硅钢资料

2.9 mm热轧3%Si高牌号无取向硅钢板（/%:0.004 6C、3.04Si、0.32Mn、0.49Als、0.004S、0.013P、0.0042N）由CSP（Compact Strip Production紧凑式带材生产线）流程:120 t BOF-70 mm CC-热轧工艺生产。热轧终轧温度872℃,卷取温度683℃。铸坯及热轧板的组织和夹杂物的分析结果表明,铸坯组织为典型的贯穿柱状晶组织;热轧板边部为再结晶组织,中部为纤维组织带有少量再结晶晶粒;高牌号无取向硅钢的主要夹杂物为铸坯-Al₂O₃,AlN和Cu₂S+MnS;热轧板-Al₂O₃,AlN,AIN+MnS和Cu₂S+MnS。 The 2.9 mm hot rolled 3%Si high grade non-oriented silicon steel plate（/%:0.004 6C,3.04Si, 0.32Mn,0.49Als,0.004S,0.013P,0.004 2N） is produced by CSP（Compact Strip Production） flow sheet i.e.120 t BOF-70 mm CC-hot rolling process with end rolling at 872℃and coiling at 683℃.The analysis results on structure and inclusions in casting slab and hot rolled plate show that the structure of slab is typical trans-columnar crystal,the structure of hot rolled plate at edge is recrystallized grain and in ce... 

热卷箱位于热连轧带钢生产线粗轧与精轧机之间,是热连轧生产中比较理想的中间保温设备。由于取向硅钢变形温度区间较窄,在生产中易出现边裂现象,同时中间坯的边部温度难于得到保证,因此一般不采用热卷箱设备生产,限制了传统热连轧生产线产品开发的品种。通过合理优化热卷箱控制工艺参数,解决了某厂传统热连轧生产线用热卷箱生产取向硅钢的边部质量问题,成功地生产出取向硅钢带。 The hot coil-box is an ideal heat retaining apparatus for hot rolling,lined between roughing mill and finishing mill. But oriented silicon steel has a narrow deformation temperature range,so that the edge crack easily occurs and it is difficult to insure the temperature of the intermediate blank. Therefore,the hot coil-box is rarely used in producing oriented silicon steel,which restricts the product development of the traditional hot rolling line. The article reasonable optimized process parame... 

研究了铝和铬元素在无取向电工钢晶粒长大过程中对织构及晶界变化的影响规律。试验结果表明:电工钢在晶粒长大过程中的主要织构组分均为{111}<112>。在晶粒生长期间,不加铝的1号试样中,{111}<112>、{111}<110>织构组分强化,而{100}<001>织构组分弱化;与1号试样相比,在加入0.2%的铝(质量分数,下同)的2号试样中,{111}<112>、{111}<110>织构组分强化(增加)的速率下降,{100}<001>织构组分变化不明显,甚至稍有增加。在含铝的试样中再加入0.3 5%的铬之后(3号试样),{111}<112>{、111}<110>和{100}<001>织构组分的变化规律与1号试样相似,但当电工钢中加入0.72%的铬之后(4号试样),上述3种织构组分的变化规律与2号试样相似。对于在晶粒生长期间持续变化的3种织构组分而言,1号试样的{1 1 1}<112>和{111}<110>织构组分的高(低)取向差角度晶界频率下降(... The effect rule of Aluminm and Chromium on texture and grain boundary transformation in the nonoriented electrical steel during grain growth was investigated.The experimental result shows that the main texture component is {111}<112> in the electrical steel.The {111}<112> and {111}<110> components in specimen 1 without Alumium were strengthened during grain growth whereas {100}<001> component was weakened.But the growth rate of {111}<112> and {111}<110> compon... 

