通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 

对RH法(真空循环脱气法)生产的冷轧硅钢的脱硫原理及影响因素进行了分析研究。研究表明:降低顶渣中FeO、MnO的含量,提高钢液温度,增加脱硫剂的加入量并延长其循环时间有利于提高脱硫效率。 The principles of desulfurization and its influence factors of cold rolling silicon steel during RH process have been studied in this paper.The result indicated that reducing contents of FeO and MnO,rising temperature of the liquid steel,increasing quantity of desulfurizer,lengthening cycle time of desulfurzer are benefit for desulfurization. 

利用OM、TEM与EDS技术,对Fe-3.2%Si低温取向硅钢热轧板进行不同常化冷却工艺处理后的显微组织、析出相及最终产品的磁性能进行分析,并与热轧板的组织和析出相进行对比。结果表明,常化板较热轧板的表层组织均匀,基体中再结晶比例增加,带状组织变窄;常化板中析出物的数量明显比热轧板的多,析出物主要有AlN、MnS及复合析出的(Cu,Mn)S等。在常化温度1120℃、保温3 min的条件下,采用二段式冷却较空冷、淬沸水、淬常温水的冷却工艺,常化板表层显微组织更均匀,沿板厚方向的显微组织的不均匀性显著,取向硅钢的磁性能最高;常化后采用二段式冷却工艺析出的细小析出物数量最多,且弥散分布在基体中,抑制剂的抑制效果最好,对成品获得高磁性最有利。 Microstructure, precipitate and magnetic characteristic of final products with different normalizing cooling processes for Fe-3.2%Si low-temperature hot-rolled grain-oriented silicon steel were analyzed and compared with the hot-rolled plate by optical microscopy(OM), transmission electron microscopy(TEM), and energy dispersive spectrometry(EDS). The results show that, the surface microstructure is uniform, the proportion of recrystallization in matrix increases, and the banding textures are nar... 

运用电子背散射衍射(EBSD)技术,研究了50W600无取向硅钢在热轧→冷轧→退火工序间织构的演变。结果表明:由于热轧板沿板厚方向的应力场和温度场存在差异,导致热轧板不同层织构类型和强度存在差异;热轧板表层主要存在铜型、黄铜和高斯织构,1/4层织构主要为α纤维织构和较弱的高斯织构,中心层织构较单一,主要为α纤维织构;和热轧板相比,冷轧板各层织构差异较小,为典型的轧制织构(α纤维织构和γ纤维织构);退火板各层都表现为γ纤维织构增强、α纤维织构减弱,旋转立方织构基本消失。 The texture evolution of 50W600non-oriented silicon steel in hot rolling,cold rolling and annealing process was investigated by electron back-scatter diffraction(EBSD)technology.Results show that the hot rolled plate texture types and intensities along thickness direction were different because of the different stress fields and temperature fields.The major texture types in the surface of hot rolled plate were copper,brass and Gauss texture.The texture was composed ofαfibre texture and weaker Ga... 

在实验室试制了TSCR流程的低碳低硅无取向硅钢,研究了在850～1050℃不同温度常化对冷轧量0.5mm厚钢板再经950℃×7min退火后的组织、织构和磁性能的影响。结果表明:随常化温度的升高,使热轧板晶粒尺寸增大,晶界更清晰,组织均匀性更好;由于第二相AlN和MnS析出物尺寸比较大,使冷轧退火后钢板晶粒也随常化温度升高呈单调增大趋势;γ有利织构和{111}、{112}不利织构与常化温度升高同时增强,但前者增强更多;冷轧板退火后铁损随常化温度升高呈单调下降,磁感呈单调上升趋势。 The low-carbon and low-silicon non-oriented silicon steel was prepared by thin slab casting and rolling(TSCR) in lab.The effect of normalizing at different temperatures in 850-1 050℃on microstructure, texture and magnetic properties of 0.5 mm cold-rolled sheets after annealing at 950℃for 7 min was researched. The results show that with increasing the normalizing temperature,the grain size of hot-rolled sheets increased,the grain boundaries were more clear and the rnicrostructure uniformity was b... 

双辊连铸技术是冶金及材料领域内的一项前沿技术,对于生产高品质硅钢具有独特优势.本实验研究了一种双辊铸轧w[Si]=4.5%的无取向硅钢,考察其铸态和常化处理后样品的组织、织构及析出相尺寸特征.结果表明:铸带组织以与铸带法向成5~20(°)倾角的柱状晶为主,晶内存在少量0.3~0.4μm的AlN析出相,铸带织构以λ(<001>//ND)织构为主,表层织构漫散.950℃/10 min常化处理后,析出相尺寸增大,表层λ织构增强. As an advanced technique of metallurgy and material science,twin- roll strip casting has unique advantages for producing high quality silicon steel. The present study was aimed at a 4. 5% Si non- oriented electrical steel for analyzing the structure,texture and the size of precipitates at the initial and normalized state. The results revealed that the initial structure mainly consisted of columnar grains with 5 ~ 20( °) angle to the normal of cast strip,and some AlN precipitates of 0. 3 ~ 0. 4 μ... 

