通过Axio Imager金相显微镜考察4.5%~7.0%硅(质量分数)对高硅钢材料组织形貌的影响,并利用Fe-6.5%Si高硅钢薄板制备方法对其进行轧制,通过DDL50电子万能试验机对阶段产品进行力学性能测试。结果证明,硅含量为5.58%的高硅钢在实验硅含量区间内存在最大延伸率及最小铸态组织晶粒尺寸。 An investigation about the influence of 4.5%-7.0% Si on microstructure and mechanical properties of high-silicon steel was presented.SEM was adopted to take an observation towards microstructure during fabrication,and DDL50electronic universal testing machine was applied into the detection of tensile curves.The results show that silicon steel with 5.58% Si provides the maximum elongation and minimum grain size as cast. 

研究了组织和析出物对高效电机用无取向硅钢退火板磁性能的影响。结果表明:随着退火温度升高,退火板平均晶粒尺寸增加,P15/50明显降低,B50略有升高。退火温度在1 000℃时,退火板的综合性能较好。析出物主要是AlN、(MnS+AlN)和(MnS+Al2O3)复合析出物,尺寸较粗大,主要集中在1.0～2.5μm,还发现少量百纳米以下的细小AlN和TiN。实验室模拟TSCR流程试制的高效电机用无取向硅钢,铁损平均值小于4.00 W/kg,磁感应强度大于1.75 T,适合作中小型高效电机铁芯材料。 Effects of microstructure and precipitation on magnetic property of non-oriented silicon steel sheets after annealing for high-efficiency motor are studied in the paper by experiments.The annealed sheet exhibits a larger average grain size,obviously decreasing iron loss and slightly raising magnetic induction with increasing temperature.The annealed sheet has better comprehensive properties at a annealing temperature of 1 000 ℃.The main precipitates are compounds of AlN、(MnS+AlN)and(MnS+Al2O3) w... 

选用国内外无取向硅钢标杆企业A、B、C的产品,采用非水溶液电解提取+SEM(EDS)方法,分析了其典型牌号对应成品试样中的夹杂物。结果表明,从磁性能控制角度而言,受钢的化学成分及生产工艺影响,A、B、C企业成品试样的夹杂物尺寸、种类、数量存在差异,这些差异对其磁性能产生显著影响;从夹杂物控制角度而言,A、B、C企业对应成品试样的夹杂物,以MnS、CuxS复合或者AlN、MnS、CuxS复合为主,其中1.0μm以下的夹杂物数量分别为2.34×107个/mm3、2.98×107个/mm3和11.98×107个/mm3,1.0μm以上夹杂物数量均很少,夹杂物的平均尺寸从大到小依次为A企业、B企业、C企业。 According to the production of three benchmarking manufacture enterprises A,B and C of non-oriented silicon steel at home and abroad,the inclusions in finished steel samples with typical grades were investigated by electrolytic extraction from non-aqueous solution and SEM(EDS).Results show that,from the viewpoint of improving the magnetic properties,affected by chemical composition and production technique,the size,type and amount of inclusions in finished steel samples are various,which will af... 

采用非水溶液电解方法来提取无取向硅钢中夹杂物。通过扫描电镜(SEM)观察结果表明:无取向硅钢中主要夹杂物为六棱柱的AlN、不规则硅酸盐及球状的铁的硫化物和氧化物,其中AlN夹杂尺寸在1~5μm,数量较多,还有部分AlN的复合夹杂。进一步研究了AlN复合夹杂形成机理,采用了Thermo-Calc热力学计算软件计算出该钢样中AlN、MnS析出温度分别为1 240℃、1 200℃,而Al2O3析出温度大于1 800℃,从而为AlN复合夹杂形成机理提供了一个理论依据。 Extracting inclusions from non-oriented silicon steel in non-aqueous electrolysis is a nondestructive method to gain inclusions.Scanning electron microscopy shows that the main inclusions in non-oriented silicon steel were hexagonal AlN,which was of large quantity,irregular silicate,spherical iron sulfide and oxide.The size of AlN inclusions ranged from 1to 5μm,and there were some duplex inclusions of AlN.To further study the formation mechanism of AlN duplex inclusions,Thermo-Calc thermodynamic... 

