结合工业化生产的无取向硅钢,进行了RH精炼添加稀土合金实验。结果表明,1.15%(质量分数)Si钢的脱硫反应,主要发生在添加稀土合金之后的前5min。最佳的稀土合金添加量为0.6～0.9kg/t钢。钢液经过稀土处理后,加入的稀土总量越多,稀土氧硫化物夹杂物的尺寸就越大,但热轧带钢再结晶效果会逐渐变差,成品带钢晶粒尺寸先是快速长大,而后逐渐减小。最佳的钢中存留稀土含量与钢的化学成分有关,应严格控制在2.0×10-3%～6.0×10-3%(质量分数)。在此范围内,钢的铁损先是快速降低,而后缓慢升高,钢的磁感应强度则单调降低。 Based on the industrial production of non-oriented electrical steel,rare earth(RE) alloy treatment during the RH refining process was studied.The results showed that the effects of desulfurization and total concentration of RE remained in steel mainly depended on the chemical compositions of different steel grades.For 1.15wt% Si steel grade,the desulfurization reaction mainly focused on the initial 5min after RE alloy added during the RH refining process.The suitable RE alloy addition was 0.6-0.... 

介绍了微合金元素锡、铌、稀土对无取向硅钢性能的影响,并扼要分析了这些元素对硅钢性能的影响机理:晶界偏聚元素Sn可细化晶粒提高硅钢磁性能;微合金元素Nb细化铁素体晶粒,提高硅钢的强度、韧性和塑性及磁性能;稀土元素(RE)在硅钢中的主要作用包括净化钢液、变质夹杂物、改善铸态组织和性能及微合金化,减少晶界上出现偏析的几率。 The influence of micro-alloy elements on properties of non-oriented silicon steel and the mechanism for effect of the micro-alloy elements including Sn、Nb and RE on the properties of steel are presented and analyzed in this paper.Grain boundary segregation elements Sn in steel can grain refinement and improve the magnetic properties;Micro-alloy elements Nb can refine the ferrite grain,increase the silicon steel strength,toughness and plastic;The main role of the RE in the silicon steel including... 

目的提高硅钢的磁性能。方法采用多弧离子镀技术,在普通取向硅钢薄板两面沉积高硅FeSi合金层制得高硅梯度硅钢,并进行热处理,观察其显微组织,测量磁性能。结果退火态高硅梯度硅钢表面的高硅FeSi合金层与基底结合紧密,均匀致密。高硅梯度硅钢中硅含量呈梯度分布,最表层硅质量分数为11.0%,随着深度增加,硅含量逐渐降低,在距表面20μm处硅质量分数仍能达到6.5%。沉积态高硅梯度硅钢的电阻率ρ、低频铁损P10/50、高频铁损P10/1k及磁感应强度B8分别为68.6μΩ·cm,0.82W/kg,83.3 W/kg和1.73 T,退火后分别为63.1μΩ·cm,0.44 W/kg,54.38 W/kg和1.89 T。结论由于表层高硅FeSi合金层的存在,梯度高硅钢的低频磁学性能良好,但高频损耗需进一步改善。 Objective To improve the magnetic properties of silicon steel. Methods FeSi alloy coatings with high-silicon content were deposited on the surface of common grain-oriented silicon steel by cathodic arc plasma evaporation,and then a kind of high silicon gradient steel was prepared. The morphologies,content and magnetic properties of the samples were tested. Results FeSi alloy coatings were featured with compact microstructures and excellent adhesive quality with the substrates. The silicon conten... 

西安重型机械研究所为武钢开发了目前国内第一台自动化水平较高的先进可靠的硅钢热轧试验轧机。本文介绍了该轧机的工艺参数、设备组成,技术特点及轧制流程,该轧机在规定的终轧温度范围内,实现了2.5 m/s的快速轧制速度,保证了控制系统准确及时的采集到轧件进出轧辊时的信号,缩短道次间隙时间,实现了自动控制,保证了产品板形及精度的高水平要求,对于硅钢尤其是对其取向硅钢新产品、新工艺的开发具有深远意义。 An experimental prototype of 400 mm silicon steel hot rolling mill was developed by Xi’an Heavy Machinery Research Institue for Wu Gang.The technological parameters,configuration and characteristic of advanced control system in the experimental prototype are introduced in detail.The experimental prototype was realized the fast rolling of 2.5 m/s in the range of specified rolling temperature.Its automatic rolling control system can acquisite the signals that a rolled piece enters in and exits fro... 

研究了锰含量对w(Si)=1.8%Si无取向电工钢组织和性能的影响。结果表明,钢中锰含量从0.3%增加到1.2%时,由于α_γ相变的产生,铸坯低倍组织、热轧板金相组织及成品织构等均发生了不同程度的变化,对成品表面质量及磁性能产生了明显的影响。 The effects of manganese content on structure and properties of w(Si)=1.8% non-oriented electrical steels have been studied.Results show that with increasing manganese content to 1.2% from 0.3%,macrostructure of continuous casting slab,hot rolled band metallurgical structure and finished product texture vary in some extent because of the occurrence of α-γ phase transformation,the surface quality and magnetic properties of finished product are affected greatly. 

