选用Q235和Q345钢,在纯锌浴和含钛量分别为0.05%、0.10%、0.15%、0.20%(质量分数)的合金浴中浸镀0.5、1、3、5、8 min。利用扫描电子显微镜和能谱仪研究了钛对热浸镀锌组织和生长动力学的影响,并提出钛对含硅钢铁锌反应抑制作用的机理。结果表明:钛的加入缩短了Γ的孕育期,促进了合金层中δ的生长和ζ的消失,δ的生长依然受扩散控制,呈抛物线生长规律;Zn-0.05%Ti锌浴可以很好的抑制高硅钢的硅反应性;含硅钢热浸镀锌钛合金浴时,在锌浴中会形成锌铁钛三元T相,该相能吸收ζ晶界处富集的硅,从而抑制了铁锌反应。 Both Q235 and Q345 steels were immersed for 0.5 to 8 min in Zn bath with different amount of Ti,ranging from 0 to 0.20 mass%,for galvanization.The effect of Ti in Zn bath on microstructure and growth kinetics of hot-dip galvanizing coatings on the two steels were investigated by means of SEM and EDS analysis.Base on the experiment,the mechanism of Ti additions in controlling Fe-Zn reaction was proposed.The results show that addition of Ti in the zinc bath decreases the incubation time of Γ phase... 

分析了影响脱碳效果和结晶行为的各种要素及其相互制约关系,提出了Hi-B连续退火工艺曲线,总结得出快速加热及合理稳态气氛是实现工艺制度的关键。结合实际工程,介绍了在连续退火炉设计中快速加热和气氛设计的考虑方法,并指出随着Hi-B产品的发展,如何改进这些方法将是连退工程研发的方向之一。 The factors which affect decarbonization and crystallization and the mutual restriction between them were analyzed.A complete continuous annealing process for Hi-B was put forward.As a result,the rapid heating and the proper steady atmosphere were two important factors.According to an actual project,the consider methods for designing rapid heating and proper steady atmosphere were introduced,and it is pointed that with the development of Hi-B technique,how to improve these techniques would be on... 

为提高无取向硅钢导磁性能,研究了不同剪切方式对无取向硅钢剪切处磁畴结构的影响。利用纳米磁流体观测无取向硅钢剪切后边部磁畴结构。结果表明,硅钢无论在机械剪切还是线切割后的边部磁畴都会发生不同程度的改变:线切割对边部磁畴结构改变较小,边部磁畴分布均匀且连续,在距边缘0～20μm范围内出现磁畴宽度变小现象;机械剪切对磁畴的改变较为严重,剪切处磁畴零乱且不连续,在距边缘20μm处仍难以观察到完整的磁畴结构。 The effects of different shearing modes on magnetic domain structure of cold rolled non-oriented silicon steel are studied in this paper.The magnetic domain of cold rolled non-oriented silicon steel is observed by nanometer magnetic fluid pattern method.The results show that the edge magnetic domain structure will be changed by mechanical shear and wire-electrode cutting,the variation of edge magnetic domain structure wire-electrode cutting edge is very small,the magnetic domain structure is wel... 

【作者】 欧阳帆； 肖侃； ...

热轧轧制工艺对产品性能和轧制稳定性影响很大,对中低牌号无取向电工钢,当在两相区轧制时,热轧塑性明显降低,板形变坏,易出现边裂等情况。以50W1000为例,通过对其变形抗力进行研究,得出把两相区控制在F4与F5之间为最佳轧制工艺的结论。在此基础上制定了一套较为合理的热轧工艺制度。采用新的轧制工艺后,50W1000热轧精轧的稳定性明显改善,热轧产品合格率由开发初期的40%左右提高到95%以上。 The hot rolling process has great influence on product′s performance and rolling stability.For the low medium grade non-oriented electrical steel,when non-oriented electrical steel is rolled in tow phase region,the hot rolling plasticity reduces obviously,the shape of strip goes bad and easily to crack at the edge.The deformation resistance of 50W1000 steel was investigated.The results show that the optimal rolling process is to control the two phase region between F4 and F5.Based on the results... 

