6.5%(质量分数)Si高硅钢具有优异的软磁性能和广阔的应用前景,然而其室温脆性和低的热加工性极大地制约了它的发展。近年来,人们对高硅钢制备技术的研究已经取得了很大的进展,如何通过织构的优化提高高硅钢的磁性能越来越受到人们的关注,归纳和总结了不同工艺制备的高硅钢中的织构演变规律和特点,以及对应的典型磁性能。 6.5wt% Si high silicon steel has excellent soft magnetic properties and wide application prospect.However,the brittleness of room-temperature and poor workability of cold rolling limit its deve-lopment.Recently,the researches of the preparations of high silicon steel have been already made great breakthroughs,and then,more and more attentions are focused on how to optimizing the texture of high silicon steel so as to obtain the best magnetic properties.The evolution of textures of 6.5% Si high s... 

概述了无抑制剂法生产取向电工钢的特性及其用途;总结无抑制剂生产取向电工钢的原理及工艺方案.重点讨论了成分方案,即元素对磁性能的影响和最终高温退火方案对二次再结晶的影响.研究结果表明,无抑制剂取向硅钢化学成分范围没有普通取向硅钢和高磁感取向硅钢严格,提高了成材率;最终高温退火决定了二次再结晶的好坏,从而最终决定成品磁性能,最佳的高温退火温度在850～950℃之间. This article provides an overview on the characteristics and uses of inhibitorless process producing grain-oriented electrical steels.The mechanism of inhibitorless process and technology programs were discussed.The results show that the chemical composition and final annealing were determined according to magnetic properties.The inhibitor-free grain oriented silicon steel has loose range of chemical composition;Secondary recrystallization occurs mainly in the final annealing and the best anneal... 

聚焦无取向硅钢产品标准,从电磁性能、表面性能、机械性能以及尺寸公差与边部质量等维度对国际标准IEC、EN、JIS、ASTM以及国标GB进行了分析研究。分析得出,各类标准在电磁性能方面要求基本一致;ASTM标准的机械性能要求有别于其他几个标准。 In this paper,non-oriented silicon steel standards of EN,JIS,GB and ASTM were compared and analyzed. It is showed that,all types of standards in electromagnetic performance requirements are basically the same. Surface properties in ASTM standard are expressed in the most detailed. The mechanical properties requirements of the standards,except for ASTM,are basically the same. 

【摘要】 <正>10月9日至11日,武钢一硅钢技术改造工...

研究了取向硅钢制备过程中常见的两种冷轧工艺,主要研究了一阶段冷轧与两阶段冷轧+中间退火工艺对初次再结晶组织及织构的影响.结果表明:采用两阶段冷轧+中间退火工艺制备以Cu2S为主抑制剂的取向硅钢,其初次再结晶平均晶粒尺寸为18.1μm,高斯晶粒的体积分数为0.6%,迁移性强的重位点阵晶界(Σ5+Σ9)和高能晶界(20°~45°取向偏差角)所占比例分别为1.8%和50.4%.与一阶段冷轧工艺相比,其初次再结晶晶粒较细,且高斯晶核与特征晶界所占的比例较高,有利于高斯晶粒发生二次再结晶. Two common cold-rolling processes of grain oriented silicon steel and the effects of the single stage cold rolling and tw o-stage cold rolling w ith intermediate annealing processes on the primary recrystallization microstructure and texture w ere investigated. The results revealed that for the grain oriented silicon steel prepared under the tw o-stage cold rolling process w ith intermediate annealing w ith Cu 2 S as the main inhibitor,the average grain size of the primary recrystallization micr... 

