对商用50W330型无取向硅钢成品在930℃下保温2 h固溶并以不同方式冷却处理,利用磁性检测仪检测分析了处理前后的磁感和铁损变化,应用光学显微镜、扫描电子显微镜、X射线衍射仪观测分析了显微组织结构的演变。考察了平均晶粒尺寸、织构组分比及第二相粒子状态对磁性能的影响规律,结果表明:固溶处理前后平均晶粒尺寸的变化对硅钢磁性能的影响非常显著;当平均晶粒尺寸相差不大时,织构组分比[Goss+{100}]/{111}越大,磁感会越高;固溶处理会将细小弥散的第二相粒子重新回溶到基体中,减小了其对磁畴壁的钉扎作用,铁损随之下降。 The commercial 50W330 non-oriented silicon steel samples were heat treated at 930℃ for 2 h and cooled in different ways,then the iron loss and the magnetic induction of the samples before and after solution treatment were measured with a magnetic detector.The evolution of microstructural texture was analyzed by optical microscopy,scanning electron microscopy and X-ray diffractometry.The effects of average grain size,texture composition ratio and the second phase particles on the magnetic propert... 

【作者】 陈迪安； 李春生； ...

利用加热炉模拟、动态再结晶以及热模拟等试验方法以及扫描电镜、金相显微镜等分析观察手段对无取向硅钢边裂的成因进行了探讨。结果表明,长时间加热使得板坯边部晶粒异常长大,晶界氧化并脱碳,轧制过程中边部温度过低,动态再结晶过程变弱,使得板坯边部延伸性能变差,是导致硅钢边裂的主要原因。建议通过适当降低铸坯加热温度、缩短保温时间、提高终轧温度来改善硅钢边裂缺陷。 The behaviors of high temperature oxidation,dynamic recrystallization,and hot ductility,microstructure evolution were investigated on the non-oriented electrical steel sheets to discuss the formation of edge crack.The key causes of cracking was found to be the coarse as-cast microstructure,grain boundary oxidation and decarburization in reheating furnace,as well as reduced temperature at strip edge region during hot rolling process resulting in reduced hot ductility and lack of enough dynamic re... 

【机构】 武汉钢铁学院轧钢七二级电工钢结业小组； ...

在现普通冷轧无取向硅钢的基础上,降低Si含量,复合添加少量辅助元素,组合热轧板处理和成品退火加热技术,研制出了免常化处理的高磁感、低铁损并具有良好耐酸腐蚀性能的新系列无取向电工钢。 Based on existing common cold rolled non-oriented silicon steel,a new series of non-orientedelectrical steel with high induction,low core loss and excellent anti-corrosion property has been developed by reducing Si element,adding complexly a small amount of supplementary elements,and employing combined treatment of hot rolled sheet and finished product annealed heated technology. 

通过热力学计算及实验室研究,对钙处理前后50W600无取向硅钢退火冷轧板中夹杂物的类型、数量及尺寸进行了系统分析。结果表明,50W600无取向硅钢经钙处理后(w(Ca)=0.002 6%),钙在1 600℃的钢液中主要以固态的CaO·2Al2O3、CaO·6Al2O3及溶解钙的形式存在。在钢液的凝固过程中,钢中的溶解钙和硫反应生成了CaS和CaS-MnS复合夹杂,有效抑制了MnS的弥散析出,减少了钢中微细夹杂物的数量。同时钙处理促进了钢中微细夹杂物的聚合长大,导致显微夹杂物的数量增加。 Based on thermodynamic calculation and laboratory experiment,the type,quantity and size of inclusions in annealed cold-rolled steel sheets of 50W600 non-oriented silicon steel before and after calcium treatment were systematically studied.Results showed that after calcium treatment(w(Ca) = 0.002 6%),calcium was mainly in the form of CaO·2Al2O3,CaO·6Al2O3 and dissolved calcium in steel at 1 600 ℃.Dissolved calcium could combine with sulfur to form CaS inclusions and compound CaS-MnS inclusions du... 

【作者】 宋波； 朱一知； ...

根据现场实际的生产控制情况,指出了热轧原料断面轮廓缺陷以一定的比列遗传给了冷轧带钢,分析了不同热轧原料断面轮廓对冷轧电工钢尺寸精度的具体影响,提出了相应的规律。并阐明了严格控制热轧原料断面轮廓形貌,对保证冷轧电工钢尺寸精度具有重大意义,对于中国现行的冷轧电工钢生产具有指导意义。 Based on the actual situation of production control,it was pointed out that the section profile defects of hot-rolled raw materials were geneticed to the cold-rolled strip.The specific impact analysis for the profile of different hot-rolled raw materials to the dimensional accuracy of cold-rolled silicon steel was analyzed.As a result, the corresponding orderliness are given;And the strict control to section profile of the hot-rolled material is of great significance to ensure the dimensional ac... 

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and... 

试验2.3Si无取向硅钢(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al)冷轧板由常化和未常化的2.5 mm热轧板冷轧至0.6 mm(压下率76%),经750~950℃2.5 min中间退火后再冷轧至0.5 mm(压下率16.7%),成品板经890℃+960℃2.5 min退火。研究了中间退火温度对该钢晶粒尺寸、织构和磁性能的影响。结果表明,随中间退火温度的升高,二次冷轧前晶粒和成品晶粒增大,成品中不利织构组分{111}和{112}减弱,磁性能得到改善。热轧板经过常化时的磁性能明显好于未经常化时的磁性能,但中间退火温度较高时常化对磁性能的有利作用减弱。 The test cold sheet of 2.3Si non-oriented silicon steel(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al) is first cold-rolled from normalized and un-normalizing 2.5 mm hot-rolled plate to 0.6 mm sheet(reduction 76%),then intermediate annealed at 750~950℃ for 2.5 min and double cold-rolled to 0.5 mm sheet(reduction16.7%),the finished sheet annealed at 890℃+960℃ for 2.5 min.Effect of the intermediate annealing temperature on grain size,texture and magnetic performance of the steel has been studied.... 

综述了电工钢从生产到成品过程中涉及到的检测项目、检测方法及仪器,并通过对电工钢标准的发展改进,详细阐述了我国现有的电工钢技术标准体系,同时对代表企业的电工钢重点指标进行了摘录对比,为综合应用电工钢检测方法并促进电工钢的发展提供了一定的参考。 This article summarizes the testing items,methods,and instruments involved in the process from manufacturing to finished products of electric steel. The current electric steel technical standards system in our country is also elaborated in detail,along with the development and improvement of electric steel standards. Meanwhile,by comparison of electric steel KPI in representitive companies,this article provides references for comprehensive application of electric steels testing methods and promo... 

采用低温板坯加热制备取向硅钢,通过透射电镜(TEM)观察并研究热轧板中的析出物,用ODF织构法研究热轧板距表面1/8、1/4和1/2处的织构分布。结果表明,热轧板中的析出物主要是密排六方AlN,AlN形貌呈规则长方形,AlN颗粒大小不等,分布密度低;热轧板中的织构沿板厚方向,由亚表层的{110}<001>织构向1/2中心层的α线织构变化,其中{110}<001>织构在热轧板距表面1/4层处最强。 The low temperature grain-oriented silicon steels were produced by acquired inhibitor method.The precipitates in hot rolling strip were observed and studied by transmission electron microscope,and the texture distribution in 1/8,1/4 and 1/2 layers of hot rolling strip were analyzed by ODF method.The results showed that the square shaped h-AlN is the main precipitates in hot rolling strip.The precipitates are varying in size and distribution.The texture of hot rolling strip in thick direction are...