硅钢资料

近年来，在节能减排背景之下，国内外众多研究者对无取向电工钢磁性能的提升做了大量研究。为了探索无取向电工钢磁性能提升的方法，对锡或锑对无取向电工钢磁性能的作用机制(晶粒尺寸和晶体织构的控制)进行分析。基于该作用机制，介绍锡或锑的添加对无取向电工钢磁性能的影响。经研究发现，适量的锡或锑在晶界偏聚，不会阻碍晶界的移动并且致使晶粒尺寸降低；与此同时，锡或锑在晶界偏聚不仅抑制{111}织构在原始晶界处形核及生长，还降低(100)晶粒表面能，促进(100)晶粒生长。因此，适量添加锡或锑，可使无取向电工钢铁损下降、磁感提升。最后结合生产工艺，建议无取向电工钢的研究方向应为稀土含量对高牌号无取向硅钢夹杂物尺寸和数量分布的影响，锡或锑的添加量和常化工艺参数(常化时间、常化温度)对常化晶粒尺寸的影响。 In recent years, due to the background of energy saving and emission reduction, numerous researchers all around the world have done a lot of investigations on the improvement of magnetic properties for non-oriented electrical steel. In order to explore the method of improving the magnetic properties of non-oriented electrical steel, the mechanism of tin or antimony on the magnetic properties(the control of grain size and crystallographic texture) of non-oriented electrical steel is illuminated. ... 

在15 kg真空感应炉上,用CaO-Al2O3-SiO2-MgO渣系进行脱硫试验,探讨了脱硫渣系碱度、MI、Al2O3、CaF2对脱硫效果的影响。研究结果表明,随脱硫渣系碱度、MI、Al2O3和CaF2含量的增加,脱硫率都呈现先增加后减少的趋势。初始硫含量为0.009 33%~0.010 73%,加入脱硫渣系4 min时间内表观脱硫速率为(0.000 96~0.001 49)%/min,平均脱硫率为81.2%,最高达86.8%。当脱硫渣中w(CaO)=58.15%、w(SiO2)=4.85%、w(Al2O3)=25%、w(MgO)=6%、w(CaF2)=6%,脱硫效果最好,此时钢液中硫为0.001 33%。 Experiments on desulfurization of molten steel using CaO-Al2O3-SiO2-MgO based desulfurization slag was carried out in a 15 kg vacuum induction furnace. The effects of desulfurization slag basicity,MI, Al2O3and CaF2on desulfurization of molten steel were studied. The results show that with the increase of basicity,MI,Al2O3or CaF2in desulfurization slag,the desulfurization rate rises initially and then decreases. In addition,as the initial sulfur content is 0. 009 33% ~ 0. 010 73%,the apparent des... 

借助高温激光共聚焦显微镜,在线观察了不同Mn含量的无取向硅钢中夹杂物的尺寸、类型、数量变化。结果表明,Mn含量(质量分数)为0.77%、0.32%时,试样中的夹杂物数量分别约为1000万个/mm3、1600万个/mm3。Mn含量较高的钢种,会优先析出球形、椭球形MnS夹杂物,其析出数量较少,尺寸相对较大,可以有效抑制AlN、CuxS夹杂物析出;Mn含量较低的钢种,会在试样再加热后冷却过程中,先析出相当数量MnS夹杂物,并作为AlN夹杂物析出核心,形成MnS+AlN复合夹杂物。这种复合夹杂物数量较多,尺寸也较大。 Based on the high temperature confocal microscope, the chage of size, type, and quantity of inclusions in non-oriented silicon steels with different Mn content were observed by in-situ SEM. Results show that the inclusion quantities are 10 million per mm3 and 16 million per mm3,while the mass fractions of Mn are 0.77% and 0.32%, respectively. In the silicon steel with higher Mn content, the spherical and ellipsoidal MnS inclusion will precipitate first, which can retard the precipitation of AlN ... 

对低温加热工艺生产的普通取向(common grain-oriented,CGO)硅钢的高温退火过程进行了中断实验,材料为含3.0%Si、0.5%Cu、0.009 8%S(均为质量分数)的以Cu2S为主抑制剂的普通取向CGO钢。原始板坯厚度为230 mm,于1 200℃均热后经4道次粗轧、7道次精轧至2.3mm;热轧板采用两次冷轧法轧至0.3mm,中间完全脱碳退火,最后于1 200℃高温退火。最后样品的磁性能:铁损P17/50为1.182W/kg,磁感应强度B8为1.897T。借助配有EDAX OIM电子背散射衍射(EBSD)系统的ZEISS SUPRA 55VP扫描电子显微镜,对高温退火过程中高斯晶粒的演变进行了研究,结果表明:升温过程中晶粒尺寸增长缓慢,650℃时取向分布函数(ODF)图出现高斯织构组分,但强度很弱,高斯晶粒偏离角小于9°;950℃时高斯晶粒平均生长速度超过其他晶粒;950~1 000℃时高斯晶粒异常长大,偏离角降至约3°;在950℃之前高斯取向晶粒相比于其他晶粒没有尺寸优势。 The high-temperature annealing process of common grain-oriented(CGO)silicon steel was investigated by interrupting test.The samples were rolled from CGO silicon steel slab under low reheating temperature.The CGO silicon steel,taking Cu2S as the main inhibitor,contains3.0%Si,0.5%Cu,and 0.0098%S.The original casting slab is 230mm in thickness.After 1 200℃reheating,four-pass rough rolling and seven-pass finish rolling were conducted to make the thickness of the slab get to 2.3mm.Then the hot rolled... 