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

针对本钢薄板坯铸机在生产无取向电工硅钢的过程中存在的铸坯拉断、中包增碳、增氮等问题,进行了连铸工艺优化。通过采用新型无碳中间包覆盖剂、环保中间包干式料及专用结晶器保护渣后,降低了铸坯增碳量;通过控制钢包到中间包的增氮环节,降低钢水增氮;适当增大二冷水量,控制钢水过热度,防止铸坯拉断等生产事故的发生。改进工艺后,精炼后到成品铸坯的平均增碳量能控制在10×10-6以内,平均增氮量能控制在4×10-6以内。 The technology optimization has been adopted for preventing nitrogen increasing and carbon increasing in Benxi thin slab producing non-oriented silicon steel.Measures accordingly were adopted and satisfactory results were achieved. 

针对攀钢高硫铁水冶炼现状,结合不同生产工艺路线,论述了攀钢近年来为实现低硫电工钢的生产,在铁水预处理、转炉冶炼、钢水精炼过程中硫控制技术的开发与应用,形成了低硫洁净钢生产工艺技术,实现了低硫电工钢的生产。低硫电工钢RH脱硫率可达到20%左右,成品[S]控制在0.006%左右。 According to the smelting situations of hot metal with high sulphur content at Panzhihua Steel,combined with different produce processes,technologies for controlling the sulfur content during hot metal pretreatment,converter smelting,and second refining are developed. Technologies in low-sulfur clean steelmaking are formed. Low-sulfur electric steel are produced. As for the desulfurization rate of lowsulfur electric steel can reach about 20%,and the content of [S] in products is controlled to ab... 

【作者】 朱传芳； 潘恒韬； ...

在实验室模拟CSP流程制备了不同含量稀土铈(质量分数0~0.018%)的1.2%Si无取向电工钢,并对其进行1 000℃×5min的再结晶退火处理,研究了铈质量分数对无取向电工钢夹杂物、显微组织、再结晶织构和磁性能的影响。结果表明:随着铈质量分数的增加,微细夹杂物数量、再结晶晶粒尺寸、{100}和{110}织构组分、磁感应强度先增后减,{111}织构组分、铁损先减后增;铈的质量分数为0.005 1%时,钢中的夹杂物数量最少,再结晶晶粒尺寸最大,有利织构最多,磁性能最优,铁损P15/50为3.253W·kg-1,磁感应强度B50为1.751T。 Non-oriented electrical steels containing different contents rare earth Ce element(0-0.018wt%) were prepared in the laboratory by simulated CSP(compact strip production)process,and then recrystallization annealing at 1 000 ℃ for 5 min were performed,the effects of Ce content on inclusion,microstructure, recrystallization texture and magnetic properties of non-oriented electrical steels were studied.The results show that with the increase of Ce content,the amounts of fine inclusion,the size of re... 

介绍了EB5325涂层液的主要性能和中冶新材生产冷轧无取向电工钢所用的涂层设备,通过多次试验摸索出使用EB5325涂层液的工艺,对涂层出现的缺陷进行分析研究,并提出解决方法,使中冶新材生产的冷轧无取向电工钢的涂层质量满足了用户的要求。 This article introduces the main properties of EB5325 and the coating equipments for cold-rolled non-oriented electrical steel. A process using EB5325 coating liquid is made through many time experiments and exploration. The appeared defects in the coating are studied and analyzed,and the solutions are proposed. The coating quality meets clients’ requirements of cold rolled non-oriented electrical steel. 

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。 Microstructure development and texture evolution of conventional grain oriented silicon steel,which were annealed at same annealing temperature and different annealing time under wet H2 atmosphere,were investigated through metallographic observation and electron backscattered diffraction analyzing.The results show that the primary recrystallization finishes in 120 s at 820 ℃ under wet H2 atmosphere.With the extending of annealing time,{111}<112> texture decreases,{111}<110> texture d...