结合实际生产0.4%Si无取向硅钢，统计了不含Sn和0.025%Sn无取向硅钢的磁性能变化，利用金相显微镜、X射线衍射仪观察分析不同成分下试样的显微组织和微观织构。试验结果表明：Sn元素可以显著降低无取向硅钢的晶粒尺寸，0.025%Sn试样的平均晶粒尺寸比不含Sn减小28.4%;加入Sn元素后抑制了无取向硅钢中不利于磁性能的{111}面织构组分强度，提高了对磁性能有利的{100}面织构组分强度，0.025%Sn与不含Sn相比磁感均值从1.756 T提升至1.768 T,铁损均值从5.476 W/kg降低至5.204 W/kg,明显改善了无取向硅钢磁性能。 In this paper combined with the actual production of 0.4% Si non oriented silicon steel, the magnetic properties of non oriented silicon steel without Sn and 0.025% Sn were counted. The microstructure and microtexture of samples with different compositions were observed and analyzed by metallographic microscope and X-ray diffraction. The results show that: Sn can significantly reduce the grain size of non oriented silicon steel, and the average grain size of 0.025% Sn sample is 28.4% smaller tha... 

冷轧中中低牌号的无取向硅钢多采用万能凸度轧机(Universal crown mill,UCM)生产,其板形好坏受制于UCM轧机板形调节手段的协调使用。为掌握UCM轧机的板形控制特点,建立基于二维变厚度有限元的辊系弹性变形和基于三维差分的轧件塑性变形的六辊轧机耦合模型,对UCM轧机的板形调控性能进行详尽的分析,包括工作辊和中间辊弯辊、中间辊窜辊的调控功效、辊间接触压力分布等。在此基础上,提出可用指导生产的板形控制策略,指出UCM轧机在横向厚差控制方面的不足。针对工业生产中UCM轧机轧制无取向硅钢横向厚差大的问题,在大量仿真计算的基础上,开发具有高次曲线函数的边部变凸度(Edge variable crown,EVC)的工作辊。采用该工作辊后,各种品种的无取向硅钢的横向厚差不大于10μm的百分比由24%提高到99%,横向厚差的均值小于6μm,远小于之前的13μm。 Medium-low grade non-oriented silicon steel is rolled often by universal crown mill(UCM) during cold rolling.Its shape quality is dependent on the coordinated control of several shape adjustment devices of UCM.In order to understand the shape control characteristics of UCM,coupling model of six-high rolling mill,based on two-dimensional varying thickness finite element rolls elastic deformation model and three-dimensional finite difference strip plastic deformation model,is setup for the detaile... 

本实用新型公开了一种硅钢片组扣件自动压平装置，包括：定位单元，定位单元包括转盘、校位板和第一驱动组件，第一驱动组件连接并驱动校位板沿竖直方向运动，校位板滑动连接有第一校位柱，第一校位柱相对转盘偏心布置；第一推送单元，位于转盘的一侧，第一推送单元包括第一推送气缸和第一推块，第一推送气缸连接并驱动第一推块沿水平方向运动；冲压单元，位于转盘背离第一推送气缸的一侧，冲压单元包括第二驱动组件和冲压柱，第二驱动组件连接并驱动冲压柱沿竖直方向运动。转盘、校位柱和第一驱动组件配合，周向定位硅钢片组，再通过冲压柱将凸出于硅钢片组的扣件压平，完成硅钢片组的整形，整体更为美观，方便后续的装配使用。

本实用新型公开了一种无取向硅钢的绝缘涂料喷涂装置，包括喷涂支架，所述喷涂支架安装有输送装置，所述喷涂支架的顶端侧壁水平方向固定有横向支撑板；本实用新型通过电机与第二行程开关接触启动工作，带动齿轮转动，驱动支撑杆左移，使喷涂喷头左移喷涂硅钢左端上表面，当电机接触到第一行程开关后，使电机工作带动齿轮反向转动，驱动支撑杆和喷涂喷头右移，在一定范围内，使喷涂喷头可以喷涂不同宽度的硅钢，通过施力转动螺杆，使螺杆左移、右移，使第一行程开关在水平方向移动，调节第一行程开关和第二行程开关之间的水平距离，从而调节喷涂喷头水平方向活动范围，根据硅钢宽度需求喷涂。

对无取向电工钢中的夹杂进行了系统的分析。利用小样电解,采取不同电解液,不同的分离方法对无取向电工钢中稳定和不稳定夹杂物进行了提取、分离和收集。利用扫描电镜(SEM)、X-射线衍射、ICP等对电解分离收集的夹杂物进行了定性和定量分析。 The inclusion analysis of the non-oriented electrical steel has been investigated.By using small sample electrolytic analysis,with different electrolytes and different separation ways,the stable inclusions and unstable inclusions was drew,separated,and collected.With utilizing the methods of SEM,X-ray and ICP,the qualitative and quantitative analysis of inclusions in the non-oriented electrical steel was obtained. 

