采用中、厚板坯生产技术对取向硅钢进行了研制和开发,对热轧及后工序样品进行了金相组织观察和EBSD分析,探讨了两种组织及织构的差异性,研究结果表明:除高温退火样品外,中板坯生产的取向硅钢各工序样品平均晶粒尺寸大;厚板坯生产的取向硅钢热轧和常化样品亚表层Goss织构强;中板坯和厚板坯的脱碳退火板织构没有明显区别。中板坯生产的取向硅钢成本低,产品磁性能和质量与厚板坯相当。 Grain oriented silicon steel was researched and developed by medium thickness slab and thick slab.Microstructures observation and EBSD analysis to the samples of hot rolling and following processes were carried out,respectively.The differences between the two kinds of microstructures and textures were discussed.The results show that the average grain sizes of every process samples are larger except that of high temperature annealing samples of grain oriented silicon steel produced by medium thic... 

薄带连铸流程下取向硅钢粗大λ晶粒(〈100〉//ND,normal direction)的“遗传”会导致磁性能恶化.为解决这一问题，针对取向硅钢的热轧孪生行为开展研究，结果表明：凝固组织粗大的取向硅钢在650℃热轧时可产生大量{112}〈111〉形变孪晶，这与具有高层错能的硅钢在较高温度下难以孪生变形的传统认知不同.热轧过程中复杂的应力状态降低了变形孪晶的取向依赖性，由于具有更高的储存能，孪晶界/孪晶界及孪晶界/晶界交叉点成为再结晶形核的优先位置，大大提高了常化过程中的再结晶率，受沿孪晶界应变分布及孪晶间距离的限制，沿孪晶界形核的再结晶晶粒通常呈“饼状”,最终形成以细小且取向漫散的再结晶晶粒为主的常化组织，消除了初始凝固组织中有害的粗大λ晶粒. In strip casting grain-oriented silicon steels, the inheritance of coarse λ grains(〈100〉//ND, normal direction) can deteriorate their magnetic properties. To solve the problem, twinning behaviors in strip casting grain-oriented silicon steels during hot rolling were investigated in this work. It is found that after rolling at 650 ℃, a number of {112}〈111〉deformation twins are formed in the coarse solidification microstructure of the steels, in contrast to the well-accepted view that it is diffic... 

本发明揭示了一种无取向硅钢及其生产方法。所述生产方法包括：按照Si0.8～1.1％、Mn0.2～0.4％、不添加Sn和Sb进行炼钢，并制坯；将铸坯加热到1060～1120℃并保温150min以上，而后轧成厚度40～45mm的中间坯，再经精轧、卷取得到厚度为3.00±0.25mm的热轧卷板，精轧开轧温度≤872℃+1000*(11*[Si]‑14*[Mn]+21*[Al])；精轧终轧温度≤820℃，卷取温度≤560℃；常化、酸连轧，得到厚度为0.500±0.005mm的冷硬卷，常化温度850～900℃；成品退火温度820～880℃，退火后经冷却、涂层和精整，得到无取向硅钢。

本发明涉及一种混合硅钢定子结构及与其配套的转子结构及永磁电机，属于电机技术领域，包括：定子，由多个第一硅钢片叠压构成；多个线圈绕组，均匀设置在定子的内壁上；第一硅钢片包括：多个连接块与多个连接臂，连接块与连接臂交替排列构成硅钢环片，连接块采用无取向硅钢且与两侧的连接臂通过拼合结构连接，连接臂采用取向硅钢；多个定子齿，呈放射状均匀设置在硅钢环片的内侧，定子齿与连接块也通过拼合结构连接，定子齿采用取向硅钢；本发明通过取向硅钢、无取向硅钢混合组成的定子，能够有效提导磁性能；本发明能够稳定提升定子上的磁性能，增加电机的输出能力，实用性强，值得推广。

【作者】 欧阳帆； 肖侃； ...

