硅钢资料

采用取向分布函数和取向线分析方法对低温板坯加热取向硅钢从热轧到初次再结晶工艺阶段的织构进行了研究。研究表明:一次冷轧后各层的织构组分与热轧板各层面的织构组分存在着继承关系,次表层存在很强的{001}<110>织构,中心层的织构和热轧板的中心层相似,存在强的{001}<110>和{112}<110>织构;中间退火后发生再结晶,各织构组分的强度有所减弱,Goss织构组分再次出现;二次冷轧后沿厚度方向上的织构不均匀性不明显,{111}<112>织构强度最高,几乎是其他织构组分的1倍,{001}<110>织构大幅降低;初次再结晶后织构沿厚度方向没有明显的不均匀性,{111}<110>为最强的织构组分,并且具有一定强度的Goss位向。 The texture from the first cold rolling to the primary recrystallization of low temperature slab reheating grain-oriented electrical steel were researched by orientation distribution function and orientation distribution intensity technique.The results show that after the first stage of cold rolling,there is a strong {001}<110> texture in the subsurface and the texture in center layer is very similar to the center layer of hot band which has strong {001}<110> and {112}<110> tex... 

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

对3层高硅电工钢复合板铸坯进行热轧及温轧变形加工后，采用正火、退火两种热处理方式处理，并观察轧制过程中产生的裂纹，研究不同状态下复合板的磁性能。对不同状态下的试样进行扩散退火处理，研究复合板中裂纹变化及其对磁性能的影响。结果表明：不同热处理工艺下合金内部的裂纹尺寸差异明显，裂纹尺寸对复合板的磁性能影响显著，相对于深裂纹，其他因素的影响较小；温轧变形加工后，复合板内层出现有序组织，但该有序组织在合金存在深裂纹的前提下并不能从本质上提高合金的磁性能；扩散退火工艺可以消除复合板内部的浅裂纹及微裂纹，但不能消除尺寸较大的裂纹，故而不能显著提高存在深裂纹的复合板的磁性能。 After hot rolling and warm rolling deformation processing of casting billet for three-layer high silicon electrical steel composite plate, it was normalized and annealed for heat treatment. Then, the cracks produced during the rolling process were observed, and the magnetic properties of composite plate in different states were also investigated. Furthermore, the samples in different states were subjected to diffusion annealing treatment, and the changes of crack in composite plate and their eff... 

为研究常化温度对热轧无取向硅钢组织与织构的影响,采用光学显微镜、背电子散射衍射技术研究了不同常化温度对其影响。结果表明,实验硅钢板在700～850℃温度下常化时,随常化温度的升高,晶粒尺寸增大,有利组分α织构增强,不利组分γ织构降低。对比研究了800℃和850℃常化热轧板CSL晶界分布图与取向差分布图,在本文研究条件下,Goss织构易在Σ=3,9的CSL晶界及晶粒取向差为30°～55°处形成。 The hot strips normalized at different temperatures were investigated by optical microscope and EBSD to study the effect of normalizing temperature on microstructure and texture of hot-rolled non-oriented silicon steel sheets.The results show that the grain size increases,the intensity of α-fibre texture increases,and the γ-fibre texture decreases when the hot strips are normalized at the 700-850 ℃.And CSL boundaries of Σ=3 and 15,and misorientation angles between 30° and 55° are more likely rel... 

某厂对电工钢的轧制策略进行了优化，粗轧道次由“1+5”改为“1+3”。在优化后的生产过程中，每次变换钢种，烫辊材就会出现窄尺现象，而紧随其后的电工钢板则出现超宽现象。文中针对该问题，介绍了宽度设定模型和宽度自适应模型的原理，阐述了该问题出现的原因及解决方案，并通过对宽度自适应模型的应用研究及优化攻关，有效地解决了问题，大幅提升了实物质量，降低了宽度封锁率。 The rolling strategy of electrical steel was optimized in a factory,and the rough rolling pass was changed from “1+5”to“1+3”.Subsequently,the following problems were occurred in the production process:when the steel grade changed,the roasting roller steel before the electrical steel appeared the narrow width phenomenon,and then the electrical steel appeared the ultra-wide phenomenon.This paper introduced the principle of width setting model and width adaptive model,and expounded the causes and s... 

【作者】 潘恒韬； 刘涛； ...

