研究了取向硅钢制备过程中常见的两种冷轧工艺,主要研究了一阶段冷轧与两阶段冷轧+中间退火工艺对初次再结晶组织及织构的影响.结果表明:采用两阶段冷轧+中间退火工艺制备以Cu2S为主抑制剂的取向硅钢,其初次再结晶平均晶粒尺寸为18.1μm,高斯晶粒的体积分数为0.6%,迁移性强的重位点阵晶界(Σ5+Σ9)和高能晶界(20°~45°取向偏差角)所占比例分别为1.8%和50.4%.与一阶段冷轧工艺相比,其初次再结晶晶粒较细,且高斯晶核与特征晶界所占的比例较高,有利于高斯晶粒发生二次再结晶. Two common cold-rolling processes of grain oriented silicon steel and the effects of the single stage cold rolling and tw o-stage cold rolling w ith intermediate annealing processes on the primary recrystallization microstructure and texture w ere investigated. The results revealed that for the grain oriented silicon steel prepared under the tw o-stage cold rolling process w ith intermediate annealing w ith Cu 2 S as the main inhibitor,the average grain size of the primary recrystallization micr... 

本文研究了丙烯酸树脂含量对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响.用盐雾实验、动电位极化及交流阻抗等试验手段研究了不同树脂含量对硅钢绝缘涂层的耐盐雾性能和电化学行为的影响,同时采用SEM对涂层的表面形貌和附着性进行研究.结果表明,树脂含量为19.9~29.4%时,涂层的耐蚀性和附着性最好;树脂含量过多时,涂层的耐蚀性和附着性均较差. This paper studies the influence of acrylic resin on the performance of insulating coating of aluminum dihydrogen phosphate on chromium-free non-oriented silicon steel.Salt spray experiment,potentiodynamic polarization and electrochemical impedance spectroscopy were used to study the influence of acrylic resin content on the salt spray resistance and electrochemical behavior of the insulation coating of nonoriented silicon steel.The surface morphologys and adhesion of coating were tested by SEM.... 

涂层技术在高磁感取向硅钢生产中起着重要的作用.根据生产实践,介绍了高磁感取向硅钢生产中涂层的种类和作用、涂料的成分和对产品性能的影响、涂层工艺质量控制要点和检验方法等,并提出了通过优化涂层工艺改善高磁感取向硅钢性能和外观质量的方法. Surface coating technique plays an important role in producing high magnetic inductivity grain-oriented silicon steel.Based on production practice,this paper describes the types and function of the coating,the composition of the coating and its effect on the product performance,the quality control and inspection method for the coatings,as well as proposes ways to improve the magnetic property and surface quality of the steel by optimizing the coating process. 

为了更好的解决电力系统防污闪涂料RTV-Ⅰ长期应用暴露出来的问题以及目前RTV-Ⅱ防污闪涂料存在的一些不足,结合具体实际需求,在电力系统外绝缘领域,应用新型防污闪硬质涂层——防污闪纳米硅钢涂层,并对分别喷涂了防污闪纳米硅钢涂层以及RTV涂料的绝缘子进行对比运行情况研究分析。研究结果表明,防污闪纳米硅钢涂层是一种同时具有优异憎水性迁移性能和自洁性能的新型涂层,具有良好的应用前景。 In order to solve the problem exposed of anti-pollution flashover coating RTV-Ⅰwhich has been used long-term in power system,as well as to better solve some shortcomings of the current anti-pollution flashover coating RTV-Ⅱ,in this paper,a new anti-pollution flashover hard coating — anti-pollution flashover nanometer silicon hard coating(NSHC) is applied in the field of power system insulation for the specific practical needs.At the same time insulators which are separately sprayed by the NSHC a... 

