本发明涉及一种硅钢片纵剪边料收卷装置，包括：用于将收卷装置固定于地面的机架底座，机架底座一端设置固定支架，固定支架上安装电动定尺收料盘；在机架底座上设置电动可移动支架，电动可移动支架在机架底座的长方向上相对固定支架移动，电动可移动支架上安装电动可调收料盘；电动可移动支架、电动定尺收料盘、电动可调收料盘与PLC控制系统连接，PLC控制系统用于控制电动可移动支架的移动距离、以及控制电动定尺收料盘和电动可调收料盘的收料速度。本发明还涉及一种硅钢片纵剪边料收卷方法。将本发明的收卷装置安装在硅钢片滚剪线切刀后面的输送平台下部，卧式布局，不占用外部空间，和滚剪线无缝集成在一起，自动完成硅钢片纵剪边料收卷工作。

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。 Microstructure development and texture evolution of conventional grain oriented silicon steel,which were annealed at same annealing temperature and different annealing time under wet H2 atmosphere,were investigated through metallographic observation and electron backscattered diffraction analyzing.The results show that the primary recrystallization finishes in 120 s at 820 ℃ under wet H2 atmosphere.With the extending of annealing time,{111}<112> texture decreases,{111}<110> texture d... 

本发明提供了一种可修饰取向硅钢表面的无机绝缘涂料及其制备和使用方法，该涂料按照重量份计，包括：大颗粒硅溶胶5‑35份、磷酸二氢铝10‑30份、小颗粒硅溶胶5‑35份、铬酐0.5‑5份、增稠剂1‑10份、钛白粉0.01‑0.5份及去离子水0‑78.49份；该涂料的固含量为20‑40％。该涂料制备方法为：将增稠剂、去离子水、磷酸二氢铝、大颗粒硅溶胶、小颗粒硅溶胶，铬酐和钛白粉依次加入反应器中搅拌均匀，室温静置0.5‑1h。该涂料在使用时，需先将取向硅钢片进行清洁干燥预处理后，再将涂料辊涂在取向硅钢片上固化烧结并控制膜厚。本发明所提供的涂料制成的涂层表面平整均匀、颜色光亮，具有优良的附着性、耐蚀性、热稳定性和绝缘性，并且能修饰因硅酸镁底层质量不良引起的露晶亮点缺陷。

针对某硅钢车间ST机组的除尘系统除尘效率较低、排放浓度不达标、二次污染较严重的问题,通过现场调研,对除尘系统、含尘气体组分与物性参数等进行测试和分析,运用管道伴热技术改善粉尘黏性后,再选取合适的除尘器对粉尘进行除尘处理,大大地提高了系统的除尘效率。 To solve the problems of low dust removal efficiency, substandard emission concentration and severe secondary pollution, some investigations are conducted to test and analyze the dust removal system,dust-gas composition and relevant physical parameters.Moreover, dust removal efficiency is greatly improved by the use of pipe heat tracing technology and by choosing appropriate dust remover. 

本实用新型属于抛丸设备技术领域，具体涉及一种硅钢抛丸用耐磨抛丸头，包括壳体、进丸管、定向套、分丸轮、多块截面呈工字形的叶片和两块对称设置的护板，多块叶片沿护板的周向均匀分布，叶片安装在两块护板之间；叶片的左右两侧分别设有一组卡槽，一组卡槽包括两个卡槽，一组卡槽上滑动连接有能与叶片表面接触的耐磨板；叶片上设有用于固定耐磨板位置的固定件；壳体内可拆卸的安装有耐磨衬板。在本方案中，将耐磨板可拆除的安装在叶片中，耐磨板对叶片有保护的作用，能避免叶片被磨损；当耐磨板损坏后只需更换新的耐磨板，而不需更换叶片，能够有效节省成本。同样的耐磨衬板对壳体也有保护作用，能够在很大程度上减少壳体被磨损。

