采用取向分布函数分析了无取向电工钢不同再结晶退火温度下的织构变化及织构对磁感应强度和铁损的影响,并计算了无取向电工钢的磁晶各向异性能。结果表明,随着实验钢的再结晶退火温度升高,Goss织构和立方织构组分显著增强,而{111}面织构强度却减弱。较高的退火温度有利于减小织构因子,提高磁感应强度。磁晶各向异性能计算结果显示,随着再结晶退火温度升高,无取向电工钢板的磁晶各向异性能降低。 The recrystallization texture and the relationship of texture to magnetic induction intensity and core loss of a non-oriented electrical steel were investigated by orientation distribution function analysis. The magnetic anisotropy energy of the steel was calculated also. The results show that,the intensity of Goss texture and cubic texture increases,but the intensity of { 111} texture decreases with increasing recrystallization annealing temperatures of the steel. The higher annealing temperatu... 

针对节能电机对无取向电工钢在磁性能方面的特殊要求,采用普通W600牌号的热轧板为原料,通过大量的现场工艺试验,研究总结出了\"超低张力\"的运行工艺、\"先快后慢\"的加热工艺、\"先湿后干\"的退火脱碳工艺、\"先缓后急\"的冷却工艺,生产出P1.5/50≤4.0 W/kg、B50≥1.70 T的冷轧电工钢产品,满足了节能电机的要求。 Based on the special requirements of no-oriented electrical steel for saving energy motor in magnetic aspects,using common W600 brand of hot rolled plate as raw material,through a large number of real tests,an ultra-low tension process,heating process which was quick at first and then slow,annealing decarburization process which was dry after the first wet,and a cooling technology of \"slow after the first urgent\" were concluded.Electrical steel product with P1.5/50≤4.0W/kg,B50≥1.70T was produced... 

利用EBSD技术研究了电工钢中长轴平行于轧向的柱状晶样品在热轧和退火过程中组织和取向的演变规律,并与长轴平行于板法向的样品的已有研究结果进行对比。结果表明,无论柱状晶按何种方向排列,只要表面存在剪切力,热轧后都可形成剪切织构,同时中心形成轧制织构,主要包括旋转立方织构和{112}<1-10>。柱状晶造成的影响主要体现在板中心层,长轴平行于轧向排列的样品热轧时形成的粗大旋转立方晶粒要到脱碳退火后才能完全消除,但破坏了正常的不同取向晶粒间的取向差分布及尺寸均匀性,导致二次再结晶不完全及磁性能降低。 The evolution of microstructure and grain orientation in an electrical steel containing columnar grains with its long axis being parallel to the rolling direction of sheet was studied during hot rolling and annealing by EBSD technique.The results are compared with those of samples containing columnar grains being parallel to normal direction of sheet reported in the reference [3].It was shown that,whether the long axis of columnar grains was arranged in RD or ND,shear textures can be formed in t... 

利用DSC、XRD,结合热焓分析对硅钢级氧化镁和二氧化硅的固相反应行为进行了研究。比较了不同二氧化硅原料及混合方法对硅钢级氧化镁反应性的影响,找到了一种更为有效的硅钢级氧化镁反应性的评估方法,克服了传统柠檬酸活性法在比较不同厂家生产的氧化镁的反应性上的局限性。进一步研究了Na₂B₄O₇添加剂、TiO₂添加剂对氧化镁和二氧化硅反应行为的影响,结果表明,Na₂B₄O₇添加剂含量的增加对反应有利,而TiO₂添加剂对反应有阻碍作用。 The solid-state reaction behavior between silicon-steel grade MgO and SiO₂ was investigated by DSC and XRD combined with enthalpimetric analysis.The influence of different kinds of SiO₂ and different preparation methods were studied and a specifical measurement that is more reliable was proposed to evaluate reactivity of silicon steel grade MgO.It overcomes the limitation of the traditional citric acid activity（CAA） method,which can not be used to evaluate the reactivity of... 

森吉米尔二十辊轧机是冷轧电工钢的主要机型,具有整体刚度大,辊径小,轧制道次压下量大,产品精度高等特点,简要介绍了近年来冷轧电工钢森吉米尔二十辊轧机领域进展,在轧机结构、厚度自动控制、板形自动控制等方面的技术及研究。 20-h Sendzmir reversible mill is the main type of cold rolled electrical steel which has the characteristic of high integral stiffness,small roller diameter,high pass reduction and high product quality.In this paper,the recent progress of frame structure,automatic gauge control,automatic flatness control of Sendzmir mill is introduced. 

取向硅钢热轧板中组织、织构梯度对发展完善的二次再结晶十分关键,通过对2种不同热轧工艺生产取向硅钢的组织、织构进行研究,结果表明:采用后道次大压下热轧工艺时热轧板表层再结区晶粒平均尺寸增加,再结晶区厚度增加,高温退火后二次晶粒尺寸减小;采用后道次大压下热轧工艺热轧时,热轧板中平均等效应变高,热轧板厚度心部{100}〈011〉和{100}〈001〉位向取向强度降低,({111}～{113})〈110〉位向取向强度提高,高温退火后{110}〈001〉位向偏离角降低,磁性能提高。 The texture and microstructure gradient in hot rolled grain oriented silicon steel strip was one of the essential factors to achieve a perfect secondary recrystallization.The texture and microstructure of grain oriented silicon steel strip as-rolled with two different hot rolling parameters was investigated.The results show that with big reduction at the end rolling process,the intensity of {100}〈011〉 and {100}〈001〉 orientation reduces with({111}-{113})〈110〉 orientation intensity enhanced in hot... 

