对无取向电工钢中的夹杂进行了系统的分析。利用小样电解,采取不同电解液,不同的分离方法对无取向电工钢中稳定和不稳定夹杂物进行了提取、分离和收集。利用扫描电镜(SEM)、X-射线衍射、ICP等对电解分离收集的夹杂物进行了定性和定量分析。 The inclusion analysis of the non-oriented electrical steel has been investigated.By using small sample electrolytic analysis,with different electrolytes and different separation ways,the stable inclusions and unstable inclusions was drew,separated,and collected.With utilizing the methods of SEM,X-ray and ICP,the qualitative and quantitative analysis of inclusions in the non-oriented electrical steel was obtained. 

本发明揭示了一种高牌号无取向硅钢及其生产方法。所述无取向硅钢的化学成分以质量百分比计包含：C:0.002～0.004％，S≤0.003％，Si:1.4～1.7％，Mn:0.7～0.95％，P≤0.03％，Sn:0.015～0.035％，11×([Si]‑1.4％)＝14×([Mn]‑0.7％)。所述无取向硅钢的生产方法中，连铸坯加热温度1120～1150℃，精轧终轧温度为890±15℃，最后一道次精轧的压下量≥30％且最后两道次精轧的总压下量≥50％，卷取温度650±20℃；在酸连轧之前不需要进行常化处理，且所得无取向硅钢的磁性能佳，表面无瓦楞缺陷，满足低成本高牌号无取向硅钢的需求。

根据新日铁、JFE及浦项等国外钢铁公司2008年以来在日本专利局、欧洲专利局(EP)及世界知识产权组织(WIPO)申请公开的有关生产Hi-B取向电工钢典型专利技术,概述了近年来国外大型钢铁企业采用低温板坯加热(坯加热温度<1 280℃)技术生产Hi-B取向电工钢主要技术重点,即将调节关键化学成分Al、N、Sn及Sb等与工艺改进相结合。最后介绍了国外大型钢铁企业采用低温板坯加热技术生产Hi-B取向电工钢实例。 The latest developments on technology for manufacturing Hi-B grain oriented electrical steel sheets developed by Nippon Steel Corp.,JFE Steel and POSCO were described according to the patents published by World Intellectual Property Organization,Japan Patent Office and European Patent Office over the recent years.The low temperature slab heating process(particularly slab-heating temperature<1 280 ℃) together with suitably adjusting key chemical elements such as Al,N,Sn and Sb elements was the... 

本实用新型公开了一种具有自动接料机构的变压器硅钢加工用防刮伤剪床，包括支撑座，所述支撑座的上端固定连接有相互对称的进料机构与出料机构，所述进料机构上设置有调节机构，所述进料机构与出料机构之间设置有切割底座，所述切割底座的两端设置有气缸，所述气缸的内侧设置有切割机构，所述切割机构上设置有卡接机构，所述出料机构的一侧设置有接料机构；本实用新型涉及剪床技术领域。该具有自动接料机构的变压器硅钢加工用防刮伤剪床，切割后的硅钢，通过出料机构输送至承接板上，挡板与侧板能够使得硅钢能够自动叠放整齐，自动叠放整齐相对于人工接料可明显节省时间，提高剪床的运行效率，减少人力成本，提高运行的安全性。

研究了无取向硅钢钙处理前后夹杂物的行为,重点考察了钙处理前后夹杂物的成分、类型、形貌和尺寸研究的变化情况,为实际生产中无取向硅钢的钙处理提供理论指导。试验发现:钙处理前夹杂物主要以Al2O3、Al2O3-MgO为主,且在夹杂物表面有AlN析出,钙处理后夹杂物以Al2O3-MgO-CaS-CaO系复合夹杂物为主,还含有少量的SiO2或AlN;钙处理前后,夹杂物形貌由多边形或不规则形逐渐向球形或近似球形转变,并且夹杂物尺寸不断增大;钙处理前后,含钙夹杂物的比例发生突变,由10%增大到74.5%,且随着钙处理时间的延长,含钙夹杂物比例下降,表明钙处理使夹杂物变性后易聚集长大并上浮去除。 Behavior of inclusions before and after calcium treatment in non-oriented silicon steel was researched by investigating changes of compositions,types,shapes and sizes of inclusions before and after calcium treatment,for the purpose of providing theoretical guidance for calcium treatment of non-oriented silicon steel in actual situation. Results indicated that Al2O3 and Al2O3-MgO were main types of inclusions before calcium treatment,sometimes AlN maybe precipitate in the outer of inclusions. Al2... 

