利用电子背散射衍射(EBSD)技术和场发射电子扫描显微镜(FESEM)研究了电工钢中柱状晶不同初始取向50%热压缩变形后的演变规律及其对粒子析出行为的影响。结果表明:〈100〉晶粒形变后仍为〈100〉取向,只发生绕ND∥〈100〉方向的转动,具有遗传性,粒子析出数量少。柱状晶长轴与压缩轴的偏转度增加,取向的稳定性变差,超过40°,可形成〈111〉取向,期间发生复杂的滑移系交互作用,产生较高的缺陷密度,促进粒子析出。MnS粒子主要在晶内析出,变形温度高、形变量低,粒子均无法充分析出。回复时,形变晶粒内高的储能和缺陷密度是促进粒子进一步析出的必要条件。 The evolution of initial orientations and their influence on precipitation of columnar-grained electrical steel after 50% hot compression deformation were investigated by electron backscatter diffraction technique and field emission scanning electron microscopy.The results indicate that the〈100〉orientated columnar grains remain still〈100〉after hot compression deformation,with only rotation around ND parallel to〈100〉direction,with heredity,and less precipitation.As the deviation angle between the... 

对w(Si)=3%无取向硅钢进行表面机械研磨处理(SMAT)和异步轧制(CSR),获得表面纳米结构,再进行550～650℃、4 h固体粉末渗硅处理,用透射电镜(TEM)、扫描电镜(SEM)和X射线衍射仪(XRD)研究表层组织演变。结果表明:经过SMAT后,w(Si)=3%无取向硅钢表面形成了等轴状、取向呈随机分布的、晶粒尺寸为10 nm的纳米晶组织;异步轧制后,表面纳米晶组织保持不变;550～650℃、4 h渗硅处理后,SMAT+CSR样品表面形成化合物层,其厚度随着温度的升高由17μm增加到52μm;化合物层由Fe3Si和FeSi相组成. Nanostructured surface layer was fabricated on a 3%(mass fraction) non-grain oriented silicon steel by means of surface mechanical attrition treatment(SMAT) and cross-shear rolling(CSR),and then a solid powder siliconizing treatment was carried out for the SMAT+CSR sample at 550~650 ℃ for 4 h.The microstructural evolution was examined by using transmission electron microscopy(TEM),scanning electron microscopy(SEM) and X-ray diffraction(XRD).Experimental results show that: equiaxed nanocrystallin... 

对新能源汽车以及驱动电机的现有市场和未来市场规模进行梳理分析，通过自建计算公式推导出我国2021年1-11月份驱动电机用电工钢的总量，进而预测未来10年中国新能源汽车驱动电机用电工钢情况，为无取向电工钢的生产和在电机中的应用提供有价值的参考。 The current market and future market size of new energy vehicles and traction motors were analyzed,and the total amount of electrical steels used in traction motors in China from January to November 2021 was derived by using self-built calculation formulas,and then the situation in the next ten years of electrical steel used in traction motors of new energy vehicles in China was predicted.It will provide a valuable reference for the production of non-grain oriented electrical steel and its appli... 

本文介绍了无取向硅钢C6涂液的性能,研究了配水量、固化程度和涂层厚度等因素对无取向硅钢C6涂层性能的影响。结果表明,随着配水量的增加,完全固化所需的时间增加,涂液固体含量降低,涂层厚度减小;随着固化程度的提高,涂层硬度先增大然后趋于恒定,而柔韧性逐渐变差,在过固化后急剧恶化;涂层厚度对涂层的表面外观、附着性和绝缘层间电阻均有显著影响。 Based on the introduction about the performance of C6 varnish for non-oriented silicon steel sheets,effects of water amount,curing degree and coating thickness are discussed. Results show that with the increase of water amount,the time required to cure completely extends,and both the solid content of C6 varnish and the coating thickness decrease. As the curing degree increases,the hardness of the coating increases first and then tends to be constant,however the flexibility degenerates,especially... 

【作者】 徐刚； ...

研究了取向硅钢制备过程中常见的两种冷轧工艺,主要研究了一阶段冷轧与两阶段冷轧+中间退火工艺对初次再结晶组织及织构的影响.结果表明:采用两阶段冷轧+中间退火工艺制备以Cu2S为主抑制剂的取向硅钢,其初次再结晶平均晶粒尺寸为18.1μm,高斯晶粒的体积分数为0.6%,迁移性强的重位点阵晶界(Σ5+Σ9)和高能晶界(20°~45°取向偏差角)所占比例分别为1.8%和50.4%.与一阶段冷轧工艺相比,其初次再结晶晶粒较细,且高斯晶核与特征晶界所占的比例较高,有利于高斯晶粒发生二次再结晶. Two common cold-rolling processes of grain oriented silicon steel and the effects of the single stage cold rolling and tw o-stage cold rolling w ith intermediate annealing processes on the primary recrystallization microstructure and texture w ere investigated. The results revealed that for the grain oriented silicon steel prepared under the tw o-stage cold rolling process w ith intermediate annealing w ith Cu 2 S as the main inhibitor,the average grain size of the primary recrystallization micr... 

