硅钢资料

【摘要】 <正>2014年5月9日,从武钢硅钢事业部获悉,...

对西昌钢钒炼钢厂200 t BOF(顶底复吹)-RH-CC工艺生产50PRW800无取向硅钢RH精炼过程中主要成份进行了分析。找出了目前工艺中影响钢液质量的主要因素是钢水脱氧处理不彻底,造成加入的部分硅元素烧损。操作工艺改为铝的脱氧即合金化操作一步完成,保证了钢水中氧处于一个较低的范围,从而减少对硅元素的烧损,提高合金收得率。 The factors of BOF-RH-CC process affecting the compositions of liquid steel were systematically investigated and studied of Xichang Steel and Vanadium Company. The main factors affecting the steel cleanliness were picked out. All results showed that the loss of silicon elements resulting from the deoxidization of liquid steel was not completely. It was suggested that the addition of aluminum for deoxidizing and alloying of molten steel was executed as one step in order to lower the oxygen potent... 

采用硅钢自动测量装置及X射线衍射仪检测出样品在实验前后的磁性能参数和织构强度.结果表明:较低的电压、9 Hz、较长的处理时间以及退火温度为650℃有利于增高铁损降低比例;较低的电压、较高的频率以及退火温度为650℃有利于增加磁感应强度增高比例.最佳的提高磁性能的实验参数是:频率为9 Hz,电压为500 V,处理时间为6 min,退火温度为650℃.通过织构分析可以验证:取向硅钢磁感应强度的变化取决于{110}<001>晶粒取向度值,而{110}<001>取向度值可看成是一个反映总体平均偏离角大小情况的综合值. An automatic measurement system for silicon steel and an X-ray diffraction meter were used for measuring the magnetic property parameters and texture of ex-processed samples and processed samples.It is shown that under the condition of a lower voltage,9Hz,a longer processed time and an annealing temperature of 650℃,the decrease rate of iron loss can be increased;a lower voltage,a higher frequency and an annealing temperature of 650℃ are in favor of improving the increase rate of magnetic inducti... 

以构建高磁感、低铁损、免轧制高硅电工钢铁芯为出发点,提出采用单辊甩带制备非晶铁硅合金薄带、微氧化法在铁硅合金粉末表面包覆高电阻率铁硅氧化物薄膜制备核壳异质结构高硅电工钢纳米粉末、放电等离子烧结快速成形制备颗粒间绝缘的高硅电工钢铁芯。研究了不同氧化包覆时间对SPS烧结试样密度、物相组成、微观结构和静磁性能的影响。研究表明,在氧化包覆5h烧结温度800℃工艺条件下,制备的6.5%Si高硅电工钢铁芯的静磁性能最佳,饱和磁化强度为128.84A.m2/kg、矫顽力为2.25kA/m、剩磁为3.47A.m2/kg。其饱和磁化强度与粉末压延法制备的高硅钢相当,但矫顽力降低了1/3。 The paper takes preparation 6.5%Si steel with high induction,low core loss and removing rolling as the starting point,amorphous Fe-Si ribbons was synthesized by melt spinning method,6.5%Si steel nanopowders with high resietivity core shell structure was prepared by the slight oxidation process and 6.5% Si steel iron core with evaluating internal was sintered by spark plasma sintering process(SPS).The essay focuses studies the effects of different oxidation cladding time on sample density,phase c... 

结合工业化生产的无取向硅钢,探讨了氧硫交互作用对钢中夹杂物生成的影响。借助非水溶液电解+扫描电镜法,研究了不同O、S含量下钢中夹杂物的变化规律。结果表明,本实验条件下,提高O含量、降低S含量,会劣化热轧组织再结晶效果。在劣化效果上,O的作用大于S;低Si、无Al硅钢中,应尽可能降低O含量、适当提高S含量,以粗化钢中微细夹杂物,减少尺寸小于1.0μm的夹杂物的数量;O、S含量与钢中夹杂物数量不具有关联性。生产过程中,不仅要严格控制O、S含量,还要严格控制生产工艺,以免生成较多的有害夹杂物。 Based on the industrial production of non-oriented silicon steel,the effects of interaction between oxygen and sulfur on the formation of inclusions were discussed.The change of non-metallic inclusions in steel sheets was investigated by means of electrolysis with non-aqueous solution under different oxygen and sulfur content.Results show that the recrystallization microstructure of hot rolled sheets will be deteriorated with the increase of oxygen content and the decrease of sulfur content.The ... 

【摘要】 <正>含6.5%Si的电工钢是软磁特性最佳的电...

