本实用新型公开了一种硅钢片生产用机器人定位台，包括箱体，所述箱体的顶部中心处活动安装有转动盘，且转动盘的顶部安装有多组转动块，所述转动块由电机驱动旋转，其中，所述转动盘的中心处安装有中心定位圆，且中心定位圆的外部设置有键槽凸口；所述箱体的顶部安装有多组气缸。本实用新型所述的一种硅钢片生产用机器人定位台，一是定圆心，四个气缸对产品的外圆挤压定位，定位完成后，产品内圆掉落至中心定位圆内；二是，定方向，现有的硅钢片内圆具有键槽口，在电机带动转动盘转动时，由于转动盘上内嵌磁铁，能将产品进行旋转，直到产品的键槽口掉落至中心定位圆的键槽凸口内，完成定位，从而将定位设计的简单化与精准化。

利用X-射线衍射织构分析和线形分析技术测定了交叉轧制双取向硅钢在制备工艺各阶段的织构及微结构,进而探讨了立方织构({100}<001>)的形成过程。通过对实验结果的分析可知,二次冷轧和交叉轧制工艺为立方织构提供了内能优势和有利的形变织构,而低温预退火工艺既强化了立方织构的内能优势,又为立方织构的异常长大提供了有利的组织保证,最终在抑制剂(AlN和MnS)的协同作用下,硅钢在二次再结晶退火后形成了强烈的立方织构。 The texture and substructure of the double oriented electrical steels produced by the cross rolling technology during the difference process has been measured by means of the X-ray texture and diffraction peak profile analysis technology,and research the formation mechanism of cube texture,{100}<001>.The results show that the dominances of inner energy and deformation texture were supplied by secondary cold rolling and the cross rolling technology and strengthened by pre-annealing at a low... 

本发明公开了一种无取向硅钢用预熔型结晶器保护渣，涉及冶金技术领域，其化学成份按质量百分比计为：CaO：25.2%‑25.6%，SiO2：39.2%‑39.6%，MgO：1.9%‑2.1%，Al2O3：2.9%‑3.1%，Na2O+K2O：10.5%‑10.7%，F：9.9%‑10.1%，Li2O：1.9%‑2.1%，MnO：2.0%‑2.2%，C固：1.9‑2.1%，余量为不可避免的杂质，熔点：1000‑1040℃，粘度at1300℃：0.18‑0.19Pa.S，通过喷雾造粒制成中空颗粒。制备的无取向硅钢结晶器保护渣是空心颗粒，堆比重轻，空心颗粒提高了铺展性，喷雾造粒的空心球颗粒能形成绝热层，可有效地降低钢水向外传热速度，隔热保温效果好。

提出一种基于粒子群优化算法实现的硅钢涂层厚度近红外光谱检测新方法。首先,采用近红外光谱仪采集获得了硅钢表面绝缘涂层的近红外光谱,然后,采用离散粒子群算法筛选出近红外光谱数据的最佳波长变量并组成新的光谱数据,最后,建立涂层厚度的核偏最小二乘定量分析模型。实验显示,所建定量分析模型对检验样本分析的绝对误差范围为-0.12～0.19μm,最大相对误差为14.31%,完全符合现场检验需要。研究表明,离散粒子群算法可以有效地筛选出携带更多有用信息的波长变量,提高定量分析模型的分析准确度和速度,是一种有效的近红外光谱波长筛选方法,同时,近红外光谱法也是一种有效的硅钢绝缘涂层厚度检测方法。 A novel thickness measurement NIR spectrometry for surface insulation coating of silicon steel based on discrete binary particle swarm optimization(DBPSO) algorithm is presented.First,we used NIR spectrometer to collect the NIR spectra of insulation coating of silicon steel,and then,DBPSO algorithm was used to select the optimal wavelength variates and composed a new spectra set.Last,the authors created the thickness quantitative analysis model using kernel partial least square algorithm.The exp... 

本发明公开了叠片装置，以及采用该叠片装置的硅钢片收料设备，包括分料装置和本发明第一方面实施例的叠片装置，分料装置包括有分料件、上分料传送带和下分料传送带，上分料传送带的一端和下分料传送带的一端与分料件连接，分料件用于将硅钢片分别输送至上分料传送带和下分料传送带，本发明第一方面实施例的叠片装置，叠片装置的数量为两个，两个叠片装置上下平行设置，并且分别与上分料传送带和下分料传送带的远离分料件的一端连接。根据本发明的叠片装置，以及采用该叠片装置的硅钢片收料设备，可实现硅钢片的自动叠片，提高生产效率。