本发明公开了一种拉矫机矫直低牌号无取向硅钢的方法，当焊缝达到拉矫机前面时，生产线的整体速度降低至28‑32m/min、拉矫机的辊系辊缝全部打开同时辊系不接触钢带、拉矫机的延伸率降到0.08％‑0.12％、拉矫机前后张力辊的压辊全部压下，焊缝通过拉矫机后，均恢复到正常水平。本发明的目的是提供一种拉矫机矫直低牌号无取向硅钢的方法，解决焊缝经过拉矫机时焊缝在拉矫机的拉伸矫直作用下发生断带的事故的问题。

本实用新型公开了E字型硅钢片的级进模冲压装置，属于冲压模具设备领域，所述下模具包括与冲孔凸模、冲方孔凸模、切断凸模分别对应且相适配的冲孔凹模、冲方孔凹模、切断凹模，所述上模具上设有对条料板进行输送的导料板，所述冲孔凸模、冲孔凹模均设有两对并且并排设置，且每对冲孔凸模、冲孔凹模均设有两个，每个所述冲孔凸模、冲方孔凸模、切断凸模的顶端均用微米级间隙固定安装于上模具上，所述冲孔凹模、冲方孔凹模、切断凹模的底端均用微米级间隙固定安装在下模具上。本实用新型中各个凸、凹模分别采用硬质合金拼块、镶块式的结构并用微米级间隙固定安装在上、下模具上，这样不仅可节省材料的费用，同时还便于人们后期对模具的维修和使用。

介绍了攀钢冶炼电工钢过程硫含量变化以及过程回硫、增硫情况,采取针对性措施,如:提高铁水装入量、转炉采用石英砂代替复合造渣剂造渣、RH脱硫等,降低钢中硫含量。结果表明:采取相应措施后,电工钢炼成率大幅提高,成品w[S]≤0.008%的比例由改进前的62%提高到92.4%,取得了明显的冶金效果。 The resulfurization and the change of sulphur content in production of electrical steel is analyzed.The targeted measures have been taken,such as increase the loaded quantity of liquid iron,quartz sand replaces the composite slagging agent in the converter and RH desulfurization to decrease the sulphur content of the steel.The result shows,after the measures have been taken,the finished product ratio of electrical steel increase a lot.The ratio of sulfur content of finished product no more than ... 

通过测试取向硅钢不同工艺条件下的碳含量,探讨了CGO取向硅钢碳含量控制的最优处理条件,研究了脱碳温度和脱碳时间对相同初始碳含量取向硅钢的脱碳效果的影响。结果表明,在气氛为(15%~20%)H2+(75%~80%)N2,炉压差为10~20 Pa的条件下,CGO取向硅钢合适的脱碳温度为1 073 K~1 123 K,脱碳时间为10~20 min。在该处理条件下,能取得较好的脱碳效果。 By means of testing carbon content of oriented silicon steel below the distinct technical conditions,inquires the excellent handle terms of carbon content controlling for CGO oriented silicon steel,studies effects of decarburization annealing temperature and decarburization annealing time to the oriented silicon steel decarburization efficiency in same initial carbon content.The results show that,under the condition of atmosphere(15% ~ 20%) H2+(75% ~ 80%)N2 and furnace pressure difference 10 ~ 2... 

【作者】 党其； ...

本发明涉及一种具有优异铁损和磁性能的无取向电工钢及其生产方法，电工钢成分及质量含量为C≤0.0015%，Si:1.10‑1.40%，Mn：0.35‑0.55%，P≤0.018%，S≤0.003%，Al：0.20‑0.30%，Ti≤0.0015%，N≤0.0028%，O≤0.0015%，N＋O≤0.0040%，余量为Fe和不可避免的杂质。生产方法包括铁水预处理、转炉冶炼、RH精炼、连铸、轧制、常化、冷轧、连退和涂层工序。本发明电工钢热轧成品微观晶粒尺寸70‑95μm，对铁损和磁性能有利的（100）组织织构控制在82‑92%，成品P15/50:3.5‑4.0w/kg，B50:1.70‑1.98T。

一种硅钢厂调功器故障报警自动复位的方法，包括：通过人机界面对炼钢炉温度进行设定，并在炼钢过程中实时获取炼钢炉温度；将炼钢炉实时温度与设定温度进行对比，当炼钢炉实时温度低于设定温度时，启动调节器；调节器输出功率使电阻带加热，使炼钢炉实时温度达到设定温度；当调节器发生故障时，调节器将故障信号发送给后台服务器，后台服务器根据故障指令，按预设规则控制与调节器连接的继电器，控制继电器按压复位按钮，使调节器自动复位。本发明解决了现有技术中通过电气人员来通过复位消除故障状态，耽误时间长，容易产生废品的问题。