硅钢资料

通过对辉光放电发射光谱参数的优化,以铁元素为内标来消除基体效应,建立了测定硅钢薄板中微量硼元素的方法。优化的实验参数为:放电电压1200 V,放电电流50 mA,预溅射时间40 s,积分时间10 s。校准曲线硼元素含量范围0.0001%~0.022%,相关系数大于0.999,测量结果与认定值一致,相对标准偏差小于10%。完全能够满足日常分析测试的要求。 A glow discharge optical emission spectrometry(GD-OES) method for determining trace boron element in silicon steel sheets were established through optimization of instrumental parameters and using Fe element as an internal standard to eliminate the matrix effect.The optimized instrumental parameters included discharge voltage,discharge current,pre-sputtering time and integration time,which are 1200 V,50 mA,40 s,and 10 s,respectively.The content of boron element that can be determined from the ca... 

应用CAFE法对6.5%Si高硅钢铸锭凝固组织进行了模拟研究,确定出了适合高硅钢组织模拟的模型。进一步用该模型研究了过热度及冷却条件对凝固组织的影响,结果表明,随着过热度的降低,凝固组织中柱状晶比例和晶粒平均面积均减小。水冷条件下,高硅钢铸锭凝固组织几乎全是柱状晶,而且晶粒粗大。空冷条件下,等轴晶区扩大,但柱状晶仍占主要部分。缓冷条件下,等轴晶区占主要部分,晶粒平均面积和空冷条件下相当。 The solidification structure of 6. 5% Si steel ingot was simulated based on CAFE method and the model suitable for simulating the structure of high silicon steel wad ascertained. The influence of superheat and cooling condition on the solidification structure were studied. It was shown that with the superheat decreasing,the proportion of columnar crystals decrease,and the average grain size become smaller. Under water cooling condition,the solidification structure of casting was composed of almo... 

高强无取向硅钢主要应用于高速电机，要求其具备高强度和优异磁性能，但目前无取向硅钢的磁性能和强度难以兼顾。因此，设计并制备了添加微量Cr的含Nb高强无取向硅钢，通过光学显微镜、EBSD、万能拉伸试验机、四探针测试仪和磁性能测量仪等研究了Cr对含Nb高强无取向硅钢微观组织、织构、力学性能及磁性能的影响。结果表明，添加质量分数为0.5%的Cr抑制了热轧组织的回复，使常化和退火组织再结晶减弱，常化和退火后有利织构面积分数增加，不利织构面积分数减小。添加质量分数为0.5%的Cr使含Nb无取向硅钢的屈服强度显著增大，磁感略升高，但对铁损几乎没有影响。Cr对屈服强度的影响一方面是由于Cr的固溶强化作用，另一方面Cr促进了Nb的析出而使Nb的析出强化效果增强；而Cr提高含Nb高强无取向硅钢的磁感主要是由于促进有利织构形成的同时抑制了不利织构的形成，使得织构因子增大；添加Cr使无取向硅钢的电阻率增加从而使铁损降低，同时Cr促进了Nb的析出，而这种富Nb析出相不仅抑制晶粒长大且会阻碍磁畴移动而使铁损增高，在两方面因素的综合作用下，添加质量分数为0.5%的Cr对含Nb高强无取向硅钢的铁损几乎没有影响。因此，... High strength non-oriented silicon steel is mainly used in high-speed motors, which requires good mechanical and magnetic properties. However, it is difficult for non-oriented silicon steel to obtain high strength and good magnetic properties at the same time. In this paper, the Cr-microalloyed Nb-containing high strength non-oriented silicon steel was designed and prepared. The effect of Cr on the microstructure, texture, mechanical properties and magnetic properties of Nb-containing high stren... 