利用OM,TEM,EDS与XRD技术,对Fe-3.15%Si低温取向硅钢热轧板不同常化处理后的显微组织、析出相及最终产品的磁性能进行了分析研究,并对热轧板和常化板经过冷轧后的冷轧板织构进行了对比分析.结果表明,采用1120℃保温3 min二段式冷却的常化处理工艺,常化板表层显微组织均匀,沿板厚方向的显微组织的不均匀性显著,对后续过程中形成高取向的Goss织构最有利,取向硅钢的磁性能最高;采用二段式冷却的常化冷却工艺最优,在此冷却工艺下析出的细小的析出物数量最多,且弥散分布在基体中,抑制剂的抑制效果最好,对成品获得高磁性最有利;热轧板、常化板经过冷轧后的冷轧板织构均主要由{111}〈110〉和{111}〈112〉织构组成,但常化板较热轧板冷轧后的冷轧板γ取向线织构密度明显增高,由此可以证实常化处理有助于取向硅钢最终获得高取向的Goss织构. The decreasing of slab heating temperature for grain-oriented silicon steel will reduce the amount of precipitates in hot rolled plate,and be disadvantage to the formation of ultimate Goss texture.The aim of normalizing is to control and adjust the amount,size and distribution of precipitates.Microstructures,precipitates and magnetic characteristics of finished products with different normalizing technologies for Fe-3.15%Si low temperature hot rolled grain-oriented silicon steel are researched,a... 

【摘要】 <正>编号:2012016获奖等级:特等完成单位:...

通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 

对硅钢板材分别进行异步和同步轧制,研究了轧制参数包括速比、压下量和道次对板材表面显微组织的演变的作用.结果表明,异步轧制硅钢板材表面形成了晶粒尺寸为10~50 nm,取向接近随机分布的纳米晶,而同步轧制板材的表面只形成了位错胞,证明异步轧制可以诱发表面纳米化.异步轧制板材表面纳米晶的形成过程为:在剪切力的反复作用下,高密度位错形成、滑移、湮灭和重组形成亚微米尺度的亚微晶/位错胞.随着压下量和轧制道次增加,高密度位错重复以上过程使晶粒尺寸减小、取向差增大,最终形成取向接近随机分布的纳米晶组织.大压下量和多道次是异步轧制诱发板材表面纳米化的关键,而速比的增加可以加快纳米化进程. Surface nanocrystallization(SNC) can effectively enhance the surface and global properties of the metallic materials,such as microhardness,intensity,fatigue,wear and corrosion resistances,therefore provides more promising practical industrial applicability.Up to now,several SNC treatment methods were developed based either on the principles of ball impactions or friction sliding,however,difficulty still exists for the surface treatment of large-dimensional samples with high efficiency.Recently,m... 

基于简化的取向硅钢片模型,系统地对不同的交流激励下的硅钢叠片内铁损、交链磁通和空气中指定位置的法向漏磁的分布进行了\"单片级\"的测量,并建立了相应的硅钢叠片级问题的三维有限元分析模型,进行了大规模的数值计算分析。模型实验和数值分析的结果表明垂直进入硅钢片的漏磁通和损耗呈现浅透入的特点,在硅钢片内引起的涡流损耗在总铁损中占据了\"举足轻重\"的份额。用电磁场有限元分析软件MagNet瞬态场时步法计算结果与测量结果相吻合,说明本文方法研究复杂的硅钢叠片问题的有效性。 The measurement and 3D finite element analysis of the iron loss,interlinkage flux inside the laminated silicon steel sheets and the magnetic flux densities at the specified positions are carried out based on a verifying silicon steel sheet model.The modeling results show that the leakage flux vertically through the silicon steel sheets has the peculiarity of shin effect,and the eddy current loss caused by the AC leakage flux is a significant component of the total iron loss.The calculated result... 

采用光学显微镜、X射线衍射仪等分析了宁波钢铁有限公司生产的取向硅钢不同工序下的组织及织构演变规律。结果表明:铸坯经过热轧后,沿着厚度方向组织不均匀;一次冷轧并经脱碳退火后,组织由条状纤维状变成等轴状的初次再结晶晶粒,初次再结晶平均晶粒尺寸为18.17μm,织构主要以α织构和γ织构为主;在二次冷轧后,晶粒再次被压缩,转变为纤维状,织构主要为γ织构;经过高温退火后,发生二次再结晶,晶粒异常长大,晶粒尺寸达到厘米级,织构成分为单一且锋锐的Goss织构。 The microstructure and texture evolution of oriented silicon steel produced by Ningbo Iron and Steel Co.,Ltd.were analyzed by optical microscope and X-ray diffraction.The results showed that the microstructure of the slab was inhomogenous along the thickness direction after hot rolling.After first cold rolling and decarburizing annealing,the microstructure changed from strip fibrous to equiaxed primary recrystallized grains,and the average grain size of the primary recrystallization microstructu...