硅钢资料

针对攀钢高硫铁水冶炼现状,结合不同生产工艺路线,论述了攀钢近年来为实现低硫电工钢的生产,在铁水预处理、转炉冶炼、钢水精炼过程中硫控制技术的开发与应用,形成了低硫洁净钢生产工艺技术,实现了低硫电工钢的生产。低硫电工钢RH脱硫率可达到20%左右,成品[S]控制在0.006%左右。 According to the smelting situations of hot metal with high sulphur content at Panzhihua Steel,combined with different produce processes,technologies for controlling the sulfur content during hot metal pretreatment,converter smelting,and second refining are developed. Technologies in low-sulfur clean steelmaking are formed. Low-sulfur electric steel are produced. As for the desulfurization rate of lowsulfur electric steel can reach about 20%,and the content of [S] in products is controlled to ab... 

借助实验室设备研究了B元素对高牌号无取向硅钢热轧板组织和磁性能的影响。结果表明,与无硼钢相比,含硼钢的热轧板晶粒尺寸略小,析出物的类型和尺寸没有区别,主要是AlN和(AlN+MnS)复合析出物,少量的MnS析出物,尺寸集中在1.0～2.5μm范围内。未发现BN析出物。在力学性能方面,B对钢的软化作用不明显。在磁性能方面,含硼钢的铁损为3.215W/kg,磁感为1.710T,综合磁性能比无硼钢差。 Influences of boron on microstructure and properties of hot rolled band in high-grade non-oriented silicon steel are researched in this paper by experimental equipments.Compared with boron-free steel,the result shows that boron-bearing steel has smaller grain size,but the type and size of precipitations have no differences.The main precipitates are AlN,(MnS + AlN) composite precipitate and few MnS,the range of which are between 1.0 μm and 2.5 μm.BN precipitation is not found.With reward to mecha... 

涂层技术在高磁感取向硅钢生产中起着重要的作用.根据生产实践,介绍了高磁感取向硅钢生产中涂层的种类和作用、涂料的成分和对产品性能的影响、涂层工艺质量控制要点和检验方法等,并提出了通过优化涂层工艺改善高磁感取向硅钢性能和外观质量的方法. Surface coating technique plays an important role in producing high magnetic inductivity grain-oriented silicon steel.Based on production practice,this paper describes the types and function of the coating,the composition of the coating and its effect on the product performance,the quality control and inspection method for the coatings,as well as proposes ways to improve the magnetic property and surface quality of the steel by optimizing the coating process. 

在实验室模拟CSP工艺条件下制备了取向硅钢,研究了二次冷轧中间退火工艺对组织和织构的影响。结果表明,中间退火温度对取向硅钢脱碳,高温退火组织及织构均产生明显影响。经940℃中间退火后,取向硅钢脱碳再结晶晶粒较850℃中间退火的多,且再经高温退火处理后,晶粒粗化,最大晶粒尺寸达4.8 mm;高斯织构组分密度达27.00,较850℃中间退火试样高。 Grain-oriented silicon steel was prepared by simulated CSP technology in laboratory. Effects of secondary cold-rolled intermediate annealing on microstructure and texture were studied. The results show that intermediate annealing has obvious effects on the microstructure and texture of the steels after decarburization annealing and high temperature annealing. After intermediate annealing at 940 ℃,recrystallized grain of decarburization annealed steel is more than that of intermediate annealed at... 

【作者】 陶永根； ...

研究二次冷轧压下率对于硅的质量分数为3.0%的无取向硅钢组织结构和磁性能的影响。结果表明:当第二次冷轧压下率从0变化至16.7%时,铁损逐渐增加,磁感逐渐降低。当第二次冷轧压下率大于16.7%时,随压下率的增加,铁损逐渐减小,磁感逐渐增加。当第二次冷轧压下率大于38%时,二次冷轧法所能获得的磁性能明显优于一次冷轧法。 Effect of double cold reduction on magnetic,microstructure and texture of 3.0% Si non-oriented silicon steel sheets was investigated.The results show that the iron loss increases and magnetic induction reduces as the percentage redcution in secondary cold rolling changes from 0 to 16.7%.The core loss can be reduced remarkably,and magnetic induction can get a little benefit if the percentage redcution in double cold reduction is higher 16.7%.In case of higher than 38% of the percentage redcution ... 

针对传统工艺生产硅钢周期长、能耗大等缺点,采用双辊连铸工艺制备3%Si无取向硅钢连铸薄带,利用MEM,SEM和TEM观察了铸带的组织、织构及析出物,同时对比了Al的质量分数为0.6%和0.9%的连铸薄带在组织、织构及析出物特征方面的异同.结果表明:双辊连铸工艺生产的3%Si无取向硅钢铸带的组织为均匀等轴晶粒,平均晶粒尺寸约为300μm;织构组成随Al质量分数的不同具有明显差别,Al质量分数为0.9%的铸带中{100}织构强度是随机织构的7倍;铸带中的析出物为AlN和MnS,最大尺寸分别为500和50 nm左右. Given the lengthy production cycle,high energy consumption,and other shortcomings of the traditional process for producing silicon steel,a twin-roll casting process was used to produce 3%Si non-oriented silicon steel casting strips. MEM,SEM,and TEM were used to compare micro-structure,texture,and precipitate characteristics of a casting strip containing 0.6%Al with another containing 0.9%Al.The structure of 3%Si non-oriented silicon steel produced by the twin-roll casting process was a uniform i... 