以取向电工钢成分为基础,制备了含C或Mn和S的4种实验钢。观察了接近平衡析出状态实验钢经60%冷轧后在600～1000℃范围再结晶退火过程中微观组织演变,统计分析了再结晶体积分数随退火时间的变化规律,进而计算了各实验钢静态再结晶的激活能。观察了高含C实验钢退火初期再结晶晶粒优先出现的部位。结果表明900～1000℃范围内各实验钢铁素体的化学成分相似,因而其再结晶激活能基本一致。在600～800℃范围内铁素体内会有阻碍再结晶进程的三次渗碳体析出,从而使再结晶激活能明显提高。高C含量实验钢中还会有从奥氏体转变而来的粗大珠光体或渗碳体,轧制过程中其附近形成的变形区会促进600～800℃加热时该区域附近率先发生再结晶形核、降低再结晶激活能。固溶的Mn、S元素可微弱提高再结晶激活能,但高Mn、S含量会改变粗渗碳体从奥氏体析出时的形态。 Four experimental steels based on grain oriented electrical steel containing C,or Mn and S were prepared.Microstructure evolution of the steels close to a state of equilibrium precipitation were observed during annealing processes at 600-1000 ℃after 60% cold rolling,the changes of recrystallization volume fraction were analyzed statistically as the annealing was prolonged,and the activation energy for static recrystallization of the steels were calculated.The locations,where the recrystallizatio... 

采用轧制法制备出具有低铁损高磁感0.23mm厚6.4%(质量分数)Si高硅钢。沿轧制方向的最终磁性能为B8=1.474 T,B50=1.714 T;P10/50=0.30W/kg,P15/50=0.88W/kg。利用X射线衍射及背散射电子衍射(EBSD)技术分析了高硅钢在轧制及退火过程中的织构演变过程。结果表明,通过采用大压下率热轧,确保热轧板次表层中产生更多的高斯织构,随后进行遗传;温轧板中粗大的晶粒有利于冷轧剪切带的形成;冷轧板经脱碳退火后生成强{210}〈001〉织构及次表层较强的高斯织构是在轧向上获得高磁感的原因,归因于其在{111}〈112〉冷轧形变晶粒内的剪切带优先形核并长大;最终退火后虽出现了随机取向,但以{310}〈001〉织构为代表的η织构得以保留并且增强,进一步提高了磁感。随着退火温度的升高及保温时间的延长,高硅钢薄板晶粒尺寸不断增大,铁损明显降低。 6.4wt%Si high silicon steel sheets(0.23mm thick)with low iron loss and high magnetic induction were successfully produced by rolling process.The final magnetic properties along the rolling direction(RD) were:B8=1.474T,B50=1.714T;P10/50=0.30 W/kg,P15/50=0.88 W/kg.The texture evolution during rolling and annealing was investigated by means of X-ray diffraction and electron backscatter diffraction(EBSD).It was found that more Goss textures formed in the subsurface of hot rolled plates by using larg... 

介绍了国内、外电工钢极薄带的生产现状及市场应用的情况,以及典型生产企业的生产规模、产品性能和应用领域,指出扩大高牌号无取向电工钢生产、提高产品质量是目前电工钢发展的迫切要求。 The production situation and market application of ultra thin electrical steel strip at home and abroad were described.The production capability,product property and application area of typical corporation were introduced.The results indicate that the urgency needed of electrical steel development is expanding high-grade non-oriented electrical steel production and improving products quality at present. 

根据相关的取向电工钢典型专利技术,概述了日本高磁感低铁损取向电工钢低温板坯加热、抑制剂合理调节、关键成分Mn、C、Sn和Sb调节与利用、新型退火剂和绝缘溶液的制备及细化磁畴等生产工艺最新动态和进展情况,并提出了国内企业申请取向电工钢专利时应当借鉴之处。 According to related typical patent technology for grain-oriented electrical steel sheets,the recent trends and progress situation for production process of grain-oriented electrical steel sheets with high magnetic flux density and low core loss in Japan are summarized including low temperature slab heating,suitably regulating inhibitors,adjusting and utilizing key element Mn,C,Sn and Sb,manufacturing for new annealing agent and insulating solutions,and fining magnetic domain,and some suggestion... 

【作者】 韩超； 代智肄； ...

西安重型机械研究所为武钢开发了目前国内第一台自动化水平较高的先进可靠的硅钢热轧试验轧机。本文介绍了该轧机的工艺参数、设备组成,技术特点及轧制流程,该轧机在规定的终轧温度范围内,实现了2.5 m/s的快速轧制速度,保证了控制系统准确及时的采集到轧件进出轧辊时的信号,缩短道次间隙时间,实现了自动控制,保证了产品板形及精度的高水平要求,对于硅钢尤其是对其取向硅钢新产品、新工艺的开发具有深远意义。 An experimental prototype of 400 mm silicon steel hot rolling mill was developed by Xi’an Heavy Machinery Research Institue for Wu Gang.The technological parameters,configuration and characteristic of advanced control system in the experimental prototype are introduced in detail.The experimental prototype was realized the fast rolling of 2.5 m/s in the range of specified rolling temperature.Its automatic rolling control system can acquisite the signals that a rolled piece enters in and exits fro...