Fe-6.5%Si高硅钢是一种具有高磁导率、低矫顽力和低铁损等优异软磁性能的合金,但是其室温脆性和低的热加工性能严重影响了其在工业领域的应用。综述了Fe-6.5%Si高硅钢的性能,评述了合金的改性法、特殊轧制法、快速凝固法、沉积扩散法、粉末冶金法等制备工艺。 It is well known that 6.5%Si high silicon steel is one kind of soft magnetic materials with higher re-lative permeability,lower coercive force and iron loss than those of conventional industrial silicon steel.However,their room-temperature embrittleness and poor workability limit their practical applications in the industry.The pre-paration technique such as modification treatment on alloy,special rolling,rapid solidification,CVD and powder me-tallurgy is reviewed. 

借助实验室设备研究了B元素对高牌号无取向硅钢热轧板组织和磁性能的影响。结果表明,与无硼钢相比,含硼钢的热轧板晶粒尺寸略小,析出物的类型和尺寸没有区别,主要是AlN和(AlN+MnS)复合析出物,少量的MnS析出物,尺寸集中在1.0～2.5μm范围内。未发现BN析出物。在力学性能方面,B对钢的软化作用不明显。在磁性能方面,含硼钢的铁损为3.215W/kg,磁感为1.710T,综合磁性能比无硼钢差。 Influences of boron on microstructure and properties of hot rolled band in high-grade non-oriented silicon steel are researched in this paper by experimental equipments.Compared with boron-free steel,the result shows that boron-bearing steel has smaller grain size,but the type and size of precipitations have no differences.The main precipitates are AlN,(MnS + AlN) composite precipitate and few MnS,the range of which are between 1.0 μm and 2.5 μm.BN precipitation is not found.With reward to mecha... 

结合工业化生产的高效硅钢,进行了RH精炼稀土处理试验研究。针对不同的稀土处理条件,观察了夹杂物的形貌和尺寸分布,探讨了稀土处理后钢中的夹杂物形成、变化规律。结果表明:试验条件下,最佳的稀土合金添加数量为0.6～0.9 kg/t。经过合适的稀土处理后,可以有效抑制尺寸相对较小的、不规则的AlN、MnS复合夹杂生成,促进钢中微细夹杂物的聚合、上浮,钢质纯净度得到明显提高。此时,钢中全氧含量最低,脱硫效果最佳,钢中的夹杂物主要是尺寸相对较大的、近似球形或者椭球形的稀土类夹杂。 Based on the industrial production of non-oriented silicon steel,the experiment on RE treatment during the RH refining process was studied.The morphology and the size distribution were observed for the steel specimens treated with different RE treatment conditions.Further more,the formation and change of inclusions of final steel sheets after RE treatment were discussed.The results show that the suitable RE added amount was 0.6～0.9 kg/t.After the suitable RE treatment,the formation of AlN and Mn... 

基于BOF→RH→CSP生产工艺,研究了RH精炼过程钢中夹杂物类型演变及MgO·Al2O3夹杂物形成规律,同时对MgO·Al2O3夹杂物的形成条件进行了热力学计算,借助CFD数值模拟软件研究了RH精炼过程卷渣行为。研究发现,RH精炼过程20和30 min时,w([MgO])/w([Al2O3])为0.005~0.020,未发现MgO·Al2O3夹杂物;RH出站后夹杂物w([MgO])/w([Al2O3])为0.3~0.5,且RH精炼结束后MgO·Al2O3夹杂物占夹杂物总量的58.4%;另外,RH精炼过程钢液表面速度CFD模拟结果为0.57 m/s,大于临界卷渣速度0.45 m/s,且顶渣成分与夹杂物成分相近,存在卷渣现象。热力学计算表明,钢液与炉渣平衡时钢中w([Al])为0.31%~0.37%,w([Mg])为0.00024%~0.00028%,在MgO·Al2O3生成区域之内。减少RH处理过程卷渣,浇铸过程下渣及控制顶渣和包衬相中MgO质量分数可抑制MgO·Al2O3夹杂物形成。 Based on the practical production of non-oriented silicon steel, the evolution of inclusion type and the formation of MgO·Al2O3inclusion were analyzed in the process of BOF→RH→CSP. The thermodynamic conditions for forming MgO·Al2O3inclusion were discussed and the behavior of slag entrapment of molten steel was also simulated by CFD software during RH refining. The results showed that the value of w([MgO])/w([Al2O3]) was in the range of 0.005-0.020 and no MgO · Al2O3 inclusion was observed at 20 ... 

