取向硅钢成品的晶粒尺寸非常大,其易磁化方向[001]晶向对于轧向的偏差角度对其磁性能影响极大。本文介绍了取向硅钢二次再结晶后成品晶粒位向的几种测定方法,包括侵蚀法、劳厄法、OIM法、极图法和非对称X射线衍射法等,并对这几种测量方法进行了比较。 The finished product of grain-oriented silicon steel has immense grain size ranging from millimeters to centimeters and the deviation angles of easy magnetization direction from rolling direction plays a remarkable role in magnetic properties of grain-oriented silicon steel.The methods in common use for determining the deviation angles of crystal direction are introduced,which include the etch-figure method,the Laue method,the OIM method,the pole figure method and the asymmetrical X-Ray diffract... 

介绍了微合金元素锡、铌、稀土对无取向硅钢性能的影响,并扼要分析了这些元素对硅钢性能的影响机理:晶界偏聚元素Sn可细化晶粒提高硅钢磁性能;微合金元素Nb细化铁素体晶粒,提高硅钢的强度、韧性和塑性及磁性能;稀土元素(RE)在硅钢中的主要作用包括净化钢液、变质夹杂物、改善铸态组织和性能及微合金化,减少晶界上出现偏析的几率。 The influence of micro-alloy elements on properties of non-oriented silicon steel and the mechanism for effect of the micro-alloy elements including Sn、Nb and RE on the properties of steel are presented and analyzed in this paper.Grain boundary segregation elements Sn in steel can grain refinement and improve the magnetic properties;Micro-alloy elements Nb can refine the ferrite grain,increase the silicon steel strength,toughness and plastic;The main role of the RE in the silicon steel including... 

采用RH精炼添加钙合金方式对硅钢进行钙处理,结果表明,钙合金添加量为0.67、1.00和1.67 kg/t钢时,钢中Ca含量分别为0、2×10-6和4×10-(6质量分数);随着钙合金添加量的增加,钢中夹杂物粒度逐渐由0～2μm向2～4μm、4～6μm偏移;不同钙处理条件下,钢中均存在粒径小于1μm和粒径为1～5μm的MnS、CuxS夹杂物,后者或单独存在,或与AlN、CaS夹杂复合;钢中粒径为5～10μm的夹杂物基本以Ca的氧化物和硫化物为主。与未经钙处理的炉次相比,钙合金添加量为0.67、1.00和1.67 kg/t钢时,粒径小于1.0μm的夹杂物减少幅度分别为68.06%、87.50%和94.94%。钙合金添加量为1.67 kg/t钢时,可以去除钢中绝大部分的微细夹杂物。 In order to improve the properties of final silicon steels,the calcium treatment was adopted by adding Ca alloys into the liquid steel during the RH refining process.Results show that when the addition of Ca alloys is 0.67 kg/t,1.00 kg/t and 1.67 kg/t,the corresponding Ca content in silicon steels is 0,2 × 10-6 and 4 × 10-6 respectively.With the increase of Ca alloy addition,the particle sizes of inclusions in steels become 2～4 μm and 4～6 μm,from 0～2 μm.Under different calcium treatments,there e... 

为了更好的解决电力系统防污闪涂料RTV-Ⅰ长期应用暴露出来的问题以及目前RTV-Ⅱ防污闪涂料存在的一些不足,结合具体实际需求,在电力系统外绝缘领域,应用新型防污闪硬质涂层——防污闪纳米硅钢涂层,并对分别喷涂了防污闪纳米硅钢涂层以及RTV涂料的绝缘子进行对比运行情况研究分析。研究结果表明,防污闪纳米硅钢涂层是一种同时具有优异憎水性迁移性能和自洁性能的新型涂层,具有良好的应用前景。 In order to solve the problem exposed of anti-pollution flashover coating RTV-Ⅰwhich has been used long-term in power system,as well as to better solve some shortcomings of the current anti-pollution flashover coating RTV-Ⅱ,in this paper,a new anti-pollution flashover hard coating — anti-pollution flashover nanometer silicon hard coating(NSHC) is applied in the field of power system insulation for the specific practical needs.At the same time insulators which are separately sprayed by the NSHC a... 

含铜抑制剂作为取向硅钢的主抑制剂或辅助抑制剂不仅可以抑制初次晶粒的长大,促进二次再结晶,还可以降低铸坯的加热温度。取向硅钢中主要抑制剂为10～50 nm Cu₂S,在钢的铸坯、热轧、冷轧、脱碳等工艺过程均可析出;（Cu,Mn）_1.8S、Cu_1.8S、ε-Cu等主要作为辅助抑制剂,尺寸一般为30～50 nm（或大于50 nm）,主要在热轧阶段析出。总结了国内外有关取向硅钢中含铜抑制剂析出行为的研究进展,当前主要研究不同生产流程和工序中含铜抑制剂的析出行为和作用机理。 As main inhibitor or auxiliary inhibitor for grain-oriented silicon steel,the particles of inhibitor bearing copper not only inhibit the primary crystal growing and promote the secondary recrystallization,but also decrease the heat temperature of casting slab.The main inhibitor for grain-oriented silicon steel is 10～50 nm Cu₂S,which precipitate in process and procedure including steel casting slab,hot rolling,cold rolling and decarburizing process,while the 30～50 nm or more than 50 nm... 

