通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 

利用X-射线衍射织构分析和线形分析技术测定了交叉轧制双取向硅钢在制备工艺各阶段的织构及微结构,进而探讨了立方织构({100}<001>)的形成过程。通过对实验结果的分析可知,二次冷轧和交叉轧制工艺为立方织构提供了内能优势和有利的形变织构,而低温预退火工艺既强化了立方织构的内能优势,又为立方织构的异常长大提供了有利的组织保证,最终在抑制剂(AlN和MnS)的协同作用下,硅钢在二次再结晶退火后形成了强烈的立方织构。 The texture and substructure of the double oriented electrical steels produced by the cross rolling technology during the difference process has been measured by means of the X-ray texture and diffraction peak profile analysis technology,and research the formation mechanism of cube texture,{100}<001>.The results show that the dominances of inner energy and deformation texture were supplied by secondary cold rolling and the cross rolling technology and strengthened by pre-annealing at a low... 

结合实际生产0.4%Si无取向硅钢，统计了不含Sn和0.025%Sn无取向硅钢的磁性能变化，利用金相显微镜、X射线衍射仪观察分析不同成分下试样的显微组织和微观织构。试验结果表明：Sn元素可以显著降低无取向硅钢的晶粒尺寸，0.025%Sn试样的平均晶粒尺寸比不含Sn减小28.4%;加入Sn元素后抑制了无取向硅钢中不利于磁性能的{111}面织构组分强度，提高了对磁性能有利的{100}面织构组分强度，0.025%Sn与不含Sn相比磁感均值从1.756 T提升至1.768 T,铁损均值从5.476 W/kg降低至5.204 W/kg,明显改善了无取向硅钢磁性能。 In this paper combined with the actual production of 0.4% Si non oriented silicon steel, the magnetic properties of non oriented silicon steel without Sn and 0.025% Sn were counted. The microstructure and microtexture of samples with different compositions were observed and analyzed by metallographic microscope and X-ray diffraction. The results show that: Sn can significantly reduce the grain size of non oriented silicon steel, and the average grain size of 0.025% Sn sample is 28.4% smaller tha... 

【作者】 凌健； ...

采用中、厚板坯生产技术对取向硅钢进行了研制和开发,对热轧及后工序样品进行了金相组织观察和EBSD分析,探讨了两种组织及织构的差异性,研究结果表明:除高温退火样品外,中板坯生产的取向硅钢各工序样品平均晶粒尺寸大;厚板坯生产的取向硅钢热轧和常化样品亚表层Goss织构强;中板坯和厚板坯的脱碳退火板织构没有明显区别。中板坯生产的取向硅钢成本低,产品磁性能和质量与厚板坯相当。 Grain oriented silicon steel was researched and developed by medium thickness slab and thick slab.Microstructures observation and EBSD analysis to the samples of hot rolling and following processes were carried out,respectively.The differences between the two kinds of microstructures and textures were discussed.The results show that the average grain sizes of every process samples are larger except that of high temperature annealing samples of grain oriented silicon steel produced by medium thic... 

通过固溶度积公式计算及热模拟实验,对不同热装和加热温度条件下的无取向硅钢铸坯中析出相进行了研究.在低于950℃热装时,铸坯中AlN的析出量和尺寸不再变化,但MnS和AlN-MnS的数量及平均尺寸随着热装温度降低而进一步增加,并在温度低于600℃时达到最大值后保持不变.与1200℃相比,1100℃加热的铸坯中AlN、MnS的总固溶量相对更少.相比850℃热装,600℃热装再加热到1100℃的铸坯中AlN和MnS的总固溶量更少,且AlN和MnS尺寸更大.合适的热装温度和加热温度分别为600℃和1100℃. Based on solubility product calculation and thermal simulation experiments,precipitated phases in continuous casting slabs of non-oriented silicon steel were systematically studied at different hot charging and heating temperatures.When the hot charging temperature is below 950 ℃,the content and size of AlN remain unchanged,but the quantity and size of MnS and AlN-MnS increase when the hot charging temperature decreases,reach maximum and remain unchanged when the hot charging temperature is belo... 

