研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient... 

结合工业化生产的高效硅钢,进行了RH精炼稀土处理试验研究。针对不同的稀土处理条件,观察了夹杂物的形貌和尺寸分布,探讨了稀土处理后钢中的夹杂物形成、变化规律。结果表明:试验条件下,最佳的稀土合金添加数量为0.6～0.9 kg/t。经过合适的稀土处理后,可以有效抑制尺寸相对较小的、不规则的AlN、MnS复合夹杂生成,促进钢中微细夹杂物的聚合、上浮,钢质纯净度得到明显提高。此时,钢中全氧含量最低,脱硫效果最佳,钢中的夹杂物主要是尺寸相对较大的、近似球形或者椭球形的稀土类夹杂。 Based on the industrial production of non-oriented silicon steel,the experiment on RE treatment during the RH refining process was studied.The morphology and the size distribution were observed for the steel specimens treated with different RE treatment conditions.Further more,the formation and change of inclusions of final steel sheets after RE treatment were discussed.The results show that the suitable RE added amount was 0.6～0.9 kg/t.After the suitable RE treatment,the formation of AlN and Mn... 

研究了含铜低碳低硅无取向电工钢中的析出相及其析出机理.由能谱(EDS)及选区电子衍射(SAED)分析可知,铁素体基体上存在的大量弥散分布的等轴状析出相为类B2结构的铜.这些铜析出相的析出机理可以是一般析出、位错析出、台阶机理相间析出和弓出机理相间析出:一般析出在550、650和750℃三个等温温度均可发生;位错析出只发生在较低的等温温度(550℃),此时析出相呈特殊的平行短列状;台阶机理相间析出也可在上述三个等温温度下发生,但650℃等温时最有利于台阶机理相间析出,此时析出相平直列状分布;弓出机理相间析出只发生在较高的等温温度(750℃),析出相弯曲列状分布. Precipitates in low-carbon low-silicon non-oriented electrical steel containing Cu were studied and the precipitation mechanism was analyzed by means of energy dispersive spectrometry(EDS) and selected area electron diffraction(SAED).It is found that the equiaxed precipitates of Cu with B2-like structure distribute dispersively in the non-oriented electrical steel.The precipitation mechanism involves general precipitation,dislocation precipitation,interphase precipitations formed by the ledge me... 

介绍了国内、外电工钢极薄带的生产现状及市场应用的情况,以及典型生产企业的生产规模、产品性能和应用领域,指出扩大高牌号无取向电工钢生产、提高产品质量是目前电工钢发展的迫切要求。 The production situation and market application of ultra thin electrical steel strip at home and abroad were described.The production capability,product property and application area of typical corporation were introduced.The results indicate that the urgency needed of electrical steel development is expanding high-grade non-oriented electrical steel production and improving products quality at present. 

分别采用传统冷轧轧制液和纳米TiO₂的冷轧轧制液,对无取向硅钢板进行了四辊冷轧实验.重点研究两种冷轧轧制液的轧制润滑性能和对轧后硅钢薄带表面质量和耐蚀性能的影响.通过场发射电子显微镜和能谱仪对使用两种轧制液轧后得到的硅钢薄带表面形貌和成分进行了分析.给出了轧制液中TiO₂纳米粒子在轧制过程中的抗磨减摩机理.在轧制载荷较高时,纳米TiO₂轧制液具有优良的轧制润滑性能并能显著改善轧后硅钢薄带的表面质量.同时在高载荷作用下,TiO₂纳米粒子被压入硅钢薄带基体,形成一个滑动系来支撑载荷,从而使润滑膜的耐磨性提高. Non-oriented silicon steel strips were rolled on a four-high cold rolling mill lubricated by a traditional cold rolling liquid and a nano-TiO₂ cold rolling liquid,with emphasis on studying the rolling lubrication performance of both the liquids and their effect on the surface quality and corrosion resisting property of the silicon steel strips.The surface micrograph and composition of the silicon steel strips after being rolled with both the liquids were characterized by field emissio... 

【作者】 彭志华； ...

对碳-锰-硅钢进行不同配分温度的Q&P(Quenching and Partitioning)处理,测试了热处理后不同钢的力学性能和残余奥氏体含量,并用扫描电子显微镜和透射电镜观察其显微组织,分析了配分温度对显微组织和力学性能的影响。结果表明:试验钢显微组织基本由低碳板条状马氏体、块状铁素体和条状残余奥氏体组成;随配分温度的升高,试验钢的抗拉强度呈下降趋势,伸长率与奥氏体含量的变化趋势相同,但变化规律不确定;提高锰含量能稳定残余奥氏体,从而提高试验钢的伸长率,并使伸长率对配分温度不敏感。 The C-Mn-Si steel was quenched and partitioned at different partitioning temperatures,the mechanical properties and residual austenite contents were investigated,the microstructure was observed by SEM and TEM,and the effect of partitioning temperature on microstructure and mechanical properties was analyzed.The results show that the microstructure of the tested steel consisted of lath martensite with low carbon,nubby ferrite and banded residual austenite.The tensile strength of the tested steel ... 

