利用XRD和EBSD研究了长轴分别平行于轧向(RD)、横向(TD)和轧面法向(ND)的柱状晶样品在热轧、冷轧及退火过程中的组织、织构演变规律,并分别从几何诱导和取向诱导两个方面分析了晶界的交互作用.结果表明,热轧时由表面摩擦剪切作用引起的组织和织构梯度直接影响并遗传给后续冷轧及退火样品.热轧后,不同样品的初始晶粒形状各向异性差异消失,形成相同的各向异性晶界组织,但晶体学各向异性发生改变,导致随后冷轧、退火组织及织构的变化均不同于直接冷轧的柱状晶样品.研究中特别关注了对磁性能有利的{100}取向区域与晶界的关系. Columnar grains show their special characteristics of morphological and crystallographic anisotropies, and thus markedly influence the microstructure and texture evolution during rolling and annealing process in electrical steel. The rolling and annealing microstructure and texture of three columnar grained samples with the long axes arranged along different directions were investigated by means of XRD and EBSD techniques, and the effects of columnar grain boundaries were analyzed from the view ... 

结合实际生产0.4%Si无取向硅钢，统计了不含Sn和0.025%Sn无取向硅钢的磁性能变化，利用金相显微镜、X射线衍射仪观察分析不同成分下试样的显微组织和微观织构。试验结果表明：Sn元素可以显著降低无取向硅钢的晶粒尺寸，0.025%Sn试样的平均晶粒尺寸比不含Sn减小28.4%;加入Sn元素后抑制了无取向硅钢中不利于磁性能的{111}面织构组分强度，提高了对磁性能有利的{100}面织构组分强度，0.025%Sn与不含Sn相比磁感均值从1.756 T提升至1.768 T,铁损均值从5.476 W/kg降低至5.204 W/kg,明显改善了无取向硅钢磁性能。 In this paper combined with the actual production of 0.4% Si non oriented silicon steel, the magnetic properties of non oriented silicon steel without Sn and 0.025% Sn were counted. The microstructure and microtexture of samples with different compositions were observed and analyzed by metallographic microscope and X-ray diffraction. The results show that: Sn can significantly reduce the grain size of non oriented silicon steel, and the average grain size of 0.025% Sn sample is 28.4% smaller tha... 

借助高温激光共聚焦显微镜,在线观察了不同Mn含量的无取向硅钢中夹杂物的尺寸、类型、数量变化。结果表明,Mn含量(质量分数)为0.77%、0.32%时,试样中的夹杂物数量分别约为1000万个/mm3、1600万个/mm3。Mn含量较高的钢种,会优先析出球形、椭球形MnS夹杂物,其析出数量较少,尺寸相对较大,可以有效抑制AlN、CuxS夹杂物析出;Mn含量较低的钢种,会在试样再加热后冷却过程中,先析出相当数量MnS夹杂物,并作为AlN夹杂物析出核心,形成MnS+AlN复合夹杂物。这种复合夹杂物数量较多,尺寸也较大。 Based on the high temperature confocal microscope, the chage of size, type, and quantity of inclusions in non-oriented silicon steels with different Mn content were observed by in-situ SEM. Results show that the inclusion quantities are 10 million per mm3 and 16 million per mm3,while the mass fractions of Mn are 0.77% and 0.32%, respectively. In the silicon steel with higher Mn content, the spherical and ellipsoidal MnS inclusion will precipitate first, which can retard the precipitation of AlN ... 

通过在实验室条件下模拟薄板坯连铸连轧流程,并在以Cu2S为主抑制剂制造普通取向硅钢(CGO)的基础上,加入适量钒钛,研究了钒钛对取向硅钢组织与磁性能的影响。结果表明,适量钒钛使热轧板和脱碳退火板组织更好,尤其使脱碳退火板的晶粒更加细小和均匀;加入适量钒钛不但使热轧板表面高斯织构强度更高,更使脱碳退火板中有利于高斯织构发展的γ织构强度更高;适量钒钛能形成Cu2S+(V,Ti)N等复合析出物,起到辅助抑制剂作用,加强抑制能力。细小均匀的晶粒、强度更高的有利织构和更强的抑制能力使CGO钢磁性能更佳。 Effect of V and Ti on microstructure and magnetic properties of conventional grain-oriented silicon steel(CGO) were investigated under simulated thin slab continuous casting and rolling process in laboratory with Cu2 S as the dominant inhibitor. The results show that appropriate amount V and Ti make the microstructures of the hot rolled sheet and the decarburizing annealed sheet better,especially make the grains of the decarburizing annealed sheet more tiny and uniform. Adding appropriate V and ... 

研究二次冷轧压下率对于硅的质量分数为3.0%的无取向硅钢组织结构和磁性能的影响。结果表明:当第二次冷轧压下率从0变化至16.7%时,铁损逐渐增加,磁感逐渐降低。当第二次冷轧压下率大于16.7%时,随压下率的增加,铁损逐渐减小,磁感逐渐增加。当第二次冷轧压下率大于38%时,二次冷轧法所能获得的磁性能明显优于一次冷轧法。 Effect of double cold reduction on magnetic,microstructure and texture of 3.0% Si non-oriented silicon steel sheets was investigated.The results show that the iron loss increases and magnetic induction reduces as the percentage redcution in secondary cold rolling changes from 0 to 16.7%.The core loss can be reduced remarkably,and magnetic induction can get a little benefit if the percentage redcution in double cold reduction is higher 16.7%.In case of higher than 38% of the percentage redcution ... 