研究了热处理工艺(退火温度、保温时间、冷却方式)对含Mn的Fe-6.5wt%Si高硅钢热轧带的显微组织及硬度的影响。结果表明,退火温度对Fe-6.5wt%Si合金的组织和显微硬度均有较大影响,随退火温度升高,平均晶粒尺寸和显微硬度均明显增大。小于1 h退火时,晶粒长大缓慢,而长时间(>1 h)退火时,一些次表层晶粒将发生异常长大。水冷组织比空冷组织略细小,但水冷显著降低了显微硬度。Mn含量提高能抑制850℃退火时晶粒的长大,并且促进退火后高硅钢的软化。 The influences of heat treatment process(annealing temperature,heating time,cooling methods) on the microstructure and microhardness of Fe-6.5wt%Si high silicon steel containing manganese for hot rolled strip were studied.The results show that the annealing temperature has a great effect on the microstructure and microhardness of Fe-6.5wt%Si alloy,and as the annealing temperature increases,the average grain sizes and microhardness will significantly increase.When annealing time for less than 1 h... 

【机构】 宝山钢铁股份有限公司规划与科技部； ...

采用XRD、SEM和激光粒度仪等手段,观察并研究了不同特性氧化镁在硅钢表面形成硅酸镁底层形貌特点,并结合热力学和差热-失重分析了MgO-SiO2的反应机理。研究结果表明:粒度小,活性值高的特种氧化镁在高温退火过程中与基体表面氧化物生成的硅酸镁底层,界面中硅酸镁底层嵌入基体较多,表面致密,颗粒细小,有利于形成附着性能优良的硅酸镁底层。 Surface microstructure of Mg2SiO4 coatings formed on the surface of oriented silicon steel coated with different kinds of MgO was investigated by XRD and SEM.The reaction mechanism between MgO and SiO2 was analyzed by TG-DSC and thermodynamic calculation.Results revealed that when the MgO with finer microstructure size and higher activity is employed,a dense Mg2SiO4 layer with finer microstructure and good binding to the steel substrate can be obtained.The results are very helpful for the prepar... 

涂层技术在高磁感取向硅钢生产中起着重要的作用.根据生产实践,介绍了高磁感取向硅钢生产中涂层的种类和作用、涂料的成分和对产品性能的影响、涂层工艺质量控制要点和检验方法等,并提出了通过优化涂层工艺改善高磁感取向硅钢性能和外观质量的方法. Surface coating technique plays an important role in producing high magnetic inductivity grain-oriented silicon steel.Based on production practice,this paper describes the types and function of the coating,the composition of the coating and its effect on the product performance,the quality control and inspection method for the coatings,as well as proposes ways to improve the magnetic property and surface quality of the steel by optimizing the coating process. 

文章以国内某公司硅钢厂连续退火机组1号辐射管加热段为研究对象,分析炉内传热机理,建立并开发了辐射管加热段的传热模型。采用生产实际数据对模型进行了验证,以总燃料消耗量最小为目标,得出该炉段长度方向上燃料的最佳分配机制。所得结论为该公司连续退火机组节能控制提供理论依据。 Taking the radiant tube heating section of No.1 continuous annealing unit in a silicon steel plant of a domestic company as the research object, the heat transfer mechanism in the furnace is analyzed, and the heat transfer model of the radiant tube heating section is established and developed. The model is verified by the actual production data. Aiming at the minimum total fuel consumption, the optimal fuel distribution mechanism in the length direction of the furnace section is obtained. The co... 

介绍了硅钢氧化镁制备方法及高质量硅钢氧化镁制备技术的研究进展,并对利用我国丰富的卤水资源制备硅钢氧化镁进行了展望。 The preparation methods of silicon steel magnesium oxide and research progress of high quality silicon steel magnesium oxide preparation technology were introduced.The use of abundant brine resources in the preparation of silicon steel magnesium oxide was prospected.