6.5%Si电工钢是一种优异的软磁材料,织构对其磁性能影响很大。利用温轧工艺对6.5%Si电工钢热轧板进行不同压下率轧制,研究了温轧板织构随压下率的变化规律。实验结果显示,随着压下率的增大,{100}〈110〉、{110}〈100〉和γ纤维织构在薄板表层中的强度先增强后减弱,当压下率达到75%时,沿板厚方向形成3个组织区域:表层细晶粒区({110}〈100〉取向为主)、过渡层({111}〈110〉和{111}〈112〉变形晶粒区)和中心层(以拉长的γ纤维织构和{100}〈110〉取向晶粒为主),这种组织和织构不均性对后期织构的发展有重大影响。 6.5wt% Si electric steel has excellent soft magnetic properties,on which texture play important role.In this experiment,warm rolling technique was employed to investigate the effect of rolling reduction on texture.It was found that the density of {100}〈110〉,{110}〈100〉 and γ-fiber textures first increased and then decreased with increasing of the rolling reduction.At 75% reduction,the microstructure along the thickness of the sheet formed three zones,containing surface layer with {110}〈100〉 orien... 

研究了冷轧大压下量,950℃退火时间对一种新型含铜无取向电工钢晶粒度和织构的影响。结果表明,大压下量冷轧,随压下量的增加,退火晶粒向γ线聚集,形成强{111}<112>织构。提高冷轧压下率,退火织构{111}<100>,{110}<001>强度减弱,增加退火时间,退火织构{111}<110>,{100}<001>,{110}<001>强度变弱。采用87.5%冷轧压下率和950℃退火60 s,有利织构{100},{110}占有率最大。 The effect of annealing(950 ℃) time with high cold rolling reduction on grain size and texture of a new non-oriented electrical steel containing copper was investigated.The results show that for high cold rolling reduction,most annealed grains are oriented along γ-fibre with increasing cold rolling reduction ratio and strong texture {111}<112> is formed.With increasing the cold rolling reduction ratio,the intensity of annealed texture {111}<110>,{011}<100> decreases.With increa... 

一种厚度≤0.15mm无取向硅钢带，其组分及wt%为：Si：2.0～6.5%，Mn：0.13～0.40%，S≤0.020%，P≤0.020%，Als：0.15～0.9%，C≤0.010%；工艺：经冶炼、浇注成坯后热轧至中间坯厚度；冷轧；常温脱脂；光亮罩式退火；经碱洗后涂覆；分条。本发明在保证铁损P1.0/400£13W/kg,磁感B2000³1.5T下，还使钢带厚度公差不超过±0.005mm,最小叠装系数³0.92完全满足连续冲制要求。

本发明涉及电机生产技术领域，特别涉及一种电机定子硅钢片叠片工装平台，包括底板、放置板、整齐装置和清理装置，所述的底板上端通过支撑柱安装有放置板，放置板上端安装有整齐装置，放置板上设置有清理装置；本发明可以解决现有的工装平台在针对多个硅钢片进行叠片时，只能对一种尺寸的硅钢片进行叠片，不能根据硅钢片的直径和硅钢片上间隔孔的宽度进行相应的调节，因此不能实现对不同尺寸的硅钢片进行整齐的功能，降低了工装平台使用的灵活性问题。本发明所采用的整齐装置在一定范围内可以根据硅钢片的直径进行相应的调节，从而实现对不同尺寸的硅钢片进行整齐的功能，提高了工装平台使用的灵活性。

根据本发明的一个实施例的双取向电工钢板，以重量％计，所述钢板包含Si：2.0至4.0％、Al：0.01至0.04％、S：0.0004至0.02％、Mn：0.05至0.3％、N：0.01％以下且0％除外、C：0.005％以下且0％除外、P：0.005至0.15％、Ti：0.001至0.005％、Ca：0.0001至0.005％和Mg：0.0001至0.005％，余量包含Fe和其他不可避免的杂质，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的面积分数为60至99％，具有从{100}＆lt;025＆gt;起15°以内的取向的晶粒的面积分数为1至30％。

针对新能源汽车的发展，制备了含Ni固溶强化、含Cu析出强化以及含Ni+Cu复合强化3%Si无取向硅钢，研究了强化方式对无取向硅钢组织、织构和性能的影响。结果表明：固溶强化型无取向硅钢热轧板中形成了粗大{221}<221>晶粒，冷轧过程中剪切变形明显并在退火后形成良好再结晶织构。析出强化型无取向硅钢热轧板中心层形成γ取向粗大晶粒，在后续的加工中γ织构逐渐增强并最终得到相对细小的再结晶晶粒。复合强化型无取向硅钢热轧板中保留了强λ取向带状组织，退火后形成了有益的Goss织构和λ织构。固溶强化型与复合强化型无取向硅钢磁感应强度B₅₀分别达到1.742、1.688 T,高于析出强化型无取向硅钢的1.645 T。同时，复合强化型无取向硅钢高频铁损最低，其P_1.0/400和P_{1.0/1 000}分别低至20.97、82.69 W/kg,这与其较小的晶粒尺寸和织构改善有关。强度计算结果表明：Ni元素固溶强化对强度的提高有限，屈服强度为468 MPa,纳米Cu析出可显著提高屈服强度（强度增量约200 MPa）,且主要来自于模量强... For the development of new energy vehicles, 3%Si non-oriented silicon steel were processed by solid solution strengthening with Ni, precipitation strengthening with Cu, and composite strengthening with Ni and Cu. The effects of different strengthening methods on the microstructure, texture and properties of high-strength non oriented silicon steel were studied.The results show that coarse {221}<221> grains are formed in the hot rolled sheet of solution strengthened non-oriented silicon ste... 