介绍了微合金元素锡、铌、稀土对无取向硅钢性能的影响,并扼要分析了这些元素对硅钢性能的影响机理:晶界偏聚元素Sn可细化晶粒提高硅钢磁性能;微合金元素Nb细化铁素体晶粒,提高硅钢的强度、韧性和塑性及磁性能;稀土元素(RE)在硅钢中的主要作用包括净化钢液、变质夹杂物、改善铸态组织和性能及微合金化,减少晶界上出现偏析的几率。 The influence of micro-alloy elements on properties of non-oriented silicon steel and the mechanism for effect of the micro-alloy elements including Sn、Nb and RE on the properties of steel are presented and analyzed in this paper.Grain boundary segregation elements Sn in steel can grain refinement and improve the magnetic properties;Micro-alloy elements Nb can refine the ferrite grain,increase the silicon steel strength,toughness and plastic;The main role of the RE in the silicon steel including... 

在实验室模拟CSP流程制备了不同含量稀土铈(质量分数0~0.018%)的1.2%Si无取向电工钢,并对其进行1 000℃×5min的再结晶退火处理,研究了铈质量分数对无取向电工钢夹杂物、显微组织、再结晶织构和磁性能的影响。结果表明:随着铈质量分数的增加,微细夹杂物数量、再结晶晶粒尺寸、{100}和{110}织构组分、磁感应强度先增后减,{111}织构组分、铁损先减后增;铈的质量分数为0.005 1%时,钢中的夹杂物数量最少,再结晶晶粒尺寸最大,有利织构最多,磁性能最优,铁损P15/50为3.253W·kg-1,磁感应强度B50为1.751T。 Non-oriented electrical steels containing different contents rare earth Ce element(0-0.018wt%) were prepared in the laboratory by simulated CSP(compact strip production)process,and then recrystallization annealing at 1 000 ℃ for 5 min were performed,the effects of Ce content on inclusion,microstructure, recrystallization texture and magnetic properties of non-oriented electrical steels were studied.The results show that with the increase of Ce content,the amounts of fine inclusion,the size of re... 

采用热模拟方法及EBSD技术,研究Fe-3 wt%Si电工钢在不同温度下组织的动、静态再结晶及晶粒取向特征,特别是少量奥氏体对铁素体动、静态再结晶组织及取向的影响。结果表明,不同温度形变的组织主要分三类:形变长条铁素体、珠光体和等轴细小铁素体。长条形变铁素体内发生动态回复或连续式的动态再结晶,奥氏体周围的铁素体动态再结晶加速,部分以传统的不连续方式动态再结晶。铁素体、奥氏体都可发生静态再结晶。奥氏体的静态再结晶在1050℃以上明显,铁素体的静态再结晶随温度的升高逐渐进行,最显著的再结晶发生在1050℃。不同温度形变的样品,其形变晶粒取向主要以<111>和<100>为主,小等轴铁素体晶粒除与大形变铁素体取向相近外,出现了<110>取向及其它取向。 Static and dynamic recrystallization and grain orientations in a hot-compressed Fe-3 wt% Si electrical steels were studied at different temperatures using Gleeble simulator and EBSD technique,particularly focusing on the effect of small amount of austenite on ferritic microstructure and orientations.The results show that microstructure of the compressed steel,depending on deformation temperature,consisted of elongated and deformed ferrite,pearlite and fine equal-axed ferrite.The elongated ferrit... 