利用热模拟试验机、光学显微镜和X射线衍射仪对Fe-3.2%Si低温取向硅钢热轧工艺参数对组织及织构的影响进行了研究。结果表明,Fe-3.2%Si硅钢在1110℃粗轧、880℃终轧,轧后以10℃/s的速度冷却到550℃卷取,然后空冷到室温,热轧硅钢板沿板厚方向的显微组织不均匀性显著,对后续发展完善的二次再结晶有重要作用。无论是热轧板,常化板还是冷轧板,它们的织构集中分布在γ取向线上,γ取向线的织构除取向密度不同外,织构种类是一致的,这说明γ取向线上织构是有继承性的。从热轧到常化,织构取向密度显著减小,经二次冷轧后,织构密度又显著升高,可见,轧制变形有助于织构的形成并使织构强度升高。 The influence of hot-rolled process parameters on the microstructure and texture of Fe-3.2%Si low temperature hot rolled grain-oriented silicon steel were researched by hot simulation experiment machine,light microscope and X-ray diffractometer.The results show that,Fe-3.2%Si silicon steel is rolled by the technology with a temperature of rough rolling of1110℃,finish rolling of 880℃,coiling with the speed of 10℃ /s,and then cooled to room temperature with air.The microstructure of hot-rolled sil... 

从影响高牌号无取向硅钢退火工艺的主要参数入手,介绍高牌号无取向硅钢退火炉在加热、气氛控制、冷却、涂层烘烤方面的新技术,并展望无取向硅钢退火炉的发展方向。 Based on the technology parameters of high-grade non-oriented silicon steel annealing,the new technology of the annealing line,which includes heating,atmosphere control,cooling,coating baking,is introduced,and the development direction of non-oriented silicon steel annealing furnace is pointed out. 

研究了锰含量对w(Si)=1.8%Si无取向电工钢组织和性能的影响。结果表明,钢中锰含量从0.3%增加到1.2%时,由于α_γ相变的产生,铸坯低倍组织、热轧板金相组织及成品织构等均发生了不同程度的变化,对成品表面质量及磁性能产生了明显的影响。 The effects of manganese content on structure and properties of w(Si)=1.8% non-oriented electrical steels have been studied.Results show that with increasing manganese content to 1.2% from 0.3%,macrostructure of continuous casting slab,hot rolled band metallurgical structure and finished product texture vary in some extent because of the occurrence of α-γ phase transformation,the surface quality and magnetic properties of finished product are affected greatly. 

介绍了CSP工艺生产无取向电工钢各工序的设备特点、采用的工艺控制手段和电工钢产品质量情况,结合生产实践证明了马钢CSP工艺开发的无取向电工钢产品丰富了薄板坯连铸连轧的品种结构,发挥了薄板坯连铸连轧生产无取向电工钢性能均一、稳定的特点。 The equipment characteristic,the process control method and the quality of non-orientated silicon steel by CSP process were introduced.Combined with the production situation,it is proved that production of non-orientated silicon steel developed on Masteel CSP line would enrich product structure of thin slab continuous casting and rolling,and it exerts stable performance of non-orientated silicon steel. 

【摘要】 <正>由西电集团、保定天威集团使用迁钢公...

在Gleeble-3500热/力模拟试验机上对HW600钢进行高温压缩试验,研究在不同试验条件下的变形抗力。试验结果表明:变形温度对变形抗力的影响最为显著,在相同的变形速率下,随着变形温度的升高,变形抗力降低;在同一变形温度下,变形速率增大,变形抗力增加;在同一变形温度、变形速率下,随着变形程度的增加,变形抗力急剧增大,真应变达到0.1后,变形抗力增加趋势变缓。 The high-temperature compression test is done for HW600 steel with Gleeble-3500 thermal simulation testing machine to research its resistance to deformation under different test conditions.It is showed from result that deformation temperature has greatest effect on the resistance,and along with the temperature getting higher the resistance lowered under same deformation rate;the resistance increases along with deformation rate getting greater under same temperature;and under same deformation tem... 

