结合工业化生产的无取向硅钢,进行了RH精炼添加稀土合金实验。结果表明,1.15%(质量分数)Si钢的脱硫反应,主要发生在添加稀土合金之后的前5min。最佳的稀土合金添加量为0.6～0.9kg/t钢。钢液经过稀土处理后,加入的稀土总量越多,稀土氧硫化物夹杂物的尺寸就越大,但热轧带钢再结晶效果会逐渐变差,成品带钢晶粒尺寸先是快速长大,而后逐渐减小。最佳的钢中存留稀土含量与钢的化学成分有关,应严格控制在2.0×10-3%～6.0×10-3%(质量分数)。在此范围内,钢的铁损先是快速降低,而后缓慢升高,钢的磁感应强度则单调降低。 Based on the industrial production of non-oriented electrical steel,rare earth(RE) alloy treatment during the RH refining process was studied.The results showed that the effects of desulfurization and total concentration of RE remained in steel mainly depended on the chemical compositions of different steel grades.For 1.15wt% Si steel grade,the desulfurization reaction mainly focused on the initial 5min after RE alloy added during the RH refining process.The suitable RE alloy addition was 0.6-0.... 

以马鞍山钢铁集团公司电工钢板形优化控制研究项目为背景,系统地研究了热轧、冷连轧和单机架轧机在电工钢生产过程中的边缘降控制问题。通过现场数据采集、工况数值模拟计算和工业化大生产试验,设计出适用、合理的电工钢板形控制的辊型优化曲线,满足了不同工序、不同机型的板形控制策略要求,解决了电工钢板形质量问题,取得了显著的经济效益。 Based on the project of electric steel strip shape optimization control,problem of edge drop control was systematically studied in production of electric steel of hot-rolling mill,cold-rolling mill and single stand mill.Roll optimization contour was designed out in point and reasonable by collection of work condition data,numerical simulation and test of industrial production.The shape control system can meet with the different working steps and difference mills,and quality problem of electric s... 

本实用新型公开了一种具有废料回收机构的硅钢板带加工用切割装置，包括箱体，所述箱体的前侧靠近顶部处设有电机，所述箱体的顶部靠近前侧处固定连接有竖板，本实用新型一种具有废料回收机构的硅钢板带加工用切割装置，电机在工作时既能带动切割刀进行切割作业，同时还能带动第一筛板和第二筛板以相邻转轴为中心上下摆动，切割的废屑从切割槽穿过达到箱体内腔，第一筛板和第二筛板对废料进行筛分处理，通过隔板设置，隔板将集料盒分为两个存储空间，隔板右侧存储穿过第一筛板和第二筛板的细料，隔板的左侧存储被第一筛板和第二筛板过滤下来的粗料，既方便操作人员对废料进行集中处理，还对废料进行了筛分处理，以此方便对废料进行分类重复利用。

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

本发明公开了一种耐热刻痕型取向硅钢涂层用涂液，其溶剂为水，其含有：磷酸盐、胶态二氧化硅、铬酐和乙醇。本发明还公开了一种耐热刻痕型取向硅钢板，其包括基板，所述基板表面具有采用上述的耐热刻痕型取向硅钢涂层用涂液涂覆在基板上而形成的涂层。相应地，本发明还公开了上述取向硅钢板的制造方法，其包括步骤：在基板表面涂覆所述涂液，基板的刻痕沟槽涂液填充率＞95％；进行烧结处理，其中烧结处理中的板温为780‑900℃。本发明的耐热刻痕型取向硅钢涂层用涂液具有良好的流动性，其可以涂覆于耐热刻痕取向硅钢基板的表面中，涂覆后，能有效填充基板的刻痕沟槽，且可以在其表面形成涂层，保证耐热刻痕取向硅钢在具有低铁损的同时具备更高的安全性。

将Fe-1.5Si硅钢试样分别在1 000~1 200℃空气条件下氧化30 min,观察发现在1 000℃和1 100℃时,氧化层与基体界面处存在硅酸亚铁,而当温度为1 200℃时,硅酸亚铁不但存在于界面处,同时也存在于氧化层中.将各温度下得到的带有氧化层的试样进行单道次热轧试验,压下率分别为10%和30%,发现1 000℃和1 100℃时,较高的压下率使氧化层破碎更加严重,但是单道次热轧未能改变氧化层的结构;当温度为1 200℃时,由于液态的硅酸亚铁的出现,单道次热轧能够将界面处的液化的硅酸亚铁层挤压到氧化层中,消除了硅酸亚铁层的钉扎基体的效应,改善了氧化层与基体界面的平直度. Specimens of Fe-1.5Si silicon steel were oxidized at 1 000 ~ 1 200 ℃ in air for 30 min.At 1 000 ℃ and 1 100 ℃ fayalite was observed at the scale/substrate interface.While at 1 200 ℃fayalite was found both at the scale/substrate interface and at the outer oxide layer.Then after the single-pass hot rolling process,with the compression ratio of 10% and 30%,it was found that at 1000 ℃ and 1 100 ℃,higher compression rate accelerated the broken of the scale layers,but the scale structure was not affec... 

