结合冶炼无取向硅钢的生产实际,对钢中硫的来源,以及炉渣性质、钢水温度、底吹强度对脱硫的影响进行了分析。研究表明,转炉钢中硫的主要来源为铁水、废钢、铁水渣及石灰带入;冶炼硅钢时,终渣碱度为3.0~3.5,w((FeO))≤20%,终点钢水温度大于等于1 680℃,加大底吹搅拌强度能提高转炉脱硫效果。硅钢平均出钢硫的质量分数为0.004 8%,能满足无取向硅钢对硫含量的要求。 With the actual production of non-oriented silicon steel,the source of sulphur and the effect of metallugic parameters like slag properties,temperature of molten steel and bottom stirring on desulphurizing ability were investigated.The results show that the main source of sulphur is molten metal,scrap,the remaining slag volume in hot metal and lime.The degree of desulphurization for smelting silicon steel can be increased through adopting the following measures,such as the basicity of finishing ... 

研究了取向硅钢制备过程中常见的两种冷轧工艺,主要研究了一阶段冷轧与两阶段冷轧+中间退火工艺对初次再结晶组织及织构的影响.结果表明:采用两阶段冷轧+中间退火工艺制备以Cu2S为主抑制剂的取向硅钢,其初次再结晶平均晶粒尺寸为18.1μm,高斯晶粒的体积分数为0.6%,迁移性强的重位点阵晶界(Σ5+Σ9)和高能晶界(20°~45°取向偏差角)所占比例分别为1.8%和50.4%.与一阶段冷轧工艺相比,其初次再结晶晶粒较细,且高斯晶核与特征晶界所占的比例较高,有利于高斯晶粒发生二次再结晶. Two common cold-rolling processes of grain oriented silicon steel and the effects of the single stage cold rolling and tw o-stage cold rolling w ith intermediate annealing processes on the primary recrystallization microstructure and texture w ere investigated. The results revealed that for the grain oriented silicon steel prepared under the tw o-stage cold rolling process w ith intermediate annealing w ith Cu 2 S as the main inhibitor,the average grain size of the primary recrystallization micr... 

利用热模拟试验机、光学显微镜和X射线衍射仪对Fe-3.2%Si低温取向硅钢热轧工艺参数对组织及织构的影响进行了研究。结果表明,Fe-3.2%Si硅钢在1110℃粗轧、880℃终轧,轧后以10℃/s的速度冷却到550℃卷取,然后空冷到室温,热轧硅钢板沿板厚方向的显微组织不均匀性显著,对后续发展完善的二次再结晶有重要作用。无论是热轧板,常化板还是冷轧板,它们的织构集中分布在γ取向线上,γ取向线的织构除取向密度不同外,织构种类是一致的,这说明γ取向线上织构是有继承性的。从热轧到常化,织构取向密度显著减小,经二次冷轧后,织构密度又显著升高,可见,轧制变形有助于织构的形成并使织构强度升高。 The influence of hot-rolled process parameters on the microstructure and texture of Fe-3.2%Si low temperature hot rolled grain-oriented silicon steel were researched by hot simulation experiment machine,light microscope and X-ray diffractometer.The results show that,Fe-3.2%Si silicon steel is rolled by the technology with a temperature of rough rolling of1110℃,finish rolling of 880℃,coiling with the speed of 10℃ /s,and then cooled to room temperature with air.The microstructure of hot-rolled sil... 

采用固溶强化、细晶强化和位错强化方法,模拟TSCR流程试开发高强度无取向电工钢,试开发钢的主要合金成分为3%Si、0.83%Al和2.99%Mn。分析热轧、常化、退火后的钢板组织,并针对不同的成品板组织,详尽地分析了相应的力学性能和磁性能。试验电工钢平均晶粒直径为12.37μm时,R p0.2为530 MPa,R m为618 MPa;当退火制度为700℃×4 min,成品组织完全为未再结晶的回复组织时,R p0.2为853.5 MPa,R m为895.5 MPa。该成分的电工钢P15/50或P10/400最小时,对应的平均晶粒直径都大于59.67μm;P10/800或P10/1000最小时,对应的平均晶粒直径都处于12.37~59.67μm尺寸区间。 TSCR was simulated to develop high-strength non-oriented electrical steel with 3% of Si,0.83% of Al and 2.99% of Mn by solution strengthening,grain refinement strengthening and dislocation strengthening.The microstructures of hot rolled plates,normalized plates and annealed plates were analyzed.Furthermore,the mechanical properties and magnetic properties of products with different microstructures were detailedly studied.As the average grain diameter of the steel was 12.37 μm,the yield strength ... 

系统研究了无取向硅钢用磷酸盐系涂层性能的影响因素。以氢氧化铝和磷酸为原料制备磷酸二氢铝,再添加适量的添加剂酒石酸铵、二氧化硅、环氧树脂,得到的涂液涂布于硅钢表面,并控制合适的烘干温度,通过耐盐雾实验考察各因素对涂液耐腐蚀性能的影响。实验结果表明,在磷酸与氢氧化铝物质的量比为3.4∶1、酒石酸铵用量为2%、二氧化硅用量为1%、环氧树脂用量为5%、烘干温度为300℃条件下,所得涂层材料的防(耐)腐蚀效果最佳。 The factors influencing the performance of phosphate anticorrosive coating for non-oriented silicon were systematically studied.Aluminum dihydrogen phosphate was prepared with aluminum hydroxide and phosphoric acid as raw materials.Then added the right amount of additives,such as ammonium tartrate,silicon dioxide,and epoxy resin to prepare the liquid coating,which was coated on the surface of the silicon steel,and finally controlled a suitable drying temperature.The influences of various factors... 

