采用经验设计法初步确定了取向硅钢铸坯感应加热线圈设计参数,应用Ansoft仿真软件分别对36组不同线圈高度、线圈内径的感应加热炉在不同频率下的三维整体磁场和铸坯的温度场进行了数值仿真。通过对比仿真结果,确定电磁场分布最佳的一组感应加热炉设计参数为线圈高度h=1.50 m、线圈内径D1=0.575 m、电流频率f=110 Hz。在该参数下应用Ansoft仿真软件对取向硅钢铸坯感应加热炉的温度场进行了仿真,结果发现温度场分布均匀,可满足取向硅钢铸坯加热要求。 The induction heating coil design parameters for the oriented silicon steel casting blank were determined preliminary by experience design method,and 36 groups three-dimensional electromagnetic field with different height and inside diameter of coil under different frequencies of the induction heating furnace and the temperature field of the casting blank were investigated by numerical simulation using Ansoft simulation software. By comparing the simulation results of electromagnetic field distr... 

介绍了国内、外电工钢极薄带的生产现状及市场应用的情况,以及典型生产企业的生产规模、产品性能和应用领域,指出扩大高牌号无取向电工钢生产、提高产品质量是目前电工钢发展的迫切要求。 The production situation and market application of ultra thin electrical steel strip at home and abroad were described.The production capability,product property and application area of typical corporation were introduced.The results indicate that the urgency needed of electrical steel development is expanding high-grade non-oriented electrical steel production and improving products quality at present. 

本实用新型公开了一种变压器硅钢片卷吊装件，包括横梁和两个吊钩组件，在横梁两端之间的中部设置有吊挂连接构件；两个吊钩组件呈左右对称设置于横梁，吊钩组件与横梁滑动连接，在吊钩组件与横梁之间设置有第一锁紧机构，横梁通过吊挂连接构件与吊机上的吊索连接，在对不同宽度的硅钢片卷进行吊装时，松开两个第一锁紧机构，调节好其中一个吊钩组件的位置，并锁紧固定好，使得固定好的吊钩组件插入硅钢片卷其中一端内，最后将另外一个吊钩组件插入硅钢片卷另一端内，并锁紧固定，本实用新型通过两个吊钩组件来勾住硅钢片卷的两端，可避免硅钢片卷在起吊过程中损坏卷边，也可满足不同宽度的硅钢片卷的吊装。

{100}织构因具有两个易磁化方向能够明显的提高磁性能,因此如何在表面获得具有{100}织构一直是无取向电工钢研究焦点。本文主要介绍了获得{100}织构的主要工艺方法及其基本原理,并结合实际生产过程对各工艺方法的优缺点进行了分析;一方面,优化无取向电工钢的成分,降低碳、锰元素含量以避免脱碳退火和真空退火,简化生产工艺;另一方面,调节升温速度、降温速度和退火气氛,使{100}晶面的表面能或弹性应变能最低,制备具有{100}织构柱状晶组织的无取向电工钢是今后的发展方向。 Because { 100} texture has two easy magnetization directions,which can significantly improve magnetization properfies,how to develop { 100} texture is a focus for researchers and manufactures. In the paper,main manufacturing processes and basic principle are introdued,and their advantages and disadvantages in practical production are analyzed. On the one hand,the production process can be simplified by optimizing chemical compositions,such as reducing the content of C and Mn,which can avoid deca... 

应用CAFE法对6.5%Si高硅钢铸锭凝固组织进行了模拟研究,确定出了适合高硅钢组织模拟的模型。进一步用该模型研究了过热度及冷却条件对凝固组织的影响,结果表明,随着过热度的降低,凝固组织中柱状晶比例和晶粒平均面积均减小。水冷条件下,高硅钢铸锭凝固组织几乎全是柱状晶,而且晶粒粗大。空冷条件下,等轴晶区扩大,但柱状晶仍占主要部分。缓冷条件下,等轴晶区占主要部分,晶粒平均面积和空冷条件下相当。 The solidification structure of 6. 5% Si steel ingot was simulated based on CAFE method and the model suitable for simulating the structure of high silicon steel wad ascertained. The influence of superheat and cooling condition on the solidification structure were studied. It was shown that with the superheat decreasing,the proportion of columnar crystals decrease,and the average grain size become smaller. Under water cooling condition,the solidification structure of casting was composed of almo... 