观察了取向硅钢极薄带经冷轧至不同厚度,并经过不同工艺热处理后的显微组织及亚结构。结果表明:冷轧压下量越大,显微组织中位错密度越高,冷变形组织越多,等轴晶粒越少;增加冷轧压下量可以使试样的再结晶温度降低,当钢带厚度为0.08 mm时,在650℃退火时就能发生明显的再结晶。 Microstructure and substructure of the grain oriented ultra-thin silicon steel sheets is analyzed,which are rolled down to different thickness and treated with different heat treatment process.The result shows that there are higher dislocation density,more cold deformation structure and less equiaxed crystal grain in microstructure of the steel sheets with more cold rolled reduction.Increase of cold rolled reduction will decrease recrystallization temperature,and when thickness of the steel shee... 

某厂对电工钢的轧制策略进行了优化，粗轧道次由“1+5”改为“1+3”。在优化后的生产过程中，每次变换钢种，烫辊材就会出现窄尺现象，而紧随其后的电工钢板则出现超宽现象。文中针对该问题，介绍了宽度设定模型和宽度自适应模型的原理，阐述了该问题出现的原因及解决方案，并通过对宽度自适应模型的应用研究及优化攻关，有效地解决了问题，大幅提升了实物质量，降低了宽度封锁率。 The rolling strategy of electrical steel was optimized in a factory,and the rough rolling pass was changed from “1+5”to“1+3”.Subsequently,the following problems were occurred in the production process:when the steel grade changed,the roasting roller steel before the electrical steel appeared the narrow width phenomenon,and then the electrical steel appeared the ultra-wide phenomenon.This paper introduced the principle of width setting model and width adaptive model,and expounded the causes and s... 

结合扫描电镜和大样电解研究了CSP流程W800牌号无取向电工钢表面线状缺陷中夹杂物成分及来源，采用SPSS软件回归分析了生产过程各因素对表面线状缺陷的影响。研究表明：稳态浇铸过程铸坯中大型夹杂物含量为5.39 mg/10 kg。引起无取向电工钢表面线状缺陷的大型夹杂物主要为脱氧产物、镁铝尖晶石和钢包顶渣，主要类型为Al₂O₃、MgO-Al₂O₃、CaO-Al₂O₃-MgO和CaO-Al₂O₃-SiO₂。非稳态浇铸过程钢水洁净度明显降低，热轧板表面线状缺陷比例上升。影响表面线状缺陷的主要因素为RH出站时顶渣的w（CaO）/w（Al₂O₃）、RH脱氧结束氧位及中间包最低吨位。 Combining scanning electron microscopy and large sample electrolysis, the composition and source of inclusions in the surface linear defects of W800 grade non-oriented electrical steel in the CSP process were studied. SPSS software was used to regress and analyze the main factors which affected the surface linear defects in the steelmaking process. Research shows that the content of large inclusions in the steady state casting process is 5.39 mg/10 kg. The large inclusions which cause linear def... 

对无取向电工钢中的夹杂进行了系统的分析。利用小样电解,采取不同电解液,不同的分离方法对无取向电工钢中稳定和不稳定夹杂物进行了提取、分离和收集。利用扫描电镜(SEM)、X-射线衍射、ICP等对电解分离收集的夹杂物进行了定性和定量分析。 The inclusion analysis of the non-oriented electrical steel has been investigated.By using small sample electrolytic analysis,with different electrolytes and different separation ways,the stable inclusions and unstable inclusions was drew,separated,and collected.With utilizing the methods of SEM,X-ray and ICP,the qualitative and quantitative analysis of inclusions in the non-oriented electrical steel was obtained. 

【摘要】 <正>近日,世界上最先进的硅钢冷连轧酸轧...

【作者】 凌健； ...