硅钢是钢铁产品中的\"工艺品\",是高附加值产品,通过对我国主要硅钢生产厂家的工艺设备,市场情况分析,简要介绍了我国硅钢生产消费现状,未来生产能力预测及硅钢未来发展趋势。 Silicon steel is the \"crafts\" of steel products,also is high value-added product.By analyzing process equipment and market condition of major silicon steel-making plant of China,it briefly introduces our current production consumption status,future production capacity prediction and future development trend of silicon steel. 

对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ... 

取向硅钢热轧板中组织、织构梯度对发展完善的二次再结晶十分关键,通过对2种不同热轧工艺生产取向硅钢的组织、织构进行研究,结果表明:采用后道次大压下热轧工艺时热轧板表层再结区晶粒平均尺寸增加,再结晶区厚度增加,高温退火后二次晶粒尺寸减小;采用后道次大压下热轧工艺热轧时,热轧板中平均等效应变高,热轧板厚度心部{100}〈011〉和{100}〈001〉位向取向强度降低,({111}～{113})〈110〉位向取向强度提高,高温退火后{110}〈001〉位向偏离角降低,磁性能提高。 The texture and microstructure gradient in hot rolled grain oriented silicon steel strip was one of the essential factors to achieve a perfect secondary recrystallization.The texture and microstructure of grain oriented silicon steel strip as-rolled with two different hot rolling parameters was investigated.The results show that with big reduction at the end rolling process,the intensity of {100}〈011〉 and {100}〈001〉 orientation reduces with({111}-{113})〈110〉 orientation intensity enhanced in hot... 

在实验室模拟CSP工艺条件下制备了取向硅钢,研究了二次冷轧中间退火工艺对组织和织构的影响。结果表明,中间退火温度对取向硅钢脱碳,高温退火组织及织构均产生明显影响。经940℃中间退火后,取向硅钢脱碳再结晶晶粒较850℃中间退火的多,且再经高温退火处理后,晶粒粗化,最大晶粒尺寸达4.8 mm;高斯织构组分密度达27.00,较850℃中间退火试样高。 Grain-oriented silicon steel was prepared by simulated CSP technology in laboratory. Effects of secondary cold-rolled intermediate annealing on microstructure and texture were studied. The results show that intermediate annealing has obvious effects on the microstructure and texture of the steels after decarburization annealing and high temperature annealing. After intermediate annealing at 940 ℃,recrystallized grain of decarburization annealed steel is more than that of intermediate annealed at... 

利用EBSD技术研究了电工钢中不同的柱状晶尺寸及退火工艺下{100}织构的演变规律。结果表明,初始晶粒尺寸的影响最显著。细小柱状晶热轧后经过常化处理,组织已均匀,但中心层有强{100}织构。粗大柱状晶中{100}织构的遗传性强,常化及中间退火后,中心层仍有粗大的以{100}取向为主的晶粒;脱碳退火后才能完成组织均匀化和织构梯度的弱化。常化时的升温速度也对织构演变存在影响,低的升温速度有利于{100}织构的保留,但升温速度的影响没有初始晶粒尺寸及退火次数的影响显著。细小柱状晶样品经过热轧及三次退火工艺适合制备取向电工钢。 Evolution of {100} texture of different columnar grains and annealing process was investigated in electrical steels with the help of EBSD technique.The results show that the effect of initial grain size is the strongest.The initial fine-grained specimen shows uniform microstructure after the normalizing process,while {100} grains appear preferentially in the central layer of sheets.The heredity of {100} texture in the initial coarse-grained specimen is more significant.{100} mainly-oriented coar... 

介绍了一种适用于超大晶粒取向硅钢的高斯晶粒取向偏离角的X射线衍射测量方法，提出了将试探法和探测器扫描法相结合的方式进行测量。结果表明：该方法可以同时获得准确的实际衍射角度和取向偏离角度，试样制备方式简单，对设备的要求低且测量结果准确。 This paper introduces a X-ray diffraction measurement method of Gaussian grain orientation deviation angle for ultra-large grain oriented silicon steel, and puts forward a method of combining the test method with the detector scanning. The results show that this method can obtain accurate actual diffraction angle and orientation deviation angle at the same time. The sample preparation method is simple, the requirements for equipment are low, and the measurement results are accurate. 

根据相关的取向电工钢典型专利技术,概述了日本高磁感低铁损取向电工钢低温板坯加热、抑制剂合理调节、关键成分Mn、C、Sn和Sb调节与利用、新型退火剂和绝缘溶液的制备及细化磁畴等生产工艺最新动态和进展情况,并提出了国内企业申请取向电工钢专利时应当借鉴之处。 According to related typical patent technology for grain-oriented electrical steel sheets,the recent trends and progress situation for production process of grain-oriented electrical steel sheets with high magnetic flux density and low core loss in Japan are summarized including low temperature slab heating,suitably regulating inhibitors,adjusting and utilizing key element Mn,C,Sn and Sb,manufacturing for new annealing agent and insulating solutions,and fining magnetic domain,and some suggestion...