无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason... 

利用本钢技术中心试验厂技术手段,并与北京钢铁研究院合作,试制了用作家电用电机、微电机、小电机或部分中型电机铁芯的冷轧无取向电工钢。试制钢硅含量小于0.5%,钢板表面平滑,公称厚度0.5mm,且厚度均匀偏差小,性能测定结果表明,产品的磁性能、力学性能满足其使用要求。 BX STEELTechnology Center pilot plant using technical means,and with Beijing Iron and Steel Research Institute,trial cold rolled non-oriented electrical steel that has been used as appliance motor core,micro motor core,small motor core,or part of the medium-sized motor core。Trial steel of silicon content is less than 0.5%,steel plate surface is smooth,the nominal thickness of 0.5mm,and the thickness deviation is small,performance measurement results show that the magnetic properties,mechanical p... 

通过对3%Si CGO硅钢进行恒变形速率、不同变形温度下的单道次压缩实验,结合Thermal-Calc软件,金相分析,SEM及EBSD技术,研究了取向硅钢热变形过程中组织和微观织构的变化规律。结果表明:实验钢是在双相区变形,变形后组织主要是铁素体和少量的珠光体。随变形温度的升高,晶粒由长条状变为等轴状,尺寸逐渐变大;CGO硅钢在热变形过程中立方{100}<001>取向是较为稳定存在的。随着变形温度的提高,{111}<110>等取向逐渐转向{110}<1 10>取向,且{110}<1 10>取向逐渐变得锋锐。 3% Si CGO silicon steel was studied at constant strain rate and different deformation temperatures by single-pass compression deformation experiments to reveal the evolution of microstructure and texture during thermal deformation in oriented silicon steel,and the Thermal-Calc software,metallurgical,SEM and EBSD technique was used in the experiment. The results show that experimental steel is deformed at the temperatures of two-phase zone. The microstructure of the deformed steel consists of fer... 

采用经验设计法初步确定了取向硅钢铸坯感应加热线圈设计参数,应用Ansoft仿真软件分别对36组不同线圈高度、线圈内径的感应加热炉在不同频率下的三维整体磁场和铸坯的温度场进行了数值仿真。通过对比仿真结果,确定电磁场分布最佳的一组感应加热炉设计参数为线圈高度h=1.50 m、线圈内径D1=0.575 m、电流频率f=110 Hz。在该参数下应用Ansoft仿真软件对取向硅钢铸坯感应加热炉的温度场进行了仿真,结果发现温度场分布均匀,可满足取向硅钢铸坯加热要求。 The induction heating coil design parameters for the oriented silicon steel casting blank were determined preliminary by experience design method,and 36 groups three-dimensional electromagnetic field with different height and inside diameter of coil under different frequencies of the induction heating furnace and the temperature field of the casting blank were investigated by numerical simulation using Ansoft simulation software. By comparing the simulation results of electromagnetic field distr... 

取向硅钢因其高磁导率、低矫顽力和大电阻系数等特性，被广泛应用于大中型变压器和大型电动机铁芯的制造。因取向硅钢性能和成分控制严格，生产工艺复杂，故其产品代表了钢铁企业特殊钢生产的最高水平。本文介绍了新钢公司卷板厂1580热连轧线生产取向硅钢过程中出现的窄尺问题，研究了取向硅钢产品的特点，分析了热轧过程中的组织转变，并结合生产实际提出了改进措施。通过对加热炉钢坯加热模式、粗轧轧制策略、精轧轧制工艺、二级模型等方面的优化和改进，取向硅钢窄尺情况明显好转，提高了产品的成材率和市场口碑。 The oriented silicon steel is widely used in the iron core manufacture of large and mediumsized transformers and large motors because of its high permeability, low coercivity and large resistance coefficient. Due to the performance and composition control of oriented silicon steel is strict, the production process is complex,therefore, its products represent the highest level of special steel production in iron and steel enterprises. This paper introduces the problem of narrow gauge in the produ... 

采用双辊薄带连铸技术试制了3.98%Si-0.71%Al无取向硅钢铸带,研究了二次冷轧法对硅钢组织和磁性能的影响。结果表明:硅钢铸带显微组织为等轴晶组织,铸带再结晶较完全,常化对铸带显微组织影响较小。二次冷轧工艺和一次冷轧工艺下,最终退火后成品显微组织为等轴晶组织,二次冷轧法最终退火后的晶粒尺寸小于一次冷轧法。二次冷轧法能够提高成品磁性能. Effect of double cold rolling on magnetic properties and microstructure of 3.98%Si-0.71%Al non-oriented silicon Steel Sheets cast by twin-roll thin strip casting process were investigated.The results show that the structure of the thin strip is equiaxed crystal,the recrystallization is complete and normalizing has lesser effect on microstructure.Using both cold rolled and double cold rolled process,the microstructure is equiaxed grain after final annealing.The average grain size of annealed shee... 

