硅钢资料

电工钢试样加工产生的剪切应力会恶化钢板的磁性,对不同牌号硅钢片的横向、纵向试样退火前后磁性能的变化进行研究,结果表明:无取向硅钢片在剪切过程中横向、纵向的磁性受到剪切应力影响是不一样的。 The electrical steel sample processing magnetic of electrical steel will worsen due to the shear stress of sample. In this paper,the magnetic change of transverse,longitudinal specimens of different type of silicon steel sheet before and after annealing are studied. The results show that the magnetic of non- oriented silicon steel sheet affected in the process of shear is not the same in horizontal and vertical direction. 

系统研究了无取向硅钢用磷酸盐系涂层性能的影响因素。以氢氧化铝和磷酸为原料制备磷酸二氢铝,再添加适量的添加剂酒石酸铵、二氧化硅、环氧树脂,得到的涂液涂布于硅钢表面,并控制合适的烘干温度,通过耐盐雾实验考察各因素对涂液耐腐蚀性能的影响。实验结果表明,在磷酸与氢氧化铝物质的量比为3.4∶1、酒石酸铵用量为2%、二氧化硅用量为1%、环氧树脂用量为5%、烘干温度为300℃条件下,所得涂层材料的防(耐)腐蚀效果最佳。 The factors influencing the performance of phosphate anticorrosive coating for non-oriented silicon were systematically studied.Aluminum dihydrogen phosphate was prepared with aluminum hydroxide and phosphoric acid as raw materials.Then added the right amount of additives,such as ammonium tartrate,silicon dioxide,and epoxy resin to prepare the liquid coating,which was coated on the surface of the silicon steel,and finally controlled a suitable drying temperature.The influences of various factors... 

通过对3%Si CGO硅钢进行恒变形速率、不同变形温度下的单道次压缩实验,结合Thermal-Calc软件,金相分析,SEM及EBSD技术,研究了取向硅钢热变形过程中组织和微观织构的变化规律。结果表明:实验钢是在双相区变形,变形后组织主要是铁素体和少量的珠光体。随变形温度的升高,晶粒由长条状变为等轴状,尺寸逐渐变大;CGO硅钢在热变形过程中立方{100}<001>取向是较为稳定存在的。随着变形温度的提高,{111}<110>等取向逐渐转向{110}<1 10>取向,且{110}<1 10>取向逐渐变得锋锐。 3% Si CGO silicon steel was studied at constant strain rate and different deformation temperatures by single-pass compression deformation experiments to reveal the evolution of microstructure and texture during thermal deformation in oriented silicon steel,and the Thermal-Calc software,metallurgical,SEM and EBSD technique was used in the experiment. The results show that experimental steel is deformed at the temperatures of two-phase zone. The microstructure of the deformed steel consists of fer... 

利用OM、TEM与EDS技术,对Fe-3.2%Si低温取向硅钢热轧板进行不同常化冷却工艺处理后的显微组织、析出相及最终产品的磁性能进行分析,并与热轧板的组织和析出相进行对比。结果表明,常化板较热轧板的表层组织均匀,基体中再结晶比例增加,带状组织变窄;常化板中析出物的数量明显比热轧板的多,析出物主要有AlN、MnS及复合析出的(Cu,Mn)S等。在常化温度1120℃、保温3 min的条件下,采用二段式冷却较空冷、淬沸水、淬常温水的冷却工艺,常化板表层显微组织更均匀,沿板厚方向的显微组织的不均匀性显著,取向硅钢的磁性能最高;常化后采用二段式冷却工艺析出的细小析出物数量最多,且弥散分布在基体中,抑制剂的抑制效果最好,对成品获得高磁性最有利。 Microstructure, precipitate and magnetic characteristic of final products with different normalizing cooling processes for Fe-3.2%Si low-temperature hot-rolled grain-oriented silicon steel were analyzed and compared with the hot-rolled plate by optical microscopy(OM), transmission electron microscopy(TEM), and energy dispersive spectrometry(EDS). The results show that, the surface microstructure is uniform, the proportion of recrystallization in matrix increases, and the banding textures are nar... 

对1990~2010年在我国申请的冷轧无取向硅钢涂层的专利数量、专利技术领域分布进行了统计,对典型涂层专利技术进行了分析,探讨了无取向硅钢涂层的发展趋势。统计分析结果表明,目前无取向硅钢涂层典型的专利技术主要有自粘结涂层、无铬含稀土元素涂层、含钼酸盐环保涂层及采用有机-无机纳米杂化材料为主成膜物形成的涂层等。无取向硅钢涂层发展的趋势主要是无铬环保的半无机、半有机型涂层。 The patent quantity of cold-rolled non-oriented silicon steel coating and distribution of technology fields applied in China in 1990-2010 were summarized.The analysis results indicate that typical patent technologies include self-adhesion coating,chromium-free and with rare earth element coating,environment-friendly and with molybdate coating,coatings with organic-inorganic hybrid materials as main forming agent and so on.The main development trends of coatings on silicon steel are among semi-in... 

研究了卷取工艺对一种新型含铜无取向电工钢晶粒尺寸、织构演变、铁损和磁感应强度的影响。结果表明,试样织构组分主要为{111}、{112}、{100}和高斯织构,在550℃卷取、保温2～3h,{100}织构有增强趋势,磁感应强度较高,铁损较低。 The effects of coiling process on grain size,texture,core loss and magnetic induction of a new cold rolled non-oriented electrical steel with copper were investigated.The results show that there are mainly {111},{112},{100} and {110}<001> texture.Coiling at 550℃and keeping for 2～3 hours,the {100} texture is enhanced,magnetic induction is higher and core loss is lower. 

