初次再结晶退火工艺对3%Si取向硅钢组织和织构的影响
试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ...
表面机械研磨/异步轧制无取向硅钢薄带的渗硅行为
对w(Si)=3%无取向硅钢进行表面机械研磨处理(SMAT)和异步轧制(CSR),获得表面纳米结构,再进行550~650℃、4 h固体粉末渗硅处理,用透射电镜(TEM)、扫描电镜(SEM)和X射线衍射仪(XRD)研究表层组织演变。结果表明:经过SMAT后,w(Si)=3%无取向硅钢表面形成了等轴状、取向呈随机分布的、晶粒尺寸为10 nm的纳米晶组织;异步轧制后,表面纳米晶组织保持不变;550~650℃、4 h渗硅处理后,SMAT+CSR样品表面形成化合物层,其厚度随着温度的升高由17μm增加到52μm;化合物层由Fe3Si和FeSi相组成. Nanostructured surface layer was fabricated on a 3%(mass fraction) non-grain oriented silicon steel by means of surface mechanical attrition treatment(SMAT) and cross-shear rolling(CSR),and then a solid powder siliconizing treatment was carried out for the SMAT+CSR sample at 550~650 ℃ for 4 h.The microstructural evolution was examined by using transmission electron microscopy(TEM),scanning electron microscopy(SEM) and X-ray diffraction(XRD).Experimental results show that: equiaxed nanocrystallin...
取向硅钢成品晶粒的位向测定方法
取向硅钢成品的晶粒尺寸非常大,其易磁化方向[001]晶向对于轧向的偏差角度对其磁性能影响极大。本文介绍了取向硅钢二次再结晶后成品晶粒位向的几种测定方法,包括侵蚀法、劳厄法、OIM法、极图法和非对称X射线衍射法等,并对这几种测量方法进行了比较。 The finished product of grain-oriented silicon steel has immense grain size ranging from millimeters to centimeters and the deviation angles of easy magnetization direction from rolling direction plays a remarkable role in magnetic properties of grain-oriented silicon steel.The methods in common use for determining the deviation angles of crystal direction are introduced,which include the etch-figure method,the Laue method,the OIM method,the pole figure method and the asymmetrical X-Ray diffract...
承钢无取向电工钢CGW800的研发
承钢采用铁水预处理(脱硫)→转炉提钒→转炉冶炼→RH精炼→连铸→轧制工艺,成功研发了无取向电工钢CGW800。试制的CGW800钢碳含量≤0.006 0%、氮含量<0.004 0%,热轧后的金相组织为铁素体和少量渗碳体,晶粒度5.5级,获得了较粗大、均匀的晶粒,钢板的成分和力学性能达到了标准要求。 In Cheng Steel,the CGW800 non- oriented electrical steel is successfully developed with process of hot metal pre- treating,vanadium extracting with converter,smelting with converter,RH refining,continuous casting and rolling. In the steel,the carbon content is not higher than 0. 006 0%,nitrogen less than0. 004 0%,the metallographic structure after hot rolling is ferrite and a little amount of cementite,grain size is 5. 5 degree,relative large and even grain got. The composition and mechanical pr...
无取向硅钢晶粒长大过程中应力对织构和晶界变化的影响
采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang...
无铬无取向硅钢涂层烧结固化工艺
为进行磷酸盐系无铬无取向硅钢涂层烧结固化工艺研究,首先对磷酸盐系无铬无取向硅钢涂层进行热重-差示扫描量热(TG-DSC)分析;然后在不同烧结固化温度条件下,测定涂层板温随时间变化曲线;最终获得涂层烧结固化温度与时间(T-t)工艺曲线。通过中性盐雾试验、动电位极化、交流阻抗、涂层附着力以及扫描电子显微镜(SEM)和能谱(EDS)分析验证。结果表明,根据涂层烧结固化温度与时间(T-t)工艺曲线制备的涂层结构致密、性能优异,证明该工艺曲线具有合理性与正确性。 In order to study the curing process of chromium-free non-oriented silicon steel coatings,phosphatic chromium-free non-oriented silicon steel insulating coating was prepared and TG-DSC analysis of the coating was conducted,then the change of the actual temperature of the coated non-oriented silicon steel sheet with time at different curing temperatures was studied. Based on the experiments,the processing curves of curing temperature vs. curing time( T-t) for the chromium-free non-oriented silico...
制备硅钢级氧化镁前驱体的原料水化研究
以青海盐湖水氯镁石为初级原料,采用喷雾热解法制备原料氧化镁,原料氧化镁通过水化制备硅钢级氧化镁前驱体氢氧化镁。原料氧化镁水化实验中对水化剂、水化温度、水化时间、液固比、搅拌速度及陈化时间对水化率、过滤速度和纯度的影响进行系统研究。采用均匀实验设计和DPS数据处理,(依次)通过建模分析、二次多项式模型回归建立数学模型,再通过各因素方差分析和总方差分析,确定了理论最优实验条件,再用理论最优条件作重复实验进行验证,最终确定了原料氧化镁的最佳水化条件。在水化温度60℃,水化时间105 min,液固比4,陈化时间4 h,水化剂1含量4.0%,水化剂2含量3.15%,洗水量4倍,搅拌速度120 r/min时,原料氧化镁的水化率达99.50%以上,得到的硅钢级氧化镁前驱体氢氧化镁纯度高、过滤性能良好。 By spray pyrolysis method,bischofite in Qinghai salt Lake,as primary raw material,was used to prepare precursor raw material MgO for silicon-steel MgO.The precursor raw material MgO was used for preparing Mg(OH)2 which was the precursor of silicon-steel MgO,by hydration method.In the hydration experiment of precursor raw material MgO,some experiment parameters were investigated systematically.such as the hydrated agent,the temperature and time of hydration,liquid/solid ratio that affected the hy...
