硅钢资料

在现普通冷轧无取向硅钢的基础上,降低Si含量,复合添加少量辅助元素,组合热轧板处理和成品退火加热技术,研制出了免常化处理的高磁感、低铁损并具有良好耐酸腐蚀性能的新系列无取向电工钢。 Based on existing common cold rolled non-oriented silicon steel,a new series of non-orientedelectrical steel with high induction,low core loss and excellent anti-corrosion property has been developed by reducing Si element,adding complexly a small amount of supplementary elements,and employing combined treatment of hot rolled sheet and finished product annealed heated technology. 

采用经验设计法初步确定了取向硅钢铸坯感应加热线圈设计参数,应用Ansoft仿真软件分别对36组不同线圈高度、线圈内径的感应加热炉在不同频率下的三维整体磁场和铸坯的温度场进行了数值仿真。通过对比仿真结果,确定电磁场分布最佳的一组感应加热炉设计参数为线圈高度h=1.50 m、线圈内径D1=0.575 m、电流频率f=110 Hz。在该参数下应用Ansoft仿真软件对取向硅钢铸坯感应加热炉的温度场进行了仿真,结果发现温度场分布均匀,可满足取向硅钢铸坯加热要求。 The induction heating coil design parameters for the oriented silicon steel casting blank were determined preliminary by experience design method,and 36 groups three-dimensional electromagnetic field with different height and inside diameter of coil under different frequencies of the induction heating furnace and the temperature field of the casting blank were investigated by numerical simulation using Ansoft simulation software. By comparing the simulation results of electromagnetic field distr... 

一种通过粉末烧结制备高磁性能含磷硅钢薄片的方法，属于粉末冶金技术领域。本发明通过真空熔炼气雾化制备成分范围为Fe‑(3‑6.5)wt.％Si‑(0.05‑1)wt.％P的合金粉，将其放置在陶瓷坩埚中均匀振实并放置重物压住，随后进行高温烧结使其冶金结合，再经热轧、冷轧、退火等处理后，得到具有优异性能的含磷硅钢薄片。本发明在硅钢材料体系中加入P元素，能够有效降低铁损、优化磁性能并促进活化烧结；采用气雾化粉末能够很好地保证产品的少夹杂和纯净度；在低熔点P元素及粉末压烧的协同作用下解决了球形气雾化粉末难以成形的缺陷，并避免了需添加成形剂导致的工艺复杂性及后续的脱胶残碳问题，有效缩短制备工艺流程，具有操作简单、生产效率高、工艺流程短、性能优异等优点。

以质量分数为25%的丙烯酸乳液MC-102、15%Al(H2PO4)3溶液、0.01%H3BO3、0.01%Zn(Ac)2·2H2O和2%二乙二醇丁醚组分,在不同固化工艺下制备涂层。极化曲线和电导率测试发现300℃处理60 s得到的涂层具有良好的耐腐蚀性和绝缘性;水煮实验证明该涂层具有良好的耐水性;断口线扫描发现涂层具有良好的附着性。 A formula comprising MC-102 acrylic emulsion 25%,aluminium dihydrogen phosphate15%,boric acid 0. 01%,zinc acetate dihydrate 0. 01% and diethylene glycol monobutyl ether 2% was used to prepare coatings via different treatment process. The conductivity test and polarization curves revealed that a coating cured at 300 ℃ for 60 s showed good insulative and anticorrosive properties. The water boiling test indicated that the said coating had good water resistance. A cross section of the coating was in... 

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

采用取向分布函数和取向线分析方法对低温板坯加热取向硅钢从热轧到初次再结晶工艺阶段的织构进行了研究。研究表明:一次冷轧后各层的织构组分与热轧板各层面的织构组分存在着继承关系,次表层存在很强的{001}<110>织构,中心层的织构和热轧板的中心层相似,存在强的{001}<110>和{112}<110>织构;中间退火后发生再结晶,各织构组分的强度有所减弱,Goss织构组分再次出现;二次冷轧后沿厚度方向上的织构不均匀性不明显,{111}<112>织构强度最高,几乎是其他织构组分的1倍,{001}<110>织构大幅降低;初次再结晶后织构沿厚度方向没有明显的不均匀性,{111}<110>为最强的织构组分,并且具有一定强度的Goss位向。 The texture from the first cold rolling to the primary recrystallization of low temperature slab reheating grain-oriented electrical steel were researched by orientation distribution function and orientation distribution intensity technique.The results show that after the first stage of cold rolling,there is a strong {001}<110> texture in the subsurface and the texture in center layer is very similar to the center layer of hot band which has strong {001}<110> and {112}<110> tex... 

