取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加铜可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布。利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧(TSCR)工艺的3种不同铜含量的取向硅钢热轧板织构。结果表明:不同铜含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;铜含量约在0.4%时,热轧板次表层的{110}<001>织构比例最高,而热轧板心部的{100}<110>织构比例最低;铜含量对热轧织构中{114}<110>和{001}<100>织构发展有显著影响。 The texture gradient in hot rolled grain oriented silicon steel strip is one of the essential factors to achieve a perfect secondary recrystallization.The addition of copper can significantly reduce the slab reheating temperature of grain oriented silicon steel,so as to impact the texture distribution in the hot rolled strip.The texture of hot rolled grain oriented silicon steel strip as-rolled by thin slab casting and rolling process(TSCR) in laboratory with three different copper contents was ... 
2011-01-28 75 5.8

1.本外观设计产品的名称:硅钢片。;2.本外观设计产品的用途:多片硅钢片用来共同组成马达的转子的其中一个部件。;3.本外观设计产品的设计要点:在于本外观设计产品的形状。;4.最能表明设计要点的图片或照片:立体图。;
2020-12-16 51 6.8

本实用新型公开了一种铁芯硅钢片卷材的自动放卷上料装置,包括放卷机、导向平台和防折组件,所述导向平台间距设置在放卷机的下方,所述导向平台与放卷机之间构成供料带缓冲的缓冲空间,所述料带在缓冲空间内呈U型状走向,所述导向平台的上方间距设置有防折组件,所述防折组件与导向平台之间构成供所述料带通过的导向通道,所述防折组件设置在料带的内弯侧。通过防折组件对料带的内弯侧进行支撑,能够有效的防止料带被过度弯折,能够对料带进行缓冲和缓冲保护,保证料带放卷上料的稳定性。
2021-12-21 81 6.8

选用Q235和Q345钢,在纯锌浴和含钛量分别为0.05%、0.10%、0.15%、0.20%(质量分数)的合金浴中浸镀0.5、1、3、5、8 min。利用扫描电子显微镜和能谱仪研究了钛对热浸镀锌组织和生长动力学的影响,并提出钛对含硅钢铁锌反应抑制作用的机理。结果表明:钛的加入缩短了Γ的孕育期,促进了合金层中δ的生长和ζ的消失,δ的生长依然受扩散控制,呈抛物线生长规律;Zn-0.05%Ti锌浴可以很好的抑制高硅钢的硅反应性;含硅钢热浸镀锌钛合金浴时,在锌浴中会形成锌铁钛三元T相,该相能吸收ζ晶界处富集的硅,从而抑制了铁锌反应。 Both Q235 and Q345 steels were immersed for 0.5 to 8 min in Zn bath with different amount of Ti,ranging from 0 to 0.20 mass%,for galvanization.The effect of Ti in Zn bath on microstructure and growth kinetics of hot-dip galvanizing coatings on the two steels were investigated by means of SEM and EDS analysis.Base on the experiment,the mechanism of Ti additions in controlling Fe-Zn reaction was proposed.The results show that addition of Ti in the zinc bath decreases the incubation time of Γ phase... 
2013-09-28 57 5.8

本发明公开一种高牌号无取向硅钢的轧制方法,用于控制森基米尔二十辊轧机对原料带钢进行轧制,所述方法包括:根据所述原料带钢的规格参数,确定所述森基米尔二十辊轧机的第一中间辊的辊型及第二中间辊的辊型;根据所述原料带钢的合金含量及所述规格参数,确定所述第一中间辊的有效平面量;根据所述规格参数,确定所述森基米尔二十辊轧机的径向调整机构的凸度值;根据所述合金含量,设定所述森基米尔二十辊轧机进行轧制时的负荷分配和张力;按照所设定的负荷分配和张力分配对所述原料带钢进行轧制,且在轧制过程中以预设乳化液流量进行喷淋,以制得成品。本发明可减少高牌号无取向硅钢在轧制过程中发生脆性断裂,提高轧制的稳定性及生产效率。
2021-09-15 47 6.8

本发明属于金属材料加工技术领域,具体涉及取向硅钢罩式炉高温退火低保温阶段二段式退火工艺,包括:将涂镁取向硅钢卷装入密闭的罩式炉中,并向罩式炉内通入氮气将炉内氧气充分排出;通电升温并将氮气转换为10m3/h氨分解气,接着点燃放散阀,将温度升至500‑600℃,恒温13h;500‑600℃低保温结束后检测内部气体露点是否小于0℃;本发明提供的取向硅钢罩式炉高温退火低保温阶段二段式退火工艺能够解决普通冷轧取向硅钢罩式炉高温退火热处理低保温阶段,钢卷在高温下不被水蒸汽氧化,消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷,降低钢带铁损、提高磁感、降低生产成本。
2021-04-30 42 6.8

一种电工钢切片用导向装置,涉及电工钢生产装置技术领域,包括导向台、支撑腿、安装块、转轴、辊体、电动机、安装板、滑杆、移动板和导向板;支撑腿设置在导向台底部;安装块设置有两个,两个安装块均设置在导向台横向一侧,两个安装块沿纵向分布;转轴转动设置在两个安装块之间;辊体设置在转轴上,辊体位于两个安装块之间,辊体位于导向台上方;电动机设置在安装块上,电动机与转轴驱动连接;安装板设置有两个,两个安装板分别设置在导向台纵向两侧上部;滑杆设置有两个,两个滑杆均设置在两个安装板之间,两个滑杆沿横向分布。本实用新型能够在电工钢的钢带切片之前进行导向限位工步,使得电工钢切割时不会被切割歪,切片的精度高。
2021-10-23 58 6.8

