试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ... 

本实用新型公开了一种变压器铁芯用硅钢片卷放料装置，其包括底座、换位旋转机构，换位旋转机构包括设置于底座上端的旋转座、换位旋转驱动组件、至少两个以上的放卷工位，换位旋转驱动组件用于驱动旋转座相对于底座绕设置的换位旋转轴线旋转，至少两个以上放卷工位以换位旋转轴线为圆心呈环形间隔设置于旋转座，放卷工位包括有可转动安装于旋转座上的放卷筒。当其中一个放卷筒进行放卷送料时，另外的放卷筒进行上卷，当该放卷筒放卷完后，换位旋转驱动组件驱动旋转座转动，使得另外的装有硅钢片卷的放卷筒转动至放卷送料的位置，而该放卷筒就可进行上卷，如此循环操作，实现了放料装置对硅钢片卷的同步放卷放料和上卷，提高生产的效率。

试验了通过NaCl-KCl-NaF-SiO₂熔盐在电流密度50 mA/cm²、电沉积脉冲电流正反向比9:1和750⁸50℃60min电沉积下阴极（/mm）20×20×0.5的1.6Si无取向冷轧硅钢片断面层硅的分布,并通过计算得出Si的扩散系数。结果表明,电沉积温度由750℃提高至850℃时,试样中Si含量增加,扩散的深度由18μm提高到40μm;电沉积温度与Si在钢中的扩散系数近似符合Arrhenius指数关系。 The distribution of silicon at cross section of cathode（/mm） 20 × 20 × 0.5 sheet of 1.6Si non-oriented cold rolled silicon steel after electro-deposit treatment by NaCl-KCl-NaF-SiO₂ molten salt with current intensity 50 mA/cm²,electro-deposit pulse current positive-negative ratio 9:1 at 750 850 ℃ for 60 min has been tested and the diffusion coefficient of Si is obtained by calculation.Results show that with increasing electro-deposit temperature from 750 ℃ to 85... 

本实用新型公开了一种变压器铁芯硅钢片纵剪缓冲保护装置，包括支撑立架、前挡横杆、后挡横杆、松弛检测组件和拉伸检测组件，所述支撑立架上在料带传送方向上间距设置有前挡横杆、后挡横杆，所述前挡横杆与后挡横杆均承托设置在料带的下方，所述前挡横杆与后挡横杆之间构成缓冲腔，所述缓冲腔内对应于料带的下方、上方分别设置有松弛检测组件、拉伸检测组件，所述松弛检测组件检测料带在松弛状态下的最低位置，所述拉伸检测组件检测料带在张紧状态下的最高位置，能够及时地对料带的松弛和拉伸程度进行监测，保证料带的缓冲安全。

本实用新型公开了水性硅钢绝缘涂料制备用袋式过滤机，包括下壳体，所述下壳体顶部铰接有一对上壳体，一对所述上壳体均具有连接板，一对所述连接板通过若干个吊环连接，所述上壳体外侧壁面设有上固定座，所述下壳体后壁面设有出液管，所述下壳体内部设有弹出支撑板机构，所述上壳体内部设有上壳体清洁机构，所述下壳体内部设有下壳体清洁机构。本实用新型涉及袋式过滤器技术领域，本装置结构紧凑，通过一对第一气缸铰接于一对上壳体两侧，使上壳体实现向自动两侧打开的功能，取出支撑板时较为方便，上壳体内壁面的挤压销能够对支撑板进行挤压，当上壳体被打开时，支撑板失去挤压销的限位作用时就会从限位槽中弹出，给人们带来了方便。

本实用新型公开了一种取向电工钢的多项性能检测装置，涉及取向电工钢技术领域，为解决检测装置在对取向电工钢涂层性能检测时较为繁杂，增加了检测难度，检测的误差增加，且检测装置的性能检测较为单一，检测效果不佳的问题。所述底座的上方设置有安装架和吊梁架，所述安装架上设置有输料辊，输料辊设置有两个，两个所述输料辊之间设置有输送带，所述吊梁架的下方设置有弹性胶带，所述弹性胶带上方的两侧均设置有第三电动伸缩杆，且第三电动伸缩杆的两端分别与吊梁架和弹性胶带通过螺钉连接，所述弹性胶带的一侧设置有检测架，所述检测架上设置有激光灯、第一滤光片、接收器、第二滤光片和聚光片，所述激光灯和第一滤光片设置在弹性胶带的上方。

