传统轧制法制备6.5wt.%高硅钢过程中温轧工艺具有显著不同于3 wt.%Si的电工钢的特点及组织织构特征,是开发新型基于织构优化的高硅钢的关键环节。采用EBSD技术对通过热轧、温轧、冷轧及退火工艺制备0.3mm厚的6.5wt.%Si电工钢板的组织和织构进行分析,重点研究温轧过程中的中间退火和大、小压下率组合以控制织构。结果表明,在热轧退火板是部分再结晶组织的情况下,一次性温轧或先小形变量、中间退火后再大形变量的工艺可得到更多的Goss晶粒;经过最终退火后Goss取向会发生偏转,形成部分黄铜取向,而{111}〈112〉取向的晶粒内形核生成近Goss取向的再结晶晶粒;大压下量轧制是最终组织中{111}取向晶粒较多的主要原因。 Warm rolling,a key process of developing new type high-Si electrical steel based on texture optimization,has significant different characteristics from 3wt% Si steel in conventional preparing process. 0. 3mm thickness 6. 5wt. % Si steel,obtained by a series of processes including hot and warm rolling,intermediate annealing and then cold rolling,was analyzed from microstructure and texture by EBSD,which are utilized mainly for investigating the intermediate annealing process and the combination o... 

Fe-6.5%Si高硅钢是一种具有高磁导率、低矫顽力和低铁损等优异软磁性能的合金,但是其室温脆性和低的热加工性能严重影响了其在工业领域的应用。综述了Fe-6.5%Si高硅钢的性能,评述了合金的改性法、特殊轧制法、快速凝固法、沉积扩散法、粉末冶金法等制备工艺。 It is well known that 6.5%Si high silicon steel is one kind of soft magnetic materials with higher re-lative permeability,lower coercive force and iron loss than those of conventional industrial silicon steel.However,their room-temperature embrittleness and poor workability limit their practical applications in the industry.The pre-paration technique such as modification treatment on alloy,special rolling,rapid solidification,CVD and powder me-tallurgy is reviewed. 

介绍了电工钢生产线连退机组的表面处理工艺,特别是电解清洗系统的工作机理、设备构造、生产工艺及各种影响因素。 This paper introduces the technology of surface treatment of continuous annealing unit in electrical steel production line,in particular the working mechanism,structure of equipment,production techniques and various influence factors of the electrolytic cleaning system. 

研究的两种取向硅钢（%:No1-0.042C、3.16Si、0.009Al、0.07Mn、0.50Cu、0.015S、0.0084N和No2-0.040C、3.20Si、0.014Al、0.22Mn、0.49Cu、0.016S、0.008 2N）由50 kg真空感应炉冶炼,锻成（mm）350×120×35板坯,经1 250℃30 min加热,开轧温度1 100℃,5道次热轧成2.3 mm板,终轧温度950～1 000℃。实验结果表明,两热轧板沿板厚方向存在组织和织构的不均匀性,热轧板次表层为再结晶组织,有较强的Goss织构组分;中心层为形变组织,具有典型的形变织构。含0.22%Mn的No2钢次表层{110}〈001〉织构组分比含0.07%Mn的No1钢弱,中心层{001}〈110〉织构组分大大强于0.07%Mn No1钢,导致两者磁性能差异,0.22%Mn No2钢磁感应强度(B₈₀₀)和铁损(P_1.7/50)分别为1.87 T和1.24 W/kg,0.07%Mn No1钢分别为1.88 T和1.18 W/kg。 Studied both grain-oriented silicon steels（%:No1- 0.042C,3.16Si,0.009Al,0.07Mn,0.50Cu, 0.015S,0.0084N and No2-0.040C,3.20Si,0.014Al,0.22Mn,0.49Cu,0.016S,0.0082N） are melted by a 50 kg vacuum induction furnace,forged to（mm） 350×120×35 slab,heated at 1 250℃for 30 min,with beginning rolling temperature 1 100℃hot-rolled to 2.3 mm plate by 5 passes,finishing-rolled at 950～1000℃.Test results show that the structure and texture along thickness of both hot-rolled plates are inhomogeneous:the subsurface ... 

对应用动态加热进行短时温度退火的取向电工钢进行了二次再结晶研究。所进行研究的实验用取向电工钢是经过终冷轧和后续罩式退火后的一条工业化生产线生产的。研究结果表明,运用短时热处理条件可引起研究钢完全的异常晶粒长大。在实验室处理的材料的织构和金相组织与工业化生产的经过终退火而获得的相同的取向电工钢类似。但是,在实验室处理的取向电工钢的二次再结晶的矩阵中可观测到\"寄生\"晶粒。从磁性观点看,这些\"寄生\"晶粒含有不理想的{111}取向织构。 The present study was made to investigate secondary recrystallization in grain-oriented steels annealed at short time temperature exposures with application of dynamical heating.The investigated GO(Grain Oriented) steels for experiments were taken from one industrial line after final cold rolling reduction and subsequent box annealing.It was shown that application of short time heat treatment conditions could lead to complete abnormal grain growth in the investigated GO steel.The texture and mic... 