本发明公开了硅钢片铁芯叠片机构，包括送料装置和叠片装置，送料装置包括有磁性传送带、送料件和第一定位杆，磁性传送带用于将已剪切的硅钢片传送至送料件，送料件安装于磁性传送带的下方，并且可沿磁性传送带的正交方向平行伸出，第一定位杆安装于送料件上，用于定位硅钢片，叠片装置设置于送料件的伸出的一方，包括有叠放台、第二定位杆和机械手，叠放台用于叠放硅钢片，第二定位杆用于定位硅钢片，机械手用于将送料件的硅钢片搬运至叠放台上，机械手包括有转动臂和取料单元，取料单元安装于转动臂的端部，包括有电永磁铁，电永磁铁用于吸取硅钢片。根据本发明的硅钢片铁芯叠片机构，可有效提高叠片速度，降低能耗，提高生产效率。

取向硅钢成品的晶粒尺寸非常大,其易磁化方向[001]晶向对于轧向的偏差角度对其磁性能影响极大。本文介绍了取向硅钢二次再结晶后成品晶粒位向的几种测定方法,包括侵蚀法、劳厄法、OIM法、极图法和非对称X射线衍射法等,并对这几种测量方法进行了比较。 The finished product of grain-oriented silicon steel has immense grain size ranging from millimeters to centimeters and the deviation angles of easy magnetization direction from rolling direction plays a remarkable role in magnetic properties of grain-oriented silicon steel.The methods in common use for determining the deviation angles of crystal direction are introduced,which include the etch-figure method,the Laue method,the OIM method,the pole figure method and the asymmetrical X-Ray diffract... 

【作者】 刘彤； ...

本实用新型涉及电机生产设备技术领域，特别涉及一种硅钢板冲裁余料处理工装，出料带通过支撑架平放在地面上，出料带的上方平行设置有安装在支撑架上的支撑砧板；支撑砧板的上方平行设置有上下滑动安装在支撑架上的刀架，刀架上设有切刀；支撑砧板的一端邻接有上料带，上料带将硅钢板冲裁余料送入到支撑砧板上。本实用新型的有益效果是：本实用新型可将成条的硅钢板冲裁余料进行自动裁切处理，裁切后的三角形的边角料会掉落到出料带中送出，此设备节省了大量的人力成本，提高了车间生产的安全性。

利用电子背散射衍射(EBSD)技术和场发射电子扫描显微镜(FESEM)研究了电工钢中柱状晶不同初始取向50%热压缩变形后的演变规律及其对粒子析出行为的影响。结果表明:〈100〉晶粒形变后仍为〈100〉取向,只发生绕ND∥〈100〉方向的转动,具有遗传性,粒子析出数量少。柱状晶长轴与压缩轴的偏转度增加,取向的稳定性变差,超过40°,可形成〈111〉取向,期间发生复杂的滑移系交互作用,产生较高的缺陷密度,促进粒子析出。MnS粒子主要在晶内析出,变形温度高、形变量低,粒子均无法充分析出。回复时,形变晶粒内高的储能和缺陷密度是促进粒子进一步析出的必要条件。 The evolution of initial orientations and their influence on precipitation of columnar-grained electrical steel after 50% hot compression deformation were investigated by electron backscatter diffraction technique and field emission scanning electron microscopy.The results indicate that the〈100〉orientated columnar grains remain still〈100〉after hot compression deformation,with only rotation around ND parallel to〈100〉direction,with heredity,and less precipitation.As the deviation angle between the... 

本发明公开了一种宽频率低铁损无取向电工钢及其制备方法，属于无取向电工钢生产制造技术领域。它从电工钢表面向内依次包括0.005mm～0.1mm的渗透层和钢材内芯；所述渗透层是由硅原子向电工钢内渗透形成，渗透层中的硅元素含量为3wt％～8wt％；所述钢材内芯包括2.0wt％～5.5wt％的硅元素和不少于93.2wt％的铁元素。本发明能保证无取向电工钢具有低频低铁损性能同时有效降低高频条件下的铁损，具体铁损性能为：铁损P1.5/50≤2.35W/kg，铁损P1.0/400≤13.8W/kg。

本发明涉及一种具有优异铁损和磁性能的无取向电工钢及其生产方法，电工钢成分及质量含量为C≤0.0015%，Si:1.10‑1.40%，Mn：0.35‑0.55%，P≤0.018%，S≤0.003%，Al：0.20‑0.30%，Ti≤0.0015%，N≤0.0028%，O≤0.0015%，N＋O≤0.0040%，余量为Fe和不可避免的杂质。生产方法包括铁水预处理、转炉冶炼、RH精炼、连铸、轧制、常化、冷轧、连退和涂层工序。本发明电工钢热轧成品微观晶粒尺寸70‑95μm，对铁损和磁性能有利的（100）组织织构控制在82‑92%，成品P15/50:3.5‑4.0w/kg，B50:1.70‑1.98T。