硅钢资料

通过热力学计算及实验室研究,对钙处理前后50W600无取向硅钢退火冷轧板中夹杂物的类型、数量及尺寸进行了系统分析。结果表明,50W600无取向硅钢经钙处理后(w(Ca)=0.002 6%),钙在1 600℃的钢液中主要以固态的CaO·2Al2O3、CaO·6Al2O3及溶解钙的形式存在。在钢液的凝固过程中,钢中的溶解钙和硫反应生成了CaS和CaS-MnS复合夹杂,有效抑制了MnS的弥散析出,减少了钢中微细夹杂物的数量。同时钙处理促进了钢中微细夹杂物的聚合长大,导致显微夹杂物的数量增加。 Based on thermodynamic calculation and laboratory experiment,the type,quantity and size of inclusions in annealed cold-rolled steel sheets of 50W600 non-oriented silicon steel before and after calcium treatment were systematically studied.Results showed that after calcium treatment(w(Ca) = 0.002 6%),calcium was mainly in the form of CaO·2Al2O3,CaO·6Al2O3 and dissolved calcium in steel at 1 600 ℃.Dissolved calcium could combine with sulfur to form CaS inclusions and compound CaS-MnS inclusions du... 

【作者】 常波； ...

采用非水溶液电解方法来提取无取向硅钢中夹杂物。通过扫描电镜(SEM)观察结果表明:无取向硅钢中主要夹杂物为六棱柱的AlN、不规则硅酸盐及球状的铁的硫化物和氧化物,其中AlN夹杂尺寸在1~5μm,数量较多,还有部分AlN的复合夹杂。进一步研究了AlN复合夹杂形成机理,采用了Thermo-Calc热力学计算软件计算出该钢样中AlN、MnS析出温度分别为1 240℃、1 200℃,而Al2O3析出温度大于1 800℃,从而为AlN复合夹杂形成机理提供了一个理论依据。 Extracting inclusions from non-oriented silicon steel in non-aqueous electrolysis is a nondestructive method to gain inclusions.Scanning electron microscopy shows that the main inclusions in non-oriented silicon steel were hexagonal AlN,which was of large quantity,irregular silicate,spherical iron sulfide and oxide.The size of AlN inclusions ranged from 1to 5μm,and there were some duplex inclusions of AlN.To further study the formation mechanism of AlN duplex inclusions,Thermo-Calc thermodynamic... 

以水氯镁石为原料,采用氨法沉镁-煅烧-添加剂的方法制备硅钢级氧化镁。考察了反应温度、反应pH值、陈化时间对中间体氢氧化镁纯度及转化率的影响;研究了煅烧温度和煅烧时间对氧化镁水化率的影响及添加剂的量对氧化镁悬浮性能的影响。控制实验条件为:反应温度55℃,pH值为9.5,陈化时间2h,煅烧温度1050℃,煅烧时间2h,添加剂量为0.8%,制得氧化镁的纯度为98.99%、水化率为2.92%、悬浮性能为3mm/h,达到硅钢级氧化镁的要求。 Using bischofite as raw material,the preparation of magnesium oxide with silico-steel grade was studied.The effects of reaction temperature,reaction pH value and aging time on the intermediate magnesium hydroxide purity and conversion rate were studied.Calcinations temperature,calcinations time relationship to the hydration rate of MgO and amount of additive to the suspension performance of MgO were investigated.The results indicated that the optimum technological conditions were as follows:reac... 

研究了常化温度、常化时间及常化后冷却速度对Si的质量分数为1.6%的无取向电工钢成品磁性能的影响。结果表明:在850~1 050℃范围内,随着常化温度的升高,成品铁损先减小后增大,成品磁感应强度先增大后减小;当常化温度为1 000℃时,成品平均铁损最低,平均磁感应强度最高;常化时间从3min延长到7min时,成品铁损先减小后增大,成品磁感应强度则呈单调下降趋势;随着常化冷却速度的降低,成品铁损先减小后增大,成品磁感应强度则呈单调增大趋势;对于Si的质量分数为1.6%的无取向电工钢,最佳的常化制度为:在1 000℃进行常化,时间5min,常化后空冷。对热轧板进行常化后,热轧板发生了不同程度的再结晶和晶粒长大。提高常化温度、延长常化时间、降低冷却速度,都能使常化板晶粒粗化,进而粗化成品板晶粒,改善磁性能。通过扫描电镜观察发现,成品板中析出物主要为AlN和MnS的复合析出物,以及少量的单独析出的AlN和MnS,而常化工艺主要是通过粗化析出相,减少细小析出相数量,从而减少对晶界钉扎作用来改善成品磁性能。 The effects of normalizing temperature,normalizing time and cooling rate after normalizing on magnetic properties of non-oriented electrical steel with mass fraction of Si of 1.6% were investigated.The results show that core loss of product decreases first and then increases,while magnetic induction increases first and then decreases with the increase of normalizing temperature from 850 to 1 050℃.Average core loss of product is the lowest and average magnetic induction is the highest when normal... 

