硅钢资料

通过后天抑制剂获得法制备了取向硅钢,对渗氮前后和高温退火升温阶段析出物的析出和转化规律进行了研究。研究结果表明,渗氮前脱碳退火态基体中存在少量的粗大AlN颗粒和细小AlN颗粒,渗氮处理后新析出大量的Si3N4析出物,高温退火升温阶段Si3N4将转化为(Al,Si)N,随着温度的继续升高(Al,Si)N颗粒将发生粗化,(Al,Si)N是后天抑制剂获得法制备取向硅钢的主要抑制剂。 Grain-oriented silicon steels were produced by acquired inhibitor method.The rule of precipitate transformation was studied after nitriding treatment and high-temperature finishing annealing.The results show that a small amount of large AlN and fine AlN are found in matrix before nitriding treatment,and a large amount of Si3N4 is precipitated in matrix after nitriding treatment.During the temperature rising period of high-temperature finishing annealing,Si3N4 would transform into(Al,Si)N,and(Al,... 

对新能源汽车以及驱动电机的现有市场和未来市场规模进行梳理分析，通过自建计算公式推导出我国2021年1-11月份驱动电机用电工钢的总量，进而预测未来10年中国新能源汽车驱动电机用电工钢情况，为无取向电工钢的生产和在电机中的应用提供有价值的参考。 The current market and future market size of new energy vehicles and traction motors were analyzed,and the total amount of electrical steels used in traction motors in China from January to November 2021 was derived by using self-built calculation formulas,and then the situation in the next ten years of electrical steel used in traction motors of new energy vehicles in China was predicted.It will provide a valuable reference for the production of non-grain oriented electrical steel and its appli... 

硅钢高温退火环形炉炉壳制作与安装精度要求较高,施工时通过对壳体原材料矫正、炉壳板拼焊、下料切割、型钢骨架组装及焊接、骨架及炉壳板矫正、骨架与炉壳板组装及焊接、炉壳矫正、零配件装置、定位钻孔、报验检查、出厂、内侧板安装、外侧板安装、顶板安装等环节的工艺技术控制,能保质高效地完成硅钢高温退火环形炉炉壳制作与安装,为以后同类工程的施工提供可借鉴经验。 The required precision of manufacture and installation technique of the silicon steel high temperature annealing annular-furnace shell is high.During construction , manufacture and installation of the silicon steel high temperature annealing annular-furnace shell could be finished high efficiently through correcting the raw materials of shell , furnace shell plate welding , material cutting , steel frame assembly and welding , skeleton and shell plate correction , skeleton and furnace shell asse... 

【作者】 李波； 杨晓江； ...

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

【作者】 周威； 刘侃； ...

目前随着电工钢用户冲压设备的升级,冲压速度逐步提高,对电工钢产品的硬度和强度指标提出了更高的要求。与普通硬度级别的无取向硅钢相比,高硬度50BW600的Hv硬度提高15~20,达到125以上,同时对电磁性能指标也有较高要求。本钢通过化学成份和热轧及冷轧连退生产工艺的设计,经过小批量生产试验,满足用户要求。通过对工艺的严格控制,在大批量生产过程中,保证了产品的力学性能和电磁性的检验合格率。 Currently with upgrading of stamping equipment of silicon steel user, gradually increasing of stamping speed, propose higher demand for hardness and strength of silicon steel. Compared with conventional 50BW600, high hardness 50BW600 have higher hardness, reach greater than 125Hv. Through design of chemical composition with hot mill and annealing, production test of small quantities, stamping performance meet user request. 

