本实用新型涉及一种硅钢片纵剪边料收卷装置，包括：用于将收卷装置固定于地面的机架底座，机架底座一端设置固定支架，固定支架上安装电动定尺收料盘；在机架底座上设置电动可移动支架，电动可移动支架在机架底座的长方向上相对固定支架移动，电动可移动支架上安装电动可调收料盘；电动可移动支架、电动定尺收料盘、电动可调收料盘与PLC控制系统连接，PLC控制系统用于控制电动可移动支架的移动距离、以及控制电动定尺收料盘和电动可调收料盘的收料速度。将本实用新型的硅钢片纵剪边料收卷装置安装在硅钢片滚剪线切刀后面的输送平台的下部，卧式布局，不占用外部空间，和滚剪线无缝集成在一起，自动完成硅钢片纵剪边料的收卷工作。

本发明涉及含Cu无取向硅钢的生产方法，转炉炼钢，真空处理过后连铸成坯；铸坯化学成分：1.0≤Si/Cu≤3.0,3.0≤Si+Cu≤5.5％，S≤0.0015％，(Mn+Cu)/S≥3000，其他为Fe,Als,P以及不可避免的杂质元素；对铸坯进行粗轧；粗轧后的中间坯采用热卷机进行强制卷取，开卷后中间坯进入保温箱，控制保温箱内冷却速度≤5℃/s；进入保温箱的中间坯温度T1满足：1000‑(Si+Cu)×103≤T1≤1100‑(Si+Cu)×103；高压除鳞，精轧，层流冷却，卷取；连续酸洗；冷轧到目标厚度，成品退火，涂层；成品卷进行时效处理。成品卷具有较低的中高频铁损，高磁感和高屈服强度。

用还原分离-原子荧光光谱法分析了硅钢中的痕量汞.分析方法的不确定度主要来自测量重复性,样品溶液浓度,工作曲线变动性,标准溶液,移取、配制标准溶液,仪器变动性等.文章分别对上述构成合成不确定度大小的分量进行了计算讨论. Trace mercury in silicon steel and galvanized sheet was analyzed by adopting reduced separation-atomic fluorescence spectrometry.The uncertainty of the analysis method mainly comes from measurement repeatability,sample concentration,working curve volatility,standard solution,pipetting and preparation of standard solution,and instrument variability,etc.The essay conducted all calculations and discussions on the above components that determine uncertainty. 

针对攀枝花钢钒有限公司难以稳定生产w(S)≤0.006%高级别电工钢的问题,通过开发RH脱硫剂、钢包渣改性及工艺参数控制,形成了RH脱硫系统工艺技术。经工业试验表明,采用该工艺技术后,钢水脱硫率最高达到42%,成品w(S)控制在0.005%以下,全氧、氮含量也得到了较好的控制,且脱硫剂没有引起钢水增碳,满足高级别电工钢的生产要求。 In light of the difficulty of production of high level electrical steel w(S)≤0.006 % steadily in Panzhihua steel & vanadium Co.,Ltd.the process technology of RH desulfurization system has been formed by developing the RH desulfurizer,modifying the ladle slag and controlling the process parameters.Industrial experiments show that the desulfurization rate of hot metal rises to 42 % and the w(S) of the finished products is controlled in below 0.005 % and total oxygen and nitrogen contents are a... 

本发明公开了一种硅钢高温加热炉用铬基高氮合金垫块及其制备方法，所述合金垫块含有Cr、Mo、N、La、Ce和Fe，不含有钨；所述合金垫块在高温抗氧化性能和高温抗蠕变性能上，优于现有技术的铬铁合金；本发明可以优化替代现有的硅钢高温加热炉用铬铁合金垫块，满足硅钢在加热炉中的加热需求，大规模工厂化生产，拥有极高的使用价值和广阔的应用市场。

本实用新型提供一种对硅钢片横剪线片料进行穿针叠柱与输送的装置，包括输送装置、穿针定位装置、纵向移动平台和转运装置，所述的输送装置设在纵向移动平台上方，所述的穿针定位装置位于输送装置底部，穿针定位装置固定在纵向移动平台上，所述的转运装置布置在输送装置的输出侧；所述的转运装置通过对接机构与输送装置对接。本实用新型能够完成硅钢片的穿针叠柱，并将此硅钢片柱整体输送到指定工位。本实用新型采用输送装置和穿针定位装置的上下分层布置结构，首先完成了硅钢片的穿针定位，然后完成硅钢片柱的整体输送，整个工艺方法中不使用吊运设备，提高了生产效率。

本实用新型公开了一种硅钢片用叠压装置，包括机架，机架上设有工作平台，工作平台的顶面上沿轴向并排设有定位块和可远离或者靠近定位块的抵紧块，定位块的水平截面呈L状，且其与定位块之间形成叠压区，叠压区的上方水平设有可竖直移动的传动板，传动板上竖向滑动穿设有若干均匀分布的导杆，导杆的两端均伸出传动板，且顶端设有限位块，底端共同安装有水平设置的压板，导杆上套设有位于压板和传动板之间的弹簧，机架上还设有与传动板和抵紧块均相连的可编程控制器。本实用新型解决了如何能高效且保质地对硅钢片进行叠压的技术问题，具有工人劳动强度低、叠压效率高且叠压质量好等优点。

