硅钢资料

为了弄清楚高硫硅钢中的硫化物析出行为及其对钢的微观组织和电磁性能的影响，以便为工业化生产制定更为合理的硫含量控制标准和采取更为有效措施减轻炼钢生产的硫含量控制压力，结合0.25% Si 无取向硅钢 ，采用非水溶液电解提取 + 扫描电镜/透射电镜观察相结合的方法 ，研究了0.006 8%、0.010 2%、0.025 5% 和 0.035 3% 硫含量条件下，钢中的硫化物夹杂物组成和存在形式及其形貌、种类、尺寸、数量变化，以及相应的热轧、成品试样的微观组织和电磁性能变化。结果表明，随着钢中硫含量的增加，钢中的硫化物逐渐由 MnS→MnS+Cu₂S→Cu₂S转变，数量逐渐增多，尺寸向高低两个方向发展。相应地，导致热轧再结晶组织劣化和抑制了成品晶粒尺寸长大。随着钢中硫含量的增加，钢的磁感、铁损劣化程度逐渐增大。钢中的硫含量平均每增加 0.01%，涡流损耗、磁滞损耗分别劣化0.24 W/kg 和 0.41 W/kg，而磁感会劣化 0.009 T。但是 ，在硫含量为 0.010 2% 时 ，铁损可以低于 6.0W/kg，而在硫含量为 0.025 5% ... In order to find out the precipitation behavior of sulfide inclusions and the corresponding changes of microstructure and electromagnetic properties of high sulfur silicon steel sheets, so that to design more suitable sulfur concentration controlling limit for industrial manufacture and to release the steel-making difficulty effectively, Based on the change of given sulfur concentration 0.006 8%, 0.010 2%0.025 3% and 0.035 3%, the type and composition, the size and number, and the size distribut... 

在50Kg氧化镁坩埚真空感应炉上进行高硅电工钢的脱氧试验。结果表明,通过控制原料的成分、高真空下的碳氧反应和炉衬分解向钢液中的供氧,可使钢液的总氧含量≤15×10-6;在维持高温高真空条件下,当钢液中的反应达到一定程度后,延长精炼时间并不能降低钢液的总氧含量;完成精炼后加入硅钙合金沉淀脱氧可进一步降低钢液的总含氧量,但脱氧效果有限。 The test of high-silicon electric steel deoxidation has been carried out in 50Kg vacuum induction furnace with magnesium oxide crucible.Results show that the total oxygen could be ≤15×10-6in molten steel by controlling material components,carbon-oxygen reaction in high vacuum and oxygen contamination from crucible materials on molten steel;And when the reaction was carried through to a certain extent,total oxygen in molten steel could not be reduced by the extension of refining period in high va... 

采用电解法和扫描电镜研究了300 t转炉-RH精炼钙处理对无取向硅钢板（%:≤0.005C、1.2～2.2Si、0.2～0.6Mn、≤0.20P、≤0.005S、0.2～0.6Al、0～0.01Ca）中夹杂物的影响。结果表明,钢中Al含量为0.25%和0.35%时,钢中溶解氧均小于1×10^-4%,钙处理后都会产生CaS夹杂物,尤其是含0.35%Al的钢水;钙处理可以有效减少钢中的夹杂物数量,尤其是0.5μm以下的微细夹杂物数量;钙处理后夹杂物的种类以AlN、CaS为主,同时还含有少量的氧化物夹杂物以及AlN-CaS复合夹杂物,尺寸主要为1.5～5.0μm。 The effect of 300 t converter-RH refining calcium treatment on inclusions in non-oriented silicon steel sheet （%:≤0.005C,1.2～2.2Si,0.2～0.6Mn,≤0.20P,≤0.005S,0.2～0.6A1,0～0.01Ca） has been studied by electrolysis and scanning electron microscope.Results show that with 0.25%and 0.35%Al content in steel,all the dissolved oxygen in liquid is less than 1×10^-4%,and the CaS inclusions are produced after calcium treatment,especial for the liquid containing 0.35%Al;the amount of inclusions in ste... 

针对本钢薄板坯铸机在生产无取向电工硅钢的过程中存在的铸坯拉断、中包增碳、增氮等问题,进行了连铸工艺优化。通过采用新型无碳中间包覆盖剂、环保中间包干式料及专用结晶器保护渣后,降低了铸坯增碳量;通过控制钢包到中间包的增氮环节,降低钢水增氮;适当增大二冷水量,控制钢水过热度,防止铸坯拉断等生产事故的发生。改进工艺后,精炼后到成品铸坯的平均增碳量能控制在10×10-6以内,平均增氮量能控制在4×10-6以内。 The technology optimization has been adopted for preventing nitrogen increasing and carbon increasing in Benxi thin slab producing non-oriented silicon steel.Measures accordingly were adopted and satisfactory results were achieved. 

利用OM、EBSD等手段研究了热轧板两段式正火时在700℃保温不同时间(0、10、30、60 min)对含Sb冷轧无取向电工钢磁性能的影响。结果表明,700℃保温10 min处理的样品铁损最小,磁感最高。对成品板的组织分析结果表明,试样的晶粒尺寸随700℃保温时间的延长先增大后减小,保温10 min时晶粒尺寸达到最大;分析成品试样织构发现,有利织构组分随700℃保温时间的延长先增加后减少,保温10 min时有利织构组分所占百分比最高。因此,含Sb冷轧无取向电工钢两段式正火时在700℃保温10 min时磁性能最好。 Effect of two-stage normalization on magnetic property of non-oriented electrical steel containing antimony was investigated by using optical microscope(OM) and electron back-scattered diffraction technology(EBSD).The experimental results show that the iron loss and magnetic permeability of the specimen insulated at 700 ℃ for 10 min are lowest and highest respectively.The grain size of the finish specimens increases first and then decreases with the increase of holding time.Similarly,the advanta... 

