脉冲磁场退火对取向硅钢磁性能的影响

【作者】
李莉娟;
刘立华;
夏强强;
翟启杰;

【Author】
LI Li-juan,LIU Li-hua,XIA Qiang-qiang,ZHAI Qi-jie(Shanghai Key Laboratory of Modern Metallurgy & Materials Processing,Shanghai University,Shanghai 200072,China)

【机构】
上海大学上海市现代冶金与材料制备重点实验室;

【摘要】 通过对取向硅钢进行脉冲磁场退火实验,发现在相同的退火时间(6.0 min)内,低于1 T的脉冲磁场可以在一定程度上提高取向硅钢的磁感(B8),而高于1 T的脉冲磁场则会使取向硅钢的磁性能急剧恶化.同时发现,脉冲直流电加热方式会使取向硅钢的磁性能恶化.研究表明,脉冲磁场退火有望成为一种调控材料微观结构的有效手段. 

【Abstract】 We have carried out experiments of annealing by pulse magnetic field.The results show that a pulse magnetic field with intensity lower than 1 T can promote magnetic induction density(B8) of grain-oriented silicon steel,while the magnetic properties deteriorate sharply when intensity is higher than 1 T.It has also been found that heating by using pulse direct current can cause the magnetic properties to deteriorate,in contrast to the traditional heating using resistance furnace.Our research shows… 

【关键词】 取向硅钢;
脉冲磁场;
退火;
磁性能;

【Key words】 grain-oriented silicon steel;
pulse magnetic field;
annealing;
magnetic property;
【基金】 国家自然科学基金资助项目(50804028)

原文发表于《上海大学学报(自然科学版)》2011年第01期

论文PDF全文下载

此内容查看价格为5.8立即购买(VIP免费)
不用注册会员、不用登陆账号,直接支付购买查看,客服QQ:1093451816,此外成为本站VIP可免费查看本内容。
原文链接:http://1guigang.com/down/thesis/44393.html,转载请注明出处~~~
0
广告位招租

站点公告

网站试运行,请大家关注本站公众号,多提宝贵意见!

显示验证码
没有账号?注册  忘记密码?