根据本发明的一个实施例的粘接涂料组合物，其包含聚乙烯丙烯酸酯，所述聚乙烯丙烯酸酯包含由以下化学式1表示的重复单元和由以下化学式2表示的重复单元，所述聚乙烯丙烯酸酯包含65至90重量％的由以下化学式1表示的重复单元、10至35重量％的由以下化学式2表示的重复单元。

本发明公开了一种耐热刻痕型取向硅钢涂层用涂液，其溶剂为水，其含有：磷酸盐、胶态二氧化硅、铬酐和乙醇。本发明还公开了一种耐热刻痕型取向硅钢板，其包括基板，所述基板表面具有采用上述的耐热刻痕型取向硅钢涂层用涂液涂覆在基板上而形成的涂层。相应地，本发明还公开了上述取向硅钢板的制造方法，其包括步骤：在基板表面涂覆所述涂液，基板的刻痕沟槽涂液填充率＞95％；进行烧结处理，其中烧结处理中的板温为780‑900℃。本发明的耐热刻痕型取向硅钢涂层用涂液具有良好的流动性，其可以涂覆于耐热刻痕取向硅钢基板的表面中，涂覆后，能有效填充基板的刻痕沟槽，且可以在其表面形成涂层，保证耐热刻痕取向硅钢在具有低铁损的同时具备更高的安全性。

通过对激光粒度分析仪测量硅钢级氧化镁(MgO)的分析条件进行优化,如分散介质、分散方式、样品预处理、仪器暗淡度等,探讨了硅钢级MgO粒度范围测量重现性较好的试验方法,满足硅钢生产过程控制对MgO粒度的要求。 The analysis condition of the laser particle size analyzer on grain oriented silicon-steel grade magnesium oxide is optimized,including the dispersion medium,dispersion methods,sample preparation,and instrument obscuration,etc.Therefore,particle size measurement with good reproducibility for silicon-steel magnesium oxide is discussed,which may meet the requirement of MgO particle size for silicon-steel process control. 

针对节能电机对无取向电工钢在磁性能方面的特殊要求,采用普通W600牌号的热轧板为原料,通过大量的现场工艺试验,研究总结出了\"超低张力\"的运行工艺、\"先快后慢\"的加热工艺、\"先湿后干\"的退火脱碳工艺、\"先缓后急\"的冷却工艺,生产出P1.5/50≤4.0 W/kg、B50≥1.70 T的冷轧电工钢产品,满足了节能电机的要求。 Based on the special requirements of no-oriented electrical steel for saving energy motor in magnetic aspects,using common W600 brand of hot rolled plate as raw material,through a large number of real tests,an ultra-low tension process,heating process which was quick at first and then slow,annealing decarburization process which was dry after the first wet,and a cooling technology of \"slow after the first urgent\" were concluded.Electrical steel product with P1.5/50≤4.0W/kg,B50≥1.70T was produced... 

本发明公开了一种控制无取向电工钢横向同板差的装置，包括热轧机、圆盘剪、冷轧机和输送辊道，圆盘剪安装在输送辊道两侧且位于热轧机和冷轧机之间，无取向电工钢在输送辊道的运输下依次经过热轧机、圆盘剪和冷轧机，设定热轧机对无取向电工钢的楔形和凸度进行控制，控制无取向电工钢的楔形在20微米内、凸度为20～45微米，冷轧机的工作辊设有倒角。冷轧机为UCM五连轧轧机，UCM五连轧轧机中1#和2#轧机工作辊的单边设有倒角，1#和2#轧机中上工作辊的操作端设有倒角，下工作辊的传动端设有倒角。倒角的深度为0.2～0.3mm，倒角在工作辊上的起始位置到工作辊端面的距离为265‑285mm。本发明还公开了一种控制无取向电工钢横向同板差的方法。

本实用新型公开了一种用于硅钢片叠装的工装，包括安装底座，所述安装底座上设置有限位装置，所述限位装置包括多个水平限位柱和多个竖直限位柱；各个水平限位柱之间的缝隙的尺寸等于其对应放置的硅钢片的宽度，各个竖直限位柱与安装底座的底边之间的距离等于其对应放置的硅钢片的总长度；所述各个竖直限位柱设置在各个水平限位柱之间的缝隙所正对的位置；采用多个水平限位柱和多个竖直限位柱进行水平和竖直方向上均对硅钢片进行定位；使用此工装叠装出来的成品，长短一致，侧面相当整齐；本实用新型，结构简单，操作方便。

