结合工业化生产的无取向硅钢,探讨了氧硫交互作用对钢中夹杂物生成的影响。借助非水溶液电解+扫描电镜法,研究了不同O、S含量下钢中夹杂物的变化规律。结果表明,本实验条件下,提高O含量、降低S含量,会劣化热轧组织再结晶效果。在劣化效果上,O的作用大于S;低Si、无Al硅钢中,应尽可能降低O含量、适当提高S含量,以粗化钢中微细夹杂物,减少尺寸小于1.0μm的夹杂物的数量;O、S含量与钢中夹杂物数量不具有关联性。生产过程中,不仅要严格控制O、S含量,还要严格控制生产工艺,以免生成较多的有害夹杂物。 Based on the industrial production of non-oriented silicon steel,the effects of interaction between oxygen and sulfur on the formation of inclusions were discussed.The change of non-metallic inclusions in steel sheets was investigated by means of electrolysis with non-aqueous solution under different oxygen and sulfur content.Results show that the recrystallization microstructure of hot rolled sheets will be deteriorated with the increase of oxygen content and the decrease of sulfur content.The ... 

通过后天抑制剂获得法制备了取向硅钢,对渗氮前后和高温退火升温阶段析出物的析出和转化规律进行了研究。研究结果表明,渗氮前脱碳退火态基体中存在少量的粗大AlN颗粒和细小AlN颗粒,渗氮处理后新析出大量的Si3N4析出物,高温退火升温阶段Si3N4将转化为(Al,Si)N,随着温度的继续升高(Al,Si)N颗粒将发生粗化,(Al,Si)N是后天抑制剂获得法制备取向硅钢的主要抑制剂。 Grain-oriented silicon steels were produced by acquired inhibitor method.The rule of precipitate transformation was studied after nitriding treatment and high-temperature finishing annealing.The results show that a small amount of large AlN and fine AlN are found in matrix before nitriding treatment,and a large amount of Si3N4 is precipitated in matrix after nitriding treatment.During the temperature rising period of high-temperature finishing annealing,Si3N4 would transform into(Al,Si)N,and(Al,... 

【作者】 常波； ...

冷轧中中低牌号的无取向硅钢多采用万能凸度轧机(Universal crown mill,UCM)生产,其板形好坏受制于UCM轧机板形调节手段的协调使用。为掌握UCM轧机的板形控制特点,建立基于二维变厚度有限元的辊系弹性变形和基于三维差分的轧件塑性变形的六辊轧机耦合模型,对UCM轧机的板形调控性能进行详尽的分析,包括工作辊和中间辊弯辊、中间辊窜辊的调控功效、辊间接触压力分布等。在此基础上,提出可用指导生产的板形控制策略,指出UCM轧机在横向厚差控制方面的不足。针对工业生产中UCM轧机轧制无取向硅钢横向厚差大的问题,在大量仿真计算的基础上,开发具有高次曲线函数的边部变凸度(Edge variable crown,EVC)的工作辊。采用该工作辊后,各种品种的无取向硅钢的横向厚差不大于10μm的百分比由24%提高到99%,横向厚差的均值小于6μm,远小于之前的13μm。 Medium-low grade non-oriented silicon steel is rolled often by universal crown mill(UCM) during cold rolling.Its shape quality is dependent on the coordinated control of several shape adjustment devices of UCM.In order to understand the shape control characteristics of UCM,coupling model of six-high rolling mill,based on two-dimensional varying thickness finite element rolls elastic deformation model and three-dimensional finite difference strip plastic deformation model,is setup for the detaile... 

【作者】 王桦； 舒子龙； ...

利用OM、SEM、TEM等实验方法研究了卷取工艺对一种新型含铜无取向电工钢晶粒度和析出相的影响。结果表明,该电工钢热轧带卷取后的晶粒尺寸为18～24μm,在卷取过程中,热轧带中有一定数量的第二相析出,经EDS能谱及选区电子衍射分析,这些析出相主要为AlN。随着卷取工艺的变化,该电工钢的晶粒度大小变化不明显,析出相的类型、尺寸大小不发生改变,体积分数发生一定的改变。 The effects of coiling process on grain size and precipitates of a new copper-bearing non-oriented electrical steel were investigated by OM,TEM and other experimental method.The results show that the grain size of hot-rolled bands after coiling is 18～24 μm.The second phases precipitate during coiling process.They are mainly AlN by EDS spectra and selected area electron diffraction.With the change of coiling process,the grain size of the electrical steel does not change significantly;the type and... 

采用取向分布函数分析了无取向电工钢不同再结晶退火温度下的织构变化及织构对磁感应强度和铁损的影响,并计算了无取向电工钢的磁晶各向异性能。结果表明,随着实验钢的再结晶退火温度升高,Goss织构和立方织构组分显著增强,而{111}面织构强度却减弱。较高的退火温度有利于减小织构因子,提高磁感应强度。磁晶各向异性能计算结果显示,随着再结晶退火温度升高,无取向电工钢板的磁晶各向异性能降低。 The recrystallization texture and the relationship of texture to magnetic induction intensity and core loss of a non-oriented electrical steel were investigated by orientation distribution function analysis. The magnetic anisotropy energy of the steel was calculated also. The results show that,the intensity of Goss texture and cubic texture increases,but the intensity of { 111} texture decreases with increasing recrystallization annealing temperatures of the steel. The higher annealing temperatu... 

