研究了锰含量对w(Si)=1.8%Si无取向电工钢组织和性能的影响。结果表明,钢中锰含量从0.3%增加到1.2%时,由于α_γ相变的产生,铸坯低倍组织、热轧板金相组织及成品织构等均发生了不同程度的变化,对成品表面质量及磁性能产生了明显的影响。 The effects of manganese content on structure and properties of w(Si)=1.8% non-oriented electrical steels have been studied.Results show that with increasing manganese content to 1.2% from 0.3%,macrostructure of continuous casting slab,hot rolled band metallurgical structure and finished product texture vary in some extent because of the occurrence of α-γ phase transformation,the surface quality and magnetic properties of finished product are affected greatly. 

针对节能电机对无取向电工钢在磁性能方面的特殊要求,采用普通W600牌号的热轧板为原料,通过大量的现场工艺试验,研究总结出了\"超低张力\"的运行工艺、\"先快后慢\"的加热工艺、\"先湿后干\"的退火脱碳工艺、\"先缓后急\"的冷却工艺,生产出P1.5/50≤4.0 W/kg、B50≥1.70 T的冷轧电工钢产品,满足了节能电机的要求。 Based on the special requirements of no-oriented electrical steel for saving energy motor in magnetic aspects,using common W600 brand of hot rolled plate as raw material,through a large number of real tests,an ultra-low tension process,heating process which was quick at first and then slow,annealing decarburization process which was dry after the first wet,and a cooling technology of \"slow after the first urgent\" were concluded.Electrical steel product with P1.5/50≤4.0W/kg,B50≥1.70T was produced... 

【作者】 张正贵； 李战库； ...

为了确定普通冷轧取向硅钢最优的中间完全脱碳退火工艺,在其一次冷轧后进行5种不同工艺的脱碳退火处理,借助扫描电镜及电子背散射衍射技术研究了不同工艺脱碳退火后的组织、织构和脱碳效果。结果表明:经5种工艺脱碳退火处理后,初次再结晶的平均晶粒尺寸均约为19μm,且不随退火温度和时间的变化而变化;经840℃×10min工艺退火后的晶粒最均匀,高斯织构位向更准确,高斯织构面积分数最多,为3.1%,可将碳脱至0.003 5%。 In order to determine the optimal intermediate complete decarburizing annealing processes for common grain-oriented(CGO)silicon steel,five kinds of intermediate decarburizing annealing processes were conducted,the microstructure,texture and decarbonization after different decarburizing annealing processes were studied by scanning electron microscopy and electro back-scattered diffraction(EBSD)technology.The results show that the average grains sizes of primary recrystallization were about 19μm a... 

通过测试取向硅钢不同工艺条件下的碳含量,探讨了CGO取向硅钢碳含量控制的最优处理条件,研究了脱碳温度和脱碳时间对相同初始碳含量取向硅钢的脱碳效果的影响。结果表明,在气氛为(15%~20%)H2+(75%~80%)N2,炉压差为10~20 Pa的条件下,CGO取向硅钢合适的脱碳温度为1 073 K~1 123 K,脱碳时间为10~20 min。在该处理条件下,能取得较好的脱碳效果。 By means of testing carbon content of oriented silicon steel below the distinct technical conditions,inquires the excellent handle terms of carbon content controlling for CGO oriented silicon steel,studies effects of decarburization annealing temperature and decarburization annealing time to the oriented silicon steel decarburization efficiency in same initial carbon content.The results show that,under the condition of atmosphere(15% ~ 20%) H2+(75% ~ 80%)N2 and furnace pressure difference 10 ~ 2... 

采用固溶强化、细晶强化和位错强化方法,模拟TSCR流程试开发高强度无取向电工钢,试开发钢的主要合金成分为3%Si、0.83%Al和2.99%Mn。分析热轧、常化、退火后的钢板组织,并针对不同的成品板组织,详尽地分析了相应的力学性能和磁性能。试验电工钢平均晶粒直径为12.37μm时,R p0.2为530 MPa,R m为618 MPa;当退火制度为700℃×4 min,成品组织完全为未再结晶的回复组织时,R p0.2为853.5 MPa,R m为895.5 MPa。该成分的电工钢P15/50或P10/400最小时,对应的平均晶粒直径都大于59.67μm;P10/800或P10/1000最小时,对应的平均晶粒直径都处于12.37~59.67μm尺寸区间。 TSCR was simulated to develop high-strength non-oriented electrical steel with 3% of Si,0.83% of Al and 2.99% of Mn by solution strengthening,grain refinement strengthening and dislocation strengthening.The microstructures of hot rolled plates,normalized plates and annealed plates were analyzed.Furthermore,the mechanical properties and magnetic properties of products with different microstructures were detailedly studied.As the average grain diameter of the steel was 12.37 μm,the yield strength ... 

【作者】 朱传芳； 潘恒韬； ...

对低温法生产的以AlN为主抑制剂的Hi-B取向硅钢高温退火过程进行了中断实验,借助EBSD及TEM技术对高温退火连续升温过程中织构与析出物的演变进行了研究。实验结果表明,800℃时ODF图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;950~1 000℃时高斯晶粒异常长大,偏离角3~6°;高温退火过程析出物主要有球形、规则立方形及不规则多面体形3种形貌,由于渗N的影响,Zener因子先增大再减小,并且析出物在高斯晶界前沿优先粗化。 The annealing process at high temperature of Hi-B silicon steel using low slab reheat temperature and with AlN as the inhibitor has been studied by interrupting test,and the evolution of texture and precipitates during continuous heating-up in the annealing process at high temperature was analyzed by EBSD and TEM. The results showed that Goss texture appears in ODF at 800 ℃,but the intensity of Goss texture was very weak and the deviation angle was more than10°. Goss grains grow abnormally durin... 

借助实验室设备研究了B元素对高牌号无取向硅钢热轧板组织和磁性能的影响。结果表明,与无硼钢相比,含硼钢的热轧板晶粒尺寸略小,析出物的类型和尺寸没有区别,主要是AlN和(AlN+MnS)复合析出物,少量的MnS析出物,尺寸集中在1.0～2.5μm范围内。未发现BN析出物。在力学性能方面,B对钢的软化作用不明显。在磁性能方面,含硼钢的铁损为3.215W/kg,磁感为1.710T,综合磁性能比无硼钢差。 Influences of boron on microstructure and properties of hot rolled band in high-grade non-oriented silicon steel are researched in this paper by experimental equipments.Compared with boron-free steel,the result shows that boron-bearing steel has smaller grain size,but the type and size of precipitations have no differences.The main precipitates are AlN,(MnS + AlN) composite precipitate and few MnS,the range of which are between 1.0 μm and 2.5 μm.BN precipitation is not found.With reward to mecha... 

【作者】 潘恒韬； 刘涛； ...

通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 

对高牌号无取向电工钢35W300的成品进行了第二次退火,对第二次退火后的成品性能、纵横向磁性能差异和组织变化进行了分析。结果表明,随着第二次退火温度的升高,晶粒长大,磁性能优化。铁损平均值下降0.087 5W/kg,磁感平均值升高0.008T。第二次退火温度为820℃的产品的磁性能能够满足用户使用要求。 The product of high grade non-oriented electrical steel 35W300 was annealed at the second time.Microstructure,the difference of magnetic properties in the vertical and horizontal and were studied.The results show that the grain grew up and magnetic properties optimized with the increase of annealing temperature for the second time.Iron loss average declines in 0.0875 W/kg,magnetic induction average increases 0.008 T.The magnetic properties can meet the requirements of users at the second anneali...