无取向硅钢的磁性能主要取决于铁素体的晶粒尺寸、晶体织构和钢中的夹杂物。通过合适的化学成分设计以及采用适宜的夹杂物控制技术,可以获得最佳的夹杂物控制效果,使其纯净度大幅度提高或者无害,最终获得磁性能优良的高级别无取向硅钢。同时,为满足节能、环保、高效需求,无取向硅钢正朝着节能降耗、环境友好以及多功能、高效率、易加工等方向发展。 The magnetic properties of non-oriented silicon steel mainly depend on the grain size of ferrite,the crystallographic texture,and the inclusions in the steel.The optimum inclusion control effects can be obtained through a suitable chemical composition design and an appropriate inclusion control technique,and then the liquid steel will get be clean or the inclusion will get be harmless,finally the excellent magnetic property of the non-oriented silicon steel can be obtained.Meanwhile,in order to ... 
2013-03-28 62 5.8

采用磁控溅射方法,分别在纯Fe以及低硅钢基片上沉积富Si膜,并对其进行真空扩散热处理.通过能谱分析及X射线衍射研究了Si在纯Fe与低硅钢基体中的扩散特征,运用DICTRA软件建立了扩散模型.研究发现Si在纯Fe基体中扩散时发生γ-Fe(Si)→α-Fe(Si)相转变,扩散速率受控于相界面的迁移.当沿截面Si含量梯度不足以驱动相界面正向迁移时,延长扩散时间会发生相界面回迁现象,最终趋于单一相内均匀化扩散过程.Si在低硅钢基体中的扩散符合Fick扩散第二定律. Si-rich films were deposited on pure iron and low-Si steel substrates by direct current magnetron sputtering,and then were subjected to vacuum annealing.The distribution characteristics of Si across Fe and low-Si steel substrates were studied by energy spectrum analysis(EDS) and X-ray diffraction(XRD).DICTRA software was used to simulate the diffusion models.It is found that the diffusion behavior of Si in the Fe substrate is from γ-Fe(Si) phase to α-Fe(Si) phase and the rate of diffusion is con... 
2012-10-28 38 5.8

本实用新型公开了一种用于硅钢片叠装的工装,包括安装底座,所述安装底座上设置有限位装置,所述限位装置包括多个水平限位柱和多个竖直限位柱;各个水平限位柱之间的缝隙的尺寸等于其对应放置的硅钢片的宽度,各个竖直限位柱与安装底座的底边之间的距离等于其对应放置的硅钢片的总长度;所述各个竖直限位柱设置在各个水平限位柱之间的缝隙所正对的位置;采用多个水平限位柱和多个竖直限位柱进行水平和竖直方向上均对硅钢片进行定位;使用此工装叠装出来的成品,长短一致,侧面相当整齐;本实用新型,结构简单,操作方便。
2021-02-02 57 6.8

研究二次冷轧压下率对于硅的质量分数为3.0%的无取向硅钢组织结构和磁性能的影响。结果表明:当第二次冷轧压下率从0变化至16.7%时,铁损逐渐增加,磁感逐渐降低。当第二次冷轧压下率大于16.7%时,随压下率的增加,铁损逐渐减小,磁感逐渐增加。当第二次冷轧压下率大于38%时,二次冷轧法所能获得的磁性能明显优于一次冷轧法。 Effect of double cold reduction on magnetic,microstructure and texture of 3.0% Si non-oriented silicon steel sheets was investigated.The results show that the iron loss increases and magnetic induction reduces as the percentage redcution in secondary cold rolling changes from 0 to 16.7%.The core loss can be reduced remarkably,and magnetic induction can get a little benefit if the percentage redcution in double cold reduction is higher 16.7%.In case of higher than 38% of the percentage redcution ... 
2012-11-28 53 5.8

试验研究了退火温度(850~950℃)和时间(5~18 min)对2.3 mm热轧硅钢板(/%:0.036C,3.15Si,0.21Mn,0.005P,0.007S,0.032A1)6道次轧制的0.35 mm冷轧板组织和织构的影响。结果表明,退火温度越高,晶粒平均尺寸越大,900℃5 min退火时平均晶粒尺寸41.39μm,试样织构主要集中在γ取向线上的{111}<112>织构组分和{111}<110>织构组分;900℃18 min退火时平均晶粒尺寸为48.08μm,试样的{111}面织构和{112}面织构密度都明显减弱,{001}面织构增强,磁性能较优。 The effect of annealing temperature(850 ~950 ℃) and holding time(5 ~ 18 min) on structure and texture of 0.35 mm sheet by 6 passes cold-rolling from 2.3 mm hot-rolled plate of silicon steel(/%:0.036 C,3.15 Si,0.21 Mn,0.005 P,0.007 S,0.032A1) has been tested and studied.Results show that the higher the annealing temperature the coarser the average grain size;As annealing at 900 ℃ for 5 min the average grain size of steel sheet is 41.39 μm,and the texture in sample is mainly concentrated in y orie... 
2014-06-28 60 5.8