两炉次无取向硅钢XG800WR（/%:0.003～0.004C、0.71～0.75Si、0.32～0.33Mn、0.004～0.007S、0.016P）的炼钢流程为铁水预处理（KR）-210 t顶底复吹转炉-钢包吹氩-RH脱碳精炼-230mm×1220 mm板坯连铸。53 t中间包钢水过热度为25～30℃,钢包到中间包采用长水口全程吹氩保护浇铸,中间包至结晶器采用浸入式水口浇铸。结果表明,在RH、中间包、结晶器过程中钢中总氧以及夹杂物数量和尺寸均明显降低;但在钢包到中间包过程T[O]、[N]和钢中夹杂物数量增加,说明长水口浇铸过程存在二次氧化。连铸坯中T[O]、[N]平均他分别为11×10^-6和30×10^-6,显微夹杂物数量平均为4个/mm²。铸坯中的显微夹杂物主要为3～5μm的AlN,同时存在少量的MnS、Al₂O₃·AlN和Al₂O₃·MgO·MnS。 The steelmaking flow sheet for two heats non-oriented silicon steel XG800WR（/%:0.003～0.004C. 0.71～0.75Si,0.32～0.33Mn,0.004～0.007S,0.016P） is hot metal pretreatment（KR）-210 t top and bottom combined blown converter-ladle argon blowing-RH decarburization refining-230 mm×1 220 mm slab casting.The superheating extent of liquid in 53 t tundish is 25～30℃,whole casting is shielded by blowing argon with long nozzle from ladle to tundish and the submerged nozzle is adopted in casting from tundish to mold... 

【作者】 朱传芳； 潘恒韬； ...

对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ... 

介绍了硅钢氧化镁制备方法及高质量硅钢氧化镁制备技术的研究进展,并对利用我国丰富的卤水资源制备硅钢氧化镁进行了展望。 The preparation methods of silicon steel magnesium oxide and research progress of high quality silicon steel magnesium oxide preparation technology were introduced.The use of abundant brine resources in the preparation of silicon steel magnesium oxide was prospected. 

取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加铜可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布。利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧(TSCR)工艺的3种不同铜含量的取向硅钢热轧板织构。结果表明:不同铜含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;铜含量约在0.4%时,热轧板次表层的{110}<001>织构比例最高,而热轧板心部的{100}<110>织构比例最低;铜含量对热轧织构中{114}<110>和{001}<100>织构发展有显著影响。 The texture gradient in hot rolled grain oriented silicon steel strip is one of the essential factors to achieve a perfect secondary recrystallization.The addition of copper can significantly reduce the slab reheating temperature of grain oriented silicon steel,so as to impact the texture distribution in the hot rolled strip.The texture of hot rolled grain oriented silicon steel strip as-rolled by thin slab casting and rolling process(TSCR) in laboratory with three different copper contents was ... 

主要对硅钢退火炉耐材施工进行阐述,对一期工程与二期工程施工经验进行总结,包括设计、施工、耐材生产、人员素质等方面,指出了工程项目所所存在的不足,为同类型炉窑的施工提供借鉴。 This paper describes the construction of silicon steel annealing furnace refractories;and it was summarized the construction experience of phase-Ⅰ and phase-Ⅱ projects,including design,construction,refractory production,the quality of personnel etc,and pointed out the shortcomings of the project,which provided a reference for the construction of the same type of furnaces. 

通过热力学计算,分析了实验钢中主要析出物析出的可能性。结果表明:在液相和固液两相区中,AlN和MnS均不能析出;在奥氏体区,AlN和MnS具备热力学析出条件,平衡析出温度分别为1547、1582 K。成品退火板中的析出物主要为AlN和MnS。扫描电镜下观察到的AlN形貌多为长条状,MnS形貌多为棒状或近似球形。这两种析出物占了析出物总量的85%以上,尺寸集中分布在400~800nm;复合析出物主要是(Al2O3+MnS)和(AlN+MnS),形貌不规则,尺寸集中在0.7~1.5μm;透射电镜下观察到了少量100nm以下独立的AlN析出。 According to thermodynamic calculation, the precipitation probability of precipitates was analyzed, AlN and MnS can not precipitate in liquid phase area and solid-liquid two-phase area. In austenite area, both the AlN and MnS have precipitation condition in thermodynamics and precipitates at 1547 K and 1582 K, respectively. The precipitates in annealing plate are mainly AlN and MnS. The shape of AlN is mostly strip, and MnS is stick or near sphericity. They accounted for over 85% of the total qu... 

