目的提高硅钢的磁性能。方法采用多弧离子镀技术,在普通取向硅钢薄板两面沉积高硅FeSi合金层制得高硅梯度硅钢,并进行热处理,观察其显微组织,测量磁性能。结果退火态高硅梯度硅钢表面的高硅FeSi合金层与基底结合紧密,均匀致密。高硅梯度硅钢中硅含量呈梯度分布,最表层硅质量分数为11.0%,随着深度增加,硅含量逐渐降低,在距表面20μm处硅质量分数仍能达到6.5%。沉积态高硅梯度硅钢的电阻率ρ、低频铁损P10/50、高频铁损P10/1k及磁感应强度B8分别为68.6μΩ·cm,0.82W/kg,83.3 W/kg和1.73 T,退火后分别为63.1μΩ·cm,0.44 W/kg,54.38 W/kg和1.89 T。结论由于表层高硅FeSi合金层的存在,梯度高硅钢的低频磁学性能良好,但高频损耗需进一步改善。 Objective To improve the magnetic properties of silicon steel. Methods FeSi alloy coatings with high-silicon content were deposited on the surface of common grain-oriented silicon steel by cathodic arc plasma evaporation,and then a kind of high silicon gradient steel was prepared. The morphologies,content and magnetic properties of the samples were tested. Results FeSi alloy coatings were featured with compact microstructures and excellent adhesive quality with the substrates. The silicon conten... 

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and... 

对w(Si)=3%无取向硅钢进行表面机械研磨处理(SMAT)和异步轧制(CSR),获得表面纳米结构,再进行550～650℃、4 h固体粉末渗硅处理,用透射电镜(TEM)、扫描电镜(SEM)和X射线衍射仪(XRD)研究表层组织演变。结果表明:经过SMAT后,w(Si)=3%无取向硅钢表面形成了等轴状、取向呈随机分布的、晶粒尺寸为10 nm的纳米晶组织;异步轧制后,表面纳米晶组织保持不变;550～650℃、4 h渗硅处理后,SMAT+CSR样品表面形成化合物层,其厚度随着温度的升高由17μm增加到52μm;化合物层由Fe3Si和FeSi相组成. Nanostructured surface layer was fabricated on a 3%(mass fraction) non-grain oriented silicon steel by means of surface mechanical attrition treatment(SMAT) and cross-shear rolling(CSR),and then a solid powder siliconizing treatment was carried out for the SMAT+CSR sample at 550~650 ℃ for 4 h.The microstructural evolution was examined by using transmission electron microscopy(TEM),scanning electron microscopy(SEM) and X-ray diffraction(XRD).Experimental results show that: equiaxed nanocrystallin... 

硅钢工业退火炉温度控制具有强耦合、纯滞后、多扰动等特点,它的控制方法代表着一类非线性系统控制的解决方法。以硅钢工业退火炉温度为控制对象,在双交叉限幅控制的基础上引入了智能学习系统,形成了基于智能学习系统的双交叉限幅控制方法来解决此类非线性系统的控制问题,并通过模块化的编程来实现其功能。结果表明:与传统的PID控制相比,该控制方法的控制精度、抗扰性等控制指标有明显提高,是解决此类非线性控制的一种有效方法。 The temperature control of silicon steel industrial annealing furnace has the features of strong coupling,pure lag,multidisturbance. The control method represents the solution of a class of nonlinear control systems. The control object is the temperature control of silicon steel industrial an-nealing furnace, the intelligent learning system based on Double Across Limit Control is introducedand used to solve control problem of this kind of nonlinear system, and the module programming isused to re... 

以太钢热连轧厂的硅钢为研究对象,利用凸度仪测量热轧带钢出口凸度值,采用矩阵和失效模式的分析方法了解影响带钢凸度变化的主次因素。研究结果表明:通过有效控制轧制过程中的加热温度、时间及采用合理的辊型,硅钢凸度精度提高了4.34%左右。 In this paper,we take the hot-rolled silicon steelsheet of Taigang as the research symbol,exit profile was measured by convex instrument,the primary and secondary factors that affect the strip profile were measured by using matrix and failure mode analysis methed.The results indicate that convexity accuracy has significantly improved by nearly 4.34% through the effective control of the heating temperature,heating time and the use of correct roller type in the process of hot rolling. 