对高磁感取向硅钢冷轧板分别进行800、950、1050和1120℃不脱碳的预退火处理,在800℃预退火,成品的磁性能较好。织构分析的结果表明,随着预退火温度升高,初次再结晶后有利织构组分{111}<112>与不利织构组分(118)[110]的比值f(111)/f(118)逐渐降低,初次再结晶织构的变化是成品磁性的影响因素之一。 Preliminary annealing process at different temperatures for cold-rolled strips of a high permeability grain-oriented silicon steel was investigated to study the effect of the annealing temperature on microstructure and magnetic performance of the steel.Results show that the magnetic performances of the products annealed at 800 ℃ are best.Analysis of primary recrystallization texture indicates that with rising temperature,f(111)/f(118) which is the ratio of the favorable component {111}<112>... 

薄带连铸流程下取向硅钢粗大λ晶粒(〈100〉//ND,normal direction)的“遗传”会导致磁性能恶化.为解决这一问题，针对取向硅钢的热轧孪生行为开展研究，结果表明：凝固组织粗大的取向硅钢在650℃热轧时可产生大量{112}〈111〉形变孪晶，这与具有高层错能的硅钢在较高温度下难以孪生变形的传统认知不同.热轧过程中复杂的应力状态降低了变形孪晶的取向依赖性，由于具有更高的储存能，孪晶界/孪晶界及孪晶界/晶界交叉点成为再结晶形核的优先位置，大大提高了常化过程中的再结晶率，受沿孪晶界应变分布及孪晶间距离的限制，沿孪晶界形核的再结晶晶粒通常呈“饼状”,最终形成以细小且取向漫散的再结晶晶粒为主的常化组织，消除了初始凝固组织中有害的粗大λ晶粒. In strip casting grain-oriented silicon steels, the inheritance of coarse λ grains(〈100〉//ND, normal direction) can deteriorate their magnetic properties. To solve the problem, twinning behaviors in strip casting grain-oriented silicon steels during hot rolling were investigated in this work. It is found that after rolling at 650 ℃, a number of {112}〈111〉deformation twins are formed in the coarse solidification microstructure of the steels, in contrast to the well-accepted view that it is diffic... 

通过热力学计算与模拟试验研究了含钒钛取向硅钢中氮化物析出相的析出规律与析出行为,并探讨了含钒钛元素的氮化物析出相作为薄板坯连铸连轧流程制备取向硅钢中辅助抑制剂的可行性.研究表明,在所冶炼的含钒钛取向硅钢的成分范围内,Ti N在钢液凝固末期便具备析出的热力学条件,而Al N与VN只可能在凝固后的α+γ或α+Fe3C两相区内析出.含钒钛取向硅钢中氮化物析出相以成分复杂的复合析出相为主,且随着钒钛加入量的增加,钢中抑制剂析出相总的分布密度由于含钒钛元素的氮化物析出相的增加而明显提高,使抑制剂抑制初次再结晶晶粒正常长大的能力得以加强,最终成品的磁感应强度值B8由1.857 T提升至1.898 T.同时,加入不高于0.007%的Ti与不高于0.005%的V不会影响中间脱碳退火工序的脱碳效果以及高温退火净化阶段硫、氮的脱除效果,其形成的含钒钛元素的纳米级氮化物析出相适合作为薄板坯连铸连轧流程制备取向硅钢的辅助抑制剂. The precipitation behavior of nitride precipitates in grain-oriented silicon steel containing vanadium and titanium elements produced by thin slab casting and rolling process was studied by thermodynamic calculation and simulation experiment. The feasibility of nitride precipitates containing V and Ti elements as auxiliary inhibitors was also investigated. It is found that Ti N is likely to precipitate at the final stage of solidification in the grain-oriented silicon steel,but VN and Al N can p... 

对高牌号无取向电工钢国内生产情况、工艺技术、产品性能及应用领域等进行了阐述,并探讨了高牌号无取向电工钢产品的发展趋势。 This paper introduces basic facts on the production status,process technology and products’ properties and their applications of non-oriented electrical steel with high grade at home,and then discusses the development trend on technology for producing the non-oriented electrical steel with high grade. 

以轻烧氧化镁粉为原料,经消化、碳化制得重镁水,在热解反应前采用络合剂对重镁水中的杂质钙、铁进行络合掩蔽,再经热解得到碱式碳酸镁,碱式碳酸镁经煅烧可制得钙、铁杂质含量较低的氧化镁。在重镁水络合除杂过程中,考察了络合剂三乙醇胺、柠檬酸、草酸单独和复合使用的除铁、除钙效果。以三乙醇胺为络合剂时,在200 mL重镁水中加10 mL三乙醇胺(1∶1),氧化镁产品中w(氧化镁)=99.3%、w(氧化钙)=0.31%、w(氧化铁)=0.042%;使用草酸和柠檬酸作为复合络合剂时,在200 mL重镁水中加入1.0 g柠檬酸和2.0 g草酸,氧化镁产品中w(氧化镁)=98.2%、w(氧化钙)=0.24%、w(氧化铁)=0.030%。 Light-burned magnesia as a raw material was hydrated and carbonated to obtain magnesium bicarbonate liquor.Before the pyrolyzing of magnesium bicarbonate liquor,complexants were used to cover Fe and Ca impurities.Then the treated liquid was pyrolyzed to obtain basic magnesium carbonate which was calcined to magnesium oxide with low calcium and iron content.During the complexing purification of magnesium bicarbonate liquor,the Fe and Ca removing effects of single or compound complexing agents,suc... 