针对某厂DMS森吉米尔轧机生产无取向硅钢表面麻面缺陷的问题，根据生产实际，对其形成原因从乳化液及工作辊两方面因素进行了分析。结果表明：乳化液对麻面缺陷的产生有一定影响，但不是主要因素，主要原因是由于二十辊森吉米尔轧机工作辊辊径较小，轧制相同长度带钢轧辊运转周期较大，容易产生疲劳失效而导致。为此，提出通过调整冷轧工序成品轧制道次的压下率以减小轧制力，从而减小工作辊的磨损疲劳；通过对轧制乳化液浓度、温度的合理控制，以改善润滑效果、提高轧制速度，而进一步缓解轧辊疲劳的改进措施，使该钢厂无取向硅钢麻面缺陷发生率由原来的18%降至0.8%,带钢表面质量明显改善。 For the problem of surface pockmarks of non-oriented silicon steel strip produced by a DMS Sendzimir mill, based on the production practice, the formation causes were analyzed from two aspects of emulsion and working roll. The results show that the emulsion has a certain effect on the formation of surface pockmarks defects, but it is not the main factor. The main reason is that the working roll diameter of the 20-high Sendzimir mill is small, and the running period of the roll rolling the same l... 

【作者】 韩超； 代智肄； ...

对高磁感取向硅钢冷轧板分别进行800、950、1050和1120℃不脱碳的预退火处理,在800℃预退火,成品的磁性能较好。织构分析的结果表明,随着预退火温度升高,初次再结晶后有利织构组分{111}<112>与不利织构组分(118)[110]的比值f(111)/f(118)逐渐降低,初次再结晶织构的变化是成品磁性的影响因素之一。 Preliminary annealing process at different temperatures for cold-rolled strips of a high permeability grain-oriented silicon steel was investigated to study the effect of the annealing temperature on microstructure and magnetic performance of the steel.Results show that the magnetic performances of the products annealed at 800 ℃ are best.Analysis of primary recrystallization texture indicates that with rising temperature,f(111)/f(118) which is the ratio of the favorable component {111}<112>... 

利用FE-SEM、EDS分析了含不同抑制剂成分的成品取向硅钢中夹杂物的组成和形貌,统计其尺寸及数量分布;结合对磁性能测试的结果,分析了Sn、Cu、Nb和Cr对取向硅钢磁性能影响的机理。结果表明:含Sn的取向硅钢试样中夹杂物主要为块状的微米级Al-Ti-C-N-O复合物,还有少量的球形Al-N-O颗粒和块状Ti-C-N-O颗粒,棒状夹杂物较少;含Cr的取向硅钢试样中夹杂物主要为球形的微米级Al2O3,还有少量Cu-Al-N-O-S复合物,棒状夹杂物和不规则夹杂物均较少;含Cr试样中1~3μm夹杂物的平均尺寸较含Sn试样小,但数量多,而大于3μm夹杂物的平均尺寸较含Sn试样大,但数量很少。磁性能测试结果表明,外场为800A/m和2500A/m时,含Cr试样磁感应强度偏低,铁损值P1.7/50较含Sn试样高,为1.171W/kg。 The composition and morphology of inclusions in the finished grain-oriented silicon steels are analyzed by using FE-SEM and EDS, and the number density and size distribution of the inclusions are counted. The influence mechanism of Sn, Cu, Nb, and Cr on the magnetic properties of the steel is also discussed. Results show that the inclusions composition in the grain-oriented silicon steel samples containing Sn is mainly block Al-Ti-C-N-O, compounding with a few spherical Al-N-O and block Ti-C-N-O... 

采用非水溶液电解方法来提取无取向硅钢中夹杂物。通过扫描电镜(SEM)观察结果表明:无取向硅钢中主要夹杂物为六棱柱的AlN、不规则硅酸盐及球状的铁的硫化物和氧化物,其中AlN夹杂尺寸在1~5μm,数量较多,还有部分AlN的复合夹杂。进一步研究了AlN复合夹杂形成机理,采用了Thermo-Calc热力学计算软件计算出该钢样中AlN、MnS析出温度分别为1 240℃、1 200℃,而Al2O3析出温度大于1 800℃,从而为AlN复合夹杂形成机理提供了一个理论依据。 Extracting inclusions from non-oriented silicon steel in non-aqueous electrolysis is a nondestructive method to gain inclusions.Scanning electron microscopy shows that the main inclusions in non-oriented silicon steel were hexagonal AlN,which was of large quantity,irregular silicate,spherical iron sulfide and oxide.The size of AlN inclusions ranged from 1to 5μm,and there were some duplex inclusions of AlN.To further study the formation mechanism of AlN duplex inclusions,Thermo-Calc thermodynamic...