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

本文以热轧常化板为初始材料,采用二次冷轧法与三次冷轧法制备了0.1 mm厚的取向硅钢薄带,测定相应的磁性能,并通过EBSD取向成像技术检测了二次冷轧法与三次冷轧法各工艺过程中织构与组织演变规律。结果表明,采用最终冷轧压下率适中的三次冷轧法,能在冷轧至0.1 mm时保存较多的高斯晶核,使得高温退火后的磁性能明显优于二次冷轧法。最终冷轧压下率通过影响脱碳退火后样品中的{111}<112>织构组分及Goss晶粒数量对最终二次再结晶产生重要影响。 Grain-oriented silicon steel sheets with a thickness of 0. 1 mm were produced from hot-rolled and normalized sheets by two-step-rolling and three-step-rolling methods. Their magnetic properties were measured,and the textures were detected by EBSD technique. The results show that the three-step-rolling method,which has a moderate reduction rate of final cold rolling,can maintain more { 110} < 001 >nucleus,and thus obtaining better magnetic properties compared with the two-step-method. The f... 

采用化学气相沉积(CVD)渗硅处理工艺连续制备6.5%Si高硅钢,具有优质的软磁性能,通过理论研究化学反应并且用简单的试验设备做进一步的探讨。根据试验的结果对连续制备6.5%Si高硅钢的CVD工艺构造提出全面、有效的建议,实现制备6.5%Si高硅钢系统。 CVD method for continuously manufacturing 6.5%Si Steel Sheet has excellent soft magnetic.Carried out a theoretical study of related chemical reaction and performing basic research with a simple test apparatus.Based on the results,finally proposed an overall process configuration to realize such a production-CVD method for continuously manufacturing 6.5%Si Steel Sheet. 

【摘要】 <正>2014年5月9日,从武钢硅钢事业部获悉,...

本实用新型涉及变压器材料检测技术领域，具体为一种硅钢片检测装置，包括材料检测装置主体，材料检测装置主体包括相互连接的铁损测试仪主机及磁导计，磁导计的顶端设置有清洁机构，清洁机构包括固定盒、拉块及刷块，固定盒固接于磁导计上，拉块插设于固定盒中、能够在固定盒中上下移动，固定盒的内部底面上及拉块的底端上分别安装有刷块，铁损测试仪主机上还设有束线机构。本实用新型使得用户可在检测硅钢片前，对硅钢片两面沾染的灰尘污渍进行擦拭，避免灰尘污渍影响对硅钢片的测定结果，可方便地对刷块进行清洁更换，使得用户可方便地对电源线和导线进行收纳。

系统研究了无取向硅钢用磷酸盐系涂层性能的影响因素。以氢氧化铝和磷酸为原料制备磷酸二氢铝,再添加适量的添加剂酒石酸铵、二氧化硅、环氧树脂,得到的涂液涂布于硅钢表面,并控制合适的烘干温度,通过耐盐雾实验考察各因素对涂液耐腐蚀性能的影响。实验结果表明,在磷酸与氢氧化铝物质的量比为3.4∶1、酒石酸铵用量为2%、二氧化硅用量为1%、环氧树脂用量为5%、烘干温度为300℃条件下,所得涂层材料的防(耐)腐蚀效果最佳。 The factors influencing the performance of phosphate anticorrosive coating for non-oriented silicon were systematically studied.Aluminum dihydrogen phosphate was prepared with aluminum hydroxide and phosphoric acid as raw materials.Then added the right amount of additives,such as ammonium tartrate,silicon dioxide,and epoxy resin to prepare the liquid coating,which was coated on the surface of the silicon steel,and finally controlled a suitable drying temperature.The influences of various factors... 

本实用新型提供一种硅钢片模具产品的吸料装置，包括固定架、电动伸缩杆、微型吸气泵、操作台、吸气机构以及放置机构，所述固定架上表面设有电动伸缩杆，所述固定架上表面设有微型吸气泵，所述微型吸气泵右端面设有吸气口，所述吸气口右端设有气管，所述电动伸缩杆底部设有吸气机构，所述吸气机构底部设有操作台，所述操作台上表面设有固定柱，所述固定柱前表面设有放置机构，与现有技术相比，本实用新型具有如下的有益效果：通过设置的橡胶套，代替手进行硅钢片的取料，通过设置固定杆，实现橡胶套的自动放料，更安全，通过设置的放置机构，实现硅钢片倾斜放置，方便进行硅钢片的拿取进行变压器装配。