电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

某厂对电工钢的轧制策略进行了优化，粗轧道次由“1+5”改为“1+3”。在优化后的生产过程中，每次变换钢种，烫辊材就会出现窄尺现象，而紧随其后的电工钢板则出现超宽现象。文中针对该问题，介绍了宽度设定模型和宽度自适应模型的原理，阐述了该问题出现的原因及解决方案，并通过对宽度自适应模型的应用研究及优化攻关，有效地解决了问题，大幅提升了实物质量，降低了宽度封锁率。 The rolling strategy of electrical steel was optimized in a factory,and the rough rolling pass was changed from “1+5”to“1+3”.Subsequently,the following problems were occurred in the production process:when the steel grade changed,the roasting roller steel before the electrical steel appeared the narrow width phenomenon,and then the electrical steel appeared the ultra-wide phenomenon.This paper introduced the principle of width setting model and width adaptive model,and expounded the causes and s... 

以CaO-CaF2复合渣系为脱硫剂,在RH精炼过程采用真空投入法进行高牌号无取向电工钢深脱硫工业试验,采用KTH模型计算分析了RH炉渣成分对硫容量CS的影响。研究结果表明,炉渣成分控制在w((CaO))/w((SiO2))为5~7,w((CaO))/w((Al2O3))为1.5~1.8,w((Al2O3))为25%~30%,w((FeO+MnO))<5%,脱硫剂加入量为6~8kg/t时,钢中硫质量分数从平均0.003 1%降低到0.001 8%,最高脱硫率达到47.1%,平均脱硫率为41.7%。 The industrial trials on deep desulphurization of high grade non-oriented electrical steel were finished through using CaO-CaF2complex based fluxes in RH process.Using the KTH model,the effect of refining slag composition on the sulfide capacities was analyzed.The results show that the chemical composition of refining slag(mass fraction,%)is w((CaO/SiO2))between 5to 7,w((CaO))/w((Al2O3))beween 1.5to 1.8,w((Al2O3)) between 25%to 30%,w((FeO+MnO))less than 5%,and the desulphurizer addition level of... 

【作者】 陶永根； ...

目前随着电工钢用户冲压设备的升级,冲压速度逐步提高,对电工钢产品的硬度和强度指标提出了更高的要求。与普通硬度级别的无取向硅钢相比,高硬度50BW600的Hv硬度提高15~20,达到125以上,同时对电磁性能指标也有较高要求。本钢通过化学成份和热轧及冷轧连退生产工艺的设计,经过小批量生产试验,满足用户要求。通过对工艺的严格控制,在大批量生产过程中,保证了产品的力学性能和电磁性的检验合格率。 Currently with upgrading of stamping equipment of silicon steel user, gradually increasing of stamping speed, propose higher demand for hardness and strength of silicon steel. Compared with conventional 50BW600, high hardness 50BW600 have higher hardness, reach greater than 125Hv. Through design of chemical composition with hot mill and annealing, production test of small quantities, stamping performance meet user request. 

文章以国内某公司硅钢厂连续退火机组1号辐射管加热段为研究对象,分析炉内传热机理,建立并开发了辐射管加热段的传热模型。采用生产实际数据对模型进行了验证,以总燃料消耗量最小为目标,得出该炉段长度方向上燃料的最佳分配机制。所得结论为该公司连续退火机组节能控制提供理论依据。 Taking the radiant tube heating section of No.1 continuous annealing unit in a silicon steel plant of a domestic company as the research object, the heat transfer mechanism in the furnace is analyzed, and the heat transfer model of the radiant tube heating section is established and developed. The model is verified by the actual production data. Aiming at the minimum total fuel consumption, the optimal fuel distribution mechanism in the length direction of the furnace section is obtained. The co... 

分析了太原钢铁(集团)有限公司第二炼钢厂80 t RH生产冷轧硅钢脱碳、脱硫原理及影响因素,认为通过合理控制RH到站钢水碳和氧含量、加大插入管内径、采用快速抽真空度等可提高脱碳效果。降低顶渣中FeO和MnO含量,保证脱硫剂加入后的循环时间可以提高RH脱硫率。 The present article analyzes the principle of decarburization and desulfurization in refining the cold rolled silicon steel in the 80 t RH in No.2 Steelmaking Plant of Taiyuan Iron & Steel(Group) Corp.,and its influencing factors.It’s determined that the decarburization effect can be achieved by properly controlling the cabon and oxygen contents in the hot metal coming into the RH station,enlarging the inner diameter of snorkel and adopting the fast evacuation method.In the meanwhile the des... 

【作者】 陶永根； ...