硅钢脱硫影响因素分析研究
对RH法(真空循环脱气法)生产的冷轧硅钢的脱硫原理及影响因素进行了分析研究。研究表明:降低顶渣中FeO、MnO的含量,提高钢液温度,增加脱硫剂的加入量并延长其循环时间有利于提高脱硫效率。 The principles of desulfurization and its influence factors of cold rolling silicon steel during RH process have been studied in this paper.The result indicated that reducing contents of FeO and MnO,rising temperature of the liquid steel,increasing quantity of desulfurizer,lengthening cycle time of desulfurzer are benefit for desulfurization.
双辊薄带连铸3.98%Si-0.71%Al无取向硅钢的组织、织构和磁性能
采用双辊薄带连铸工艺制备了厚度为2.4mm的3.98%Si-0.71%Al无取向硅钢带,经常化、冷轧、不同温度退火后,对其显微组织、析出物、织构和磁性能进行了检测分析。结果表明:随着退火温度的提高,退火板晶粒尺寸增大,组织均匀性提高;退火板析出物主要是AlN和MnS与AlN复合析出物,尺寸较粗大,达0.5~2.5μm;退火板织构沿厚度方向变化明显,表层和1/2层存在较强的{100}织构,1/2层还存在较强的{111}织构,1/4层主要是{112}织构;随退火温度的升高相应的铁损和磁感应强度均降低。 Using twin roll thin strip continuous casting technique,the 3.98%Si-0.71%Al no-oriented silicon steel strip in thickness of 2.4mm was produced.The microstructure,precipitates,texture,and magnetic properties of the sheet after normalizing,cold rolling and annealing at different temperatures were studied.The results show that with annealing temperature increase,the grain size and uniformity of annealed sheet increased.The main precipitates in coarse size of 0.5-2.5μm in annealed sheet were AlN and...
无取向硅钢钢液增钛原因分析
对无取向硅钢炼钢全流程钢液增钛的原因进行了分析,认为铁水钛含量、转炉出钢温度、转炉下渣量、精炼渣TiO2含量、钢水罐及RH浸入管混钢种生产是影响钢液增钛的主要原因。通过采取低钛铁水冶炼,减少转炉下渣量,提高出钢温度,添加白灰改质精炼渣等措施,均能够降低钢液中的钛含量。 After analyzing the causes leading to increased content of titanium in molten nonoriented silicon steel during whole steelmaking process, it was concluded that such factors as content of titanium in hot metal, tapping temperature from converter, quantity of roughing slag entered into the ladle from converter, content of TiO2 in refining slag, molten steel ladle car,carrying out the steelmaking of different steel grades by the same ladle and same RH immersion tube were the main causes ...
典型半工艺电工钢产品M660-50K5生产及应用技术解析
对欧盟市场汽车压缩机专用产品进行技术解析,对比分析了其电磁性能、退火和发蓝处理、物理性能、化学成分、应用特点等参数。探讨国内外电工钢产品应用方式的不同特点,并结合鞍钢自身工艺装备和炼钢、热轧、冷轧工艺参数介绍了其生产可行性。提供了冶金工艺流程下,后工序电工钢专业生产线及传统冷轧系统生产线两种生产方式,均能满足用户最终使用要求。 The technology of automotive compressor accommodation manufacture of European Economic and Monetary Union market was described.The magnetic properties,annealing bluing,physical properties,chemical composition,application parameters were analysed.The different characteristics of the application of electrical steel products,the feasibility of manufacture on the existing technology and equipment,steelmaking,hot rolled,cold rolled technical parameters were discussed.The professional product line of ...
无取向电工钢硫含量控制技术研究
针对采用含钒铁水生产无取向电工钢存在的铁水脱硫率低、转炉冶炼过程回硫量大、成品硫含量偏高的问题,通过对含钒钛铁水脱硫,减少转炉冶炼过程回硫以及RH脱硫技术等方面的研究,大幅度降低了电工钢成品硫含量。生产表明钢中w(S)=0.001 9%~0.006 9%,平均为0.004 2%;w(S)≤0.008%的比例达到了100%,且w(S)≤0.005%的比例也达到了91.43%。 In cognizance of the problems of low desulphurization rate for hot metal,large sulfur-recovery in converter as well as high sulfur content in products in producing non-orientation electrical steel with vanadium-content hot metal countermeasures have been carried out.Sulfur content in non-orientation electrical steel is decreased obviously by way of study on technologies of desulphurization for hot metal with vanadium & titanium,sulfur-recovery control in converter and desulphurization in RH ...