研究了薄板坯连铸连轧流程(TSCR)条件下热轧工艺对3.2%Si-0.7%Al无取向硅钢组织、织构演变及磁性能的影响规律。结果表明,提高均热温度和热轧温度有助于获得粗大的变形组织和强烈的{001}〈110〉织构,进而对后续的组织、织构演变进程及磁性能产生有利的遗传影响。与低温均热和低温热轧相比,高温均热和高温热轧得到的最终成品板的再结晶晶粒较粗大,λ纤维再结晶织构较强而γ纤维再结晶织构较弱,磁感应强度较高。 It was investigated that the effects of thin slab cast rolling(TSCR) hot rolling processes on microstructural,textural evolution and magnetic properties of 3.2%Si-0.7%Al non-oriented silicon steel.The results show that much larger hot rolling deformed microstructure and much stronger {001}〈110〉 texture could be obtained by increasing the soaking and hot rolling temperatures,which had good heritable effects on subsequent microstructural,textural evolution and magnetic properties.The final sheets ... 

对冷轧无取向硅钢在冶炼过程中各个工序的顶渣进行了检测,分析了顶渣变化原因,并得出结论:硅钢生产宜采用复吹转炉,以降低吹炼终点渣中TFe含量,进而减轻对精炼的压力;使用低S、低Al2O3含量中间包覆盖剂;RH脱氧及合金化顺序采用先加硅铁后加铝;首罐宜经LF提温并降低渣中TFe。 The top-surface slag used for the various production processes in smelting coldrolled non-oriented electrical steel is tested and based on tested results the cause of the top surface slag change is analyzed.So it is concluded that the combined blown converter is more suitable to be used for smelting electrical steel in order to reduce the content of TFe in slag at blow end point and then much better results can be achieved during the period of refining.Secondly the tundish flux contenting low co... 

本实用新型公开了一种硅钢片加工用进料结构，涉及到硅钢片加工技术领域，包括壳体，壳体的两侧均贯穿开设有通槽，通槽的内部活动贯穿设置有活动板，活动板位于壳体内部的一端贯穿开设有方槽，其中一个方槽的顶端内壁和另一个方槽的底端内壁均固定设置有多个呈等间距分布的锯齿。本实用新型通过将多个硅钢片均挂在两个架板上的挂槽内，因硅钢片重量，带动两个延伸杆向下移动，延伸杆带动活动块向下移动，活动块带动齿条向下移动，从而带动齿轮转动，齿轮转动的同时，能够通过多个锯齿带动两个活动板相互靠近，从而使两个夹板相互靠近并夹紧多个硅钢片，从而能够固定住硅钢片，防止硅钢片传输时滑动，造成磨损。

本实用新型属于硅钢片加工技术领域，具体涉及一种利于常化的硅钢缝合结构，包括上层硅钢片、下层硅钢片和连接带，下层硅钢片的一端位于上层硅钢片的下方并与上层硅钢片叠合，上层硅钢片和下层硅钢片的叠合处开有多个排成直线的桥型孔，连接带依次穿过各个桥型孔并同时卡合在上层硅钢片和下层硅钢片上。本方案中，在上层硅钢片和下层硅钢片的叠合处开设桥型孔，利用连接带穿过上层硅钢片和下层硅钢片叠合处的桥型孔，相当于利用连接带将上层硅钢片和下层硅钢片缝合在一起，这样设置能够较好将上层硅钢片和下层硅钢片连接成一体。

基于BOF→RH→CSP生产工艺,研究了RH精炼过程钢中夹杂物类型演变及MgO·Al2O3夹杂物形成规律,同时对MgO·Al2O3夹杂物的形成条件进行了热力学计算,借助CFD数值模拟软件研究了RH精炼过程卷渣行为。研究发现,RH精炼过程20和30 min时,w([MgO])/w([Al2O3])为0.005~0.020,未发现MgO·Al2O3夹杂物;RH出站后夹杂物w([MgO])/w([Al2O3])为0.3~0.5,且RH精炼结束后MgO·Al2O3夹杂物占夹杂物总量的58.4%;另外,RH精炼过程钢液表面速度CFD模拟结果为0.57 m/s,大于临界卷渣速度0.45 m/s,且顶渣成分与夹杂物成分相近,存在卷渣现象。热力学计算表明,钢液与炉渣平衡时钢中w([Al])为0.31%~0.37%,w([Mg])为0.00024%~0.00028%,在MgO·Al2O3生成区域之内。减少RH处理过程卷渣,浇铸过程下渣及控制顶渣和包衬相中MgO质量分数可抑制MgO·Al2O3夹杂物形成。 Based on the practical production of non-oriented silicon steel, the evolution of inclusion type and the formation of MgO·Al2O3inclusion were analyzed in the process of BOF→RH→CSP. The thermodynamic conditions for forming MgO·Al2O3inclusion were discussed and the behavior of slag entrapment of molten steel was also simulated by CFD software during RH refining. The results showed that the value of w([MgO])/w([Al2O3]) was in the range of 0.005-0.020 and no MgO · Al2O3 inclusion was observed at 20 ...