本实用新型公开了一种硅钢片激光曲线开料机，本实用新型涉及电力设备技术领域，目前现有的硅钢立体三角形卷铁芯的机械式斜度开料机在开料过程中精度差、效率低，且在硅钢片送料的过程中，长时间后硅钢片容易发生松散情况，同时只能对单一厚度的硅钢片进行输送工作，包括放料组件和开料组件以及收料组件，所述放料组件用于对硅钢片的放料工作，所述开料组件用于对硅钢片的开料工作，所述收料组件用于对硅钢片的收料工作。该硅钢片激光曲线开料机，通过利用高速激光曲线开料，效率高精度好，且硅钢片在输送的过程中，能够自动调整导向辊的位置，进而能够对硅钢片起到很好的导向作用，使其表面时刻为张紧状态，进而保证硅钢片的开料效果。

本实用新型公开了一种取向硅钢喷涂用涂料的加工上料装置，包括底座，所述底座固定连接有立柱，所述立柱固定连接有搅拌桶，所述立柱上滑动连接有桶盖和电机支架，所述电机支架固定连接有电机，所述电机的输出端固定连接有搅拌杆，所述搅拌杆穿过桶盖并固定连接有搅拌叶片，所述电机支架与桶盖之间固定连接有弹簧，所述滑槽中位于电机支架和桶盖之间固定设有限位块，通过电机、搅拌杆、搅拌叶片之间的配合，使涂料在配制时能够混合均匀；通过电机支架、桶盖、弹簧和限位块之间的配合，使得在搅拌过程中，桶盖始终紧紧盖住搅拌桶，防止搅拌过程中涂料洒漏。

本发明公开了大型风电电机硅钢片自动装配系统，涉及机械生产技术领域。该发明包括硅钢片、自动导引运输车、硅钢片标准运输箱、机械手、吸盘夹具和大型风电电机转子；自动导引运输车与硅钢片标准运输箱插接配合；吸盘夹具设置在机械手末端；大型风电电机转子周圈地面粘贴电磁轨道；自动导引运输车与电磁轨道滚动配合。本发明通过设置好的程序，自动导引运输车沿着电磁轨道移动，到达程序设定工位，自动导引运输车自动停止，机械手开始动作，通过吸盘夹具上的真空吸盘吸取硅钢片，然后机械手将吸取的硅钢片移动装配位置，此时红外位置传感器再次精确定位，机械手对硅钢片的位置进行微调，位置调整好后，机械手完成最后的自动叠片步骤。

本发明公开了一种消除取向硅钢热轧边裂的制造方法，通过成分设计、热轧加热和轧制参数优化等方面控制方面，有效解决取向硅钢热轧板边裂缺陷，提高材料的成材率，可以有效消除取向硅钢热轧板的边裂并能保证良好的成品磁性能。

本发明公开了一种取向硅钢产品的在线性能判级与精确分切装置和方法，使得同一个分卷上的性能分布均匀，避免分卷出现性能废品或多个性能等级的情况，提高分卷性能稳定性。提供的一种取向硅钢产品的在线性能判级与精准分切方法包括生产数据采集、铁损曲线自学习、数据存储、性能在线判级、缺陷数据采集、缺陷判级、智能分切等模块，依据修正后的磁性能全长数据，得到产品的性能判级结果，结合表面缺陷判级结果，综合确定分切位置，制定最佳分切方案。本发明可以实现取向硅钢生产过程中的性能在线判级和精准分切，得到性能均匀、表面质量好的分卷，减少分卷性能不稳定带来的损失。

该电磁钢板用涂敷组合物含有环氧树脂、潜伏性环氧树脂固化剂和热塑性弹性体，上述热塑性弹性体的熔点为100℃～200℃，并且弯曲弹性模量为超过5MPa且为100MPa以下，相对于上述环氧树脂与上述潜伏性环氧树脂固化剂的合计100质量份，上述热塑性弹性体的含量为10质量份以上且低于40质量份。

本发明公开了一种高牌号硅钢的穿带激光焊接方法，包括：将焊缝中硅含量降低到Si焊＜1.9%。采用激光+填丝焊接，填丝ER50‑6碳钢焊丝；根据焊缝截面积和激光焊接速度；激光填丝焊接时，激光线能量应足够大，达到填丝在熔池中充分混合，均匀分布，不至于填丝的成分浮在熔池的上半部分。采用此方法使焊缝组织从粗大铁素体变成细小、致密的无碳贝氏体，晶内沉淀相和晶间脆性相相对大幅减少，提高了焊缝韧性和成形性能，保证了高硅硅钢带的穿带焊接和连续生产。