采用拉伸试验和显微组织观测的方法确定了GTN损伤模型中的9个损伤参数,运用GTN损伤模型对冷轧硅钢薄板边部缺陷的扩展及边裂的产生进行了有限元模拟,并与预置缺口的钢板轧制试验进行对比。结果表明:轧制过程中边部缺陷是造成钢板边部裂纹萌生和扩展的一个重要原因,GTN损伤模型可用来预测含边部缺陷硅钢薄板在冷轧过程中边裂的产生;预测结果与试验结果基本一致。 The crack initiation and propagation of silicon steel strip with edge defect during cold rolling process was studied by using GTN damage model in this paper.Nine damage parameters in GTN model were identified by tensile testing and microstructure observing,and then the FE simulation of edge defect evolution of silicon steel strip during rolling process was conducted on the base of GTN damage model,and then the results were compared with rolling experimental results.The results show that the edge... 

一种超低硫硅钢冶炼工艺方法，属于炼钢技术领域。本发明公开了一种超低硫硅钢冶炼工艺方法，主要步骤包括KR铁水预处理—转炉冶炼—RH真空精炼—连铸保护浇注。在冶炼超低硫硅钢前，铁水包、转炉先处理1‑2炉低硫钢种，清洗设备；KR脱硫采用三次扒渣法，第一次扒除高炉出铁带渣，将铁水S含量脱至目标值后进行第二次扒渣，然后开通铁水包底吹，软吹后进行第三次扒渣，脱S后铁水S≤0.0005％，铁水兑入转炉后，热态下清理铁包结渣；转炉使用硫含量小于35ppm的低硫废钢，且废钢比不超过15％；RH和连铸过程均使用低硫合金及原辅料。本发明可使连铸结晶器钢水中S含量小于15ppm达标率由原来的48.6％左右提高至95％以上。

本实用新型公开了一种具有导气槽的低空载损耗电工钢用罩式炉，包括：炉台，顶部设置有加热元件以及连通炉台外缘至中心凹陷的导气通道；炉板，压设于炉台上，设置有与中心凹陷上下对应的中心通孔；砂封槽，设置于炉台的外周，槽底低于导气通道；炉罩，罩设于炉台的顶部及外周形成炉腔，与砂封槽相压接；进气通道，穿设于炉台的中心凹陷中，具有开口向上的排气口；炉罩的炉台套接段内壁设置有导气槽，导气槽的延伸方向与炉罩的高度方向一致，导气槽将气流导向炉台外缘的导气通道进气口。该具有导气槽的低空载损耗电工钢用罩式炉的炉罩设置有导气槽，利用导气槽将硅钢卷外周下行的气流导入炉台的导气通道中，改善钢卷热处理过程中的流场和温度场。

本发明涉及一种取向硅钢热轧钢带的板形控制方法，所述取向硅钢热轧钢带的工艺流程包括铸坯加热过程、轧制过程及层流冷却过程；其中轧制过程中采取取向硅钢与普钢交叉轧制的方式；粗轧过程采取R1轧制1道次、R2轧制5道次的1+5轧制工艺，并控制轧制工艺参数；精轧过程中控制F1～F7轧制工艺参数。本发明通过设定合理的交叉轧制工艺及取向硅钢热轧工艺，使取向硅钢的轧制稳定性大幅提高，取向硅钢带形控制良好，凸度控制在30～50μm之内，楔形控制在30μm之内，板形平坦度控制在25iu之内；从而为冷轧工序提供了优质原料。

本发明相对于板厚较薄的电磁钢板提供不会导致磁特性劣化的基于激光的加工方法。在对电磁钢板进行使用激光的熔断并将该电磁钢板加工成规定的形状的电磁钢板的加工方法中，使上述激光的扫描速度成为10000mm/min以上来进行上述熔断。

本发明公开了一种半无机硅钢片漆及其制备方法和应用，其包括：聚酰胺酰亚胺清乳液、二氧化钛、二氧化硅、硫酸钡和氨基树脂，聚酰胺酰亚胺清乳液的制备：在保护气体保护下和回流状态下，使偏苯三酸酐与特定的复合双端氨基化合物在第一有机溶剂中反应，加入磷酸三丁酯、三乙胺，反应；向外蒸出第一有机溶剂，加入第二有机溶剂，加入直链烷基苯磺酸钠、脂肪醇聚氧乙烯醚硫酸钠和脂肪醇聚氧乙烯醚，混合，在搅拌条件下滴加水，滴加完之后，加入双马来酰亚胺进行封端，制成；该半无机硅钢片漆通过将各组分混合超声分散而制成，可在硅钢片中作为覆盖漆应用，且不仅可以采用水作为主体溶剂，环保型好，而且还兼具耐高温、高粘结强度、电气性能强等优点。