2.9 mm热轧3%Si高牌号无取向硅钢板（/%:0.004 6C、3.04Si、0.32Mn、0.49Als、0.004S、0.013P、0.0042N）由CSP（Compact Strip Production紧凑式带材生产线）流程:120 t BOF-70 mm CC-热轧工艺生产。热轧终轧温度872℃,卷取温度683℃。铸坯及热轧板的组织和夹杂物的分析结果表明,铸坯组织为典型的贯穿柱状晶组织;热轧板边部为再结晶组织,中部为纤维组织带有少量再结晶晶粒;高牌号无取向硅钢的主要夹杂物为铸坯-Al₂O₃,AlN和Cu₂S+MnS;热轧板-Al₂O₃,AlN,AIN+MnS和Cu₂S+MnS。 The 2.9 mm hot rolled 3%Si high grade non-oriented silicon steel plate（/%:0.004 6C,3.04Si, 0.32Mn,0.49Als,0.004S,0.013P,0.004 2N） is produced by CSP（Compact Strip Production） flow sheet i.e.120 t BOF-70 mm CC-hot rolling process with end rolling at 872℃and coiling at 683℃.The analysis results on structure and inclusions in casting slab and hot rolled plate show that the structure of slab is typical trans-columnar crystal,the structure of hot rolled plate at edge is recrystallized grain and in ce... 

本发明公开了一种低碳低硅钢铝质复合脱氧剂及其制备和使用方法，属于钢铁冶金技术领域。本发明为改善低碳低硅钢种可浇性差、夹杂降级率高的问题，提供了一种低碳低硅钢铝质复合脱氧剂，其包括：金属铝：50～60％；7Al2O3·12CaO预熔渣：10～20％，钝化CaO：10％～20％，Fe：10～20％，其余为微量杂质元素。本发明通过深入研究铝脱氧后钢中夹杂物的行为，提供了一种低碳低硅钢铝质复合脱氧剂，通过在转炉出钢过程加入该脱氧剂，能够有效降低钢中大型夹杂比例、对夹杂物改性，在不延长精炼时间的情况下降低夹杂物总量，改善目前此类钢种生产过程中存在的可浇性差，夹杂降级率高的问题。

本发明提供了一种提高无取向硅钢铁损均匀性的方法，所述方法包括，对无取向硅钢板坯进行加热和粗轧，获得中间坯；将所述中间坯精轧后以620‑750℃的温度进行卷取，获得热轧卷；将所述热轧卷进行酸洗和冷轧，获得冷轧卷；对所述冷轧卷升温至900‑960℃的温度保温50‑90s的时间，进行退火，获得铁损均匀性良好的无取向硅钢。本发明提供的方法，其铁损P1.0/50为1.379‑2.721W/kg，P1.5/50为2.751‑5.438W/kg，B5000为1.706‑1.741T，在线P1.0/50极差为0.062‑0.188W/kg，无取向硅钢的铁损更均匀。

本实用新型公开了一种便于墙面阳角安装的饰面硅钢石膏板，包括第一基材和第二基材，第一基材和第二基材均与墙面贴合，第一基材和第二基材相邻端设有阳角线条，阳角线条与墙面之间设有固定柱，固定柱一端固定连接在墙面内，固定柱通过通孔贯穿第一基材，阳角线条外侧固定连接有固定块，固定块靠近阳角线条的一侧设有插槽，固定柱远离墙面的一端贯穿阳角线条插设在插槽内，固定柱一侧设有限位槽，固定块一侧设有限位机构，限位机构一侧与限位槽相对应，本实用新型对板材的安装和拆卸更加方便，在石膏板材中添加硅钢素后，更加增强石膏板的钢性、表面的硬度及表面的流动性平整度。

本申请提供了一种高强度变压器取向硅钢片，属于变压器硅钢片领域，该一种高强度变压器取向硅钢片，包括第一硅钢片本体和固定机构，所述第一硅钢片本体表面开设有两个第一通孔、两个第一通槽和一个第二通槽，所述第一通槽间隔设置在两个所述第一通孔之间，所述第一硅钢片本体表面设有滑条，所述第二硅钢片本体插接在所述通槽内，所述第一螺纹杆插接在所述第二通孔内，所述第二螺纹杆插接在所述第一通孔内，所述螺帽螺纹连接在所述第一螺纹杆和所述第二螺纹杆两端，该一种高强度变压器取向硅钢片能够将垂直和横向均产生拉力来固定硅钢片减轻了振动，噪音小且利用凹槽和滑条进行堆叠能够精确的将硅钢片表面的通孔对齐。