常化快冷是生产高牌号无取向硅钢和高磁感取向硅钢不可缺少的一个工艺环节,气-雾冷却则是实现常化快冷的关键方式之一。介绍了国内自主设计建设的常化酸洗机组气雾冷却系统的技术特性,并对其特点进行了系统分析,最后给出该系统在设计、运行参数的选择上若干注意事项,对气-雾冷却系统设计和使用具有一定的指导作用。 The normalizing rapid cooling is a indispensable process to high grade non-oriented silicon steel and high magnetic induction oriented silicon steel’ s production. The fog cooling is a key ways of coming true the normalizing rapid cooling. This paper introduces the technical features of the fog cooling system in normalizing pickling line which is the domestic independent design and construction. Meanwhile,the fog cooling system’s characteristic is analyzed systematacially. In the end,this paper ... 

试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ... 

介绍了双蓄热燃烧技术的特点和高温硅钢加热炉的特点,探讨了双蓄热燃烧技术在高温硅钢加热炉中使用的技术难点,分析了双蓄热燃烧技术在高温硅钢加热炉上使用的可能性。 Introduced characteristics of double regenerative combustion technology and high temperature silicon steel reheating furnace,discussed technical difficulties for using double regenerative combustion technology,analyzed the possibility of double regenerative combustion technology applied to high temperature silicon steel reheating furnace. 

根据本发明的一个实施例的取向电工钢板的制造方法，其包含：对板坯进行热轧，以制造热轧钢板的步骤；对热轧钢板进行热轧板退火的步骤；对热轧板退火后的热轧钢板进行一次冷轧的步骤；对一次冷轧后的钢板进行一次脱碳退火的步骤；对完成脱碳退火的钢板进行二次冷轧的步骤；对完成二次冷轧的钢板进行二次脱碳退火的步骤；以及对二次脱碳退火后的钢板进行连续退火的步骤。

本发明公开了一种精确控制高磁感取向硅钢连铸坯Als成分的方法，本发明涉及的主要是高磁感取向硅钢生产过程的连铸工艺环节，负责将高温液态钢水浇注凝固成固态连铸坯。通过采取控制大包下渣、加入足量中间包覆盖剂、采用长水口+石墨垫圈+氩封保护浇注等方法，将精炼结束到连铸过程Als降低量稳定控制在0.0030～0.0045%范围内，稳定了二次氧化程度。通过采用本方法生产的连铸坯Als含量稳定在0.0245～0.0275%范围内，为提高取向硅钢产品的磁感和铁损性能奠定坚实的基础保障。

本发明属于金属材料加工技术领域，具体涉及取向硅钢罩式炉高温退火低保温阶段节能工艺，包括：1)将涂镁取向硅钢卷装入密闭的罩式炉中，并向罩式炉内通入氮气将炉内氧气充分排出，使炉内氧含量浓度≤300PPm；2)通电升温并将氮气转换为10m3/h氮气与氨分解气的混合气体，升温2h将温度升温至500‑600℃后，恒温13h；3)将温度氮气与氨分解气的混合气体转换为12m3/h氨分解气，并升温2h将温度升至650℃恒温15h，使内部气体露点小于‑10℃；本发明提供退火工艺，钢卷在高温下不被水蒸汽氧化，消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷，降低钢带铁损、提高磁感、降低生产成本。此外，本发明进一步减少退火过程中氨分解气的用量，具有极高的工业应用价值。

本发明公开了一种超高效变频空调压缩机用无取向硅钢薄带及其制造方法，属于无取向硅钢技术领域。本发明包括以下重量百分比的组分：C≤0.003％，Si：2.0％～2.5％，Mn：0.15％～0.5％，Als：0.3％～0.7％，Sn：0.05％～0.11％，S≤0.003％，P≤0.03％，B：0.002％～0.004％，Ca：0.003％～0.005％，N≤0.003％，Ti≤0.003％，其余为Fe及不可避免的杂质，且Mn/S比控制在20～60范围内，B/N比控制在0.7～1.5，Ca/S的比例≥1。为解决现有技术中存在的问题，本发明通过添加合金元素以及偏析元素，配合连铸、热轧、常化和连续退火等热处理工艺，以及优良的冷轧板形控制技术，实现0.30～0.35mm厚度薄规格的高效无取向硅钢产品，具备优异的磁性能和高屈强比的力学性能，满足高效变频空调压缩机电机磁性能和关节式定子高速冲裁对力学性能和板形的高标准要求。