硅钢资料

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

本实用新型公开了一种能限位的硅钢片，包括主体，主体的上表面设置有限位柱，限位柱的轴心处开设有散热孔，主体的上表面开设有限位槽，主体的外壁设置有凹槽，主体的下表面设置有限位凸起，主体的下表面开设有限位孔；该一种能限位的硅钢片通过在主体的外壁设置凹槽可以方便拿取，在其上下表面分别设置限位柱与限位孔，可以使主体间的位置相对固定不会轻易挪动。

本发明特别涉及一种控制边部翘皮的热轧电工钢的生产方法和生产系统，属于钢表面质量检测技术领域，方法包括：建立热轧电工钢边部翘皮的数据库，数据库包括翘皮类型及各翘皮类型的翘皮发生原因和翘皮发生的区域；对待质检的热轧电工钢表面进行识别，并对比数据库，获得待质检的热轧电工钢表面翘皮的翘皮类型；根据待质检的热轧电工钢表面翘皮的俏皮类型获得该类型翘皮的翘皮发生原因和翘皮发生的区域；根据翘皮发生原因和翘皮发生的区域，调整生产操作，用以减少热轧电工钢的边部翘皮；通过对边部翘皮进行准确分类及识别，能够准确的分辨出边部翘皮的产生原因，采取有针对性的措施防止缺陷扩大，最大程度的降低缺陷发生量，提高质量控制水平。

研究了硅钢铸坯再加热过程中夹杂物的析出行为。采用非水溶液电解提取+扫描电镜观察方法,观察了试样的显微组织,统计了夹杂物的尺寸、种类、数量、分布。结果表明,均热温度为1 523 K时,水淬试样的夹杂物尺寸绝大部分小于0.5μm,0.5～5.0μm的夹杂物数量很少,没有发现5.0μm以上的夹杂物。此外,均热时间为10、30、60、90、120、240 min时,对应试样中0.05～0.2μm的夹杂物数量分别为4.04×104、4.73×104、3.70×104、3.33×104、3.10×104、1.56×104个/mm3。绝大部分夹杂物以MnS、AlN、CuxS类为主,并以三类夹杂物中的两类复合或三类复合居多。三类复合夹杂物总量占每组试样夹杂物总量的90%或以上。随均热时间延长,典型的夹杂物组成会发生如下变化:MnS+AlN+CuxS MnS+AlN AlN。与此同时,MnS、AlN、CuxS三者复合比例从45.2%(均热10 min)降为9.7%(均热240 min)。 The methods of electrolysis extraction from nonaqueous solution and scanning electron microscope were adopted to study the precipitation behavior of non-metallic inclusions in Si steel slabs during reheating processes.The morphologies,chemical compositions,quantity and size distribution of non-metallic inclusions in these steel samples were analyzed.Results show that,when the soaking temperature is 1 523 K,almost all of the non-metallic inclusions are smaller than 0.5 μm,few are in the range of ... 

本实用新型公开了超薄硅钢铁芯卷绕张力控制装置和纠偏装置，包括工作台、固定架和底座，工作台的顶部安装有固定架，所述工作台的底部设置有按压杆组件，所述按压杆组件的底部连接有底座，所述工作台顶部的前端和尾端均安装有固定板，所述固定板的内壁设置有收捆轴，所述工作台的顶部安装有滑轨板，且滑轨板位于固定板的内侧。本实用新型通过导向辊和衔接板的设置，工作人员在使用时，根据收捆轴上铁芯的缠绕位置，对两侧导向辊进行调节，从而通过导向辊的转动性对铁芯的活动起到定位作用，两侧导向辊的主要作用是起到带料输送出来时的导向作用，能够保证带料快速平稳的送料时不发生跑偏现象。

该电磁钢板用涂敷组合物含有环氧树脂、潜伏性环氧树脂固化剂和热塑性弹性体，上述热塑性弹性体的熔点为100℃～200℃，并且弯曲弹性模量为超过5MPa且为100MPa以下，相对于上述环氧树脂与上述潜伏性环氧树脂固化剂的合计100质量份，上述热塑性弹性体的含量为10质量份以上且低于40质量份。

以能量平衡和辐射换热理论为基础,通过合理假定,建立了硅钢无氧化加热炉数学模型。采用数值计算的方法,通过自编程序,完成对带钢加热过程温度场的仿真。结果显示:数学模型能够反映带钢在无氧化炉内的加热过程,其升温曲线能够与工艺曲线相吻合;现行炉温分布并非最优,数学模型能够为炉温分布的优化、炉段的设计提供理论依据。 Mathematical model of NOF Section of Continuous Annealing Furnace is established based on energy balance and radiation heat exchange. The temperature field of steel is simulated by mathematical computation. The simulating results show that the mathematical model can reflect the heating process of silicon steel in NOF section, and the heat-up curve is coincide with the processing curve. From the results,it is known that the current furnace temperature gradient is not the best, and the mathematica... 

