采用扫描电镜、原子力显微镜研究了铬酸镁半无机绝缘涂层的微观结构。结果表明,涂层厚度为数微米,涂层中的有机树脂乳液颗粒均匀分布在无机涂层的表面,从而保证了涂层具有良好的冲片性能。采用极化曲线研究了涂层的耐蚀性能,发现铬酸镁与铬酸锌绝缘涂层的耐蚀性能相当。 In this paper,the microstructure and anti-corrosion property of magnesium chromate coating on non-oriented silicon steel were studied.The microstructure was observed by SEM and AFM.The anti-corrosion properties were evaluated by polarization curves.The results show that the thickness of coating is several microns and the polymer particles were scattered on the surface of inorganic coating,which is the guarantee for lamination property.The corrosion resistance of the magnesium chromate film was e... 

采用经验设计法初步确定了取向硅钢铸坯感应加热线圈设计参数,应用Ansoft仿真软件分别对36组不同线圈高度、线圈内径的感应加热炉在不同频率下的三维整体磁场和铸坯的温度场进行了数值仿真。通过对比仿真结果,确定电磁场分布最佳的一组感应加热炉设计参数为线圈高度h=1.50 m、线圈内径D1=0.575 m、电流频率f=110 Hz。在该参数下应用Ansoft仿真软件对取向硅钢铸坯感应加热炉的温度场进行了仿真,结果发现温度场分布均匀,可满足取向硅钢铸坯加热要求。 The induction heating coil design parameters for the oriented silicon steel casting blank were determined preliminary by experience design method,and 36 groups three-dimensional electromagnetic field with different height and inside diameter of coil under different frequencies of the induction heating furnace and the temperature field of the casting blank were investigated by numerical simulation using Ansoft simulation software. By comparing the simulation results of electromagnetic field distr... 

提供一种如下的无取向性电磁钢板用钢板：含有：C：0.0040％以下、Si：1.9％以上3.5％以下、Al：0.10％以上3.0％以下、Mn：0.10％以上2.0％以下、P：0.09％以下、S：0.005％以下、N：0.0040％以下、B：0.0060％以下；剩余部分由Fe和杂质构成；分别从板宽方向的两端部向板宽中央10mm的各位置的板厚方向截面组织的重结晶率不足50％；将板宽记为W时，分别距板宽方向的两端部1/4W的位置的板厚方向截面组织的重结晶率在50％以上。

本发明涉及冶金技术领域，具体涉及一种高牌号硅钢用连铸结晶器保护渣及其制备方法和应用。本发明提供的连铸结晶器保护渣，所述保护渣包括如下质量百分比的化学成分：SiO2：40‑45％、CaO：20‑27％、MgO：1.0‑2.5％、Al2O3：1‑3％、Na2O：12‑16％、F：10‑13％、C：1‑3％，其余为不可避免的杂质；其中所述保护渣的二元碱度CaO/SiO2为0.5‑0.6，熔点为950‑1000℃，1300℃下的粘度为0.25‑0.35Pa·s。本发明提供的连铸结晶器保护渣，通过低碱度、低熔点、低粘度的保护渣可有效抑制高牌号硅钢材料在连铸时铸坯表面易出现凹陷和裂纹的现象。

借助OM、激光共聚焦显微镜、质谱仪和电解萃取等设备和方法，研究了添加微量稀土La（质量分数0.001 1%）的取向硅钢在轧制前采用不同加热保温时间对抑制剂固溶行为的影响。结果表明：当稀土取向硅钢在1 250℃分别保温10、20、30 min后，试验钢晶粒尺寸随保温时间延长有先快后慢的长大趋势；三种抑制剂元素Mn、Cu和Al均发生固溶，保温时间对Mn和Cu两种元素的固溶影响明显，固溶量分别由69.8%和43.7%增加至84.2%和85.2%；随着保温时间的延长，稀土取向硅钢中抑制剂的小尺寸未溶物逐渐减少直至消失，较大尺寸未溶物（300～600 nm）逐渐转变为小尺寸未溶物逐步溶入基体中，数量减少且未溶物的类型由复杂逐渐转变为单一。 In this paper the solid solution behavior of the inhibitor under various holding time in 0.001 1 %La oriented silicon steel during reheating had been investigated by using OM, LM, methods of electrolytic extraction and mass spectrometer. The results showed that grain size of the test steel increased significantly with the holding time prolonging when the rare earth oriented silicon steel was heated to1 250 ℃ and held for 10, 20 min and 30 min respectively, and the growth trend slowed down after ... 