采用X-射线衍射分析技术测定了取向硅钢热轧板在不同压下率下不同厚度处的织构。结果表明,在压下率低于80%的情况下,几乎所有试样的不同厚度处的织构均为旋转立方织构类型{100}<011>,但不同压下率、不同厚度处的织构强度存在很大差异;在压下率大于80%的情况下,不同试样的不同厚度处的织构类型发生了变化,其织构类型为旋转立方织构或高斯织构{011}<100>,且当织构类型为旋转立方织构时,织构强度存在很大差异,而当织构类型为高斯织构时,织构强度差异相对较小。 The texture of the grain oriented silicon steel hot rolled plate at different compressibility has been measured.The experimental results have shown that the texture of all samples at different thickness is {100}<011> when the compressibility is below 80%,and its intensity at different compressibility and thickness is difference.The texture of all samples at different thickness is variable when the compressibility is above 80%,it is {100}<011> or {011}<100>,and the intensity of ... 

为探究铬、锰元素及退火温度对高强无取向硅钢性能的影响规律,借助OM、SEM、EBSD与万能拉伸试验机等分析不同制造工艺下3组不同含量铬、锰元素的无取向硅钢热轧、常化及退火处理后组织与性能。结果表明,试验钢热轧后组织不均匀,心部为沿轧向分布纤维状组织,边部为少量再结晶晶粒,常化处理能显著改善热轧板组织均匀性,消除热轧板中心部位的纤维状组织。经冷轧及退火后得到多边形铁素体晶粒,其中960℃退火,晶粒尺寸偏大,有利织构{100}组分体积分数减少,不利织构{111}组分体积分数增加,成分为0.2Mn-1Cr的1号试验钢960℃退火后铁损最大,磁感强度偏小;成分为0.5Mn-1Cr的2号试验钢930℃退火后,磁性能与强度等综合性能最佳,工频铁损P_1.5/50为2.41W/kg,高频铁损P_1.0/400为17.36W/kg,磁感应强度B_{5 000}为1.638T,抗拉强度为685MPa。 In order to study the effect of Cr,Mn and annealing temperature on the properties of high-strength non-oriented silicon steel,the microstructure and properties of three groups of non-oriented silicon steel with different Cr,Mn content under different manufacturing processes were analyzed by means of OM,SEM,EBSD and universal tensile tester.The results show that the structure of experimental steel is not uniform after hot rolling,and the core is distributed in fibrous structure along the rolling ... 

为了更好的解决电力系统防污闪涂料RTV-Ⅰ长期应用暴露出来的问题以及目前RTV-Ⅱ防污闪涂料存在的一些不足,结合具体实际需求,在电力系统外绝缘领域,应用新型防污闪硬质涂层——防污闪纳米硅钢涂层,并对分别喷涂了防污闪纳米硅钢涂层以及RTV涂料的绝缘子进行对比运行情况研究分析。研究结果表明,防污闪纳米硅钢涂层是一种同时具有优异憎水性迁移性能和自洁性能的新型涂层,具有良好的应用前景。 In order to solve the problem exposed of anti-pollution flashover coating RTV-Ⅰwhich has been used long-term in power system,as well as to better solve some shortcomings of the current anti-pollution flashover coating RTV-Ⅱ,in this paper,a new anti-pollution flashover hard coating — anti-pollution flashover nanometer silicon hard coating(NSHC) is applied in the field of power system insulation for the specific practical needs.At the same time insulators which are separately sprayed by the NSHC a... 

利用电子背散射衍射(EBSD)技术和场发射电子扫描显微镜(FESEM)研究了电工钢中柱状晶不同初始取向50%热压缩变形后的演变规律及其对粒子析出行为的影响。结果表明:〈100〉晶粒形变后仍为〈100〉取向,只发生绕ND∥〈100〉方向的转动,具有遗传性,粒子析出数量少。柱状晶长轴与压缩轴的偏转度增加,取向的稳定性变差,超过40°,可形成〈111〉取向,期间发生复杂的滑移系交互作用,产生较高的缺陷密度,促进粒子析出。MnS粒子主要在晶内析出,变形温度高、形变量低,粒子均无法充分析出。回复时,形变晶粒内高的储能和缺陷密度是促进粒子进一步析出的必要条件。 The evolution of initial orientations and their influence on precipitation of columnar-grained electrical steel after 50% hot compression deformation were investigated by electron backscatter diffraction technique and field emission scanning electron microscopy.The results indicate that the〈100〉orientated columnar grains remain still〈100〉after hot compression deformation,with only rotation around ND parallel to〈100〉direction,with heredity,and less precipitation.As the deviation angle between the... 