借助电子背散射衍射(EBSD)及ZEISS-200MAT金相显微镜对某钢厂普通取向硅钢(CGO)进行研究,研究结果表明:热轧板组织、织构沿板厚方向存在明显的不均匀性,在热轧板表层及次表层发生再结晶,同时存在强度较高的Goss织构,中心层存在较强的{001}<110>变形织构。冷轧组织均呈纤维状条带组织,一次冷轧后,热轧板中的Goss织构消失,织构主要为α、γ织构,经中间脱碳退火后,α、γ织构强度减弱,并出现一定强度的Goss织构和利于Goss织构发展的{554}<225>、{332}<113>等织构,经二次冷轧后,二次冷轧织构类型与一次冷轧织构一致,但织构强度不同。 The grain-oriented silicon steel produced by a steel factory was investigated by EBSD and ZEISS-200 MAT metallographic microscope.The results show that the textures and microstructures along thickness of hot rolled slab are inhomogeneous.The surface layer and the layer near that are recrystallized structure which has a high Goss texture,but there is deformation texture{001}<110>in the central layer.The structure after cold rolling is a structure like fiber strip.After the first cold rollin... 

西安重型机械研究所为武钢开发了目前国内第一台自动化水平较高的先进可靠的硅钢热轧试验轧机。本文介绍了该轧机的工艺参数、设备组成,技术特点及轧制流程,该轧机在规定的终轧温度范围内,实现了2.5 m/s的快速轧制速度,保证了控制系统准确及时的采集到轧件进出轧辊时的信号,缩短道次间隙时间,实现了自动控制,保证了产品板形及精度的高水平要求,对于硅钢尤其是对其取向硅钢新产品、新工艺的开发具有深远意义。 An experimental prototype of 400 mm silicon steel hot rolling mill was developed by Xi’an Heavy Machinery Research Institue for Wu Gang.The technological parameters,configuration and characteristic of advanced control system in the experimental prototype are introduced in detail.The experimental prototype was realized the fast rolling of 2.5 m/s in the range of specified rolling temperature.Its automatic rolling control system can acquisite the signals that a rolled piece enters in and exits fro... 

介绍了国内、外电工钢极薄带的生产现状及市场应用的情况,以及典型生产企业的生产规模、产品性能和应用领域,指出扩大高牌号无取向电工钢生产、提高产品质量是目前电工钢发展的迫切要求。 The production situation and market application of ultra thin electrical steel strip at home and abroad were described.The production capability,product property and application area of typical corporation were introduced.The results indicate that the urgency needed of electrical steel development is expanding high-grade non-oriented electrical steel production and improving products quality at present. 

介绍了微合金元素锡、铌、稀土对无取向硅钢性能的影响,并扼要分析了这些元素对硅钢性能的影响机理:晶界偏聚元素Sn可细化晶粒提高硅钢磁性能;微合金元素Nb细化铁素体晶粒,提高硅钢的强度、韧性和塑性及磁性能;稀土元素(RE)在硅钢中的主要作用包括净化钢液、变质夹杂物、改善铸态组织和性能及微合金化,减少晶界上出现偏析的几率。 The influence of micro-alloy elements on properties of non-oriented silicon steel and the mechanism for effect of the micro-alloy elements including Sn、Nb and RE on the properties of steel are presented and analyzed in this paper.Grain boundary segregation elements Sn in steel can grain refinement and improve the magnetic properties;Micro-alloy elements Nb can refine the ferrite grain,increase the silicon steel strength,toughness and plastic;The main role of the RE in the silicon steel including... 

通过后天抑制剂获得法制备了取向硅钢,对渗氮前后和高温退火升温阶段析出物的析出和转化规律进行了研究。研究结果表明,渗氮前脱碳退火态基体中存在少量的粗大AlN颗粒和细小AlN颗粒,渗氮处理后新析出大量的Si3N4析出物,高温退火升温阶段Si3N4将转化为(Al,Si)N,随着温度的继续升高(Al,Si)N颗粒将发生粗化,(Al,Si)N是后天抑制剂获得法制备取向硅钢的主要抑制剂。 Grain-oriented silicon steels were produced by acquired inhibitor method.The rule of precipitate transformation was studied after nitriding treatment and high-temperature finishing annealing.The results show that a small amount of large AlN and fine AlN are found in matrix before nitriding treatment,and a large amount of Si3N4 is precipitated in matrix after nitriding treatment.During the temperature rising period of high-temperature finishing annealing,Si3N4 would transform into(Al,Si)N,and(Al,... 

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

将Fe-1.5Si硅钢试样分别在1 000~1 200℃空气条件下氧化30 min,观察发现在1 000℃和1 100℃时,氧化层与基体界面处存在硅酸亚铁,而当温度为1 200℃时,硅酸亚铁不但存在于界面处,同时也存在于氧化层中.将各温度下得到的带有氧化层的试样进行单道次热轧试验,压下率分别为10%和30%,发现1 000℃和1 100℃时,较高的压下率使氧化层破碎更加严重,但是单道次热轧未能改变氧化层的结构;当温度为1 200℃时,由于液态的硅酸亚铁的出现,单道次热轧能够将界面处的液化的硅酸亚铁层挤压到氧化层中,消除了硅酸亚铁层的钉扎基体的效应,改善了氧化层与基体界面的平直度. Specimens of Fe-1.5Si silicon steel were oxidized at 1 000 ~ 1 200 ℃ in air for 30 min.At 1 000 ℃ and 1 100 ℃ fayalite was observed at the scale/substrate interface.While at 1 200 ℃fayalite was found both at the scale/substrate interface and at the outer oxide layer.Then after the single-pass hot rolling process,with the compression ratio of 10% and 30%,it was found that at 1000 ℃ and 1 100 ℃,higher compression rate accelerated the broken of the scale layers,but the scale structure was not affec...