硅钢资料

运用电子背散射衍射(EBSD)和X射线衍射(XRD)技术对硅钢热轧板的织构在板厚方向的分布进行了研究,并分析了两种织构测量方法的特点。EBSD技术能直观给出板厚方向的微观织构,XRD能得到钢板的宏观统计织构信息,结合两种技术的分析,能更直观更精确的研究不同织构在板厚方向的分布。 The texture distribution along the thickness of the silicon steel has been investigated by electron backscatter diffraction(EBSD) and X-ray diffraction(XRD) technique.The characteristics of two technique of texture analysis have been investigated.Combined the two techniques,the texture distribution along the thickness of the silicon steel could be realized distinctly and accurately. 

分析了太原钢铁(集团)有限公司第二炼钢厂80 t RH生产冷轧硅钢脱碳、脱硫原理及影响因素,认为通过合理控制RH到站钢水碳和氧含量、加大插入管内径、采用快速抽真空度等可提高脱碳效果。降低顶渣中FeO和MnO含量,保证脱硫剂加入后的循环时间可以提高RH脱硫率。 The present article analyzes the principle of decarburization and desulfurization in refining the cold rolled silicon steel in the 80 t RH in No.2 Steelmaking Plant of Taiyuan Iron & Steel(Group) Corp.,and its influencing factors.It’s determined that the decarburization effect can be achieved by properly controlling the cabon and oxygen contents in the hot metal coming into the RH station,enlarging the inner diameter of snorkel and adopting the fast evacuation method.In the meanwhile the des... 

对高磁感取向硅钢冷轧板分别进行800、950、1050和1120℃不脱碳的预退火处理,在800℃预退火,成品的磁性能较好。织构分析的结果表明,随着预退火温度升高,初次再结晶后有利织构组分{111}<112>与不利织构组分(118)[110]的比值f(111)/f(118)逐渐降低,初次再结晶织构的变化是成品磁性的影响因素之一。 Preliminary annealing process at different temperatures for cold-rolled strips of a high permeability grain-oriented silicon steel was investigated to study the effect of the annealing temperature on microstructure and magnetic performance of the steel.Results show that the magnetic performances of the products annealed at 800 ℃ are best.Analysis of primary recrystallization texture indicates that with rising temperature,f(111)/f(118) which is the ratio of the favorable component {111}<112>... 

以不断增长的薄板坯流程为背景,与传统流程对比分析了薄板坯流程无取向电工钢热轧晶粒组织特征;以50W800和50W1300钢为典型实例,探讨了两种流程下成品板晶粒组织、织构、磁性能及其磁时效行为的基体差异和相关原理。研究表明,薄板坯流程热轧板组织较粗大,有利于在成品板中获得粗大的晶粒和有利的织构,从而得到较低的铁损和较高的磁感。然而,薄板坯流程会造成第二相粒子的细小弥散分布与不充分析出,容易因磁时效而使磁性能恶化。 Based on the rapid development of compact strip production(CSP) processing,the characteristics of hot band grain structure produced by CSP processing were analyzed in comparison with those of conventional technology.The basic differences in grain size,texture,magnetic properties and the magnetic aging behaviors of the final sheet products produced by the two processing technologies and the corresponding principles were discussed,while steel 50W800 and 50W1300 were taken as examples.It is indicat... 

本文中简要介绍了武汉钢铁有限公司采用薄板坯连铸连轧CSP(compact strip production, CSP)工艺生产中低牌号无取向硅钢的实践情况.CSP工艺生产的硅钢具有成品磁性均匀、板形好的优势，但是在利用该技术生产中低牌号无取向硅钢时，常存在成品板表面瓦楞状缺陷严重、连铸生产效率低等问题.通过优化炼钢成分、热轧等相关工艺，可消除热轧板厚度方向中心的粗大形变组织，从源头上避免了粗大{100}<011>纤维组织的出现，消除了瓦楞状缺陷；通过提升冶炼效率和控制钢中夹杂物总量，可优化隧道炉的加热温度与在炉时间，大幅度提升了连铸生产效率，实现了中低牌号无取向硅钢的批量稳定制造，使CSP产线成为中低牌号无取向硅钢热轧板原料的主要供给生产线.如何进一步提升钢水纯洁度、提高连铸生产效率、降低生产成本，以及挖掘该产线生产薄带钢的技术优点，是未来工作的重点. This paper briefly introduces the practice of producing medium and low grade non oriented silicon steel(NGO) with CSP(compact strip production, CSP)technology in Wuhan Iron and Steel Co., Ltd.. This technology has the inherent advantages of uniform magnetic properties and good shape for silicon steel finished strip. However, in the actual production process, there are serious corrugated defects on the surface of silicon steel finished strip, and production efficiency of continuous casting is low... 

【作者】 潘恒韬； 欧阳帆； ...

