运用电子背散射衍射(EBSD)和X射线衍射(XRD)技术对硅钢热轧板的织构在板厚方向的分布进行了研究,并分析了两种织构测量方法的特点。EBSD技术能直观给出板厚方向的微观织构,XRD能得到钢板的宏观统计织构信息,结合两种技术的分析,能更直观更精确的研究不同织构在板厚方向的分布。 The texture distribution along the thickness of the silicon steel has been investigated by electron backscatter diffraction(EBSD) and X-ray diffraction(XRD) technique.The characteristics of two technique of texture analysis have been investigated.Combined the two techniques,the texture distribution along the thickness of the silicon steel could be realized distinctly and accurately. 

本实用新型属于冷轧硅钢技术领域的一种冷轧硅钢无压回水自动控制设备，包括底座，底座外表面的上端固定连接有工作台，工作台外表面上端的两侧分别固定连接有固定柱和压辊主体，工作台外表面上端的中部滑动连接有移动架，压辊主体的下端设置有集水槽，集水槽的内表面设置有浮球液位传感器。液压杆工作推动移动架位移到合适的位置，再通过气缸使伸缩管发生位移，使出水口接近钢板，设置的水箱高于出水口所以水可以在重力的作用下流淌，流出的水流到集水槽内，水流在集水槽内聚集，水流使浮球液位传感器的浮球上升，上升到合适的位置时，浮球液位传感器通过电缆发生电信号至控制器，此设置可以实现设备的自动控制，省去人工进行操作。

本发明一种铝镇静含硅钢的脱氧方法，包括转炉冶炼、LF炉精炼工序，转炉工序：转炉出钢过程采用含硅脱氧剂进行脱氧，出钢完毕后，向钢液表面加入顶渣改质剂，数量为400±25kg/炉，所述顶渣改质剂的成分及其质量百分含量为：Al2O3：9％±1％，CaO：27.5％±1.5％，SiO2：3％±1％，Al：50％±2％，CaF2：7％±1％。精炼工序：采用铝脱氧剂进行脱氧、造渣。本发明通过两步脱氧工艺，大幅降低脱氧成本同时提高钢水质量，由于硅脱氧相对于铝脱氧在钢水中形成的夹杂物更容易上浮，所以也提高了钢水纯净度，提高钢水质量。

【作者】 陶永根； ...

本发明涉及一种无取向电工钢片绝缘涂液，它的主要有效成分包括有机树脂、水溶性磷酸二氢盐、硅溶胶、涂料助剂、和特定水溶性金属盐。上述各组分的质量组成比例为：有机树脂100份，水溶性磷酸二氢盐100‑250份，硅溶胶0‑100份、涂料助剂0‑20份，特定水溶性金属盐10‑50份，其余为水，涂液的固含量为15～40％。其中特定水溶性金属盐是指水溶性磷酸二氢盐以外的二价或多价金属盐，这种盐可以在磷酸二氢盐溶液中稳定存在，但是在电工钢涂层烧结温区会氧化或分解。本发明的绝缘涂液固化速度快且固化彻底，涂层具有优异的耐盐雾性能。

针对传统工艺生产硅钢周期长、能耗大等缺点,采用双辊连铸工艺制备3%Si无取向硅钢连铸薄带,利用MEM,SEM和TEM观察了铸带的组织、织构及析出物,同时对比了Al的质量分数为0.6%和0.9%的连铸薄带在组织、织构及析出物特征方面的异同.结果表明:双辊连铸工艺生产的3%Si无取向硅钢铸带的组织为均匀等轴晶粒,平均晶粒尺寸约为300μm;织构组成随Al质量分数的不同具有明显差别,Al质量分数为0.9%的铸带中{100}织构强度是随机织构的7倍;铸带中的析出物为AlN和MnS,最大尺寸分别为500和50 nm左右. Given the lengthy production cycle,high energy consumption,and other shortcomings of the traditional process for producing silicon steel,a twin-roll casting process was used to produce 3%Si non-oriented silicon steel casting strips. MEM,SEM,and TEM were used to compare micro-structure,texture,and precipitate characteristics of a casting strip containing 0.6%Al with another containing 0.9%Al.The structure of 3%Si non-oriented silicon steel produced by the twin-roll casting process was a uniform i... 

本发明公开了一种高强度碳化硅钢球，所述高强度碳化硅钢球包括以下重量份的原料：碳化硅20‑30份、铬1‑2份、氮化硼3‑5份、铁10‑20份、钼2‑3份、锰钢30‑40份、镍5‑8份、钛6‑8份、磷2‑3份、硫2‑3份；一种高强度碳化硅钢球制备方法，包括如下步骤S1、熔融；S2、模锻成球；S3、打磨；S4、二次加热；S5、高温淬火；S6、机油回火；S7、检测成品。本发明制备的高强度碳化硅钢球具有抗折强度高、洛氏硬度高及抗压强度高等优异的机械性能，并且使用寿命长，运转精确度高，并且其工艺简单，生产耗能低，无“三废”产生，环保性高。