本发明属于涂料技术领域，具体公开了一种用于取向硅钢的无铬无机绝缘涂料，包括以下重量份配比的原料：小颗粒硅溶胶10‑50份、大颗粒硅溶胶10‑50份、磷酸二氢铝溶液5‑50份、助剂0.1‑10份及水10‑100份。本发明还提供了一种用于取向硅钢的无铬无机绝缘涂料的制备方法，通过将小颗粒硅溶胶和大颗粒硅溶胶混合均匀成硅溶胶混合液后加水得到混合硅溶胶水溶液；再依次向其中加入磷酸二氢铝和助剂并持续拌至均匀，得到用于取向硅钢的无铬无机绝缘涂料。本发明提供的无铬无机绝缘涂料适用于取向硅钢，使取向硅钢环保无害的同时具有与含铬取向硅钢相当的耐腐蚀时效，从而实现取向硅钢产业绿色化并大大改善取向硅钢的综合性能。

以市场上购买的取向硅钢成品板为原料，经不同压下率冷轧至0.23～0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量，利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征，分析了硅钢超薄带的塑性变形行为。结果发现，在平面压缩应力下，{112}<111>滑移系的取向因子较大。随冷轧压下率的增加，Goss织构的含量逐渐减少，{212}<141>织构组分的含量先增加后减少，{111}<112>织构组分的含量逐渐增加，织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶，其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。 The commercial finished oriented silicon steel plate as the raw material were rolled to 0.23-0.08 mm. With the X-ray diffractometer(XRD), the texture components and their volume fractions in the cold-rolled samples were detected. And the orientation factor distribution of the cross-section of the samples was measured by the electron backscattering technique(EBSD). The morphology and crystallographic characteristics of twins were observed, and the plastic deformation behaviors of the ultra-thin o... 

轧制力是影响冷轧带钢厚度精度的关键因素。为实现高精度的冷轧带钢厚度控制,通过优化变形抗力模型参数和摩擦系数模型参数提高冷轧轧制力模型计算精度,并使用指数平滑法的自学习算法保证轧制力精度的稳定性。在首钢股份公司迁安钢铁公司20辊森基米尔轧机生产线进行S12硅钢钢种轧制力优化试验,将优化的模型参数应用于L2并投入现场生产,结果表明该优化方法不仅提高了轧制力设定精度,而且减小了冷轧硅钢的厚度超差长度,提高了成材率。 The rolling force is the key factor which influences the accuracy of cold-rolling strip thickness. To implement high precision control of cold-rolling strip thickness,we optimize the deformation resistance model parameters and friction coefficient model parameters to improve the calculation precision of cold-rolling force model,and use exponential smoothing self-learn algorithm to ensure the stability of rolling force accuracy. In Shougang Qiangang 20-high Sendzimir mill single stand production ... 

本发明公开了一种低损耗宽料取向硅钢的生产方法。本发明所述生产方法是通过在罩式炉的内罩中增加带有通气孔的聚气罩及与聚气罩配合的炉底板，配合工艺优化，控制原料化学成分，使气体和钢卷之间的浓度更均匀，反应更充分，气流流动方向更易控制，所制备的取向硅钢性能稳定，磁性能优良，且铁损达到1.12W/KG以下的比例提高至98.77％，平均铁损达到1.06W/KG以内，使取向硅钢卷的铁损大幅度降低，电磁性能更好。

主要研究了0.7%Si无取向电工钢退火试样的组织、晶粒尺寸和织构对其磁性能的影响。结果表明,随着退火温度的升高,晶粒尺寸逐渐增大,组织的均匀性得到改善;ɑ取向线上的纤维织构多集中于{114}<110>和{223}<110>附近,再结晶结束后,织构含量变化不大。{111}<110>织构取向密度值随温度升高而下降,{112}<111>织构与{111}<110>织构变化相反。晶粒尺寸增大对磁感强度的影响较小,而对铁损的影响较大。 Influences of microstructure,grain size and texture on the magnetic properties of 0.7% Si non-oriented electrical steels annealed samples were studied.The results show that with annealing temperature increasing the average grain size is increased gradually.Uniformity of the microstructure is improved;the textures of ɑ-fiber gathered in the vicinity of the { 114} < 110 > and { 223 } < 110 > texture.After recrystallization,the volume fraction of texture changes small.{ 111} < 110 &g... 

【作者】 陈迪安； 李春生； ...

采用电子背散射衍射技术测定50SW1300冷轧无取向硅钢中不同尺寸范围晶粒的含量,利用主成分回归分析法,综合研究不同尺寸范围晶粒的含量对无取向硅钢磁性能的影响。结果表明:通过主成分回归分析法能够从不同尺寸范围晶粒的含量的多个影响因素中获取主要的因素,定量研究它们对无取向硅钢磁性能的影响规律。分析表明,无取向硅钢的铁损与不同尺寸范围晶粒的含量之间存在着可靠的多元线性关系,在一定范围内,较大尺寸晶粒的含量越多,其对铁损优化的作用越明显;而无取向硅钢的磁感与不同尺寸范围晶粒的含量之间并无线性关系。 Distribution of grain size in cold rolled non-oriented silicon steel 50SW1300 was measured by EBSD.The effects of the distribution of grain size on magnetic properties of the non-oriented silicon steel were comprehensively researched by means of principal component regression method.The results indicate that the main factors influencing the magnetic properties in the distribution of grain sizes,which can be used to guantitative study the magnetlic properies of the steel,are obtained by principal...