连续酸洗退火机组(CPAL)对于当前生产高磁感取向硅钢和高牌号无取向硅钢是必不可少的一个环节。常化炉是常化酸洗机组关键的组成部分。本文对国内自主建造的两条退火酸洗机组的工艺流程,特别是常化炉段进行了对比分析。总结出了常化炉的工艺及组成特点,对生产过程中暴露的问题进行了仔细的分析并提出了改进的意见,对于以后新建常化炉具有一定的提示作用。 The continous pickling annealing line(CPAL) is an essential step in producing high magnetic induction grain-oriented silicon steel and high grade non-oriented silicon steel.The normalizing furnace is a very important part of the CAPL.In this paper,the process flows of two CAPL with independent manufacture in our country have been compared,especially the part of normalizing furnaces.The characteristics of process and component are summarized and problems of the normalizing furnace during the prod... 

【机构】 商务部进出口公平贸易局； ...

对熔融态钢液进行处理,研究了电脉冲对于取向硅钢凝固组织的影响作用,利用正交试验法研究了脉冲电容、频率、处理时间和电压等脉冲参数的作用效果。结果表明:电脉冲对钢锭晶粒组织具有明显的细化作用,凝固组织的等轴晶比例大幅上升,影响等轴晶比例的最显著性因素为脉冲频率,最优正交试验参数为电容1 200μF,脉冲频率1 Hz,处理时间5 s,脉冲电压800 V。随着输入能量的增大等轴晶率先增大后减小,脉冲输入能量为某值时,等轴晶率最大,利用经典形核理论和热力学对这一现象进行了解释。 The influence of electric pulse on the solidification structure of oriented silicon steel was investigated by applying electric pulse in molten steel.The affection due to different electric pulse parameters such as electric capacity,frequency,applied time and voltage was studied by orthogonal design test.The result showed that solidification structure of oriented silicon steel could be improved by the electric pulse,and the equiaxed crystal ratio increased obviously.The most influential paramete... 

研究了应用电感耦合等离子体质谱法(ICP-MS)测定硅钢中痕量铜和镍的分析方法。采用硝酸分解样品,通过内标校正和基体匹配消除了基体干扰的影响,同时根据测量时存在的质谱干扰情况,选择同位素65Cu和60Ni作为测定元素和通过调节仪器参数使双电荷离子的产率最低,以减少带来的干扰。该方法用于硅钢中痕量铜和镍的测定,所得的结果与ICP-AES法测定结果完全吻合,各元素测定结果的RSD值小于5%,加标回收率为97.3%～100.3%。 A method for the determination trace copper and nickel in silicon steel by inductively coupled plasma mass spectrometry(ICP-MS) was studied.The samples were dissolved in HNO3.The effect of matrix interference was eliminated by internal standard correction and matrix matching.Meanwhile,according to the mass spectral interferences in determination,the isotopes including 65Cu and 60Ni were used as measuring elements.The yield of double-charge ions were minimized by adjusting instrumental parameters... 

两炉次无取向硅钢XG800WR（/%:0.003～0.004C、0.71～0.75Si、0.32～0.33Mn、0.004～0.007S、0.016P）的炼钢流程为铁水预处理（KR）-210 t顶底复吹转炉-钢包吹氩-RH脱碳精炼-230mm×1220 mm板坯连铸。53 t中间包钢水过热度为25～30℃,钢包到中间包采用长水口全程吹氩保护浇铸,中间包至结晶器采用浸入式水口浇铸。结果表明,在RH、中间包、结晶器过程中钢中总氧以及夹杂物数量和尺寸均明显降低;但在钢包到中间包过程T[O]、[N]和钢中夹杂物数量增加,说明长水口浇铸过程存在二次氧化。连铸坯中T[O]、[N]平均他分别为11×10^-6和30×10^-6,显微夹杂物数量平均为4个/mm²。铸坯中的显微夹杂物主要为3～5μm的AlN,同时存在少量的MnS、Al₂O₃·AlN和Al₂O₃·MgO·MnS。 The steelmaking flow sheet for two heats non-oriented silicon steel XG800WR（/%:0.003～0.004C. 0.71～0.75Si,0.32～0.33Mn,0.004～0.007S,0.016P） is hot metal pretreatment（KR）-210 t top and bottom combined blown converter-ladle argon blowing-RH decarburization refining-230 mm×1 220 mm slab casting.The superheating extent of liquid in 53 t tundish is 25～30℃,whole casting is shielded by blowing argon with long nozzle from ladle to tundish and the submerged nozzle is adopted in casting from tundish to mold... 

