硅钢资料

为了确定普通冷轧取向硅钢最优的中间完全脱碳退火工艺,在其一次冷轧后进行5种不同工艺的脱碳退火处理,借助扫描电镜及电子背散射衍射技术研究了不同工艺脱碳退火后的组织、织构和脱碳效果。结果表明:经5种工艺脱碳退火处理后,初次再结晶的平均晶粒尺寸均约为19μm,且不随退火温度和时间的变化而变化;经840℃×10min工艺退火后的晶粒最均匀,高斯织构位向更准确,高斯织构面积分数最多,为3.1%,可将碳脱至0.003 5%。 In order to determine the optimal intermediate complete decarburizing annealing processes for common grain-oriented(CGO)silicon steel,five kinds of intermediate decarburizing annealing processes were conducted,the microstructure,texture and decarbonization after different decarburizing annealing processes were studied by scanning electron microscopy and electro back-scattered diffraction(EBSD)technology.The results show that the average grains sizes of primary recrystallization were about 19μm a... 

从影响高牌号无取向硅钢退火工艺的主要参数入手,介绍高牌号无取向硅钢退火炉在加热、气氛控制、冷却、涂层烘烤方面的新技术,并展望无取向硅钢退火炉的发展方向。 Based on the technology parameters of high-grade non-oriented silicon steel annealing,the new technology of the annealing line,which includes heating,atmosphere control,cooling,coating baking,is introduced,and the development direction of non-oriented silicon steel annealing furnace is pointed out. 

针对攀枝花钢钒有限公司难以稳定生产w(S)≤0.006%高级别电工钢的问题,通过开发RH脱硫剂、钢包渣改性及工艺参数控制,形成了RH脱硫系统工艺技术。经工业试验表明,采用该工艺技术后,钢水脱硫率最高达到42%,成品w(S)控制在0.005%以下,全氧、氮含量也得到了较好的控制,且脱硫剂没有引起钢水增碳,满足高级别电工钢的生产要求。 In light of the difficulty of production of high level electrical steel w(S)≤0.006 % steadily in Panzhihua steel & vanadium Co.,Ltd.the process technology of RH desulfurization system has been formed by developing the RH desulfurizer,modifying the ladle slag and controlling the process parameters.Industrial experiments show that the desulfurization rate of hot metal rises to 42 % and the w(S) of the finished products is controlled in below 0.005 % and total oxygen and nitrogen contents are a... 

介绍了硅钢氧化镁制备方法及高质量硅钢氧化镁制备技术的研究进展,并对利用我国丰富的卤水资源制备硅钢氧化镁进行了展望。 The preparation methods of silicon steel magnesium oxide and research progress of high quality silicon steel magnesium oxide preparation technology were introduced.The use of abundant brine resources in the preparation of silicon steel magnesium oxide was prospected. 

针对某硅钢车间ST机组的除尘系统除尘效率较低、排放浓度不达标、二次污染较严重的问题,通过现场调研,对除尘系统、含尘气体组分与物性参数等进行测试和分析,运用管道伴热技术改善粉尘黏性后,再选取合适的除尘器对粉尘进行除尘处理,大大地提高了系统的除尘效率。 To solve the problems of low dust removal efficiency, substandard emission concentration and severe secondary pollution, some investigations are conducted to test and analyze the dust removal system,dust-gas composition and relevant physical parameters.Moreover, dust removal efficiency is greatly improved by the use of pipe heat tracing technology and by choosing appropriate dust remover. 

【作者】 常波； ...

通过热力学计算,分析了实验钢中主要析出物析出的可能性。结果表明:在液相和固液两相区中,AlN和MnS均不能析出;在奥氏体区,AlN和MnS具备热力学析出条件,平衡析出温度分别为1547、1582 K。成品退火板中的析出物主要为AlN和MnS。扫描电镜下观察到的AlN形貌多为长条状,MnS形貌多为棒状或近似球形。这两种析出物占了析出物总量的85%以上,尺寸集中分布在400~800nm;复合析出物主要是(Al2O3+MnS)和(AlN+MnS),形貌不规则,尺寸集中在0.7~1.5μm;透射电镜下观察到了少量100nm以下独立的AlN析出。 According to thermodynamic calculation, the precipitation probability of precipitates was analyzed, AlN and MnS can not precipitate in liquid phase area and solid-liquid two-phase area. In austenite area, both the AlN and MnS have precipitation condition in thermodynamics and precipitates at 1547 K and 1582 K, respectively. The precipitates in annealing plate are mainly AlN and MnS. The shape of AlN is mostly strip, and MnS is stick or near sphericity. They accounted for over 85% of the total qu... 

用Gleeble1500D模拟试验机在变形温度为950～1 200℃、应变速率为0.01～8s-1、最大变形程度为60%的条件下,对硅钢50A1300做单道次压缩试验,首先分析了不同参数对流变应力的影响,然后用回归法确定了应力模型中的变形激活能及材料常数,得到硅钢50A1300在峰值应力条件和稳态应力条件下的变形激活能分别为270.360和91.557kJ/mol,同时得到了流变峰值应力模型,模型的相关系数为0.997。最后通过作lnθ-ε图的方法找到了硅钢50A1300发生动态再结晶的临界应变量,并回归得到峰值应变量、临界应变量与参数Z/C的关系式。 To analyze the effects of different parameters on the flow stress and critical strain of the dynamic recrystallization,single-pass compression experiments were carried out with silicon steel 50A1300 specimens using a Gleeble1500D thermal simulator at a temperature range of 950-1 200 ℃ and strain rate range of 0.01-8 s-1 under the condition of maximum deformation of 60%.The average deformation activation energy is respectively 270.360 and 91.557 kJ/mol under the peak stress and steady-state stres... 

