硅钢资料

采用化学气相沉积(CVD)渗硅处理工艺连续制备6.5%Si高硅钢,具有优质的软磁性能,通过理论研究化学反应并且用简单的试验设备做进一步的探讨。根据试验的结果对连续制备6.5%Si高硅钢的CVD工艺构造提出全面、有效的建议,实现制备6.5%Si高硅钢系统。 CVD method for continuously manufacturing 6.5%Si Steel Sheet has excellent soft magnetic.Carried out a theoretical study of related chemical reaction and performing basic research with a simple test apparatus.Based on the results,finally proposed an overall process configuration to realize such a production-CVD method for continuously manufacturing 6.5%Si Steel Sheet. 

【摘要】 <正>据武钢股份公司提供的消息,武钢将与...

采用双辊薄带连铸技术试制了3.98%Si-0.71%Al无取向硅钢铸带,研究了二次冷轧法对硅钢组织和磁性能的影响。结果表明:硅钢铸带显微组织为等轴晶组织,铸带再结晶较完全,常化对铸带显微组织影响较小。二次冷轧工艺和一次冷轧工艺下,最终退火后成品显微组织为等轴晶组织,二次冷轧法最终退火后的晶粒尺寸小于一次冷轧法。二次冷轧法能够提高成品磁性能. Effect of double cold rolling on magnetic properties and microstructure of 3.98%Si-0.71%Al non-oriented silicon Steel Sheets cast by twin-roll thin strip casting process were investigated.The results show that the structure of the thin strip is equiaxed crystal,the recrystallization is complete and normalizing has lesser effect on microstructure.Using both cold rolled and double cold rolled process,the microstructure is equiaxed grain after final annealing.The average grain size of annealed shee... 

对低温加热工艺生产的普通取向(common grain-oriented,CGO)硅钢的高温退火过程进行了中断实验,材料为含3.0%Si、0.5%Cu、0.009 8%S(均为质量分数)的以Cu2S为主抑制剂的普通取向CGO钢。原始板坯厚度为230 mm,于1 200℃均热后经4道次粗轧、7道次精轧至2.3mm;热轧板采用两次冷轧法轧至0.3mm,中间完全脱碳退火,最后于1 200℃高温退火。最后样品的磁性能:铁损P17/50为1.182W/kg,磁感应强度B8为1.897T。借助配有EDAX OIM电子背散射衍射(EBSD)系统的ZEISS SUPRA 55VP扫描电子显微镜,对高温退火过程中高斯晶粒的演变进行了研究,结果表明:升温过程中晶粒尺寸增长缓慢,650℃时取向分布函数(ODF)图出现高斯织构组分,但强度很弱,高斯晶粒偏离角小于9°;950℃时高斯晶粒平均生长速度超过其他晶粒;950~1 000℃时高斯晶粒异常长大,偏离角降至约3°;在950℃之前高斯取向晶粒相比于其他晶粒没有尺寸优势。 The high-temperature annealing process of common grain-oriented(CGO)silicon steel was investigated by interrupting test.The samples were rolled from CGO silicon steel slab under low reheating temperature.The CGO silicon steel,taking Cu2S as the main inhibitor,contains3.0%Si,0.5%Cu,and 0.0098%S.The original casting slab is 230mm in thickness.After 1 200℃reheating,four-pass rough rolling and seven-pass finish rolling were conducted to make the thickness of the slab get to 2.3mm.Then the hot rolled... 

介绍了双蓄热燃烧技术的特点和高温硅钢加热炉的特点,探讨了双蓄热燃烧技术在高温硅钢加热炉中使用的技术难点,分析了双蓄热燃烧技术在高温硅钢加热炉上使用的可能性。 Introduced characteristics of double regenerative combustion technology and high temperature silicon steel reheating furnace,discussed technical difficulties for using double regenerative combustion technology,analyzed the possibility of double regenerative combustion technology applied to high temperature silicon steel reheating furnace. 

【摘要】 <正>2012年3月29日中国钢铁工业协会在上...

研究的两种取向硅钢（%:No1-0.042C、3.16Si、0.009Al、0.07Mn、0.50Cu、0.015S、0.0084N和No2-0.040C、3.20Si、0.014Al、0.22Mn、0.49Cu、0.016S、0.008 2N）由50 kg真空感应炉冶炼,锻成（mm）350×120×35板坯,经1 250℃30 min加热,开轧温度1 100℃,5道次热轧成2.3 mm板,终轧温度950～1 000℃。实验结果表明,两热轧板沿板厚方向存在组织和织构的不均匀性,热轧板次表层为再结晶组织,有较强的Goss织构组分;中心层为形变组织,具有典型的形变织构。含0.22%Mn的No2钢次表层{110}〈001〉织构组分比含0.07%Mn的No1钢弱,中心层{001}〈110〉织构组分大大强于0.07%Mn No1钢,导致两者磁性能差异,0.22%Mn No2钢磁感应强度(B₈₀₀)和铁损(P_1.7/50)分别为1.87 T和1.24 W/kg,0.07%Mn No1钢分别为1.88 T和1.18 W/kg。 Studied both grain-oriented silicon steels（%:No1- 0.042C,3.16Si,0.009Al,0.07Mn,0.50Cu, 0.015S,0.0084N and No2-0.040C,3.20Si,0.014Al,0.22Mn,0.49Cu,0.016S,0.0082N） are melted by a 50 kg vacuum induction furnace,forged to（mm） 350×120×35 slab,heated at 1 250℃for 30 min,with beginning rolling temperature 1 100℃hot-rolled to 2.3 mm plate by 5 passes,finishing-rolled at 950～1000℃.Test results show that the structure and texture along thickness of both hot-rolled plates are inhomogeneous:the subsurface ... 

