利用热模拟试验机、光学显微镜和X射线衍射仪对Fe-3.2%Si低温取向硅钢热轧工艺参数对组织及织构的影响进行了研究。结果表明,Fe-3.2%Si硅钢在1110℃粗轧、880℃终轧,轧后以10℃/s的速度冷却到550℃卷取,然后空冷到室温,热轧硅钢板沿板厚方向的显微组织不均匀性显著,对后续发展完善的二次再结晶有重要作用。无论是热轧板,常化板还是冷轧板,它们的织构集中分布在γ取向线上,γ取向线的织构除取向密度不同外,织构种类是一致的,这说明γ取向线上织构是有继承性的。从热轧到常化,织构取向密度显著减小,经二次冷轧后,织构密度又显著升高,可见,轧制变形有助于织构的形成并使织构强度升高。 The influence of hot-rolled process parameters on the microstructure and texture of Fe-3.2%Si low temperature hot rolled grain-oriented silicon steel were researched by hot simulation experiment machine,light microscope and X-ray diffractometer.The results show that,Fe-3.2%Si silicon steel is rolled by the technology with a temperature of rough rolling of1110℃,finish rolling of 880℃,coiling with the speed of 10℃ /s,and then cooled to room temperature with air.The microstructure of hot-rolled sil... 

采用取向分布函数分析了无取向电工钢不同再结晶退火温度下的织构变化及织构对磁感应强度和铁损的影响,并计算了无取向电工钢的磁晶各向异性能。结果表明,随着实验钢的再结晶退火温度升高,Goss织构和立方织构组分显著增强,而{111}面织构强度却减弱。较高的退火温度有利于减小织构因子,提高磁感应强度。磁晶各向异性能计算结果显示,随着再结晶退火温度升高,无取向电工钢板的磁晶各向异性能降低。 The recrystallization texture and the relationship of texture to magnetic induction intensity and core loss of a non-oriented electrical steel were investigated by orientation distribution function analysis. The magnetic anisotropy energy of the steel was calculated also. The results show that,the intensity of Goss texture and cubic texture increases,but the intensity of { 111} texture decreases with increasing recrystallization annealing temperatures of the steel. The higher annealing temperatu... 

介绍了EB5325涂层液的主要性能和中冶新材生产冷轧无取向电工钢所用的涂层设备,通过多次试验摸索出使用EB5325涂层液的工艺,对涂层出现的缺陷进行分析研究,并提出解决方法,使中冶新材生产的冷轧无取向电工钢的涂层质量满足了用户的要求。 This article introduces the main properties of EB5325 and the coating equipments for cold-rolled non-oriented electrical steel. A process using EB5325 coating liquid is made through many time experiments and exploration. The appeared defects in the coating are studied and analyzed,and the solutions are proposed. The coating quality meets clients’ requirements of cold rolled non-oriented electrical steel. 

【摘要】 <正>编号:2012016获奖等级:特等完成单位:...

研究了应用电感耦合等离子体质谱法(ICP-MS)测定硅钢中痕量铜和镍的分析方法。采用硝酸分解样品,通过内标校正和基体匹配消除了基体干扰的影响,同时根据测量时存在的质谱干扰情况,选择同位素65Cu和60Ni作为测定元素和通过调节仪器参数使双电荷离子的产率最低,以减少带来的干扰。该方法用于硅钢中痕量铜和镍的测定,所得的结果与ICP-AES法测定结果完全吻合,各元素测定结果的RSD值小于5%,加标回收率为97.3%～100.3%。 A method for the determination trace copper and nickel in silicon steel by inductively coupled plasma mass spectrometry(ICP-MS) was studied.The samples were dissolved in HNO3.The effect of matrix interference was eliminated by internal standard correction and matrix matching.Meanwhile,according to the mass spectral interferences in determination,the isotopes including 65Cu and 60Ni were used as measuring elements.The yield of double-charge ions were minimized by adjusting instrumental parameters... 

对硅钢板材分别进行异步和同步轧制,研究了轧制参数包括速比、压下量和道次对板材表面显微组织的演变的作用.结果表明,异步轧制硅钢板材表面形成了晶粒尺寸为10~50 nm,取向接近随机分布的纳米晶,而同步轧制板材的表面只形成了位错胞,证明异步轧制可以诱发表面纳米化.异步轧制板材表面纳米晶的形成过程为:在剪切力的反复作用下,高密度位错形成、滑移、湮灭和重组形成亚微米尺度的亚微晶/位错胞.随着压下量和轧制道次增加,高密度位错重复以上过程使晶粒尺寸减小、取向差增大,最终形成取向接近随机分布的纳米晶组织.大压下量和多道次是异步轧制诱发板材表面纳米化的关键,而速比的增加可以加快纳米化进程. Surface nanocrystallization(SNC) can effectively enhance the surface and global properties of the metallic materials,such as microhardness,intensity,fatigue,wear and corrosion resistances,therefore provides more promising practical industrial applicability.Up to now,several SNC treatment methods were developed based either on the principles of ball impactions or friction sliding,however,difficulty still exists for the surface treatment of large-dimensional samples with high efficiency.Recently,m... 

分析了冲裁硅钢芯片时出现的质量问题,针对影响硅钢芯片冲裁质量的4大因素——人、原材料状态、工艺和工装进行了工艺试验和分析,根据原材料状态的差异,采用不同工艺方案,特别是如何合理选择冲裁模具间隙,解决了硅钢芯片冲裁时产生的主要质量问题,使冲裁的硅钢芯片达到最佳质量状态,并满足硅钢芯片的使用性能。 The problems occurred during silicon steel chip punching and the factors that affect the quality of silicon steel chip punching were analyzed,the factors include 4aspects,that is,people,raw material status,process and frock,at the same time,process tests and analysis aimed at the factors that affect punching quality were did,according to the difference of raw material status,corresponding process schedules wee taken,especially in how to reasonably select punching dies clearance,which solved the ... 