目前随着电工钢用户冲压设备的升级,冲压速度逐步提高,对电工钢产品的硬度和强度指标提出了更高的要求。与普通硬度级别的无取向硅钢相比,高硬度50BW600的Hv硬度提高15~20,达到125以上,同时对电磁性能指标也有较高要求。本钢通过化学成份和热轧及冷轧连退生产工艺的设计,经过小批量生产试验,满足用户要求。通过对工艺的严格控制,在大批量生产过程中,保证了产品的力学性能和电磁性的检验合格率。 Currently with upgrading of stamping equipment of silicon steel user, gradually increasing of stamping speed, propose higher demand for hardness and strength of silicon steel. Compared with conventional 50BW600, high hardness 50BW600 have higher hardness, reach greater than 125Hv. Through design of chemical composition with hot mill and annealing, production test of small quantities, stamping performance meet user request. 

热卷箱位于热连轧带钢生产线粗轧与精轧机之间,是热连轧生产中比较理想的中间保温设备。由于取向硅钢变形温度区间较窄,在生产中易出现边裂现象,同时中间坯的边部温度难于得到保证,因此一般不采用热卷箱设备生产,限制了传统热连轧生产线产品开发的品种。通过合理优化热卷箱控制工艺参数,解决了某厂传统热连轧生产线用热卷箱生产取向硅钢的边部质量问题,成功地生产出取向硅钢带。 The hot coil-box is an ideal heat retaining apparatus for hot rolling,lined between roughing mill and finishing mill. But oriented silicon steel has a narrow deformation temperature range,so that the edge crack easily occurs and it is difficult to insure the temperature of the intermediate blank. Therefore,the hot coil-box is rarely used in producing oriented silicon steel,which restricts the product development of the traditional hot rolling line. The article reasonable optimized process parame... 

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。 Microstructure development and texture evolution of conventional grain oriented silicon steel,which were annealed at same annealing temperature and different annealing time under wet H2 atmosphere,were investigated through metallographic observation and electron backscattered diffraction analyzing.The results show that the primary recrystallization finishes in 120 s at 820 ℃ under wet H2 atmosphere.With the extending of annealing time,{111}<112> texture decreases,{111}<110> texture d... 

试验的铸态取向硅钢（/%:0.044⁰.056C,3.12³.32Si,0.08⁰.11Mn,0.002⁰.008S,0.002 9⁰.029 1Als,0.006 2⁰.010 9N）由30 kg高频真空感应炉熔炼。通过场发射扫描电子显微镜/能谱仪（FE-SEM/EDS）研究结果表明,0.002 9%Als钢中氧化物主要为SiO₂,存在片状、棒状及近似球状的独立MnS,未发现含铝的氧化物或氮化物;0.0090%Als钢中出现以Al₂O₃为主的复合氧化夹杂物,存在MnS与AlN的复合析出物。钢中Als增加,复合析出物多呈簇状发展。氧化物容易成为MnS-AlN复合析出的核心,钢中Als含量越低,夹杂物中的MnS含量越高;作为核心的氧化物夹杂的尺寸越小,形成的复合夹杂物的形状越规则,尺寸也越小。热力学计算结果表明,钢中Als含量主要影响了钢中氧化物夹杂的组成和AlN的析出温度及析出量。 Test as-cast grain-oriented silicon steel（/%:0.044 ⁰.056C,3.12 3.32Si,0.08 0.11Mn,0.002⁰.008S,0.002 9⁰.029 1 Als,0.006 2⁰.010 9N） is melted by a 30 kg high frequency vacuum induction furnace.The research results by using field emission-scanning electron microscope/energy dispersive spectrometer（FE-SEM/EDS） show that in 0.002 9%Als steel the main oxide is SiO₂,and there is independent laminable,rod-like and approximate ... 

采用CVD法制备6.5%Si高硅钢,介绍了具体的制备工艺过程,研究了温度对渗硅速率和试样质量减轻的影响,同时分析了扩散时间对高硅钢中硅分布的影响。结果表明:在CVD反应过程中,反应温度高于1050℃将大大提高渗硅速率,但当温度大于1200℃后,渗硅速率趋于稳定;渗硅后,试样会减轻、减薄,随着温度升高,试样质量减轻的速率逐渐增大,在1200℃左右趋于稳定;扩散时间越长,硅分布越均匀,结合制备效率进行考虑,满足Δw表-中/b≤5的时间为适宜的扩散时间。 6.5%Si high silicon steel was manufactured by using CVD method and the process was introduced,the influence of temperature on the siliconizing rate and quality reducing rate,diffusion time on silicon distribution were investigated.Results as follows: the siliconizing rate will increase quickly when the temperature is higher than 1050 ℃,but the siliconizing rate will become steadily as the temperature up to 1200 ℃;The quality reducing rate will increase with the elevating of temperature and the r...