稀土元素在许多钢中发挥着独特而且不可替代的重要作用。半个世纪以来,它的作用已经在各种低合金和特殊合金钢中的研究及应用中得到充分的证明;然而,作为具有稀土资源优势的中国,在属于重要功能材料的无取向电工钢中稀土的应用却落后于国外,本文就中国稀土在无取向电工钢中的应用研究作简要的评述,希望能够进一步推进此领域的研究,并且促进中国稀土在无取向电工钢中应用技术的发展,缩短与国外差距,并提出了在此应用领域今后需深入开展的研究方向。 Rare earth elements play a unique and irreplaceable role in a lot of steels,it has given the full proof by the practice of various low alloy steels and special alloy steels since half century.However,as our country has the advantage of rare earth resources,RE application technology in non-oriented electrical steels has lagged behind abroad.The application researches of rare earth in non-oriented electrical steel in our country are briefly reviewed in this paper,which hope to promote the research... 

利用EBSD技术研究了电工钢中不同的柱状晶尺寸及退火工艺下{100}织构的演变规律。结果表明,初始晶粒尺寸的影响最显著。细小柱状晶热轧后经过常化处理,组织已均匀,但中心层有强{100}织构。粗大柱状晶中{100}织构的遗传性强,常化及中间退火后,中心层仍有粗大的以{100}取向为主的晶粒;脱碳退火后才能完成组织均匀化和织构梯度的弱化。常化时的升温速度也对织构演变存在影响,低的升温速度有利于{100}织构的保留,但升温速度的影响没有初始晶粒尺寸及退火次数的影响显著。细小柱状晶样品经过热轧及三次退火工艺适合制备取向电工钢。 Evolution of {100} texture of different columnar grains and annealing process was investigated in electrical steels with the help of EBSD technique.The results show that the effect of initial grain size is the strongest.The initial fine-grained specimen shows uniform microstructure after the normalizing process,while {100} grains appear preferentially in the central layer of sheets.The heredity of {100} texture in the initial coarse-grained specimen is more significant.{100} mainly-oriented coar... 

利用EBSD技术研究了电工钢中长轴平行于轧向的柱状晶样品在热轧和退火过程中组织和取向的演变规律,并与长轴平行于板法向的样品的已有研究结果进行对比。结果表明,无论柱状晶按何种方向排列,只要表面存在剪切力,热轧后都可形成剪切织构,同时中心形成轧制织构,主要包括旋转立方织构和{112}<1-10>。柱状晶造成的影响主要体现在板中心层,长轴平行于轧向排列的样品热轧时形成的粗大旋转立方晶粒要到脱碳退火后才能完全消除,但破坏了正常的不同取向晶粒间的取向差分布及尺寸均匀性,导致二次再结晶不完全及磁性能降低。 The evolution of microstructure and grain orientation in an electrical steel containing columnar grains with its long axis being parallel to the rolling direction of sheet was studied during hot rolling and annealing by EBSD technique.The results are compared with those of samples containing columnar grains being parallel to normal direction of sheet reported in the reference [3].It was shown that,whether the long axis of columnar grains was arranged in RD or ND,shear textures can be formed in t... 