通过金相分析和电子背散射衍射技术研究了一种新型含铜无取向电工钢在950℃退火不同时间(3～180s)空冷后的组织和织构取向的演变。结果表明:该钢在退火3s时的主要织构为α和γ线织构,{100}<110>织构最强;退火20s时织构以<111><112>、{111}<110>、{112}<110>、高斯织构和立方织构为主,随着退火时间的延长,高斯织构和立方织构强度呈减弱趋势;合理控制保温时间有利于提高{100}、{110}面织构的占有率。 Evolution of microstructure and texture oriented of a new non-oriented electrical steel during annealing at 950℃for different times(3-180) s and air cooling was studied by metallography and electron back-scattering diffraction analysis.The results show that after annealing for 3 s most of the texture oriented alongα-fibre andγ-fibre,the intensity of {100}〈110〉was the strongest.{111}〈112〉,{111}〈110〉,{112}〈110〉,Gauss texture and cube texture were the main texture after annealing for 20 s,with the ... 

​6月28日国联证券发布：《电力设备出海2024年中期投资策略：需求方兴未艾，供给释...

本发明提供了一种无取向电工钢，以质量百分比计，其成分包括C：0.0010～0.0050％，Si≤2.5％，Al≤0.01％，Mn≤0.80％，P≤0.10％，S≤0.0070％，N≤0.0030％，其余为Fe及不可避免的杂质。本发明还提供了一种无取向电工钢的制备方法。本发明提供的一种无取向电工钢，不添加偏析或稀土等贵重元素且磁性能好、成材率高，本发明提供的无取向电工钢制备方法，工艺流程简单、生产周期短、制取成本低，且无需热轧板常化。

本实用新型公开了一种铁芯硅钢片卷料的上料装置，包括升降机构、固定座、转动执行机构和转动平台，所述固定座固定设置在地面上，所述升降机构相邻设置在固定座的一侧，所述固定座对立于升降机构的一侧设置有转动平台，所述转动平台的一端铰接设置在固定座上，且所述转动平台的另一端为自由端，所述转动平台在竖向面内朝向或远离于升降机构偏转，所述固定座上设置有转动执行机构，所述转动执行机构驱动转动平台转动；所述转动平台上的物料通过转动可位移至固定座和升降机构上，能够安全的、快速的将卷料转移至升降机构上，从而便于上料。

本发明属于冶金技术领域，具体涉及一种基于纳米析出强化制备高强度无取向硅钢的方法。该无取向硅钢包括如下重量百分比的化学成分：Si2.5～4.5wt.％，Ni2.5～6.5wt.％，Al1.0～3.0wt.％，Mn0.1～1.0wt.％，Cu0～1.0wt.％，(C+N+O+S)≤100ppm，其余为Fe；该无取向硅钢的制造方法包括：真空冶炼、浇铸锻造及热轧加工(或者薄带连铸)、常化热处理、酸洗与冷轧加工、再结晶退火、时效热处理。本发明制备的新能源汽车驱动电机转子用高强无取向硅钢厚度为0.20～0.50mm，磁感应强度B50为1.60～1.70T，P10/400为10～31W/kg，屈服强度Rp0.2为700～1000MPa，抗拉强度Rm为740～1150MPa，延伸率A为8～20％，可以满足用户对新能源汽车驱动电机用无取向硅钢性能要求。

本发明公布了以铜析出粒子为抑制剂的一类取向电工钢及其生产方法，所述取向电工钢化学成分的质量百分比为：C：0.001％～0.07％；Si：2.5％～3.5％；Si+Mn+Al：≤3.5％；Cu：1.0％～2.0％；S：≤0.003％；N：≤0.0045％；其余为Fe和不可避免杂质元素。该取向电工钢的生产工艺步骤可以包括：连铸坯板坯加热、热轧、常化、冷轧、脱碳处理、时效处理、二次再结晶退火处理等。本方法免除了高温热轧加热和二次再结晶后高温长时间加热以净化钢板基体的退火环节，进而可实现连续式二次再结晶退火，大幅度降低了生产能耗，并显著提高生产效率。

一种电工钢切片用导向装置，涉及电工钢生产装置技术领域，包括导向台、支撑腿、安装块、转轴、辊体、电动机、安装板、滑杆、移动板和导向板；支撑腿设置在导向台底部；安装块设置有两个，两个安装块均设置在导向台横向一侧，两个安装块沿纵向分布；转轴转动设置在两个安装块之间；辊体设置在转轴上，辊体位于两个安装块之间，辊体位于导向台上方；电动机设置在安装块上，电动机与转轴驱动连接；安装板设置有两个，两个安装板分别设置在导向台纵向两侧上部；滑杆设置有两个，两个滑杆均设置在两个安装板之间，两个滑杆沿横向分布。本实用新型能够在电工钢的钢带切片之前进行导向限位工步，使得电工钢切割时不会被切割歪，切片的精度高。