以能量平衡和辐射换热理论为基础,通过合理假定,建立了硅钢无氧化加热炉数学模型。采用数值计算的方法,通过自编程序,完成对带钢加热过程温度场的仿真。结果显示:数学模型能够反映带钢在无氧化炉内的加热过程,其升温曲线能够与工艺曲线相吻合;现行炉温分布并非最优,数学模型能够为炉温分布的优化、炉段的设计提供理论依据。 Mathematical model of NOF Section of Continuous Annealing Furnace is established based on energy balance and radiation heat exchange. The temperature field of steel is simulated by mathematical computation. The simulating results show that the mathematical model can reflect the heating process of silicon steel in NOF section, and the heat-up curve is coincide with the processing curve. From the results,it is known that the current furnace temperature gradient is not the best, and the mathematica... 

无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason... 

【机构】 宝山钢铁股份有限公司规划与科技部； ...

研究了应用电感耦合等离子体质谱(ICP-MS)同时测定硅钢中痕量铝、钼、钒、钛、铌元素的分析方法。通过条件试验对测量参数进行了优化,确定RF功率1 400 W,泵速30rpm,采样深度140,雾化压力0.90。样品采用硝酸分解,以Be、Y混合内标校正了测量过程中高基体引起的信号漂移。根据测量时存在的质谱干扰情况,选择同位素27 Al、98 Mo、51 V、47 Ti和93 Nb作为测定同位素,同时通过调节仪器参数使得双电荷离子和氧化物离子的产率最低,以减少其带来的干扰。采用基体匹配法配制校准溶液,以标准加入法建立工作曲线,并扣除试剂空白。该方法各元素的测定下限均可达到1μg/g。用于硅钢标准样品的测定,所得结果与参考值完全吻合,各元素的RSD小于5.2%。 A method for the determination of trace aluminum,molybdenum,vanadium,titanium and niobium in silicon steel by inductively coupled plasma mass spectrometry(ICP-MS) was described.A series of single parameter condition experiment was conducted.The optimized operation parameters with RF power 1 400 W,turbo pump rate 30 rpm,sampling depth 140 and nebulizer pressure 0.90 were obtained.The samples were dissolved by HNO3,and the Be and Y mixing internal standard were used to eliminate the signal drift c... 

利用场发射扫描电镜观察了以MnS为主要抑制剂的普通取向电工钢加工过程中第二相粒子的分布状态,统计了粒子面密度、平均尺寸以及相应的尺寸分布.结果显示,热轧加工造成了大量第二相粒子弥散、细小地析出,同时基体仍保持过饱和状态.冷轧变形会造成第二相粒子的回溶行为,而基体的过饱和状态会减弱回溶现象.中间退火与脱碳退火过程中会同时存在新粒子的形核及已析出粒子的粗化两个过程,而在最终二次再结晶升温阶段则以第二相粒子明显粗化为主. The distribution of second phase particles in conventional grain-oriented electrical steels during manufacturing processes with MnS as inhibitors was observed by field emission scanning electron microscopy,while the areal particle density,the average particle size and the corresponding size distribution were statistically determined.It is indicated that hot rolling leads to dispersive precipitation of a large amount of fine second phase particles and the matrix keeps a supersaturated state furth... 

试验2.3Si无取向硅钢(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al)冷轧板由常化和未常化的2.5 mm热轧板冷轧至0.6 mm(压下率76%),经750~950℃2.5 min中间退火后再冷轧至0.5 mm(压下率16.7%),成品板经890℃+960℃2.5 min退火。研究了中间退火温度对该钢晶粒尺寸、织构和磁性能的影响。结果表明,随中间退火温度的升高,二次冷轧前晶粒和成品晶粒增大,成品中不利织构组分{111}和{112}减弱,磁性能得到改善。热轧板经过常化时的磁性能明显好于未经常化时的磁性能,但中间退火温度较高时常化对磁性能的有利作用减弱。 The test cold sheet of 2.3Si non-oriented silicon steel(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al) is first cold-rolled from normalized and un-normalizing 2.5 mm hot-rolled plate to 0.6 mm sheet(reduction 76%),then intermediate annealed at 750~950℃ for 2.5 min and double cold-rolled to 0.5 mm sheet(reduction16.7%),the finished sheet annealed at 890℃+960℃ for 2.5 min.Effect of the intermediate annealing temperature on grain size,texture and magnetic performance of the steel has been studied.... 

研究了冷轧大压下量,950℃退火时间对一种新型含铜无取向电工钢晶粒度和织构的影响。结果表明,大压下量冷轧,随压下量的增加,退火晶粒向γ线聚集,形成强{111}<112>织构。提高冷轧压下率,退火织构{111}<100>,{110}<001>强度减弱,增加退火时间,退火织构{111}<110>,{100}<001>,{110}<001>强度变弱。采用87.5%冷轧压下率和950℃退火60 s,有利织构{100},{110}占有率最大。 The effect of annealing(950 ℃) time with high cold rolling reduction on grain size and texture of a new non-oriented electrical steel containing copper was investigated.The results show that for high cold rolling reduction,most annealed grains are oriented along γ-fibre with increasing cold rolling reduction ratio and strong texture {111}<112> is formed.With increasing the cold rolling reduction ratio,the intensity of annealed texture {111}<110>,{011}<100> decreases.With increa...