以马鞍山钢铁集团公司电工钢板形优化控制研究项目为背景,系统地研究了热轧、冷连轧和单机架轧机在电工钢生产过程中的边缘降控制问题。通过现场数据采集、工况数值模拟计算和工业化大生产试验,设计出适用、合理的电工钢板形控制的辊型优化曲线,满足了不同工序、不同机型的板形控制策略要求,解决了电工钢板形质量问题,取得了显著的经济效益。 Based on the project of electric steel strip shape optimization control,problem of edge drop control was systematically studied in production of electric steel of hot-rolling mill,cold-rolling mill and single stand mill.Roll optimization contour was designed out in point and reasonable by collection of work condition data,numerical simulation and test of industrial production.The shape control system can meet with the different working steps and difference mills,and quality problem of electric s... 

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

根据现场实际的生产控制情况,指出了热轧原料断面轮廓缺陷以一定的比列遗传给了冷轧带钢,分析了不同热轧原料断面轮廓对冷轧电工钢尺寸精度的具体影响,提出了相应的规律。并阐明了严格控制热轧原料断面轮廓形貌,对保证冷轧电工钢尺寸精度具有重大意义,对于中国现行的冷轧电工钢生产具有指导意义。 Based on the actual situation of production control,it was pointed out that the section profile defects of hot-rolled raw materials were geneticed to the cold-rolled strip.The specific impact analysis for the profile of different hot-rolled raw materials to the dimensional accuracy of cold-rolled silicon steel was analyzed.As a result, the corresponding orderliness are given;And the strict control to section profile of the hot-rolled material is of great significance to ensure the dimensional ac... 

通过试验确定氩气分析流量为3.5L/min,静态流量为0.75L/min,冲洗时间为3s,预燃时间为12s,积分时间为5s的激发条件,采用火花源原子发射光谱法测定取向硅钢中碳、硅、锰、磷、硫。分别采用铣床铣样、砂轮磨样两种制样方式进行了精密度考察,发现制样方式对结果影响不大;讨论了取向硅钢样品中碳、硅、锰、磷、硫测定时可能存在的共存元素干扰,发现硅对锰元素的干扰不可忽略,采用干扰系数法进行了校正,据此拟合得到各元素校准曲线的相关系数均在0.999 0以上。精密度考察结果表明,碳、硅、锰、磷、硫的相对标准偏差(n=10)在0.71%~9.4%之间。对两块取向硅钢生产样品进行分析,并与钢铁研究总院进行比对分析,结果一致,且偏差均在允许范围内。 Carbon,silicon,manganese,phosphorus and sulfur in oriented silicon steel were determined by spark source atomic emission spectrometry.The selected excitation conditions were as follows:the analytical flow rate of argon was 3.5L/min,the static flow rate was 0.75L/min,the flush time was3s,the precombustion time was 12sand the integration time was 5s.Two sample preparation methods,including milling machine and grinding wheel,were investigated.The precision test results showed that,the determination... 

森吉米尔二十辊轧机是冷轧电工钢的主要机型,具有整体刚度大,辊径小,轧制道次压下量大,产品精度高等特点,简要介绍了近年来冷轧电工钢森吉米尔二十辊轧机领域进展,在轧机结构、厚度自动控制、板形自动控制等方面的技术及研究。 20-h Sendzmir reversible mill is the main type of cold rolled electrical steel which has the characteristic of high integral stiffness,small roller diameter,high pass reduction and high product quality.In this paper,the recent progress of frame structure,automatic gauge control,automatic flatness control of Sendzmir mill is introduced. 

【摘要】 <正>近日,从重钢集团获悉,日前重钢炼钢厂...

对高牌号无取向电工钢35W300的成品进行了第二次退火,对第二次退火后的成品性能、纵横向磁性能差异和组织变化进行了分析。结果表明,随着第二次退火温度的升高,晶粒长大,磁性能优化。铁损平均值下降0.087 5W/kg,磁感平均值升高0.008T。第二次退火温度为820℃的产品的磁性能能够满足用户使用要求。 The product of high grade non-oriented electrical steel 35W300 was annealed at the second time.Microstructure,the difference of magnetic properties in the vertical and horizontal and were studied.The results show that the grain grew up and magnetic properties optimized with the increase of annealing temperature for the second time.Iron loss average declines in 0.0875 W/kg,magnetic induction average increases 0.008 T.The magnetic properties can meet the requirements of users at the second anneali... 