对CSP流程生产的高磁感无取向电工钢50W1300在偏离轧制方向不同角度处的磁性能进行了测试和分析。结果表明:在偏离轧向不同角度处,磁性能差异显著,尤其在α=60°时磁感最低;偏离轧制方向不同角度处的磁性能大小取决于织构类型、强度及分布状态;增强{100}<0vw>和α、η取向的有利织构组分,降低不利的γ取向织构组分,且使有利织构组分分布越漫散,磁各向异性越小。 Magnetic properties of high magnetic induction non-oriented electrical steel 50W1300 produced by CSP processes were investigated with different direction in relation to the rolling direction.The result shows that magnetic properties are significantly different in relation to the rolling direction,in particular,the minimum magnetic induction occurs at 60° in relation to the rolling direction.Magnetic properties of different directions in relation to rolling direction depend on type and distributi... 

以轻烧氧化镁粉为原料,经消化、碳化制得重镁水,在热解反应前采用络合剂对重镁水中的杂质钙、铁进行络合掩蔽,再经热解得到碱式碳酸镁,碱式碳酸镁经煅烧可制得钙、铁杂质含量较低的氧化镁。在重镁水络合除杂过程中,考察了络合剂三乙醇胺、柠檬酸、草酸单独和复合使用的除铁、除钙效果。以三乙醇胺为络合剂时,在200 mL重镁水中加10 mL三乙醇胺(1∶1),氧化镁产品中w(氧化镁)=99.3%、w(氧化钙)=0.31%、w(氧化铁)=0.042%;使用草酸和柠檬酸作为复合络合剂时,在200 mL重镁水中加入1.0 g柠檬酸和2.0 g草酸,氧化镁产品中w(氧化镁)=98.2%、w(氧化钙)=0.24%、w(氧化铁)=0.030%。 Light-burned magnesia as a raw material was hydrated and carbonated to obtain magnesium bicarbonate liquor.Before the pyrolyzing of magnesium bicarbonate liquor,complexants were used to cover Fe and Ca impurities.Then the treated liquid was pyrolyzed to obtain basic magnesium carbonate which was calcined to magnesium oxide with low calcium and iron content.During the complexing purification of magnesium bicarbonate liquor,the Fe and Ca removing effects of single or compound complexing agents,suc... 

利用XRD和EBSD研究了长轴分别平行于轧向(RD)、横向(TD)和轧面法向(ND)的柱状晶样品在热轧、冷轧及退火过程中的组织、织构演变规律,并分别从几何诱导和取向诱导两个方面分析了晶界的交互作用.结果表明,热轧时由表面摩擦剪切作用引起的组织和织构梯度直接影响并遗传给后续冷轧及退火样品.热轧后,不同样品的初始晶粒形状各向异性差异消失,形成相同的各向异性晶界组织,但晶体学各向异性发生改变,导致随后冷轧、退火组织及织构的变化均不同于直接冷轧的柱状晶样品.研究中特别关注了对磁性能有利的{100}取向区域与晶界的关系. Columnar grains show their special characteristics of morphological and crystallographic anisotropies, and thus markedly influence the microstructure and texture evolution during rolling and annealing process in electrical steel. The rolling and annealing microstructure and texture of three columnar grained samples with the long axes arranged along different directions were investigated by means of XRD and EBSD techniques, and the effects of columnar grain boundaries were analyzed from the view ... 

采用X-射线衍射分析技术测定了取向硅钢热轧板在不同压下率下不同厚度处的织构。结果表明,在压下率低于80%的情况下,几乎所有试样的不同厚度处的织构均为旋转立方织构类型{100}<011>,但不同压下率、不同厚度处的织构强度存在很大差异;在压下率大于80%的情况下,不同试样的不同厚度处的织构类型发生了变化,其织构类型为旋转立方织构或高斯织构{011}<100>,且当织构类型为旋转立方织构时,织构强度存在很大差异,而当织构类型为高斯织构时,织构强度差异相对较小。 The texture of the grain oriented silicon steel hot rolled plate at different compressibility has been measured.The experimental results have shown that the texture of all samples at different thickness is {100}<011> when the compressibility is below 80%,and its intensity at different compressibility and thickness is difference.The texture of all samples at different thickness is variable when the compressibility is above 80%,it is {100}<011> or {011}<100>,and the intensity of ... 

无取向硅钢中夹杂物的存在会抑止晶粒生长,使基体的均匀连续性中断,其在钢中的形态、含量及分布情况都不同程度影响着硅钢的性能,尤其是对磁性能起关键的作用。因此,全尺度分布考察夹杂物对无取向硅钢夹杂物的研究极为重要。本实验确定了适用于不同牌号无取向硅钢夹杂物全尺度分布的分析方法:样品制备—小样电解—过滤喷金—根据不同牌号的要求选择合适的放大倍率扫描观测—夹杂物颗粒的分类统计。通过统计的结果,结合电解的失重量可以得到不同尺度的体积分布数据。实验分析了不同牌号和工艺无取向硅钢夹杂物的种类、形貌、大小和尺度分布,并初步考查了夹杂物与磁性能的关系,对无取向硅钢的工艺研究具有一定参考价值。 Inclusions in non-oriented silica steel could inhibit the growth of grain and cause discontinuity of micro-structure.The configuration,content and size distribution of inclusion have different effects on the performance of silica steel,especially significant on the magnetic property.Therefore,it is very useful to completely characterize inclusions with full size distribution in silica steel.In our research,full size analysis method for inclusion in silica steel had been established as follows: s...