采用CVD法制备6.5%Si高硅钢,介绍了具体的制备工艺过程,研究了温度对渗硅速率和试样质量减轻的影响,同时分析了扩散时间对高硅钢中硅分布的影响。结果表明:在CVD反应过程中,反应温度高于1050℃将大大提高渗硅速率,但当温度大于1200℃后,渗硅速率趋于稳定;渗硅后,试样会减轻、减薄,随着温度升高,试样质量减轻的速率逐渐增大,在1200℃左右趋于稳定;扩散时间越长,硅分布越均匀,结合制备效率进行考虑,满足Δw表-中/b≤5的时间为适宜的扩散时间。 6.5%Si high silicon steel was manufactured by using CVD method and the process was introduced,the influence of temperature on the siliconizing rate and quality reducing rate,diffusion time on silicon distribution were investigated.Results as follows: the siliconizing rate will increase quickly when the temperature is higher than 1050 ℃,but the siliconizing rate will become steadily as the temperature up to 1200 ℃;The quality reducing rate will increase with the elevating of temperature and the r... 

本文以热轧常化板为初始材料,采用二次冷轧法与三次冷轧法制备了0.1 mm厚的取向硅钢薄带,测定相应的磁性能,并通过EBSD取向成像技术检测了二次冷轧法与三次冷轧法各工艺过程中织构与组织演变规律。结果表明,采用最终冷轧压下率适中的三次冷轧法,能在冷轧至0.1 mm时保存较多的高斯晶核,使得高温退火后的磁性能明显优于二次冷轧法。最终冷轧压下率通过影响脱碳退火后样品中的{111}<112>织构组分及Goss晶粒数量对最终二次再结晶产生重要影响。 Grain-oriented silicon steel sheets with a thickness of 0. 1 mm were produced from hot-rolled and normalized sheets by two-step-rolling and three-step-rolling methods. Their magnetic properties were measured,and the textures were detected by EBSD technique. The results show that the three-step-rolling method,which has a moderate reduction rate of final cold rolling,can maintain more { 110} < 001 >nucleus,and thus obtaining better magnetic properties compared with the two-step-method. The f... 

硅钢是钢铁产品中的\"工艺品\",是高附加值产品,通过对我国主要硅钢生产厂家的工艺设备,市场情况分析,简要介绍了我国硅钢生产消费现状,未来生产能力预测及硅钢未来发展趋势。 Silicon steel is the \"crafts\" of steel products,also is high value-added product.By analyzing process equipment and market condition of major silicon steel-making plant of China,it briefly introduces our current production consumption status,future production capacity prediction and future development trend of silicon steel. 

通过微观组织表征、高温拉伸和断口形貌分析,研究了钇(Y)元素对6.5%Si无取向硅钢组织、高温拉伸及断裂机制的影响。研究结果表明,添加Y元素可以在钢液中形成YS和YP的复合析出。YS和YP可以充当异质形核基底,提高形核率,细化凝固组织。热轧组织不均匀,由表层至芯部分别形成等轴晶、等轴晶/拉长晶和拉长晶的混合组织。退火后,热轧变形组织转变为等轴晶,含Y实验钢的退火组织得到明显细化。500℃时效处理后,含Y实验钢具备较低的有序度,300℃的拉伸断口呈现韧性断裂特征,断后伸长率达到20.2%。相反,无Y实验钢发生脆性断裂,断后伸长率仅为2.1%。研究结果证实,Y元素可以通过组织细化和降低有序度提高6.5%Si无取向硅钢的中温塑性。 The effects of yttrium(Y)on microstructure,elevated-temperature tensile properties and fracture mechanism of 6.5% Si non-oriented electrical steel were investigated by means of microstructure characterization,high-temperature tensile test and fracture analysis.The results showed that the doping of Y introduced composite Y-rich precipitates(YS/YP)in the melt.YS and YP precipitates were qualified for heterogeneous nucleation agents,which thus raised the nucleation rate and refined the solidificati... 

为探究铬、锰元素及退火温度对高强无取向硅钢性能的影响规律,借助OM、SEM、EBSD与万能拉伸试验机等分析不同制造工艺下3组不同含量铬、锰元素的无取向硅钢热轧、常化及退火处理后组织与性能。结果表明,试验钢热轧后组织不均匀,心部为沿轧向分布纤维状组织,边部为少量再结晶晶粒,常化处理能显著改善热轧板组织均匀性,消除热轧板中心部位的纤维状组织。经冷轧及退火后得到多边形铁素体晶粒,其中960℃退火,晶粒尺寸偏大,有利织构{100}组分体积分数减少,不利织构{111}组分体积分数增加,成分为0.2Mn-1Cr的1号试验钢960℃退火后铁损最大,磁感强度偏小;成分为0.5Mn-1Cr的2号试验钢930℃退火后,磁性能与强度等综合性能最佳,工频铁损P_1.5/50为2.41W/kg,高频铁损P_1.0/400为17.36W/kg,磁感应强度B_{5 000}为1.638T,抗拉强度为685MPa。 In order to study the effect of Cr,Mn and annealing temperature on the properties of high-strength non-oriented silicon steel,the microstructure and properties of three groups of non-oriented silicon steel with different Cr,Mn content under different manufacturing processes were analyzed by means of OM,SEM,EBSD and universal tensile tester.The results show that the structure of experimental steel is not uniform after hot rolling,and the core is distributed in fibrous structure along the rolling ... 