本实用新型涉及切割设备技术领域，尤其涉及一种电工钢切片用切割刀架。其包括机架、升降架、第一输送辊、第二输送辊、升降块和切割装置；升降架和升降块均设置有两个；两个升降架均设置在机架上；两个升降块分别滑动设置在两个升降架上；第一输送辊的两端分别转动设置在两个升降块上；升降架上设置有用于驱动升降块移动的升降机构；第二输送辊转动设置在机架上，且第二输送辊位于第一输送辊的下方；机架上设置有用于驱动第二输送辊转动的驱动电机；第二输送辊上设置有用于驱动第一输送辊转动的传动机构；切割装置滑动设置在机架上；机架上设置有用于驱动切割装置移动的驱动机构。本实用新型能够方便对电工钢进行切割，且能够自动放卷。

本发明涉及含Cu无取向硅钢的生产方法，转炉炼钢，真空处理过后连铸成坯；铸坯化学成分：1.0≤Si/Cu≤3.0,3.0≤Si+Cu≤5.5％，S≤0.0015％，(Mn+Cu)/S≥3000，其他为Fe,Als,P以及不可避免的杂质元素；对铸坯进行粗轧；粗轧后的中间坯采用热卷机进行强制卷取，开卷后中间坯进入保温箱，控制保温箱内冷却速度≤5℃/s；进入保温箱的中间坯温度T1满足：1000‑(Si+Cu)×103≤T1≤1100‑(Si+Cu)×103；高压除鳞，精轧，层流冷却，卷取；连续酸洗；冷轧到目标厚度，成品退火，涂层；成品卷进行时效处理。成品卷具有较低的中高频铁损，高磁感和高屈服强度。

本发明涉及一种基于全流程数据的冷轧硅钢厚度控制方法、装置，该方法包括：针对某个冷轧钢卷，首道次默认使用监控AGC，在进入冷轧机工序生产之前，获取其前序全流程的生产工艺和质量数据，并进行预鉴定，若发现硅钢性能波动，则首道次额外再使用秒流量AGC；若发现硅钢厚度波动不剧烈，则首道次额外再使用前馈AGC。本发明无需人工干涉，采用上述规则在生产前就能自动确定最优的AGC生产模式，保证了硅钢产品厚度精度，避免硅钢厚度指标上的缺陷。

以一种新的Fe-Si合金制备工艺为出发点,研究了不同放电等离子体快速烧结工艺(SPS)和Si含量变化对Fe-Si合金材料显微组织与磁性能的影响。结果表明,在烧结温度为1 000℃时制备的Fe-6.5%Si合金(质量分数,下同)的综合磁性能较好,其在50Hz下的铁损为0.549W/kg,最大磁感应强度为0.124 3T,矫顽力245.6 A/m,磁导率0.338mH/m。另外,材料的最大磁感应强度随Si含量的增加显著增长,1 000Hz下,Fe-10.0%Si的最大磁感应强度可达到Fe-6.5%Si合金的5倍左右。 The effects of Si content and SPS technology on microstructure and magnetic properties of Fe-Si alloy material were studied in the paper.It shows that the magnetic properties are the best when the content of Si is 6.5wt% and the sintering temperature is 1 000℃,the iron loss is 0.549W / kg in 50Hz,maximum magnetic induction is 0.124 3T,coercive force is 245.6A / m and permeability is 0.338mH / m。And,the maximum magnetic induction increases significantly with the increase of Si.The maximum magneti... 

本发明提供一种改善表面麻点缺陷的薄规格中低牌号无取向硅钢及其生产方法，成分C≤0.0025％，1.2≤Si≤1.65％，0.25％≤Mn≤0.35％，0.06％≤P≤0.11％，0.1％≤Als≤0.2％，S≤0.0025％、N≤0.0025％，Ti≤0.0025％，其余为Fe及不可避免的杂质。与现有技术相比，本发明采用较低氢气浓度，防止炉内氧化铁皮还原，减轻碳套辊的腐蚀程度，减少碳套辊结瘤率，改善带钢表面质量；采用合理合金成分设计，提高带钢的力学强度，降低碳套辊结瘤对带钢表面的影响程度，改善带钢表面质量。产品厚度为0.35mm，板面麻点发生率降低，无手感，且辊身周长周期范围内麻点个数≤5个。

本实用新型公开了一种硅钢片制作用防止硅胶泄露结构，包括运行组件与固定密封组件，所述运行组件的内侧壁设有固定密封组件，所述运行组件包括板体、第一凹槽、壳体、硅钢片、支撑板、连接块、密封圈、防护板和通孔，所述板体的内侧壁开设有第一凹槽，所述第一凹槽的内部设有壳体，所述壳体的内侧壁设有硅钢片，所述硅钢片的两侧相互对称焊接有四个连接块，四个所述连接块相斥一侧均贴合于第一凹槽的内侧壁，本实用新型首先通过硅钢片两侧密封圈保障密封效果，设置的橡胶管起到二次密封防护作用，并借助其内部的弹簧及U型板实现防偏移的效果，最后一方面可以在壳体相邻组件内侧加胶并且提高其内部硅钢片的厚度，以此实现多重密封防漏。