运用EBSD和光学显微镜,研究了0.25%~0.45%Cu对无取向电工钢热轧板显微组织,成品板显微组织、织构和磁性能的影响。实验结果表明:卷取过程中Cu元素在热轧板表层的偏聚作用显著阻碍了热轧板表层再结晶晶粒长大,导致热轧板表层晶粒尺寸随着Cu含量增加而逐渐较小,但热轧板中间晶粒尺寸变化不大。同时发现Cu元素能够明显改善织构类型,使有利织构组分增加,不利织构组分减少,同时减弱织构强度。从实验结果可知0.35%Cu能够显著改善电工钢的磁性能,铁损P15/50最低达到4.1 W/kg,磁感B50最高值达到1.8 T。 Effects of high content Cu on microstructure of hot rolled plates and microstructure,texture and magnetic properties of annealed finish product plates of non-oriented electrical steel were examined by means of EBSD technique and optical microscope. The results show that surface segregation of Cu significantly hindered recrystallized grain growth of surface layer in hot rolled plate during the coiling,as a result,the surface grain sizes of the hot-rohed plates decrease with the increase of Cu con... 

从影响高牌号无取向硅钢退火工艺的主要参数入手,介绍高牌号无取向硅钢退火炉在加热、气氛控制、冷却、涂层烘烤方面的新技术,并展望无取向硅钢退火炉的发展方向。 Based on the technology parameters of high-grade non-oriented silicon steel annealing,the new technology of the annealing line,which includes heating,atmosphere control,cooling,coating baking,is introduced,and the development direction of non-oriented silicon steel annealing furnace is pointed out. 

常化快冷是生产高牌号无取向硅钢和高磁感取向硅钢不可缺少的一个工艺环节,气-雾冷却则是实现常化快冷的关键方式之一。介绍了国内自主设计建设的常化酸洗机组气雾冷却系统的技术特性,并对其特点进行了系统分析,最后给出该系统在设计、运行参数的选择上若干注意事项,对气-雾冷却系统设计和使用具有一定的指导作用。 The normalizing rapid cooling is a indispensable process to high grade non-oriented silicon steel and high magnetic induction oriented silicon steel’ s production. The fog cooling is a key ways of coming true the normalizing rapid cooling. This paper introduces the technical features of the fog cooling system in normalizing pickling line which is the domestic independent design and construction. Meanwhile,the fog cooling system’s characteristic is analyzed systematacially. In the end,this paper ... 

结合工业化生产的无取向硅钢,探讨了氧硫交互作用对钢中夹杂物生成的影响。借助非水溶液电解+扫描电镜法,研究了不同O、S含量下钢中夹杂物的变化规律。结果表明,本实验条件下,提高O含量、降低S含量,会劣化热轧组织再结晶效果。在劣化效果上,O的作用大于S;低Si、无Al硅钢中,应尽可能降低O含量、适当提高S含量,以粗化钢中微细夹杂物,减少尺寸小于1.0μm的夹杂物的数量;O、S含量与钢中夹杂物数量不具有关联性。生产过程中,不仅要严格控制O、S含量,还要严格控制生产工艺,以免生成较多的有害夹杂物。 Based on the industrial production of non-oriented silicon steel,the effects of interaction between oxygen and sulfur on the formation of inclusions were discussed.The change of non-metallic inclusions in steel sheets was investigated by means of electrolysis with non-aqueous solution under different oxygen and sulfur content.Results show that the recrystallization microstructure of hot rolled sheets will be deteriorated with the increase of oxygen content and the decrease of sulfur content.The ... 

【作者】 宋波； 朱一知； ...

取向硅钢成品的晶粒尺寸非常大,其易磁化方向[001]晶向对于轧向的偏差角度对其磁性能影响极大。本文介绍了取向硅钢二次再结晶后成品晶粒位向的几种测定方法,包括侵蚀法、劳厄法、OIM法、极图法和非对称X射线衍射法等,并对这几种测量方法进行了比较。 The finished product of grain-oriented silicon steel has immense grain size ranging from millimeters to centimeters and the deviation angles of easy magnetization direction from rolling direction plays a remarkable role in magnetic properties of grain-oriented silicon steel.The methods in common use for determining the deviation angles of crystal direction are introduced,which include the etch-figure method,the Laue method,the OIM method,the pole figure method and the asymmetrical X-Ray diffract...