研究了薄板坯连铸连轧流程(TSCR)条件下热轧工艺对3.2%Si-0.7%Al无取向硅钢组织、织构演变及磁性能的影响规律。结果表明,提高均热温度和热轧温度有助于获得粗大的变形组织和强烈的{001}〈110〉织构,进而对后续的组织、织构演变进程及磁性能产生有利的遗传影响。与低温均热和低温热轧相比,高温均热和高温热轧得到的最终成品板的再结晶晶粒较粗大,λ纤维再结晶织构较强而γ纤维再结晶织构较弱,磁感应强度较高。 It was investigated that the effects of thin slab cast rolling(TSCR) hot rolling processes on microstructural,textural evolution and magnetic properties of 3.2%Si-0.7%Al non-oriented silicon steel.The results show that much larger hot rolling deformed microstructure and much stronger {001}〈110〉 texture could be obtained by increasing the soaking and hot rolling temperatures,which had good heritable effects on subsequent microstructural,textural evolution and magnetic properties.The final sheets ... 

【作者】 吴玉美； 陆晔； ...

采用铸坯低倍组织检验和化学分析的方法,研究板坯连铸机二冷区电磁搅拌器电流和频率参数对无取向电工钢XG800WR板坯中心偏析和等轴晶率的影响,结果表明:铸坯等轴晶率随着搅拌器电流强度和电流频率的增大而增加。采用二冷区电磁搅拌可减小中心易偏析元素S的偏析,试验得出:减小铸坯S偏析效果最好的电磁搅拌参数为电流380～400A,频率6Hz。 The effect of electromagnetic stirring current and frequency parameter at secondary cooling area on the central segregation and equiaxed crystal ratio of XG800WR non - oriented electrical steels slab was investigated through the methods of chemical and macrostructure analysis.The results shows that the rate of equiaxed crystal zone is going up with increasing of current intensity and current frequency.Electromagnetic stirring in the secondary cooling area can be easily reduced segregation caused... 

研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient... 

冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content、high addedvalue product. Its process is complex, Its production cycle is of Length, and Its Process control is difficult. Which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, Which Directly determines iron loss of the silicon steel and electromagnetic property, etc many index. 

结合工业化生产的无取向硅钢,进行了RH精炼喂CaSi线去除钢中的非金属夹杂物试验研究。针对不同的钙处理条件,分析了CaS夹杂生成热力学,观察了夹杂物的形貌和尺寸分布,确定了夹杂物的类型、数量,探讨了钙处理后钢中夹杂物的变化规律。结果表明,本试验条件下,钙处理可以有效抑制MnS、AlN夹杂物的生成,有效促进钢中微细夹杂物的聚合、上浮、去除,钢质纯净度明显提高。经过合适的钙处理后,钢中的夹杂物以独立存在的CaO为主,同时有少量含CaO、SiO2、MgO的复合夹杂,没有发现CaS夹杂存在。这部分夹杂物的尺寸集中分布在2～20μm,数量约为1.8×105个/mm3。 Experimental study on removal of non-metallic inclusions in non-oriented silicon steel obtained from industrial production by CaSi wire feeding during RH refining process was carried out.The thermodynamics of CaS inclusion formation was analyzed,the morphology and the size distribution of inclusions were observed,and the numbers and types of inclusions were also determined for the steel specimens treated under different calcium treatment conditions.Furthermore,the variation of inclusion characte... 

概述了高磁感取向硅钢生产工艺的研究现状及发展趋势。介绍了国内外薄板坯连铸连轧流程生产高磁感取向硅钢的研究现状。从流程工序特点、热履历、组织与抑制剂控制方面进行对比,分析了薄板坯连铸连轧流程相对传统板坯流程生产高磁感取向硅钢的技术优势,在此基础上提出了利用该流程生产高磁感取向硅钢需要解决的主要技术难点。 The current status and development trend of production process for high magnetic induction grain-oriented silicon steel are summarized.The research status of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process at home and abroad is introduced.The potential technical advantages of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process are obtained by analyzing in terms of process characteristics,t... 

对碳-锰-硅钢进行不同配分温度的Q&P(Quenching and Partitioning)处理,测试了热处理后不同钢的力学性能和残余奥氏体含量,并用扫描电子显微镜和透射电镜观察其显微组织,分析了配分温度对显微组织和力学性能的影响。结果表明:试验钢显微组织基本由低碳板条状马氏体、块状铁素体和条状残余奥氏体组成;随配分温度的升高,试验钢的抗拉强度呈下降趋势,伸长率与奥氏体含量的变化趋势相同,但变化规律不确定;提高锰含量能稳定残余奥氏体,从而提高试验钢的伸长率,并使伸长率对配分温度不敏感。 The C-Mn-Si steel was quenched and partitioned at different partitioning temperatures,the mechanical properties and residual austenite contents were investigated,the microstructure was observed by SEM and TEM,and the effect of partitioning temperature on microstructure and mechanical properties was analyzed.The results show that the microstructure of the tested steel consisted of lath martensite with low carbon,nubby ferrite and banded residual austenite.The tensile strength of the tested steel ... 

介绍了一种适用于超大晶粒取向硅钢的高斯晶粒取向偏离角的X射线衍射测量方法，提出了将试探法和探测器扫描法相结合的方式进行测量。结果表明：该方法可以同时获得准确的实际衍射角度和取向偏离角度，试样制备方式简单，对设备的要求低且测量结果准确。 This paper introduces a X-ray diffraction measurement method of Gaussian grain orientation deviation angle for ultra-large grain oriented silicon steel, and puts forward a method of combining the test method with the detector scanning. The results show that this method can obtain accurate actual diffraction angle and orientation deviation angle at the same time. The sample preparation method is simple, the requirements for equipment are low, and the measurement results are accurate. 

Fe-6.5%Si高硅钢是一种具有高磁导率、低矫顽力和低铁损等优异软磁性能的合金,但是其室温脆性和低的热加工性能严重影响了其在工业领域的应用。综述了Fe-6.5%Si高硅钢的性能,评述了合金的改性法、特殊轧制法、快速凝固法、沉积扩散法、粉末冶金法等制备工艺。 It is well known that 6.5%Si high silicon steel is one kind of soft magnetic materials with higher re-lative permeability,lower coercive force and iron loss than those of conventional industrial silicon steel.However,their room-temperature embrittleness and poor workability limit their practical applications in the industry.The pre-paration technique such as modification treatment on alloy,special rolling,rapid solidification,CVD and powder me-tallurgy is reviewed. 

以水氯镁石为原料,采用氨法沉镁-煅烧-添加剂的方法制备硅钢级氧化镁。考察了反应温度、反应pH值、陈化时间对中间体氢氧化镁纯度及转化率的影响;研究了煅烧温度和煅烧时间对氧化镁水化率的影响及添加剂的量对氧化镁悬浮性能的影响。控制实验条件为:反应温度55℃,pH值为9.5,陈化时间2h,煅烧温度1050℃,煅烧时间2h,添加剂量为0.8%,制得氧化镁的纯度为98.99%、水化率为2.92%、悬浮性能为3mm/h,达到硅钢级氧化镁的要求。 Using bischofite as raw material,the preparation of magnesium oxide with silico-steel grade was studied.The effects of reaction temperature,reaction pH value and aging time on the intermediate magnesium hydroxide purity and conversion rate were studied.Calcinations temperature,calcinations time relationship to the hydration rate of MgO and amount of additive to the suspension performance of MgO were investigated.The results indicated that the optimum technological conditions were as follows:reac... 

【作者】 潘恒韬； 刘涛； ...