结合实际生产0.4%Si无取向硅钢，统计了不含Sn和0.025%Sn无取向硅钢的磁性能变化，利用金相显微镜、X射线衍射仪观察分析不同成分下试样的显微组织和微观织构。试验结果表明：Sn元素可以显著降低无取向硅钢的晶粒尺寸，0.025%Sn试样的平均晶粒尺寸比不含Sn减小28.4%;加入Sn元素后抑制了无取向硅钢中不利于磁性能的{111}面织构组分强度，提高了对磁性能有利的{100}面织构组分强度，0.025%Sn与不含Sn相比磁感均值从1.756 T提升至1.768 T,铁损均值从5.476 W/kg降低至5.204 W/kg,明显改善了无取向硅钢磁性能。 In this paper combined with the actual production of 0.4% Si non oriented silicon steel, the magnetic properties of non oriented silicon steel without Sn and 0.025% Sn were counted. The microstructure and microtexture of samples with different compositions were observed and analyzed by metallographic microscope and X-ray diffraction. The results show that: Sn can significantly reduce the grain size of non oriented silicon steel, and the average grain size of 0.025% Sn sample is 28.4% smaller tha... 

针对不同牌号的无取向硅钢产生结疤缺陷的难易程度和表面结疤缺陷的外形特征及分布规律,分析了该缺陷产生的原因。通过调整剪前导板的对中度,设置精轧侧导板开度余量及短行程数值,及时修补与更换侧导板,减少带坯与侧导板挤撞程度,有效地降低了结疤缺陷发生率。 This article analyses the cause of the scab defects according to the defects appearance characters and distribution law,degree of difficulty to form scar of non-oriented silicon steel. It can effectively decrease the scabs by different methods,such as adjusting the center line of guide plate,setting the opening margin and short stroke value of the side guide on finishing mill,timely repairing and replacing of side guide,decreasing the collision between the strip and side guide. 

硅钢是钢铁产品中的\"工艺品\",是高附加值产品,通过对我国主要硅钢生产厂家的工艺设备,市场情况分析,简要介绍了我国硅钢生产消费现状,未来生产能力预测及硅钢未来发展趋势。 Silicon steel is the \"crafts\" of steel products,also is high value-added product.By analyzing process equipment and market condition of major silicon steel-making plant of China,it briefly introduces our current production consumption status,future production capacity prediction and future development trend of silicon steel. 

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。 Microstructure development and texture evolution of conventional grain oriented silicon steel,which were annealed at same annealing temperature and different annealing time under wet H2 atmosphere,were investigated through metallographic observation and electron backscattered diffraction analyzing.The results show that the primary recrystallization finishes in 120 s at 820 ℃ under wet H2 atmosphere.With the extending of annealing time,{111}<112> texture decreases,{111}<110> texture d... 

借助OM、激光共聚焦显微镜、质谱仪和电解萃取等设备和方法，研究了添加微量稀土La（质量分数0.001 1%）的取向硅钢在轧制前采用不同加热保温时间对抑制剂固溶行为的影响。结果表明：当稀土取向硅钢在1 250℃分别保温10、20、30 min后，试验钢晶粒尺寸随保温时间延长有先快后慢的长大趋势；三种抑制剂元素Mn、Cu和Al均发生固溶，保温时间对Mn和Cu两种元素的固溶影响明显，固溶量分别由69.8%和43.7%增加至84.2%和85.2%；随着保温时间的延长，稀土取向硅钢中抑制剂的小尺寸未溶物逐渐减少直至消失，较大尺寸未溶物（300～600 nm）逐渐转变为小尺寸未溶物逐步溶入基体中，数量减少且未溶物的类型由复杂逐渐转变为单一。 In this paper the solid solution behavior of the inhibitor under various holding time in 0.001 1 %La oriented silicon steel during reheating had been investigated by using OM, LM, methods of electrolytic extraction and mass spectrometer. The results showed that grain size of the test steel increased significantly with the holding time prolonging when the rare earth oriented silicon steel was heated to1 250 ℃ and held for 10, 20 min and 30 min respectively, and the growth trend slowed down after ... 

某冷连轧机生产无取向硅钢板材时,其边缘降的长度合格率频繁超标。为满足用户的叠片厚度精度要求,这类产品必须以增大切边量的方式来保证交货质量,而这种方式又直接降低了金属收得率,提高了生产成本。基于此,以该产线现有设备特性为基础,详细分析其软、硬件功能模式,分别对辊形与反馈控制进行全面分析与优化改进。通过现场试验论证,充分明确依托辊形优化与反馈控制程序的改进能显著提高边缘降的控制水平,该技术的使用为生产现场的边缘降控制提供了合理的技术支撑。 A cold rolling mill production of non-oriented silicon steel sheet,the thickness difference of the edge( edge-drop) is usually exceed the preset standard value,In order to meet the accuracy requirements of the user flatness,these production must be trimed wider length to meet the delivery quality of the user need, which directly reduce the metal yield and increase the manufacturing cost. Therefor,the software and hardware of the production line has been analyzed, and the work roll shape and feed...