主要研究了氧化锌对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响.用盐雾实验和动电位极化研究了不同氧化锌含量对硅钢绝缘涂层的耐蚀性和电化学行为的影响.采用SEM和体视显微镜对涂层的表面形貌和附着性能进行研究.结果表明,氧化锌含量为4.0%时,氧化锌能完全中和涂层表面的游离磷酸,涂层的耐蚀性和附着性最好;氧化锌含量过少或过多时,涂层的耐蚀性和附着性都较差. This paper studies the influence of zinc oxide on the performance of chromium-free non-oriented silicon steel insulating coating which based on aluminum dihydrogen phosphate.Salt spray experiment and potentiodynamic polarization were used to study the influence of zinc oxide content on the corrosion resistance and electrochemical behavior of the insulation coating of silicon steel.The surface morphology and adhesion of coating were tested by SEM and stereo microscope.The results show that when t... 

为了弄清楚高硫硅钢中的硫化物析出行为及其对钢的微观组织和电磁性能的影响，以便为工业化生产制定更为合理的硫含量控制标准和采取更为有效措施减轻炼钢生产的硫含量控制压力，结合0.25% Si 无取向硅钢 ，采用非水溶液电解提取 + 扫描电镜/透射电镜观察相结合的方法 ，研究了0.006 8%、0.010 2%、0.025 5% 和 0.035 3% 硫含量条件下，钢中的硫化物夹杂物组成和存在形式及其形貌、种类、尺寸、数量变化，以及相应的热轧、成品试样的微观组织和电磁性能变化。结果表明，随着钢中硫含量的增加，钢中的硫化物逐渐由 MnS→MnS+Cu₂S→Cu₂S转变，数量逐渐增多，尺寸向高低两个方向发展。相应地，导致热轧再结晶组织劣化和抑制了成品晶粒尺寸长大。随着钢中硫含量的增加，钢的磁感、铁损劣化程度逐渐增大。钢中的硫含量平均每增加 0.01%，涡流损耗、磁滞损耗分别劣化0.24 W/kg 和 0.41 W/kg，而磁感会劣化 0.009 T。但是 ，在硫含量为 0.010 2% 时 ，铁损可以低于 6.0W/kg，而在硫含量为 0.025 5% ... In order to find out the precipitation behavior of sulfide inclusions and the corresponding changes of microstructure and electromagnetic properties of high sulfur silicon steel sheets, so that to design more suitable sulfur concentration controlling limit for industrial manufacture and to release the steel-making difficulty effectively, Based on the change of given sulfur concentration 0.006 8%, 0.010 2%0.025 3% and 0.035 3%, the type and composition, the size and number, and the size distribut... 

通过制备磷酸二氢铝硅钢涂层,研究了氧化锌对无铬涂层耐盐雾性能、电化学性能和附着性的影响。结果表明,硅钢表面涂层含有4.0%的氧化锌时,涂层具有最高的耐腐蚀性能和电化学性能,而且其致密表面最为平整,没有裂纹出现。 The effects of ZnO on the salt spray resistance property, electrochemical performance and adhesiveness of silicon steel insulating coating were studied. The results show that the best corrosion resistance and electrochemical properties can be obtained when the coating contains 4.0% oxide zinc, and the dense surface is smooth without cracks. 

研究了无取向硅钢钙处理前后夹杂物的行为,重点考察了钙处理前后夹杂物的成分、类型、形貌和尺寸研究的变化情况,为实际生产中无取向硅钢的钙处理提供理论指导。试验发现:钙处理前夹杂物主要以Al2O3、Al2O3-MgO为主,且在夹杂物表面有AlN析出,钙处理后夹杂物以Al2O3-MgO-CaS-CaO系复合夹杂物为主,还含有少量的SiO2或AlN;钙处理前后,夹杂物形貌由多边形或不规则形逐渐向球形或近似球形转变,并且夹杂物尺寸不断增大;钙处理前后,含钙夹杂物的比例发生突变,由10%增大到74.5%,且随着钙处理时间的延长,含钙夹杂物比例下降,表明钙处理使夹杂物变性后易聚集长大并上浮去除。 Behavior of inclusions before and after calcium treatment in non-oriented silicon steel was researched by investigating changes of compositions,types,shapes and sizes of inclusions before and after calcium treatment,for the purpose of providing theoretical guidance for calcium treatment of non-oriented silicon steel in actual situation. Results indicated that Al2O3 and Al2O3-MgO were main types of inclusions before calcium treatment,sometimes AlN maybe precipitate in the outer of inclusions. Al2... 

通过金相分析和电子背散射衍射技术研究了一种新型含铜无取向电工钢在950℃退火不同时间(3～180s)空冷后的组织和织构取向的演变。结果表明:该钢在退火3s时的主要织构为α和γ线织构,{100}<110>织构最强;退火20s时织构以<111><112>、{111}<110>、{112}<110>、高斯织构和立方织构为主,随着退火时间的延长,高斯织构和立方织构强度呈减弱趋势;合理控制保温时间有利于提高{100}、{110}面织构的占有率。 Evolution of microstructure and texture oriented of a new non-oriented electrical steel during annealing at 950℃for different times(3-180) s and air cooling was studied by metallography and electron back-scattering diffraction analysis.The results show that after annealing for 3 s most of the texture oriented alongα-fibre andγ-fibre,the intensity of {100}〈110〉was the strongest.{111}〈112〉,{111}〈110〉,{112}〈110〉,Gauss texture and cube texture were the main texture after annealing for 20 s,with the ...