结合冶炼无取向硅钢的生产实际,对钢中硫的来源,以及炉渣性质、钢水温度、底吹强度对脱硫的影响进行了分析。研究表明,转炉钢中硫的主要来源为铁水、废钢、铁水渣及石灰带入;冶炼硅钢时,终渣碱度为3.0~3.5,w((FeO))≤20%,终点钢水温度大于等于1 680℃,加大底吹搅拌强度能提高转炉脱硫效果。硅钢平均出钢硫的质量分数为0.004 8%,能满足无取向硅钢对硫含量的要求。 With the actual production of non-oriented silicon steel,the source of sulphur and the effect of metallugic parameters like slag properties,temperature of molten steel and bottom stirring on desulphurizing ability were investigated.The results show that the main source of sulphur is molten metal,scrap,the remaining slag volume in hot metal and lime.The degree of desulphurization for smelting silicon steel can be increased through adopting the following measures,such as the basicity of finishing ... 

针对目前大部分无取向电工钢处理液为含铬处理液、且需在较高温度下固化的情况,在分析成膜物质性质的基础上,试验研究了一种可低温快速固化的电工钢环保绝缘处理液,研究了其涂装工艺,并测定了涂层的附着性、绝缘性、耐热性、耐蚀性等性能。试验结果表明:该处理液可在150~250℃下快速烘干固化,涂层表面光滑且致密均匀,性能优良,可满足中小电机的使用要求。 At present,most of the insulating fluid for non-oriented electrical steel contains chromium,and should be cured at high temperature.On the basis of analyzing the characteristics of the film-forming substance,a kind of eco-friendly insulating fluid with lower curing temperature for non-oriented electrical steel sheet was developed in the experiments.Then its coating process was studied,and the adhesiveness,insulativity,heat resistance,corrosion resistance and other properties of the coating was m... 

对无取向电工钢中的夹杂进行了系统的分析。利用小样电解,采取不同电解液,不同的分离方法对无取向电工钢中稳定和不稳定夹杂物进行了提取、分离和收集。利用扫描电镜(SEM)、X-射线衍射、ICP等对电解分离收集的夹杂物进行了定性和定量分析。 The inclusion analysis of the non-oriented electrical steel has been investigated.By using small sample electrolytic analysis,with different electrolytes and different separation ways,the stable inclusions and unstable inclusions was drew,separated,and collected.With utilizing the methods of SEM,X-ray and ICP,the qualitative and quantitative analysis of inclusions in the non-oriented electrical steel was obtained. 

对高磁感取向硅钢冷轧板分别进行800、950、1050和1120℃不脱碳的预退火处理,在800℃预退火,成品的磁性能较好。织构分析的结果表明,随着预退火温度升高,初次再结晶后有利织构组分{111}<112>与不利织构组分(118)[110]的比值f(111)/f(118)逐渐降低,初次再结晶织构的变化是成品磁性的影响因素之一。 Preliminary annealing process at different temperatures for cold-rolled strips of a high permeability grain-oriented silicon steel was investigated to study the effect of the annealing temperature on microstructure and magnetic performance of the steel.Results show that the magnetic performances of the products annealed at 800 ℃ are best.Analysis of primary recrystallization texture indicates that with rising temperature,f(111)/f(118) which is the ratio of the favorable component {111}<112>... 

通过在实验室条件下模拟薄板坯连铸连轧流程,并在以Cu2S为主抑制剂制造普通取向硅钢(CGO)的基础上,加入适量钒钛,研究了钒钛对取向硅钢组织与磁性能的影响。结果表明,适量钒钛使热轧板和脱碳退火板组织更好,尤其使脱碳退火板的晶粒更加细小和均匀;加入适量钒钛不但使热轧板表面高斯织构强度更高,更使脱碳退火板中有利于高斯织构发展的γ织构强度更高;适量钒钛能形成Cu2S+(V,Ti)N等复合析出物,起到辅助抑制剂作用,加强抑制能力。细小均匀的晶粒、强度更高的有利织构和更强的抑制能力使CGO钢磁性能更佳。 Effect of V and Ti on microstructure and magnetic properties of conventional grain-oriented silicon steel(CGO) were investigated under simulated thin slab continuous casting and rolling process in laboratory with Cu2 S as the dominant inhibitor. The results show that appropriate amount V and Ti make the microstructures of the hot rolled sheet and the decarburizing annealed sheet better,especially make the grains of the decarburizing annealed sheet more tiny and uniform. Adding appropriate V and ... 

【摘要】 <正>2012年3月29日中国钢铁工业协会在上...

无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason... 

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 

选用Q235和Q345钢,在纯锌浴和含钛量分别为0.05%、0.10%、0.15%、0.20%(质量分数)的合金浴中浸镀0.5、1、3、5、8 min。利用扫描电子显微镜和能谱仪研究了钛对热浸镀锌组织和生长动力学的影响,并提出钛对含硅钢铁锌反应抑制作用的机理。结果表明:钛的加入缩短了Γ的孕育期,促进了合金层中δ的生长和ζ的消失,δ的生长依然受扩散控制,呈抛物线生长规律;Zn-0.05%Ti锌浴可以很好的抑制高硅钢的硅反应性;含硅钢热浸镀锌钛合金浴时,在锌浴中会形成锌铁钛三元T相,该相能吸收ζ晶界处富集的硅,从而抑制了铁锌反应。 Both Q235 and Q345 steels were immersed for 0.5 to 8 min in Zn bath with different amount of Ti,ranging from 0 to 0.20 mass%,for galvanization.The effect of Ti in Zn bath on microstructure and growth kinetics of hot-dip galvanizing coatings on the two steels were investigated by means of SEM and EDS analysis.Base on the experiment,the mechanism of Ti additions in controlling Fe-Zn reaction was proposed.The results show that addition of Ti in the zinc bath decreases the incubation time of Γ phase... 

【机构】 宝山钢铁股份有限公司规划与科技部； ...

Fe-6.5%Si高硅钢是一种具有高磁导率、低矫顽力和低铁损等优异软磁性能的合金,但是其室温脆性和低的热加工性能严重影响了其在工业领域的应用。综述了Fe-6.5%Si高硅钢的性能,评述了合金的改性法、特殊轧制法、快速凝固法、沉积扩散法、粉末冶金法等制备工艺。 It is well known that 6.5%Si high silicon steel is one kind of soft magnetic materials with higher re-lative permeability,lower coercive force and iron loss than those of conventional industrial silicon steel.However,their room-temperature embrittleness and poor workability limit their practical applications in the industry.The pre-paration technique such as modification treatment on alloy,special rolling,rapid solidification,CVD and powder me-tallurgy is reviewed. 

在50Kg氧化镁坩埚真空感应炉上进行高硅电工钢的脱氧试验。结果表明,通过控制原料的成分、高真空下的碳氧反应和炉衬分解向钢液中的供氧,可使钢液的总氧含量≤15×10-6;在维持高温高真空条件下,当钢液中的反应达到一定程度后,延长精炼时间并不能降低钢液的总氧含量;完成精炼后加入硅钙合金沉淀脱氧可进一步降低钢液的总含氧量,但脱氧效果有限。 The test of high-silicon electric steel deoxidation has been carried out in 50Kg vacuum induction furnace with magnesium oxide crucible.Results show that the total oxygen could be ≤15×10-6in molten steel by controlling material components,carbon-oxygen reaction in high vacuum and oxygen contamination from crucible materials on molten steel;And when the reaction was carried through to a certain extent,total oxygen in molten steel could not be reduced by the extension of refining period in high va...