熔盐电沉积过程温度对1.6Si无取向硅钢Si扩散的影响
试验了通过NaCl-KCl-NaF-SiO2熔盐在电流密度50 mA/cm2、电沉积脉冲电流正反向比9:1和750850℃60min电沉积下阴极（/mm）20×20×0.5的1.6Si无取向冷轧硅钢片断面层硅的分布,并通过计算得出Si的扩散系数。结果表明,电沉积温度由750℃提高至850℃时,试样中Si含量增加,扩散的深度由18μm提高到40μm;电沉积温度与Si在钢中的扩散系数近似符合Arrhenius指数关系。 The distribution of silicon at cross section of cathode（/mm） 20 × 20 × 0.5 sheet of 1.6Si non-oriented cold rolled silicon steel after electro-deposit treatment by NaCl-KCl-NaF-SiO2 molten salt with current intensity 50 mA/cm2,electro-deposit pulse current positive-negative ratio 9:1 at 750 850 ℃ for 60 min has been tested and the diffusion coefficient of Si is obtained by calculation.Results show that with increasing electro-deposit temperature from 750 ℃ to 85...
多元抑制剂对高磁感取向硅钢性能的影响
介绍在取向硅钢生产中抑制剂的作用以及多元抑制剂的机理和应用情况,分析多元抑制剂方案中各种元素对高磁感取向硅钢性能的影响,并根据生产实践提出了进一步研究的方向. The role of an inhibitor in the production of grain oriented silicon steel,and the mechanism of multiplex inhibitor in the production are described in the present article.In addition,the influence of various elements in the multiplex inhibitor on the performance of grain oriented silicon steel with high magnetic induction is elucidated.Further work needed in this research is also indicated.
节能电机用无取向电工钢带退火工艺的试验与应用
针对节能电机对无取向电工钢在磁性能方面的特殊要求,采用普通W600牌号的热轧板为原料,通过大量的现场工艺试验,研究总结出了\"超低张力\"的运行工艺、\"先快后慢\"的加热工艺、\"先湿后干\"的退火脱碳工艺、\"先缓后急\"的冷却工艺,生产出P1.5/50≤4.0 W/kg、B50≥1.70 T的冷轧电工钢产品,满足了节能电机的要求。 Based on the special requirements of no-oriented electrical steel for saving energy motor in magnetic aspects,using common W600 brand of hot rolled plate as raw material,through a large number of real tests,an ultra-low tension process,heating process which was quick at first and then slow,annealing decarburization process which was dry after the first wet,and a cooling technology of \"slow after the first urgent\" were concluded.Electrical steel product with P1.5/50≤4.0W/kg,B50≥1.70T was produced...
电力变压器用高磁感取向硅钢的发展及应用
阐述了国内外高磁感取向硅钢的生产研究水平与发展趋势,包括通过提高高斯晶粒取向度、细化磁畴、涂覆张力涂层、减薄钢片厚度进一步降低铁损以及低温加热技术和短流程技术新工艺。分析高磁感取向硅钢在我国大型电力变压器上的应用情况,结果表明,发展更薄规格高磁感、低铁损、低磁致伸缩取向硅钢可为大型变压器的安全性、节能性及环保性提供有效保障。 The research progress and development trend of high magnetic induction grain-oriented silicon steel at home and abroad are summarized,including the technology of improving the Goss alignment,refining domain wall,adding stress coating,decreasing thickness of sheet,and the new technique of reducing heating temperature of casting slab and shortening operational.Moreover,the application of high magnetic induction grain-oriented silicon in power transformer is presented.Developing grain-oriented sili...
不同尺寸电工钢样品磁性能检测对比分析
对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ...
钒钛对取向硅钢组织、织构和析出物的影响
通过在实验室条件下模拟薄板坯连铸连轧流程,并在以Cu2S为主抑制剂制造普通取向硅钢(CGO)的基础上,加入适量钒钛,研究了钒钛对取向硅钢组织与磁性能的影响。结果表明,适量钒钛使热轧板和脱碳退火板组织更好,尤其使脱碳退火板的晶粒更加细小和均匀;加入适量钒钛不但使热轧板表面高斯织构强度更高,更使脱碳退火板中有利于高斯织构发展的γ织构强度更高;适量钒钛能形成Cu2S+(V,Ti)N等复合析出物,起到辅助抑制剂作用,加强抑制能力。细小均匀的晶粒、强度更高的有利织构和更强的抑制能力使CGO钢磁性能更佳。 Effect of V and Ti on microstructure and magnetic properties of conventional grain-oriented silicon steel(CGO) were investigated under simulated thin slab continuous casting and rolling process in laboratory with Cu2 S as the dominant inhibitor. The results show that appropriate amount V and Ti make the microstructures of the hot rolled sheet and the decarburizing annealed sheet better,especially make the grains of the decarburizing annealed sheet more tiny and uniform. Adding appropriate V and ...
钙处理对无取向硅钢中非金属夹杂物的影响
采用电解法和扫描电镜研究了300 t转炉-RH精炼钙处理对无取向硅钢板（%:≤0.005C、1.2～2.2Si、0.2～0.6Mn、≤0.20P、≤0.005S、0.2～0.6Al、0～0.01Ca）中夹杂物的影响。结果表明,钢中Al含量为0.25%和0.35%时,钢中溶解氧均小于1×10-4%,钙处理后都会产生CaS夹杂物,尤其是含0.35%Al的钢水;钙处理可以有效减少钢中的夹杂物数量,尤其是0.5μm以下的微细夹杂物数量;钙处理后夹杂物的种类以AlN、CaS为主,同时还含有少量的氧化物夹杂物以及AlN-CaS复合夹杂物,尺寸主要为1.5～5.0μm。 The effect of 300 t converter-RH refining calcium treatment on inclusions in non-oriented silicon steel sheet （%:≤0.005C,1.2～2.2Si,0.2～0.6Mn,≤0.20P,≤0.005S,0.2～0.6A1,0～0.01Ca） has been studied by electrolysis and scanning electron microscope.Results show that with 0.25%and 0.35%Al content in steel,all the dissolved oxygen in liquid is less than 1×10-4%,and the CaS inclusions are produced after calcium treatment,especial for the liquid containing 0.35%Al;the amount of inclusions in ste...
试样剪切应力对冷轧无取向电工钢磁性能的影响
电工钢试样加工产生的剪切应力会恶化钢板的磁性,对不同牌号硅钢片的横向、纵向试样退火前后磁性能的变化进行研究,结果表明:无取向硅钢片在剪切过程中横向、纵向的磁性受到剪切应力影响是不一样的。 The electrical steel sample processing magnetic of electrical steel will worsen due to the shear stress of sample. In this paper,the magnetic change of transverse,longitudinal specimens of different type of silicon steel sheet before and after annealing are studied. The results show that the magnetic of non- oriented silicon steel sheet affected in the process of shear is not the same in horizontal and vertical direction.