利用场发射扫描电镜观察了以MnS为主要抑制剂的普通取向电工钢加工过程中第二相粒子的分布状态,统计了粒子面密度、平均尺寸以及相应的尺寸分布.结果显示,热轧加工造成了大量第二相粒子弥散、细小地析出,同时基体仍保持过饱和状态.冷轧变形会造成第二相粒子的回溶行为,而基体的过饱和状态会减弱回溶现象.中间退火与脱碳退火过程中会同时存在新粒子的形核及已析出粒子的粗化两个过程,而在最终二次再结晶升温阶段则以第二相粒子明显粗化为主. The distribution of second phase particles in conventional grain-oriented electrical steels during manufacturing processes with MnS as inhibitors was observed by field emission scanning electron microscopy,while the areal particle density,the average particle size and the corresponding size distribution were statistically determined.It is indicated that hot rolling leads to dispersive precipitation of a large amount of fine second phase particles and the matrix keeps a supersaturated state furth... 

通过对激光粒度分析仪测量硅钢级氧化镁(MgO)的分析条件进行优化,如分散介质、分散方式、样品预处理、仪器暗淡度等,探讨了硅钢级MgO粒度范围测量重现性较好的试验方法,满足硅钢生产过程控制对MgO粒度的要求。 The analysis condition of the laser particle size analyzer on grain oriented silicon-steel grade magnesium oxide is optimized,including the dispersion medium,dispersion methods,sample preparation,and instrument obscuration,etc.Therefore,particle size measurement with good reproducibility for silicon-steel magnesium oxide is discussed,which may meet the requirement of MgO particle size for silicon-steel process control. 

某冷连轧机生产无取向硅钢板材时,其边缘降的长度合格率频繁超标。为满足用户的叠片厚度精度要求,这类产品必须以增大切边量的方式来保证交货质量,而这种方式又直接降低了金属收得率,提高了生产成本。基于此,以该产线现有设备特性为基础,详细分析其软、硬件功能模式,分别对辊形与反馈控制进行全面分析与优化改进。通过现场试验论证,充分明确依托辊形优化与反馈控制程序的改进能显著提高边缘降的控制水平,该技术的使用为生产现场的边缘降控制提供了合理的技术支撑。 A cold rolling mill production of non-oriented silicon steel sheet,the thickness difference of the edge( edge-drop) is usually exceed the preset standard value,In order to meet the accuracy requirements of the user flatness,these production must be trimed wider length to meet the delivery quality of the user need, which directly reduce the metal yield and increase the manufacturing cost. Therefor,the software and hardware of the production line has been analyzed, and the work roll shape and feed... 

【作者】 周威； 刘侃； ...

通过对辉光放电发射光谱法分析电工钢样品光谱行为的研究,分析其工作参数如:电压、电流、预溅射时间和积分时间对光谱强度和稳定性的影响,并以铁为内标元素,优化了工作参数。确定了直流辉光放电光谱法测定电工钢中碳、硅、锰、磷、硫、铬、镍、铜共8种元素的定量分析方法,并对该方法分析的精密度和准确度进行验证,结果表明,各元素的测定结果与认定值和其他方法测定值一致,测量元素结果RSD值小于2%。 Based on research on analyzing the spectrum behavior of the sample taken from the electrical steel by glow discharge optical emission spectrometry,the effect of its operational parameters such as current,voltage,pre-sputtering time and integrating time on the spectral intensity and spectral stability is analyzed.Taking the Fe as an element applied by internal standard method,these operational parameters are optimized,and therefore the quantitative analysis method for testing eight kinds of eleme... 

对RH法(真空循环脱气法)生产的冷轧硅钢的脱硫原理及影响因素进行了分析研究。研究表明:降低顶渣中FeO、MnO的含量,提高钢液温度,增加脱硫剂的加入量并延长其循环时间有利于提高脱硫效率。 The principles of desulfurization and its influence factors of cold rolling silicon steel during RH process have been studied in this paper.The result indicated that reducing contents of FeO and MnO,rising temperature of the liquid steel,increasing quantity of desulfurizer,lengthening cycle time of desulfurzer are benefit for desulfurization. 

【摘要】 <正>2012年3月29日中国钢铁工业协会在上...

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。 Microstructure development and texture evolution of conventional grain oriented silicon steel,which were annealed at same annealing temperature and different annealing time under wet H2 atmosphere,were investigated through metallographic observation and electron backscattered diffraction analyzing.The results show that the primary recrystallization finishes in 120 s at 820 ℃ under wet H2 atmosphere.With the extending of annealing time,{111}<112> texture decreases,{111}<110> texture d...