【作者】 周威； 刘侃； ...

研究了CSP流程试制50W270高牌号无取向硅钢热轧→常化→冷轧→退火过程中织构的演变.利用电子背散射衍射技术对全流程织构进行测量和分析.发现热轧板织构在厚度方向上存在较大差异,表层主要为铜型、黄铜和高斯织构,1/4层存在微弱的高斯织构和旋转立方织构,中心层以γ纤维织构和旋转立方织构为主,还含有较弱的α纤维织构.与热轧板相比,常化板表层和1/4层织构变化不大,中心层旋转立方织构和α纤维织构增强.冷轧板各层均具有α纤维织构和γ纤维织构.与冷轧板相比,成品板各层中α纤维织构基本消失,还出现了立方织构和高斯织构. This article focuses on texture evolution in 50W270 high-brand non-oriented silicon steel produced by CSP in hot rolling,normalizing,cold rolling,and annealing processes.The texture in the whole process was measured and analyzed by electron back-scatter diffraction.It is found that the texture along the thickness direction in hot-rolled strips changes obviously;there are mainly copper,brass,and Goss textures in the surface layer;the 1/4 layer has weak Goss texture and rotating cube texture;γ-fib... 

采用双辊薄带连铸技术试制了3.98%Si-0.71%Al无取向硅钢铸带,研究了二次冷轧法对硅钢组织和磁性能的影响。结果表明:硅钢铸带显微组织为等轴晶组织,铸带再结晶较完全,常化对铸带显微组织影响较小。二次冷轧工艺和一次冷轧工艺下,最终退火后成品显微组织为等轴晶组织,二次冷轧法最终退火后的晶粒尺寸小于一次冷轧法。二次冷轧法能够提高成品磁性能. Effect of double cold rolling on magnetic properties and microstructure of 3.98%Si-0.71%Al non-oriented silicon Steel Sheets cast by twin-roll thin strip casting process were investigated.The results show that the structure of the thin strip is equiaxed crystal,the recrystallization is complete and normalizing has lesser effect on microstructure.Using both cold rolled and double cold rolled process,the microstructure is equiaxed grain after final annealing.The average grain size of annealed shee... 

分析了影响脱碳效果和结晶行为的各种要素及其相互制约关系,提出了Hi-B连续退火工艺曲线,总结得出快速加热及合理稳态气氛是实现工艺制度的关键。结合实际工程,介绍了在连续退火炉设计中快速加热和气氛设计的考虑方法,并指出随着Hi-B产品的发展,如何改进这些方法将是连退工程研发的方向之一。 The factors which affect decarbonization and crystallization and the mutual restriction between them were analyzed.A complete continuous annealing process for Hi-B was put forward.As a result,the rapid heating and the proper steady atmosphere were two important factors.According to an actual project,the consider methods for designing rapid heating and proper steady atmosphere were introduced,and it is pointed that with the development of Hi-B technique,how to improve these techniques would be on... 

为研究常化温度对热轧无取向硅钢组织与织构的影响,采用光学显微镜、背电子散射衍射技术研究了不同常化温度对其影响。结果表明,实验硅钢板在700～850℃温度下常化时,随常化温度的升高,晶粒尺寸增大,有利组分α织构增强,不利组分γ织构降低。对比研究了800℃和850℃常化热轧板CSL晶界分布图与取向差分布图,在本文研究条件下,Goss织构易在Σ=3,9的CSL晶界及晶粒取向差为30°～55°处形成。 The hot strips normalized at different temperatures were investigated by optical microscope and EBSD to study the effect of normalizing temperature on microstructure and texture of hot-rolled non-oriented silicon steel sheets.The results show that the grain size increases,the intensity of α-fibre texture increases,and the γ-fibre texture decreases when the hot strips are normalized at the 700-850 ℃.And CSL boundaries of Σ=3 and 15,and misorientation angles between 30° and 55° are more likely rel...