为进行磷酸盐系无铬无取向硅钢涂层烧结固化工艺研究,首先对磷酸盐系无铬无取向硅钢涂层进行热重-差示扫描量热(TG-DSC)分析;然后在不同烧结固化温度条件下,测定涂层板温随时间变化曲线;最终获得涂层烧结固化温度与时间(T-t)工艺曲线。通过中性盐雾试验、动电位极化、交流阻抗、涂层附着力以及扫描电子显微镜(SEM)和能谱(EDS)分析验证。结果表明,根据涂层烧结固化温度与时间(T-t)工艺曲线制备的涂层结构致密、性能优异,证明该工艺曲线具有合理性与正确性。 In order to study the curing process of chromium-free non-oriented silicon steel coatings,phosphatic chromium-free non-oriented silicon steel insulating coating was prepared and TG-DSC analysis of the coating was conducted,then the change of the actual temperature of the coated non-oriented silicon steel sheet with time at different curing temperatures was studied. Based on the experiments,the processing curves of curing temperature vs. curing time( T-t) for the chromium-free non-oriented silico... 

介绍了EB5325涂层液的主要性能和中冶新材生产冷轧无取向电工钢所用的涂层设备,通过多次试验摸索出使用EB5325涂层液的工艺,对涂层出现的缺陷进行分析研究,并提出解决方法,使中冶新材生产的冷轧无取向电工钢的涂层质量满足了用户的要求。 This article introduces the main properties of EB5325 and the coating equipments for cold-rolled non-oriented electrical steel. A process using EB5325 coating liquid is made through many time experiments and exploration. The appeared defects in the coating are studied and analyzed,and the solutions are proposed. The coating quality meets clients’ requirements of cold rolled non-oriented electrical steel. 

【摘要】 <正>目前,日本进口硅钢猛增,6月份4181吨,...

对取向硅钢熔融态钢液进行处理,对比研究了不同脉冲参数的作用效果。结果表明,电脉冲对钢锭晶粒组织具有明显的细化作用,凝固组织等轴晶比例大幅上升。在脉冲电容、频率、处理时间和电压中,影响等轴晶比例的最显著性因素为脉冲频率;最优正交实验参数为:电容1 200μF,脉冲频率1 Hz,处理时间5 s,脉冲电压800 V;随着输入能量的增大,等轴晶率先增大后减小,脉冲输入能量为某值时,等轴晶率最大,通过经典形核理论和热力学对这一现象进行了解释。 Research on the influence of the electric pulse on the solidification structure of oriented silicon steel was preformed.Electric pulses in different parameters were applied to molten steel and results were compared.The result shows that solidification structure of oriented silicon steel can be improved by the electric pulse,and the equiaxed crystal ratio increases obviously.Among the four parameter factors of electric capacity,frequency,applied time and voltage,the most effective factor is frequ... 

针对川威950的工艺现状,结合无取向低硅钢SGG生产的工艺特点,主要从控制其钢坯加热和轧制以及终轧温度和卷曲温度几方面入手,进行无取向低硅钢生产的工艺控制研究。同时根据近6000吨的生产实践表明,该工艺措施能很好的满足该钢种的需要。 950 process Chuanwei status quo,with non-oriented silicon steel production process features low,mainly from the control of billet heating and rolling and finish rolling temperature and coiling temperature of several aspects,for non-oriented silicon steel production process of low control at the same time According to nearly 6,000 tons of production practice shows that the process measures could well meet the needs of the steel. 

研究了无取向硅钢钙处理前后夹杂物的行为,重点考察了钙处理前后夹杂物的成分、类型、形貌和尺寸研究的变化情况,为实际生产中无取向硅钢的钙处理提供理论指导。试验发现:钙处理前夹杂物主要以Al2O3、Al2O3-MgO为主,且在夹杂物表面有AlN析出,钙处理后夹杂物以Al2O3-MgO-CaS-CaO系复合夹杂物为主,还含有少量的SiO2或AlN;钙处理前后,夹杂物形貌由多边形或不规则形逐渐向球形或近似球形转变,并且夹杂物尺寸不断增大;钙处理前后,含钙夹杂物的比例发生突变,由10%增大到74.5%,且随着钙处理时间的延长,含钙夹杂物比例下降,表明钙处理使夹杂物变性后易聚集长大并上浮去除。 Behavior of inclusions before and after calcium treatment in non-oriented silicon steel was researched by investigating changes of compositions,types,shapes and sizes of inclusions before and after calcium treatment,for the purpose of providing theoretical guidance for calcium treatment of non-oriented silicon steel in actual situation. Results indicated that Al2O3 and Al2O3-MgO were main types of inclusions before calcium treatment,sometimes AlN maybe precipitate in the outer of inclusions. Al2... 

对w(Si)=3%无取向硅钢进行表面机械研磨处理(SMAT)和异步轧制(CSR),获得表面纳米结构,再进行550～650℃、4 h固体粉末渗硅处理,用透射电镜(TEM)、扫描电镜(SEM)和X射线衍射仪(XRD)研究表层组织演变。结果表明:经过SMAT后,w(Si)=3%无取向硅钢表面形成了等轴状、取向呈随机分布的、晶粒尺寸为10 nm的纳米晶组织;异步轧制后,表面纳米晶组织保持不变;550～650℃、4 h渗硅处理后,SMAT+CSR样品表面形成化合物层,其厚度随着温度的升高由17μm增加到52μm;化合物层由Fe3Si和FeSi相组成. Nanostructured surface layer was fabricated on a 3%(mass fraction) non-grain oriented silicon steel by means of surface mechanical attrition treatment(SMAT) and cross-shear rolling(CSR),and then a solid powder siliconizing treatment was carried out for the SMAT+CSR sample at 550~650 ℃ for 4 h.The microstructural evolution was examined by using transmission electron microscopy(TEM),scanning electron microscopy(SEM) and X-ray diffraction(XRD).Experimental results show that: equiaxed nanocrystallin...