研究了含铜低碳低硅无取向电工钢中的析出相及其析出机理.由能谱(EDS)及选区电子衍射(SAED)分析可知,铁素体基体上存在的大量弥散分布的等轴状析出相为类B2结构的铜.这些铜析出相的析出机理可以是一般析出、位错析出、台阶机理相间析出和弓出机理相间析出:一般析出在550、650和750℃三个等温温度均可发生;位错析出只发生在较低的等温温度(550℃),此时析出相呈特殊的平行短列状;台阶机理相间析出也可在上述三个等温温度下发生,但650℃等温时最有利于台阶机理相间析出,此时析出相平直列状分布;弓出机理相间析出只发生在较高的等温温度(750℃),析出相弯曲列状分布. Precipitates in low-carbon low-silicon non-oriented electrical steel containing Cu were studied and the precipitation mechanism was analyzed by means of energy dispersive spectrometry(EDS) and selected area electron diffraction(SAED).It is found that the equiaxed precipitates of Cu with B2-like structure distribute dispersively in the non-oriented electrical steel.The precipitation mechanism involves general precipitation,dislocation precipitation,interphase precipitations formed by the ledge me... 

取向硅钢成品的晶粒尺寸非常大,其易磁化方向[001]晶向对于轧向的偏差角度对其磁性能影响极大。本文介绍了取向硅钢二次再结晶后成品晶粒位向的几种测定方法,包括侵蚀法、劳厄法、OIM法、极图法和非对称X射线衍射法等,并对这几种测量方法进行了比较。 The finished product of grain-oriented silicon steel has immense grain size ranging from millimeters to centimeters and the deviation angles of easy magnetization direction from rolling direction plays a remarkable role in magnetic properties of grain-oriented silicon steel.The methods in common use for determining the deviation angles of crystal direction are introduced,which include the etch-figure method,the Laue method,the OIM method,the pole figure method and the asymmetrical X-Ray diffract... 

本发明涉及到一种铸铝转子硅钢片、采用该硅钢片的转子及制造转子的方法，该铸铝转子硅钢片包括圆形板片状本体，本体中心开设有转轴孔，本体上还以转轴孔为中心周向均布有多个铸铝孔，本体外缘设置有与铸铝孔一一对应的凹槽，本体两侧侧面均涂覆有绝缘层。采用上述硅钢片的转子包括转轴，所述转轴上套接有铁芯，该铁芯由大量上述的硅钢片层层叠压而成，每片硅钢片上的铸铝孔均相互正对，在铁芯上形成多条贯穿铁芯的通孔，每条通孔内设置有一条导条，铁芯两端分别连接有导电端环，各导条的两端分别伸出通孔与导电端环电性连接，各导条对两导电端环的拉力使两导电端环紧压在铁芯两端。

本实用新型涉及硅钢技术领域，尤其为一种用于硅钢绝缘涂料生产用储存装置，包括储存装置、顶盖和定位板，所述储存装置与顶盖铰链连接，所述顶盖内侧后端固定连接有定位块，所述定位块前端转动连接有连接块，所述连接块的另一端内侧转动连接有转动杆，通过设置的定位块、连接块、转动块、转动杆、推杆、档杆、挡块、弹簧、固定板和垫片，在使用时，盖上顶盖后，通过推动推杆，使推杆通过转动块带动转动杆在连接块内转动，推杆推动挡块，使挡块通过档杆挤压弹簧，从而对推杆进行限位，然后带动连接块在定位块上转动，从而使连接块挤压固定板，使固定板带动垫片，使垫片与储存装置贴合更紧，防止漏气，防止空气进去，防止涂料干燥。

本发明是关于一种薄规格无取向硅钢35BW440，该无取向硅钢35BW440包括以下质量百分比的元素：C：≤0.003％，Si：0.8％‑2.0％，Mn：0.4％‑1.2％，P：≤0.015％，S：≤0.003％，Als：0.25％‑0.6％，N：≤0.003％，Sb：0.04％‑0.1％，O：≤0.0025％，其余为Fe及不可避免的杂质。在没有电磁搅拌设备增加无取向硅钢磁感应强度的前提下，通过加入Sb元素，增加对电磁性能有利的{110}和{100}织构组分，提高电磁性能，采用二次冷轧及中间连续退火的工艺，提高无取向硅钢的表面质量。