本发明揭示了一种无取向硅钢及其生产方法。该无取向硅钢的化学成分:Si:2.95%~3.15%,Al:0.75%~0.95%,Si+2Al:4.6%~4.9%,Mn:0.5%~0.7%,Sn:0.03%~0.04%,Cu≤0.03%,Cr≤0.03%,Ni≤0.03%,Nb≤0.004%,V≤0.004%,Ti≤0.004%,C≤0.0025%,P≤0.015%,S≤0.0015%,N≤0.004%,余量铁;Mn/S≥380,Al/N≥200;无取向硅钢的再结晶晶粒尺寸50~80μm。本发明在保证磁性能的同时,提高了强度,解决了现有技术所存在的磁性能和强度的兼顾问题。
2021-10-26 55 6.8

日本住友金属成功地开发了一种资源节约型高强度无取向电工钢SXRC,这种电工钢是通过固溶铌适度抑制位错的合并对消而得到一种特殊的微观组织,因此兼具很高的力学性能和磁性,特别适用于HEV、EV驱动电机转子。而且,不使用昂贵的镍就可以达到期望的强度,合金成本可控,是一种优越的资源节约型产品。 Sumitomo metal industries ltd of Japan successfully developed a type of high strength non-orientation electrical steel SXRC of resources-saving.The steel has both high mechanical performance and good magnetic property thanks to the special microstructure produced by the formation of Nb solid solution serving to appropriately inhibit the combination and cancellation of dislocations.The material is,in particular,suitable for manufacturing rotors of HEV and EV driving motors.Besides,expected streng... 
2011-06-28 51 5.8

本实用新型涉及一种便捷型铁芯硅钢片组装系统。该便捷型铁芯硅钢片组装系统包括硅钢片叠放装置,硅钢片叠放装置包括固定座,固定座上通过轴承转动装配有齿圈,固定座上固定连接有与齿圈同轴的固定盘,固定盘的中心设有中心孔,固定盘上设有六个沿固定盘径向延伸的滑槽,六个滑槽沿固定盘周向均匀分布,每个滑槽内分别滑动装配有滑块,齿圈的上侧面设有上螺纹,滑槽的下侧面设有与上螺纹相匹配的下螺纹,滑块的内端设有定位板,定位板的外侧面上设有用于与硅钢片中心孔孔壁上的割槽相匹配的定位条。相比于现有技术,本实用新型能够对硅钢片进行定位,从而确保各片硅钢片的中心孔以及割槽相对应,提高了硅钢片叠放效率,从而提高了生产效率。
2021-05-26 37 6.8

利用场发射电镜及能谱仪研究了取向电工钢薄、厚板坯铸锭中不同区域的析出相差异,确定了MnS、AlN及Fe3C的析出顺序和形貌特征。结果表明AlN以先析出的MnS为形核核心,形成粗大微米级的复合析出相。针状Fe3C既可以在复合析出相表面形成也可以在基体中单独出现,主要受冷却速度的影响。在1250℃保温1~2 h,AlN、Fe3C均可完全回溶,但部分MnS仍不回溶。MnS尺寸随着保温时间延长而增大。导致热轧板中沿轧向分布的粗大MnS,减弱了粒子钉扎力。 Precipitates in thin and thick slabs of electrical silicon steel were investigated by means of field emission SEM and EDS analysis.The precipitation sequence and the morphology of MnS,AlN and Fe3C particles were identified.AlN particles are observed to be nucleated on surface of MnS forming micron-meter-sized complex particles.Acicular Fe3C can precipitate on surface of the complex MnS/AlN particles or directly from matrix depending on cooling rate of the slabs.After holding at 1250 ℃ for 1-2 h,... 
2011-08-28 44 5.8

本实用新型公开了一种硅钢卷上料装置,包括两支撑台和设置在两支撑台之间的输送组件,所述输送组件包括轨道和设置在轨道上的输送件,所述输送件包括滑板、支撑板、承重板和气缸,所述轨道平行于两支撑台设置在两支撑台之间,所述滑板可滑动设置在轨道上,所述支撑板通过气缸可升降设置在滑板上,所述承重板设置在支撑板上,所述承重板的截面呈U型,其上设置有第二缓冲条。其可实现硅钢卷的轻松上料,省时省力的同时,安全性大大提高。
2021-12-20 69 6.8