为研究退火工艺对普通取向硅钢初次再结晶组织的影响,对经不同温度、保温时间和升温速率退火后的材料组织进行了分析。结果表明:在等温退火条件下,加热至600℃时开始发生初次再结晶,800℃以上初次再结晶组织发展完善;而在最终冷轧板直接进行最终高温退火的情况下,加热温度在500～700℃时,将升温速率提高到80℃/h,初次再结晶组织更易于发展完善。 To investigate the influence of annealing process on the recrystallization of common grain oriented silicon steel,microstructures of sheets annealed at different temperature,soaking time and heating rate are observed.Results show that under the condition of isothermal annealing,recrystallization begins at 600℃ and fully develops above 800℃,while in the case that the final cold rolled sheets are directly thrown to final high temperature annealing,recrystallization is likely to develop with the he... 

本实用新型公开了一种能限位的硅钢片，包括主体，主体的上表面设置有限位柱，限位柱的轴心处开设有散热孔，主体的上表面开设有限位槽，主体的外壁设置有凹槽，主体的下表面设置有限位凸起，主体的下表面开设有限位孔；该一种能限位的硅钢片通过在主体的外壁设置凹槽可以方便拿取，在其上下表面分别设置限位柱与限位孔，可以使主体间的位置相对固定不会轻易挪动。

该电磁钢板为母材钢板的其中一个或两个表面中的至少一部分被具有接合能力的绝缘被膜覆盖的电磁钢板，所述绝缘被膜的25～100℃的温度范围的对数衰减率为0.3以下。

一种薄规格中高牌号无取向硅钢酸轧生产工艺，属于无取向硅钢冷轧成型技术领域，该生产工艺在焊接前对焊缝预加热和焊接后对焊缝两次后加热，采用五机架六辊冷连轧机组轧制，其压下率分别为35％‑45％、35％‑45％，30％‑36％，25％‑30％，1％‑10％，第一二冷轧机间、第二三冷轧机间、第三四冷轧机间、第四五冷轧机间的单位张力分别为120‑130KN/mm2、130‑140KN/mm2、150‑160KN/mm2和160‑180KN/mm2，本发明的有益效果是，本发明通过对冷连轧的工艺进行改进优化，提高了薄规格中高牌号无取向硅钢带的轧制效率，提高了同板差的合格率，降低了轧制的断带率和轧烂率。

本实用新型公开了一种硅钢环形炉台车用垫片，垫片为多个陶瓷纤维高密度板拼接而成的环状，垫片的内边缘和外边缘均呈正八边形；陶瓷纤维高密度板的导热系数不大于0.15W/(m·k)。上述垫片在实际使用时，铺设于台车的底座，并在垫片上砌筑耐火砖，最后在耐火砖上浇筑耐火浇注料。因垫片的导热系数很低，因此能够减少台车底座背面热量的散失，并且能够避免高温对台车内钢卷造成影响，保证了钢卷的质量。因此，本实用新型提出的硅钢环形炉台车用垫片，对台车进行了改进，保证了钢卷的品质，解决了现阶段该领域的难题。

本发明提供一种高磁感低铁损硅钢极薄带的生产方法，包括：对硅钢极薄带进行清洗，并对清洗后的所述硅钢极薄带进行烘干；对烘干后的硅钢极薄带进行涂覆隔离层；将涂覆有所述隔离层的硅钢极薄带进行高温退火处理，其中，高温退火过程包括：快速升温至300～600℃，慢速升温至800～1300℃，并在预设温度时进行保温，保温至预设时间后进行冷却，冷却至50～300℃；对退火处理后的硅钢极薄带进行表面清洗、干燥以及涂覆绝缘层；将涂敷绝缘涂层的硅钢极薄带进行烘干烧结处理，并卷取成品。利用本发明，解决目前硅钢极薄带在连续退火涂层工艺存中存在张力不易控制，而导致硅钢带材的板形变差且极易发生断带等问题。