硅钢资料

对低温加热工艺生产的以AlN为主抑制剂的高磁感取向硅钢高温退火过程进行中断实验,借助电子背散射衍射技术对高温退火过程中高斯晶粒的演变进行了研究.在升温过程中高斯晶粒平均尺寸先减小再增大.800℃时取向分布函数图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;900℃时高斯晶粒平均生长速率超过其他晶粒;950~1000℃时高斯晶粒异常长大,偏离角3°~6°;在1000℃之前高斯取向晶粒相比于其他晶粒没有尺寸优势. The high-temperature annealing process of high permeability grain-oriented silicon steel with AlN as an inhibitor was studied by interrupting test.The evolution of Goss texture in this process was analyzed by electron back-scattered diffraction.It is found that the Goss grain size first decreases and then increases with the rise of temperature.Goss texture appears in the orientation distribution function at 800 ℃,but the intensity is very weak and the deviation angle is more than 10°.The average... 

一种不含铬取向电磁钢板用涂料、其制备方法及带涂层的不含铬取向电磁钢板的制备方法，属于取向电磁钢板技术领域。所述涂料按质量份配比组成如下：100份磷酸盐、60～120份二氧化硅溶胶、5～50份氧化锡溶胶、2～40份硼酸和0.5～10份二氧化硅粉体。本发明所述制备方法环境友好、能够满足规模化生产要求，制备的涂料不含铬、具有良好的稳定性和涂敷性，并且本发明所述涂料能够使取向电磁钢板表面涂层具有良好的耐吸湿性、耐腐蚀性、耐热性、张力效果和抗粘片性。

【作者】 王桦； 舒子龙； ...

以水氯镁石为原料,采用氨法沉镁-煅烧-添加剂的方法制备硅钢级氧化镁。考察了反应温度、反应pH值、陈化时间对中间体氢氧化镁纯度及转化率的影响;研究了煅烧温度和煅烧时间对氧化镁水化率的影响及添加剂的量对氧化镁悬浮性能的影响。控制实验条件为:反应温度55℃,pH值为9.5,陈化时间2h,煅烧温度1050℃,煅烧时间2h,添加剂量为0.8%,制得氧化镁的纯度为98.99%、水化率为2.92%、悬浮性能为3mm/h,达到硅钢级氧化镁的要求。 Using bischofite as raw material,the preparation of magnesium oxide with silico-steel grade was studied.The effects of reaction temperature,reaction pH value and aging time on the intermediate magnesium hydroxide purity and conversion rate were studied.Calcinations temperature,calcinations time relationship to the hydration rate of MgO and amount of additive to the suspension performance of MgO were investigated.The results indicated that the optimum technological conditions were as follows:reac... 

本发明公开了一种低磁场条件下高磁感应强度无取向电工钢及生产方法，步骤包括：冶炼：炼钢、连铸生产铸坯，所述铸坯中：以质量百分比计，Si2.0％、Mn0.2‑0.5％、ALs0.3‑0.6％、N≤0.002％、S≤0.002％、Ca≤0.001％，余量为Fe及不可避免的杂质；板坯热轧、卷取；常化处理；退火处理。本发明通过合理的电工钢成分设定、生产工艺、稳定的控制精度，从一贯制角度对产品进行设计及控制，最终能够保证产品质量稳定、具有低磁场条件下高磁感应强度的Si含量2％的0.35mm厚度无取向电工钢产品。

本发明属于涂料技术领域，具体公开了一种用于取向硅钢的无铬无机绝缘涂料，包括以下重量份配比的原料：小颗粒硅溶胶10‑50份、大颗粒硅溶胶10‑50份、磷酸二氢铝溶液5‑50份、助剂0.1‑10份及水10‑100份。本发明还提供了一种用于取向硅钢的无铬无机绝缘涂料的制备方法，通过将小颗粒硅溶胶和大颗粒硅溶胶混合均匀成硅溶胶混合液后加水得到混合硅溶胶水溶液；再依次向其中加入磷酸二氢铝和助剂并持续拌至均匀，得到用于取向硅钢的无铬无机绝缘涂料。本发明提供的无铬无机绝缘涂料适用于取向硅钢，使取向硅钢环保无害的同时具有与含铬取向硅钢相当的耐腐蚀时效，从而实现取向硅钢产业绿色化并大大改善取向硅钢的综合性能。

