本钢高硬度无取向电工钢50BW600的研发
目前随着电工钢用户冲压设备的升级,冲压速度逐步提高,对电工钢产品的硬度和强度指标提出了更高的要求。与普通硬度级别的无取向硅钢相比,高硬度50BW600的Hv硬度提高15~20,达到125以上,同时对电磁性能指标也有较高要求。本钢通过化学成份和热轧及冷轧连退生产工艺的设计,经过小批量生产试验,满足用户要求。通过对工艺的严格控制,在大批量生产过程中,保证了产品的力学性能和电磁性的检验合格率。 Currently with upgrading of stamping equipment of silicon steel user, gradually increasing of stamping speed, propose higher demand for hardness and strength of silicon steel. Compared with conventional 50BW600, high hardness 50BW600 have higher hardness, reach greater than 125Hv. Through design of chemical composition with hot mill and annealing, production test of small quantities, stamping performance meet user request.
本钢热轧厂无取向硅钢生产工艺
冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content、high addedvalue product. Its process is complex, Its production cycle is of Length, and Its Process control is difficult. Which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, Which Directly determines iron loss of the silicon steel and electromagnetic property, etc many index.
CN202110417963.1薄规格无取向硅钢35BW440及其生产方法
本发明是关于一种薄规格无取向硅钢35BW440,该无取向硅钢35BW440包括以下质量百分比的元素:C:≤0.003%,Si:0.8%‑2.0%,Mn:0.4%‑1.2%,P:≤0.015%,S:≤0.003%,Als:0.25%‑0.6%,N:≤0.003%,Sb:0.04%‑0.1%,O:≤0.0025%,其余为Fe及不可避免的杂质。在没有电磁搅拌设备增加无取向硅钢磁感应强度的前提下,通过加入Sb元素,增加对电磁性能有利的{110}和{100}织构组分,提高电磁性能,采用二次冷轧及中间连续退火的工艺,提高无取向硅钢的表面质量。
本钢薄板坯连铸机生产无取向电工钢的工艺优化
针对本钢薄板坯铸机在生产无取向电工硅钢的过程中存在的铸坯拉断、中包增碳、增氮等问题,进行了连铸工艺优化。通过采用新型无碳中间包覆盖剂、环保中间包干式料及专用结晶器保护渣后,降低了铸坯增碳量;通过控制钢包到中间包的增氮环节,降低钢水增氮;适当增大二冷水量,控制钢水过热度,防止铸坯拉断等生产事故的发生。改进工艺后,精炼后到成品铸坯的平均增碳量能控制在10×10-6以内,平均增氮量能控制在4×10-6以内。 The technology optimization has been adopted for preventing nitrogen increasing and carbon increasing in Benxi thin slab producing non-oriented silicon steel.Measures accordingly were adopted and satisfactory results were achieved.
中低牌号无取向硅钢冷轧工艺优化生产实践
无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason...
本钢无取向硅钢热轧生产工艺路线的实践
冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content 、high added value product. Its process is complex, its production cycle is of length, and its process control is difficult, which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, which directly determines iron loss of the silicon steel and electromagnetic property,as well as other many index.
CN202111652927.X一种罩式中间退火高牌号无取向硅钢50BW350的生产方法
本发明涉及一种罩式中间退火高牌号无取向硅钢50BW350的生产方法,包括钢水化学成分设计、热轧工艺、冷轧工艺和退火工艺等步骤;钢水化学成分包括C≤0.004%、Si1.80‑2.1%、Mn0.70‑0.90%、Als0.30‑0.45%、P≤0.015%、S≤0.0030%、O≤0.0020%、N≤0.0025%、Sb0.06‑0.12%,余量为Fe。本发明通过特殊的化学设计,添加Sb元素,通过优化产品的结构组织提高电磁性能,适当降低Si含量,并提高Mn元素含量,通过二次冷轧法消除热轧粗大纤维组织的影响,得到了没有表面瓦楞缺陷的高牌号无取向硅钢产品,与传统高牌号生产方法相比,成本较低,生产出的硅钢电磁性能优良。
我国硅钢发展现状及发展趋势
硅钢是钢铁产品中的\"工艺品\",是高附加值产品,通过对我国主要硅钢生产厂家的工艺设备,市场情况分析,简要介绍了我国硅钢生产消费现状,未来生产能力预测及硅钢未来发展趋势。 Silicon steel is the \"crafts\" of steel products,also is high value-added product.By analyzing process equipment and market condition of major silicon steel-making plant of China,it briefly introduces our current production consumption status,future production capacity prediction and future development trend of silicon steel.
CN202111510034.1一种农用电机用无取向硅钢的生产方法
本发明涉及一种农用电机用无取向硅钢的生产方法,包括钢水化学成分设计、热轧工艺和冷轧工艺等步骤;钢水化学成分包括:C≤0.04%、Si0.35‑0.55%、Mn0.10‑0.30%、Als0.02‑0.06%、P≤0.030%、S≤0.0040%、O≤0.003%、N≤0.003%,余量为Fe及不可避免的夹杂物。本发明方法生产出的硅钢与家用电机目前使用的普通无取向电工钢50BW1300相比,磁感提高0.02T以上,而且采用普通C含量≤0.040%设计,不需要深脱碳,大幅降低炼钢工序成本,采用无Al无P,低Mn含量,降低合金成本,与普通50BW1300无取向电工钢产品相比,生产成本大幅降低。
冷轧无取向电工钢的试制
利用本钢技术中心试验厂技术手段,并与北京钢铁研究院合作,试制了用作家电用电机、微电机、小电机或部分中型电机铁芯的冷轧无取向电工钢。试制钢硅含量小于0.5%,钢板表面平滑,公称厚度0.5mm,且厚度均匀偏差小,性能测定结果表明,产品的磁性能、力学性能满足其使用要求。 BX STEELTechnology Center pilot plant using technical means,and with Beijing Iron and Steel Research Institute,trial cold rolled non-oriented electrical steel that has been used as appliance motor core,micro motor core,small motor core,or part of the medium-sized motor core。Trial steel of silicon content is less than 0.5%,steel plate surface is smooth,the nominal thickness of 0.5mm,and the thickness deviation is small,performance measurement results show that the magnetic properties,mechanical p...