采用\"热轧复合+冷轧减薄+退火\"方法成功制备了0.20mm厚的硅浓度梯度高硅钢薄带,并采用SEM和X射线衍射技术对制备过程中组织和织构演变进行了研究。热轧复合板微观组织呈明显层状分布,复合界面为紧密冶金结合且经过83%的大冷轧变形未开裂。热轧和冷轧复合板带中均形成强α和γ织构,再结晶退火后形成强γ织构。冷轧和退火织构沿板厚呈显著的梯度分布特征,其主要来自于复合界面两侧硅浓度和初始热轧织构的差异性以及冷变形的不均匀性。 Gradient high silicon steel thin sheets with thickness of 0.20 mm were successfully produced by the rolling and annealing method,including hot rolling bonding,cold rolling,and annealing.Microstructure and texture evolution was investigated by means of SEM and X-ray diffraction.Microstructure of hot-rolling-bonding shows obviously layered distribution,the composite interface was closely metallurgical bonding and no cracking appears even after 83%cold rolling.Strongαandγfibers develop in the hot a... 

以轻烧氧化镁粉为原料,经消化、碳化制得重镁水,在热解反应前采用络合剂对重镁水中的杂质钙、铁进行络合掩蔽,再经热解得到碱式碳酸镁,碱式碳酸镁经煅烧可制得钙、铁杂质含量较低的氧化镁。在重镁水络合除杂过程中,考察了络合剂三乙醇胺、柠檬酸、草酸单独和复合使用的除铁、除钙效果。以三乙醇胺为络合剂时,在200 mL重镁水中加10 mL三乙醇胺(1∶1),氧化镁产品中w(氧化镁)=99.3%、w(氧化钙)=0.31%、w(氧化铁)=0.042%;使用草酸和柠檬酸作为复合络合剂时,在200 mL重镁水中加入1.0 g柠檬酸和2.0 g草酸,氧化镁产品中w(氧化镁)=98.2%、w(氧化钙)=0.24%、w(氧化铁)=0.030%。 Light-burned magnesia as a raw material was hydrated and carbonated to obtain magnesium bicarbonate liquor.Before the pyrolyzing of magnesium bicarbonate liquor,complexants were used to cover Fe and Ca impurities.Then the treated liquid was pyrolyzed to obtain basic magnesium carbonate which was calcined to magnesium oxide with low calcium and iron content.During the complexing purification of magnesium bicarbonate liquor,the Fe and Ca removing effects of single or compound complexing agents,suc... 

针对新能源汽车的发展，制备了含Ni固溶强化、含Cu析出强化以及含Ni+Cu复合强化3%Si无取向硅钢，研究了强化方式对无取向硅钢组织、织构和性能的影响。结果表明：固溶强化型无取向硅钢热轧板中形成了粗大{221}<221>晶粒，冷轧过程中剪切变形明显并在退火后形成良好再结晶织构。析出强化型无取向硅钢热轧板中心层形成γ取向粗大晶粒，在后续的加工中γ织构逐渐增强并最终得到相对细小的再结晶晶粒。复合强化型无取向硅钢热轧板中保留了强λ取向带状组织，退火后形成了有益的Goss织构和λ织构。固溶强化型与复合强化型无取向硅钢磁感应强度B₅₀分别达到1.742、1.688 T,高于析出强化型无取向硅钢的1.645 T。同时，复合强化型无取向硅钢高频铁损最低，其P_1.0/400和P_{1.0/1 000}分别低至20.97、82.69 W/kg,这与其较小的晶粒尺寸和织构改善有关。强度计算结果表明：Ni元素固溶强化对强度的提高有限，屈服强度为468 MPa,纳米Cu析出可显著提高屈服强度（强度增量约200 MPa）,且主要来自于模量强... For the development of new energy vehicles, 3%Si non-oriented silicon steel were processed by solid solution strengthening with Ni, precipitation strengthening with Cu, and composite strengthening with Ni and Cu. The effects of different strengthening methods on the microstructure, texture and properties of high-strength non oriented silicon steel were studied.The results show that coarse {221}<221> grains are formed in the hot rolled sheet of solution strengthened non-oriented silicon ste... 

通过对取向硅钢进行脉冲磁场退火实验,发现在相同的退火时间(6.0 min)内,低于1 T的脉冲磁场可以在一定程度上提高取向硅钢的磁感(B8),而高于1 T的脉冲磁场则会使取向硅钢的磁性能急剧恶化.同时发现,脉冲直流电加热方式会使取向硅钢的磁性能恶化.研究表明,脉冲磁场退火有望成为一种调控材料微观结构的有效手段. We have carried out experiments of annealing by pulse magnetic field.The results show that a pulse magnetic field with intensity lower than 1 T can promote magnetic induction density(B8) of grain-oriented silicon steel,while the magnetic properties deteriorate sharply when intensity is higher than 1 T.It has also been found that heating by using pulse direct current can cause the magnetic properties to deteriorate,in contrast to the traditional heating using resistance furnace.Our research shows...