对两种硅钢水溶性极厚绝缘涂层进行了不同温度的热老化实验。通过TG-DTA,GDS,FT-IR,SEM和光泽度仪等测试方法对老化的涂层进行分析表征,提出了评估硅钢水溶性极厚绝缘涂层热老化性能的合理温度区间,探讨了涂层热老化行为,并分析了两种涂层热老化性能的差异。结果表明,涂层附着性随着老化时间的延长逐渐下降。FT-IR表征结果显示,热老化过程中,涂料交联形成的化学键未发生断裂,交联剂氨基树脂的三嗪环被破坏是聚合物三维网络结构坍塌的主要原因。 Thermal aging expriments at different temperature were carried out on two types of water-soluble and extra-thick insulation coatings for non-oriented silicon steel,and a series of test methods such as glossmeters,TG-DTA,FT-IR,GDS,SEM were applied in analysis.For evaluating the thermal aging effect of this kind of insulation coating,the proper temperature range was proposed.The difference of aging performance between two coatings was been investigated and the related behaviors were been discussed... 

实验室模拟薄板坯连铸连轧(TSCR)流程制造高磁感取向硅钢,借助电子背散射衍射(EBSD)技术对不同Sn含量的热轧板织构进行了研究。研究结果表明:不同Sn含量热轧板表层及次表层均为高斯织构、铜型织构及黄铜织构的混合织构,中心层为{100}面织构;Sn含量为0.1%时,热轧板表层及次表层高斯织构组分最多,取向密度最大,成品磁感最高,达到1.875 T。 Texture of grain oriented silicon steel hot rolled by thin slab casting and rolling process(TSCR) in laboratory with different Sn contents was analyzed by electron back-scattered diffraction(EBSD).The results show that the hot rolled slabs with different Sn contents have the same texture,i.e.,Goss,Copper and Brass.Specifically,the texture of core layer is {100};While the hot rolled slab with 0.10% Sn,the surface layer and subsurface layer have a sharpness Goss texture and the finished products h... 

采用XRD、SEM和激光粒度仪等手段,观察并研究了不同特性氧化镁在硅钢表面形成硅酸镁底层形貌特点,并结合热力学和差热-失重分析了MgO-SiO2的反应机理。研究结果表明:粒度小,活性值高的特种氧化镁在高温退火过程中与基体表面氧化物生成的硅酸镁底层,界面中硅酸镁底层嵌入基体较多,表面致密,颗粒细小,有利于形成附着性能优良的硅酸镁底层。 Surface microstructure of Mg2SiO4 coatings formed on the surface of oriented silicon steel coated with different kinds of MgO was investigated by XRD and SEM.The reaction mechanism between MgO and SiO2 was analyzed by TG-DSC and thermodynamic calculation.Results revealed that when the MgO with finer microstructure size and higher activity is employed,a dense Mg2SiO4 layer with finer microstructure and good binding to the steel substrate can be obtained.The results are very helpful for the prepar... 

取向硅钢利用析出物作为抑制剂,抑制初次再结晶晶粒的长大,抑制剂是取向硅钢发生二次再结晶的基本条件之一。文中通过低温板坯加热技术制备取向硅钢,采用透射电镜(TEM)观察并研究了高温退火阶段抑制剂的演化过程。结果表明,渗氮后形成的非晶态Si3N4析出物不稳定,在700～750℃退火升温阶段转化为(Al,Si)N;(Al,Si)N颗粒在800℃发生团聚,随后长大并粗化;(Al,Si)N是低温取向硅钢主要抑制剂,随退火温度的升高,(Al,Si)N抑制力大幅下降。 Precipitates as inhibitor are used to inhibit the grain growth of primary recrystallization in grain-oriented silicon steel,and inhibitor is one of the basic conditions for occurring of secondary recrystallization.The grain-oriented silicon steel was produced by low temperature slab heating and nitriding technique.The evolution of inhibitor was observed by transmission electron microscopy.The results show that Si3N4 particles are precipitated after nitriding,and Si3N4 particles are amorphous and... 

【摘要】 <正>国家硅钢技术研究中心自2008年落户武...