针对新能源汽车的发展，制备了含Ni固溶强化、含Cu析出强化以及含Ni+Cu复合强化3%Si无取向硅钢，研究了强化方式对无取向硅钢组织、织构和性能的影响。结果表明：固溶强化型无取向硅钢热轧板中形成了粗大{221}<221>晶粒，冷轧过程中剪切变形明显并在退火后形成良好再结晶织构。析出强化型无取向硅钢热轧板中心层形成γ取向粗大晶粒，在后续的加工中γ织构逐渐增强并最终得到相对细小的再结晶晶粒。复合强化型无取向硅钢热轧板中保留了强λ取向带状组织，退火后形成了有益的Goss织构和λ织构。固溶强化型与复合强化型无取向硅钢磁感应强度B₅₀分别达到1.742、1.688 T,高于析出强化型无取向硅钢的1.645 T。同时，复合强化型无取向硅钢高频铁损最低，其P_1.0/400和P_{1.0/1 000}分别低至20.97、82.69 W/kg,这与其较小的晶粒尺寸和织构改善有关。强度计算结果表明：Ni元素固溶强化对强度的提高有限，屈服强度为468 MPa,纳米Cu析出可显著提高屈服强度（强度增量约200 MPa）,且主要来自于模量强... For the development of new energy vehicles, 3%Si non-oriented silicon steel were processed by solid solution strengthening with Ni, precipitation strengthening with Cu, and composite strengthening with Ni and Cu. The effects of different strengthening methods on the microstructure, texture and properties of high-strength non oriented silicon steel were studied.The results show that coarse {221}<221> grains are formed in the hot rolled sheet of solution strengthened non-oriented silicon ste... 

本发明提供的一种耐热型低损耗取向硅钢，取向硅钢的单面采用激光刻痕形成平行线状沟槽；所述激光刻痕为取向硅钢制备工艺中的渗氮步骤之后和在涂覆MgO涂层步骤之前实施；在渗氮步骤之后和在涂覆MgO涂层步骤之前进行激光刻痕加工不会破坏高温退火后形成的硅酸镁底层，底层完整性好，刻痕形成的沟槽位于取向硅钢带材金属基体表面，在高温退火过程中沟槽内直接反应生成硅酸镁底层，最终取向硅钢带材表面涂覆张应力涂层后光滑、平整、无凹凸，取向硅钢带材损耗低、叠片系数高、耐热，成品取向硅钢带材既可用于制备立体卷铁心变压器也可用于制备叠片铁心变压器。

本实用新型公开了一种硅钢板带加工用表面成型设备，包括底座，所述底座的上端固定连接有底部支撑架，所述底部支撑架的上端固定连接有机体，所述机体的上端固定连接有密封盖。本实用新型在打磨过程中，水泵可以将过滤箱内的冷却液通过进液机构上的进液管泵入到进液机构内，再经过进液孔进入到第二转轴内，再进入到打磨辊筒内，最后经过喷头喷到钢带表面，对钢带表面进行冷却，且可以将打磨下来的粉末带走，防止粉末飘散；冷却在喷出后，经过集液斗的收集，进入到过滤箱内，在过滤箱内设置过滤网可以对冷却液进行过滤，从而可以对冷却液进行重复使用。

本发明公开了一种电机制造硅钢片酸洗处理设备及其酸洗处理方法，该电机制造硅钢片酸洗处理设备包括开卷机、一号安装台、二号安装台、一号限位机构、二号限位机构、打磨装置、酸洗装置、干燥装置和切分装置。此外本发明还提一种电机制造硅钢片酸洗处理设备的使用方法,包括以下步骤：S1、硅钢卷安装开卷；S2、表面打磨；S3、硅钢酸洗；S4、表面干燥；S5、硅钢切分。本发明能够在硅钢片在酸洗前对其表面进行打磨处理，有效去除硅钢片表面较为明显的锈迹或者粘附有杂物，使得酸溶液能够与硅钢片表面充分接触反应，而且在硅钢片酸洗后能够及时干燥，有效防止酸溶液继续与硅钢片过度反应，达到提高产品质量的目的。

本发明涉及金属冶炼工艺，尤其是一种降低无取向硅钢W800冶炼成本的方法，开吹阶段，着火后，加入头批渣料，石灰加入量占石灰总加入量的70%，石灰石加入量占石灰石总加入总量的100%，轻烧白云石加入量占轻烧白云石总加入总量的100%，待化渣后，枪位降低；化渣后将剩余30%石灰加入，加入剩余石灰过程中利用矿石调整温度；吹炼后期，并逐步压枪，终点拉碳枪位至1.4m，并使枪位在此高度不少于30s；到达冶炼终点。本工艺通过降低转炉渣量、提碳降氧和提高终点温度来减少铁水锰氧化量和促进氧化锰还原量，进而降低RH金属锰加入量，降低生产成本。

针对陶瓷辊表面结瘤清除时间长、清除效果差等缺陷,研究正反转陶瓷辊除瘤法,以缩短除瘤时间,增强除瘤效果。 The general removal of ceramic roller surface tumor costs a long time and the effect is poor.This paper probed into the ceramic roller tumor removal in order to shorten time and enhance the effect of eliminating.