通过热力学计算与模拟试验研究了含钒钛取向硅钢中氮化物析出相的析出规律与析出行为,并探讨了含钒钛元素的氮化物析出相作为薄板坯连铸连轧流程制备取向硅钢中辅助抑制剂的可行性.研究表明,在所冶炼的含钒钛取向硅钢的成分范围内,Ti N在钢液凝固末期便具备析出的热力学条件,而Al N与VN只可能在凝固后的α+γ或α+Fe3C两相区内析出.含钒钛取向硅钢中氮化物析出相以成分复杂的复合析出相为主,且随着钒钛加入量的增加,钢中抑制剂析出相总的分布密度由于含钒钛元素的氮化物析出相的增加而明显提高,使抑制剂抑制初次再结晶晶粒正常长大的能力得以加强,最终成品的磁感应强度值B8由1.857 T提升至1.898 T.同时,加入不高于0.007%的Ti与不高于0.005%的V不会影响中间脱碳退火工序的脱碳效果以及高温退火净化阶段硫、氮的脱除效果,其形成的含钒钛元素的纳米级氮化物析出相适合作为薄板坯连铸连轧流程制备取向硅钢的辅助抑制剂. The precipitation behavior of nitride precipitates in grain-oriented silicon steel containing vanadium and titanium elements produced by thin slab casting and rolling process was studied by thermodynamic calculation and simulation experiment. The feasibility of nitride precipitates containing V and Ti elements as auxiliary inhibitors was also investigated. It is found that Ti N is likely to precipitate at the final stage of solidification in the grain-oriented silicon steel,but VN and Al N can p... 

根据相关的取向电工钢典型专利技术,概述了日本高磁感低铁损取向电工钢低温板坯加热、抑制剂合理调节、关键成分Mn、C、Sn和Sb调节与利用、新型退火剂和绝缘溶液的制备及细化磁畴等生产工艺最新动态和进展情况,并提出了国内企业申请取向电工钢专利时应当借鉴之处。 According to related typical patent technology for grain-oriented electrical steel sheets,the recent trends and progress situation for production process of grain-oriented electrical steel sheets with high magnetic flux density and low core loss in Japan are summarized including low temperature slab heating,suitably regulating inhibitors,adjusting and utilizing key element Mn,C,Sn and Sb,manufacturing for new annealing agent and insulating solutions,and fining magnetic domain,and some suggestion... 

将Fe-1.5Si硅钢试样分别在1 000~1 200℃空气条件下氧化30 min,观察发现在1 000℃和1 100℃时,氧化层与基体界面处存在硅酸亚铁,而当温度为1 200℃时,硅酸亚铁不但存在于界面处,同时也存在于氧化层中.将各温度下得到的带有氧化层的试样进行单道次热轧试验,压下率分别为10%和30%,发现1 000℃和1 100℃时,较高的压下率使氧化层破碎更加严重,但是单道次热轧未能改变氧化层的结构;当温度为1 200℃时,由于液态的硅酸亚铁的出现,单道次热轧能够将界面处的液化的硅酸亚铁层挤压到氧化层中,消除了硅酸亚铁层的钉扎基体的效应,改善了氧化层与基体界面的平直度. Specimens of Fe-1.5Si silicon steel were oxidized at 1 000 ~ 1 200 ℃ in air for 30 min.At 1 000 ℃ and 1 100 ℃ fayalite was observed at the scale/substrate interface.While at 1 200 ℃fayalite was found both at the scale/substrate interface and at the outer oxide layer.Then after the single-pass hot rolling process,with the compression ratio of 10% and 30%,it was found that at 1000 ℃ and 1 100 ℃,higher compression rate accelerated the broken of the scale layers,but the scale structure was not affec... 

电工钢反复弯曲次数是电工钢性能检验的重要指标之一,直接影响到用户在使用电工钢过程的机加工性能。主要分析了试样宽度、试样张力、晶粒取向、反复弯曲设备等因素对电工钢反复弯曲试验的影响,并对各个因素的影响程度进行量化以及原因探讨,从而归纳形成各影响因素的基本规律,以便为电工钢实际生产、用户使用提供科学指导。结果表明:试样宽度增加,反复弯曲次数也会不断增加,晶粒位向对取向电工钢的反复弯曲次数影响较大,当支座顶部到拨杆底部的距离减小或拉紧力增加时,反复弯曲次数会不断减小,但当拉紧力达到60N以上时,对反复弯曲次数影响不大,试样经退火后,反复弯曲次数略有上升。 The reverse bend number is an important performance of electrical steels′capabilities,affecting the machining performance directly when the customers used.It investigated some factors,such as sample′s width,sample′s tension load,grain orientation and equipment,how to effect the reverse bend test for electrical steel,measured the influence degree,and discussed the reason,in order to form basic rules which could be guided the manufacturing and using for electrical steel.Results showed that the rev...