为研究退火工艺对普通取向硅钢初次再结晶组织的影响,对经不同温度、保温时间和升温速率退火后的材料组织进行了分析。结果表明:在等温退火条件下,加热至600℃时开始发生初次再结晶,800℃以上初次再结晶组织发展完善;而在最终冷轧板直接进行最终高温退火的情况下,加热温度在500～700℃时,将升温速率提高到80℃/h,初次再结晶组织更易于发展完善。 To investigate the influence of annealing process on the recrystallization of common grain oriented silicon steel,microstructures of sheets annealed at different temperature,soaking time and heating rate are observed.Results show that under the condition of isothermal annealing,recrystallization begins at 600℃ and fully develops above 800℃,while in the case that the final cold rolled sheets are directly thrown to final high temperature annealing,recrystallization is likely to develop with the he... 

综述了国内外大钢铁企业与研究机构采用获得抑制剂法生产低温高磁感取向硅钢的开发及应用情况,分析了以该法生产高磁感取向硅钢过程中抑制剂的控制技术,包括固有抑制剂组成方案、气态渗氮方式与工艺及高温退火工艺的制定.研究表明,固有抑制剂组成方案的设计思路大体一致,化合物抑制剂以AlN为主、硫化物为辅,同时添加少量Sn,Sb等单元素抑制剂,但组成元素含量存在一定差别;在脱碳退火后用NH3进行非平衡渗氮处理已成为气态渗氮的主要方式,但最佳方式仍未明确,具体选择需依据实际生产条件,相应脱碳及渗氮工艺的控制条件差别较大;高温退火工艺中升温制度差别不大,升温阶段退火气氛中N2含量的选择存在差别.此外,分析了抑制剂控制技术目前存在的关键问题,并指出了进一步的研究方向. The current application and exploitation on production of low-temperature high magnetic induction grain-oriented silicon steel with acquired inhibitor method at both iron and steel enterprises and research institutions in the world are reviewed. The control techniques of inhibitors, which include the composition design for inherent inhibitors, nitriding method and process, and secondary recrystallization annealing, are thoroughly analyzed and proposed. It is indicated that the design ideas for i... 

结合冶炼无取向硅钢的生产实际,对钢中硫的来源,以及炉渣性质、钢水温度、底吹强度对脱硫的影响进行了分析。研究表明,转炉钢中硫的主要来源为铁水、废钢、铁水渣及石灰带入;冶炼硅钢时,终渣碱度为3.0~3.5,w((FeO))≤20%,终点钢水温度大于等于1 680℃,加大底吹搅拌强度能提高转炉脱硫效果。硅钢平均出钢硫的质量分数为0.004 8%,能满足无取向硅钢对硫含量的要求。 With the actual production of non-oriented silicon steel,the source of sulphur and the effect of metallugic parameters like slag properties,temperature of molten steel and bottom stirring on desulphurizing ability were investigated.The results show that the main source of sulphur is molten metal,scrap,the remaining slag volume in hot metal and lime.The degree of desulphurization for smelting silicon steel can be increased through adopting the following measures,such as the basicity of finishing ... 

【作者】 胡志强； 张文康； ...

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

将Fe-1.5Si硅钢试样分别在1 000~1 200℃空气条件下氧化30 min,观察发现在1 000℃和1 100℃时,氧化层与基体界面处存在硅酸亚铁,而当温度为1 200℃时,硅酸亚铁不但存在于界面处,同时也存在于氧化层中.将各温度下得到的带有氧化层的试样进行单道次热轧试验,压下率分别为10%和30%,发现1 000℃和1 100℃时,较高的压下率使氧化层破碎更加严重,但是单道次热轧未能改变氧化层的结构;当温度为1 200℃时,由于液态的硅酸亚铁的出现,单道次热轧能够将界面处的液化的硅酸亚铁层挤压到氧化层中,消除了硅酸亚铁层的钉扎基体的效应,改善了氧化层与基体界面的平直度. Specimens of Fe-1.5Si silicon steel were oxidized at 1 000 ~ 1 200 ℃ in air for 30 min.At 1 000 ℃ and 1 100 ℃ fayalite was observed at the scale/substrate interface.While at 1 200 ℃fayalite was found both at the scale/substrate interface and at the outer oxide layer.Then after the single-pass hot rolling process,with the compression ratio of 10% and 30%,it was found that at 1000 ℃ and 1 100 ℃,higher compression rate accelerated the broken of the scale layers,but the scale structure was not affec... 

介绍了攀钢冶炼电工钢过程硫含量变化以及过程回硫、增硫情况,采取针对性措施,如:提高铁水装入量、转炉采用石英砂代替复合造渣剂造渣、RH脱硫等,降低钢中硫含量。结果表明:采取相应措施后,电工钢炼成率大幅提高,成品w[S]≤0.008%的比例由改进前的62%提高到92.4%,取得了明显的冶金效果。 The resulfurization and the change of sulphur content in production of electrical steel is analyzed.The targeted measures have been taken,such as increase the loaded quantity of liquid iron,quartz sand replaces the composite slagging agent in the converter and RH desulfurization to decrease the sulphur content of the steel.The result shows,after the measures have been taken,the finished product ratio of electrical steel increase a lot.The ratio of sulfur content of finished product no more than ...