【作者】 张正贵； 李战库； ...

为了更好的解决电力系统防污闪涂料RTV-Ⅰ长期应用暴露出来的问题以及目前RTV-Ⅱ防污闪涂料存在的一些不足,结合具体实际需求,在电力系统外绝缘领域,应用新型防污闪硬质涂层——防污闪纳米硅钢涂层,并对分别喷涂了防污闪纳米硅钢涂层以及RTV涂料的绝缘子进行对比运行情况研究分析。研究结果表明,防污闪纳米硅钢涂层是一种同时具有优异憎水性迁移性能和自洁性能的新型涂层,具有良好的应用前景。 In order to solve the problem exposed of anti-pollution flashover coating RTV-Ⅰwhich has been used long-term in power system,as well as to better solve some shortcomings of the current anti-pollution flashover coating RTV-Ⅱ,in this paper,a new anti-pollution flashover hard coating — anti-pollution flashover nanometer silicon hard coating(NSHC) is applied in the field of power system insulation for the specific practical needs.At the same time insulators which are separately sprayed by the NSHC a... 

为了确定普通冷轧取向硅钢最优的中间完全脱碳退火工艺,在其一次冷轧后进行5种不同工艺的脱碳退火处理,借助扫描电镜及电子背散射衍射技术研究了不同工艺脱碳退火后的组织、织构和脱碳效果。结果表明:经5种工艺脱碳退火处理后,初次再结晶的平均晶粒尺寸均约为19μm,且不随退火温度和时间的变化而变化;经840℃×10min工艺退火后的晶粒最均匀,高斯织构位向更准确,高斯织构面积分数最多,为3.1%,可将碳脱至0.003 5%。 In order to determine the optimal intermediate complete decarburizing annealing processes for common grain-oriented(CGO)silicon steel,five kinds of intermediate decarburizing annealing processes were conducted,the microstructure,texture and decarbonization after different decarburizing annealing processes were studied by scanning electron microscopy and electro back-scattered diffraction(EBSD)technology.The results show that the average grains sizes of primary recrystallization were about 19μm a... 

【作者】 谌剑； ...

针对传统工艺生产硅钢周期长、能耗大等缺点,采用双辊连铸工艺制备3%Si无取向硅钢连铸薄带,利用MEM,SEM和TEM观察了铸带的组织、织构及析出物,同时对比了Al的质量分数为0.6%和0.9%的连铸薄带在组织、织构及析出物特征方面的异同.结果表明:双辊连铸工艺生产的3%Si无取向硅钢铸带的组织为均匀等轴晶粒,平均晶粒尺寸约为300μm;织构组成随Al质量分数的不同具有明显差别,Al质量分数为0.9%的铸带中{100}织构强度是随机织构的7倍;铸带中的析出物为AlN和MnS,最大尺寸分别为500和50 nm左右. Given the lengthy production cycle,high energy consumption,and other shortcomings of the traditional process for producing silicon steel,a twin-roll casting process was used to produce 3%Si non-oriented silicon steel casting strips. MEM,SEM,and TEM were used to compare micro-structure,texture,and precipitate characteristics of a casting strip containing 0.6%Al with another containing 0.9%Al.The structure of 3%Si non-oriented silicon steel produced by the twin-roll casting process was a uniform i... 

借助实验室设备研究了B元素对高牌号无取向硅钢热轧板组织和磁性能的影响。结果表明,与无硼钢相比,含硼钢的热轧板晶粒尺寸略小,析出物的类型和尺寸没有区别,主要是AlN和(AlN+MnS)复合析出物,少量的MnS析出物,尺寸集中在1.0～2.5μm范围内。未发现BN析出物。在力学性能方面,B对钢的软化作用不明显。在磁性能方面,含硼钢的铁损为3.215W/kg,磁感为1.710T,综合磁性能比无硼钢差。 Influences of boron on microstructure and properties of hot rolled band in high-grade non-oriented silicon steel are researched in this paper by experimental equipments.Compared with boron-free steel,the result shows that boron-bearing steel has smaller grain size,but the type and size of precipitations have no differences.The main precipitates are AlN,(MnS + AlN) composite precipitate and few MnS,the range of which are between 1.0 μm and 2.5 μm.BN precipitation is not found.With reward to mecha...