主要研究了0.7%Si无取向电工钢退火试样的组织、晶粒尺寸和织构对其磁性能的影响。结果表明,随着退火温度的升高,晶粒尺寸逐渐增大,组织的均匀性得到改善;ɑ取向线上的纤维织构多集中于{114}<110>和{223}<110>附近,再结晶结束后,织构含量变化不大。{111}<110>织构取向密度值随温度升高而下降,{112}<111>织构与{111}<110>织构变化相反。晶粒尺寸增大对磁感强度的影响较小,而对铁损的影响较大。 Influences of microstructure,grain size and texture on the magnetic properties of 0.7% Si non-oriented electrical steels annealed samples were studied.The results show that with annealing temperature increasing the average grain size is increased gradually.Uniformity of the microstructure is improved;the textures of ɑ-fiber gathered in the vicinity of the { 114} < 110 > and { 223 } < 110 > texture.After recrystallization,the volume fraction of texture changes small.{ 111} < 110 &g... 

【作者】 朱凤泉； 黄生银； ...

对CSP流程生产的高磁感无取向电工钢50W1300在偏离轧制方向不同角度处的磁性能进行了测试和分析。结果表明:在偏离轧向不同角度处,磁性能差异显著,尤其在α=60°时磁感最低;偏离轧制方向不同角度处的磁性能大小取决于织构类型、强度及分布状态;增强{100}<0vw>和α、η取向的有利织构组分,降低不利的γ取向织构组分,且使有利织构组分分布越漫散,磁各向异性越小。 Magnetic properties of high magnetic induction non-oriented electrical steel 50W1300 produced by CSP processes were investigated with different direction in relation to the rolling direction.The result shows that magnetic properties are significantly different in relation to the rolling direction,in particular,the minimum magnetic induction occurs at 60° in relation to the rolling direction.Magnetic properties of different directions in relation to rolling direction depend on type and distributi... 

实验室模拟薄板坯连铸连轧(TSCR)流程制造高磁感取向硅钢,借助电子背散射衍射(EBSD)技术对不同Sn含量的热轧板织构进行了研究。研究结果表明:不同Sn含量热轧板表层及次表层均为高斯织构、铜型织构及黄铜织构的混合织构,中心层为{100}面织构;Sn含量为0.1%时,热轧板表层及次表层高斯织构组分最多,取向密度最大,成品磁感最高,达到1.875 T。 Texture of grain oriented silicon steel hot rolled by thin slab casting and rolling process(TSCR) in laboratory with different Sn contents was analyzed by electron back-scattered diffraction(EBSD).The results show that the hot rolled slabs with different Sn contents have the same texture,i.e.,Goss,Copper and Brass.Specifically,the texture of core layer is {100};While the hot rolled slab with 0.10% Sn,the surface layer and subsurface layer have a sharpness Goss texture and the finished products h... 

无取向硅钢中夹杂物的存在会抑止晶粒生长,使基体的均匀连续性中断,其在钢中的形态、含量及分布情况都不同程度影响着硅钢的性能,尤其是对磁性能起关键的作用。因此,全尺度分布考察夹杂物对无取向硅钢夹杂物的研究极为重要。本实验确定了适用于不同牌号无取向硅钢夹杂物全尺度分布的分析方法:样品制备—小样电解—过滤喷金—根据不同牌号的要求选择合适的放大倍率扫描观测—夹杂物颗粒的分类统计。通过统计的结果,结合电解的失重量可以得到不同尺度的体积分布数据。实验分析了不同牌号和工艺无取向硅钢夹杂物的种类、形貌、大小和尺度分布,并初步考查了夹杂物与磁性能的关系,对无取向硅钢的工艺研究具有一定参考价值。 Inclusions in non-oriented silica steel could inhibit the growth of grain and cause discontinuity of micro-structure.The configuration,content and size distribution of inclusion have different effects on the performance of silica steel,especially significant on the magnetic property.Therefore,it is very useful to completely characterize inclusions with full size distribution in silica steel.In our research,full size analysis method for inclusion in silica steel had been established as follows: s... 

以市场上购买的取向硅钢成品板为原料，经不同压下率冷轧至0.23～0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量，利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征，分析了硅钢超薄带的塑性变形行为。结果发现，在平面压缩应力下，{112}<111>滑移系的取向因子较大。随冷轧压下率的增加，Goss织构的含量逐渐减少，{212}<141>织构组分的含量先增加后减少，{111}<112>织构组分的含量逐渐增加，织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶，其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。 The commercial finished oriented silicon steel plate as the raw material were rolled to 0.23-0.08 mm. With the X-ray diffractometer(XRD), the texture components and their volume fractions in the cold-rolled samples were detected. And the orientation factor distribution of the cross-section of the samples was measured by the electron backscattering technique(EBSD). The morphology and crystallographic characteristics of twins were observed, and the plastic deformation behaviors of the ultra-thin o...