利用OM、SEM、TEM等实验方法研究了卷取工艺对一种新型含铜无取向电工钢晶粒度和析出相的影响。结果表明,该电工钢热轧带卷取后的晶粒尺寸为18～24μm,在卷取过程中,热轧带中有一定数量的第二相析出,经EDS能谱及选区电子衍射分析,这些析出相主要为AlN。随着卷取工艺的变化,该电工钢的晶粒度大小变化不明显,析出相的类型、尺寸大小不发生改变,体积分数发生一定的改变。 The effects of coiling process on grain size and precipitates of a new copper-bearing non-oriented electrical steel were investigated by OM,TEM and other experimental method.The results show that the grain size of hot-rolled bands after coiling is 18～24 μm.The second phases precipitate during coiling process.They are mainly AlN by EDS spectra and selected area electron diffraction.With the change of coiling process,the grain size of the electrical steel does not change significantly;the type and... 

{100}织构因具有两个易磁化方向能够明显的提高磁性能,因此如何在表面获得具有{100}织构一直是无取向电工钢研究焦点。本文主要介绍了获得{100}织构的主要工艺方法及其基本原理,并结合实际生产过程对各工艺方法的优缺点进行了分析;一方面,优化无取向电工钢的成分,降低碳、锰元素含量以避免脱碳退火和真空退火,简化生产工艺;另一方面,调节升温速度、降温速度和退火气氛,使{100}晶面的表面能或弹性应变能最低,制备具有{100}织构柱状晶组织的无取向电工钢是今后的发展方向。 Because { 100} texture has two easy magnetization directions,which can significantly improve magnetization properfies,how to develop { 100} texture is a focus for researchers and manufactures. In the paper,main manufacturing processes and basic principle are introdued,and their advantages and disadvantages in practical production are analyzed. On the one hand,the production process can be simplified by optimizing chemical compositions,such as reducing the content of C and Mn,which can avoid deca... 

冷轧无取向硅钢（/%:0.003C,2.35Si,0.22Mn,0.011P,0.002S,0.36A1,0.003 0N）经890℃或940℃3 min常化的2.3 mm热轧板冷轧成0.35 mm薄板。研究了常化温度和800⁹20℃3 min退火对该钢高频（400Hz）磁性能和抗拉强度的影响。结果表明,830⁹20℃退火时高频铁损P_10/400值最低,随退火温度增加,晶粒尺寸增大,钢的抗拉强度降低;该钢的最佳热处理工艺为常化温度940℃,退火温度830℃,其抗拉强度R_m、高频铁损P_10/400和磁感应强度J₅₀分别为565 MPa,21.5 W/kg和1.69 T。 The cold-rolled non-oriented silicon steel（/%:0.003C,2.35Si,0.22Mn,0.011P,0.002S,0.36A1,0.003 0N） is cold-rolled to 0.35 mm sheet from 2.3 mm hot-rolled plate normalized at 890 ℃ or 940℃ for 3 min.The effect of normalizing temperature and annealing process at 800 ⁹20 °C for 3 min on high frequency（400 Hz） magnetic properties and tensile strength of the steel has been tested and studied.Results show that with annealing at 830 920 ℃the high frequency iron loss value P_10... 

采用铸坯低倍组织检验和化学分析的方法,研究板坯连铸机二冷区电磁搅拌器电流和频率参数对无取向电工钢XG800WR板坯中心偏析和等轴晶率的影响,结果表明:铸坯等轴晶率随着搅拌器电流强度和电流频率的增大而增加。采用二冷区电磁搅拌可减小中心易偏析元素S的偏析,试验得出:减小铸坯S偏析效果最好的电磁搅拌参数为电流380～400A,频率6Hz。 The effect of electromagnetic stirring current and frequency parameter at secondary cooling area on the central segregation and equiaxed crystal ratio of XG800WR non - oriented electrical steels slab was investigated through the methods of chemical and macrostructure analysis.The results shows that the rate of equiaxed crystal zone is going up with increasing of current intensity and current frequency.Electromagnetic stirring in the secondary cooling area can be easily reduced segregation caused... 

借助OM、激光共聚焦显微镜、质谱仪和电解萃取等设备和方法，研究了添加微量稀土La（质量分数0.001 1%）的取向硅钢在轧制前采用不同加热保温时间对抑制剂固溶行为的影响。结果表明：当稀土取向硅钢在1 250℃分别保温10、20、30 min后，试验钢晶粒尺寸随保温时间延长有先快后慢的长大趋势；三种抑制剂元素Mn、Cu和Al均发生固溶，保温时间对Mn和Cu两种元素的固溶影响明显，固溶量分别由69.8%和43.7%增加至84.2%和85.2%；随着保温时间的延长，稀土取向硅钢中抑制剂的小尺寸未溶物逐渐减少直至消失，较大尺寸未溶物（300～600 nm）逐渐转变为小尺寸未溶物逐步溶入基体中，数量减少且未溶物的类型由复杂逐渐转变为单一。 In this paper the solid solution behavior of the inhibitor under various holding time in 0.001 1 %La oriented silicon steel during reheating had been investigated by using OM, LM, methods of electrolytic extraction and mass spectrometer. The results showed that grain size of the test steel increased significantly with the holding time prolonging when the rare earth oriented silicon steel was heated to1 250 ℃ and held for 10, 20 min and 30 min respectively, and the growth trend slowed down after ...