某厂对电工钢的轧制策略进行了优化，粗轧道次由“1+5”改为“1+3”。在优化后的生产过程中，每次变换钢种，烫辊材就会出现窄尺现象，而紧随其后的电工钢板则出现超宽现象。文中针对该问题，介绍了宽度设定模型和宽度自适应模型的原理，阐述了该问题出现的原因及解决方案，并通过对宽度自适应模型的应用研究及优化攻关，有效地解决了问题，大幅提升了实物质量，降低了宽度封锁率。 The rolling strategy of electrical steel was optimized in a factory,and the rough rolling pass was changed from “1+5”to“1+3”.Subsequently,the following problems were occurred in the production process:when the steel grade changed,the roasting roller steel before the electrical steel appeared the narrow width phenomenon,and then the electrical steel appeared the ultra-wide phenomenon.This paper introduced the principle of width setting model and width adaptive model,and expounded the causes and s... 

对RH法(真空循环脱气法)生产的冷轧硅钢的脱硫原理及影响因素进行了分析研究。研究表明:降低顶渣中FeO、MnO的含量,提高钢液温度,增加脱硫剂的加入量并延长其循环时间有利于提高脱硫效率。 The principles of desulfurization and its influence factors of cold rolling silicon steel during RH process have been studied in this paper.The result indicated that reducing contents of FeO and MnO,rising temperature of the liquid steel,increasing quantity of desulfurizer,lengthening cycle time of desulfurzer are benefit for desulfurization. 

本实用新型公开了硅钢片卷材加工用张力机构以及硅钢片剪切机，包括安装架、转动装置和按压装置，安装架的上安装块、连接块和下安装块组成凹槽，转动装置包括下转轴和转动驱动单元，下转轴水平设置，可转动地安装于下安装块上，设置于凹槽中，按压装置包括有上转轴和按压驱动单元，上转轴水平设置于下转轴的上方，可转动地安装于上安装块上，设置于凹槽中，并且可沿上安装块上下运动，其中，上转轴可与下转轴抵接。根据本实用新型的硅钢片卷材加工用张力机构以及硅钢片剪切机，可加强硅钢片卷材输送过程中的张力，降低硅钢片卷材输送的位置偏差率，提高产品合格率，提高原材料利用率，从而提高生产效率。

本实用新型公开了一种新型取向硅钢薄板，所述硅钢薄板包括薄板主体,薄板主体呈方形,薄板主体的内部具有硅钢基板,所述薄板主体的上部具有耐磨层,耐磨层底部还具有抗压层，耐磨层具有若干均匀分布的耐磨条,耐磨层之间分别等距间隔布置，间隔的耐磨条之间形成透气槽,透气槽具有两个侧边，透气槽底部具有透气通孔,所述透气槽两侧具有导风侧凸条,导风侧凸条具有根部和端部，根部分布在透气槽的底部左侧和右侧位置，所述端部延向透气槽两侧边部上部，所述耐磨条为均匀排列的若干双V型结构，双V型结构纵向排列，耐磨条和抗压层之间具有硬质包覆层，在不影响耐磨作用的前提下能够起到透气通风的效果，不需要增加硅钢薄板的厚度。

本实用新型公开了一种铁芯硅钢片移动夹具，包括底板，所述底板上表面固定连接有固定板，所述底板的后表面固定连接有支撑腿，右侧所述支撑腿的前表面固定连接有转轴，所述转轴的外表面转动连接有转动板，所述底板的上表面且位于固定板的右侧固定连接有支杆，所述底板的上表面且位于支杆的右侧固定连接有第一电机。本实用新型，通过设计转动板、第一绳索与第二伸缩杆，实现在转移硅钢片时，将其竖直排列，增加其抗弯能力，通过设计第一伸缩杆与限位块，实现其在移动的过程中避免相互摩擦，达到保护硅钢片的目的，通过设计滑动板、第二伸缩杆、支撑板，实现在上下转运的过程中，仅有上侧进行接触，且呈三角形更加稳定。

对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ... 

本发明涉及一种含磷无铝高效无取向硅钢生产方法，生产方法取消常化工艺，具体步骤如下：1)将钢水冶炼至目标成分后，浇铸成坯；2)板坯热装，热装温度≥500℃，热轧板坯加热炉均热段板坯温度1150～1200℃；终轧温度控制在860～930℃，卷取温度700～800℃3)酸洗后冷轧，控制冷轧整体压下率80％以内，至成品厚度；4)连续退火炉快速加热段温度设定1050～1180℃，增加有利织构组织形核，均热段温度设定830～950℃，全氮气干气氛保护，退火工艺速度120～150m/min，满足晶粒度8～4级。本发明不需进行热轧卷常化处理，降低了制造成本。