采用自主研发的脉冲磁场退火装置，在取向硅钢脱碳退火过程中分别施加不同强度的磁场，并采用光学显微镜和X射线衍射仪研究了脉冲磁场脱碳退火后试样的显微组织和宏观织构。结果表明，脱碳退火过程中施加脉冲磁场后取向硅钢的平均晶粒尺寸均增加，当磁场强度为40 mT时，平均晶粒尺寸最大，为13.06μm。此外，取向硅钢试样的立方织构{001}<100>强度减弱，高斯织构{110}<001>和{111}<112>织构增强，有利于获得更好的成品织构和磁性能。 Self-developed pulsed magnetic field annealing device was used to apply magnetic field of different intensities during decarburization annealing of an oriented silicon steel, and microstructure and macro-texture of the specimens after decarburization annealing in a pulsed magnetic field were studied by using optical microscope and X-ray diffractometer. The results show that the average grain size of the oriented silicon steel increases with the application of pulsed magnetic field during decarbu... 

对无取向电工钢中的夹杂进行了系统的分析。利用小样电解,采取不同电解液,不同的分离方法对无取向电工钢中稳定和不稳定夹杂物进行了提取、分离和收集。利用扫描电镜(SEM)、X-射线衍射、ICP等对电解分离收集的夹杂物进行了定性和定量分析。 The inclusion analysis of the non-oriented electrical steel has been investigated.By using small sample electrolytic analysis,with different electrolytes and different separation ways,the stable inclusions and unstable inclusions was drew,separated,and collected.With utilizing the methods of SEM,X-ray and ICP,the qualitative and quantitative analysis of inclusions in the non-oriented electrical steel was obtained. 

本实用新型提供了一种防止冷轧硅钢卷错位的剪切用输送装置，所述支架安装在放置架一侧，所述支架上设有安装块，所述安装块上设有支撑杆，所述支撑杆上设有气缸一，所述气缸一上设有固定片，所述放置架下设有安装块一，所述安装块一下设有万向轮，所述放置架一侧设有通口一，在使用的时候，可以对于冷轧硅钢卷进行剪切，可以防止在剪切的过程中错位，安装的支撑杆，可以用来放置硅钢卷，里面安装的气缸一可以固定硅钢卷的位置，方便进行旋转，外壳内两侧安装的压板可以通过气缸二压住硅钢片，可以防止其在剪切的过程中错位，安装的刀片可以通过滑轨进行前后移动切割，支架与底座之间没有连接，可以在一卷硅钢卷使用完之后进行更换。

通过对辉光放电发射光谱法分析电工钢样品光谱行为的研究,分析其工作参数如:电压、电流、预溅射时间和积分时间对光谱强度和稳定性的影响,并以铁为内标元素,优化了工作参数。确定了直流辉光放电光谱法测定电工钢中碳、硅、锰、磷、硫、铬、镍、铜共8种元素的定量分析方法,并对该方法分析的精密度和准确度进行验证,结果表明,各元素的测定结果与认定值和其他方法测定值一致,测量元素结果RSD值小于2%。 Based on research on analyzing the spectrum behavior of the sample taken from the electrical steel by glow discharge optical emission spectrometry,the effect of its operational parameters such as current,voltage,pre-sputtering time and integrating time on the spectral intensity and spectral stability is analyzed.Taking the Fe as an element applied by internal standard method,these operational parameters are optimized,and therefore the quantitative analysis method for testing eight kinds of eleme... 

本发明提供在金属带钢表面以所希望的槽宽度形成线状槽进而磁特性极其优异的方向性电磁钢板。在金属带钢的至少单面形成抗蚀剂被膜，接着，对上述抗蚀剂被膜一边在横穿上述金属带钢的轧制方向的方向进行扫描一边照射激光，除去经上述激光照射的部分的上述抗蚀剂被膜，接着，对上述金属带钢的除去了上述抗蚀剂被膜的部分实施蚀刻处理而形成线状槽，上述抗蚀剂被膜以固体成分换算计含有20质量％以上的无机化合物，在上述金属带钢表面，上述激光具有长轴直径与短轴直径之比为5.0以上的椭圆状的射束形状，并且扫描正交方向的射束直径为10μm～100μm。

本发明公开了一种高磁感取向硅钢实验室轧机一次冷轧方法，包括：1)取样，实验室冷轧材料选取经过常化酸洗后的厚度为2.3mm的取向硅钢试样；2)制样，利用取向硅钢专用剪板机，裁剪试样尺寸为轧向600mm×横向150mm；将试样表层轻涂一层薄薄的轧制油；3)冷轧轧制规程制定，轧前厚度为2.3mm；其中：轧制总道次为6次时轧后厚度为0.35mm，轧制总道次为7次时轧后厚度为0.27mm，轧制总道次为8次时轧后厚度为0.23mm。本发明的目的是提供一种高磁感取向硅钢实验室轧机一次冷轧方法，为工业试制提供一定的技术参考，以及后续工艺研究提供了更加可靠的试样和条件。