硅钢资料

通过制备磷酸二氢铝硅钢涂层,研究了氧化锌对无铬涂层耐盐雾性能、电化学性能和附着性的影响。结果表明,硅钢表面涂层含有4.0%的氧化锌时,涂层具有最高的耐腐蚀性能和电化学性能,而且其致密表面最为平整,没有裂纹出现。 The effects of ZnO on the salt spray resistance property, electrochemical performance and adhesiveness of silicon steel insulating coating were studied. The results show that the best corrosion resistance and electrochemical properties can be obtained when the coating contains 4.0% oxide zinc, and the dense surface is smooth without cracks. 

本发明公开了一种控制无取向硅钢厚度稳定性的轧制工艺，涉及硅钢厚度控制方法领域。本发明通过降低硅钢精轧入口温度，并调节粗轧区域、精轧区域和卷取区域的生产参数，保证后续卷取工序的轧制稳定性及卷形质量，严格控制无取向硅钢的厚度稳定性。本发明提供的轧制工艺使硅钢的厚度命中率得到了明显提升，提升了后续冷轧工艺的轧制速度，轧制力波动减小，提高了产品质量。

本发明提出了一种控制磁畴结构来降低铁损的取向性电磁钢板的制造方法中，即使在实施了去应力退火的情况下，也能够保持铁损降低效果，并且在磁畴控制处理后磁通密度不会降低的方法。本发明的制造方法中，在取向性电磁钢板的表面，沿与钢板的轧制方向交叉的方向线状地照射周边比中心低的环状的强度分布的激光。

对新能源汽车以及驱动电机的现有市场和未来市场规模进行梳理分析，通过自建计算公式推导出我国2021年1-11月份驱动电机用电工钢的总量，进而预测未来10年中国新能源汽车驱动电机用电工钢情况，为无取向电工钢的生产和在电机中的应用提供有价值的参考。 The current market and future market size of new energy vehicles and traction motors were analyzed,and the total amount of electrical steels used in traction motors in China from January to November 2021 was derived by using self-built calculation formulas,and then the situation in the next ten years of electrical steel used in traction motors of new energy vehicles in China was predicted.It will provide a valuable reference for the production of non-grain oriented electrical steel and its appli... 

本申请提供了一种提高高磁感取向硅钢渗氮效率的方法，属于高磁感取向硅钢渗氮处理技术领域，包括所述高磁感取向硅钢按重量百分比包括：Si：2.8～3.4％、C：0.040～0.070％、Als：0.015～0.045％、Mn：0.06～0.14％、S：0.003～0.020％、N：0.003～0.010％、Cu：0.01～0.025％、Sn：0.03％～0.07％、Cr及Ni，Cr和Ni的总含量小于0.5％，其余为Fe和不可避免杂质物，其特征在于，控制脱碳退火后钢带表层氧化物中铁系氧化物的比例，该装置能够增加脱碳退火后钢带表面氧化层中铁系氧化物占整个氧化层重量的比例，从而在获得同等渗氮量的情况下实现了快速渗氮，缩短渗氮时间，提高渗氮效率。

本实用新型公开一种电机加工硅钢片上料装置，包括上料底座，上料底座的顶部固定连接有若干个硅钢片卷料限位柱，上述装置还包括设置在上料底座上方的上料顶座，上料顶座的底部固定连接有若干个与硅钢片卷料限位柱配合的定位柱，上料底座与上料顶座之间滑动连接有两个对称设置的滑动螺杆，滑动螺杆滑动连接所述上料顶座，滑动螺杆的上端螺纹连接有装配螺母，上料底座的左右侧壁部位均装配有第一折形板，上料顶座左右侧壁部位均装配有与第一折形板对称设置的第二折形板，第一折形板与第二折形板之间装配有悬吊组件。采用上述方式不仅实现将若干个硅钢片卷料采用一个夹持定位设备进行夹持定位，且上述装置部件设计安全上料。

本实用新型提供了一种带连接筋的硅钢盘，包括多个周向间隔排列的硅钢块，任意相邻的两所述硅钢块之间连接至少两连接筋，以将相邻的两所述硅钢块之间的空间分割为分设在所述硅钢盘轴向两侧的转子槽，及位于两所述转子槽之间的若干个收纳孔。多个所述硅钢块通过连接筋连接，并形成一整体的硅钢盘，相对现有技术独立成型多个硅钢块来说，不仅避免硅钢块丢失，还有效提升硅钢盘装配为转子盘的成型效率，以及保证各硅钢块在转子盘上的位置一致性，并且增加所述连接筋的数量，有效增强相邻两硅钢块的连接性能，从而大幅增强转子盘的机械可靠性。