借助光学显微镜、扫描电镜、交流磁性能测量仪和万能拉伸试验机研究了0.3 mm厚高强无取向电工钢冷轧板在780、820、860和900℃退火保温2 min后的组织、织构和性能。结果表明:在退火温度范围内,试验钢均发生了完全再结晶,得到等轴状的铁素体晶粒;随着退火温度的升高,平均晶粒尺寸从9.2μm增长到41.3μm,工频铁损和400 Hz高频铁损均先大幅减小后趋于平缓,磁感应强度先升高后降低。在820℃退火时,铁损P_1.5/50=5.51 W/kg,P_1.0/400=33.22 W/kg均处于较低值,磁感应强度B₅₀₀₀最大,为1.649 T。试验钢的屈服强度和抗拉强度均随退火温度的升高而降低,780℃退火时屈服强度为496 MPa, 900℃退火时降低至407 MPa。综合磁性能和力学性能考虑,试验钢的最佳退火温度是820℃。 Microstructure, texture and properties of 0.3 mm thick high strength non-oriented electrical steel cold rolled sheet annealed at 780 ℃, 820 ℃, 860 ℃ and 900 ℃ for 2 min were studied by means of optical microscope, scanning electron microscopy, AC magnetic property tester and universal tensile testing machine. The results show that in the annealing temperature range, complete recrystallization of the experimental steel occurs and equiaxed ferrite grains are obtained. With the increase of annealin... 

电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

利用背散射衍射技术(EBSD)和XRD,研究了两段式脱碳退火工艺对取向硅钢纵截面初次再结晶的微区取向、取向差分布、特殊晶界(CSL)及高温退火试样高斯织构。分析了初次再结晶晶界特征对取向硅钢高温退火后宏观织构的影响。结果表明:初次再结晶的纵截面基体中Σ3和Σ5晶界使得高斯晶粒有着较高的迁移率,在高温退火时借助20o～45°的大角度晶界的界面能吞并周围{111}<112>晶粒迅速长大,形成密度水平较高的高斯织构。 Micro area orientation of primary recrystallization,the misorientation distribution,special boundaries under different two-stage decarburization annealing and the Goss texture under high temperature annealing the longitudinal section of grain-oriented silicon steel were detected by electron back scattering diffraction(EBSD) and X-ray diffraction(XRD).The effect of primary recrystallization grain boundary on macrotexture after high temperature annealing was analyzed.The results show that the Σ3 a... 

分析了冲裁硅钢芯片时出现的质量问题,针对影响硅钢芯片冲裁质量的4大因素——人、原材料状态、工艺和工装进行了工艺试验和分析,根据原材料状态的差异,采用不同工艺方案,特别是如何合理选择冲裁模具间隙,解决了硅钢芯片冲裁时产生的主要质量问题,使冲裁的硅钢芯片达到最佳质量状态,并满足硅钢芯片的使用性能。 The problems occurred during silicon steel chip punching and the factors that affect the quality of silicon steel chip punching were analyzed,the factors include 4aspects,that is,people,raw material status,process and frock,at the same time,process tests and analysis aimed at the factors that affect punching quality were did,according to the difference of raw material status,corresponding process schedules wee taken,especially in how to reasonably select punching dies clearance,which solved the ... 

为了消除硅钢在连续退火机组产生的浪形缺陷,对浪形缺陷产生的主要原因进行了分析。制定了相应控制措施,对炉内带钢张力、冷却段输出、碳套辊与带钢的同步性、无氧化炉燃烧状态等参数进行了调整;在生产组织上安排高低牌号宽窄规格穿插生产、定期更换碳套辊等,实施后效果明显。 The main cause leading to waviness defects of silicon steel is analyzed in order to eliminate the waviness defects of silicon steel in continuous annealing line.And thus corresponding measures for controlling these defects are made by means of adjusting these parameters such as the tension of silicon steel coils in continuous annealing furnace,the output in cooling section and the combusting condition of the non-oxidation furnace as well as keeping the synchronization between carbon sleeved roll... 

为了解决在纹理背景下冷轧硅钢表面缺陷的分割问题,提出了基于局部信息结构张量和活动轮廓模型的硅钢表面缺陷分割方法。将图像的局部信息引入到结构张量中;在结构张量提取的特征空间中,以KL距离作为区域的概率密度相似性度量建立分割图像的活动轮廓模型;采用Split-Bregman数值解法对模型进行求解。运用提出的分割方法对硅钢表面的一些常见缺陷如纵向划伤、横向划伤、异物和孔洞等进行分割实验。实验结果表明,该方法可以准确地分割出硅钢表面缺陷区域,验证了该方法的有效性。 In order to address the segmentation problem for cold rolled silicon steel surface defect based on the texture background,a novel method based on structure tensor and active contour model is proposed.Image local information is introduced to the structure tensor.In the extracted feature space of structure tensor,KL distance is treated as a regional similarity measure of the probability density to establish active contour model for image segmentation.The numerical solution of Split-Bregman is used... 