系统研究了无取向硅钢用磷酸盐系涂层性能的影响因素。以氢氧化铝和磷酸为原料制备磷酸二氢铝,再添加适量的添加剂酒石酸铵、二氧化硅、环氧树脂,得到的涂液涂布于硅钢表面,并控制合适的烘干温度,通过耐盐雾实验考察各因素对涂液耐腐蚀性能的影响。实验结果表明,在磷酸与氢氧化铝物质的量比为3.4∶1、酒石酸铵用量为2%、二氧化硅用量为1%、环氧树脂用量为5%、烘干温度为300℃条件下,所得涂层材料的防(耐)腐蚀效果最佳。 The factors influencing the performance of phosphate anticorrosive coating for non-oriented silicon were systematically studied.Aluminum dihydrogen phosphate was prepared with aluminum hydroxide and phosphoric acid as raw materials.Then added the right amount of additives,such as ammonium tartrate,silicon dioxide,and epoxy resin to prepare the liquid coating,which was coated on the surface of the silicon steel,and finally controlled a suitable drying temperature.The influences of various factors... 

【作者】 康凌晨； 王丽娜； ...

研究二次冷轧压下率对于硅的质量分数为3.0%的无取向硅钢组织结构和磁性能的影响。结果表明:当第二次冷轧压下率从0变化至16.7%时,铁损逐渐增加,磁感逐渐降低。当第二次冷轧压下率大于16.7%时,随压下率的增加,铁损逐渐减小,磁感逐渐增加。当第二次冷轧压下率大于38%时,二次冷轧法所能获得的磁性能明显优于一次冷轧法。 Effect of double cold reduction on magnetic,microstructure and texture of 3.0% Si non-oriented silicon steel sheets was investigated.The results show that the iron loss increases and magnetic induction reduces as the percentage redcution in secondary cold rolling changes from 0 to 16.7%.The core loss can be reduced remarkably,and magnetic induction can get a little benefit if the percentage redcution in double cold reduction is higher 16.7%.In case of higher than 38% of the percentage redcution ... 

【作者】 吴玉美； 陆晔； ...

利用EBSD技术研究了电工钢中长轴平行于轧向的柱状晶样品在热轧和退火过程中组织和取向的演变规律,并与长轴平行于板法向的样品的已有研究结果进行对比。结果表明,无论柱状晶按何种方向排列,只要表面存在剪切力,热轧后都可形成剪切织构,同时中心形成轧制织构,主要包括旋转立方织构和{112}<1-10>。柱状晶造成的影响主要体现在板中心层,长轴平行于轧向排列的样品热轧时形成的粗大旋转立方晶粒要到脱碳退火后才能完全消除,但破坏了正常的不同取向晶粒间的取向差分布及尺寸均匀性,导致二次再结晶不完全及磁性能降低。 The evolution of microstructure and grain orientation in an electrical steel containing columnar grains with its long axis being parallel to the rolling direction of sheet was studied during hot rolling and annealing by EBSD technique.The results are compared with those of samples containing columnar grains being parallel to normal direction of sheet reported in the reference [3].It was shown that,whether the long axis of columnar grains was arranged in RD or ND,shear textures can be formed in t... 

研究的两种取向硅钢（%:No1-0.042C、3.16Si、0.009Al、0.07Mn、0.50Cu、0.015S、0.0084N和No2-0.040C、3.20Si、0.014Al、0.22Mn、0.49Cu、0.016S、0.008 2N）由50 kg真空感应炉冶炼,锻成（mm）350×120×35板坯,经1 250℃30 min加热,开轧温度1 100℃,5道次热轧成2.3 mm板,终轧温度950～1 000℃。实验结果表明,两热轧板沿板厚方向存在组织和织构的不均匀性,热轧板次表层为再结晶组织,有较强的Goss织构组分;中心层为形变组织,具有典型的形变织构。含0.22%Mn的No2钢次表层{110}〈001〉织构组分比含0.07%Mn的No1钢弱,中心层{001}〈110〉织构组分大大强于0.07%Mn No1钢,导致两者磁性能差异,0.22%Mn No2钢磁感应强度(B₈₀₀)和铁损(P_1.7/50)分别为1.87 T和1.24 W/kg,0.07%Mn No1钢分别为1.88 T和1.18 W/kg。 Studied both grain-oriented silicon steels（%:No1- 0.042C,3.16Si,0.009Al,0.07Mn,0.50Cu, 0.015S,0.0084N and No2-0.040C,3.20Si,0.014Al,0.22Mn,0.49Cu,0.016S,0.0082N） are melted by a 50 kg vacuum induction furnace,forged to（mm） 350×120×35 slab,heated at 1 250℃for 30 min,with beginning rolling temperature 1 100℃hot-rolled to 2.3 mm plate by 5 passes,finishing-rolled at 950～1000℃.Test results show that the structure and texture along thickness of both hot-rolled plates are inhomogeneous:the subsurface ... 

以CaO-CaF2复合渣系为脱硫剂,在RH精炼过程采用真空投入法进行高牌号无取向电工钢深脱硫工业试验,采用KTH模型计算分析了RH炉渣成分对硫容量CS的影响。研究结果表明,炉渣成分控制在w((CaO))/w((SiO2))为5~7,w((CaO))/w((Al2O3))为1.5~1.8,w((Al2O3))为25%~30%,w((FeO+MnO))<5%,脱硫剂加入量为6~8kg/t时,钢中硫质量分数从平均0.003 1%降低到0.001 8%,最高脱硫率达到47.1%,平均脱硫率为41.7%。 The industrial trials on deep desulphurization of high grade non-oriented electrical steel were finished through using CaO-CaF2complex based fluxes in RH process.Using the KTH model,the effect of refining slag composition on the sulfide capacities was analyzed.The results show that the chemical composition of refining slag(mass fraction,%)is w((CaO/SiO2))between 5to 7,w((CaO))/w((Al2O3))beween 1.5to 1.8,w((Al2O3)) between 25%to 30%,w((FeO+MnO))less than 5%,and the desulphurizer addition level of...