硅钢资料

冷轧取向硅钢工程中有很多的超长、大体积以及薄壁的混凝土结构,裂缝控制是土建施工的关键。在工程中,按照\"抗放兼施、先放后抗、以抗为主\"的原则,采用\"无缝分块跳仓法\",防止超长混凝土结构收缩产生裂缝;在隧道和池体的底板与墙板施工中,采用\"整体浇筑\"法,避免了墙板因约束应力而产生的裂缝。 In the Cold-rolled grain-oriented silicon steel project,there are many overlength,bulk mass,thin-walled concretes structures,how to control the crack is the key of civil engineering construction.In these projects,according to the principle of\"release with resist,resist before release,resist is dominant \",the crack of the over-long structure and shrinkage can be prevented by the method of\"seamless block skip bin \".In the construction of the bottom plate and wall of the tunnel and the pool,the cra... 

研究了常化温度、常化时间及常化后冷却速度对Si的质量分数为1.6%的无取向电工钢成品磁性能的影响。结果表明:在850~1 050℃范围内,随着常化温度的升高,成品铁损先减小后增大,成品磁感应强度先增大后减小;当常化温度为1 000℃时,成品平均铁损最低,平均磁感应强度最高;常化时间从3min延长到7min时,成品铁损先减小后增大,成品磁感应强度则呈单调下降趋势;随着常化冷却速度的降低,成品铁损先减小后增大,成品磁感应强度则呈单调增大趋势;对于Si的质量分数为1.6%的无取向电工钢,最佳的常化制度为:在1 000℃进行常化,时间5min,常化后空冷。对热轧板进行常化后,热轧板发生了不同程度的再结晶和晶粒长大。提高常化温度、延长常化时间、降低冷却速度,都能使常化板晶粒粗化,进而粗化成品板晶粒,改善磁性能。通过扫描电镜观察发现,成品板中析出物主要为AlN和MnS的复合析出物,以及少量的单独析出的AlN和MnS,而常化工艺主要是通过粗化析出相,减少细小析出相数量,从而减少对晶界钉扎作用来改善成品磁性能。 The effects of normalizing temperature,normalizing time and cooling rate after normalizing on magnetic properties of non-oriented electrical steel with mass fraction of Si of 1.6% were investigated.The results show that core loss of product decreases first and then increases,while magnetic induction increases first and then decreases with the increase of normalizing temperature from 850 to 1 050℃.Average core loss of product is the lowest and average magnetic induction is the highest when normal... 

研究了传统工艺流程生产的2%Si无取向电工钢在不同退火温度下的磁性能。研究结果表明,随着退火温度的升高,显微组织均匀性提高且晶粒尺寸增大;有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;成品的铁损P1.5/50先下降后略有上升,磁感B50上升平缓;在890℃×2 min的退火工艺条件下,成品电工钢的磁性能最佳,对应的铁损P1.5/50小于3.2 W/kg,磁感B50高于1.74 T。 In this paper,the effect of annealing temperature on magnetic properties of non-oriented electrical steel with 2% silicon was studied.Results show that the uniformity of microstructure and the average grain size increase with the rise of annealing temperature.The texture components of annealing can be improved by enhancing {100} <0vw>,α,η fiber textures and weakening {111} <112> fiber texture.The tendency of core loss P1.5/50 shows that it decreases first and then increases,while the... 

选用国内外无取向硅钢标杆企业A、B、C的产品,采用非水溶液电解提取+SEM(EDS)方法,分析了其典型牌号对应成品试样中的夹杂物。结果表明,从磁性能控制角度而言,受钢的化学成分及生产工艺影响,A、B、C企业成品试样的夹杂物尺寸、种类、数量存在差异,这些差异对其磁性能产生显著影响;从夹杂物控制角度而言,A、B、C企业对应成品试样的夹杂物,以MnS、CuxS复合或者AlN、MnS、CuxS复合为主,其中1.0μm以下的夹杂物数量分别为2.34×107个/mm3、2.98×107个/mm3和11.98×107个/mm3,1.0μm以上夹杂物数量均很少,夹杂物的平均尺寸从大到小依次为A企业、B企业、C企业。 According to the production of three benchmarking manufacture enterprises A,B and C of non-oriented silicon steel at home and abroad,the inclusions in finished steel samples with typical grades were investigated by electrolytic extraction from non-aqueous solution and SEM(EDS).Results show that,from the viewpoint of improving the magnetic properties,affected by chemical composition and production technique,the size,type and amount of inclusions in finished steel samples are various,which will af... 

高强无取向硅钢主要应用于高速电机，要求其具备高强度和优异磁性能，但目前无取向硅钢的磁性能和强度难以兼顾。因此，设计并制备了添加微量Cr的含Nb高强无取向硅钢，通过光学显微镜、EBSD、万能拉伸试验机、四探针测试仪和磁性能测量仪等研究了Cr对含Nb高强无取向硅钢微观组织、织构、力学性能及磁性能的影响。结果表明，添加质量分数为0.5%的Cr抑制了热轧组织的回复，使常化和退火组织再结晶减弱，常化和退火后有利织构面积分数增加，不利织构面积分数减小。添加质量分数为0.5%的Cr使含Nb无取向硅钢的屈服强度显著增大，磁感略升高，但对铁损几乎没有影响。Cr对屈服强度的影响一方面是由于Cr的固溶强化作用，另一方面Cr促进了Nb的析出而使Nb的析出强化效果增强；而Cr提高含Nb高强无取向硅钢的磁感主要是由于促进有利织构形成的同时抑制了不利织构的形成，使得织构因子增大；添加Cr使无取向硅钢的电阻率增加从而使铁损降低，同时Cr促进了Nb的析出，而这种富Nb析出相不仅抑制晶粒长大且会阻碍磁畴移动而使铁损增高，在两方面因素的综合作用下，添加质量分数为0.5%的Cr对含Nb高强无取向硅钢的铁损几乎没有影响。因此，... High strength non-oriented silicon steel is mainly used in high-speed motors, which requires good mechanical and magnetic properties. However, it is difficult for non-oriented silicon steel to obtain high strength and good magnetic properties at the same time. In this paper, the Cr-microalloyed Nb-containing high strength non-oriented silicon steel was designed and prepared. The effect of Cr on the microstructure, texture, mechanical properties and magnetic properties of Nb-containing high stren... 