运用电子背散射衍射(EBSD)技术,研究了50W600无取向硅钢在热轧→冷轧→退火工序间织构的演变。结果表明:由于热轧板沿板厚方向的应力场和温度场存在差异,导致热轧板不同层织构类型和强度存在差异;热轧板表层主要存在铜型、黄铜和高斯织构,1/4层织构主要为α纤维织构和较弱的高斯织构,中心层织构较单一,主要为α纤维织构;和热轧板相比,冷轧板各层织构差异较小,为典型的轧制织构(α纤维织构和γ纤维织构);退火板各层都表现为γ纤维织构增强、α纤维织构减弱,旋转立方织构基本消失。 The texture evolution of 50W600non-oriented silicon steel in hot rolling,cold rolling and annealing process was investigated by electron back-scatter diffraction(EBSD)technology.Results show that the hot rolled plate texture types and intensities along thickness direction were different because of the different stress fields and temperature fields.The major texture types in the surface of hot rolled plate were copper,brass and Gauss texture.The texture was composed ofαfibre texture and weaker Ga... 

为了确定普通冷轧取向硅钢最优的中间完全脱碳退火工艺,在其一次冷轧后进行5种不同工艺的脱碳退火处理,借助扫描电镜及电子背散射衍射技术研究了不同工艺脱碳退火后的组织、织构和脱碳效果。结果表明:经5种工艺脱碳退火处理后,初次再结晶的平均晶粒尺寸均约为19μm,且不随退火温度和时间的变化而变化;经840℃×10min工艺退火后的晶粒最均匀,高斯织构位向更准确,高斯织构面积分数最多,为3.1%,可将碳脱至0.003 5%。 In order to determine the optimal intermediate complete decarburizing annealing processes for common grain-oriented(CGO)silicon steel,five kinds of intermediate decarburizing annealing processes were conducted,the microstructure,texture and decarbonization after different decarburizing annealing processes were studied by scanning electron microscopy and electro back-scattered diffraction(EBSD)technology.The results show that the average grains sizes of primary recrystallization were about 19μm a... 

采用RH精炼添加钙合金方式对硅钢进行钙处理。结果表明,钙合金添加量为0.67、1.00、1.67kg/t钢时,钢中钙含量分别为0、2×10-6、4×10-6;随着钙合金添加量增大,钢中夹杂物粒度逐渐由0～2μm向2～4、4～6μm偏移;不同钙处理条件下,钢中均存在粒径小于1μm和粒径为1～5μm的MnS、CuxS夹杂物,后者或单独存在,或同AlN、CaS夹杂复合;粒径为5～10μm区间,钢中的夹杂物基本以钙的氧、硫化物为主。与钙处理前相比,钙合金添加量为0.67、1.00、1.67kg/t钢时,粒径小于1.0μm的微细夹杂物减少幅度分别为68.06%、87.50%、94.94%。钙合金添加量为1.67kg/t钢时,可以去除钢中绝大部分的微细夹杂物。 Ca alloy was added into the liquid steel during RH refining,and the results show that Ca concentration in final Si steel sheets is insignificant,about 0,2×10-6 and 4×10-6 when the added amount of Ca is 0.67,1.00 and 1.67 kg/t steel,respectively.With the increase in the added Ca alloy amount,the inclusions in the steel gradually change from those of 0～2 μm to those of 2～4 and 4～6 μm.Under different Ca treatments,there exist MnS and CuxS inclusions whose size is below 1 μm as well as MnS and CuxS ... 

本发明涉及取向硅钢制造技术领域，公开了一种快速判断取向硅钢初次再结晶晶粒直径的方法，包括如下步骤：选取取向硅钢热轧来料，进行生产，对产出的钢板在同部位各取若干个拉伸试样，加工拉伸和分析，取得屈服强度，在拉伸试样部位两侧连续制取金相试样，计算对应拉伸试样的平均晶粒直径D，将性能数据和平均晶粒直径进行统计分析，建立屈服强度与晶粒直径的对应关系，实际生产时，在产出的钢板上取判断试样，取得判断试样的屈服强度，进而取得判断试样的晶粒直径。本发明快速判断取向硅钢初次再结晶晶粒直径的方法，通过机械性能检验，来间接指示初次晶粒的大小，检测速度快，评价更准确。

采用CVD法制备6.5%Si高硅钢,介绍了具体的制备工艺过程,研究了温度对渗硅速率和试样质量减轻的影响,同时分析了扩散时间对高硅钢中硅分布的影响。结果表明:在CVD反应过程中,反应温度高于1050℃将大大提高渗硅速率,但当温度大于1200℃后,渗硅速率趋于稳定;渗硅后,试样会减轻、减薄,随着温度升高,试样质量减轻的速率逐渐增大,在1200℃左右趋于稳定;扩散时间越长,硅分布越均匀,结合制备效率进行考虑,满足Δw表-中/b≤5的时间为适宜的扩散时间。 6.5%Si high silicon steel was manufactured by using CVD method and the process was introduced,the influence of temperature on the siliconizing rate and quality reducing rate,diffusion time on silicon distribution were investigated.Results as follows: the siliconizing rate will increase quickly when the temperature is higher than 1050 ℃,but the siliconizing rate will become steadily as the temperature up to 1200 ℃;The quality reducing rate will increase with the elevating of temperature and the r...