产,结果表明该优化方法不仅提高了轧制力设定精度,而且减小了冷轧硅钢的厚度超差长度,提高了成材率。 The rolling force is the key factor which influences the accuracy of cold-rolling strip thickness. To implement high precision control of cold-rolling strip thickness,we optimize the deformation resistance model parameters and friction coefficient model parameters to improve the calculation precision of cold-rolling force model,and use exponential smoothing self-learn algorithm to ensure the stability of rolling force accuracy. In Shougang Qiangang 20-high Sendzimir mill single stand production ... 

研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient... 

一种无取向电磁钢板用热轧钢板，其以质量％计，含有C：0.0010～0.0050％、Si：1.90％～3.50％、Al：0.10％～3.00％、Mn：0.05～2.00％、P：0.100％以下、S：0.005％以下、N：0.0040％以下、B：0.0060％以下、Sn：0～0.50％、Sb：0～0.50％、Cu：0～0.50％、REM：0～0.0400％、Ca：0～0.0400％及Mg：0～0.0400％，剩余部分为Fe及杂质；该无取向电磁钢板用热轧钢板的特征在于，在无取向电磁钢板用热轧钢板的板宽方向端部中，板厚中心部(t/2位置)的加工组织的硬度HD为Hv220以下。