两炉次无取向硅钢XG800WR（/%:0.003～0.004C、0.71～0.75Si、0.32～0.33Mn、0.004～0.007S、0.016P）的炼钢流程为铁水预处理（KR）-210 t顶底复吹转炉-钢包吹氩-RH脱碳精炼-230mm×1220 mm板坯连铸。53 t中间包钢水过热度为25～30℃,钢包到中间包采用长水口全程吹氩保护浇铸,中间包至结晶器采用浸入式水口浇铸。结果表明,在RH、中间包、结晶器过程中钢中总氧以及夹杂物数量和尺寸均明显降低;但在钢包到中间包过程T[O]、[N]和钢中夹杂物数量增加,说明长水口浇铸过程存在二次氧化。连铸坯中T[O]、[N]平均他分别为11×10^-6和30×10^-6,显微夹杂物数量平均为4个/mm²。铸坯中的显微夹杂物主要为3～5μm的AlN,同时存在少量的MnS、Al₂O₃·AlN和Al₂O₃·MgO·MnS。 The steelmaking flow sheet for two heats non-oriented silicon steel XG800WR（/%:0.003～0.004C. 0.71～0.75Si,0.32～0.33Mn,0.004～0.007S,0.016P） is hot metal pretreatment（KR）-210 t top and bottom combined blown converter-ladle argon blowing-RH decarburization refining-230 mm×1 220 mm slab casting.The superheating extent of liquid in 53 t tundish is 25～30℃,whole casting is shielded by blowing argon with long nozzle from ladle to tundish and the submerged nozzle is adopted in casting from tundish to mold... 

对高牌号无取向电工钢35W300的成品进行了第二次退火,对第二次退火后的成品性能、纵横向磁性能差异和组织变化进行了分析。结果表明,随着第二次退火温度的升高,晶粒长大,磁性能优化。铁损平均值下降0.087 5W/kg,磁感平均值升高0.008T。第二次退火温度为820℃的产品的磁性能能够满足用户使用要求。 The product of high grade non-oriented electrical steel 35W300 was annealed at the second time.Microstructure,the difference of magnetic properties in the vertical and horizontal and were studied.The results show that the grain grew up and magnetic properties optimized with the increase of annealing temperature for the second time.Iron loss average declines in 0.0875 W/kg,magnetic induction average increases 0.008 T.The magnetic properties can meet the requirements of users at the second anneali... 

通过对连退线SF炉内的电加热体的焊接技术进行总结分析,得出焊接时应采用的主要方法,采用本焊接方法可提高电加热体的焊接速度和焊接质量,保证了焊接质量和施工工期。 SF furnace for continuous annealing line heating body welding technology summary,the main method used in welding,welding method by using the electric heater to improve the welding speed and welding quality through the implementation of this method to ensure the welding quality and Construction period. 

【作者】 程志明； ...

采用双辊连铸工艺制备了硅的质量分数分别为0.5%,1.0%,3.0%,4.5%的硅钢薄带,用光学显微镜观察其组织,并研究了后处理工艺对薄带组织和性能的影响。结果表明:硅含量为0.5%和1.0%的薄带适合采用一次冷轧+850～950℃退火的后处理工艺,而硅含量在3.0%以上的薄带适合采用二次冷轧+950℃退火的后处理工艺;硅含量为3.0%和4.5%的薄带在冷轧并950℃退火后,其磁性能最佳,铁芯损耗约为4.30 W·kg^-1,磁感应强度约为1.68T。 Silicon steel thin strips with silicon content of 0.5wt%,1.0wt%,3.0wt%and 4.5wt%were prepared by twin-roll continuous casting process,and the microstructure of the strips were observed by means of optical microscopy,and on the basis,the effect of post-treatment process on microstructure and properties of the strips was studied.The results show that the post-treatment process of one-time cold rolling and annealing between 850—950℃was suitable for the strips with silicon content of 0.5wt%and 1.0wt... 

借助高温激光共聚焦显微镜,在线观察了不同Mn含量的无取向硅钢中夹杂物的尺寸、类型、数量变化。结果表明,Mn含量(质量分数)为0.77%、0.32%时,试样中的夹杂物数量分别约为1000万个/mm3、1600万个/mm3。Mn含量较高的钢种,会优先析出球形、椭球形MnS夹杂物,其析出数量较少,尺寸相对较大,可以有效抑制AlN、CuxS夹杂物析出;Mn含量较低的钢种,会在试样再加热后冷却过程中,先析出相当数量MnS夹杂物,并作为AlN夹杂物析出核心,形成MnS+AlN复合夹杂物。这种复合夹杂物数量较多,尺寸也较大。 Based on the high temperature confocal microscope, the chage of size, type, and quantity of inclusions in non-oriented silicon steels with different Mn content were observed by in-situ SEM. Results show that the inclusion quantities are 10 million per mm3 and 16 million per mm3,while the mass fractions of Mn are 0.77% and 0.32%, respectively. In the silicon steel with higher Mn content, the spherical and ellipsoidal MnS inclusion will precipitate first, which can retard the precipitation of AlN ...