取向硅钢成品的晶粒尺寸非常大,其易磁化方向[001]晶向对于轧向的偏差角度对其磁性能影响极大。本文介绍了取向硅钢二次再结晶后成品晶粒位向的几种测定方法,包括侵蚀法、劳厄法、OIM法、极图法和非对称X射线衍射法等,并对这几种测量方法进行了比较。 The finished product of grain-oriented silicon steel has immense grain size ranging from millimeters to centimeters and the deviation angles of easy magnetization direction from rolling direction plays a remarkable role in magnetic properties of grain-oriented silicon steel.The methods in common use for determining the deviation angles of crystal direction are introduced,which include the etch-figure method,the Laue method,the OIM method,the pole figure method and the asymmetrical X-Ray diffract... 

简述了无取向硅钢环保涂层发展背景,分析了硅钢环保涂层的特点及国内、外研究进展,提出了硅钢保涂层下一步的发展方向。 The back ground of environmental protection coating of non-oriented silicon steel was described in this paper.The characteristics and study progress in domestic and foreign of environmental protection coating of non-oriented silicon steel were analysised.The next development direction of environmental protection coating of non-oriented silicon steel was put forward. 

选用Q235和Q345钢,在纯锌浴和含钛量分别为0.05%、0.10%、0.15%、0.20%(质量分数)的合金浴中浸镀0.5、1、3、5、8 min。利用扫描电子显微镜和能谱仪研究了钛对热浸镀锌组织和生长动力学的影响,并提出钛对含硅钢铁锌反应抑制作用的机理。结果表明:钛的加入缩短了Γ的孕育期,促进了合金层中δ的生长和ζ的消失,δ的生长依然受扩散控制,呈抛物线生长规律;Zn-0.05%Ti锌浴可以很好的抑制高硅钢的硅反应性;含硅钢热浸镀锌钛合金浴时,在锌浴中会形成锌铁钛三元T相,该相能吸收ζ晶界处富集的硅,从而抑制了铁锌反应。 Both Q235 and Q345 steels were immersed for 0.5 to 8 min in Zn bath with different amount of Ti,ranging from 0 to 0.20 mass%,for galvanization.The effect of Ti in Zn bath on microstructure and growth kinetics of hot-dip galvanizing coatings on the two steels were investigated by means of SEM and EDS analysis.Base on the experiment,the mechanism of Ti additions in controlling Fe-Zn reaction was proposed.The results show that addition of Ti in the zinc bath decreases the incubation time of Γ phase... 

采用ZMLMC超高梯度定向凝固装置,研究了5种凝固速率(10、35、80、150和450μm/s)对定向凝固50W600无取向硅钢的固液界面稳定性转变规律和一次、二次枝晶间距的影响。研究结果表明,在特定的温度梯度下,随着凝固速率的增加,定向凝固的固液界面由胞状晶转变为胞状枝晶,再转变为细小的树枝晶。随着凝固速率的增加,定向凝固组织的枝晶形貌逐渐细化,一次和二次枝晶间距逐渐减小,且与冷却速率之间都符合指数关系:λ1=151.73×(G L·R)-0.31,λ2=22.07×(G L·R)-0.44。当冷却速率达到4.275℃/s时,一次、二次枝晶间距分别为112μm、14.1μm。 Under the conditions of certain temperature gradient and different solidification rate,the directional solidification experiment of non-oriented electrical steel 50W600 was carried out.The microstructure of 50W600 steel was also analyzed in different solidification rate.The result shows that the solid/liquid interface of the steel undergoes an evolution from cellular,cellular dendrite and finally to fine dendrite morphologies.The dendrite refines gradually and the distance between dendrites decr... 

通过固溶度积公式计算及热模拟实验,对不同热装和加热温度条件下的无取向硅钢铸坯中析出相进行了研究.在低于950℃热装时,铸坯中AlN的析出量和尺寸不再变化,但MnS和AlN-MnS的数量及平均尺寸随着热装温度降低而进一步增加,并在温度低于600℃时达到最大值后保持不变.与1200℃相比,1100℃加热的铸坯中AlN、MnS的总固溶量相对更少.相比850℃热装,600℃热装再加热到1100℃的铸坯中AlN和MnS的总固溶量更少,且AlN和MnS尺寸更大.合适的热装温度和加热温度分别为600℃和1100℃. Based on solubility product calculation and thermal simulation experiments,precipitated phases in continuous casting slabs of non-oriented silicon steel were systematically studied at different hot charging and heating temperatures.When the hot charging temperature is below 950 ℃,the content and size of AlN remain unchanged,but the quantity and size of MnS and AlN-MnS increase when the hot charging temperature decreases,reach maximum and remain unchanged when the hot charging temperature is belo...