6.5%Si硅钢具有优异的磁学性能和广泛的应用前景。本文综述了6.5%Si硅钢的物理、机械及磁学特性,讨论了传统轧制、温轧、薄带连铸、快速凝固、CVD、粉末轧制等不同制备工艺的关键技术及特点,概括了6.5%Si硅钢在高效节能电机、汽车马达及磁屏蔽等领域中的主要应用,介绍了硅钢的制备技术取得的研究进展,并指出了其广阔的发展前景。 6.5% Si silicon steel has good magnetic properties and wide applications.In this paper physical and mechanical magnetic properties were summarized,and key technology and characteristic of several preparation methods,such as traditional rolling,warm rolling,thin strip continuous casting,rapid solidification,CVD and powder rolling,were discussed.Main applications of 6.5% Si steel in the fields of high-efficiency electrical motors,automobile motors,transformer cores and magnetic shielding were gene... 

【作者】 潘恒韬； 刘涛； ...

采用经验设计法初步确定了取向硅钢铸坯感应加热线圈设计参数,应用Ansoft仿真软件分别对36组不同线圈高度、线圈内径的感应加热炉在不同频率下的三维整体磁场和铸坯的温度场进行了数值仿真。通过对比仿真结果,确定电磁场分布最佳的一组感应加热炉设计参数为线圈高度h=1.50 m、线圈内径D1=0.575 m、电流频率f=110 Hz。在该参数下应用Ansoft仿真软件对取向硅钢铸坯感应加热炉的温度场进行了仿真,结果发现温度场分布均匀,可满足取向硅钢铸坯加热要求。 The induction heating coil design parameters for the oriented silicon steel casting blank were determined preliminary by experience design method,and 36 groups three-dimensional electromagnetic field with different height and inside diameter of coil under different frequencies of the induction heating furnace and the temperature field of the casting blank were investigated by numerical simulation using Ansoft simulation software. By comparing the simulation results of electromagnetic field distr... 

硅钢工业退火炉温度控制具有强耦合、纯滞后、多扰动等特点,它的控制方法代表着一类非线性系统控制的解决方法。以硅钢工业退火炉温度为控制对象,在双交叉限幅控制的基础上引入了智能学习系统,形成了基于智能学习系统的双交叉限幅控制方法来解决此类非线性系统的控制问题,并通过模块化的编程来实现其功能。结果表明:与传统的PID控制相比,该控制方法的控制精度、抗扰性等控制指标有明显提高,是解决此类非线性控制的一种有效方法。 The temperature control of silicon steel industrial annealing furnace has the features of strong coupling,pure lag,multidisturbance. The control method represents the solution of a class of nonlinear control systems. The control object is the temperature control of silicon steel industrial an-nealing furnace, the intelligent learning system based on Double Across Limit Control is introducedand used to solve control problem of this kind of nonlinear system, and the module programming isused to re... 

利用EBSD技术对CGO硅钢热轧、中间退火、脱碳退火及二次再结晶退火组织及织构进行分析,研究了CGO硅钢各阶段加工制备过程中高斯{110}<001>晶粒的形状、尺寸及分布特点,分析了高斯取向晶粒在各工序过程中的遗传继承性特点。结果表明,CGO硅钢热轧板的次表层存在Goss取向晶粒,历经一次冷轧及中间退火后Goss取向晶粒基本消失,一次再结晶之后Goss织构仍不是主要织构,主要织构为{111}<110>和{111}<112>,说明Goss取向晶粒在二次再结晶退火前数量及尺寸上并不占优势,二次再结晶过程中Goss取向晶粒异常长大形成锋锐Goss织构。{111}<110>和{111}<112>织构组分的强度在一次冷轧中不断增加,{111}<112>织构组分的强度在二次冷轧后达到最大而{111}<110>织构组分是在初次再结晶后变强。 Grain shape,size and distribution of { 110} < 001 > Goss grains in CGO steel and the hereditary characteristics of Goss orientated grains during each processing period were investigated,based on the analysis of the microstructure and texture of the CGO silicon steel during hot rolling,intermediate annealing,decarburizing annealing and secondary recrystallization annealing by means of EBSD. The results show that Goss orientated grains exist in the subsurface of the hot rolled plate,and Goss... 