研究了常化温度、常化时间及常化后冷却速度对Si的质量分数为1.6%的无取向电工钢成品磁性能的影响。结果表明:在850~1 050℃范围内,随着常化温度的升高,成品铁损先减小后增大,成品磁感应强度先增大后减小;当常化温度为1 000℃时,成品平均铁损最低,平均磁感应强度最高;常化时间从3min延长到7min时,成品铁损先减小后增大,成品磁感应强度则呈单调下降趋势;随着常化冷却速度的降低,成品铁损先减小后增大,成品磁感应强度则呈单调增大趋势;对于Si的质量分数为1.6%的无取向电工钢,最佳的常化制度为:在1 000℃进行常化,时间5min,常化后空冷。对热轧板进行常化后,热轧板发生了不同程度的再结晶和晶粒长大。提高常化温度、延长常化时间、降低冷却速度,都能使常化板晶粒粗化,进而粗化成品板晶粒,改善磁性能。通过扫描电镜观察发现,成品板中析出物主要为AlN和MnS的复合析出物,以及少量的单独析出的AlN和MnS,而常化工艺主要是通过粗化析出相,减少细小析出相数量,从而减少对晶界钉扎作用来改善成品磁性能。 The effects of normalizing temperature,normalizing time and cooling rate after normalizing on magnetic properties of non-oriented electrical steel with mass fraction of Si of 1.6% were investigated.The results show that core loss of product decreases first and then increases,while magnetic induction increases first and then decreases with the increase of normalizing temperature from 850 to 1 050℃.Average core loss of product is the lowest and average magnetic induction is the highest when normal... 

研究了冷轧95%变形量无取向硅钢不同退火温度(710～1 050℃)下再结晶织构特征.再结晶刚完成时(710℃退火),呈现强γ({111<112>～<134>)与弱{114}<481>织构特征;随退火温度升高至900℃,γ明显减弱,{114}<481>组分持续增强,形成典型的{h,1,1}<1/h,1,2>织构;进一步升温至1 050℃,再结晶织构不再发生明显变化.基于EBSD分析,{114}<481>组分的持续强化可归因于其明显的尺寸优势以及较高频率的高能晶界(取向差角为20°～45°). A non-oriented silicon steel was heavily rolled to 95% reduction and subsequently annealed at 710~1 050 ℃ to investigate recrystallization texture evolution.When annealed at 710 ℃ with complete recrystallization,the texture is characterized by a strong partial γ fiber spreading from {111}<112> to {111}<134> and a weak {114}<481> component.As annealing at 900 ℃,γ fiber is decreased significantly while {114}<481> is increased consistently,producing a typical {h,1,1}<1/h,... 

采用铸坯低倍组织检验和化学分析的方法,研究板坯连铸机二冷区电磁搅拌器电流和频率参数对无取向电工钢XG800WR板坯中心偏析和等轴晶率的影响,结果表明:铸坯等轴晶率随着搅拌器电流强度和电流频率的增大而增加。采用二冷区电磁搅拌可减小中心易偏析元素S的偏析,试验得出:减小铸坯S偏析效果最好的电磁搅拌参数为电流380～400A,频率6Hz。 The effect of electromagnetic stirring current and frequency parameter at secondary cooling area on the central segregation and equiaxed crystal ratio of XG800WR non - oriented electrical steels slab was investigated through the methods of chemical and macrostructure analysis.The results shows that the rate of equiaxed crystal zone is going up with increasing of current intensity and current frequency.Electromagnetic stirring in the secondary cooling area can be easily reduced segregation caused... 

利用EBSD技术研究了电工钢中长轴平行于轧向的柱状晶样品在热轧和退火过程中组织和取向的演变规律,并与长轴平行于板法向的样品的已有研究结果进行对比。结果表明,无论柱状晶按何种方向排列,只要表面存在剪切力,热轧后都可形成剪切织构,同时中心形成轧制织构,主要包括旋转立方织构和{112}<1-10>。柱状晶造成的影响主要体现在板中心层,长轴平行于轧向排列的样品热轧时形成的粗大旋转立方晶粒要到脱碳退火后才能完全消除,但破坏了正常的不同取向晶粒间的取向差分布及尺寸均匀性,导致二次再结晶不完全及磁性能降低。 The evolution of microstructure and grain orientation in an electrical steel containing columnar grains with its long axis being parallel to the rolling direction of sheet was studied during hot rolling and annealing by EBSD technique.The results are compared with those of samples containing columnar grains being parallel to normal direction of sheet reported in the reference [3].It was shown that,whether the long axis of columnar grains was arranged in RD or ND,shear textures can be formed in t... 

本实用新型公开了一种电机转子硅钢片用转运装置，包括电机转子主体，所述电机转子主体的下端设置有螺旋杆，所述螺旋杆的上端设置有轴承二，所属轴承二的上端设置有转轮，所述转轮的上端设置有铜电磁圈组件，所述铜电磁圈组件的一侧外表面设置有硅钢转子组件，所述硅钢转子组件包括固定环、组合安转管型组件、硅钢片、圆片、外齿、铜丝捆绑槽、凸出叠加圆环、上端对接圆环齿、对接齿槽、下端对接圆环齿，所述铜电磁圈组件的上端设置有转子压圈，所述转子压圈的上端设置有转换器。本实用新型所述的一种电机转子硅钢片用转运装置，具备安装拆卸简、散热性能好，易清理去除污渍等优点，带来更好的使用前景。