本发明涉及电机技术领域，具体涉及一种具有低应力结构的硅钢片、转子和电机。包括硅钢片、开设在硅钢片上的磁钢槽和嵌设在所述磁钢槽内的磁钢组件，所述磁钢组件包括多个磁钢组，所述磁钢组包括靠近转子边缘的一对小永磁体和靠近转子内侧的一对大永磁体，所述硅钢片在转子轭部沿周向分布有径向开槽，且所述径向开槽从硅钢片的中心向边缘延伸。其通过在转子轭部沿周向分设置从硅钢片的中心向边缘延伸的径向开槽，能降低大永磁体左右两侧铁芯刚度差距，从而有效降低隔磁桥处的应力，防止磁钢和铁芯产生形变而断裂。其无需改变电机转子外圆结构，在保证转矩输出的前提下，防止高速旋转时带来空气啸叫声。

本发明提供一种含铜一般取向硅钢及其制备方法，制备方法包括：对钢板进行脱碳退火，得到脱碳钢，其中，将所述脱碳钢的氧含量控制在如下公式计算的范围内：ψO＝(0.0504×ωSi×H2±0.00005)×106，其中，ψO为脱碳钢的氧含量，单位为ppm；ωSi为钢板中Si的重量百分含量；H为钢板的厚度，单位为mm；将所述脱碳钢进行冷轧、涂布氧化镁涂层、卷曲和成卷退火，得到退火钢卷；对所述退火钢卷进行开卷，再涂敷张应力涂层和拉伸平整退火，制得含铜一般取向硅钢。本发明根据钢板中Si的实际含量及钢板厚度，调整脱碳钢的氧含量，以获得表面质量良好、磁性水平稳定的含铜一般取向硅钢产品。

本申请提供一种电工钢及其制备方法，制备方法包括：将电工钢的板坯进行热轧获得钢卷；将热轧后的钢卷进行酸洗冷轧；将酸洗冷轧后的钢卷进行第一次罩式退火；将第一次罩式退火后的钢卷进行平整；将平整后的钢卷进行第二次罩式退火；将第二次罩式退火后的钢卷进行重卷，以获得电工钢。本申请提供的电工钢的制备方法采用两次罩式退火，退火的主要目的是消除酸洗冷轧工序产生的加工硬化，使钢板充分再结晶，获得理想的铁损及磁感应强度。而采用两次罩式退火，相对于一次罩式退火工序来说，能够进一步降低铁损，提高电工钢的磁性能。

本发明公开了一种降低无取向硅钢W800头部窄尺的控制方法，步骤1、筛选板坯长度，并使板坯进入加热炉后头部均朝向轧机方向；步骤2、控制板坯头部温差小于10℃；步骤3、固定粗轧到精轧区间内的轧机机架轧制速度；步骤4、固定相变机架，使板坯的奥氏体‑铁素体相变发生在F2和F3机架中；步骤5、调整精轧机架间的负荷分配，降低F2和F3机架的压下量；步骤6、调整活套张力，降低F2和F3机架的活套单位张力补偿；步骤7、降低模型AGC增益，降低F2和F3机架的AGC补偿的辊缝波动量。本发明通过控制固定相变机架、优化相变机架的负荷分配、AGC补偿系数、活套张力等，使秒流量保持平衡，减少无取向硅钢W800头部窄尺。

本发明涉及硅钢带的制备技术领域，具体公开一种软磁性高硅钢极薄带及其制备方法。所述软磁性高硅钢极薄带的制备方法包括熔炼、包覆CaF2和TiB2偶合涂层、微波热压成型、酸洗、渗氮、一次退火、三道热轧、二次退火、三次温轧和三次退火。本发明提供的软磁性高硅钢极薄带的制备方法制得的软磁性高硅钢极薄带的晶粒细化程度高、组织均匀，改变了传统的相析出路径，有效消除了有序相的形成，使其具有优异的延展性，并具备更高的磁感和更低的铁损。

【作者】 杨佳直； ...

本发明公开了一种低磁场条件下高磁感应强度无取向电工钢及生产方法，步骤包括：冶炼：炼钢、连铸生产铸坯，所述铸坯中：以质量百分比计，Si2.0％、Mn0.2‑0.5％、ALs0.3‑0.6％、N≤0.002％、S≤0.002％、Ca≤0.001％，余量为Fe及不可避免的杂质；板坯热轧、卷取；常化处理；退火处理。本发明通过合理的电工钢成分设定、生产工艺、稳定的控制精度，从一贯制角度对产品进行设计及控制，最终能够保证产品质量稳定、具有低磁场条件下高磁感应强度的Si含量2％的0.35mm厚度无取向电工钢产品。