采用双辊薄带连铸工艺制备了厚度为2.4mm的3.98%Si-0.71%Al无取向硅钢带,经常化、冷轧、不同温度退火后,对其显微组织、析出物、织构和磁性能进行了检测分析。结果表明:随着退火温度的提高,退火板晶粒尺寸增大,组织均匀性提高;退火板析出物主要是AlN和MnS与AlN复合析出物,尺寸较粗大,达0.5~2.5μm;退火板织构沿厚度方向变化明显,表层和1/2层存在较强的{100}织构,1/2层还存在较强的{111}织构,1/4层主要是{112}织构;随退火温度的升高相应的铁损和磁感应强度均降低。 Using twin roll thin strip continuous casting technique,the 3.98%Si-0.71%Al no-oriented silicon steel strip in thickness of 2.4mm was produced.The microstructure,precipitates,texture,and magnetic properties of the sheet after normalizing,cold rolling and annealing at different temperatures were studied.The results show that with annealing temperature increase,the grain size and uniformity of annealed sheet increased.The main precipitates in coarse size of 0.5-2.5μm in annealed sheet were AlN and... 

结合工业化生产的无取向硅钢,探讨了氧硫交互作用对钢中夹杂物生成的影响。借助非水溶液电解+扫描电镜法,研究了不同O、S含量下钢中夹杂物的变化规律。结果表明,本实验条件下,提高O含量、降低S含量,会劣化热轧组织再结晶效果。在劣化效果上,O的作用大于S;低Si、无Al硅钢中,应尽可能降低O含量、适当提高S含量,以粗化钢中微细夹杂物,减少尺寸小于1.0μm的夹杂物的数量;O、S含量与钢中夹杂物数量不具有关联性。生产过程中,不仅要严格控制O、S含量,还要严格控制生产工艺,以免生成较多的有害夹杂物。 Based on the industrial production of non-oriented silicon steel,the effects of interaction between oxygen and sulfur on the formation of inclusions were discussed.The change of non-metallic inclusions in steel sheets was investigated by means of electrolysis with non-aqueous solution under different oxygen and sulfur content.Results show that the recrystallization microstructure of hot rolled sheets will be deteriorated with the increase of oxygen content and the decrease of sulfur content.The ... 

通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 

本实用新型提供一种定子铁心硅钢片固定结构，包括硅钢片堆叠结构、扣片，所述硅钢片堆叠结构由多个硅钢片层层堆叠而成，所述硅钢片沿边缘处设有多个凹槽，多个硅钢片堆叠后，其凹槽形成一条条通槽，所述扣片扣在通槽上，其扣片的两端设有弯折面将硅钢片堆叠结构的两端卡住，利用扣片的方式进行硅钢片固定，减少硅钢片导通现象，达到减少涡流损失的目的，扣片有极易更换的方便性，可轻易改变硅钢叠片的厚度，只需要更换扣片长度即可。

本发明属于双取向硅钢技术领域，公开了一种双取向硅钢薄带及其制备方法，包括：选取具有Si、Al、Mn、C和Fe，且具有一定取向的硅钢薄带；将其进行冷轧；将冷轧板在N2、H2保护气氛中进行退火处理。本发明通过合理的轧制和退火工艺搭配，使具有Goss取向的硅钢薄带转变为具有旋转立方取向的硅钢薄带，将单取向硅钢转变为双取向硅钢。本发明具有工艺简单和便于利用钢铁企业现有设备的特点，所制备的双取向硅钢薄带具有双向铁损低和磁感高的性能。本发明制备的双取向硅钢薄带在与轧向成45°的两个方向上具有优异的双向磁性能，解决了现有双取向硅钢薄带的制备工艺复杂、设备要求高、不利于工业生产的问题。

本发明公开了一种适应高频率工况下低铁损无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯—热轧—正火—酸洗—冷轧—连续退火—涂绝缘涂层并固化；所述冷轧步骤中，采用六辊单机架往复式轧机经5道次一次冷轧至目标厚度，冷轧过程中前三道次采用变速异步轧制方法，使钢板表层在剪应力作用下位错密度增加，这样在退火后表层晶粒尺寸细化而心部晶粒粗大，通过本发明的方法可生产得到心部为粗大等轴晶粒，表层为纳米级细等轴晶粒的电工钢产品，该产品的铁损P1.5/50≤2.35W/kg，P1.0/400≤14.0W/kg。