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 
2013-02-28 56 5.8

本发明涉及电机生产技术领域,特别涉及一种电机定子硅钢片叠片工装平台,包括底板、放置板、整齐装置和清理装置,所述的底板上端通过支撑柱安装有放置板,放置板上端安装有整齐装置,放置板上设置有清理装置;本发明可以解决现有的工装平台在针对多个硅钢片进行叠片时,只能对一种尺寸的硅钢片进行叠片,不能根据硅钢片的直径和硅钢片上间隔孔的宽度进行相应的调节,因此不能实现对不同尺寸的硅钢片进行整齐的功能,降低了工装平台使用的灵活性问题。本发明所采用的整齐装置在一定范围内可以根据硅钢片的直径进行相应的调节,从而实现对不同尺寸的硅钢片进行整齐的功能,提高了工装平台使用的灵活性。
2021-08-23 51 6.8

本发明涉及硅钢带的制备技术领域,具体公开一种软磁性高硅钢极薄带及其制备方法。所述软磁性高硅钢极薄带的制备方法包括熔炼、包覆CaF2和TiB2偶合涂层、微波热压成型、酸洗、渗氮、一次退火、三道热轧、二次退火、三次温轧和三次退火。本发明提供的软磁性高硅钢极薄带的制备方法制得的软磁性高硅钢极薄带的晶粒细化程度高、组织均匀,改变了传统的相析出路径,有效消除了有序相的形成,使其具有优异的延展性,并具备更高的磁感和更低的铁损。
2021-12-31 117 6.8

【作者】 陈迪安; 李春生; ...
2023-05-09 90 5.8

本发明公开了一种高热导率耐腐蚀电工钢自粘结涂料及制备方法,本发明的自粘结涂料包括以下质量百分比的组分:双酚A型环氧树脂25%~35%、酚醛环氧树脂4%~8%、异辛基磷酸酯0.2%~0.5%、丙二醇甲醚5%~10%、乳化剂5%~8%、二甲氨基乙氧基三恶硼杂八环1%~3%、铵封闭路易斯酸盐0.5%~2%、氮化硼纤维3%~12%、氧化铝纤维0.4%~1.0%、研磨助剂0.2%~0.3%、余量为纯水。该自粘结涂料一次固化后形成的活化态自粘结涂层显著提高对电工钢基材的耐腐蚀性,该自粘结涂层具有良好的热导率,一次固化与二次热压固化工艺条件操作难度显著降低。本发明的自粘结涂料制备方法操作简单,实施可行性高。
2021-04-29 67 6.8

本实用新型公开了一种变压器硅钢片剪切收料装置,其包括底板和存放架推出机构,底板的前侧中部设置有用于放置外设剪切设备的放置区;存放架推出机构包括滑动板座、锁紧组件,滑动板座可左右滑动地安装于底板的上表面,在滑动板的上表面设置有两个用于放置外设的硅钢片存放架的存放架放置槽,两个存放架放置槽呈左右间隔设置,锁紧组件用于锁紧滑动板座与底板之间的相对位置。当该硅钢片存放架存放完后,将滑动板座推动至使得另外一个存放架放置槽设置于放置区的正后方,另外的硅钢片存放架继续接受剪切设备掉落的硅钢片体,可连续地实现硅钢片体的落料存放,令转运和落料的操作不相互干涉,提高生产的效率。
2021-04-26 33 6.8

本实用新型公开了一种硅钢片切割装置,包括底座和硅钢片本体,所述底座的上表面分别设置有驱动机构和切割框,驱动机构的表面设置有激光切割机构,切割框的内底壁开设有条形槽,条形槽的内壁转动连接有丝杠,丝杠的表面螺纹连接有滑动块,滑动块的上表面固定安装有定位框,定位框的内壁设置有电动推杆,电动推杆的推送端设置有定位板。该硅钢片切割装置,在对硅钢片进行切割时,能够通过小型电机的转动使定位框从切割框内移出,从而便于操作人员对硅钢片本体的放置,放置完成后,小型电机反转,使定位框带动硅钢片本体进入切割框内并与在转动辊的作用下滑动进入定位槽内,从而实现对硅钢片本体的有效定位,提高了切割的精确性。
2021-10-15 48 6.8