组织和织构是影响无取向硅钢性能的重要因素。为改善产品性能，研究了冷轧压下率（71.7%～87.0%）对高牌号无取向硅钢组织、织构、磁性能和力学性能的影响。结果表明，随冷轧压下率的增加，退火晶粒平均尺寸先减小后增大；高斯和立方织构强度减弱，γ纤维织构增强，α纤维织构转变为较强的α^*（{h, 1, 1}〈1/h, 1, 2〉）织构，并随冷轧压下率的增加而增强，同时其峰值逐渐向{111}面移动；工频铁损P_1.5/50、高频铁损P_1.0/400和磁极化强度J₅₀₀₀同时降低，屈服强度变化不大，表面硬度逐渐增加。当冷轧压下率由84.7%增至87.0%、厚度减至0.30 mm时，高频铁损降幅是工频铁损的11倍，表面硬度增幅变大。以上研究成果对硅钢减薄后织构及组织的优化提供了很好的指导。 Microstructure and texture are critical factors on non-oriented silicon steel properties. In order to improve product properties, this paper studied the effect of cold rolling reduction rate（71.7%-87.0%） on microstructure, texture, magnetic properties and mechanical properties of high-grade non-oriented silicon steel. The results show that with the increase of cold rolling reduction rate, the average size of annealing grain decreases first and then increases. The intensity of Goss and λ fiber te... 

用还原分离-原子荧光光谱法分析了硅钢中的痕量汞.分析方法的不确定度主要来自测量重复性,样品溶液浓度,工作曲线变动性,标准溶液,移取、配制标准溶液,仪器变动性等.文章分别对上述构成合成不确定度大小的分量进行了计算讨论. Trace mercury in silicon steel and galvanized sheet was analyzed by adopting reduced separation-atomic fluorescence spectrometry.The uncertainty of the analysis method mainly comes from measurement repeatability,sample concentration,working curve volatility,standard solution,pipetting and preparation of standard solution,and instrument variability,etc.The essay conducted all calculations and discussions on the above components that determine uncertainty. 

对取向硅钢熔融态钢液进行处理,对比研究了不同脉冲参数的作用效果。结果表明,电脉冲对钢锭晶粒组织具有明显的细化作用,凝固组织等轴晶比例大幅上升。在脉冲电容、频率、处理时间和电压中,影响等轴晶比例的最显著性因素为脉冲频率;最优正交实验参数为:电容1 200μF,脉冲频率1 Hz,处理时间5 s,脉冲电压800 V;随着输入能量的增大,等轴晶率先增大后减小,脉冲输入能量为某值时,等轴晶率最大,通过经典形核理论和热力学对这一现象进行了解释。 Research on the influence of the electric pulse on the solidification structure of oriented silicon steel was preformed.Electric pulses in different parameters were applied to molten steel and results were compared.The result shows that solidification structure of oriented silicon steel can be improved by the electric pulse,and the equiaxed crystal ratio increases obviously.Among the four parameter factors of electric capacity,frequency,applied time and voltage,the most effective factor is frequ... 

借助电子背散射(EBSD)技术对AlN为主抑制剂的Hi-B取向硅钢常化工艺的中间冷却制度进行了研究。结果表明:常化后试样均发生了完全再结晶,在60℃/s冷速下组织最均匀;在合适的冷却制度下常化板表层保留了强的Goss织构,它深入到1/4厚度处,并且形成对Goss织构有利的强{554}<225>织构。 The intermediate cooling system of Hi-B oriented silicon steel with AlN main inhibitor in normalizing process was studied by means of electron back diffraction(EBSD) technique. The results show that:the specimens after normalizing are fully recrystallization, and the microstructure is most uniform under the intermediate cooling rate of 60℃/s; under suitable cooling system, normalized plate surface retains strong Goss texture, it penetrates into the 1/4 thickness of the plate and forming strong {... 

针对某厂DMS森吉米尔轧机生产无取向硅钢表面麻面缺陷的问题，根据生产实际，对其形成原因从乳化液及工作辊两方面因素进行了分析。结果表明：乳化液对麻面缺陷的产生有一定影响，但不是主要因素，主要原因是由于二十辊森吉米尔轧机工作辊辊径较小，轧制相同长度带钢轧辊运转周期较大，容易产生疲劳失效而导致。为此，提出通过调整冷轧工序成品轧制道次的压下率以减小轧制力，从而减小工作辊的磨损疲劳；通过对轧制乳化液浓度、温度的合理控制，以改善润滑效果、提高轧制速度，而进一步缓解轧辊疲劳的改进措施，使该钢厂无取向硅钢麻面缺陷发生率由原来的18%降至0.8%,带钢表面质量明显改善。 For the problem of surface pockmarks of non-oriented silicon steel strip produced by a DMS Sendzimir mill, based on the production practice, the formation causes were analyzed from two aspects of emulsion and working roll. The results show that the emulsion has a certain effect on the formation of surface pockmarks defects, but it is not the main factor. The main reason is that the working roll diameter of the 20-high Sendzimir mill is small, and the running period of the roll rolling the same l...