研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient... 

电工钢反复弯曲次数是电工钢性能检验的重要指标之一,直接影响到用户在使用电工钢过程的机加工性能。主要分析了试样宽度、试样张力、晶粒取向、反复弯曲设备等因素对电工钢反复弯曲试验的影响,并对各个因素的影响程度进行量化以及原因探讨,从而归纳形成各影响因素的基本规律,以便为电工钢实际生产、用户使用提供科学指导。结果表明:试样宽度增加,反复弯曲次数也会不断增加,晶粒位向对取向电工钢的反复弯曲次数影响较大,当支座顶部到拨杆底部的距离减小或拉紧力增加时,反复弯曲次数会不断减小,但当拉紧力达到60N以上时,对反复弯曲次数影响不大,试样经退火后,反复弯曲次数略有上升。 The reverse bend number is an important performance of electrical steels′capabilities,affecting the machining performance directly when the customers used.It investigated some factors,such as sample′s width,sample′s tension load,grain orientation and equipment,how to effect the reverse bend test for electrical steel,measured the influence degree,and discussed the reason,in order to form basic rules which could be guided the manufacturing and using for electrical steel.Results showed that the rev... 

本发明涉及无取向硅钢技术领域，具体提供了一种无取向硅钢的制备方法，对再结晶率为70‑90％、平均晶粒尺寸为10‑15μm、硬度HV为140‑170的硅钢半成品在温度为T＝(772～777)+2900×W(Si)的条件下进行去应力退火，制得无取向硅钢，晶粒在去应力退火过程中均匀长大，平均晶粒尺寸80μm以上，有效降低铁损，使磁性能大幅度提高，铁损P1.5/50≤3.5W/kg，磁感B5000≥1.72T，电磁性能优异，满足客户使用要求，此外，本发明采用的硬度HV为140‑170的硅钢半成品在冲压过程中不易变形，机械加工性能优良。

本实用新型提供了一种便于清洗的冷轧硅钢生产用轧机，两个所述支架安装在底座上，所述支架上设有安装盖，支架之间设有上支撑辊，上支撑辊下设有上工作辊，上工作辊安装在支架之间，上工作辊下设有下工作辊，这种便于清洗的冷轧硅钢生产用轧机，在使用的时候，可以对于冷轧硅钢进行生产处理，生产之后可以进行清洗设备，安装的上工作辊与下工作辊可以对于硅钢进行冷轧处理，在工作时，两侧安装的承重块可以对于机械进行一个固定，起到稳固作用，两侧安装的转动辊可以放置硅钢，安装的清洗头可以对于机械进行清洗，吹风器可以对于机械进行干燥处理，防止机械生锈，底座上安装的沥水板可以隔断灰尘和铁屑，防止堵塞。

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and... 

本实用新型公开了一种硅钢片生产用冲压机构，包括安装底板，所述安装底板的侧壁设置有固定件，安装底板的上表面设置有工位调节机构，工位调节机构包括固定连接在安装底板上表面的四个安装块，每两个安装块为一组，两组安装块的相对面均转动连接有往复丝杠，正面两个安装块的正面均固定连接有驱动往复丝杠转动的伺服电机，往复丝杠的表面螺纹连接有工位安装板。该硅钢片生产用冲压机构，在冲压加工过程中，通过伺服电机带动往复丝杠转动，能够带动两个工位安装板移动，从而使冲压母模沿往复丝杠进行移动，在加工过程中，通过对两个冲压母模进行交换，能够节省硅钢片上料与下料的时间，从而提高冲压加工的效率，且能够提高生产的安全性。

本实用新型公开了一种取向硅钢绝缘涂液用深度过滤装置，涉及深度过滤装置技术领域，为解决现有深度过滤装置在工作过滤时，一般都是依靠液体本身流动的力量穿过滤网，但液体流速较慢，工作效率不高的问题。所述过滤装置主体的下端安装有出水管，所述过滤装置主体外表面的一侧安装有进水管，所述进水管与出水管的一端均安装有安装底座，且安装底座设置有两个，所述安装底座的一侧安装有六角固定螺母，且六角固定螺母设置有十二个，所述安装底座的另一侧安装有密封橡胶垫圈，且密封橡胶垫圈设置有两个，所述进水管的内部设置有进水口。