针对传统工艺生产硅钢周期长、能耗大等缺点,采用双辊连铸工艺制备3%Si无取向硅钢连铸薄带,利用MEM,SEM和TEM观察了铸带的组织、织构及析出物,同时对比了Al的质量分数为0.6%和0.9%的连铸薄带在组织、织构及析出物特征方面的异同.结果表明:双辊连铸工艺生产的3%Si无取向硅钢铸带的组织为均匀等轴晶粒,平均晶粒尺寸约为300μm;织构组成随Al质量分数的不同具有明显差别,Al质量分数为0.9%的铸带中{100}织构强度是随机织构的7倍;铸带中的析出物为AlN和MnS,最大尺寸分别为500和50 nm左右. Given the lengthy production cycle,high energy consumption,and other shortcomings of the traditional process for producing silicon steel,a twin-roll casting process was used to produce 3%Si non-oriented silicon steel casting strips. MEM,SEM,and TEM were used to compare micro-structure,texture,and precipitate characteristics of a casting strip containing 0.6%Al with another containing 0.9%Al.The structure of 3%Si non-oriented silicon steel produced by the twin-roll casting process was a uniform i... 

研究了罩式炉常化工艺对50W350硅钢热轧板组织、夹杂物和性能的影响。研究结果显示，罩式炉常化工艺在温度一定的情况下，随着保温时间延长，硅钢晶粒逐步再结晶并长大，同时析出物也在聚集长大。通过制定合理的罩式炉常化工艺，可以实现硅钢晶粒的再结晶和长大，从而达到连续退火炉常化工艺产品技术要求。 The influence of normalization process with a bell furnace on the structure,inclusions and properties of 50W350electrical steel hot-rolled sheet was studied.The research results showed that:when the steel was normalized at a certain temperature in the bell furnace,the silicon steel grains gradually recrystallized and grew up with the extension of the annealing holding time,and at the same time,the precipitates also gathered and grew up.The recrystallization and growth of the silicon steel grains... 

【作者】 朱传芳； 潘恒韬； ...

对高牌号无取向电工钢国内生产情况、工艺技术、产品性能及应用领域等进行了阐述,并探讨了高牌号无取向电工钢产品的发展趋势。 This paper introduces basic facts on the production status,process technology and products’ properties and their applications of non-oriented electrical steel with high grade at home,and then discusses the development trend on technology for producing the non-oriented electrical steel with high grade. 

无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason... 

选取了三种50W 800无取向电工钢,分析了化学成分、晶粒尺寸、织构、以及200℃时效处理48 h前后的磁性能和第二相粒子析出状态的变化。结果表明,钢板中第二相粒子的分布密度对钢板铁损有最重要的影响。降低钢中C、N元素含量,或改进钢板热加工参数以降低成品钢板中第二相粒子形成元素的过饱和度均有利于明显降低钢板磁时效过程中的铁损增幅。钢板中对磁性能有利的织构也有利于降低钢板铁损的时效幅度。 The evolution of chemical composition,grain size,texture,as well as magnetic property after aging treatment at 200 ℃ for 48 h and distribution of second phase particles precipitation in three selected 50W800 non-oriented electrical steels were analyzed.The results show that the distribution density of second phase particles has great influence on core loss.Reducing C and N content,or improving hot-working parameters to reduce the supersaturation of elements forming second phase particles in prod... 

【摘要】 <正>目前,日本进口硅钢猛增,6月份4181吨,...

热轧轧制工艺对产品性能和轧制稳定性影响很大,对中低牌号无取向电工钢,当在两相区轧制时,热轧塑性明显降低,板形变坏,易出现边裂等情况。以50W1000为例,通过对其变形抗力进行研究,得出把两相区控制在F4与F5之间为最佳轧制工艺的结论。在此基础上制定了一套较为合理的热轧工艺制度。采用新的轧制工艺后,50W1000热轧精轧的稳定性明显改善,热轧产品合格率由开发初期的40%左右提高到95%以上。 The hot rolling process has great influence on product′s performance and rolling stability.For the low medium grade non-oriented electrical steel,when non-oriented electrical steel is rolled in tow phase region,the hot rolling plasticity reduces obviously,the shape of strip goes bad and easily to crack at the edge.The deformation resistance of 50W1000 steel was investigated.The results show that the optimal rolling process is to control the two phase region between F4 and F5.Based on the results... 

利用EBSD技术对CGO硅钢热轧、中间退火、脱碳退火及二次再结晶退火组织及织构进行分析,研究了CGO硅钢各阶段加工制备过程中高斯{110}<001>晶粒的形状、尺寸及分布特点,分析了高斯取向晶粒在各工序过程中的遗传继承性特点。结果表明,CGO硅钢热轧板的次表层存在Goss取向晶粒,历经一次冷轧及中间退火后Goss取向晶粒基本消失,一次再结晶之后Goss织构仍不是主要织构,主要织构为{111}<110>和{111}<112>,说明Goss取向晶粒在二次再结晶退火前数量及尺寸上并不占优势,二次再结晶过程中Goss取向晶粒异常长大形成锋锐Goss织构。{111}<110>和{111}<112>织构组分的强度在一次冷轧中不断增加,{111}<112>织构组分的强度在二次冷轧后达到最大而{111}<110>织构组分是在初次再结晶后变强。 Grain shape,size and distribution of { 110} < 001 > Goss grains in CGO steel and the hereditary characteristics of Goss orientated grains during each processing period were investigated,based on the analysis of the microstructure and texture of the CGO silicon steel during hot rolling,intermediate annealing,decarburizing annealing and secondary recrystallization annealing by means of EBSD. The results show that Goss orientated grains exist in the subsurface of the hot rolled plate,and Goss... 

【摘要】 <正>2014年5月9日,从武钢硅钢事业部获悉,...

研究二次冷轧压下率对于硅的质量分数为3.0%的无取向硅钢组织结构和磁性能的影响。结果表明:当第二次冷轧压下率从0变化至16.7%时,铁损逐渐增加,磁感逐渐降低。当第二次冷轧压下率大于16.7%时,随压下率的增加,铁损逐渐减小,磁感逐渐增加。当第二次冷轧压下率大于38%时,二次冷轧法所能获得的磁性能明显优于一次冷轧法。 Effect of double cold reduction on magnetic,microstructure and texture of 3.0% Si non-oriented silicon steel sheets was investigated.The results show that the iron loss increases and magnetic induction reduces as the percentage redcution in secondary cold rolling changes from 0 to 16.7%.The core loss can be reduced remarkably,and magnetic induction can get a little benefit if the percentage redcution in double cold reduction is higher 16.7%.In case of higher than 38% of the percentage redcution ... 

本文对某厂硅钢DR510温度、成分及过程控制水平和成品的组织、力学性能进行了研究,并在此基础上提出了工艺优化方案,有一定的借鉴和推广价值。 In this paper,the critical process and the products quality,including temperature,composition and process controlling level,the organization and mechanical properties of the finished product,were studied.On the basis of that the optimized technical plan provided,and this control technology is worth using and spreading.