含铜抑制剂作为取向硅钢的主抑制剂或辅助抑制剂不仅可以抑制初次晶粒的长大,促进二次再结晶,还可以降低铸坯的加热温度。取向硅钢中主要抑制剂为10～50 nm Cu₂S,在钢的铸坯、热轧、冷轧、脱碳等工艺过程均可析出;（Cu,Mn）_1.8S、Cu_1.8S、ε-Cu等主要作为辅助抑制剂,尺寸一般为30～50 nm（或大于50 nm）,主要在热轧阶段析出。总结了国内外有关取向硅钢中含铜抑制剂析出行为的研究进展,当前主要研究不同生产流程和工序中含铜抑制剂的析出行为和作用机理。 As main inhibitor or auxiliary inhibitor for grain-oriented silicon steel,the particles of inhibitor bearing copper not only inhibit the primary crystal growing and promote the secondary recrystallization,but also decrease the heat temperature of casting slab.The main inhibitor for grain-oriented silicon steel is 10～50 nm Cu₂S,which precipitate in process and procedure including steel casting slab,hot rolling,cold rolling and decarburizing process,while the 30～50 nm or more than 50 nm... 

传统轧制法制备6.5wt.%高硅钢过程中温轧工艺具有显著不同于3 wt.%Si的电工钢的特点及组织织构特征,是开发新型基于织构优化的高硅钢的关键环节。采用EBSD技术对通过热轧、温轧、冷轧及退火工艺制备0.3mm厚的6.5wt.%Si电工钢板的组织和织构进行分析,重点研究温轧过程中的中间退火和大、小压下率组合以控制织构。结果表明,在热轧退火板是部分再结晶组织的情况下,一次性温轧或先小形变量、中间退火后再大形变量的工艺可得到更多的Goss晶粒;经过最终退火后Goss取向会发生偏转,形成部分黄铜取向,而{111}〈112〉取向的晶粒内形核生成近Goss取向的再结晶晶粒;大压下量轧制是最终组织中{111}取向晶粒较多的主要原因。 Warm rolling,a key process of developing new type high-Si electrical steel based on texture optimization,has significant different characteristics from 3wt% Si steel in conventional preparing process. 0. 3mm thickness 6. 5wt. % Si steel,obtained by a series of processes including hot and warm rolling,intermediate annealing and then cold rolling,was analyzed from microstructure and texture by EBSD,which are utilized mainly for investigating the intermediate annealing process and the combination o... 

随着中国电工钢产量的增加,硅钢级氧化镁需求量不断增加,传统的以白云石为原料制备氧化镁的工艺已经无法满足市场需求。中国是一个卤水资源丰富的国家,因此,研究如何资源化综合利用盐湖资源变得越来越重要。硅钢级氧化镁是一种制备取向硅钢的涂层材料,主要用于取向硅钢高温退火处理阶段,起到隔离剂、绝缘膜层、脱硫、脱磷等作用。综述了制备硅钢级氧化镁的方法、工艺流程、研究进展及存在的问题,指出了硅钢级氧化镁制备技术的发展方向,并对中国卤水资源的利用提出了建议。 With the increasing output of electric steel,the demand for silicon steel grade magnesium oxide(MgO) is larger and larger in China,and the traditional MgO production process with dolomite as raw material has been unable to meet market demand.China is a brine resource-rich country,the study of how to comprehensively utilize salt lake resources has become increasingly important.As a coating material used for preparing oriented silicon steel,silicon steel grade MgO is mainly used in the process of ... 

分析了高转矩和高转速条件下高效驱动马达铁芯材料对无取向硅钢磁性能要求,讨论了无取向硅钢的高磁通密度和低铁损对电机转矩和效率的影响,介绍了国内外高磁感无取向硅钢发展情况。在生产工艺上,提高钢质纯净度,弱化夹杂物和第二相粒子对畴壁移动和再结晶晶粒长大的钉扎作用,添加微量晶界和带钢表面的偏析元素促使有利织构发展等技术可提高无取向硅钢的磁通密度。 The requirements of high efficient drive motor core materials under the conditions of high torque and high speed were analyzed.The effects of high magnetic flux density of non-oriented silicon steel on the torque and efficiency of the motor were discussed.The development of non-oriented silicon steel with high magnetic was introduced.The magnetic flux density of non-oriented silicon steel sheet can be obviously improved by some production technologies,such as purification steel,weakening the pin...