目的提高硅钢的磁性能。方法采用多弧离子镀技术,在普通取向硅钢薄板两面沉积高硅FeSi合金层制得高硅梯度硅钢,并进行热处理,观察其显微组织,测量磁性能。结果退火态高硅梯度硅钢表面的高硅FeSi合金层与基底结合紧密,均匀致密。高硅梯度硅钢中硅含量呈梯度分布,最表层硅质量分数为11.0%,随着深度增加,硅含量逐渐降低,在距表面20μm处硅质量分数仍能达到6.5%。沉积态高硅梯度硅钢的电阻率ρ、低频铁损P10/50、高频铁损P10/1k及磁感应强度B8分别为68.6μΩ·cm,0.82W/kg,83.3 W/kg和1.73 T,退火后分别为63.1μΩ·cm,0.44 W/kg,54.38 W/kg和1.89 T。结论由于表层高硅FeSi合金层的存在,梯度高硅钢的低频磁学性能良好,但高频损耗需进一步改善。 Objective To improve the magnetic properties of silicon steel. Methods FeSi alloy coatings with high-silicon content were deposited on the surface of common grain-oriented silicon steel by cathodic arc plasma evaporation,and then a kind of high silicon gradient steel was prepared. The morphologies,content and magnetic properties of the samples were tested. Results FeSi alloy coatings were featured with compact microstructures and excellent adhesive quality with the substrates. The silicon conten... 

【作者】 杨洪林； ...

利用DSC、XRD,结合热焓分析对硅钢级氧化镁和二氧化硅的固相反应行为进行了研究。比较了不同二氧化硅原料及混合方法对硅钢级氧化镁反应性的影响,找到了一种更为有效的硅钢级氧化镁反应性的评估方法,克服了传统柠檬酸活性法在比较不同厂家生产的氧化镁的反应性上的局限性。进一步研究了Na₂B₄O₇添加剂、TiO₂添加剂对氧化镁和二氧化硅反应行为的影响,结果表明,Na₂B₄O₇添加剂含量的增加对反应有利,而TiO₂添加剂对反应有阻碍作用。 The solid-state reaction behavior between silicon-steel grade MgO and SiO₂ was investigated by DSC and XRD combined with enthalpimetric analysis.The influence of different kinds of SiO₂ and different preparation methods were studied and a specifical measurement that is more reliable was proposed to evaluate reactivity of silicon steel grade MgO.It overcomes the limitation of the traditional citric acid activity（CAA） method,which can not be used to evaluate the reactivity of... 

对应用动态加热进行短时温度退火的取向电工钢进行了二次再结晶研究。所进行研究的实验用取向电工钢是经过终冷轧和后续罩式退火后的一条工业化生产线生产的。研究结果表明,运用短时热处理条件可引起研究钢完全的异常晶粒长大。在实验室处理的材料的织构和金相组织与工业化生产的经过终退火而获得的相同的取向电工钢类似。但是,在实验室处理的取向电工钢的二次再结晶的矩阵中可观测到\"寄生\"晶粒。从磁性观点看,这些\"寄生\"晶粒含有不理想的{111}取向织构。 The present study was made to investigate secondary recrystallization in grain-oriented steels annealed at short time temperature exposures with application of dynamical heating.The investigated GO(Grain Oriented) steels for experiments were taken from one industrial line after final cold rolling reduction and subsequent box annealing.It was shown that application of short time heat treatment conditions could lead to complete abnormal grain growth in the investigated GO steel.The texture and mic... 

结合硅钢退火炉项目中应用PDSOFT软件进行三维配管设计的案例,描述PDSOFT软件的应用过程,总结其使用要点,分析其优缺点,并提出了推广三维设计软件的思路,对今后PDSOFT在相似项目中的推广应用有参考和借鉴价值。 Combining the case of using PDSOFT software to design the three-dimensional piping,the application process of the PDSOFT software is described,the using points are summarized,the advantages and disadvantages are analyzed,and the ideas of promoting the three-dimensional design software are put forward,which have a strong reference value for the promotion and application of PDSOFT in similar projects in the future. 

根据新日铁、JFE及浦项等国外钢铁公司2008年以来在日本专利局、欧洲专利局(EP)及世界知识产权组织(WIPO)申请公开的有关生产Hi-B取向电工钢典型专利技术,概述了近年来国外大型钢铁企业采用低温板坯加热(坯加热温度<1 280℃)技术生产Hi-B取向电工钢主要技术重点,即将调节关键化学成分Al、N、Sn及Sb等与工艺改进相结合。最后介绍了国外大型钢铁企业采用低温板坯加热技术生产Hi-B取向电工钢实例。 The latest developments on technology for manufacturing Hi-B grain oriented electrical steel sheets developed by Nippon Steel Corp.,JFE Steel and POSCO were described according to the patents published by World Intellectual Property Organization,Japan Patent Office and European Patent Office over the recent years.The low temperature slab heating process(particularly slab-heating temperature<1 280 ℃) together with suitably adjusting key chemical elements such as Al,N,Sn and Sb elements was the...