为研究退火工艺对普通取向硅钢初次再结晶组织的影响,对经不同温度、保温时间和升温速率退火后的材料组织进行了分析。结果表明:在等温退火条件下,加热至600℃时开始发生初次再结晶,800℃以上初次再结晶组织发展完善;而在最终冷轧板直接进行最终高温退火的情况下,加热温度在500～700℃时,将升温速率提高到80℃/h,初次再结晶组织更易于发展完善。 To investigate the influence of annealing process on the recrystallization of common grain oriented silicon steel,microstructures of sheets annealed at different temperature,soaking time and heating rate are observed.Results show that under the condition of isothermal annealing,recrystallization begins at 600℃ and fully develops above 800℃,while in the case that the final cold rolled sheets are directly thrown to final high temperature annealing,recrystallization is likely to develop with the he... 

冷轧无取向硅钢（/%:0.003C,2.35Si,0.22Mn,0.011P,0.002S,0.36A1,0.003 0N）经890℃或940℃3 min常化的2.3 mm热轧板冷轧成0.35 mm薄板。研究了常化温度和800⁹20℃3 min退火对该钢高频（400Hz）磁性能和抗拉强度的影响。结果表明,830⁹20℃退火时高频铁损P_10/400值最低,随退火温度增加,晶粒尺寸增大,钢的抗拉强度降低;该钢的最佳热处理工艺为常化温度940℃,退火温度830℃,其抗拉强度R_m、高频铁损P_10/400和磁感应强度J₅₀分别为565 MPa,21.5 W/kg和1.69 T。 The cold-rolled non-oriented silicon steel（/%:0.003C,2.35Si,0.22Mn,0.011P,0.002S,0.36A1,0.003 0N） is cold-rolled to 0.35 mm sheet from 2.3 mm hot-rolled plate normalized at 890 ℃ or 940℃ for 3 min.The effect of normalizing temperature and annealing process at 800 ⁹20 °C for 3 min on high frequency（400 Hz） magnetic properties and tensile strength of the steel has been tested and studied.Results show that with annealing at 830 920 ℃the high frequency iron loss value P_10... 

【作者】 朱传芳； 潘恒韬； ...

结合冶炼无取向硅钢的生产实际,对钢中硫的来源,以及炉渣性质、钢水温度、底吹强度对脱硫的影响进行了分析。研究表明,转炉钢中硫的主要来源为铁水、废钢、铁水渣及石灰带入;冶炼硅钢时,终渣碱度为3.0~3.5,w((FeO))≤20%,终点钢水温度大于等于1 680℃,加大底吹搅拌强度能提高转炉脱硫效果。硅钢平均出钢硫的质量分数为0.004 8%,能满足无取向硅钢对硫含量的要求。 With the actual production of non-oriented silicon steel,the source of sulphur and the effect of metallugic parameters like slag properties,temperature of molten steel and bottom stirring on desulphurizing ability were investigated.The results show that the main source of sulphur is molten metal,scrap,the remaining slag volume in hot metal and lime.The degree of desulphurization for smelting silicon steel can be increased through adopting the following measures,such as the basicity of finishing ... 

聚焦无取向硅钢产品标准,从电磁性能、表面性能、机械性能以及尺寸公差与边部质量等维度对国际标准IEC、EN、JIS、ASTM以及国标GB进行了分析研究。分析得出,各类标准在电磁性能方面要求基本一致;ASTM标准的机械性能要求有别于其他几个标准。 In this paper,non-oriented silicon steel standards of EN,JIS,GB and ASTM were compared and analyzed. It is showed that,all types of standards in electromagnetic performance requirements are basically the same. Surface properties in ASTM standard are expressed in the most detailed. The mechanical properties requirements of the standards,except for ASTM,are basically the same. 

取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加铜可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布。利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧(TSCR)工艺的3种不同铜含量的取向硅钢热轧板织构。结果表明:不同铜含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;铜含量约在0.4%时,热轧板次表层的{110}<001>织构比例最高,而热轧板心部的{100}<110>织构比例最低;铜含量对热轧织构中{114}<110>和{001}<100>织构发展有显著影响。 The texture gradient in hot rolled grain oriented silicon steel strip is one of the essential factors to achieve a perfect secondary recrystallization.The addition of copper can significantly reduce the slab reheating temperature of grain oriented silicon steel,so as to impact the texture distribution in the hot rolled strip.The texture of hot rolled grain oriented silicon steel strip as-rolled by thin slab casting and rolling process(TSCR) in laboratory with three different copper contents was ... 

【作者】 杨佳直； ...